Low-maintenance coatings

- Cardinal CG Company

The invention provides a substrate bearing a low-maintenance coating. The coating includes two films: a first film comprising silica (e.g., silicon dioxide) and a second film comprising titania (e.g., titanium dioxide). Preferably, both films are provided within particular thickness ranges. The invention also provides methods of depositing such coatings.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description
CROSS REFERENCE To RELATED APPLICATIONS

The present application claims priority to provisional U.S. patent application filed Jul. 12, 2004 and assigned Ser. No. 60/587,210, and provisional U.S. patent application filed Mar. 7, 2005 and assigned Ser. No. 60/659,491, the entire disclosures of which are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention provides thin film coatings for glass sheets and other substrates. More particularly, the invention provides thin film coatings including a thin photocatalytic film, such as titania, deposited over a thin base layer, such as silica. The invention also provides methods of depositing such coatings onto glass sheets and other substrates.

BACKGROUND OF THE INVENTION

For many years, it has been known that titanium dioxide can be used as a photocatalyst. A great deal of research has been done with a view toward providing photocatalytic coatings that have self-cleaning properties. The pursuit of self-cleaning photocatalytic window coatings, in particular, has been an active field of exploration. Such coatings typically involve a titanium dioxide layer carried by a glass pane. These coatings are commonly provided with a relatively thick layer of titanium dioxide and/or a specific under-layer system designed for achieving high levels of photoactivity. Thick titanium dioxide layers, unfortunately, produce high levels of visible reflectance, thus creating a somewhat mirror-like appearance. This high visible reflection tends to exaggerate the appearance of dirt on a window. Further, known under-layer systems commonly teach that specific materials and crystal structures must be used for the under-layer film(s) to achieve acceptable photoactivity levels. Moreover, many photocatalytic coating systems teach that heating is required during or after film deposition to achieve acceptable levels of photoactivity.

Known photocatalytic coatings also tend to have properties that are less than ideal for applications in which the coatings are used on windows. As noted above, the visible reflectance of many known photocatalytic coatings is unacceptably high. Moreover, the reflected colors of these coatings tend not to be ideal. Further, some of these coatings have particularly high surface roughness, as they are designed to have large surface areas that facilitate high photoactivity levels. These rough coatings, unfortunately, tend to be quite vulnerable to being abraded. They are also particularly susceptible to taking on and stubbornly retaining dirt and other contaminants, due to their high surface roughness. Finally, with many recent photocatalytic coatings (e.g., those in which complex under-layer systems are used to maximize photoactivity), it is unclear whether these coatings will exhibit the longevity (e.g., in-field durability over time) that is required for number-one-surface coatings.

The present invention provides low-maintenance coatings that offer exceptional durability, exceptional optical properties, reliable production processes, and surprising cleanliness/maintenance properties.

SUMMARY OF THE INVENTION

In certain embodiments, the invention provides a low-maintenance coating on a glass sheet. The low-maintenance coating comprises a first film positioned directly over a first major surface of the glass sheet and a second film positioned directly over the first film. In various embodiments of the present invention, the first film includes a thin base film, (e.g. silica) that has a thickness of less than about 300 angstroms, alternatively less than about 150 angstroms, and further alternatively between about 70 angstroms and about 120 angstroms. The second film in various embodiments of the present invention includes a thin photocatalytic film (e.g. titania) that has a thickness of less than about 300 angstroms, alternatively less than about 150 angstroms, and further alternatively between about 30 angstroms and about 120 angstroms.

In other embodiments, the invention provides a method of depositing a low-maintenance coating. The method comprises depositing a low-maintenance coating on a glass sheet by depositing first film directly over a first major surface of the glass sheet and then depositing a second film directly over the first film. In one embodiment of the present invention, the first film comprises silica and is deposited at a thickness of between about 70 angstroms and about 120 angstroms. The second film comprises titania and is deposited at a thickness of between about 30 angstroms and about 120 angstroms. In some of these embodiments, both films are deposited by sputtering, preferably while maintaining the substrate at a low temperature (e.g., less than about 250 degrees Celsius, and preferably less than 200 degrees Celsius).

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a partially broken-away schematic cross-sectional side view of a substrate bearing a low-maintenance coating in accordance with certain embodiments of the invention;

FIG. 2 is a partially broken-away perspective view of a window pane bearing a low-maintenance coating, the pane is mounted in an exterior wall of a building in accordance with certain embodiments of the invention; and

FIG. 3 is a schematic side end view of a sputtering chamber that is adapted for use in certain methods of the invention.

 DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The following detailed description is to be read with reference to the drawings, in which like elements in different drawings have like reference numerals. The drawings, which are not necessarily to scale, depict selected embodiments and are not intended to limit the scope of the invention. Skilled artisans will recognize that the given examples have many alternatives that fall within the scope of the invention.

In certain embodiments, the invention provides a substrate 10 bearing a low-maintenance coating 40. A variety of substrates are suitable for use in the invention. Preferably, the substrate 10 is a sheet-like substrate having generally or substantially opposed first 12 and second 14 major surfaces. In many embodiments, the substrate is a sheet of transparent material (i.e., a transparent sheet). The substrate, however, is not required to be transparent. For most applications, though, the substrate will comprise a transparent (or at least translucent) material, such as glass or clear plastic. For example, the substrate 10 is a glass sheet (e.g., a window pane) in preferred embodiments. A variety of known glass types can be used, and soda-lime glass is preferred.

Substrates of various sizes can be used in the present invention. Commonly, large-area substrates are used. Certain embodiments involve a substrate 10 having a width of at least about 0.5 meter, preferably at least about 1 meter, perhaps more preferably at least about 1.5 meters (e.g., between about 2 meters and about 4 meters), and in some cases at least about 3 meters.

Substrates of various thicknesses can be used in the present invention. Commonly, substrates (e.g., glass sheets) having a thickness of about 1-5 mm are used. Certain embodiments involve a substrate 10 with a thickness of between about 2.3 mm and about 4.8 mm, and perhaps more preferably between about 2.5 mm and about 4.8 mm. In some cases, a sheet of glass (e.g., soda-lime glass) with a thickness of about 3 mm will be used.

In certain embodiments, the invention provides a substrate 10 bearing a low-maintenance coating 40. The coating 40 is preferably deposited over (e.g., over an entirety of) a major surface 12 of the substrate 10. The low-maintenance coating 40 includes two films: (1) a first film 30 deposited over a major surface 12 of the substrate 10; and (2) a second film 50 deposited over the first film 30.

In various embodiments of the present invention, the first film 30 includes a base film, such as silica (e.g., silicon dioxide), and desirably is deposited directly over the substrate 10 (e.g., directly over a major surface 12 of the substrate). This film preferably consists of, or consists essentially of, silicon dioxide. The silica in the first film 30, however, can include small amounts of an electrically-conductive material, such as aluminum, which may be oxidized in the film 30. For example, this film 30 can be deposited by sputtering a silicon-containing target that includes a small amount of aluminum or another metal that enhances the electrical conductivity of the target. The first film 30 (an entire thickness of which may consist essentially of silica) desirably has (e.g., is deposited at) a physical thickness of less than about 300 angstroms, alternatively less than about 150 angstroms (e.g., between about 40 angstroms and about 150 angstroms), and further alternatively about 70 angstroms and about 120 angstroms. These incredibly small thicknesses facilitate a surprisingly array of exceptional properties in the present coating.

The coating 40 includes a second film 50 that includes a photocatalytic film, such as titania, and desirably is deposited directly over the first film 30. It is noted that one or more photocatalytic materials may be used in embodiments of the present invention including but not limited to oxides of titanium, iron, silver, copper, tungsten, aluminum, zinc, strontium, palladium, gold, platinum, nickel, cobalt and combinations thereof. In preferred embodiments, this film 50 consists of, or consists essentially of, titanium dioxide. In some embodiments though, the second film 50 consists of, or consists essentially of, substoichiometric titanium oxide (TiOx, where x is less than 2). The second film 50 (an entire thickness of which may consist essentially of titania) desirably has (e.g., is deposited at) a physical thickness of less than about 300 angstroms, alternatively less than about 150 angstroms (e.g., between about 30 angstroms and about 150 angstroms), and further alternatively between about 30 angstroms and about 120 angstroms. It has been discovered that the second film 50 when provided at these incredibly small thicknesses, particularly when consisting essentially of titanium oxide and provided in combination with a first film consisting essentially of silicon dioxide at the noted thicknesses, provides unexpected maintenance properties (including exceptional characteristics in terms of taking on limited amounts of dirt and other contaminants and providing easy removal of those contaminants that do accumulate on the coating), while at the same time achieving exceptionally low visible reflection, neutral color, and exceptional durability. Moreover, in preferred embodiments, the second film is a sputtered film deposited at low temperatures (e.g., sputter deposited while maintaining the substrate at less than about 250 degrees Celsius and preferably less than 200 degrees Celsius), and it is especially surprising that a sputtered film of this nature exhibits such exceptional low-maintenance properties.

Certain particular embodiments provide a substrate 10 (e.g., a glass sheet) having a first major surface 12 directly over which is deposited a first film 30 consisting essentially of silica (e.g., SiO2) at a thickness of between about 70 angstroms and about 120 angstroms, wherein a second film 50 consisting essentially of titania (e.g., TiO2) is deposited directly over the first film 30 at a thickness of between about 30 angstroms and about 300 angstroms. In some preferred embodiments of this nature, the first film 30 has a thickness of between about 70 angstroms and about 120 angstroms, perhaps optimally about 100 angstroms, while the second film 50 has a thickness of between about 30 angstroms and about 120 angstroms, perhaps optimally about 100 angstroms.

