HIGH VOLTAGE WINDOW ELECTROLYTE FOR SUPERCAPACITORS

Abstract

A supercapacitor according to the present invention includes a negative carbon-comprising electrode which does not intercalate sodium, and a positive carbon-comprising electrode. An electrolyte composition comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The supercapacitor has an electrochemical voltage window of from +0.0 V to 3.5 V (full cell voltage). The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na+. A method of making and a method of operating a supercapacitor is also disclosed.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional patent application of U.S. Non-Provisional patent application Ser. No. 15/806,693 filed Nov. 8, 2017, which claims priority to U.S. Provisional Patent Application No. 62/419,141 filed Nov. 8, 2016, entitled “HIGH VOLTAGE WINDOW ELECTROLYTE FOR SUPERCAPACITORS”, the entireties of which are all hereby incorporated herein by reference.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH

This invention was made with government support under contract no. DE-AC05-000R22725 awarded by the US Department of Energy. The government has certain rights in this invention.

FIELD OF THE INVENTION

The present invention relates to supercapacitors, and more particularly to high voltage supercapacitors.

BACKGROUND OF THE INVENTION

Supercapacitors store ionic charge electrostatically at the interface of high surface area electrodes, such as carbon electrodes, in a liquid electrolyte composition. Supercapacitors are also referred to interchangeably as ultracapacitors or electric double-layer capacitors (EDLC). Efforts to increase the energy density of supercapacitors have focused mainly on developing higher surface area electrodes and controlling electrode pore size. Energy density of supercapacitors can also be increased through faradaic mechanisms commonly known as pseudocapacitance, which arises from the introduction of redox active groups through functionalization of the carbon electrode surface or the incorporation of metal oxides.

Despite significant improvements in electrode materials design, most non-aqueous electrochemical capacitors use the same electrolyte compositions: either a mixture of tetraethylammonium tetrafluoroborate (TEABF₄) in acetonitrile (AN) or TEABF₄ in propylene carbonate (PC). These electrolyte compositions have a high specific conductivity that minimizes resistive losses and enables capacitors to operate at high power. However, these electrolyte compositions typically exhibit a practical voltage window around only 2.5-3.0 V, beyond which the capacitor lifetime is significantly reduced. Ionic liquids and other organic solvents (adiponitrile, sulfones, and carbonates) have been considered for high voltage electrolytes for capacitors. Of these, ionic liquids have generated the most interest due to their high stability, but remain limited by high cost, low purity, and low conductivity. Since the energy stored in a capacitor increases quadratically with voltage, extending the electrochemical window of the electrolyte composition could significantly improve the energy density of the capacitor.

With prolonged cycling, the capacitance of EDLCs decreases and the resistance increases. The performance degrades more rapidly at elevated temperature or higher voltage. Degradation is typically attributed to decomposition of the electrolyte, and is very sensitive to the electrolyte composition, electrode polarity, carbon surface functionality, and trace moisture. The long-term performance of EDLCs can also be limited by the stability of other components in the cell including the carbon, polymer binders, and current collectors (typically aluminum). Commercial EDLCs with organic electrolytes operate over a voltage window between approximately 1.5 and 4.5 V vs. Na/Na⁺. Developing higher voltage electrolytes for EDLCs requires careful consideration and control of all possible side reactions. For example, extending the positive voltage limit beyond 4.5 V vs. Na/Na⁺ likely requires strategies to effectively suppress corrosion of the aluminum current collector. Carbon oxidation may also occur at high voltage.

Extending the negative voltage limit below 1.5 V vs. Na/Na⁺ also presents certain challenges. The solvents most commonly used in lithium-ion batteries and EDLCs (carbonates and ACN) passivate electrodes at potentials below about 1.2 V vs. Na/Na⁺. Effective passivation of the negative electrode is critically important for the operation of lithium-ion batteries, but detrimental for double-layer capacitors. Even very thin insulating surface films can reduce the double layer capacitance and block small pores. Binders based on polytetrafluoroethylene (PTFE), which are commonly used in commercial EDLC electrodes, are also reduced below about 1.0 V vs. Na/Na⁺. Finally, the stability of the carbon itself with respect to reduction and/or intercalation of cations must be considered. Accordingly, there remains a continued need for an electrolyte composition that can extend the operating voltage window of a supercapacitor.

