Fiber reinforced thermoplastic sheets with surface coverings

- Hanwha Azdel, Inc.

A composite sheet material in one embodiment includes a porous core layer. The porous core layer includes a thermoplastic polymer, about 20 weight percent to about 80 weight percent of reinforcing fibers based on a total weight of the porous core layer, and an effective amount of a flame retardant agent.

Skip to: Description  ·  Claims  ·  References Cited  · Patent History  ·  Patent History
Description
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Continuation-In-Part application of U.S. patent application Ser. No. 10/810,739, filed Mar. 26, 2004 now U.S. Pat. No. 7,244,501, which is hereby incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION

This invention relates generally to porous fiber-reinforced thermoplastic polymer composite sheets, and more particularly to porous fiber-reinforced thermoplastic polymer composite sheets having flame retardants, smoke suppressants, and/or synergistic compounds along with surface coverings providing for at least one of reduced flame spread, reduced smoke density, reduced heat release, and reduced gas emissions.

Porous fiber-reinforced thermoplastic composite sheets have been described in U.S. Pat. Nos. 4,978,489 and 4,670,331 and are used in numerous and varied applications in the product manufacturing industry because of the ease molding the fiber reinforced thermoplastic sheets into articles. For example, known techniques such as thermo-stamping, compression molding, and thermoforming have been used to successfully form articles from fiber reinforced thermoplastic sheets.

Because of the varied applications, fiber-reinforced thermoplastic sheets are subjected to various performance tests. For example flame spread, smoke density, and gaseous emissions characteristics of the fiber-reinforced thermoplastic sheets are important when the formed articles are used in environments that might be subjected to a flame event, such as a fire. Because of safety concerns, there is a need to improve the flame, smoke and toxicity performance of fiber reinforced thermoplastic sheet products.

BRIEF DESCRIPTION OF THE INVENTION

In one aspect, a composite sheet material is provided that includes a porous core layer. The porous core layer includes a thermoplastic polymer, about 20 weight percent to about 80 weight percent of reinforcing fibers based on a total weight of the porous core layer, and an effective amount of a flame retardant agent.

In another aspect, a method of manufacturing a porous fiber-reinforced thermoplastic sheet is provided. The method includes providing a porous fiber-reinforced thermoplastic sheet having at least one porous core layer including a thermoplastic material, from about 20 weight percent to about 80 weight percent of reinforcing fibers, and an effective amount of a flame retardant agent. The method also includes laminating at least one skin to a surface of the porous fiber-reinforced thermoplastic sheet. Each skin includes at least one of a thermoplastic film, an elastomeric film, a metal foil, a thermosetting coating, an inorganic coating, a fiber based scrim, a non-woven fabric, and a woven fabric, the skin having a limiting oxygen index greater than about 22, as measured per ISO 4589, to enhance at least one of the flame, smoke, heat release and gaseous emissions characteristics of the porous fiber-reinforced thermoplastic sheet.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is cross sectional illustration of an exemplary fiber reinforced thermoplastic sheet in accordance with an embodiment of the present invention.

FIG. 2 is cross sectional illustration of an exemplary fiber reinforced thermoplastic sheet in accordance with another embodiment of the present invention.

FIG. 3 is cross sectional illustration of an exemplary fiber reinforced thermoplastic sheet in accordance with another embodiment of the present invention.

