POLY(ETHYLENE TEREPHTHALATE)-GRAPHENE NANOCOMPOSITES FROM IMPROVED DISPERSION
A composition and a method are provided for graphene reinforced polyethylene terephthalate (PET). Graphene nanoplatelets comprising a suitable surface area are added to a dispersion medium for producing graphene reinforced PET. The average surface area may range between substantially 15 m2/g and 750 m2/g. In some embodiments, the dispersion medium may be comprised of ethylene glycol. The dispersion medium and graphene nanoplatelets are sonicated to disperse the nanoplatelets within the dispersion medium. The dispersion medium and graphene nanoplatelets are centrifuged to remove larger nanoplatelets that are not suitably dispersed within the dispersion medium. A supernatant solution of dispersed graphene nanoplatelets and dispersion medium is decanted and then used for polymerization of the graphene reinforced PET. The resultant graphene reinforced PET is comprised of a continuous matrix of PET with a reinforcement material comprising dispersed phase graphene nanoplatelets.
Latest Niagara Bottling, LLC Patents:
This application claims the benefit of and priority to U.S. Provisional Application, entitled “Poly(Ethylene Terephthalate)-Graphene Nanocomposites From Improved Dispersion,” filed on May 9, 2018 and having application Ser. No. 62/669,282.
FIELDEmbodiments of the present disclosure generally relate to the field of polymer composites. More specifically, embodiments of the disclosure relate to a graphene reinforced polyethylene terephthalate composition and methods for dispersing graphene nanoplatelets within polyethylene terephthalate.
BACKGROUNDComposites are multi-phase materials comprised of a matrix and a reinforcement material. Herein, the matrix is a polymer and the reinforcement a nanofiller dispersed in the matrix. Polymer composites take on characteristics dependent on their reinforcement, including changes in elastic modulus and tensile strength. A broad range of inorganic and organic particles, such as minerals, glass, carbon black, and wood, have been used as fillers in the development of thermoplastic composites. Recent research into nanomaterials has led to the development of nanoscale fillers that can be used to create nanocomposites with enhanced properties compared to conventional composites. The logical progression is to develop polymer nanocomposites, which are defined as a multi-phase, polymer-based material, such as thermoplastics, thermosets, or elastomers, with a filler exhibiting at least one dimension below 100 nm.
Nanofillers characteristically have a high surface-area-to-volume ratio. The material properties of composites depend on the interaction between the matrix and the nanofiller. Nanocomposites often have more significant improvements in properties per volume fraction of filler than conventional composites. This is because of the higher surface-area-to-volume ratio of nanoscale materials, which allows for more interaction between the filler and the matrix per volume fraction. Due to the low fraction of filler, nanomaterials are typically much lighter than conventional composites. They are also more easily incorporated into existing polymer processing methods. This leads to materials that have many potential applications in a variety of industries, such as packaging materials, automotive, and aerospace applications. Over the past two decades, several different types of nanofillers, (e.g. nanoparticles, clay, carbon nanofibers (CNFs), carbon nanotubes (CNTs), graphene, SiO2, TiO2, etc.) have been utilized for the development of polymer nanocomposites. While improvements in various properties of polymer nanocomposites are dependent on the type of nanofiller used, the way they are integrated into the matrix also affects the performance and properties of the finished product. When producing nanocomposites, the most significant challenge is often obtaining a uniform distribution of the nanofiller in the matrix. Several studies describe commonly used methods to fabricate nanocomposites such as solution blending, in-situ polymerization, and melt compounding.
Solution blending consists of the dissolution of the polymer in a suitable solvent followed by mixing with a dispersed suspension of nanofiller. While the production of nanocomposites through this approach is straightforward, one of the limitations is the selection of a suitable solvent. Due to the low solubility of some polymers in various solvents, blending often requires elevated temperatures which can make processing challenging. In addition, the solvent's properties can affect the distribution of the nanofiller, having a negative impact on the properties of nanocomposites prepared by this technique.
In-situ polymerization is another approach for the development of nanocomposites. This technique involves a chemical reaction resulting in the incorporation of a nanofiller within a polymer matrix. For example, for in-situ polymerization of PET nanocomposites, the nanofiller is first dispersed in ethylene glycol (EG), a liquid, PET polymer precursor. The dispersions are then mixed along with terephthalic acid (TPA) through an esterification reaction to create the monomer. The second step, polycondensation reaction, is undertaken to continue the preparation of the polymer with intercalated nanofillers. This technique can result in a more homogenous distribution of nanofiller in the matrix.
Melt compounding consists of mixing the polymer and the nanofiller at high temperatures. In this process, the nanofiller is first compounded with the molten polymer to then fabricate nanocomposites using an injection molding process. Melt compounding utilizes shear forces to incorporate the nanofiller in the matrix. Of the three methods, melt compounding is the most industrially accessible, since it does not require solvents and can be used in existing large-scale processes.
Poly(ethylene terephthalate) (PET) is a thermoplastic polyester. Depending on its processing, such as thermal history (rate of cooling) and mechanical history (stretching), it can exist in both amorphous and semi-crystalline structures. Through a multi-step polymerization process, PET can be synthesized with a specifically desired molecular weight. The molecular structure of PET consists of a phenyl ring and two ester groups and is illustrated in
PET is semi-crystalline. The degree of crystallinity in PET has a dominant influence on the mechanical and thermal properties, meaning that the physical properties of PET can be significantly improved by arrangment and degree of crystallization in the microstructure. In polymer processing, the crystallization half-time (inverse of crystallization rate), t1/2, refers to the time at which the extend of crystallization is completed at 50%. The crystallization half-time is often used to estimate the processing conditions of a new polymer by comparing the t1/2 with those of known polymers. Compared to other polyesters, PET has a slow crystallization rate. Huang et al. and Chen et al. compared the PET crystallization rate with other polyesters including poly(butylene terephthalate) (PBT) and poly(trimethylene terephthalate) (PTT). They ranked the crystallization rate in the order of PBT>PTT>PET. Based on the results obtained in this research, it was found that the crystallization half-time (inverse of crystallization rate) was 0.95±0.15 min for pristine PET. Additionally, PET has limited barrier performance, which constrains the use of PET in some applications. However, research suggests that the addition of nanofillers increases the crystallinity of PET, which also contributes to enhancement in its mechanical and barrier properties.
Graphene is a relatively new nanofiller that has been used in the development of polymer nanocomposites. Graphene-based nanocomposites consist of single-layer graphene sheets, few-layer graphene sheets, and multi-layer graphene sheets. Within the layers, covalent bonds are strong, whereas between the layers the weaker Van der Waals force dominates. The elastic properties and breaking strength of graphene sheets have been measured and reported as 100 times greater than steel, with a Young's modulus of 1.0±0.1 TPa and tensile strength of 130 GPa. Geim and Novoselov's 2010 Nobel Prize-winning research illustrated that a one-square-meter graphene hammock would support a 4 kg cat while only weighing as much as one of the cat's whiskers. Recent discoveries revealed the thermal conductivity of graphene to be in the range of 1500 to 2500 W/(m·K). When incorporated appropriately, graphene can significantly improve the mechanical, electrical, and thermal properties of the host polymer. This makes it a desirable nanofiller in nanocomposites for a variety of applications.
There is increasing demand for graphene-based nanocomposite materials. Zhao et al., reported a 150% increase in tensile strength by only adding 1.8% (vol. %) graphene nanoplatelets into poly(vinyl alcohol) (PVA). Graphene shows promise in biomedical devices as sensors because of its large surface-area-to-volume ratio. Research suggests that certain molecules are sensitive to disease indicators and are likely to attach to the carbon atoms in graphene. Furthermore, graphene-based materials have been used to develop supercapacitors acting as energy storage materials due to their long cycle life and higher power density. Micromechanical cleavage is a well-known technique to produce graphene using an adhesive tape on graphite. In this approach, graphene is detached from graphite powder. By repeating this procedure, multi-layer graphene can be cleaved into few-layer graphene. Although this method is simple, it is impractical for obtaining larger amounts of graphene. Graphene can also be dispersed in a liquid-phase medium through exfoliation of graphite. However, the size of the dispersed graphene sheet is low compared to micromechanically cleaved graphene. In addition to these approaches, chemical vapor deposition (CVD) has also been reported as a useful process to synthesize graphene on transition metals. In this method, graphene deposited on the metal can be easily transferred to other substrates with PET being a common choice. While the CVD method is efficient to produce graphene with better crystallinity than that formed by any other method, controlling the thickness of graphene during synthesis is a hurdle impacting future applications. Table 1 summarizes the advantages and disadvantages of the techniques used to produce graphene.
Recently, Istrate et al., reported on the fabrication of melt-compounded PET-graphene nanocomposites. They found that at a nanofiller loading as low as 0.07 wt. %, the stiffness increased by 10% compared to pristine PET. In addition to improvements to the mechanical properties, graphene can also enhance the electrical properties of PET. According to Zhang et al., owing to graphene's large surface area, a high electrical conductivity of 2.11 S/m can be achieved by an addition of 3 vol % of graphene. Li et al. found that graphene can also improve themial degradation temperatures of PET nanocomposites, compared to pure PET, nanocomposites at 7 wt. % showed a thermo-oxidative degradation temperature 32° C. higher for 30% weight loss. Due to the differences in surface energies of PET and graphene, graphene tends to agglomerate, which negatively impacts the properties of the nanocomposite. To avoid the agglomeration of graphene sheets, functionalizing the graphene's surface chemically helps to reduce the surface energy. However, the addition and removal of the functionalized group adds complexity to the development of nanocomposites.
The orientation of the graphene inside the matrix can influence the electrical, mechanical, and thermal properties and controlling it is a challenge. According to Vaia et al. and Wang et al., a random distribution of nanofiller inside the matrix provides less enhancement in the matrix compared to aligned distribution.
Several researchers have evaluated the properties of PET-based nanocomposites using different types of nanofillers. Graphene-based materials have attracted significant research interest because of their ability to increase electrical conductivity and stiffness in polymers. Melt compounding is the most studied technique for the preparation of PET nanocomposites. It can be used to incorporate graphene into a PET matrix, resulting in a nanocomposite with improved mechanical, thermal and electrical properties. Unfortunately, it provides limited control over the characteristics of the distribution of the nanofiller in the resulting composite. The high temperature used in melt compounding, which liquefies the polymer phase, increases the intercalation of graphene in PET. However, at high loadings of graphene, the viscosity of the melt increases too much before achieving the intended concentration of graphene. This leads to difficulty in mixing graphene powder uniformly into the melt. Achieving a uniform distribution of graphene in PET is the first obstacle faced in the development of graphene-based polymer nanocomposites. As such, more research efforts are needed to undertake a new method to disperse graphene in PET and to better understand the conditions and optimal parameters involved in the process to improve the level of the distribution of graphene.
What is needed, therefore, is an effective and reliable process whereby graphene nanoplatelets may be uniformly dispersed in PET so as to provide reinforced bulk PET, and micromechanical models whereby the material properties of reinforced bulk PET may be predicted.
SUMMARYA composition and a method are provided for graphene reinforced polyethylene terephthalate (PET). Graphene nanoplatelets comprising a suitable surface area are added to a dispersion medium for producing graphene reinforced PET. The average surface area may range between substantially 15 m2/g and 750 m2/g. In some embodiments, the dispersion medium may be comprised of ethylene glycol. The dispersion medium and graphene nanoplatelets are sonicated to disperse the nanoplatelets within the dispersion medium. The dispersion medium and graphene nanoplatelets are centrifuged to remove larger nanoplatelets that are not suitably dispersed within the dispersion medium. A supernatant solution of dispersed graphene nanoplatelets and dispersion medium is decanted and then used for polymerization of the graphene reinforced PET. The resultant graphene reinforced PET is comprised of a continuous matrix of PET with a reinforcement material comprising dispersed phase graphene nanoplatelets.
Polymer nanocomposites are multi-phase materials comprised of a polymer matrix and a reinforcement nanofiller. Graphene is one of the most promising nanofillers with a unique combination of properties. To achieve the maximum enhancement in the properties of nanocomposites, graphene must be well-incorporated within the polymer matrix. In the present research, poly(ethylene terephthalate) (PET) and graphene nanoplatelets (GNPs) were used to fabricate PET-GNP nanocomposites through melt compounding, in-situ polymerization, and dispersion dosing.
Three methods are provided in the present disclosure whereby GNPs may be dispersed in PET. The first method involves melt compounding of a mixture of GNPs with PET pellets and powders. This method was investigated to evaluate the improvements in mechanical and thermal properties of PET. We hypothesize that dispersion of GNPs in a liquid medium, compatible with PET chemistry, can be used to achieve a more uniform distribution of GNPs in the PET matrix. We tested this in two methods: in-situ polymerization and dispersion dosing. In the in-situ polymerization method, GNPs were first dispersed and exfoliated in EG, and the dispersions were used for the development of the PET nanocomposites through in-situ polymerization. Introducing the EG-GNP dispersions, with a sufficient fraction of exfoliated GNPs, to the polymerization reactions creates well-incorporated PET-GNP nanocomposites. In the dispersion dosing method, the GNPs were dispersed in PEG, a dispersion medium with a higher viscosity than EG, and the dispersions were used for the development of the PET nanocomposites through PEG-GNP dispersion dosing via injection molding based on the following hypothesis: The higher viscosity of PEG leads to slower sedimentation of the dispersed GNPs, resulting in a higher concentration of dispersed GNPs in the medium. The addition of dispersions, with a higher concentration of highly exfoliated, few- to monolayer-graphene, to the PET melt creates PET-GNP nanocomposites with a more uniform incorporation of GNPs into the PET matrix, resulting in improved thermal and mechanical properties.