SUMMARY OF THE INVENTION

A supercapacitor includes a negative carbon-comprising electrode which does not intercalate sodium, and a positive carbon-comprising electrode. An electrolyte composition comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The supercapacitor has an electrochemical voltage window of from +0.0 V to 3.5 V (full cell voltage). The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na+.

The electrolyte composition can consist essentially of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte composition can consist of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

The positive carbon-comprising electrode and the negative carbon-comprising electrode can have a specific surface area of between 500 and 2000 m²/g. The positive carbon-comprising electrode and the negative carbon-comprising electrode can comprise between 80 and 95 wt % carbon, and between 5 and 20 wt % binder.

A method of making a supercapacitor can include the steps of providing a negative carbon-comprising electrode which does not intercalate sodium on a negative electrode current collector, and providing a positive carbon-comprising electrode on a positive electrode current collector. An electrolyte composition is provided which comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte is positioned between the positive electrode and the negative electrode. The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na⁺. The supercapacitor has an electrochemical voltage window of from +0.0 V to 3.5 V (full cell voltage).

An electrolyte for a supercapacitor comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na+. The electrolyte can consist essentially of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte can consist of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

A method of operating a supercapacitor can include the steps of providing a negative carbon-comprising electrode which does not intercalate sodium on a negative electrode current collector, and providing a positive carbon-comprising electrode on a positive electrode current collector. An electrolyte composition is provided which comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte is positioned between the positive electrode and the negative electrode to form a supercapacitor. The supercapacitor is operated within an electrochemical voltage window of from +0 V to 3.5 V (full cell voltage).

These and other features and advantages of the present invention will become apparent from the following description of the invention, when viewed in accordance with the accompanying drawings and appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

There are shown in the drawings embodiments that are presently preferred it being understood that the invention is not limited to the arrangements and instrumentalities shown, wherein:

FIG. 1 is a schematic cross-sectional illustration of a three-electrode cell which is used to evaluate separately the individual electrodes of a supercapacitor.

FIG. 2 is a schematic cross-sectional illustration of a supercapacitor fabricated as a button cell stack.

FIG. 3 shows the complex impedance (−Im(Z)(Ω) vs. Re(Z)(Ω)) of a single carbon BP2000 electrode with the electrolyte of the invention (1.0 m NaPF₆ in DME). The measurements were made in the three-electrode configuration of FIG. 1.

FIG. 4 is a plot of capacitance (F/g) vs. voltage (V vs. Na/Na⁺) of the carbon BP2000 electrode in the electrolyte of the invention (1.0 m NaPF₆ in DME). The capacitance values were derived from complex impedance measurements using the three-electrode cell configuration of FIG. 1. Example impedance curves are shown in FIG. 3.

FIG. 5 shows the leakage current (μA/cm²) vs. time (h) at the carbon BP2000 electrode when it is used as an anode (negative electrode) of a supercapacitor. The measurements were made in the three-electrode configuration of FIG. 1.

FIG. 6 is a plot of the leakage current (μA/cm²) vs. time (h) at the carbon BP2000 electrode when it is used as a cathode (positive electrode) of a supercapacitor. The measurements were made in the three-electrode configuration of FIG. 1.

FIG. 7 shows the charge and discharge curves (cell voltage vs. capacity (mAh)) for a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the invention (1.0 m NaPF₆ in DME). Representative charge-discharge cycles are shown (cycles 1, 50, 200, 500, 1000, 2000, and 3000). The measurements were made in the two-electrode configuration of FIG. 2.

FIG. 8 shows the coulombic efficiency (%) vs. cycle number for the supercapacitor of FIG. 7, over 3000 charge-discharge cycles. The measurements were made in the two-electrode configuration of FIG. 2.

FIG. 9 shows the complex impedance (−Im(Z)(Ω) vs. Re(Z)(Ω)) of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the invention (1.0 m NaPF₆ in DME). The measurements were made in the two-electrode configuration of FIG. 2.

FIG. 10 is a plot of capacitance (F/g) vs. voltage for a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the invention (1.0 m NaPF₆ in DME). The capacitance values were derived from complex impedance measurements using the two-electrode cell configuration of FIG. 2. Example impedance curves are shown in FIG. 9.