 DETAILED DESCRIPTION OF THE INVENTION

Multi-layered porous fiber-reinforced thermoplastic composite sheets having characteristics of reduced flame spread, reduced smoke density, reduced heat release, and reduced gas emissions are described below in detail. In an exemplary embodiment, the multi-layered porous fiber-reinforced thermoplastic sheets include one or more porous core layers that are formed from one or more thermoplastic materials, about 20 weight percent to about 80 weight percent of fibers dispersed in the thermoplastic material, and an effective amount of a halogen fire retardant agent. At least one surface of the core layer is covered by a skin laminated to the core layer under heat and/or pressure with or without the use of an adhesive or a tie layer. The skin materials are chosen, at least in part, to impart the desired reduction in flame spread, heat release, smoke density, and gaseous emissions of the composite sheet when exposed to a fire event. Also, handling, moldability and end use performance can be improved by laminating two or more porous core layers together having different thermoplastic materials and/or different fibers. Further, skins can be laminated between core layers to affect performance characteristics. Additionally, moldability and formability can be improved by laminating at least one skin to a surface of the core layer where the skin is at least one of a fiber-based scrim, a non-woven fabric and a woven fabric.

Referring to the drawings, FIG. 1 is a cross sectional illustration of an exemplary fiber reinforced thermoplastic composite sheet 10 that includes one porous core layer 12 and skins 14 and 16 laminated to outer surfaces 18 and 20 of core layer 12. In one embodiment, composite sheet 10 has a thickness of about 0.5 millimeters (mm) to about 50 mm and in another embodiment, a thickness of about 0.5 mm to about 25 mm. Also, skins 14 and 16 each have a thickness in one embodiment of about 25 micrometers to about 5 mm, and in another embodiment from about 25 micrometers to about 2.5 mm.

Core layer 12 is formed from a web made up of open cell structures formed by random crossing over of reinforcing fibers held together, at least in part, by one or more thermoplastic resins, where the void content of porous core layer 12 ranges in general between about 5% and about 95% and in particular between about 30% and about 80% of the total volume of core layer 12. In an another embodiment, porous core layer 12 is made up of open cell structures formed by random crossing over of reinforcing fibers held together, at least in part, by one or more thermoplastic resins, where about 40% to about 100% of the cell structure are open and allow the flow of air and gases through. Core layer 12 has a density in one embodiment of about 0.2 gm/cc to about 1.8 gm/cc and in another embodiment about 0.3 gm/cc to about 1.0 gm/cc. Core layer 12 is formed using known manufacturing process, for example, a wet laid process, an air laid process, a dry blend process, a carding and needle process, and other known process that are employed for making non-woven products. Combinations of such manufacturing processes are also useful. Core layer 12 includes about 20% to about 80% by weight fibers having a high tensile modulus of elasticity and an average length of between about 7 and about 200 mm, and about 20% to about 80% by weight of a wholly or substantially unconsolidated fibrous or particulate thermoplastic materials, where the weight percentages are based on the total weight of core layer 12 In another embodiment, core layer includes about 35% to about 55% by weight fibers. The web is heated above the glass transition temperature of the thermoplastic resins on core layer 12 to substantially soften the plastic materials and is passed through one or more consolidation devices, for example nip rollers, calendaring rolls, double belt laminators, indexing presses, multiple daylight presses, autoclaves, and other such devices used for lamination and consolidation of sheets and fabrics so that the plastic material can flow and wet out the fibers. The gap between the consolidating elements in the consolidation devices are set to a dimension less than that of the unconsolidated web and greater than that of the web if it were to be fully consolidated, thus allowing the web to expand and remain substantially permeable after passing through the rollers. In one embodiment, the gap is set to a dimension about 5% to about 10% greater than that of the web if it were to be fully consolidated. A fully consolidated web means a web that is fully compressed and substantially void free. A fully consolidated web would have less than 5% void content and have negligible open cell structure.

A high tensile modulus of elasticity means a tensile modulus of elasticity substantially higher than that of a consolidated sheet which could be formed from the web structure. Fibers falling into this category include metal, metalized inorganic, metalized synthetic, glass, graphite, carbon and ceramic fibers and fibers such as the aramid fibers sold under the trade names Kevlar and Nomex, and generally includes any fiber having a tensile modulus higher than about 10,000 Mega Pascals at room temperature and pressure.