In a further embodiment, the thickness of the second film 50 is less than 100 angstroms (and optionally less than about 80 angstroms) but greater than about 30 angstroms, while the first film 30 has a thickness of less than about 300 angstroms (and optionally less than about 100 angstroms) but greater than about 30 angstroms. In some cases of this nature, the first film consists essentially of silica while the second film consists essentially of titania.

In the present coating 40, the second film 50 desirably is the outermost film of the coating. Conventional wisdom in the art would suggest that the thin nature of the present coating 40 would not have enough photoactivity to give desirable self-cleaning properties, especially for embodiments where the second film 50 is sputtered, particularly while maintaining the substrate at a low temperature. Surprisingly, though, the present coating is incredibly effective in keeping windows (e.g., monolithic panes or IG units) free of the particular contaminants that build up on windows during the course of routine production. The present coatings also exhibit advantageous water-sheeting properties, while at the same time having exceptional optical properties and durability.

In FIG. 3, the illustrated substrate 10 is provided with two coatings: the low-maintenance coating 40 on the first surface 12 of the substrate and a low-emissivity coating 80 on the second surface 14 of the substrate. It is noted that, alternatively, in an insulating glass unit, the low-emissivity coating 80 may be positioned on the third surface of the insulated glass unit (the third surface is considered the surface of the second, e.g., inboard, pane that is exposed to the between-pane space of the insulated glass unit). The low-emissivity coating 80 is optional. When provided, any desired low-emissivity coating can be used. Suitable examples of a low-emissivity coating are described in U.S. patent application Ser. No. 09/728,435, entitled “Haze-Resistant Transparent Film Stacks”, the entire teachings of which are incorporated herein by reference.

With reference to FIG. 2, the low-maintenance coating 40 is preferably on the “first” surface of a window. This can be appreciated with reference to FIG. 2, which exemplifies embodiments wherein the substrate 10 (which may be a glass pane) is a window pane that is mounted on a window frame 95 (e.g., in an exterior wall 98 of a building 99). In certain applications, the coated first surface (i.e., the surface 12 on which the coating 40 is provided) of such a window will be exposed to an outdoor environment (e.g., such that the coating 40 will be in periodic contact with rain). In another embodiment, the low-maintenance coating is applied to the “fourth” surface of a window (e.g., the #4 surface of a double-pane window unit), optionally in addition to providing the low-maintenance coating 40 on the first surface of the same window. Further, in monolithic windows, the low-maintenance coating 40 can be provided on only the #1 surface, on only the #2 surface, or on both the #1 and #2 surfaces.

The invention also provides methods for producing coated substrates. These methods involve depositing a low-maintenance coating 40 (i.e., by depositing each film 30, 50 of any embodiment described above) upon a substrate 10. As noted above, the low-maintenance coating includes two films. These films 30, 50 can be deposited by a variety of well known coating techniques. In certain particularly preferred embodiments, the coating 40 (or at least the second film 50) is deposited by sputtering, preferably at a low temperature (e.g., while maintaining the substrate at below about 250 degrees Celsius, and more preferably below 200 degrees Celsius). However, other coating techniques, such as chemical vapor deposition (CVD), plasma enhanced chemical vapor deposition, and pyrolytic deposition can be used. Various embodiments of the coating 40 have been described, and the present methods involve depositing any of the described coating embodiments by any thin film deposition method, with sputtering being preferred, though not required, for at least the second film 50 and preferably for the whole coating 40.

Sputtering is well known in the present art. FIG. 3 depicts an exemplary magnetron sputtering chamber 200. Magnetron sputtering chambers and related equipment are commercially available from a variety of sources (e.g., Leybold). Useful magnetron sputtering techniques and equipment are described in U.S. Pat. No. 4,166,018, issued to Chapin, the entire teachings of which are incorporated herein by reference.

In preferred embodiments, the invention provides methods of producing a coated substrate by sputter depositing onto the substrate each film of any above-described coating embodiment. Preferably, the sputtering of the coating 40 (or at least the sputtering of the second film 50) is carried out while maintaining the substrate at a temperature of less than about 250 degrees Celsius, and more preferably less than 200 degrees Celsius (e.g., without heating the substrate).

In favored methods of the invention, the low-maintenance coating 40 is applied to a substrate 10 in a multiple-chamber sputtering line. Sputtering lines are well known in the present art. A typical sputtering line includes a series of sputtering chambers aligned and connected such that a sheet-like substrate can be passed from one chamber to the next by conveying the substrate horizontally over spaced-apart transport rollers 210 in each of the chambers (the rollers form a continuous path of substrate travel P through the sputtering line). The substrate is typically conveyed at speeds of between about 100-500 inches per minute.

In one particular method, the substrate 10 is positioned at the inlet of the sputtering line and conveyed to a desired coat zone. This coat zone is provided with three cathodes that are adapted to deposit the first film 30. In more detail, each of these cathodes comprises a silicon sputtering target. The silicon targets in this coat zone are sputtered in an oxidizing atmosphere to deposit a silicon dioxide film directly upon the first major surface 12 of the substrate. This atmosphere may consist essentially of oxygen (e.g., about 100% O2). Alternatively, this atmosphere may comprise Ar/O2 (e.g., oxygen and up to about 40% argon). A power of about 38 kW is applied to the first cathode, while a power of about 38 kW is applied to the second cathode, and a power of about 38 kW is applied to the third cathode. The substrate 10 is conveyed beneath all three of these targets at a rate of about 200 inches per minute, while sputtering each of these targets at the noted power level, such that a silicon dioxide film is applied at a thickness of about 100 Å. As noted above, each silicon target may include some aluminum or another material to enhance the conductivity of the target.

The thus coated substrate is then conveyed into a subsequent coat zone. In this zone, three cathodes are used to deposit the second film 50. Each of these three cathodes comprises a titanium sputtering target. The titanium targets in this coat zone are sputtered in an oxidizing atmosphere to deposit a titanium dioxide film directly upon the first film 30. This atmosphere may consist essentially of oxygen. Alternatively, this atmosphere may comprise Ar/O2. A power of about 43 kW is applied to the first cathode, a power of about 43 kW is applied to the second cathode, and a power of about 43 kW is applied to the third cathode. The substrate 10 is conveyed beneath all three of these targets at a rate of about 200 inches per minute, while sputtering each of these targets at the noted power level, such that a titanium dioxide film is applied at a thickness of about 100 Å. This titanium dioxide forms the outermost portion (and is exposed) of the coating 40 in the present embodiment.

In the method just described, it is to be appreciated that the second major surface 14 of the substrate 10 may previously have been, or may subsequently be, coated with an optional low-emissivity coating 80. For instance, the coat zones just described for use in depositing the first 30 and second 50 films can be a sputter-up coat zones located toward the end of a sputtering line that includes a relatively large number of preceding sputter-down coat zones in which the optional low-emissivity coating 80 may have been applied. Particularly useful sputter-up/sputter-down methods and equipment are described in U.S. patent application Ser. No. 09/868,542, the entire contents of which are incorporated herein by reference.

While preferred embodiments of the present invention have been described, it should be understood that numerous changes, adaptations, and modifications can be made therein without departing from the spirit of the invention and the scope of the appended claims.

Claims

1. A low-maintenance coating on a glass sheet, the coating comprising a first base film positioned directly over a first major surface of the glass sheet and a second photocatalytic film positioned directly over the first base film, wherein the first base film includes a base film and has a thickness of less than about 100 angstroms, and wherein the second film includes a photocatalytic film and has a thickness of less than about 100 angstroms.

2. The low-maintenance coating of claim 1 wherein the base film is silica.

3. The low-maintenance coating of claim 2 wherein the coated first major surface is in periodic contact with rain.

4. The low-maintenance coating of claim 1 wherein the photocatalytic film is titania.

5. The low-maintenance coating of claim 1 wherein the thickness of the first base film is between about 70 angstroms and about 100 angstroms.

6. The low-maintenance coating of claim 1 wherein the thickness of the second photocatalytic film is between about 30 angstroms and about 120 100 angstroms.

7. The low-maintenance coating of claim 1 wherein the glass sheet is a window pane mounted in a window frame, and wherein the coated first major surface is exposed to an outdoor environment.

8. The low-maintenance coating of claim 1 wherein the first base film consists essentially of silica and the second photocatalytic film consists essentially of titania.

9. The low-maintenance coating of claim 8 wherein the silica is silicon dioxide, and the titania is titanium dioxide or substoichiometric titanium oxide.

10. The low-maintenance coating of claim 1 wherein the first base and second photocatalytic films are both sputtered films.

11. A low-maintenance coating on a glass sheet, the coating comprising a first film positioned directly over a first major surface of the glass sheet and a second film positioned directly over the first film, wherein the first film consists essentially of silica and has a thickness of between about 30 angstroms and about 100 angstroms, and wherein the second film consists essentially of titania and has a thickness of less than 100 angstroms but greater than about 30 angstroms.

12. The low-maintenance coating of claim 11 wherein the second film has a thickness of less than about 80 angstroms.

13. The low-maintenance coating of claim 11 wherein the silica of the first film contains aluminum oxide.

14. The low-maintenance coating of claim 11 wherein the silica of the first film includes an electrically conductive material present in oxidized form.

15. The low-maintenance coating of claim 14 wherein the second film is an outermost film of the coating.

16. The low-maintenance coating of claim 2 wherein the base film further comprises an oxidized electrically conductive material.