Experimental designs are disclosed whereby the level of distribution of graphene in the matrix may be evaluated as well as the enhancements in the nanocomposites' properties as follows:
-
- 1. Fabrication of nanocomposites through melt compounding PET with GNPs:
- Evaluation of GNP surface area and mixing methods; and characterization of nanocomposites through the addition of GNPs.
- 2. Fabrication of nanocomposites through in-situ polymerization:
- Evaluation of the EG-GNP dispersions for their concentration, size distribution, and stability; and characterization of enhanced PET prepared by introducing the EG-GNP dispersions to the polymerization reactions.
- 3. Fabrication of PET-GNP nanocomposites through injection molding:
- Evaluation of the PEG-GNP dispersions for their concentration, size distribution, and stability; and characterization of enhanced PET prepared by injection molding via PEG-GNP dispersion method.
- 1. Fabrication of nanocomposites through melt compounding PET with GNPs:
GNPs were melt-compounded with both PET pellets and PET powders to create the nanocomposites. At 20 wt. % GNPs, the elastic modulus of PET powders and pellets improved by 182% and 101%, respectively and the tensile strength of PET powders and pellets improved by 35% and 14%, respectively. Confocal microscopy showed that the GNPs inside the PET-GNP nanocomposites, prepared by PET pellets, agglomerated to a degree much greater than PET powders.
With the goal of achieving a more uniform distribution of GNPs in the PET matrix, ultrasonic exfoliation method was employed to disperse the GNPs in ethylene glycol (EG) and poly(ethylene glycol) (PEG). Multiple characterization techniques confirmed the exfoliation and estimated the number of GNP layers dispersed in EG was 5 to 10 layers. GNP dispersions in EG and PEG were used as precursors to develop the PET-GNP nanocomposites through in-situ polymerization and dispersion dosing via injection molding, respectively. The effectiveness of GNPs by weight (c) in the nanocomposite was evaluated by the improvement in elastic modulus. The ε for the in-situ polymerized nanocomposite at 2 wt. % was estimated to be 21±7, more significant than that for the melt-compounded one at the same concentration (ε=3±4). Interestingly, the ε for the dispersion-dosed nanocomposite at 0.006 wt. % was estimated to be 1000±600, much more significant than that for the melt-compounded one at 2 wt. %, with the same improvement in elastic modulus. A review of sampled literature on PET nanocomposite elastic modulus improvement indicates that the effectiveness of GNPs obtained by dispersion dosing is significantly greater. Thus, the early promise of outstanding mechanical reinforcement by graphene in a polymer has been demonstrated.
In an exemplary embodiment, a polymer nanocomposite comprises: a matrix comprising polyethylene terephthalate; and a reinforcement material comprising dispersed phase graphene nanoplatelets. In another exemplary embodiment, the graphene nanoplatelets comprise a surface area of at least about 15 m2/g. In another exemplary embodiment, the graphene nanoplatelets comprise an average thickness ranging between about 10 nanometers (nm) and 20 nm. In another exemplary embodiment, the graphene nanoplatelets comprise a surface area ranging between about 120 m2/g and 150 m2/g. In another exemplary embodiment, the graphene nanoplatelets comprise an average thickness ranging between about 6 nm and 8 nm. In another exemplary embodiment, the graphene nanoplatelets comprise a surface area ranging between about 300 m2/g and 750 m2/g. In another exemplary embodiment, the graphene nanoplatelets comprise an average thickness ranging between about 2 nm and 3 nm.
In an exemplary embodiment, a method for preparing graphene reinforced polyethylene terephthalate (PET) comprises: obtaining graphene nanoplatelets comprising a suitable surface area; adding the graphene nanoplatelets to a dispersion medium suitable for producing PET; sonicating the dispersion medium and graphene nanoplatelets so as to cause a homogeneous dispersion of the graphene nanoplatelets within the dispersion medium; centrifuging the dispersion medium and graphene nanoplatelets to remove a portion of larger graphene nanoplatelets that are not suitably dispersed within the dispersion medium; decanting a supernatant solution of graphene nanoplatelets dispersed in the dispersion medium; and using the supernatant solution for polymerization of the graphene reinforced PET.
In another exemplary embodiment, the graphene nanoplatelets comprise a surface area of at least about 15 m2/g. In another exemplary embodiment, the graphene nanoplatelets comprise a surface area ranging between about 120 m2/g and 150 m2/g. In another exemplary embodiment, the graphene nanoplatelets comprise a surface area ranging between about 300 m2/g and 750 m2/g.
In another exemplary embodiment, sonicating comprises immersing the solvent and graphene nanoplatelets in a bath sonicator for a period of time and operating the bath sonicator at a frequency suitable for dispersing the graphene nanoplatelets within the solvent. In another exemplary embodiment, sonicating comprises selecting the period of time so as desirably reduce an average length and width of the graphene nanoplatelets. In another exemplary embodiment, the frequency is a ultrasonic and the period of time ranges between at least 30 minutes and 180 minutes. In another exemplary embodiment, centrifuging comprises subjecting the solvent and graphene nanoplatelets to a rotational speed of centrifugation ranging between at least 1400 RPM and 7200 RPM.
In another exemplary embodiment, adding further comprises selecting polyethylene glycol as the dispersion medium suitable for producing the graphene reinforced PET. In another exemplary embodiment, selecting polyethylene glycol comprises selecting any one of PEG-300, PEG-400, and PEG-600 as the dispersion medium. In another exemplary embodiment, adding further comprises selecting ethylene glycol as the dispersion medium suitable for producing the graphene reinforced PET. In another exemplary embodiment, using the supernatant solution for polymerization further comprises performing an esterification reaction to produce bis(2-hydroxyl ethyl) terephthalate (BHET) with water as a by-product, followed by performing a polycondensation reaction so as to produce the graphene reinforced PET. In another exemplary embodiment, performing the polycondensation reaction further comprises including one or more catalysts comprising any one or more of Antimony (Sb), Cobalt (Co), and Phosphoric Acid.
The drawings refer to embodiments of the present disclosure in which:
While the present disclosure is subject to various modifications and alternative forms, specific embodiments thereof have been shown by way of example in the drawings and will herein be described in detail. The invention should be understood to not be limited to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the present disclosure.
DETAILED DESCRIPTIONIn the following description, numerous specific details are set forth in order to provide a thorough understanding of the present disclosure. It will be apparent, however, to one of ordinary skill in the art that the invention disclosed herein may be practiced without these specific details. In other instances, specific numeric references such as “first phase,” may be made. However, the specific numeric reference should not be interpreted as a literal sequential order but rather interpreted that the “first phase” is different than a “second phase.” Thus, the specific details set forth are merely exemplary. The specific details may be varied from and still be contemplated to be within the spirit and scope of the present disclosure. The term “coupled” is defined as meaning connected either directly to the component or indirectly to the component through another component. Further, as used herein, the terms “about,” “approximately,” or “substantially” for any numerical values or ranges indicate a suitable dimensional tolerance that allows the part or collection of components to function for its intended purpose as described herein.
As is known in the art, some nanofillers enhance the properties of the polymer matrix, owing to their high aspect ratio. Nanofillers can be classified as either structural or functional. Lightweight materials with high elastic modulus and tensile strength are called structural nanofillers, while nanofillers with other properties such as electrical and thermal conductivity are called functional nanofillers. Nanofillers used in the development of nanocomposites can also be classified into zero-dimensional (i.e. spherical particulates), one-dimensional (i.e. fibers, rods, and nanotubes), and two-dimensional (i.e. layered-platelet) structures.
Nanoparticles (zero-dimensional) are defined as particulate structures with a dimension in the range of 1 to 100 nm. Metal (Fe, Au, and Ag) and metal oxide (ZnO, CaCO3, and TiO2) particles have been employed in nanocomposites. Zhang et al. found that the tensile strength and elastic modulus of high-impact polystyrene (HIPS) can be increased significantly by the addition of TiO2 as low as 2%. In another investigation, researchers reported a 50% increase in toughness by only adding 5% (vol. %) of SiO2 in polymethylmethacrylate (PMMA) matrix. Nanoparticles also have applications in biomedical engineering. Various biodegradable polymers have been utilized in the formation of nanocomposites. While the major goals in designing nanoparticles are controlling the nanoparticles' size and properties, they can be used as potential drug delivery devices, increasing the stability of the drugs. However, some nanoparticles are known to present a toxicity risk.
Carbon nanotubes (CNTs), are allotropes of carbon with exceptional properties that have already proven valuable for several applications in industries including electronics, optics, and nanotechnology engineering. CNTs possess a high thermal conductivity of 6000 W/(m·K). The superior mechanical properties of CNTs, Young's modulus and tensile strength in the range of 0.2-0.9 TPa and 11-63 GPa, respectively, offer exciting opportunities for the development of nanocomposites. Coleman et al., investigated the addition of nanotubes in two different case studies. They reported an increase of 370% in elastic modulus, 430% in tensile strength, and 170% in toughness when added to polyvinyl alcohol (PVA) at less than 1 wt. %, and in polypropylene (PP), the addition of CNTs at equivalent loadings, resulted in an increase of 310%, 390%, and 440% in modulus, strength, and toughness, respectively.
To date, the main challenges for CNTs are to improve the dispersion and alignment in the polymer matrix when processing the nanocomposites. Analyses of these nanocomposites show that the performance of the final product is dependent on the types of CNTs (single-walled carbon nanotubes (SWNTs) or multi-walled carbon nanotubes (MWNTs)), their morphology and structure (length and chirality), and processing method. Functionalization of CNTs allows to achieve a good dispersion in the polymer matrix, therefore significant mechanical gain, as shown by Coleman et al. Nevertheless, the expensive cost to use the synthesis techniques for making CNTs remain a significant challenge. According to Breuer et al., high quality/purity CNTs currently cost $800/g, significantly higher than what has been reported for graphene (see Table 2).
Nanostructures such as nanoplatelets or layered materials can be classified as two-dimensional (2D) nanofillers. Improvement in mechanical properties of nanocomposites have been observed when a 2D nanofiller is incorporated in the polymer.
Clays are naturally found as platelets and are stacked layers ranging from few- to thousands of individual layers that possess Young's modulus from 0.18 to 0.26 TPa. One layer of clay has a thickness of 1 nm with platelet widths being in the range of 100 to 200 nm. The majority of recent research has focused on nanocomposites based on layered materials such as silicate compounds and synthetic clay. Toyota Central Research & Development Co. Inc. fabricated the first successful nanocomposites (Nylon 6/Clay) in 1994. According to Yu et al., clays can be used to enhance the mechanical and physical properties of polymers due to their high aspect ratio and large surface area-to-volume ratio.
Although clay is one of the most commonly used nanofillers for creating nanocomposites, manufacturing of polymer nanocomposites with efficient mechanical use of the clay is challenging. Organic modification of the clay is generally needed to promote improved intercalation in the polymer matrix. Additionally, nanofillers like clay are often from natural sources such as montmorillonite, which contains ions or contaminants and influences the performance of the final product. Garcia et al. showed that silicate composites possess weak electrical and thermal conductivity. In the case of polymer nanocomposites, improving several properties simultaneously, without negative impact on any key property, can be achieved when the dispersion and the interfacial interaction between the nanofiller and the matrix are controlled. Gupta et al. reported on the challenges of clay-based nanocomposites. According to them, in many cases, the performance of the final product did not meet expectations regarding the improvement in useful properties. While it has been shown that the addition of clay could increase the stiffness of thermoplastics, for example, they found that the strength of the matrix would ultimately decrease.
Another type of 2D nanofiller that shows promise is graphite. Graphite is a crystalline allotrope of carbon. Graphite is chemically similar to CNTs and structurally analogous to layered silicates. When exfoliated into an individual layer, the sp2 bonded carbon layers are isolated and are referred to as a “graphene sheet”. Graphene is a planar, electrically conductive, elastic, crystalline allotrope of carbon that can be described as a one-atom-thick layer, arranged in a 2D, hexagonal pattern. Graphene has a very high strength-to-weight ratio, with a bond length of the C—C bond 0.14 nm and a thickness of a single graphene sheet 0.34 nm.
Carbon nanomaterials such as CNTs and graphene are advantageous over clay, due to their superior mechanical, thermal, and electrical properties. Recent research shows that graphene is even more advantageous and likely to be used as alternative nanofiller to CNTs in the production of polymer nanocomposites. As stated earlier, graphene offers enhanced mechanical properties over CNTs. This is due to the planar structure and the aspect ratio provided during the nanocomposite processing. The current research progress on graphene has helped finding potential applications for graphene-based nanocomposites. However, like the other nanofillers, the properties of graphene-polymer nanocomposites depend on the extend of distribution of graphene in the polymer matrix.