Particulate plastic materials include short plastics fibers which can be included to enhance the cohesion of the web structure during manufacture. Bonding is effected by utilizing the thermal characteristics of the plastic materials within the web structure. The web structure is heated sufficiently to cause the thermoplastic component to fuse at its surfaces to adjacent particles and fibers.

In one embodiment, individual reinforcing fibers should not on he average be shorter than about 7 millimeters, because shorter fibers do not generally provide adequate reinforcement in the ultimate molded article. Also, fibers should not on average be longer than about 200 millimeters since such fibers are difficult to handle in the manufacturing process.

In one embodiment, glass fibers are used, and in order to confer structural strength the fibers have an average diameter between about 7 and about 22 microns. Fibers of diameter less than about 7 microns can easily become airborne and can cause environmental health and safety issues. Fibers of diameter greater than about 22 microns are difficult to handle in manufacturing processes and do not efficiently reinforce the plastics matrix after molding.

In one embodiment, the thermoplastics material is, at least in part, in a particulate form. Suitable thermoplastics include, but are not limited to, polyethylene, polypropylene, polystyrene, acrylonitrylstyrene, butadiene, polyethyleneterephthalate, polybutyleneterephthalate, polybutyleneterachlorate, and polyvinyl chloride, both plasticised and unplasticised, and blends of these materials with each other or other polymeric materials. Other suitable thermoplastics include, but are not limited to, polyarylene ethers, polycarbonates, polyestercarbonates, thermoplastic polyesters, polyetherimides, acrylonitrile-butylacrylate-styrene polymers, amorphous nylon, polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone, polyether sulfone, liquid crystalline polymers, poly(1,4 phenylene) compounds commercially known as PARMAX®, high heat polycarbonate such as Bayer's APEC® PC, high temperature nylon, and silicones, as well as alloys and blends of these materials with each other or other polymeric materials. Preferably, the thermoplastic material has a limited oxygen index (LOI) greater than about 22, as measured in accordance with ISO 4589-2, second edition, Mar. 15, 1996, test method. It is anticipated that any thermoplastics resin can be used which is not chemically attacked by water and which can be sufficiently softened by heat to permit fusing and/or molding without being chemically or thermally decomposed.

In one embodiment, the plastic particles need not be excessively fine, but particles coarser than about 1.5 millimeters are unsatisfactory in that they do not flow sufficiently during the molding process to produce a homogenous structure. The use of larger particles can result in a reduction in the flexural modulus of the material when consolidated. In one embodiment, the plastics particles are not more than about 1 millimeter in size.

Core layer 12 further includes an effective amount of at least one flame retardant agent containing at least one of N, P, As, Sb, Bi, S, Se, Te, Po, F, Cl, Br, I, and At. In one exemplary embodiment, the flame retardant agent is a halogen flame retardant agent. In another embodiment, the flame retardant agent is a halogenated thermoplastic polymer, for example, tetra-bromo bisphenol-A. The amount of the flame retardant in core layer 12 can range in one embodiment from about 2 weight percent to about 13 weight percent, in another embodiment from about 2 weight percent to about 5 weight percent, and in another embodiment, from about 5 weight percent to about 13 weight percent.

Core layer 12 can also include one or more smoke suppressant compositions in the amount of about 0.2 weight percent to about 10 weight percent. Suitable smoke suppressant compositions include, but are not limited to, stannates, zinc borates, zinc molybdate, magnesium silicates, calcium zinc molybdate, calcium silicates, calcium hydroxides, and mixtures thereof.

Core layer 12 can also include a synergist material to increase the efficacy of the halogen flame retardants. Suitable synergist materials include, but are not limited to, sodium trichlorobenzene sulfonate potassium, diphenyl sulfone-3-sulfonate, and mixtures thereof.