17. The low-maintenance coating of claim 16 wherein the electrically conductive material is aluminum.

18. The low-maintenance coating of claim 8 wherein the base film has a thickness of between about 70 angstroms and about 100 angstroms, and the photocatalytic film has a thickness of between about 30 angstroms and about 100 angstroms.

19. A low-maintenance coating on a substrate, the coating comprising a base film extending directly from a first major surface of the substrate to a thickness of less than about 100 angstroms, and a photocatalytic film extending directly from a surface of the base film to a thickness of less than about 100 angstroms.

20. The low-maintenance coating of claim 19 wherein the base film consists essentially of silica and the photocatalytic film consists essentially of titania.

21. The low-maintenance coating of claim 19 wherein the base and photocatalytic films are both sputtered films.

22. The low-maintenance coating of claim 19 wherein the base film extends directly from the first major surface of the substrate to a thickness of between about 70 angstroms and about 100 angstroms, and the photocatalytic film extends directly from the surface of the base film to a thickness of between about 30 angstroms and about 100 angstroms.

Referenced Cited
U.S. Patent Documents
1256818 February 1918 Nile
2808351 October 1952 Colbert
2780553 February 1957 Pawlyk
3505092 April 1970 Ryan
3528906 September 1970 Cash, Jr.
3679291 July 1972 Apfel
3727666 April 1973 Vander Sluis
3829197 August 1974 Thelen
3840451 October 1974 Golyanov
3844924 October 1974 Cunningham
3852098 December 1974 Bloss
3854796 December 1974 Thelen
3911579 October 1975 Lane
3925182 December 1975 Carmichael
3934961 January 27, 1976 Itoh
3968018 July 6, 1976 Lane
3970037 July 20, 1976 Sopko
3990784 November 9, 1976 Gelber
4012119 March 15, 1977 Adams
4029566 June 14, 1977 Brandmair
4045125 August 30, 1977 Farges
4052520 October 4, 1977 Chang
4060660 November 29, 1977 Carlson
4107350 August 15, 1978 Berg
4130672 December 19, 1978 Onoki
4166018 August 28, 1979 Chapin
4194022 March 18, 1980 Gillery
4212663 July 15, 1980 Aslami
4212903 July 15, 1980 Schnell
4214014 July 22, 1980 Hofer
4216259 August 5, 1980 Groth
4238276 December 9, 1980 Kinugawa
4252629 February 24, 1981 Bewer
4261722 April 14, 1981 Novak
4322276 March 30, 1982 Meckel
4331526 May 25, 1982 Kuehnie
4332922 June 1, 1982 Kossmehl
4336119 June 22, 1982 Gillery
4351861 September 28, 1982 Henery
4356073 October 26, 1982 McKelvey
4377613 March 22, 1983 Gordon
4422916 December 27, 1983 McKelvey
4422917 December 27, 1983 Hayfield
4440822 April 3, 1984 Gordon
4465575 August 14, 1984 Love
4466258 August 21, 1984 Sando
4466877 August 21, 1984 McKelvey
4485146 November 27, 1984 Mizuhashi
4486286 December 4, 1984 Lewin
4503125 March 5, 1985 Nelson
4504519 March 12, 1985 Zelez
4556599 December 3, 1985 Sato
4568622 February 4, 1986 Minami
4569738 February 11, 1986 Kieser
4571350 February 18, 1986 Parker
4576864 March 18, 1986 Krautter
4661409 April 28, 1987 Kieser
4663234 May 5, 1987 Bouton
4673475 June 16, 1987 Windischmann
4692428 September 8, 1987 Murrell
4704339 November 3, 1987 Green
4713311 December 15, 1987 Senske
4717622 January 5, 1988 Kurokawa
4725345 February 16, 1988 Sakamoto
4728529 March 1, 1988 Etzkorn
4732454 March 22, 1988 Saito
4737252 April 12, 1988 Hoffman
4769291 September 6, 1988 Belkind
4777090 October 11, 1988 Ovshinsky
4780334 October 25, 1988 Ackerman
4798660 January 17, 1989 Ermer
4814056 March 21, 1989 Welty
4816127 March 28, 1989 Eltouky
4834857 May 30, 1989 Gillery
4838935 June 13, 1989 Dunlop
4849081 July 18, 1989 Ross
4851095 July 25, 1989 Scobey
4854670 August 8, 1989 Mellor
4859493 August 22, 1989 Lemelson
4861680 August 29, 1989 Meyer
4882827 November 28, 1989 Kusumi
4883574 November 28, 1989 Dos Santos
4894133 January 16, 1990 Hedgcoth
4902580 February 20, 1990 Gillery
4915977 April 10, 1990 Okamoto
4919778 April 24, 1990 Dietrich
4931213 June 5, 1990 Guajardo
4931315 June 5, 1990 Mellor
4931778 June 5, 1990 Guajardo
4940636 July 10, 1990 Brock
4952430 August 28, 1990 Bowser
4954465 September 4, 1990 Kawashima
4961958 October 9, 1990 Desphandey
4963240 October 16, 1990 Fukasawa
4981568 January 1, 1991 Taranko
4990234 February 5, 1991 Szczyrbowski
4995893 February 26, 1991 Jenkins
4997576 March 5, 1991 Heller
5006248 April 9, 1991 Anderson
5008002 April 16, 1991 Uno
5020288 June 4, 1991 Swensen
5026415 June 25, 1991 Yamamoto
5032421 July 16, 1991 Sarma
5035784 July 30, 1991 Anderson
5047131 September 10, 1991 Wolfe
5071206 December 10, 1991 Hood
5073241 December 17, 1991 Watanabe
5073450 December 17, 1991 Nietering
5073451 December 17, 1991 Iida
5090985 February 25, 1992 Soubeyrand
5104539 April 14, 1992 Anderson
5105310 April 14, 1992 Dickey
5106671 April 21, 1992 Amberger
5107643 April 28, 1992 Swensen
5108574 April 28, 1992 Kirs
5110637 May 5, 1992 Ando
5126218 June 30, 1992 Clarke
RE34035 August 18, 1992 Dimigen
5139633 August 18, 1992 Kashida
5160534 November 3, 1992 Hiraki
5165972 November 24, 1992 Porter
5168003 December 1, 1992 Proscia
5171414 December 15, 1992 Amberger
5176897 January 5, 1993 Lester
5179468 January 12, 1993 Gasloli
5190807 March 2, 1993 Kimock
5194990 March 16, 1993 Boulos
5196400 March 23, 1993 Chen
5201926 April 13, 1993 Szczyrbowski
5209996 May 11, 1993 Kashida
5211759 May 18, 1993 Zimmermann
5234487 August 10, 1993 Wickersham
5245468 September 14, 1993 Demiryont
5254392 October 19, 1993 Burns
5284539 February 8, 1994 McKernan
5286524 February 15, 1994 Slutz
5298048 March 29, 1994 Lingle
5298338 March 29, 1994 Hiraki
5302449 April 12, 1994 Eby
5306547 April 26, 1994 Hood
5306569 April 26, 1994 Hiraki
5318830 June 7, 1994 Takamatsu
5338422 August 16, 1994 Belkind
5342676 August 30, 1994 Zagdoun
5346600 September 13, 1994 Nieh
5354446 October 11, 1994 Kida
5356718 October 18, 1994 Athey
5366764 November 22, 1994 Sunthankar
5378527 January 3, 1995 Nakanishi
5394269 February 28, 1995 Takamatsu
5397050 March 14, 1995 Mueller
5401543 March 28, 1995 O'Neill
5405517 April 11, 1995 Lampkin
5415756 May 16, 1995 Wolfe
5417827 May 23, 1995 Finley
5424130 June 13, 1995 Nakanishi
5453459 September 26, 1995 Roberts
5470527 November 28, 1995 Yamanobe
5470661 November 28, 1995 Bailey
5476713 December 19, 1995 Abiko
5482602 January 9, 1996 Cooper
5496621 March 5, 1996 Makita
5498475 March 12, 1996 Takigawa
5507930 April 16, 1996 Yamashita
5512152 April 30, 1996 Schicht
5513039 April 30, 1996 Lu
5514485 May 7, 1996 Ando
5520996 May 28, 1996 Balian
5525406 June 11, 1996 Goodman
5527755 June 18, 1996 Wenski
5529631 June 25, 1996 Yoshikawa
5552180 September 3, 1996 Finley
5558751 September 24, 1996 Mahler
5563734 October 8, 1996 Wolfe
5569362 October 29, 1996 Lerbet
5569501 October 29, 1996 Bailey
5589280 December 31, 1996 Gibbons
5593784 January 14, 1997 Chinzi
5593786 January 14, 1997 Parker
5594585 January 14, 1997 Komatsu
5595813 January 21, 1997 Ogawa
5595825 January 21, 1997 Guiselin
5597622 January 28, 1997 Zoller
5599422 February 4, 1997 Adams
5605609 February 25, 1997 Ando
5607723 March 4, 1997 Plano et al.
5609924 March 11, 1997 McCurdy
5611899 March 18, 1997 Maass
5616225 April 1, 1997 Sieck
5616532 April 1, 1997 Heller
5618388 April 8, 1997 Seeser
5618590 April 8, 1997 Naruse
5620572 April 15, 1997 Bjornard
5624423 April 29, 1997 Anjur
5624760 April 29, 1997 Collins