Graphene can be produced in a form called graphene nanoplatelets (GNPs). GNPs are nanoparticles in stacks of small graphene sheets between 5-50 layers thick. GNPs, with wide aspect ratio, represent a new class of graphene. The platelet shape of GNPs results in a relatively higher number of carbon edges per unit volume, making them easier to chemically bond and change the fundamental properties of the polymer matrix. At small loadings, they can create electrically and thermally conductive materials. According to Wu et al., using GNPs can improve the electrical conductivity of thin film as high as 2,200 S/cm, significantly higher than that formed by other carbon-based materials, (i.e. CNTs).
Dr. Lawrence T. Drzal, from Michigan State University, has shown that GNPs are potential candidates to improving barrier properties, modulus, and surface toughness, after being incorporated into a polymer matrix. More recently, Dr. Bor Jang, from Wright State University, investigated developing GNPs suitable for applications such as conductive composites, heat radiation, conductive inks, and rubber. Table 2 summarizes the specifications of the investigated GNPs used in the current research.
To incorporate graphene into composites using dispersions or in-situ polymerization it is necessary for the graphene to be dispersed in a liquid medium. Though certain specific criteria must be met to produce a graphene dispersion suitable for a particular application, exfoliation of graphene in various liquid media has been widely studied. Exfoliation can be useful for obtaining monolayer graphene that is considered the most desirable structure of graphene for many research areas. Sonication is a process of agitating particles in a liquid medium using high-intensity sound waves with frequencies above 20 kHz. Sonicators either produce the ultrasonic waves from the outside of a container into a water bath, wherein samples are submerged (called bath sonicators) or can be propagated down a probe that is immersed directly into the sample (known as probe sonicators). During sonication, the ultrasonic waves radiate through the medium with rapidly alternating low and high pressures resulting in cavitation. In the low-pressure stage, millions of micro-bubbles form and grow. The following high-pressure stage collapses the bubbles and releases a large amount of energy. To calculate the power density, the power delivered to the convertor with the probe in air (not immersed in the sample) can be recorded. Without changing the amplitude, the probe should be immersed into the sample and the amount of delivered power can be again recorded. The difference between power readings is divided by the area of the probe to calculate the power that is being delivered to the sample (power density) using the following equation:
where P is the power density (Watts/cm2), P2 is the power when probe is immersed (Watts), P1 is the power when probe is in air (Watts), and r is the radious of probe tip (cm). Using the power density, the total input energy delivered during sonication can be calculated using the following equation:
E=P×t (2)
Where E is the energy density released to the sample during sonication (J/cm2), P is power density (Watts/cm2), and t is time (s).
In probe sonication, the generator transforms AC power to a 20 kHz signal that drives a converter. In the converter, the signal is converted to a mechanical vibration, which is then amplified and transmitted through the probe's tip which is immersed in the sample. The measurement of the tip's excursion is referred to as amplitude and can be set manually during sonication. Amplitude is an important parameter in probe sonication. Operation at low or high amplitude will deliver low and high intensity, respectively. While bath sonication provides a weak sonication, with approximately 25 Watts of output power, probe sonication provides a higher output, resulting in a uniform ultrasonic transmittance and cavitation. Due to the uniform cavitation in probe sonication, the effectiveness of the sonication process is much higher, offering a potential application in dispersing nanomaterials in liquids.
In the present research, both probe and bath sonication methods were used to create the graphene dispersions in liquids. The energy released from ultrasonic cavitation separates the graphene sheets from the multi-layer graphene. To obtain a homogeneous dispersion of few- to monolayer-graphene, the sonicated dispersion is then centrifuged. Centrifugation separates the heavier and unexfoliated multi-layer graphene, from the lighter and exfoliated few- to single-layer graphene. This results in a stable dispersion containing few- to single-layer graphene.
Though sonication is an effective technique to disperse graphene into a solution, there are several challenges associated with the process. The radiation of ultrasonic waves in bath sonication is unevenly distributed through the tank, causing an uneven sonication effect. Due to the low power density of bath sonication, the scalability of the process is very poor. In probe sonication, however, ultrasonic processing causes the solution's temperature to elevate quickly, resulting in reduced cavitation and efficiency of the process. It is important to keep the temperature as cold as possible to improve the effectiveness. Furthermore, the effectiveness of the sonication is affected by the viscosity of the solutions. Higher viscosity results in more efficient sonication because of more efficient energy transfer from the probe to the sample, as less energy is lost to free-flowing motion of the liquid, but at the same time the higher viscosity slows the dispersion of the exfoliated platelets into the surrounding dispersion medium.
Many organic compounds have a polar hydroxyl group and a non-polar hydrocarbon chain. When placed in water, these compounds form aggregates and try to minimize the contact between the non-polar hydrocarbon and the polar water molecules. Van der Waals interactions are responsible for the solubility of the organic molecules. When the hydrocarbon portion is small, the polar hydroxyl portion is responsible for the weak Van der Waals interaction, which facilitates solubility in water. However, as the hydrocarbon's length increases, the non-polar portion dominates, affecting the interactions by reducing solubility in water. When they are large enough, they tend to aggregate, resulting in their agglomeration. This phenomenon is referred to as the hydrophobic effect. Graphene is non-polar and exhibits hydrophobicity, and thus does not interact strongly with polar solvents like water.
Creating a stable/uniform dispersion of graphene with ultrasonic exfoliation relies on using a dispersion medium whose surface energy is comparable to that of graphene. According to Hildebrand theory, materials with similar surface energies are likely to interact well and be miscible. Surface energy can be correlated with enthalpy of mixing using the Hildebrand solubility parameter, δ, from following equation:
where ΔHmix is enthalpy of mixing per unit volume (mJ/m3), Vmix is the volume of mixture, Make is the thickness of graphene flake, ϕ is volume fraction of graphene, and δi is square root of the surface energy of phase i (δi=√{square root over (Esurface energyi)})((mJ/m2).
Exfoliation happens when the energetic penalty between the medium and graphene is minimized. For multi-layer graphene sheets, surface energy can be defined as the energy per unit area required to overcome the Van der Waals forces, when peeling two sheets apart. To overcome the Van der Waals forces between graphene sheets (˜61 meV per C atom), we would, in fact, need an energy input of over 2 eV/nme. As seen from Eq. (3), a good exfoliation of graphene in a dispersion medium suggests the enthalpy of mixing to be close to zero. This suggests that liquid media with surface energies matching that of graphene would lead to more exfoliated dispersions than others. In addition to surface energy, surface tension has also been used to better understand the interaction between a solvent and graphene and the wettability of graphene from a thermodynamics viewpoint. According to Lyklema, surface tension can be calculated using the value of surface energy of the materials using the following equation:
γ=ESurSol−TSSurSol (4)
where γ is the surface tension (mJ/m2), ESurSol is the solvent surface energy (mJ/m2), T is the temperature (K), and SSurSol is the solvent surface entropy (mJ/(m2K)).
Adamson et al. reported that the wetting or spreading of water can happen when the spreading coefficient is positive by utilizing the following equation:
Sw/g=γg−γw−γgw>0 (5)
where Sw/g is the spreading coefficient (mN/m), γg is the surface tension of graphene (mN/m), γw is the surface tension of liquid water (mN/m), and γgw is the interfacial energy of the water/graphene interface (mN/m).
A negative spreading coefficient reflects the hydrophobicity of a material. The surface tension of water at 25° C. is about 72.8 mN/m whereas the surface energy of graphene is estimated as 46.7 mN/m. The interfacial energy has been estimated to be around 90.5 mN/m, suggesting the spreading coefficient to be negative and confirming the hydrophobicity of graphene.
There are two groups of dispersion media that can be used to disperse graphene. The first group of dispersion media are those with high surface energy. For these, the surface energy is usually close to that of graphene, which helps disperse graphene without the use of any stabilizing agents. Coleman et al. have published several studies on using sonication and centrifugation methods to disperse graphene in a wide range of dispersion media including non-polar solvents such as dimethylformamide (DMF), and n-methyl-2-pyrrolidone (NMP). Graphene can be exfoliated in these compounds due to their high surface energy, and their strong interaction with C—C bonds in graphene. As mentioned earlier, graphene is non-polar and it does interact well with non-polar solvents. Though non-polar solvents are more likely better media to achieve a graphene dispersion, many of them, (e.g. NMP), are expensive and highly toxic. Moreover, the final concentration may not be high enough for many industrial applications. In the studies by Hernandez et al., graphene was dispersed at a low concentration of 0.01 mg/mL.
The other group of dispersion media are those with low surface energy such as isopropyl alcohol (IPA) and water. Due to the hydrophobicity of graphene, these media are usually combined with stabilizing agents, (i.e. surfactants). Surfactants refer to a class of molecules that tend to adsorb onto a molecule to lower the surface tension between the molecule and the dispersion medium. To understand the effects of surfactants in graphene dispersions, we must consider the structure of these molecules. A surfactant is comprised of two regions. The first region is known as the hydrophobic tail, whereas the latter one is known as the hydrophilic head. Stabilizing the graphene dispersions with surfactants involves an interaction between the hydrophobic tails of surfactants with graphene, while the hydrophilic regions are attracted to water molecules. According to Green et al., stabilizing graphene with surfactants can increase the degree of exfoliation in aqueous dispersions up to 60% while the concentration of graphene is estimated around 0.012 mg/mL.
Until now, researchers have investigated using the following surfactants: sodium dodecyl sulfate (SDS), sodium dodecylbenzenesulfonate (SDBS), cetyltrimethyl ammoniumbromide (CTAB), sodium taurodeoxycholate (TDOC), sodium deoxycholate (DOC), Tween80, Tween85, and TritonX100. A schematic representing the addition of surfactants to graphene dispersions is illustrated in
Graphene dispersions in an appropriate medium can be incorporated into polymer matrices through in-situ polymerization. Depending on the chemical structure of the host polymer, different media can be selected to create a graphene dispersion. A list of research reported on in-situ polymerization for the development of nanocomposites using graphene-based materials with different polymer matrices is summarized in Table 4. In an ideal situation, graphene would be uniformly incorporated into the polymer matrix. However, depending on the polymer molecule's chain structure, graphene may or may not affect the properties of the nanocomposite. For example, in the studies reported in polymerization of PMMA-based nanocomposites, while Jang et al. showed that graphene, due to its high surface area, can increase the glass transition temperature of the matrix, Liao et al. did not observe an increase in the glass transition temperature. To explain this behavior, the interactions between polymer chains and incorporated graphene sheets needs further investigation.
One published method uses graphene dispersions prepared primarily using non-polar solvents. The non-polar solvents typically have high boiling points, leading to difficulties in both removal of the solvent during composite preparation, and the formation of aggregations of graphene during solvent evaporation. Functionalization can improve the dispersibility of graphene. Functionalization can be divided into non-covalent (e.g. π-π interactions and surfactants) and covalent functionalization (e.g. graphene oxide (GO) and reduced graphene oxide (rGO). Using surfactants is the most promising route to improve the dispersion of graphene in a polar solvent. However, surfactants can interfere with polymerization during the formation of polymer nanocomposites. The interaction between the surfactant molecules and the polymer matrix depends on the molecular structure of both components. The presence of the surfactant molecules in a polymeric matrix can detrimentally alter the properties of the polymer. Removing surfactant molecules before the incorporation into the polymer adds complexity to the process and increases the production cost of nanocomposites.
Based on the aforementioned findings, further investigation of dispersing graphene in a polar medium, without the aid of surfactants, is needed to incorporate them into a compatible polymer matrix and create nanocomposites with higher efficiency.
Embodiments herein utilize PET resin of a commercially available grade (Mw=84100 g/mol) from Leading Synthetics Australia (Oz-PET™ GG-2180) in the forms of pellets and powders. PET pellets (average pellet height and diameter of 3.10 mm and 2.10 mm, respectively) were ground into fine powders (average particle size of 0.8±0.1 mm) GNPs from XG Sciences and Nano Graphene Platelets from Angstron Materials (see Table 2) were obtained. As shown in
Herein, validating graphene dispersion in ethylene glycol (EG) and poly(ethylene glycol) (PEG) are disclosed, aiming to demonstrate how the dispersion medium affects the quality of graphene dispersion. EG (Mw=62.07 g/mol) was purchased from Sigma-Aldrich and Fisher Chemicals. PEG-300 (Mw=300 g/mol) and PEG-400 (Mw=400 g/mol) were obtained from Sigma-Aldrich. A high-viscosity-PEG, PEG-600, (Mw=600 g/mol) was purchased from the VWR and DOW Chemicals. Both PEG and EG are polar compounds due to the presence of a hydroxide group in their molecular structures. PEG possesses higher viscosity compared to EG. Table 5 summarizes the properties of EG, PEG-300, PEG-400, and PEG-600.
In the present disclosure, GNP-15, GNP-150, and GNP-750 (presented in Table 2), may be used to prepare GNP dispersions for various experimental studies. EG and PEG, with varied molecular weights, were also used as liquid media for dispersion production. Probe and bath sonication techniques were used in different studies to prepare the GNP dispersions. Water temperature increases during sonication over a prolonged period, causing considerable evaporation. This leads to a decreasing water level in the sonicator and an uneven distribution of energy to the samples. To overcome this problem, a water pipe and pump were installed in the tank to circulate water between the bath and a chilled water source to keep the temperature under 40° C.