FIG. 11 is a schematic diagram of one duty cycle of the protocol used to generate the data shown in FIGS. 12, 13, and 14. Supercapacitors were tested in the two-electrode configuration of FIG. 2. The maximum cell voltage was chosen to be either 3.0 (FIG. 13) or 3.5 V (FIGS. 12 and 14).

FIG. 12 shows the complex impedance (−Im(Z)(Ω) vs. Re(Z)(Ω)) of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the invention (1.0 m NaPF6 in DME). The measurements were made in the two-electrode configuration of FIG. 2. The supercapacitor was cycled using the duty cycle shown in FIG. 11. The maximum cell voltage reached 3.5 V. The time durations in the figure legend represent the cumulative time at 3.5 V before each impedance measurement.

FIG. 13 shows the complex impedance (−Im(Z)(Ω) vs. Re(Z)(Ω)) of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in a conventional electrolyte (1.0 m tetraethylammonium tetrafluoroborate in acetonitrile). The measurements were made in the two-electrode configuration of FIG. 2. The supercapacitor was cycled using the duty cycle shown in FIG. 11. The maximum cell voltage reached 3.0 V. The time durations in the figure legend represent the cumulative time at 3.0 V before each impedance measurement.

FIG. 14 shows the complex impedance(−Im(Z)(Ω) vs. Re(Z)(Ω)) of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in a conventional electrolyte (1.0 m tetraethylammonium tetrafluoroborate in acetonitrile). The measurements were made in the two-electrode configuration of FIG. 2. The supercapacitor was cycled using the duty cycle shown in FIG. 11. The maximum cell voltage reached 3.5 V. The time durations in the figure legend represent the cumulative time at 3.5 V before each impedance measurement.

FIG. 15 is a plot of capacitance (F/g) vs. hours at voltage maximum for supercapacitors consisting of a carbon BP2000 anode and carbon BP2000 cathode in different electrolytes. The supercapacitors were cycled using the duty cycle shown in FIG. 11 with different values for the maximum cell voltage.

FIG. 16 shows the resistance (Ω) vs. hours at maximum voltage for supercapacitors consisting of a carbon BP2000 anode and carbon BP2000 cathode in different electrolytes. The supercapacitors were cycled using the duty cycle shown in FIG. 11 with different values for the maximum cell voltage.

DETAILED DESCRIPTION OF THE INVENTION

The invention is directed to high voltage electrolytes for supercapacitors. A supercapacitor and an electrolyte composition for use in a supercapacitor are described herein. The supercapacitor includes a negative carbon electrode having a current collector, a positive carbon electrode having a current collector, an ion-permeable separator disposed between the negative and positive electrodes, and an electrolyte composition disposed between the negative and positive electrodes. A new combination of solvent and salt compositions is stable up to 3.9 V electrochemical window. The electrolyte composition includes a conductive sodium salt component including sodium hexafluorophosphate (NaPF₆) and a non-aqueous solvent component including dimethoxyethane (DME).

High voltage electrolytes are common to the lithium battery and lithium-ion battery industries. These electrolytes typically consist of a lithium salt (or mixture of lithium salts) dissolved in a solvent or mixture of solvents. The solvents for these high voltage applications are typically selected from the list: Acetonitrile (AN), γ-Butyrolactone (BL), 1,2-Dimethoxyethane (DME,monoglyme), 1.2-Diethoxyethane (DEE, diglyme), Triglyme, Tetraglyme, Diethyl Carbonate (DEC), Dimethyl Carbonate (DMC), Dimethylformamide (DMF), Dimethylsulfite (DMS), Dimethylsulfoxide (DMSO), Dioxolane (DL), Ethylene Carbonate (EC), Ethylene Glycol Sulfite (EGS), Ethyl Propyl Carbonate (EPC), Methyl Acetate (MA), Methyl Formate (MF), Methyl Ethyl Carbonate (MEC), 3-Methyl-2-Oxazolidinone (3-Me-20X), N-Methyl Pyrrilidinone (NMP), Methyl Propyl Carbonate (MPC), 2-Methyltetrahydrofuran (2-MeTHF), Nitromethane (NM), Propylene Carbonate (PC), Tetrahydrofuran (THF), Thionyl Chloride (SOCl₂, also a cathode material), Sulfolane (SL), Sulfuryl Chloride (SO₂Cl₂, also a cathode material), Sulfur Dioxide (SO₂, also a cathode material).