5633208 May 27, 1997 Ishikawa
5635287 June 3, 1997 Balian
5643423 July 1, 1997 Kimock
5643432 July 1, 1997 Qiu
5645699 July 8, 1997 Sieck
5645900 July 8, 1997 Ong
5669144 September 23, 1997 Hahn
5674625 October 7, 1997 Takahashi
5674658 October 7, 1997 Burberry
5679431 October 21, 1997 Chen
5679978 October 21, 1997 Kawahara
5683560 November 4, 1997 Szczyrbowski
5683561 November 4, 1997 Hollars
5686372 November 11, 1997 Langford
5698262 December 16, 1997 Soubeyrand
5715103 February 3, 1998 Amano
5719705 February 17, 1998 Machol
5723172 March 3, 1998 Sherman
5724187 March 3, 1998 Varaprasad
5733660 March 31, 1998 Makita
5733669 March 31, 1998 Veyhl
5744215 April 28, 1998 Neuman
5745291 April 28, 1998 Jenkinson
5750265 May 12, 1998 Goodman
5755867 May 26, 1998 Chikuni
5762674 June 9, 1998 Maltby, Jr.
5763087 June 9, 1998 Falabella
5780119 July 14, 1998 Dearnaley
5780149 July 14, 1998 McCurdy
5780380 July 14, 1998 Endoh
5789040 August 4, 1998 Martinu
5811191 September 22, 1998 Neuman
5812405 September 22, 1998 Meredith, Jr.
5814195 September 29, 1998 Lehan
5814196 September 29, 1998 Hollars
5820994 October 13, 1998 Gotoh
5827490 October 27, 1998 Jones
5830252 November 3, 1998 Finley
5830327 November 3, 1998 Kolenkow
5830332 November 3, 1998 Babich
5846613 December 8, 1998 Neuville
5849200 December 15, 1998 Heller
5853866 December 29, 1998 Watanabe
5854169 December 29, 1998 Heller
5854708 December 29, 1998 Komatsu
5863398 January 26, 1999 Kardokus
5866199 February 2, 1999 Swidler
5866260 February 2, 1999 Adams, Jr.
5869187 February 9, 1999 Nakamura
5869808 February 9, 1999 Hyllberg
5871843 February 16, 1999 Yoneda
5873203 February 23, 1999 Thiel
5874701 February 23, 1999 Watanabe
5877391 March 2, 1999 Kanno
5888593 March 30, 1999 Petrmichl
5891556 April 6, 1999 Anderson
5896553 April 20, 1999 Lo
5897957 April 27, 1999 Goodman
5935716 August 10, 1999 McCurdy
5939188 August 17, 1999 Moncur
5939194 August 17, 1999 Hashimoto
5939201 August 17, 1999 Boire
5948538 September 7, 1999 Brochot
5961843 October 5, 1999 Hayakawa
5962115 October 5, 1999 Zmelty
5965246 October 12, 1999 Guiselin
5968328 October 19, 1999 Teschner
5972184 October 26, 1999 Hollars
5981426 November 9, 1999 Langford
5993734 November 30, 1999 Snowman
6013372 January 11, 2000 Hayakawa
6027766 February 22, 2000 Greenberg
6037289 March 14, 2000 Chopin
6040939 March 21, 2000 Demiryont
6045903 April 4, 2000 Seino
6046403 April 4, 2000 Yoshikawa
6054024 April 25, 2000 Toyama
6054227 April 25, 2000 Greenberg
6068914 May 30, 2000 Boire
6071606 June 6, 2000 Yamazaki
6071623 June 6, 2000 Sugawara
6074981 June 13, 2000 Tada
6077482 June 20, 2000 Kanno
6077492 June 20, 2000 Anpo
6090489 July 18, 2000 Hayakawa
6103363 August 15, 2000 Boire
6114043 September 5, 2000 Joret
6120747 September 19, 2000 Sugishima
6124044 September 26, 2000 Swidler
6139803 October 31, 2000 Watanabe
6139968 October 31, 2000 Knapp
6153067 November 28, 2000 Maishev
6154311 November 28, 2000 Simmons
6156171 December 5, 2000 Hollars
6156409 December 5, 2000 Doushita
6165256 December 26, 2000 Hayakawa
6165598 December 26, 2000 Nelson
6165616 December 26, 2000 Lemelson
6171659 January 9, 2001 Vanden Brande
6179971 January 30, 2001 Kittrell
6179972 January 30, 2001 Kittrell
6191062 February 20, 2001 Hayakawa
6193378 February 27, 2001 Tonar
6193856 February 27, 2001 Kida
6194346 February 27, 2001 Tada
6197101 March 6, 2001 Matsumura
6210750 April 3, 2001 Cho
6210779 April 3, 2001 Watanabe
6228480 May 8, 2001 Kimura
6228502 May 8, 2001 Saitoh
6238738 May 29, 2001 McCurdy
6242752 June 5, 2001 Soma
6248397 June 19, 2001 Ye
6261693 July 17, 2001 Veerasamy
6270633 August 7, 2001 Onaka
6274244 August 14, 2001 Finley
6299981 October 9, 2001 Azzopardi
6319326 November 20, 2001 Koh
6326079 December 4, 2001 Philippe
6329060 December 11, 2001 Barkac
6329925 December 11, 2001 Skiver
6333084 December 25, 2001 Woodard
6334938 January 1, 2002 Kida
6335479 January 1, 2002 Yamada
6336998 January 8, 2002 Wang
6337124 January 8, 2002 Anderson
6346174 February 12, 2002 Finley
6350397 February 26, 2002 Heikkila
6352755 March 5, 2002 Finley
6354109 March 12, 2002 Boire
6362121 March 26, 2002 Chopin
6365010 April 2, 2002 Hollars
6365014 April 2, 2002 Finley
6368664 April 9, 2002 Veerasamy
6368668 April 9, 2002 Kobayashi
6379746 April 30, 2002 Birch
6379776 April 30, 2002 Tada
6387844 May 14, 2002 Fujishima
6403686 June 11, 2002 Pickett
6403689 June 11, 2002 Pickett
6413581 July 2, 2002 Greenberg
6414213 July 2, 2002 Ohmori
6419800 July 16, 2002 Anzaki
6425670 July 30, 2002 Komatsu
6428172 August 6, 2002 Hutzel
6436542 August 20, 2002 Ogino
6440278 August 27, 2002 Kida
6447123 September 10, 2002 Tonar
6451178 September 17, 2002 Szczyrbowski
6461686 October 8, 2002 Vanderstraeten
6464951 October 15, 2002 Kittrell
6465088 October 15, 2002 Talpaert
6468402 October 22, 2002 Vanderstraeten
6468403 October 22, 2002 Shimizu
6468428 October 22, 2002 Nishii
6488824 December 3, 2002 Hollars
6500690 December 31, 2002 Yamagishi
6501387 December 31, 2002 Skiver
6511587 January 28, 2003 Vanderstraeten
6570709 May 27, 2003 Katayama
6576344 June 10, 2003 Doushita
6582839 June 24, 2003 Yamamoto
6596664 July 22, 2003 Kittrell
6635155 October 21, 2003 Miyamura
6660365 December 9, 2003 Krisko
6673738 January 6, 2004 Ueda
6677063 January 13, 2004 Finley
6679978 January 20, 2004 Johnson
6680135 January 20, 2004 Boire
6682773 January 27, 2004 Medwick
6716323 April 6, 2004 Siddle
6720066 April 13, 2004 Talpaert
6722159 April 20, 2004 Greenberg
6730630 May 4, 2004 Okusako
6733889 May 11, 2004 Varanasi
6743343 June 1, 2004 Kida
6743749 June 1, 2004 Morikawa
6761984 July 13, 2004 Anzaki
6770321 August 3, 2004 Hukari
6777030 August 17, 2004 Veerasamy
6777091 August 17, 2004 Kijima
6781738 August 24, 2004 Kikuchi
6787199 September 7, 2004 Anpo
6789906 September 14, 2004 Tonar
6794065 September 21, 2004 Morikawa
6800182 October 5, 2004 Mitsui
6800183 October 5, 2004 Takahashi
6800354 October 5, 2004 Baumann
6804048 October 12, 2004 MacQuart
6811856 November 2, 2004 Nun
6818309 November 16, 2004 Talpaert
6829084 December 7, 2004 Takaki
6830785 December 14, 2004 Hayakawa
6833089 December 21, 2004 Kawahara
6835688 December 28, 2004 Morikawa
6840061 January 11, 2005 Hurst
6846556 January 25, 2005 Boire
6869644 March 22, 2005 Buhay
6870657 March 22, 2005 Fitzmaurice
6872441 March 29, 2005 Baumann
6875319 April 5, 2005 Nadaud
6878242 April 12, 2005 Wang
6878450 April 12, 2005 Anpo
6881701 April 19, 2005 Jacobs
6890656 May 10, 2005 Iacovangelo
6908698 June 21, 2005 Yoshida
6908881 June 21, 2005 Sugihara
6916542 July 12, 2005 Buhay
6921579 July 26, 2005 O'Ohaughnessy
6929862 August 16, 2005 Hurst
6939611 September 6, 2005 Fujishima
6952299 October 4, 2005 Fukazawa
6954240 October 11, 2005 Hamamoto
6962759 November 8, 2005 Buhay
6964731 November 15, 2005 Krisko
6974629 December 13, 2005 Krisko
6997570 February 14, 2006 Nakaho
7005188 February 28, 2006 Anderson
7005189 February 28, 2006 Tachibana
7011691 March 14, 2006 Abe
7022416 April 4, 2006 Teranishi
7049002 May 23, 2006 Greenberg
7052585 May 30, 2006 Veerasamy
7060643 June 13, 2006 Sanbayashi
7096692 August 29, 2006 Greenberg
7118936 October 10, 2006 Kobayashi
7138181 November 21, 2006 McCurdy
7157840 January 2, 2007 Fujishima
7175911 February 13, 2007 Zhou
7179527 February 20, 2007 Sato
7195821 March 27, 2007 Tixhon
7198699 April 3, 2007 Thomsen