For probe sonication, the sample beaker was placed in a temperature-controlled water bath (maintained between 50 to 60° C.) for the duration of sonication. After sonication, the sample was divided into two portions to then transfer to two plastic centrifuge tubes. Each centrifuge tube was filled with 30 mL of the sonicated dispersion pipetted from the middle of the beaker to avoid sediment. Then, centrifugation was performed at rotational speeds of 1500 and 4500 RPM (revolutions per minute) for 45 minutes. During the centrifugal acceleration, sedimentation of GNPs happens in response to the forces acting on them. The force exerted on GNPs in the centrifuge is traditionally named “relative centrifugal force”, G-Force (RCF), and is a simple function of the rotational speed and can be calculated using the following equation:
G-Force=1.12×R×(RPM/1000)2 (6)
where R is the radius of rotational radius in centimeters (cm), and RPM is rotational speeds measured in revolutions per minute. After centrifugation, the top 10 mL of the six supernatants was carefully pipetted and transferred for further use. Table 6 summarizes the GNP dispersions prepared by the probe and bath sonication techniques for various purposes. Table 7 summarizes the technical and experimental applications of the dispersions used in current research.
The absorption of transmitted light can be correlated with the amount of material that absorbs light using the Beer-Lambert (BL) Law:
A=αCL (7)
where A is absorbance of liquid, a is absorption coefficient mL/(mg·m), L is cell path length (m), and C is concentration of material (mg/mL). The BL law can be used to measure the concentration of exfoliated graphene dispersed in solvents examined with spectrophotometry analysis. The concentration of material remaining after centrifuge can be evaluated by measuring the optical absorbance and can be correlated to the concentration of graphene after centrifuge (CG) using BL once the absorption coefficient is known. While the concentration of graphene depends on several factors including flake size and thickness, it is important to emphasize that BL law is only valid for dispersions with a relatively low concentration. The BL law is not obeyed when a highly-concentrated dispersion is present. Scattering, on the other hand, is another important factor that should be absent throughout spectrophotometry analysis.
To find the absorption coefficient (α) of a graphene dispersion, a series of dispersion samples were prepared using varied processing parameters, including sonication times and centrifugal forces. With a subsequent decanting, 10 mL of the supernatant of each sample was filtered through a porous (0.2 μm) Alumina filter membrane using a vacuum-assisted system (see
In this work, all samples were analyzed using a VIS-IR spectrophotometer with a cell path length of 10 mm in a cuvette. The absorbance values of samples in this study were measured at λ=660 nm. According to several studies, the absorbance of exfoliated graphene dispersion can be measured at this particular wavelength. Using this particular wavelength is useful to define the concentration of graphene in the solution when scattering is absent. Due to the low volume of the cuvette, a small quantity of GNPs might attach to the side of the cuvette while emptying between tests. To clean the cell after use, before each test was performed, the cell was rinsed off five times with distilled water and dried out with compressed air flow for one minute.
In this study, Raman spectroscopy was carried out for five different locations on each sample at room temperature (see
To characterize the GNP dispersions, transmission electron microscopy (TEM) was performed at 200 kV and λ=0.0025 nm to capture bright field (BF) micrographs for all dispersion samples (see
During the analysis of the TEM micrographs, the GNPs very frequently appeared as small aggregates, instead of the expected distribution of few- to monoloayer GNPs. This might have been a result of heat treatment used for the TEM grid preparation. To avoid this issue, a cryogenic condition was used to investigate direct imaging of a frozen EG dispersion using Cryo-TEM. Cryo-TEM has been increasingly investigated in studying biological samples (e.g. cells, viruses, and biological assemblies) at molecular resolution. Cryo-TEM enables direct imaging of objects in solutions under cryogenic conditions. With an objective of imaging the GNPs, while dispersed in a dispersion medium, Cryo-TEM were employed to image a frozen EG dispersion sample.
An FEI Vitrobot, a plunge freezer with an environment-controlled chamber, was used on 4 μl of a dispersion sample to prepare the Cryo-TEM grid. The sample was put on a holey carbon grid and then it was blotted away with filter paper. The thickness of the sample, coated on the TEM grid, is important and needs to meet certain criteria to result in useful images. Therefore, extra care was undertaken during blotting the dispersion to leave the thinnest possible layer of your sample on the grid without drying out (i.e. 100 to 200 nm thick). If the sample is over blotted, there will not be enough material useful for imaging. If the sample is not blotted enough, there will be a thick layer of liquid, which blocks the electron beam.
While the humidity of the chamber was set around 80-100% to avoid drying out the grid, the grid was plunged into liquid ethane to freeze the sample in a vitreous state (i.e. no crystalline ice). The grid was then transferred into a liquid nitrogen chilled grid box, in which it could be stored indefinitely. To image the frozen sample, a specific Cryo-TEM holder that could maintain −170 to −180° C. in vacuum was used. A low-dose TEM image mode (10 electrons/square angstrom) was used to avoid causing excessive electron beam damage to the sample or the frozen solvent. During the plunge freezing, it was observed that the viscosity of the dispersion medium can make the process challenging, resulting in a thick layer of sample. Cryo-TEM analysis was not conducted on PEG dispersions as the viscosity of the PEG was above the range that could be used for plunge freezing procedure. Although Cryo-TEM was useful to collect images, the use of this technique was discontinued due to technical difficulties.
The PEG dispersions were evaluated for GNP size distribution using laser diffraction. The samples for size measurements were divided into two sets based on the viscosity of the dispersion media. The as-received GNP powders were used as a reference for measurements. The Hydro MV and Aero S accessories were used to analyze the wet dispersions and the GNPs powder, respectively. For wet analysis, a few drops of dispersion were added to the Hydro MV tank until a sizable obscuration was obtained. A high disperser pressure, 4 bar, was used to complete the dry analysis. A general refractive index of 1.58/1 was used for the analyses. The dispersion samples were prepared using the GNP-15 and PEG-300 and PEG-600, at a concentration of 5 mg/mL. Table 8 summarizes the samples with the process parameters used for testing. The particle size distribution was calculated based on the Mie theory of light scattering. Based on this theory, three percentile values, which include Dx10, Dx50, and Dx90, are selected to define the volume-weighted distribution of the population.
To evaluate the effect of surface area of the GNPs on the properties of the nanocomposites, GNPs with three different surface areas were selected to make nanocomposites. The GNPs were mixed with PET pellets using two different mixing approaches: dry powder mixing and solution evaporation methods, were tested with the objective of maximizing the distribution of GNPs in PET.
A solution evaporation approach was used with the intention of creating an incorporated mixture at a lower concentration of GNPs. To do that, an aqueous dispersion of GNPs was prepared at a concentration of 0.1 mg/mL (0.001 wt. %). Five grams of PET resin was then mixed with the dispersion and placed in an oven at 200° C. for two hours to help evaporate the water (see
With the barrel temperature being set at 270° C., the screw speed at 100 RPM, and process time of 1 minute, nanocomposite samples were prepared and were divided into two different groups depending upon the approach that had been selected to mix the GNPs with PET resin. A double cavity mold with a dogbone shape was used to make the tensile bars based on the ASTM D 638 standard, type I specification. Using a micro-compounder and micro-injection molder, nanocomposite tensile bars were fabricated. Nanocomposite tensile bars prepared at 2 wt. % are shown in
Furthermore, with an objective of increasing the surface area of the PET pellets, and improving the interactions between the GNPs sheets and the PET chains, PET pellets were ground into a fine powder using a Laboratory Mill (see
PET polymerization was attempted using a melt-polymerization unit, available at the polymer institute at the University of Toledo, equipped with an esterification (ES) reactor and a polycondensation (PC) reactor, each with a 3 L capacity.
The GNP-15 were selected to prepare the dispersions in EG. Bath sonication was utilized for 60 minutes to disperse the GNPs in EG immediately before it was introduced into the reactor. The amount of graphene needed to prepare the dispersions was calculated based on the desired graphene weight fraction in the theoretical yield of PET during the PC reaction, ˜1.384 kg, and it was dispersed in 0.672 kg of EG for each batch. With the EG/TPA molar ratio being set at 1.5, the dispersions were added to 1.2 kg of TPA to start with the ES reaction.
During the ES reaction, EG and water (a reaction by-product) evaporate at the high temperatures in the reactor and flow into the reflux column. As the temperature of the reaction increases, the temperature of the bottom portion of the reflux column increases. Water, due to its lower boiling temperature compared to EG, starts evaporating first. The vapor travels to the condenser to form liquid. Once the temperature of the top portion of the reflux column reaches 100° C., the reflux valve, located at the end of the condenser, opens. This valve can flow the produced water either into a flask or into the top portion of the reflux column. When water returns to the reflux column, the temperature of the top portion tends to stay cooler than other portions, creating a temperature gradient in the reflux column. The bottom portion of the reflux column stays hotter than the top portion of the column. Due to the temperature gradient inside the reflux column, EG vapor condenses as it reaches the top portion of the column and comes back to the reaction chamber. The esterification reaction takes place at a high temperature between 220 to 240° C. which produced bis(2-hydroxyl ethyl) terephthalate (BHET) with water as a by-product. The schematic shown in
Once a sufficient quantity of water was produced during the ES reaction (˜0.2 kg), the reaction was considered finished. The BHET monomers with GNPs and water were transferred to the PC reactor.
During the PC reaction, the intrinsic viscosity (I.V.) was monitored and recorded. The reaction was considered finished after achieving a desired I.V. (>0.60 dL/g) of the polymer melt. The polymer strands were collected from the bottom of the PC reactor on a winder, fast-cooled in an ice/water bath, and air-dried overnight to reduce the residue of water. Strands were copped for pelletizing. Pellets were vacuum-dried overnight at 120° C. The schematic shown in
I.V. is a measure of the polymer's molecular weight, and is correlated with the polymer's other properties (e.g. the melting point, crystallinity, and the tensile strength). Polymers with higher I.V. often exhibit greater tensile strength compared to those with lower I.V. As mentioned in the previous section, during the PC reaction the I.V. was monitored. With an objective of improving the I.V. of the polymer obtained after polymerization, solid state polymerization (SSP) was carried out. SSP was done at 220° C. to remove volatiles (e.g. air and water) from the polymer. An inert gas (N2) is purged to remove the by-products of the reactions (e.g. ethylene glycol and acetaldehyde). These by-products diffuse to the surface of the polymer and are carried away by the inert gas flow or vacuum. During the SSP the polymer chain lengths are increased, and as a result, the I.V. of the polymer improves. Depending on the desired improvements and the initial value of I.V., SSP can be carried out from 2 to 8 hours (the higher the initial I.V., the shorter the SSP and vice versa). To evaluate the I.V. of the material, and study the effects of SSP on I.V., melt viscosities were measured. A small quantity of the material before and after SSP was taken and was vacuum dried at 110° C. for 1 day. The measurements were carried out at 270° C. and 15% strain using a parallel plate dynamic analyzer. The gap between the plates (diameter: 25 mm) was set at 1.2 mm. Using a calibration curve, the I.V. value of complex viscosity at 1 rad/s is used to determine the I.V.
Including a control batch to synthesize PET, PET nanocomposite pellets were prepared by adding GNP dispersions at varied concentrations, summarized in Table 11, and processed using bath sonication for 60 minutes immediately before addition to the reactor. Additionally, a GNP dispersion, processed for 90 minutes and centrifuged at 260 RCF, was prepared using probe sonication, in 12 small batches (due to equipment size and volume constraints) approximately one week before use at a different facility. The small batches were mixed into one container before shipment to the facility with the polymerization reactors. There, the dispersion was bath sonicated for 10 minutes to re-disperse the GNPs immediately before introduction to the reactor. Table 11 summarizes the dispersion samples prepared for the polymerization experiments.
Using the experimental procedure, described hereinabove, the PET-GNP nanocomposite tensile bars were fabricated by melt compounding the PET-GNP nanocomposite pellets.
The PET and PET nanocomposite were fabricated using the PEG-GNP dispersions and masterbatch pellets to further understand and evaluate the effects of sonication on the properties of the final product.
With an objective of exfoliating and incorporating the GNPs into PET and creating well-incorporated PET-GNP nanocomposites, GNP-15, were first dispersed in PEG-600 through probe sonication. To study the effects of the addition of GNP dispersions on the properties of the nanocomposites, the GNP dispersions were added to PET melt using dosing equipment as the screw barrel is filled with new polymer. Desired dosing rates were employed for the dosing process to achieve known concentrations of GNPs in the PET nanocomposites. The details including the concentration of the dispersions, dosing rates, and the concentrations of the nanocomposites are summarized in Table 13.
In addition, the masterbatch pellets were diluted by PET pellets at known concentrations, and the solid-state mixtures were then used to fabricate the PET-GNP nanocomposites (Table 14).