The salt (or salt mixture) for high voltage battery electrolytes is typically selected from the list: Lithium Bromide (LiBr), Lithium Perchlorate (LiClO₄), Lithium Tetrafluoroborate (LiBF₄), Lithium Tetrachloroaluminate (LiAlCl₄), Lithium Hexafluorophosphate (LiPF₆), Lithium Hexafluoroarsenate (LiAsF₆), Lithium Trifluoromethanesulfonate (LiTFS, LiCF₃SO₃), Lithium Perfluoromethylsulfonyl Imide (LiTFSI, LiN(CF₃SO₂)₂), Lithium Perfluoromethylsulfonyl Methide (LiC((CF₃S0₂)₃), Lithium Bis(oxalato) borate (LiBOB, LiC₄B0₈).

These battery electrolytes are not used in supercapacitors because (at negative potentials) most of these solvents are reduced to yield insoluble compounds which passivate the electrode surface. These passive films are essential for the safe operation of lithium and lithium-ion batteries, but they reduce the capacitance at carbon electrodes (often by several orders of magnitude) and are therefore not useful in supercapacitors which rely on high capacitance at the carbon electrode surface. Furthermore, lithium ions and solvent-coordinated lithium ions intercalate into many carbon electrode materials (lithium intercalation is the preferred reaction for lithium-ion batteries) and this can lead to exfoliation of the carbon and destruction of the electrode. Therefore, for supercapacitors, the lithium salt is replaced with an organic cation salt typically selected from the list: Tetraethylammonium Hexafluorophosphate (Et₄NPF₆), Tetraethylammonium Tetrafluoroborate (Et₄NBF₄), Tetraethylammonium Trifluoromethanesulfonate (Et₄NCF₃SO₃), Tetraethylammonium Perfluoromethylsulfonyl Imide (Et₄N(CF₃SO₂)₂N), Tetraethylammouinm Perchlorate (Et₄NClO₄), Tetrabutylammonium Perchlorate (Bu₄NClO₄), Trimethylethylammonium Hexafluorophosphate (Me₃EtNPF₆), Tripropylmethylammonium Hexapfuorophosphate (Pr₃MeNPF₆), Triisopropylmethylammonium Hexafluorophosphate (iPr₃MeNPF₆), Diisopropylethylmethylammonium Hexafluorophosphate (iPr₂EtMeNPF₆), Tributylmethylammonium Hexafluorophosphate (Bu₃MeNPF₆), Triisobutylmethylammonium Hexafluorophosphate (iBu₃MeNPF₆), Triethylmethylphosphonium Hexafluorophosphate (Et₃MePPF₆), Tributylmethylphosphonium Hexafluorophosphate (Bu₃MePPF₆).

Virtually all commercial nonaqueous supercapacitors utilize either Et₄NBF₄ in acetonitrile or Et₄NBF₄ in propylene carbonate. Acetonitrile and propylene carbonate are each oxidatively stable to >4.0 V vs Li/Li⁺. Both solvents, however are reductively unstable and this leads to a working voltage range of ˜2.7 V for supercapacitors with these electrolytes.

Glyme solvents and in particular DME are oxidatively stable to >3.9 V vs Na/Na⁺, and they are reductively stable to <0.05 vs Na/Na⁺. This voltage stability range enables a possible working voltage window of approximately 3.9 V for supercapacitors. However, organic cation salts exhibit relatively low solubility in glyme solvents. Nevertheless, monovalent alkali cation salts exhibit much higher solubility because the cations coordinate with the ether oxygen linkages on the glyme molecules. Specifically, DME has a high donor number (20) and it strongly coordinates with alkali cations. Li⁺ and K⁺ cations readily intercalate into carbon electrodes at negative potentials, thereby limiting the use of lithium and potassium salts for supercapacitors. However, Na⁺ cations exhibit anomalous intercalation behavior into carbon which depends very much on the crystallographic structure of the carbon and on the solvent. Some solvents co-intercalate into some carbons with the Na⁺ cations to yield C-Na-solvent ternary compounds. In particular, Na⁺ salts in THF, 2MeTHF and diglyme solvents exhibit this behavior.