7211513 May 1, 2007 Remington, Jr.
7211543 May 1, 2007 Nakabayashi
7223523 May 29, 2007 Boykin
7232615 June 19, 2007 Buhay
7255831 August 14, 2007 Wei
7261942 August 28, 2007 Andrews
7264741 September 4, 2007 Hartig
7294365 November 13, 2007 Hayakawa
7294404 November 13, 2007 Krisko
7300634 November 27, 2007 Yaniv
7309405 December 18, 2007 Cho
7309664 December 18, 2007 Marzolin
7311961 December 25, 2007 Finley
7320827 January 22, 2008 Fujisawa
7323249 January 29, 2008 Athey
7348054 March 25, 2008 Jacquiod
7354624 April 8, 2008 Millero
7361963 April 22, 2008 Ikadai
7387839 June 17, 2008 Gueneau
7534466 May 19, 2009 Hartig
7604865 October 20, 2009 Krisko
7713632 May 11, 2010 Krisko
20010007715 July 12, 2001 Toyoshima
20010016262 August 23, 2001 Toyoshima
20010030808 October 18, 2001 Komatsu
20020012779 January 31, 2002 Miyashita
20020014634 February 7, 2002 Koyama
20020016250 February 7, 2002 Hayakawa
20020028361 March 7, 2002 Boire
20020045073 April 18, 2002 Finley
20020046945 April 25, 2002 Hosokawa
20020071956 June 13, 2002 Boire
20020102352 August 1, 2002 Hartig
20020110638 August 15, 2002 Boire
20020119307 August 29, 2002 Boire
20020155265 October 24, 2002 Choi
20020155299 October 24, 2002 Harris
20020172775 November 21, 2002 Buhay
20020189938 December 19, 2002 Baldwin
20030038028 February 27, 2003 Schultheis
20030039843 February 27, 2003 Johnson
20030043464 March 6, 2003 Dannenberg
20030048538 March 13, 2003 Tonar
20030054177 March 20, 2003 Jin
20030064231 April 3, 2003 Hurst
20030096701 May 22, 2003 Fujishima
20030143437 July 31, 2003 Ohtsu
20030152780 August 14, 2003 Baumann
20030180547 September 25, 2003 Buhay
20030186089 October 2, 2003 Kikuchi
20030207028 November 6, 2003 Boire
20030215647 November 20, 2003 Yoshida
20030224620 December 4, 2003 Kools
20030235695 December 25, 2003 Greenberg
20030235720 December 25, 2003 Athey
20040005466 January 8, 2004 Arai
20040009356 January 15, 2004 Medwick
20040020761 February 5, 2004 Thomsen
20040032655 February 19, 2004 Kikuchi
20040043260 March 4, 2004 Nadaud
20040063320 April 1, 2004 Hollars
20040069623 April 15, 2004 Vanderstraeten
20040115362 June 17, 2004 Hartig
20040140198 July 22, 2004 Cho
20040146721 July 29, 2004 Hartig
20040149307 August 5, 2004 Hartig
20040163945 August 26, 2004 Hartig
20040179978 September 16, 2004 Kobayashi
20040180216 September 16, 2004 Veerasamy
20040180220 September 16, 2004 Gueneau
20040196580 October 7, 2004 Nakaho
20040202890 October 14, 2004 Kutilek
20040206024 October 21, 2004 Graf
20040214010 October 28, 2004 Murata
20040216487 November 4, 2004 Boire
20040219348 November 4, 2004 Jacquiod
20040241040 December 2, 2004 Wei
20040241490 December 2, 2004 Finley
20040247901 December 9, 2004 Suzuki
20040248725 December 9, 2004 Hiraoka
20040253382 December 16, 2004 De Bosscher
20040253471 December 16, 2004 Thiel
20050003672 January 6, 2005 Kools
20050016835 January 27, 2005 Krisko
20050019505 January 27, 2005 Hamamoto
20050019700 January 27, 2005 Hayakawa
20050020444 January 27, 2005 Hiraoka
20050025982 February 3, 2005 Krisko
20050031876 February 10, 2005 Lu
20050042375 February 24, 2005 Minami
20050044894 March 3, 2005 Nelson
20050051422 March 10, 2005 Rietzel
20050084688 April 21, 2005 Garrec
20050106397 May 19, 2005 Krisko
20050137084 June 23, 2005 Krisko
20050191505 September 1, 2005 Akarsu
20050191522 September 1, 2005 Anzaki
20050221098 October 6, 2005 Azzopardi
20050227008 October 13, 2005 Okada
20050233893 October 20, 2005 Sakatani
20050233899 October 20, 2005 Anzaki
20050238861 October 27, 2005 Buhay
20050244678 November 3, 2005 Arfsten
20050245382 November 3, 2005 Iwahashi
20050245383 November 3, 2005 Iwahashi
20050247555 November 10, 2005 Thiel
20050248824 November 10, 2005 Fukazawa
20050252108 November 17, 2005 Sanderson
20050258030 November 24, 2005 Finley
20050266248 December 1, 2005 Millero
20050272590 December 8, 2005 Iwahashi
20060003545 January 5, 2006 Veerasamy
20060011945 January 19, 2006 Spitzer-Keller
20060014027 January 19, 2006 Oudard
20060014050 January 19, 2006 Gueneau
20060019104 January 26, 2006 Hurst
20060029813 February 9, 2006 Kutilek
20060031681 February 9, 2006 Smith
20060032739 February 16, 2006 Ikeda
20060051597 March 9, 2006 Anzaki
20060055513 March 16, 2006 French
20060057298 March 16, 2006 Krisko
20060057401 March 16, 2006 Krisko
20060070869 April 6, 2006 Krisko
20060090996 May 4, 2006 Yaniv
20060102465 May 18, 2006 Blondeel
20060105103 May 18, 2006 Hartig
20060107599 May 25, 2006 Luten
20060110605 May 25, 2006 Luten
20060118406 June 8, 2006 Delahoy
20060121315 June 8, 2006 Myli
20060127604 June 15, 2006 Ikadai
20060134322 June 22, 2006 Harris
20060134436 June 22, 2006 Maschwitz
20060141290 June 29, 2006 Sheel
20060152832 July 13, 2006 Aumercier
20060159906 July 20, 2006 Messere
20060165996 July 27, 2006 Veerasamy
20060194066 August 31, 2006 Ye
20060196765 September 7, 2006 Cheng
20060201203 September 14, 2006 Labrousse
20060210783 September 21, 2006 Seder
20060210810 September 21, 2006 Harris
20060225999 October 12, 2006 Fukawa
20060228476 October 12, 2006 McCurdy
20060234064 October 19, 2006 Baubet
20060247125 November 2, 2006 Choi
20060263610 November 23, 2006 Greenberg
20060275612 December 7, 2006 Baubet
20070025000 February 1, 2007 Lin
20070029187 February 8, 2007 Krasnov
20070029527 February 8, 2007 Mills
20070030569 February 8, 2007 Lu
20070031593 February 8, 2007 Krasnov
20070031681 February 8, 2007 Anzaki
20070031682 February 8, 2007 Krasnov
20070042893 February 22, 2007 Koike
20070065670 March 22, 2007 Varaprasad
20070077406 April 5, 2007 Jacobs
20070087187 April 19, 2007 Lu
20070092734 April 26, 2007 Durandeau
20070108043 May 17, 2007 Lu
20070109543 May 17, 2007 Hoffman
20070111012 May 17, 2007 Rimmer
20070116966 May 24, 2007 Mellott
20070116967 May 24, 2007 Medwick
20070129248 June 7, 2007 Labrousse
20070134501 June 14, 2007 McMaster
20070137673 June 21, 2007 Boykin
20070148064 June 28, 2007 Labrousse
20070184291 August 9, 2007 Harris
20070196563 August 23, 2007 Wuwen
20070218264 September 20, 2007 Gueneau
20070218265 September 20, 2007 Harris
20070218311 September 20, 2007 O'Shaughnessy
20070224357 September 27, 2007 Buhay
20070231501 October 4, 2007 Finley
20070237968 October 11, 2007 Kijima
20070254163 November 1, 2007 Veerasamy
20070254164 November 1, 2007 Veerasamy
20070264494 November 15, 2007 Krisko
20070275252 November 29, 2007 Krasnov
20070275253 November 29, 2007 Thiel
20080011408 January 17, 2008 Maschwitz
20080014349 January 17, 2008 Otani
20080026161 January 31, 2008 Frings
20080115471 May 22, 2008 Labrousse
20080119352 May 22, 2008 Kitaguchi
20080124460 May 29, 2008 Athey
20080188370 August 7, 2008 Vormberg
Foreign Patent Documents
2290999 May 1998 CA
39 06 453 September 1990 DE
43 13 284 October 1994 DE
19736925 March 1998 DE
19644752 April 1998 DE
19831610 January 1999 DE
10100221 July 2001 DE
10100223 July 2001 DE
0 207 646 January 1987 EP
0 470 379 February 1992 EP
0 470 379 February 1992 EP
0 279 550 April 1993 EP
0 369 581 December 1993 EP
0 574 119 December 1993 EP
0 590 477 April 1994 EP
0 601 928 June 1994 EP
0 611 733 August 1994 EP
0 515 847 February 1995 EP
0 515 847 February 1995 EP
0 636 702 February 1995 EP
0 637 572 February 1995 EP
0 639 655 February 1995 EP
0 657 562 June 1995 EP
0 689 096 December 1995 EP
0 689 096 December 1995 EP
0 689 962 January 1996 EP
0 689 962 January 1996 EP
0 737 513 October 1996 EP