The 90-ton injection molding machine, shown in
Furthermore, with an objective of understanding the effects of the addition of GNP dispersions and the dispersion medium on the PET's properties, several process parameters (e.g. sonication times, amplitudes, and centrifugal force) were undertaken to prepare the GNP dispersions in PEG-400 and PEG-600 for dosing experiments using a dosing equipment. The dispersions were added into PET at 1.5% dosing rate. Screw slippage occurred when the dosing rate of 2.5% was used. Table 15, Table 16, and Table 17 summarize the process parameters that were involved in each study.
Tensile testing was performed using an Instron universal testing machine equipped with a 30 kN load cell at a strain rate of 5 mm/min. A non-contact laser extensometer was used for recording strain. Based on the reflections from a self-reflective tape, the laser records the displacement to mark the gauge length during testing (
Distribution of the GNPs in PET was visualized using a light microscope at 20× and 40×. To prepare the samples for light microscopy, a microtomy method was used to cut small sections (1 mm×1 mm) with thickness of 850 nm and 1 μm. A glass knife was used to prepare the microtome sections. The thickness of the sections was verified with their color using a scale proposed by Peachey. To study the morphology of the samples, low magnification scanning electron microscopy (SEM) was performed. Samples for SEM testing were chosen from the fractured surface of the tensile bars, after mechanical testing, and were Au coated. An attempt was made to make thin sections of the sample for high resolution transmission electron microscopy (HR-TEM) testing.
X-Ray diffraction (XRD), a non-destructive analytical technique, is commonly used to evaluate the atomic structure of crystalline materials. GNPs exhibit “Graphene-2H” reflections corresponding to the (002) plane (26.54°2θ for CuKα X-rays). The triclinic crystal structure of PET can be observed with four principle reflections from the (010), (110), (100), and (105) planes (17.5°, 22.5°, 25.6°, and 42.6°2θ for CuKα X-rays). XRD analysis can also be informative to understand the effects of GNPs' content on the crystallinity of the nanocomposites. In this study, 2D diffraction frames were collected using a Bruker AXS Hi-Star 2D detector. CuKα radiation (λ=1.54184 Å) was used. Samples of PET and PET nanocomposites were prepared by cutting a cubic shape from the sections before and after mechanical testing of nanocomposites, and were fixed onto a Si single crystal substrate (zero background substrate) using Fomblin Perfluorinated grease for data collection in the reflection mode under a 60 sec scanning time.
Further, the general area diffraction detection system (GADDS) was used to investigate the crystallographic textures of the nanocomposite samples prepared by a dry mix of the GNPs with PET powders and pellets at 2 wt. % and 10 wt. %. To determine the orientation of the GNPs, 2D diffraction patterns were collected at fixed θ1 and θ2=12.5° by rotating the sample along the φ direction in steps of 5° at positions of −5° and 32° in χ direction. The 2D diffraction patterns were integrated along 2θ for every 1° in χ direction. The data are plotted as pole figures and presented plane for both the PET and PET nanocomposites in terms of contours of intensity of reflections from the (002) plane.
X-Ray computed tomography (X-ray μCT or MCT) is a non-destructive technique that offers 3D imaging of materials. It involves computed X-ray measurements to produce cross-sectional (tomographic) images of specific areas of a scanned sample. The X-rays can be transmitted through the specimen and can be correlated with the specimens' properties using the following equation:
I=I0e−μ
where I is the transmitted X-ray intensity, I0 is the initial X-ray intensity, μm is mass attenuation coefficient, ρ is density, and x is the material thickness. During tomography testing, the geometry information is collected and recorded as radiographs. The radiographs are then reconstructed into tomographs, which allows imaging inside the sample without cutting it. While X-ray tomography offers 3D imaging, resulting in a more effective analysis, sample preparation for optimal imaging adds difficulty to the process. For high resolution, samples larger than 2 mm×2 mm are best cut in thin squared sections. This minimizes artifact corrections needed to image larger samples.
With the objective of understanding the distribution of GNPs inside the PET matrix, MCT was performed. In this work, MCT was carried out on the PET nanocomposite sample prepared by mixing PET pellets with GNP-15 at a concentration of 2%. A bulk section of the sample (200 μm×200 μm×1000 μm) from the outer surface of the amorphous section of the sample was scanned on Zeiss Xradia 410 X-ray computed tomography system at 0.97 μm/pixel resolution. Radiographs were collected and the reconstructed tomographs were visualized using a 3D visualization software.
Differential scanning calorimetry (DSC) was carried out to understand the effects of GNPs on thermal properties of a sample with the weight of 8 to 10 mg. Samples were taken from both amorphous and stretch sections of each nanocomposite tensile bar used for XRD measurements (
where Xc is percent crystallinity, ΔHf is the heat of fusion (J/g), ΔHcc is the heat of cold-crystallization (J/g), and ΔH°c is the heat of fusion for 100% crystalline polymer, 140.1 (J/g) for PET.
To describe the relationship between graphene concentration and color of the samples, PET and PET nanocomposite preforms were evaluated for their color using CIEL*a*b* scale.
To understand the effects of the GNPs on the properties of the nanocomposite, the nanocomposite tensile bars were produced to evaluate the effects of the surface area of the GNPs and the effects of the mixing method of PET with GNPs on the properties of the final product.
Mechanical Properties
Comparison of the modulus of elasticity and tensile strength of nanocomposites with different surface areas of GNPs prepared by dry powder and solution evaporation methods is presented in
Thermal Properties
To study the effects of GNP surface area on thermal properties of the nanocomposite tensile bars, the mechanically-stretched samples were tested from the amorphous sections.
Distribution Analysis
To study the distribution of the GNPs inside the PET matrix, also called dispersion analysis, samples were observed through SEM. When GNPs were loaded at 0.001 wt. %, the PET nanocomposites showed a fracture surface similar to pristine PET; a ragged edge which was caused by a uniform failure (see
Samples with 1 μm thickness were examined using confocal microscopy to study their internal structure. As shown in
XRD Analysis
To further study the crystallinity of the nanocomposites, XRD measurements were carried out.
While the XRD measurements were not useful for absolute crystallinity measurement, they provided additional information correlating to the area under the amorphous hump or broad peak from PET. The values for the area under these humps for each sample was correlated with PET's percent crystallinity obtained using the DSC measurements.
MCT Analysis
PET-GNP nanocomposites prepared through pellet mixing at 2 wt. % was analyzed by X-ray CT to characterize the level of distribution of GNPs.
Mechanical Properties
In the study of the effect of surface area of GNPs on the properties of PET, the GNP-15 exhibited a higher mechanical gain compared to other grades. To further study the effect of GNP-15 on nanocomposite properties, they were added to PET pellets and powders at different concentrations, as explained in section 3.4.1. As shown in
Thermal Properties
Further, to study the effects of GNP concentration and the preparation method on nanocomposite crystallinity, tensile bars, with different GNP concentrations prepared using PET powders and pellets, were examined through DSC measurements to evaluate thermal properties.
The crystallinity measured for the nanocomposites from injection molding prepared through pellet mixing shows a similar increasing trend compared to powder-mixed nanocomposites. Further investigation is needed to study the effects of GNPs at higher concentrations on the crystallinity of the PET. The non-isothermal crystallinity was also obtained through DSC. As shown in
Distribution Analysis
Samples with 850 nm thickness were examined by a confocal microscope to understand the effects of mixing method on the distribution of the GNPs inside the PET matrix.
XRD Analysis
Diffraction patterns were collected from PET and PET nanocomposite tensile bars.
To evaluate the orientation of the crystalline structure, pole figures for the (002) diffraction plane, representing the presence of graphene, were measured.
With an interest in incorporating the GNP dispersions into a PET monomer through in-situ polymerization, EG, one of the raw materials in polymerizing PET, was selected as the dispersion medium. The following sections summarize the preliminary results obtained by characterizing the GNP dispersions in EG.
Monolayer graphene can be identified from the bright field TEM micrographs because of their well-defined edges. Multi-layer graphene, however, can be identified from the larger objects, contiguous clumps extended over several grid openings, regularly observed in the original pre-sonication samples. TEM micrographs of the as-received GNP-15 and the dispersion samples sonicated for 90 and 180 minutes and centrifuged at 260 and 2350 RCF were taken and analyzed using binary filters.
To limit the effects of potential heat trauma from sample preparation for traditional TEM, we investigated the same type of samples from the previous section using Cryo-TEM.
According to Khan et al., Hernandez et al., and O'Neill et al. increasing the sonication time better separates the starting material into individual layers followed by a decrease in the size of the dispersed graphene. To investigate this, the lengths and widths of GNPs were collected from the TEM micrographs of all samples for more representative statistics. As shown in
To evaluate the concentration of the GNP dispersions using the optical absorbance technique, filtration testing was first examined to calculate the absorption coefficient of the samples. Table 19 summarizes the samples prepared with GNP-15 for the filtration tests. An average value of 2374 mL/(mg·m) was estimated by filtering 10 mL of the dispersions using the procedure reported in Table 20.
To study the effects of sonication time and centrifugal force on the concentration of the dispersions, a series of dispersion samples was prepared with varied sonication times and centrifugal forces. The concentration of the remaining GNPs after centrifugation can be estimated knowing the average value of absorption coefficient for graphene dispersions in EG. Table 21 and Table 22 summarize the concentration results for the dispersion samples prepared by probe and bath sonication techniques, respectively. The results here show that by increasing the centrifugal force from 260 to 2350 RCF, the concentration significantly drops.
Prior work demonstrates that the thickness of few-layer GNPs can be revealed in by the analysis of the Raman spectra. Latil et al. and Saito et al. reported on electronic structure and determination of number of layers by using the ratio of the 2D and G bands, I2D/IG. Ferrari et al. investigated the evolution of monolayer and few-layer graphene by Raman spectroscopy and compared their results with graphite. They reported that the 2D band possesses a unique line shape for single-layer graphene. As the number of graphene layers increases, the electronic band structure varies and approaches that of graphite. They add that the shape and the formation of sub-components under the 2D band can be used as a graphene “fingerprint” to estimate the number of graphene layers.
To better understand the stability of the dispersions and effects of sonication time on the stability of the dispersions, a series of dispersions were prepared in EG medium. To quantify the settling of GNPs over time, filtration tests were performed on 10 mL of the dispersions pipetted from the top surface layer of the dispersions, while the remaining samples remained intact, at different time points.
To further understand the effects of polymerization on the level of GNP distribution in PET and effects on properties, the in-situ polymerized pellets were produced through ES and PC reactions, as described herein, and were used to fabricate nanocomposite tensile bars through the melt compounding approach, as described herein.
The measurements of elastic modulus and tensile strength of the PET and PET nanocomposites are illustrated in
PET nanocomposites were also examined for their toughness. As shown in
PET nanocomposites, prepared at 0.004 wt. %, 0.1 wt. %, 0.5 wt. %, 1 wt. %, and 2 wt. %, were examined by SEM to analyze their microstructure after mechanical testing.
The nanocomposite samples with 1 μm thickness were also examined by a confocal microscope to understand the distribution of the GNPs inside the PET matrix.
Diffraction patterns were collected from the PET and the PET nanocomposite tensile bars.
With the intent of incorporating the GNPs into PET through dosing process of GNP dispersions, PEG-400 and PEG-600 were selected as the dispersion media. The following sections present the results obtained by characterizing the dispersions of GNP-15 in PEG-300 and PEG-600.
GNP dispersions in PEG were examined for evaluation of concentration of dispersed GNPs similarly to the previous procedure for the EG dispersions. Table 24 summarizes the sample preparation for the filtration tests. An average value of 1451 mL/(mg·m) was obtained based on the data reported in Table 25.
To study the effect of the viscosity of the dispersion medium on the concentration of the dispersed GNPs, PEG-300 was first selected to compare to EG. Concentrations of the sets of dispersions, after centrifugation, were calculated using the absorbance coefficients for EG and PEG-300 that were calculated through the filtration tests. The initial concentration was set at 0.25 mg/mL and the process parameters, (i.e. sonication times and centrifugal forces), were taken from the previous experiment to disperse GNP-15 in PEG-300. As shown in Table 26, using PEG resulted in higher values of the concentrations of dispersed GNPs. PEG resulted in higher values of the concentrations of dispersed GNPs.
Further, the GNP dispersions in PEG-300, prepared at higher initial concentrations, were examined to study the effects of the higher initial concentrations on the maximum achievable final concentration in the dispersion (Table 27). A quantitative analysis of the concentrations of the GNP dispersions in PEG-300 showed that increasing the initial concentration of the GNPs above 1 mg/mL would not affect the final concentration in the dispersion, suggesting a saturation limit.
Using a similar experimental procedure as with PEG-300 dispersions, PEG-600 was used to study the effects of higher viscosity on the final concentration of the dispersed GNPs. Table 28 summarizes the concentration values and a comparison between the PEG dispersions with different viscosities.
As shown in Table 28, the PEG-600 dispersion medium results in higher values of the dispersed GNPs. To study the effects of increasing the initial concentration on the final concentration of the dispersed GNPs, a set of three samples prepared at different concentrations, but processed using the same sonication time and the centrifugal force of 90 minutes and 260 RCF, respectively, were examined for concentration measurements. The results herein showed that by increasing the concentration to 5 mg/mL, the concentration of the dispersed GNPs increases to 1.17 mg/mL. This trend is reported in Table 29.