Referring to FIG. 1, skins 14 and 16 are formed from materials that can withstand processing temperatures of between about 200° C. and about 425° C. Skins 14 and 16 can be thermoplastic films, elastomeric films, metal foils, thermosetting coating, inorganic coatings, fiber reinforced scrims, and woven or non-woven fabric materials. Any suitable thermoplastic material, including blends of thermoplastic materials, having a LOI greater than about 22, as measured in accordance with ISO 4589-2, second edition, Mar. 15, 1996, test method, can be used for forming the thermoplastic films, for example, poly(ether imide), poly(ether ketone), poly(ether-ether ketone), poly(phenylene sulfide), poly(ether sulfone), poly(amide-imide), poly(aryl sulfone) and combinations thereof. Suitable fibers for forming the scrims include, but are not limited to, glass fibers, aramid fibers, carbon fibers, inorganic fibers, metal fibers, metalized synthetic fibers, metalized inorganic fibers, and combinations thereof. Preferably, the fibers used in forming the scrims have a LOI greater than about 22, as measured in accordance with ISO 4589-2, second edition, Mar. 15, 1996, test method.

In one embodiment, the inorganic coating includes a layer of at least one of gypsum paste, a calcium carbonate paste, a mortar and a concrete. The fiber-based scrim includes a light-weight non-woven covering material manufactured via wet laid, air laid, spunbond, and spunlace processes. The fiber based scrim includes, for example, glass, carbon, polyacrylonitrile, aramid, poly(p-phenylene-benzobisoxazole), poly (ether-imide), poly(phenylene sulfide), etc. The non-woven fabric includes a thermoplastic material, a thermal setting binder, inorganic fibers, metal fibers, metallized inorganic fibers and metallized synthetic fibers.

Skins 14 and 16 are laminated to core layer 12 by any suitable lamination process using heat and/or pressure with or without the use of an adhesive or a tie layer, for example using nip rollers or a lamination machine. Skins 14 and 16 are laminated to core 12 after it has been formed, and in one embodiment, skins 14 and 16 are laminated to core layer 12 before it has been cut into sheets of predetermined size. In another embodiment, skins 14 and 16 are laminated to core layer 12 after it has been cut into sheets. In one embodiment, the temperature of the lamination process is greater than the glass transition temperature of the thermoplastic resins of the skins and core layer, for example, greater than about 100° C. In another embodiment, skins 14 and 16 are bonded to core layer 12 at room temperature using thermal setting adhesives and pressure.

FIG. 2 is a cross sectional illustration of another exemplary fiber reinforced thermoplastic sheet 30 that includes core layers 32 and 34, and skins 36, 38 and 40 laminated to core layers 32 and 34. Particularly, core layer 32 includes a first surface 42 and a second surface 44, and core layer 34 includes a first surface 46 and a second surface 48. Core layers 32 and 34 are arranged so that second surface 44 of core layer 32 is adjacent to first surface 46 of core layer 34. Skin 36 is positioned over first surface 42 of core layer 32, skin 38 is positioned over second surface 48 of core layer 34, and skin 40 is positioned between second surface 44 of core layer 32 and first surface 46 of core layer 34. Core layers 32 and 34, and skins 36, 38, and 40 are laminated together to form fiber reinforced thermoplastic sheet 30.

Core layers 32 and 34, similar to core layer 12 described above, includes about 20% to about 80% by weight fibers having a high tensile modulus of elasticity and about 20% to about 80% by weight of thermoplastics material. The thermoplastic material and/or the fibers of core layer 32 can be the same or different from the thermoplastic material and/or the fibers of core layer 34 depending on the desired properties of sheet 30.

Skins 36, 38, and 40, similar to skins 14 and 16 described above, are formed from materials that can withstand processing temperatures of between about 200° C. and about 425° C. Skins 36, 38, and 40 can be thermoplastic films, fiber reinforced scrims, and woven or non-woven fabric materials. Skins 36, 38, and 40 can be formed from the same materials or can be formed from different materials depending on the desired properties of sheet 30.