0 328 257 April 1997 EP
0 328 257 April 1997 EP
0 787 696 August 1997 EP
0 820 967 January 1998 EP
0 820 967 January 1998 EP
0 771 766 September 1998 EP
0 870 530 October 1998 EP
0 753 882 November 1998 EP
0 884 288 December 1998 EP
0 799 255 February 1999 EP
0 901 991 March 1999 EP
0 345 045 January 2000 EP
0 838 535 February 2000 EP
0 850 203 January 2001 EP
1 066 878 January 2001 EP
0 850 204 December 2001 EP
1 179 515 February 2002 EP
0 944 557 November 2002 EP
1 254 870 November 2002 EP
0 737 513 September 2003 EP
0 887 104 November 2003 EP
1 046 727 November 2003 EP
1 375 444 January 2004 EP
1 411 386 April 2004 EP
1 074 525 September 2004 EP
1 466 665 October 2004 EP
1 466 665 October 2004 EP
1 500 634 January 2005 EP
1 518 836 March 2005 EP
1 640 149 March 2006 EP
0 816 466 May 2006 EP
1 506 143 May 2006 EP
2699164 February 1995 FR
2738812 March 1997 FR
2738813 March 1997 FR
2738836 March 1997 FR
2800731 May 2001 FR
2814094 March 2002 FR
2838734 October 2003 FR
2838735 October 2003 FR
2857885 January 2005 FR
2861385 April 2005 FR
2861386 April 2005 FR
2869897 November 2005 FR
2884147 October 2006 FR
0232680 April 1925 GB
1231280 May 1971 GB
1426906 March 1976 GB
1438462 June 1976 GB
2028376 March 1980 GB
1595061 August 1981 GB
2201428 February 1988 GB
2302102 January 1997 GB
2316687 August 1997 GB
2327428 July 1998 GB
57-140339 August 1982 JP
57-140339 August 1982 JP
60-081048 May 1985 JP
60081048 May 1985 JP
61-091042 May 1986 JP
61-091042 May 1986 JP
62-161945 July 1987 JP
62-161945 July 1987 JP
01-014129 January 1989 JP
01-014129 January 1989 JP
01-118807 May 1989 JP
01-118807 May 1989 JP
3-122274 May 1991 JP
3-122274 May 1991 JP
3-187039 August 1991 JP
3-187039 August 1991 JP
3-193872 August 1991 JP
3-193872 August 1991 JP
4-276066 October 1992 JP
5-214525 August 1993 JP
6-330297 November 1994 JP
7-149545 June 1995 JP
7-149545 June 1995 JP
7-215074 August 1995 JP
7-215074 August 1995 JP
7-233469 September 1995 JP
7-233469 September 1995 JP
7-508491 September 1995 JP
7-508491 September 1995 JP
7-315874 December 1995 JP
7-315874 December 1995 JP
7-315889 December 1995 JP
7-315889 December 1995 JP
8-011631 January 1996 JP
8-011631 January 1996 JP
8-012378 January 1996 JP
8-012378 January 1996 JP
8-109043 April 1996 JP
8-109043 April 1996 JP
8-134638 May 1996 JP
8-134638 May 1996 JP
8-158048 June 1996 JP
8-227006 September 1996 JP
8-227006 September 1996 JP
9-189801 July 1997 JP
9-189801 July 1997 JP
9-202651 August 1997 JP
9-202651 August 1997 JP
9-249967 September 1997 JP
9-249967 September 1997 JP
10-36144 February 1998 JP
10-36144 February 1998 JP
10-048805 February 1998 JP
10-048805 February 1998 JP
10-278165 October 1998 JP
11-095014 April 1999 JP
11-095014 April 1999 JP
11-302038 November 1999 JP
2000-094569 April 2000 JP
2003-311157 November 2003 JP
2005-213585 August 2005 JP
2006-305527 November 2006 JP
WO 87/06626 November 1987 WO
WO 89/10430 November 1989 WO
WO 92/17621 October 1992 WO
WO 92/17621 October 1992 WO
WO 96/25534 August 1996 WO
WO 97/03763 February 1997 WO
WO 97/07066 February 1997 WO
WO 97/07069 February 1997 WO
WO 97/08359 March 1997 WO
WO 97/10185 March 1997 WO
WO 97/10186 March 1997 WO
WO 97/11916 April 1997 WO
WO 97/15499 May 1997 WO
WO 97/25201 July 1997 WO
WO 97/37801 October 1997 WO
WO 97/37946 October 1997 WO
WO 97/42351 November 1997 WO
WO 97/42357 November 1997 WO
WO 98/06675 February 1998 WO
WO 98/23549 June 1998 WO
WO 98/25700 June 1998 WO
WO 99/11896 March 1999 WO
WO 99/44954 September 1999 WO
WO 00/13257 March 2000 WO
WO 00/15571 March 2000 WO
WO 00/27771 May 2000 WO
WO 00/37376 June 2000 WO
WO 00/37377 June 2000 WO
WO 00/40402 July 2000 WO
WO 00/50354 August 2000 WO
0075083 December 2000 WO
WO 00/75083 December 2000 WO
WO 00/75087 December 2000 WO
WO 01/02496 January 2001 WO
WO 01/32578 May 2001 WO
WO 01/68786 September 2001 WO
WO 01/71055 September 2001 WO
WO 03/12540 February 2002 WO
WO 03/012540 February 2002 WO
WO 02/24971 March 2002 WO
WO 02/40417 May 2002 WO
WO 02/49980 June 2002 WO
WO 02/085809 October 2002 WO
WO 03/009061 January 2003 WO
WO 03006393 January 2003 WO
WO 03/050056 June 2003 WO
WO 03/053577 July 2003 WO
WO 03/062166 July 2003 WO
WO 03/068500 August 2003 WO
WO 03/072849 September 2003 WO
WO 03/080530 October 2003 WO
WO 03/087002 October 2003 WO
WO 03/087005 October 2003 WO
WO 03/091471 November 2003 WO
WO 03/093188 November 2003 WO
WO 03/095385 November 2003 WO
WO 03/095695 November 2003 WO
WO 03/097549 November 2003 WO
WO 03/106732 December 2003 WO
WO 2004/013376 February 2004 WO
WO 2004/034105 April 2004 WO
WO 2004061151 July 2004 WO
WO 2004/067464 August 2004 WO
WO 2004/085699 October 2004 WO
WO 2004/085701 October 2004 WO
WO 2004/086104 October 2004 WO
WO 2004/087985 October 2004 WO
WO 2004/089836 October 2004 WO
WO 2004/089838 October 2004 WO
WO 2004/089839 October 2004 WO
WO 2004/092088 October 2004 WO
WO 2004/092089 October 2004 WO
WO 2004/097063 November 2004 WO
WO 2004/108618 December 2004 WO
WO 2004/108619 December 2004 WO
WO 2004/108846 December 2004 WO
WO 2004/113064 December 2004 WO
WO 2005/000758 January 2005 WO
WO 2005/000759 January 2005 WO
WO 2005/005337 January 2005 WO
WO 2005/007286 January 2005 WO
WO 2005/009914 February 2005 WO
WO 2005/012593 February 2005 WO
WO 2005/023723 March 2005 WO
WO 2005/040056 May 2005 WO
WO 2005/040058 May 2005 WO
WO 2005/063646 July 2005 WO
WO 2005/102952 November 2005 WO
WO 2005/102953 November 2005 WO
WO 2005/110937 November 2005 WO
WO 2005/111257 November 2005 WO
WO 2006/004169 January 2006 WO
WO 2006/007062 January 2006 WO
WO 2006/017311 February 2006 WO
WO 2006/017349 February 2006 WO
WO 2006/019995 February 2006 WO
WO 2006/020477 February 2006 WO
WO 2006/028729 March 2006 WO
WO 2006/036605 April 2006 WO
WO 2006/054954 May 2006 WO
WO 2006/055513 May 2006 WO
WO 2006/057830 June 2006 WO
WO 2006/062902 June 2006 WO
WO 2006/064059 June 2006 WO
WO 2006/064060 June 2006 WO
WO 2006/066101 June 2006 WO
WO 2006/077839 July 2006 WO
WO 2006/089964 August 2006 WO
WO 2006/101994 September 2006 WO
WO 2006/108985 October 2006 WO
WO 2006/117345 November 2006 WO
WO 2006/134335 December 2006 WO
WO 2007/016127 February 2007 WO
WO 2007/018974 February 2007 WO
WO 2007/018975 February 2007 WO
WO 2007/045805 April 2007 WO
WO 2007/080428 July 2007 WO
WO 2007/092511 August 2007 WO
WO 2007/093823 August 2007 WO
WO 2007/096461 August 2007 WO
WO 2007/110482 October 2007 WO
WO 2007/121211 October 2007 WO
WO 2007/121215 October 2007 WO
WO 2007/127060 November 2007 WO
WO 2007/130140 November 2007 WO
Other references
  • Anderson et al., “An Improved Photocatalyst of TiO2/SiO2 prepared by a Sol-Gel Synthesis”, J. Phys. Chem., 1995, 99, 9882-9885.
  • Anderson et al., “Improved Photocatalytic Activity and Characterization of Mixed TiO2/SiO2 and TiO2/Al2O3 Materials”, J. Phys. Chem., 1997, 101, 2611-2616.
  • Ang et al., “Deposition of high stability thin film ternary alloy resistors by sputtering,” In: International conf. On Vacuum Metallurgy, 4th, Tokyo, Japan Jun. 4-8, 1973.
  • U.S. Appl. No. 11/273,979 Non Final Office Action mailed Jun. 16, 2008, 9 pgs.
  • U.S. Appl. No. 11/273,979 Response to Non Final Office Action filed Dec. 16, 2008, 15 pgs.
  • Bell et al., “Electrochromism in sol-gel deposited TiO2 films,” Proceedings SPIE—The International Society for Optical Engineering, vol. 2255, Apr. 18-22, 1994.