Other side reactions may also limit the working range of the supercapacitor. In addition to strong alkali cation coordination, the glyme solvents also strongly coordinate to other cations such as Al⁺³. These solvents dramatically accelerate the corrosion of aluminum current collectors. Conventional supercapacitor electrodes utilize Polytetrafluoroethylene (PTFE) as a binder in the formation of the electrodes from carbon powders. PTFE, however, is reduced at potentials approximately <0.7 V vs Na/Na⁺. Therefore, PTFE-bonded carbon electrodes will exhibit a working voltage range approximately 0.65 V lower than the voltage window of the DME solvent. In order to enable the utilization of the 3.9 V working voltage range of the electrolyte of the current invention, it is necessary to identify the precise sodium salt and the precise carbon structure that does not permit intercalation of Na⁺ or the cointercalation of the solvent to yield ternary intercalation compounds. And, a new binder for the carbon electrode must be identified and the aluminum corrosion reaction must be eliminated.

The NaPF₆ salt minimizes corrosion of the aluminum current collectors. DME has a low viscosity, which promotes high electrolyte conductivity. Glymes with higher molecular weight also can be capable of providing a similar voltage window. Sodium carboxymethyl cellulose can be used as an electrode binder primarily for its excellent stability over a wide voltage window. This binder also has the advantage of being water-soluble and environmentally benign. The DME-based electrolyte shows an electrochemical window up to 3.5 V in full cells with high-surface-area carbon electrodes. The high voltage performance could significantly increase the overall energy density of EDLCs.

The invention represents an unexpected discovery that combination of NaPF₆ in DME does not intercalate (or co-intercalate solvent) or form ternary intercalation compounds in BP2000 carbon. Furthermore, the PF₆⁻ anion inhibits aluminum corrosion, and the use of sodium carboxymethyl cellulose as the binder for the BP2000 carbon electrode (in place of PTFE) enables the utilization of the approximately 3.9V window of the electrolyte of the current invention in supercapacitor whose electrodes are comprised of sodium carboxymethyl cellulose bonded BP2000 carbon.

An electrolyte consisting of NaPF₆ salt in 1,2-dimethoxyethane (DME) can extend the voltage window of electric double-layer capacitors (EDLCs) to >3.5 V. DME does not passivate carbon electrodes at very negative potentials (near Na/Na⁺), extending the practical voltage window by about 1.0 V compared to standard, non-aqueous electrolytes based on acetonitrile. The voltage window is demonstrated in two- and three-electrode cells using a combination of electrochemical impedance spectroscopy (EIS), charge-discharge cycling, and measurements of leakage current. DME-based electrolytes cannot match the high conductivity of acetonitrile solutions, but they can satisfy applications that demand high energy density at moderate power. The conductivity of NaPF₆ in DME is comparable to commercial lithium-ion battery electrolytes and superior to most ionic liquids.

A supercapacitor according to the present invention includes a negative carbon-comprising electrode which does not intercalate sodium, and a positive carbon-comprising electrode. An electrolyte composition comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na⁺. The upper limit of the voltage window can be 3.5 V, 3.6 V, 3.7 V, 3.8 V, and 3.9 V vs. Na/Na⁺, or within a range of any high and low value selected from these.

The electrolyte composition can consist essentially of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte composition can consist of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

The positive carbon-comprising electrode and the negative carbon-comprising electrode can have a specific surface area of between 500 and 2000 m²/g. The positive carbon-comprising electrode and the negative carbon-comprising electrode can comprise between 80 and 95 wt % carbon, and between 5 and 20 wt % binder.

A method of making a supercapacitor according to the invention includes the steps of providing a negative carbon-comprising electrode which does not intercalate sodium on a negative electrode current collector, and providing a positive carbon-comprising electrode on a positive electrode current collector. An electrolyte composition is provided which comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte is positioned between the positive electrode and the negative electrode. The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na⁺.

A method of operating a supercapacitor according to the invention includes the steps of providing a negative carbon-comprising electrode which does not intercalate sodium on a negative electrode current collector, and providing a positive carbon-comprising electrode on a positive electrode current collector. An electrolyte composition is provided which comprises sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte is positioned between the positive electrode and the negative electrode. The supercapacitor is operated within an electrochemical voltage window of from +0.0 V to 3.5 V (full cell voltage).

An electrolyte for a supercapacitor according to the invention includes sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether. The electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na⁺.