To study the effects of sonication and centrifugation and the viscosity of the dispersion media on the size of the dispersed GNPs, laser diffraction was performed. The volume-weighted particle size distributions collected from sample set I, PEG-300, are illustrated in
Similar to the EG dispersions, GNP dispersion in PEG-300 and PEG-600 were prepared and examined for stability. While the GNP dispersions in PEG-300, prepared at initial concentration of 5 mg/mL, did not change the stability of the dispersions, those prepared at initial concentration of 0.25 mg/mL showed a lower sedimentation rate compared to the dispersions in EG (
The measurements of Elastic modulus and the tensile strength of PET and PET nanocomposites are shown in
PET and the PET nanocomposites were evaluated for their crystallinity and thermal properties with respect to the GNPs concentration.
In order to evaluate the distribution of the GNPs in the PET matrix, confocal microscopy images were collected from the nanocomposite samples with 1 μm thickness.
To understand better the effects of ultrasonic exfoliation on the level of the distribution of GNPs, HR-TEM were utilized on samples prepared at 0.2 wt. % concentration of GNPs. As shown in
The PET nanocomposites were analyzed for their color using the CIEL*a*b* scale color analysis method, shown in
Based on data collected as discussed herein, it was found that the PET-GNP nanocomposites, fabricated through PEG-GNP dispersion dosing, outperform those that were prepared using masterbatch. To further understand the effects of the dispersion dosing method, the nanocomposite tensile preforms were produced by dosing GNP dispersions, prepared by varied process parameters. Individual studies were conducted on effects of centrifugation, concentration of dispersions, and different sonication times and amplitudes, employed during the dispersion preparation, on the final properties of PET-GNP nanocomposites.
Measurements of elastic modulus and tensile strength of PET, PEG, and PET nanocomposites prepared in concentration study (Table 16) are presented in
Crystallinity of PET, PEG, and PET nanocomposites prepared by the PEG-GNP dispersions dosing method was evaluated. Results are presented in
With an objective of understanding the effects of sonication energy on the properties of the nanocomposites, two different amplitude settings were used to prepare the GNP dispersions in PEG-400. Using a 19 mm probe, the P1 value of 5 Watts and P2 values of 70 Watts and 140 Watts were recorded for the amplitude of 50% and 100%, respectively. The energy densities was estimated using the Eqs. 1 and 2, disclosed hereinabove. Table 34 summarizes the energy densities calculated for different sonication times.
The luminosity measurements of PET nanocomposites prepared by PEG-GNP dispersions are shown in
Ultrasonic exfoliation is an effective method to exfoliate GNPs and to create few- to monolayer graphene in a dispersion medium. This conclusion is supported in two ways. First, it was observed, from TEM, that increasing the sonication time further exfoliates the as-received GNP and separates them from each other. This is reasonably attributed to exfoliation of the GNPs due to the released energy during sonication, and is independent of centrifugation. As shown in
Based on the concentration data collected for EG dispersions, samples centrifuged at 2350 RCF showed almost 80% loss in the quantity of the dispersed GNPs compared to 260 RCF. Increasing the centrifugal force better separates the larger GNPs, which were sonicated but not as completely exfoliated, from the as-received powder, increasing the relative frequency of monolayer graphene.
A dispersion of GNPs with a relatively higher concentration can be achieved at higher sonication times beyond 30 minutes at both 260 and 2350 RCF (Table 19 and Table 20). Even though the concentration of the dispersed GNPs significantly drops from 260 to 2350 RCF, increasing the G-Force better separates the thicker GNPs from thinner ones. The apparent plateau in concentration after 30 minutes of sonication may reflect a saturation level of GNPs in EG. It is important to note how other measurements indicate that an increase in sonication time decreases the average platelet size, indicating that longer-sonicated samples likely have a higher number of platelets per unit volume than the shorter-sonicated samples. This also suggests that sonication may be fracturing the GNPs into smaller platelets. Further investigation is needed to understand whether or not this behavior affects the final nanocomposites. For the GNP dispersions in EG, the concentrations that can be achieved by probe sonication are in the same range as with bath sonication. This appears to be an advantage of using probe sonication: achieving approximately the same quantity of dispersed GNPs with a significantly shorter amount of time.
To estimate the energy required to exfoliate the GNP-150 in an EG dispersion during sonication process with a 19 mm probe at 50% amplitude, the energy density was calculated for different process conditions (i.e. sonication time and G-Force). Using a 19 mm probe, the Pi value of 5 Watts and P2 value of 60 Watts were recorded for amplitude of 50%. Based on Eqs. 1 and 2, the power density and the energy density values were calculated. Using the average area of the dispersed GNPs, reported in Table 18, and the energy density values, the energy required to exfoliate a bilayer GNP was calculated for the corresponding sonication time and G-Force and reported as exfoliation energy. The exfoliation energy values were then compared to 8×1011 eV/cm2, the energy with which graphene sheets are bound, and the difference was reported as excess energy. Table 35 summarizes the comparison between the energy density, exfoliation energy, and the excess energy during sonication. As seen, this energy at each process condition is higher than what it is required to break a bilayer graphene sheet, supporting that exfoliation of GNPs occurred during the sonication process.
The stability analysis showed that the GNP dispersions in PEG-600 has a significantly lower sedimentation rate compared to the dispersions in EG and PEG-300. Even though increasing the starting concentrations of the dispersions in PEG-600 increases the sedimentation rate, the percent decrease in the concentration is smaller than EG and PEG-300 dispersions. This indicates that part of the GNPs remain dispersed over a period of two weeks (Table 33). Our preliminary studies for GNP dispersions in EG indicated that sedimentation happens over a period of four days. Due to the higher viscosity of PEG, it appears that the movement of the particles are significantly reduced, leading to a lower sedimentation rate. Our primary data showed that the maximum achievable concentration in GNP dispersions is directly related to the viscosity of the medium. In addition, higher viscosity is correlated with greater stability.
Performance Evaluation of PET-GNP NanocompositesMelt compounding is a promising method for the fabrication of nanocomposites due to low production cost. However, it has limitations in controlling the distribution of GNPs in PET, since flow of the GNPs is hindered by the viscosity of the molten PET. Based on the data collected from tensile bars, as described hereinabove, it was found that lower surface area GNPs leads to a greater improvement in elastic modulus of PET, suggesting that they provide a larger interface for more efficient interaction (i.e. more free edges per unit volume) with the polymer matrix. Moreover, it was found that mixing GNPs with PET powders lead to a more uniform distribution of GNPs in the matrix compared to the mixture with PET pellets, as described herein. This is attributed to a better interaction between the GNPs and PET powders, due to an increase in PET surface-area-to-volume ratio compared to PET pellets. The data here suggest that increasing the compounding time between the GNPs and PET pellets, could lead to better mixing of graphene in the melt. However, the longer mixing time results in increased PET thermal degradation. Future investigation is needed to explore alternative methods to improve the level of the distribution of dispersed GNPs in PET. One such future direction is futher reduction in the PET powder size.
Nawani et al. determined the orientation of a nanofiller in polymer nanocomposite films using an X-ray scattering method. According to them, for a system with some orientation the distribution of the nanofiller can be identified by a radial and an angular component, similar to what we have observed for the edge on view direction.
SEM micrographs, shown in
In order to be tough, a material must be both strong and ductile. Based on the data collected from mechanical testing, the PET nanocomposites showed improvments in tensile strength. However, fracture analysis did not consistently show ductility. The data showed that at low concentration of the GNPs, 2 wt. %, the structure of the stretch section in polymer demonstrates a ductile failure. As the GNPs concentration increases to 7.5 wt. %, the failure behavior changes, becoming predominantly brittle. This observation is consistent with an increasing void fraction at higher concentrations. The voids can act to prematurly fraction the composite. They also diminish the stifness of the composite, suggesting the stifness increase observed here is less than what would be possible for a fully dense composite. The improved material properties of the composites are however, already impressive. Haghnegandar et al., reported on the fracture analysis of polypropylene (PP)/ethylene propylene diene monomer (EPDM)/graphene nanocomposites using the Essential Work of Fracture (EWF) method. In that case, the multi-layer GNPs acted as stress concentration sites, facilitating crack initiation. Further investigation is required to confirm the abovementioned observation in our case of PET nancomposites. Therefore, future studies will include using the EWF method to investigate the deformation mechanism and fracture toughness behavior of PET nanocomposites with respect to the concentration of GNPs.
Based on the data collected from the PET-GNP nanocomposites that were prepared by dosing PEG-GNP dispersions, it was found that the addition of PEG dispersion medium increases the elastic modulus of the PET matrix. Both PEG-400 and PEG-600 liquid media increased the elastic modulus of PET by 9%. Increasing the concentration of dispersed GNPs in PEG media from 0.006 wt. % to 0.02 wt. %, however, had a negative impact on the mechanical properties and luminosity results. This is attributed to a poor distribution of the GNPs, caused by agglomeration of the GNPs in PEG medium, as described herein. The early studies suggest that an increase in the concentration of the GNPs in PEG dispersions, when only sonicated, can decrease the luminosity of the nanocomposites due to a high fraction of more light-absorbing unexfoliated GNPs. When centrifugation is employed, however, the fraction of light-absorbing unexfoliated GNPs lessens as the centrifugation speed increases. This results in an increased luminosity in the nanocomposites.
Based on the mechanical testing data reported herein, the PET-GNP nanocomposites at 0.0015 wt. % concentration of GNPs (experiment 2 in Table 11) increased the elastic modulus and the tensile strength of PET by 9% and 11%, respectively. More significant improvements were observed at 2 wt. % concentration of GNPs (experiment 8 in Table 11); the elastic modulus and the tensile strength improved by 22% and 10%, respectively. In experiments 3, 4, and 5, sonication for 60 minutes helped exfoliate a fraction of the GNPs. This led to a significant fraction of unexfoliated GNPs in the dispersions. Assuming that the energy density delivered to the samples, over the same volume and time, is the same, it is reasonable to expect that the resulting concentration of the exfoliated GNPs is a function of the starting concentration of unexfoliated GNPs. While the samples below 0.5 wt. % (experiments 3, 4, and 5) did not show a significant improvement in mechanical properties, at 0.5 wt. % (experiment 6) improvements in PET mechanical properties are apparent. As shown in
This is attributed to a sufficient concentration of exfoliated GNPs in the PET nanocomposites. Below 0.5 wt. % concentration of GNPs, sonication for 60 minutes is insufficient to exfoliate enough GNPs to affect mechanical properties. The data here suggest that an initial concentration of GNPs at 0.5 wt. % leads to a sufficient fraction of exfoliated GNPs in 60 minutes to improve the properties of PET. To understand the effects of process parameters involved in dispersion preparation on PET-GNP nanocomposites, a qualitative analysis on the GNP dispersions was performed. The precursors used for experiments 2 and 5 (Table 11) were selected and examined by TEM and analyzed using the binary filters to evaluate the degree of exfoliation of GNPs.
The primary difference between the two experiments is due to centrifugation. According to several studies, exfoliation of GNPs from the starting powder is achieved through sonication and is independent of the centrifugation. During centrifugation, however, the larger, or unexfoliated, GNPs separate from the exfoliated GNPs. This indicates that centrifugation is advantageous as it can lead to achieving a dispersion with a higher fraction of few- to monolayer graphene sheets, therefore, a better distribution of active graphene surface area in the final polymer composite. These results suggest the most powerful interaction happens at the nano-scale, when exfoliated GNPs are present in the dispersions. This is not surprising, but it is useful to observe such results. This nano-interaction is dependent on the composite production process successfully exfoliating graphene. Our results here show GNP dispersions as promising candidates for the development of graphene-based PET nanocomposites, at least through in-situ polymerization.
The thermal analysis of the PET-GNP nanocomposites showed that the addition of GNPs affected PET crystallization. Crystallization occurs in two major steps. Those include nucleation, in which a crystalline phase appears, and crystal growth, which is the increase in the size of the nucleate to form a crystal state. Based on DSC data collected from the tensile bars, it was found that the addition of GNPs affected the heat flow in PET and crystallization by possibly promoting more crystals in the matrix. This was also observed in the increase in crystallization temperature. This either suggests that GNPs can serve as nucleation sites or their high thermal conductivity has affected the heat flow in PET. Examining different quenching time during injection molding of PET nanocomposites, prepared at the same GNP concentration, would help determine the underlying mechanism. Additionally, the glass transition temperature decreased with increasing GNP concentration. This could be due to agglomeration of GNPs inside the PET matrix. Agglomerated GNPs can act as plasticizer by getting in between the polymer chains, and spacing them out from each other. This causes the polymer chains to slide past each other more easily at lower temperature, Tg, than they would without the plasticizer. The glass transition temperature of a semi-crystalline polymer is considered to be higher and broader than that of the amorphous polymer. The glass transition temperature of a polymer is influenced by its molecular weight (chain length). According to Flory et al., the glass transition temperature can be related to the molecular weight using the Flory-Fox equation:
where Tg is the glass transition temperature, Tg,∞ is the maximum glass transition temperature that can be achieved at a theoretical infinite molecular weight, K is an empirical parameter that is related to the, free volume present in the polymer sample, and Mn is the molecular weight of polymer
Free volume refers to polymer chain's ability to move and achieve different physical conformations, and it depends on the number of polymer chain ends. A polymer with long chain lengths (high molecular weights) will have fewer chain ends and less free volume than a polymer with short chain lengths (low molecular weight). Fewer chain ends or free volume results in a higher Tg. In the case of PET-GNP nanocomposites, the agglomerated GNPs can increase the free volume, therefore decrease the Tg. Also, the Tm shifted to higher values, suggesting the presence of crystalline zones in PET. In addition, increasing GNP concentration increased percent crystallinity in the nanocomposites. Additional crystallinity also tends to improve mechanical properties. Further investigation is needed to understand the nucleation mechanism and properly attribute the effects of graphene and crystallinity on mechanical enhancement.