  • Brat et al., “The Influence of Tungsten-10Wt% Titanium Sputtering Target Purity and Density on VLSI Applications,” 2nd ASM International™ Electronic Materials and Processing Congress (Apr. 24-28, 1989, Philadelphia, PA).
  • Chen Wen-mei et al, “The Effect of SiO2 Additive on Super-hydrophilic Property of TiO2-SiO2 Thin Film by Sol-gel Method”, Journal of Wuhan University of Technology-Mater. Sci. Ed. (Sep. 2001), vol. 16, No. 3, 30-33.
  • Creighton, “Non-Selective Tungsten CVD Using Tungsten Hezxacarbonyl,” Sandia National Laboratories, Albuquerque, NM, 1987.
  • de Tacconi et al., “Nanoporous TiO2 and WO3 Films by Anodization of Titanium and Tungsten Substrates: Influence of process Variables on Morphology and Photoelectrochemical Response,” J. Phys. Chem B 2006, 110, pp. 25347-25355.
  • Derwent Abstract 007612002 (Abstract of JP 879697), (1988).
  • Diesburg et al., “Low Mobile Ion Contamination From Sputtered High Purity Tungsten,” 12th International Plansee Seminar, 1973, 1989, pp. 371-378.
  • Enesca et al., “Novel Approach of TiO2/WO3 for Water Splitting,” 20th European photovoltaic Solar Energy Conference, Jun. 6-10, 2005, pp. 262-265.
  • Gao et al., “Great Enhancement of Photocatalytic Activity of Nitrogen-Doped Titania by Coupling with Tungsten Ozxide,” J. Phys. Chem B 2006, 110, pp. 14391-14397.
  • Göttsche et al., “Electrochromic mixed Wo3—TiO2 thin films produced by sputtering and the sol-gel technique: a comparison,” Solar Energy Materials and Solar Cells 31 (1993) pp. 415-428.
  • Guan et al, “Enhanced effect and mechanism of SiO2 addition in super-hydrophilic property of TiO2 films” Surf. And Coating Tech 173 (2003) pp. 219-223.
  • Guan, “Hydrophilic property of TiO2/SiO2 mixing films” Trans. Nonferrous Met. Soc. China (2004), vol. 14, No. 2, pp. 251-254.
  • Guan, “Relationship between photocatalytic activity, hydrophilicity and self-cleaning effect of TiO2/SiO2 films” Surf. And Coating Tech 191 (2005) pp. 155-160.
  • Gusev et al., “Sputtering of tungsten, tungsten oxide, and tungsten—carbon mixed layers by deuterium ions in the threshold energy region,” Tech Phys. 44 (9), Sep. 1999, pp. 1123-1127.
  • Hamelmann et al., “Metal oxide/silicon oxide multilayer with smooth interfaces produced by in situ controlled plasma-enhanced MOCVD,” Thin Solid Films 358 (2000), pp. 90-93.
  • Hashimoto et al., “Lifetime of Electrochromism of AmorphousWO3-TiO2 thin Films,” J. Electrochem. Soc., vol. 138, No. 8, Aug. 1991, pp. 2403-2408.
  • Herrera et al., “Synthesis, characterization, and catalytic function of novel highly dispersed tungsten oxide catalysts on mesoporous silica,” J. Catalysis 239 (2006), pp. 200-211.
  • Higashimoto et al., “Photoelectrochemical properties of hybrid WO3TiO2 electrode. Effect of structures of WO3 on charge separation,” Thin Solid Films 503 (2006), pp. 201-206.
  • Hodgson et al., “Photocatalytic Reactor Systems with Tungsten Oxide-Modified Titanium Dioxide for Indoor Air Applications,” 11th Conference on TiO2 Photocatalysis: fundamentals & Applications (Sep. 25-28, 2006, Pittsburgh, PA).
  • Ingo et al., “XPS studies of SiO2-TiO2 powders prepared by sol-gel process”, Appl. Surf. Sci. 1993, 70/71A, pp. 230-234.
  • Irie et al., “Interfacial structure dependence of layered TiO2/Wo3 thin films on the photoinduced hydrophilic property,” Vacuum 74 (2004), pp. 625-629.
  • Jossen et al., “Thermal stability and catalytic activity of flame-made silica-vanadia-tungsten oxide-titania,”, App. Catalysis B: Environmental 69 (2007), pp. 181-188.
  • Kanou, “Application of High Purity W for VLSI Sputtering Targets,” 7th International Tungsten Symposium, Sep. 1996, pp. 410-418.
  • Keller et al., “Photocatalytic oxidation of butyl acetate in vapor phase on TiO2, Pt/TiO2 and WO3/TiO2 catalysts,” Journal of Catalysis 215 (2003), pp. 129-138.
  • Kobayashi et al., “V2 O5-WO3/TiO2-SiO2-SO42- catalysts: Influence of active components and supports on activities in the selective catalytic reduction of NO by NH3 and in the oxidation of SO2” App. Cat. B: Enviro 63. (2006), pp. 104-113.
  • Kobayashi et al., “V2O5-WO3/TiO2-SiO2-SO42-catalysts: Influence of active components and supports on activities in the selective catalytic reduction of NO by NH3 and in the oxidation of SO2,” Applied Catalysis B: Environmental 63 (2006), pp. 104-113.
  • Lassaletta et al., “Spectroscopic Characterization of Quantum-Sized TiO2 Supported on Silica: Influence of Size and TiO2-SiO2 Interface Composition”, J. Phys. Chem., 1995, 99, 484-1490.
  • Lo et al., “Influence of Target Structure on Film Stress in WTI Sputtering,” Mat. Res. Soc. Symp. Proc. vol. 505, 1998, pp. 427-432.
  • Manfred Von Ardenne, “The Effects of Physics and Their Applications,” Verlag Harri Deutsch, Thun and Frankfurt am Main, 1997, 4 pages.
  • Manfred Von Ardenne, “The Effects of Physics and Their Applications,” Verlag Harri Deutsch, Thun and Frankfurt am Main, 1997, 7 pages (English Translation).
  • Matthews et al., “An Adsorption Water Purifier with in Situ Photocatalytic Regeneration”, J. Catal. 1988, 113, pp. 549-555.
  • MikroElektronick—High-rate Sputtering System for Two-Sided Coating (HZS-04).
  • Minero et al., “Role of Adsorption in Photocatalyzed Reactions of Organic Molecules in Aqueous of TiO2 Suspensions”, Langmuir, 1992, 113, pp. 481-486.
  • Miyashita et al., “Spectrum response of the vacuum-deposited SiO2/TiO2 multilayer film with improved photo-catalytic activity”, Journal of Materials Science Letters, 2001, 20, 2137-2140.
  • Miyashita, et al., “Enhanced Effect of Vacuum-deposited SiO2 Overlayer on Photo-induced Hydrophilicity of TiO2 Film”, Journal of Materials Science 36 (2001) p. 3877-3884.
  • Miyauchi et al., “A Highly Hydrophilic Thin Film Under 1 μW/cm2 UV Illumination,” Adv. Mater. 2000, 12, pp. 1923-1927.
  • Nakamura, et al., “Hydrophilic property of SiO2/TiO2 double layer films” Photocatalytic Coatings, Panel Session, pp. 345-350.
  • Niwa et al., Ammoxidation of Toluene Over SiO2-Al2O3 ZrO2-SiO2 and TiO2-SiO2, J. Catal. 1981, 69, pp. 69-76.
  • Novotná, et al., “Photocatalytical TiO2/SiO2-PDMS layers on glass” Photocatalytic Coatings, Panel Session, pp. 383-387.
  • Obee et al., “A Kinetic Study of Photocatalytic Oxidation of VOCs on WO3 Coated Titanium Dioxide,” 11th Conference on TiO2 Photocatalysis: fundamentals & Applications (Sep. 25-28, 2006, Pittsburgh, PA).
  • Ohsaki, et al., “Photocatalytic properties of SnO2/TiO2 multilayers” Photocatalytic Coatings, Panel Session, pp. 369-376.
  • Okimura et al., “Characteristics of rutile TiO2 films prepared by R.F. magnetron sputtering at a low temperature,” Thin Solid Films 281-282 (1996) pp. 427-430.
  • Ramana et al., “Structural Stability and Phase Transitions in WO3 Thin Films,” J. Phys Chem B (2006), pp. 10430-10435.
  • Ramirez-Del-Solar et al., “Effect of the Method of Preparation on the Texture of TiO2-SiO2 Gels”, J. Non-Cryst. Solids 1990, 121, pp. 84-89.
  • Richardson et al., “Tungsten-Vanadium Oxide Sputtered Films for Electrochromic Devices,” http://btech.lbl.gov/papers/42381.pdf.
  • Saeki et al., “The Photoelectrochemical Response of TiO2-Wo3 Mixed Oxide Films Prepared by Thermal Oxidation of Titanium Coated with Tungsten,” J. Electrochem. Soc., vol. 143, No. 7, Jul. 1996, pp. 2226-2229.
  • Salvado et al., “TiO2-SiO2 glasses prepared by the alkoxide route”, J. Non-Cryst. Solids 1992, 147/148, pp. 256-261.