In an alternate embodiment, sheet 30 does not include skin 40 laminated between core layers 32 and 34. In further alternate embodiments, only one of the outer surfaces of sheet 30 includes a skin and/or a skin laminated between core layers 32 and 34. In a further alternate embodiment, sheet 30 includes a skin or a skin 40 laminated between core layers 32 and 34 that covers at least a part of second surface 44 of core layer 32 and first surface 46 of core layer 34. FIG. 3 is a cross sectional illustration of another exemplary fiber reinforced thermoplastic sheet 60 that includes porous core layers 62, 64, and 66, and skins 68, 70, 72, and 74 laminated to core layers 62, 64, and 66. Particularly, core layer 62 includes a first surface 76 and a second surface 78, core layer 64 includes a first surface 80 and a second surface 82, and core layer 66 includes a first surface 84 and a second surface 86. Core layers 62, 64, and 66 are arranged so that second surface 78 of core layer 62 is adjacent to first surface 80 of core layer 64, and second surface 82 of core layer 64 is adjacent to first surface 84 of core layer 66. Skin 68 is positioned over first surface 76 of core layer 62, skin 70 is positioned over second surface 86 of core layer 66, skin 72 is positioned between second surface 78 of core layer 62 and first surface 80 of core layer 64, and skin 74 is positioned between second surface 82 of core layer 64 and first surface 84 of core layer 66. Core layers 62, 64, and 66, and skins 68, 70, 72, and 74 are laminated together to form fiber reinforced thermoplastic sheet 60.

Core layers 62, 64, and 66, similar to core layer 12 described above, includes about 20% to about 80% by weight fibers having a high modulus of elasticity and about 20% to about 80% by weight of one or more thermoplastic materials. The thermoplastic material and/or the fibers of each core layer 62, 64, and 66 can be the same or different from the thermoplastic material and/or the fibers of each other core layer depending on the desired properties of sheet 60.

Skins 68, 70, 72, and 74, similar to skins 14 and 16 described above, are formed from materials that can withstand processing temperatures of between about 200° C. and about 425° C. Skins 68, 70, 72, and 74 can be thermoplastic films, fiber reinforced scrims, and woven or non-woven fabric materials. Skins 68, 70, 72, and 74 can be formed from the same materials or can be formed from different materials depending on the desired properties of sheet 60. In an alternate embodiments, sheet 60 includes one or more of skins 68, 70, 72, and 74 but not all four skins. In another embodiment, sheet 60 includes one or more of skins 68, 70, 72, and 74 covering at least a part of the surfaces of core layers 62, 64, and 66.

The porous fiber-reinforced thermoplastic composite sheets described above can be used in, but not limited to, building infrastructure, aircraft, train and naval vessel side wall panels, ceiling panels, cargo liners, office partitions, elevator shaft lining, ceiling tiles, recessed housing for light fixtures and other such applications that are currently made with honeycomb sandwich structures, thermoplastic sheets, and FRP. The composite sheets can be molded into various articles using methods known in the art including, for example, pressure forming, thermal forming, thermal stamping, vacuum forming, compression forming, and autoclaving. The combination of high stiffness to weight ratio, ability to be thermoformed with deep draw sections, end of life recyclability, acoustics and desirable low flame spread index, heat release, smoke density and gas emission properties make the porous fiber-reinforced thermoplastic composite a more desirable product than the products currently being used.

The invention will be further described by reference to the following examples which are presented for the purpose of illustration only and are not intended to limit the scope of the invention. Unless otherwise indicated, all amounts are listed as parts by weight.