Even though significant progress has been made to develop polymer nanocomposites, a general understanding of the enhanced modulus and strength has yet to emerge. A major challenge in developing these nanocomposites is the lack of structure-property models. Micromechanical models are widely used to predict the behavior of composite materials based on the properties of the pure components and the morphology of the composite material. Halpin and Tsai developed a composite theory to predict the elastic modulus of unidirectional composite materials as a function of aspect ratio. According to their model, the composite modulus can be estimated based on the modulus of the matrix and filler, as well as the shape and volume fraction of filler. The longitudinal modulus of the composite material (E11) is predicted using the following equation:
where Em is modulus of matrix, Af is aspect ratio of the filler (L/t=length/thickness), ϕ is volume fraction of the filler, and Er is the ratio of the filler's modulus to matrix's modulus.
The Hui-Shia model, suggested by Hui and Shia in 1998, is another micromechanical model that has been widely used to predict the modulus of the composites including unidirectional aligned disk-like platelets. In this theory, all moduli depend on a geometrical parameter, g, which depends on the inverse aspect ratio. The longitudinal and transverse modulus of the composite materials can be estimated using the following equations:
where E11 is longitudinal modulus of the composite, E22 is transverse modulus of the composite, Em is modulus of matrix, Ef is the filler's modulus, ϕ is volume fraction of the filler, and α is the inverse aspect ratio (t/L).
As can be seen from the aforementioned equations, the aspect ratio (L/t) of the GNPs is one of the important input parameters that should be used to evaluate the micromechanical models. Several attempts were made to make thin sections (70 nm) of the samples for TEM testing in order to estimate the length and thickness of the GNPs. However, due to the size of the granules in the block matrix, which appeared to be relatively large, the polymer was brittle for sectioning. The larger granules appeared resistant to sectioning and tended to fragment when striking the knife edge, resulting in shredded thin sections on a glass knife. Therefore, the thin sections were not successfully produced for TEM testing.
In the current research, the effectiveness of GNPs by weight in the nanocomposites was evaluated based on the following equation:
where ε is the value representing the effectiveness of GNPs by weight, E2 is elastic modulus of the PET-GNP nanocomposite, E1 is elastic modulus of PET, and Wt. % is weight fraction of GNPs used to prepare the nanocomposites.
It is important to note that sonication was employed in both in-situ polymerization and dispersion dosing methods. The higher effectiveness of the GNPs could be attributed to the greater level of exfoliation of the GNPs dispersed through sonication, resulting in a higher fraction of monolayer graphene.
A review of a subset of the published data of PET nanocomposite elastic modulus improvements, summarized in Table 37, allows for the same calculation of nanofiller effectiveness using Eq. 18. This indicates that the dispersion dosing is significantly more effective than the results summarized.
The main objective of this research was to achieve a uniform distribution of GNPs in PET nanocomposites via dispersion preparation followed by injection molding. The following results were derived through the applications of melt compounding, in-situ polymerization, and injection molding over the course of this research:
Melt Compounding:Amongst the GNPs with three different surface areas, the GNP-15 (surface area=15 m2/g) showed the highest improvement in elastic modulus.
The low surface area GNPs appears to provide a larger interface with more efficient interaction with the polymer matrix. This is because the GNP-15 contain larger graphene sheets per gram compared to GNP-150 and GNP-750, resulting in more free carbon edges and graphene surface area available to interact with PET chains.
Mixing PET and GNP powders resulted in a more uniform distribution of the GNPs in the matrix compared to the mixture with PET pellets. This indicates the spacing between graphene particles before melting in the compounder influences the final product.
Melt compounding GNPs with PET powders compared to PET pellets led to a greater improvement in elastic modulus and tensile strength. Based on the current literature, the powder melt compounding was newly tested, and showed significantly higher improvments than pellet melt compounding. At 20 wt. % GNPs, the elastic modulus of PET powders and pellets improved by 182% and 101%, respectively. At 20 wt. % GNPs, the tensile strength of PET powders and pellets improved by 35% and 14%, respectively.
Addition of GNPs on PET powders had a positive impact on PET crystallinity; but not an increasing trend. The crystallinity of pristine PET powders and pellets was measured 9% and 12%, respectively. An addition of 10 wt. % GNPs, amongst concentrations ranging from 2 wt. % to 20 wt. %, led to the highest improvement of 14% and 13% for PET powders and pellets, respectively. Why this occurs is unclear and is an opportunity for future research.
A decreasing trend on non-isothermal crystallinity of PET powders and pellets was observed with respect to concentration of GNPs. This is due to the presence of early nucleation sites by the addition of GNPs.
XRD analysis indicated that GNPs had a preferred orientation along the transverse direction of the PET tensile bars, likely caused by injection molding.
In-Situ Polymerization:Ultrasonic exfoliation is effective in dispersing GNPs in EG. Either probe or bath sonication methods are effective.
Probe sonication is more effective, likely due to the higher localized energy during cavitation, but it adds much more heat to the system compared to bath sonication. Overheating can severely damage the sonicator system and negatively impact the cavitation effectiveness during sample processing.
Increasing the G-Force during centrifugation separated the larger, or unexfoliated, GNPs from the exfoliated GNPs, which is an important step for maximizing the effectiveness of graphene in a composite.
Longer sonication times are associated with a reduction in the average GNP size, indicating that exposure to sonication fractures the GNPs. It is not clear if this fracture occurs on a weakened graphene sheet or is only the consequence of separation of agglomerated, intercalated layers of an already small size.
The exfoliation of GNPs from the starting powder is achieved through sonication and is independent of centrifugation. TEM confirmed the presence of monolayer graphene after sonication for 90 and 180 minutes and centrifugation at 260 and 2350 RCF. This is an area for future study to determine the optimized sonication times and centrifugation speeds.
A combination of TEM and Raman spectroscopy techniques helped estimate the size and number of layers of the dispersed GNPs in the liquid medium after sonication and centrifugation. This combined method is easy and recommended for future applications of GNP dispersions. However, it would be useful to try both techniques on frozen dispersions to prevent agglomeration of the GNPs caused by using heat treatment in the sample preparation.
The resulting PET-GNP nanocomposite at 2 wt. % was found to be more effective (ε=21±7) than nanocomposite prepared by melt compounding at the same concentration (ε=3±4).
An initial concentration of GNPs at 0.5 wt. % leads to sufficient fraction of exfoliated GNPs in 60 minutes to improve the properties of PET.
Once in dispersion, unexfoliated GNPs can be removed with centrifugation. If not, they do not negatively impact the nanocomposite, as measured by the tensile strength and elastic modulus, while visually decreasing the luminosity.
There was an increasing trend in elastic modulus as the concentration of graphene increased. At 2 wt. % concentration of GNPs, the elastic modulus increased by 22%. Whether this is an upper limit, is yet to be established.
Our results here show GNP dispersions as promising candidates for the development of graphene-based PET nanocomposites through in-situ polymerization.
PEG-GNP Dispersions and Masterbatch:The PET-GNP nanocomposites, fabricated through PEG-GNP dispersion dosing, outperform those that were prepared using masterbatch, exhibiting greater improvements in tensile strength of the PET. This is most likely due to exfoliation happening during the sonication that was used in preparation of dispersions. Exfoliation results in a higher fraction of few- to monolayer graphene sheets.
PEG shows promise to be used as dispersion medium for GNPs in creation of PET-GNP nanocomposites through the dispersion dosing approach due to its high viscosity and compatibility with PET chemistry. Improvements in crystallinity, modulus, and strength of PET observed in samples prepared by dosing PEG-400 dispersions.
Viscosity of the dispersion medium affects the stability and the achievable concentration of the dispersion, by reducing the sedimentation rate of dispersed GNPs.
The resulting PET-GNP nanocomposite at 0.006 wt. % was found to be significantly more effective (ε=1000±600) than nanocomposite prepared by melt compounding, with the same improvement in elastic modulus (ε=3±4).
GNP dispersions in PEG-400 at 0.006 wt. % improved the elastic modulus and tensile strength of PEG-dosed PET preforms by 8% and 4%, respectively. A decreasing trend in the elastic modulus and tensile strength of PEG-dosed PET preforms was observed by an increase in concentration of GNPs. This is due to the agglomeration of the dispersed GNPs, caused by the higher viscosity of PEG relative to EG.
The luminosity of nanocomposites was a function of the concentration of GNPs, specifically the number of platelets per unit volume.
An increase in the sonication time, and therefore energy density, during dispersion processing, decreases the luminosity of the preforms by also increasing the number of platelets per unit volume by fracturing the GNPs during sonication.
Centrifugation, employed during dispersion processing, has positive impact on luminosity of PET nanocomposites. Centrifugation separates out the unexfoliated GNPs from exfoliated ones. Increasing the centrifugation speed leads to a lower fraction of more light-absorbing unexfoliated GNPs, resulting in an increased luminosity of PET nanocomposites.
No significant improvement was observed for the modulus of PEG-dosed PET preforms when a GNP dispersion with an initial concentration of 1 mg/mL was dosed. Similar behavior was observed for the same dispersion after centrifugation, resulting in the final GNP dispersions with concentrations of <1 mg/mL. This is because the centrifugation leaves only a small fraction of the dispersed GNPs in the dispersions. Regardless of the degree of exfoliation, GNP dispersions at concentrations of ≤1 mg/mL does not impact the modulus of PET.
Significant improvement was observed for the tensile strength of PEG-dosed PET preforms when a high-viscosity dispersion medium (Mw=600 g/mol) with an initial concentration of 1 mg/mL was dosed. Similar behavior was observed for the same dispersions after centrifugation, resulting in the final GNP dispersions with concentrations of <1 mg/mL. The higher viscosity of the medium leads to a uniform dispersion of the exfoliated GNPs before and after centrifugation, resulting in a more uniform distribution of GNPs in the PET matrix.
No significant improvement was observed for the elastic modulus and the tensile strength of PEG-dosed PET preforms when GNP dispersions of >5 mg/mL were dosed. This is because at such high concentrations, the dispersions may never process well during sonication, resulting in a dispersion of agglomerated and poorly-distributed multi-layer GNPs.
As disclosed hereinabove, graphene-based poly(ethylene terephthalate) nanocomposites were successfully fabricated through several fabrication methods. Although extensive research has been demonstrated at lab scale, transferring the hierarchical fabrication methods to industrial scale production, is yet to be investigated. In this regard, different types of materials, GNPs and dispersion media, as well as processing routes and characterization methods through insightful analysis have a real potential for future development of PET-GNP nanocomposites. In light of the presented data disclosed herein, the following points are contemplated for future work:
Materials:GNPs, with different surface areas, are commercially available through different manufacturing processes. While the data in this research are primarily collected from the GNP-15 (surface area=15 m2/g), it would be helpful to prepare the PET-GNP nanocomposites using the GNPs of different surface area to understand better the changes in nanocomposites properties with respect to the surface area of GNPs.
Nanocomposite Processing Methods:Melt compounding is a promising method for the fabrication of nanocomposites due to low production cost at a moderate scale. Melt-compounded GNPs with PET pellets and powders showed significant improvement in tensile strength and elastic modulus of PET matrix. A better interaction between the GNPs and PET powders, due to an increase in PET surface-area-to-volume ratio compared to PET pellets, led to a more uniform distribution of GNPs in PET. Based on the data collected here, it is reasonable to expect to gain insight with an even smaller PET power or compounding with the PET pellets for a longer time. However, the constraint on melt time for PET must be considered as it leads to thermal degradation in ultimate applications. Future investigation is needed to further reduce the PET powder size and evaluate the level of distribution of GNPs and properties of the nanocomposites prepared by such PET matrix.
Additionally, PET-GNP nanocomposites prepared through in-situ polymerization were characterized by superior mechanical properties compared to those prepared through melt compounding. As stated earlier, bath sonication was utilized to prepare the GNP dispersions for the fabrication of nanocomposites. Effects of probe sonication on the quality of the dispersions and subsequent properties in the PET nanocomposites are still unknown. Therefore, future investigation is required to build upon and to optimize the existing results obtained through this method for commercial application. During the preparation of GNP dispersion, it was found that centrifugation had a positive effect on the mechanical properties of the nanocomposites prepared through in-situ polymerization. As shown in this research, the yield of the exfoliated GNPs after centrifugation is very low. This may limit the potential application of the GNP dispersion for the development of PET-GNP nanocomposites. According to Hernandez et al. and Paton et al., recycling the sediment separated from the supernatant, after centrifugation in the GNP dispersions, can help improve the yield of the exfoliated graphene. The process involves re-dispersing a portion of the sediment from the original sample in fresh dispersion medium in exactly the same way as the original dispersion was made. Further investigation is needed to understand this process and study the effects of sediment recycling and testing the resulting EG and PEG dispersions quality and nanocomposite products. PEG dispersions shows promise to improve the mechanical and thermal properties of PET. The nanocomposite tensile preforms were characterized to by superior mechanical and thermal properties compared to pristine PET. For our intended composites, the PEG dispersions must be stable to be uses for the industrial scale production of PET bottles during injection molding and blow molding process. Therefore, further investigation is required to fabricate and investigate the PET bottles using the PEG dispersions.