  • Satoh et al., “Sol-gel-derived binary silica glasses with high refractive index”, J. Non-Cryst. Solids 1992, 146, pp. 121-128.
  • Schiller et al., “Influence of Deposition Parameters on the Optical and Structural Properties of TiO2 Films Produced by Reactive D.C. Plasmetron Sputtering,” Thin Solid Films 83 (1981), pp. 239-245.
  • Schintlmeister et al., “Optical Coatings (nb2O5, Ta2O5 and WO3) for LAC-applications Obtained by DC Quaslreactive magnetron Sputtering of Ceramic Sputtering Targets,” 46th Annual Technical Conference Proceedings—Soc. Of Vacuum Coaters, May 3-8, 2003, pp. 296-301.
  • Schraml-Marth et al., “Porous silica gels and TiO2-SiO2 mixed oxides prepared via the sol-gel process: characterization by spectroscopic techniques”, J. Non-Cryst. Solids 1992, 143, pp. 93-111.
  • Schwarz et al., Thermal material spraying—an alternative technique for the production of special purpose sputtering targets—abstract.
  • Shen et al., “A new method to prepare tungsten and nitrogen co-doped titanium dioxide and its excellent photocatalytic activities irradiated by visible light,” 11th Conference on TiO2 Photocatalysis: fundamentals & Applications (Sep. 25-28, 2006, Pittsburgh, PA).
  • Shibata, K., et al., “Acidic Properties of Binary Metal Oxides”, Bull. Chem. Soc. Jpn. 1973, 46, pp. 2985-2988.
  • Shiyanovskaya et al., “Biocomponent WO3/TiO2 Films as Photoelectrodes,” J. Electrochemical Soc. 146 (1999), pp. 243-249.
  • Sinel'nikova et al., “Interaction of a Mixture of Oxides of Tungsten and Silicon With Carbon,” Soviet Powder Metallurgy and Metal Ceramics, vol. 29, No. 3(327), Mar. 1990, pp. 234-236.
  • Song et al., “Efficient degradation of organic pollutant with Wox modified nano TiO2 under visible irradiation,” J. of Photochemistry and Photobiology A: Chemistry 181 (2006), pp. 421-428.
  • Staffler et al, “Advanced Coating Technology Based Upon Sputtering Targets Produced by Powder Metallurgy,” Horizons of Powder Metallurgy Part I, Proceedings of the 1986 International Powder Metallurgy Conference and Exhibition, Jul. 7-11, 1986, pp. 219-222.
  • Stakheev, et al., “XPS and XAES Study of TiO2-SiO2 Mixed Oxide System”, J. Phys. Chem. 1993, 97, pp. 5668-5672.
  • Stankova et al., “Thin (0 0 1) tungsten trioxide films grown by laser deposition,” App. Surface Science 247 (2005), pp. 401-405.
  • Stumpp et al, “Manufacturing of Superclean Refractory and Reactive Metals and Alloys in High Vacuum for Advanced Technologies,” 8th ICVM: Special Melting/Refining and Metallurgical Coating Under Vacuum or Controlled Atmosphere, vol. 2, Sep. 1985, pp. 1310-1324.
  • Su et al., “All Solid-State Smart Window of Electrodeposited WO3 and TiO2 Particulate Film With PTREFG Gel Electrolyte,” J. Phys Chem Solids, vol. 59, No. 8, 1998, pp. 1175-1180.
  • “Surface Hardening of Ceramic and Glass Materials,” IBM Technical Disclosure Bulletin, vol. 36, Issue 1 (Jan. 1993), p. 225.
  • “Surface Hardening of Ceramic and Glass Materials,” IBM Technical Disclosure Bulletin, vol. 36, Issue 3 (Mar. 1993), pp. 291-292.
  • Szczyrbowski et al., “Properties of TiO2—Layers Prepared by Medium Frequency and DC Reactive Sputtering,” 1997 Soc. Of Vacuum Coaters (1997), pp. 237-241.
  • Tada et al., “Deactivation of the TiO2 Photocatalyst by Coupling with WO3 and the Electrochemically Assisted High Photocatalytic Activity of WO3,” Langmuir 20 (2004), pp. 4665-4670.
  • Takeuchi, et al., “Preparation of Titanium-Silicon Binary Oxide Thin Film Photocatalysts by an Ionized Cluster Beam Deposition Method. Their Photocatalytic Activity and Photoinduced Super-Hydrophilicity”, J. Phys. Chem. 2003, 107, pp. 14278-14282.
  • Veersamy, et al., “Optical and Electronic Properties of Amorphous Diamond.” Diamond and Related Materials, vol. 2 (1993), pp. 782-787.
  • Wachs et al., “Catalysis science of the solid acidity of model supported tungsten oxide catalysts,” Catalysis Today 116 (2006), pp. 162-168.
  • Wilhartitz et al., “3D-SIMS analysis of ultra high purity molybdenum and tungsten: a characterisation of different manufacturing techniques,” Fresenius J Anal Chem. (1995) 353: pp. 524-532.
  • Yamamoto et al., “Characteristics of Tungsten Gate Devices for MOS VLSI's,” Materials Research Society, 1986, pp. 297-311.
  • Yamamoto et al., “Fabrication of Highly Reliable Tungsten Gate MOS VLSI's,” J. Electrochem. Soc., vol. 133, No. 2, Feb. 1986, pp. 401-407.
  • Yamauchi et al., “Development of W-Ti Binary Alloy Sputtering Target and Study of its sputtering Characteristics,” Nippon Tungsten Review, vol. 22 (1989), pp. 55-72.
  • Yoo et al., “Effects of annealing temperature and method on structural and optical properties of TiO2 films prepared by RF magnetron sputtering at room temperature,” App. Surface Science 253 (2007), pp. 3888-3892.
  • Yoon et al., “Growth kinetics and oxidation behavior of WSi2 coating formed by chemical vapor deposition of Si on W substrate,” J. Alloys and Compounds 420 (2006), pp. 199-206.
  • Yu et al., “The grain size and surface hydroxyl content of super-hydrophilic TiO2-SiO2 composite nanometer thin films” J. Mat. Sci. Lett. (2001) 20, pp. 1745-1748.
  • Zanhai et al., “Preparation of W-Ti Sputtering Targets under Inert Atmosphere,” Chinese Journal of Rare Metals, vol. 30, No. 5, 2006, Abstract.
  • Zanhai et al., “Tungsten-Titanium Targets and Manufacturing Technology,” Chinese Journal of Rare Metals, vol. 30, No. 1, 2006, Abstract.
  • Zemen et al., “Self-cleaning and antifogging effects of TiO2 films prepared by radio frequency magnetron sputtering,” J. Vac. Sci. Technol. A, Mar./Apr. 2002, pp. 388-393.
  • International Preliminary Report on Patentability, dated Oct. 22, 2008 for PCT Application No. PCT/US2007/066685, 7 pages.
  • International Search Report and Written Opinion, dated Sep. 1, 2009 for PCT Application No. PCT/US2008/076183, 10 pages.
  • International Search Report and Written Opinion, dated Apr. 17, 2009 for PCT Application No. PCT/US2008/076157, 18 pages.
  • Hans-Joachim Becker et al., “Herstellung and Eigenschaften von Flachgläsern, die mittels Hochvakuum-zerstäubungsverfahrens beschichtet wurden” Magazine Silikattechnik 36 (1985) Issue 5.
  • Hans-Joachin Gläser, “Beschichtung groβflächiger Substratscheiben durch Kathodenzerstäubung” Glastechnische Berichte 56 (1983) No. 9.
  • Ion-Based Methods for Optical Thin Film Deposition (Journal of Material Science; J.P. Marting, 21 (1986) 1-25).
  • Vakuumbeschichtung 5 Anwendungen Teil II, VDI Verlag 1993, ISBN 3-18-401315-4.
  • English-language abstract for JP 2005-213585 (Konica Minolta).
  • English-language abstract for DE 39 06 453 (Leybold AG).
  • Spectrum Response of the Vacuum-Deposited SiO2/TiO2 Multilayer Film With Improved Photo-Catalytic Activity, Journal of Materials Science Letters 20, 2001, pp. 2137-2140.
  • Abstract—Japanese Patent Publication 4-276066.
  • Abstract—Japanese Patent Publication 5-214525.
  • Abstract—Japanese Patent Publication 6-330297.
  • Derwent Abstract 007612002 (Abstract of JP 879697).
  • Abstract Japanese Patent Publication 08158048A.
Patent History
Patent number: RE43817
Type: Grant
Filed: Oct 12, 2011
Date of Patent: Nov 20, 2012
Assignee: Cardinal CG Company (Eden Prairie, MN)
Inventors: Annette J. Krisko (Sauk City, WI), Kari B. Myli (Sauk City, WI), Gary L. Pfaff (Cazenovia, WI), James E. Brownlee (Northfield, MN)
Primary Examiner: David R Sample
Attorney: Fredrikson & Byron, P.A.
Application Number: 13/271,794