In one embodiment, a method of forming a supercapacitor includes providing a negative electrode consisting of sodium carboxymethyl cellulose bonded carbon Black Pearls 2000 (BP2000, Cabot Corporation) and having an aluminum current collector; and providing a positive electrode consisting of carbon BP2000 or other high surface area carbon and having a current collector; providing an ion-permeable separator in a space between the negative and positive electrodes, and providing an electrolyte composition in the space between the negative and positive electrodes. The electrolyte composition includes a conductive sodium salt component including sodium hexafluorophosphate (NaPF₆) and a non-aqueous solvent component including dimethoxyethane (DME).

In another embodiment, the electrolyte composition may further contain additional salts such as: sodium trifluoromethanesulfonate (NaTFS), sodium perchlorate (NaClO₄), tetrabutylammonium perchlorate (TBAClO₄), tetrabutylammonium hexafluorophosphate (TBAPF₆), or combinations thereof. The electrolyte composition may also further contain additional solvents such as: diglyme, triglyme, tetraglyme, tetrahydrofuran, 2-methyltetrahydrofuran, or combinations thereof.

Experimental Procedure

Electrolyte Preparation

All procedures were carried out in a glove box filled with high-purity argon. Sodium hexafluorophosphate (NaPF₆, 98% Sigma Aldrich) was dissolved in 1,2-dimethoxyethane (DME, battery grade, Mitsubishi Chemical Company) at a concentration of 1 molal (m). Some control experiments were performed with a standard acetonitrile-based electrolyte. Tetraethylammonium tetrafluoroborate (TEABF₄, electrochemical grade, Sigma Aldrich) was dissolved in acetonitrile (ACN, 99.8%, anhydrous, Sigma Aldrich) at 1 m concentration. Both electrolytes were dried over 4 A molecular sieve for several days. After drying, the DME-based electrolyte was stored over sodium metal to remove other impurities.

Electrode Preparation:

High-surface-area carbon electrodes were prepared using 85 wt. % Black Pearls 2000 (BP2000, Cabot Corporation, BET surface area 1500 m²/g) and 15 wt. % sodium carboxymethyl cellulose (CMC, Sigma Aldrich, molecular weight 700,000). BP2000 and CMC were ultrasonicated in water to produce a homogenous suspension. Electrodes were deposited by spray-coating onto aluminum foil. Electrode thickness ranged from 25 to 130 μm with loadings from 0.4 to 2.2 mg/cm².

Electrochemical Testing:

Two-electrode button cells (316L stainless steel, size CR2032, Hohsen. Corp. Japan) were prepared using high-surface-area carbon electrodes and a polymer separator (Celgard 2325). Some measurements were performed using a three-electrode cell (EL-Cell GmbH) with sodium metal for the reference and counter electrodes, using the configuration shown in FIG. 1. The two-electrode button cell configuration is shown in FIG. 2. Potentials measured with the three-electrode cell are referenced to the Na/Na+ potential (E_Na/Na+≈+0.13 V vs. E_Li/Li+). One polymer separator and one glass fiber separator were used in the three-electrode cells to provide sufficient electrode separation to accommodate the reference electrode. Unless stated otherwise, 1 m NaPF₆ in DME was used as the electrolyte. Cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), charge-discharge cycling, float tests, and leakage current measurements were acquired using Bio-Logic instruments (VSP and MPG2). All tests were conducted at room temperature.

FIG. 3 shows EIS (20 kHz-10 mHz) of the carbon electrode in 1 m NaPF₆/DME electrolyte at different voltages measured in the three-electrode cell of FIG. 1 with sodium counter and reference electrodes. The carbon electrode was held at each voltage step for 2 h prior to measurement, and EIS was taken between 0.05 and 3.9 V vs. Na/Na+.

FIG. 3 shows the complex impedance of a single carbon BP2000 electrode in the electrolyte of the current invention (1.0 m NaPF6 in DME). The measurements were made in the three-electrode configuration of FIG. 1. The negative voltage limit extends almost to the sodium potential. FIG. 3 shows EIS spectra collected between 0.05 and 3.9 V vs. Na/Na⁺. The low-frequency EIS data form vertical lines over this entire voltage range, indicating that no side-reactions occur within this window. Importantly, the electrode is not passivated even within 50 mV of the sodium potential.

FIG. 4 shows the capacitance of the carbon BP2000 electrode in the electrolyte of the current invention. The capacitance values were derived from complex impedance measurements using the three-electrode cell configuration of FIG. 1. Example impedance curves are shown in FIG. 3.