Comparative example tests comparing the flame, smoke and gaseous emissions of a control sample designated Sample A and exemplary samples of an embodiment of the invention designated Samples B and C. Sample A is a porous fiber-reinforced sheet formed from a blend of poly(ether-imide), commercially available from General Electric Company under the ULTEM trademark, and bisphenol A polycarbonate resin containing a bromine based fire retardant additive, commercially available from General Electric Company under the LEXAN trademark, the resins blended in weight ratios of 5 percent and 55 percent. The blended resins were dispersed in a porous fiber-reinforced sheet containing about 40 weight percent glass fibers having a nominal fiber diameter of 16 microns and an average length of 12.7 mm. Sample B is the porous fiber-reinforced sheet of Sample A laminated with 76 micron thick poly(ether-imide) films, commercially available from General Electric Company under the ULTEM trademark, in accordance with an embodiment of the present invention. Sample C is the porous fiber-reinforced sheet of Sample A laminated with 27 g/m2 aramid scrims, commercially available from E.I. du Pont de Nemours and Company under the KEVLAR trademark laminated onto the exterior surfaces in accordance with an embodiment of the present invention. Sample D is the porous fiber-reinforced sheet of Sample A laminated with 8 mil thick polypropylene films. Sample D is a comparative sample that contains laminated polypropylene films that have an LOI of 17. The results are presented below in Tables I to II.

Comparative example tests comparing the flame and smoke characteristics of Sample E, a porous fiber-reinforced sheet formed from a blend of poly(ether-imide) and polycarbonate resins in weight ratio of 25 percent each with 50 weight percent glass fibers of 16 micron in diameter and 12.7 mm in length, Sample F, a porous fiber-reinforced sheet formed from a blend of poly(ether-imide) and an eco-friendly flame retardant based polycarbonate resin in a weight ratios of 5 and 55 percent combined with 40 weight percent glass fibers of 16 microns diameter and 12.7 mm length, Sample G, a porous fiber-reinforced sheet formed from a polycarbonate resin with 50 weight percent glass fibers of 16 micron diameter and 12.7 mm length, Sample H, a porous fiber-reinforced sheet formed from polypropylene with 55 weight percent glass fibers of 16 micron diameter and 12.7 mm length, Sample I, a porous fiber-reinforced sheet formed from a polyarylene ether resin with 50 weight percent glass fibers, and Sample J, a porous fiber-reinforced sheet formed from blend of polycarbonate and polybutylene terephthalate combined in a weight ratio of 33 percent and 17 percent each with 50 weight percent glass fibers of 16 micron diameter and 12.7 mm length are presented below in Table IV.

The fiber-reinforced thermoplastic sheets for Samples A-J were made using the wet-laid paper making process described in United Kingdom Patent Nos. 1129757 and 1329409. The fiber-reinforced thermoplastic sheet was further subjected to heat and pressure in a double belt laminator at 325° C. and 2 bar to partially consolidate the sheet and have the resin wet the fibers. Sample B was prepared from the same fiber-reinforced thermoplastic sheet as Sample A, but with a 75 micrometer thick poly(ether-imide) film covering the surfaces using the double belt laminator under the conditions described above. Sample C was prepared from the same fiber-reinforced thermoplastic sheet as Sample A, but with a 27 g/m2 aramid scrim covering the surfaces using the double belt laminator under the conditions described above. Sample D was prepared from the same fiber-reinforced thermoplastic sheet as Sample A, but with a 8 mil thick polypropylene film covering the surfaces using the double belt laminator under the conditions described above.

The flame characteristics were measured using a radiant heat source and an inclined specimen of the sample material in accordance with ASTM method E-162-02A titled Standard Method for Surface Flammability of Materials Using a Radiant Heat Energy Source. A flame spread index was derived from the rate of progress of the flame front and the rate of heat liberation by the material under test. Key criteria are a flame spread index (FSI) and dripping/burning dripping observations. United States and Canadian requirements for passenger bus applications for interior materials are a FSI of 35 or less with no flaming drips. The Underwriters Laboratory (UL) requires that parts greater than 10 square feet should have an FSI of 200 or less to obtain a listing from UL.