Characterization of Nanocomposites:TEM testing was successfully performed on the GNP dispersions to evaluate the size and thickness of the GNPs dispersed in EG. As mentioned herein, TEM testing of the PET-GNP nanocomposites was not successful due to the challenges associated with sample preparation. The data disclosed herein suggests that the PET-GNP nanocomposites, fabricated through PEG-GNP dispersion dosing, outperform those that were prepared using masterbatch, exhibiting greater improvements in stiffness and tensile strength of the PET. The HR-TEM micrographs indicated a more uniform distribution of GNPs in PET for these nanocomposites, however, more statistical data is needed to further support this claim. Therefore, information related to the size and thickness of the exfoliated GNPs dispersed in PET remains unknown. Research suggests that atomic force microscopy (AFM) is a useful method to determine the number of layers and provide thickness distribution of graphene in polymer nanocomposites. Therefore, further research is needed to combine HR-TEM and AFM techniques to evaluate the size and thickness of layers of the GNPs dispersed in PET.
Raman SpectroscopyRaman spectroscopy is by far the most straightforward method to study the level of defects and identify the number of layers in graphene materials. A typical Raman spectrum of graphene consists of three major bands including D band, G band, and 2D band near 1355 cm−1, 1570 cm−1, and 2700 cm−1, respectively. The D band is a weak feature of the Raman spectrum. It is due to a one-phonon scattering from defects. It is either absent or extremely weak in a spectrum for monolayer graphene, but it becomes distinguishable when there is a significant amount of defects. The G band is due to the degeneration of the optical phonon mode in graphene. According to Yoon et al., the intensity (I) of the G band is sensitive and increases with the number of layers up to 7 layers. The shape of this band does not vary much. Childres et al., showed that the ratio of the intensity of the D band to the G band, ID/IG in Raman spectra, can be used to characterize the level of defects in graphene related materials. According to Khan et al. and Paton et al., if defects present in graphene are edge defects or pre-existing defects in the material, then the ID/IG of the as-received powder and the samples after the sonication and centrifugation could be approximately related to the lateral size of graphene by:
where ID/IG is the ratio of the intensity of the Raman D and G bands, and k is estimated to be 0.17. The 2D band, on the other hand, is a strong band that is due to a two-phonon scattering. This band is also referred to as G′. The line shape of the 2D band reflects the electronic band structure and the number of layers of graphene.
Electron Band Structure in GrapheneRaman spectroscopy is a widely used characterization technique in the structural and electronic studies of graphene. To better understand the electronic structure of graphene, it is helpful to review the bond structure in graphene. As discussed earlier, three of the four atoms' electrons are involved in sp2 bonding, and they contribute very little to grapheme's electronic structure. The remaining atom in a state so-called π state plays an important role in the electronic structure of graphene. Band theory has been successfully used to explain physical properties of materials like electrical conductivity and optical absorption. According to solid-state physics, there will be an energy level in a solid where no electron can exist. This is called a band gap. In general, an electronic band structure of an insulator solid, shown in
In insulator solids, the energy bands are either full or empty. Considering the momentum behavior of electrons' energy, the bands will look like parabolas (
where γ02 is the nearest-neighbor hopping energy ≈2.8 eV, a is the lattice constant ≈2.46 Å, and E+ and E− represent the two energy bands for valence and conduction bands.
Transmission Electron MicroscopyIn TEM, a beam of electrons is used as a source of illumination. As shown in
When interacting with the specimen, electrons act as ionizing radiation. In particular, ionizing radiation is capable of removing tightly-bounded inner-shell electrons by transferring energy to the atoms in the specimen. The wavelength of an electron beam is significantly shorter than that of visible light, allowing visualization of the internal structure of a specimen. According to De Broglie's law, the wavelength (λ) of an electron beam is inversely proportional to the energy of the electrons (E) and can be calculated using the equation below:
SAED is an experimental technique used in TEM analysis. In SAED, a diffraction pattern is formed when an electron beam passes through a crystalline specimen in a TEM. It is one of the available crystallographic techniques to study the crystal structure of graphene. SAED not only can be used to identify crystal structures, but also to examine crystal defects. With the intention of distinguishing a monolayer with a multi-layer graphene, SAED were employed during the TEM testing in this study. The diffraction pattern represents a reciprocal lattice plane, which contains the diffraction response of lattice planes belonging to one crystal zone, and reciprocal lattice points, which are shown as diffraction spots.
In laser diffraction, a laser beam passes through a dispersed particle in the sample and the angular variation in intensity of the scattered light is measured. While large particles scatter light at small angles, small particles scatter light at large angles. This is illustrated in
One common approach to understand the particle size measurements is to report a distribution along with one or more values to describe the width of the size distribution. For the Mastersizer 3000, three different values on the x-axis are generally selected to define the volume-weighted distribution of the population. These values include Dx10, Dx50, and Dx90 and are shown in
With reference to
Surfactants may not be an option to stabilize dispersions due to the interference they cause in subsequent processing. While sonication provides the essential activation energy required to overcome the Van der Waals forces between graphene sheets, as mentioned earlier, the surface tension of the dispersion media is key to an effective exfoliation of graphene dispersions. Surface tension of the media also impacts the stability of the dispersed graphene. To create a high-quality graphene dispersion, graphene must be dispersed at a concentration useful to the appropriate application, and remain dispersed with high stability over a reasonable period. There are several parameters affecting the stability of the dispersions that are well-established in the field of colloid science.
Colloids are two-phase systems consisting of a dispersed phase, also called a discontinuous phase, and a dispersion medium, also called a continuous phase. A system in which the dispersed phase is of the same size are called monodisperse system. If a range of sizes are present, the system is then called polydisperse. From a chemistry standpoint, colloid systems include mixtures in which the dispersed phase is insoluble, with random movement or Brownian motion, and is suspended in the dispersion medium. Compared to a bulk material, a colloidal dispersion represents a state of higher free energy. Colloidal dispersions have a tendency to reduce their free energy by reducing the surface energy, altering the stability of the dispersion. When a substantial energy barrier exists, the dispersion's free energy will not be altered, resulting in stability for a significant period of time, a phenomenon called colloidal stability. However, if the energy barrier becomes too small, the colloid will become unstable. In such cases, the collisions caused by the Brownian motion of the particles lead to aggregation. A discussion of the intermolecular forces can help with understanding the stability of the dispersions and the reasons behind aggregation. Intermolecular forces comprise electrostatic forces (repulsive) and Van der Waals forces (attractive). The intermolecular forces between two molecules can be found using the Lennard-Jones potential from the below equation:
where V is the Lennard-Jones potential (J), ε is a measure of how strongly two molecules attract each other (J), σ is a constant parameter, a distance at which the intermolecular potential between two molecules is zero (nm), and r is the intermolecular distance between the two molecules (nm).
The Lennard-Jones potential describes the potential energy when two non-bonding molecules interact with each other based on their intermolecular distance. The Lennard-Jones potential is comprised of two terms: a repulsive force,
and an attractive force,
and it provides a useful overview of the total intermolecular interactions. When the two molecules are at an infinite distance, the possibility of them interacting is negligible, indicating the potential energy is zero. At this point, the molecules are most stable. As the molecules' separation distance decreases, the probability of the interaction increases. They come closer until they reach a region in which potential energy decreases from zero to a negative value. If the molecules become closer, the repulsive force will dominate, indicating an overlapping of atomic orbitals. In this case, atoms attempt to regain the space.
In the case of dispersions, when the repulsion forces dominate, the molecules do not aggregate, resulting in a stability of the dispersion. If the attractive forces prevail, the particles aggregate and alter the stability of the dispersion. In an unstable dispersion, the collisions of the particles lead to aggregate formation, followed by sedimentation or creaming Sedimentation is when the dispersed phase is denser than the dispersion medium and so the aggregations sink, whereas creaming happens when the dispersed phase is less dense, and the aggregations float.
GNPs with High Surface Area
While the invention has been described in terms of particular variations and illustrative figures, those of ordinary skill in the art will recognize that the invention is not limited to the variations or figures described. In addition, where methods and steps described above indicate certain events occurring in certain order, those of ordinary skill in the art will recognize that the ordering of certain steps may be modified and that such modifications are in accordance with the variations of the invention. Additionally, certain of the steps may be performed concurrently in a parallel process when possible, as well as performed sequentially as described above. To the extent there are variations of the invention, which are within the spirit of the disclosure or equivalent to the inventions found in the claims, it is the intent that this patent will cover those variations as well. Therefore, the present disclosure is to be understood as not limited by the specific embodiments described herein, but only by scope of the appended claims.
Claims
1. A polymer nanocomposite comprising:
- a matrix comprising polyethylene terephthalate; and
- a reinforcement material comprising dispersed phase graphene nanoplatelets.
2. The nanocomposite of claim 1, wherein the graphene nanoplatelets comprise a surface area of at least about 15 m2/g.
3. The nanocomposite of claim 1, wherein the graphene nanoplatelets comprise an average thickness ranging between about 10 nanometers (nm) and 20 nm.
4. The nanocomposite of claim 1, wherein the graphene nanoplatelets comprise a surface area ranging between about 120 m2/g and 150 m2/g.
5. The nanocomposite of claim 1, wherein the graphene nanoplatelets comprise an average thickness ranging between about 6 nm and 8 nm.
6. The nanocomposite of claim 1, wherein the graphene nanoplatelets comprise a surface area ranging between about 300 m2/g and 750 m2/g.
7. The nanocomposite of claim 1, wherein the graphene nanoplatelets comprise an average thickness ranging between about 2 nm and 3 nm.
8. A method for preparing graphene reinforced polyethylene terephthalate (PET), comprising:
- obtaining graphene nanoplatelets comprising a suitable surface area;
- adding the graphene nanoplatelets to a dispersion medium suitable for producing PET;
- sonicating the dispersion medium and graphene nanoplatelets so as to cause a homogeneous dispersion of the graphene nanoplatelets within the dispersion medium;
- centrifuging the dispersion medium and graphene nanoplatelets to remove a portion of larger graphene nanoplatelets that are not suitably dispersed within the dispersion medium;
- decanting a supernatant solution of graphene nanoplatelets dispersed in the dispersion medium; and
- using the supernatant solution for polymerization of the graphene reinforced PET.
9. The method of claim 8, wherein the graphene nanoplatelets comprise a surface area of at least about 15 m2/g.
10. The method of claim 8, wherein the graphene nanoplatelets comprise a surface area ranging between about 120 m2/g and 150 m2/g.
11. The method of claim 8, wherein the graphene nanoplatelets comprise a surface area ranging between about 300 m2/g and 750 m2/g.
12. The method of claim 8, wherein sonicating comprises immersing the solvent and graphene nanoplatelets in a bath sonicator for a period of time and operating the bath sonicator at a frequency suitable for dispersing the graphene nanoplatelets within the solvent.
13. The method of claim 12, wherein sonicating comprises selecting the period of time so as desirably reduce an average length and width of the graphene nanoplatelets.
14. The method of claim 12, wherein the frequency is a ultrasonic and the period of time ranges between at least 30 minutes and 180 minutes.
15. The method of claim 8, wherein centrifuging comprises subjecting the solvent and graphene nanoplatelets to a rotational speed of centrifugation ranging between at least 1400 RPM and 7200 RPM.
16. The method of claim 8, wherein adding further comprises selecting polyethylene glycol as the dispersion medium suitable for producing the graphene reinforced PET.
17. The method of claim 16, wherein selecting polyethylene glycol comprises selecting any one of PEG-300, PEG-400, and PEG-600 as the dispersion medium.
18. The method of claim 8, wherein adding further comprises selecting ethylene glycol as the dispersion medium suitable for producing the graphene reinforced PET.
19. The method of claim 18, wherein using the supernatant solution for polymerization further comprises performing an esterification reaction to produce bis(2-hydroxyl ethyl) terephthalate (BHET) with water as a by-product, followed by performing a polycondensation reaction so as to produce the graphene reinforced PET.
20. The method of claim 19, wherein performing the polycondensation reaction further comprises including one or more catalysts comprising any one or more of Antimony (Sb), Cobalt (Co), and Phosphoric Acid.
Type: Application
Filed: May 9, 2019
Publication Date: Jan 2, 2020
Applicant: Niagara Bottling, LLC (Ontario, CA)
Inventors: Jay Clarke Hanan (Ontario, CA), Vahid Shabafrooz (Ontario, CA)
Application Number: 16/408,213