FIG. 4 shows the electrode capacitance taken from the EIS data. A minimum in the capacitance occurs near 3.0 V vs. Na/Na+, which also corresponds to the open circuit potential. This minimum reflects the potential of zero charge of the carbon electrode. Moving away from the potential of zero charge, the capacitance steadily increases, confirming the electrodes do not passivate over this voltage range. The capacitance values measured by EIS range from 50 to 250 F/g, which is comparable to what is obtained with high surface area electrodes in ACN-based electrolyte with three-electrode cells.

To verify that no side-reactions occur between 0.05 and 3.9 V vs. Na/Na⁺ leakage currents were also measured in the three-electrode cells. FIG. 5 shows the leakage current at the carbon BP2000 electrode when it is used as an anode (negative electrode) of a supercapacitor. The measurements were made in the three-electrode configuration of FIG. 1. FIG. 6 shows the leakage current at the carbon BP2000 electrode when it is used as a cathode (positive electrode) of a supercapacitor. The measurements were made in the three-electrode configuration of FIG. 1.

The carbon electrode was held at different potentials for 12 h while the decay in the current was monitored. FIG. 5 shows that the leakage currents are <2 μA/cm² at the low limit of the voltage window. FIG. 6 shows that the leakage currents are <1 μA/cm² at the high limit of the voltage window. Impedance spectra were collected before and after the leakage current measurements to verify that the low currents were not due to electrode passivation (data not shown). Together, the data obtained from the three-electrode cells indicate that the NaPF₆/DME electrolyte has a voltage window from 0.05-3.9 V vs. Na/Na⁺.

FIG. 7 shows the charge and discharge curves for a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the current invention (1.0 m NaPF₆ in DME). Representative charge-discharge cycles are shown. The measurements were made in the two-electrode configuration of FIG. 2.

FIG. 8 shows the coulombic efficiency of the supercapacitor of FIG. 7 over 3000 charge-discharge cycles. The measurements were made in the two-electrode configuration of FIG. 2.

FIG. 9 shows the complex impedance of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the current invention (1.0 m NaPF6 in DME). The measurements were made in the two-electrode configuration of FIG. 2.

The voltage window for the full cells was checked by EIS. FIG. 9 shows the EIS response of a full cell charged to different voltages. Up to 3.8 V the EIS spectra are vertical lines, indicating the cell behaves as an ideal capacitor with no measurable side-reactions. At 4.0 V the EIS spectrum is no longer vertical, demonstrating that the voltage window has been exceeded.

FIG. 10 shows the capacitance of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the current invention (1.0 m NaPF6 in DME). The capacitance values were derived from complex impedance measurements using the two-electrode cell configuration of FIG. 2. Example impedance curves are shown in FIG. 9. The capacitance of the full cell with the DME-based electrolyte is comparable to what can typically be achieved with ACN-based electrolytes in similar two-electrode cells.

FIG. 11 shows the schematic of one duty cycle of the protocol used to generate the data shown in FIGS. 12, 13, and 14. Supercapacitors were tested in the two-electrode configuration of FIG. 2. The maximum cell voltage was chosen to be either 3.0 (FIG. 13) or 3.5 V (FIGS. 12 and 14). Cells were cycled four times at 1 mA/cm² followed by a two hour hold at the maximum voltage. Cells were then discharged prior to EIS analysis (20 kHz-100 mHz). EIS results for up to 25 consecutive duty cycles are shown corresponding to a total float time of 50 h at the maximum voltage.

FIG. 12 shows the complex impedance of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in the electrolyte of the current invention (1.0 m NaPF6 in DME). The measurements were made in the two-electrode configuration of FIG. 2. The supercapacitor was cycled using duty cycle shown in FIG. 11. For each duty cycle the cell was cycled four times at 1 mA/cm² followed by a two hour hold at 3.5 V. The supercapacitor was then fully discharged and the complex impedance was measured. Complex impedance spectra are shown for up to 25 consecutive duty cycles corresponding to a total float time of 50 h at the maximum voltage. The impedance spectra are stable and reproducible after 50 h confirming that the electrolyte is stable under these conditions.

FIG. 13 shows the complex impedance of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in a conventional electrolyte (1.0 m tetraethylammonium tetrafluoroborate in acetonitrile). The measurements were made in the two-electrode configuration of FIG. 2. The supercapacitor was cycled using duty cycle shown in FIG. 11. For each duty cycle the cell was cycled four times at 1 mA/cm² followed by a two hour hold at 3.0 V. The supercapacitor was then fully discharged and the complex impedance was measured. Complex impedance spectra are shown for up to 25 consecutive duty cycles corresponding to a total float time of 50 h at the maximum voltage. The impedance spectra are stable and reproducible after 50 h confirming that the electrolyte is stable under these conditions.

FIG. 14 shows the complex impedance of a supercapacitor consisting of a carbon BP2000 anode and carbon BP2000 cathode in a conventional electrolyte (1.0 m tetraethylammonium tetrafluoroborate in acetonitrile). The measurements were made in the two-electrode configuration of FIG. 2. The supercapacitor was cycled using duty cycle shown in FIG. 11. For each duty cycle the cell was cycled four times at 1 mA/cm² followed by a two hour hold at 3.5 V. The supercapacitor was then fully discharged and the complex impedance was measured. Complex impedance spectra are shown for up to 20 consecutive duty cycles corresponding to a total float time of 40 h at the maximum voltage. The changes in the impedance spectra show that the electrolyte is not stable under these conditions.

FIG. 15 shows the capacitance of supercapacitors consisting of a carbon BP2000 anode and carbon BP2000 cathode in different electrolytes. The supercapacitors were cycled using the duty cycle shown in FIG. 11 with different values for the maximum cell voltage. The capacitance values were derived from complex impedance measurements using the two-electrode cell configuration of FIG. 2. Example impedance curves are shown in FIGS. 12-14.

FIG. 16 shows the resistance of supercapacitors consisting of a carbon BP2000 anode and carbon BP2000 cathode in different electrolytes. The supercapacitors were cycled using the duty cycle shown in FIG. 11 with different values for the maximum cell voltage. The capacitance values were derived from complex impedance measurements using the two-electrode cell configuration of FIG. 2. Example impedance curves are shown in FIGS. 12-14.

This invention can be embodied in other forms without departing from the essential attributes thereof. Accordingly, reference should be made to the following claims to determine the scope of the invention.

Claims

1. A method of making a supercapacitor, comprising the steps of:

providing a negative carbon-comprising electrode which does not intercalate sodium on a negative electrode current collector;

providing a positive carbon-comprising electrode on a positive electrode current collector;

providing an electrolyte composition comprising sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether;

positioning the electrolyte between the positive electrode and the negative electrode;

wherein the electrolyte has an electrochemical voltage window of from +0.05 V to 3.9 V vs. Na/Na+.

2. The method of making a supercapacitor according to claim 1, wherein the electrolyte composition consists essentially of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

3. The method of making a supercapacitor according to claim 1, wherein the electrolyte composition consists of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

4. The method of making a supercapacitor according to claim 1, wherein the positive carbon-comprising electrode and the negative carbon-comprising electrode comprise between 80 and 95 wt % carbon, and between 5 and 20 wt % binder.

5. The method of making a supercapacitor according to claim 1, wherein the negative carbon-comprising electrode is comprised of carbon black, wherein the carbon black is high surface area carbon black Black Pearls® 2000.

6. A method of operating a supercapacitor, comprising the steps of:

providing a negative carbon-comprising electrode which does not intercalate sodium on a negative electrode current collector;

providing a positive carbon-comprising electrode on a positive electrode current collector;

providing an electrolyte composition comprising sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether;

positioning the electrolyte between the positive electrode and the negative electrode to form a supercapacitor; and,

operating the supercapacitor within an electrochemical voltage window of from +0 V to 3.5 V (full cell voltage).

7. The method of operating a supercapacitor according to claim 6, wherein the electrolyte composition consists essentially of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

8. The method of operating a supercapacitor according to claim 6, wherein the electrolyte composition consists of sodium hexafluorophosphate and a non-aqueous solvent comprising at least one selected from the group consisting of ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, and tetraethylene glycol dimethyl ether.

9. The method of operating a supercapacitor according to claim 6, wherein the positive carbon-comprising electrode and the negative carbon-comprising electrode comprise between 80 and 95 wt % carbon, and between 5 and 20 wt % binder.

10. The method of operating a supercapacitor according to claim 6, wherein the negative carbon-comprising electrode is comprised of carbon black, wherein the carbon black is high surface area carbon black Black Pearls® 2000.