The smoke characteristics were measured by exposing test specimens to flaming and non flaming conditions within a closed chamber according to ASTM method E-662-03 titled Standard Test Method for Specific Optical Density of Smoke Generated by Solid Materials. Light transmissions measurements were made and used to calculate specific optical density of the smoke generated during the test time period. Key criteria are an optical density (Ds) of smoke produced by a sample exposed to a radiant furnace or a radiant furnace plus multiple flames. The optical density is plotted versus time for generally 20 minutes. Maximum optical density and time to reach this maximum are important outputs. United States and Canadian Rail regulations and some United States and Canadian Bus guidelines set a maximum Ds of 100 or less at 1.5 minutes, and a maximum Ds of 200 or less at 4 minutes. Global Air regulations sets the Ds at 4 minutes for many large interior applications at 200 or less.

FAA requirements for toxicity and flame were also measured in accordance FAA tests BSS-7239, developed by Boeing Corporation, and FAR 25.853 (a) Appendix F, Part IV (OSU 65/65) Calorimeter.

A large part in an aircraft passenger cabin interior typically will need to meet the ASTM E162 and ASTM E662 described above as well a maximum Ds of 200 at 4 minutes. A difficult test for plastics has traditionally been the OSU 65/65 heat release test. In this test, the test material is exposed to defined radiant heat source, and calorimeter measurements are recorded. Key criteria are an average maximum heat release during the 5 minute test that should not exceed 65 kW/m2, and an average total heat released during the first 2 minutes of the test that should not exceed 65 kW-min/m2.

In the 60 second vertical burn test, the part is exposed to a small-scale open flame for 60 seconds and the key criteria are a burned length of 150 mm or less, an after flame time of 15 seconds or less, and flame time drippings of 3 seconds or less.

TABLE I Test Method Sample A Sample B Sample C Sample D ASTM E-162: Average Flame Spread 10 5.5 6.0 >200 Index Fs Flaming Drips None None None Yes ASTM E-662: Smoke Density Ds at 1.5 9 2 6 6 minutes Smoke Density Ds at 4.0 65 25 133 133 minutes Maximum Smoke Density 315 182 289 289 DsMax FAR 25.853 (a) N/A Appendix F, Part IV: 2 minutes Total Heat 54 kW/m2 45 kW/m2 48 kW/m2 Release Maximum Heat Release 54 KW/m2 41 KW/m2 48 KW/m2 60 Second Vertical Burn: Vertical Burn Time Pass Pass Pass Burn Length 91.4 mm 61.0 mm 53.3 mm

TABLE II BSS-7239: Sample A Sample B Gases (ppm at 4 minutes) (ppm at 4 minutes) HCN 1 1 CO 200 100 NO + NO3 2 2 SO2 <1 <1 HF <1 <1 HCL 2 1

TABLE III Sample Sample Sample Sample Sample Sample Test Method E F G H I J ASTM E-162: Fs 27.5 50 45 245 39 69 Flaming Drips None None None F.D.* None None ASTM E-662: N/A Ds at 1.5 minutes 13 18 21 28 16 Ds at 4.0 minutes 114 100 146 53 79 Max. DsMax 299 388 495 59 294 *F.D. = flaming drips.

The above test results show that the fiber reinforced thermoplastic sheet with poly(ether imide) skins of Sample B and with aramid scrims of Sample C exhibit a reduced flame spread index Fs, a reduced smoke density Ds, reduced heat release, and reduced gaseous emissions over Sample A. As shown in Table 1, Samples B and C exhibit test results that are superior to the test results of Sample A. For example, Samples B and C exhibited a lower flame spread index Fs, 5.5 and 6.0 respectively, than Sample A, which had a Fs of 10. Particularly, Samples B and C exhibited lower test results for the tests run according to ASTM E-162, ASTM E-662, FAR 25.853 (a), and the 60 second vertical burn test. The only anomaly being the 4 minute smoke density D, result of Sample C. Comparative Example D, which included a thermoplastic film having an LOI of only 17, exhibited a flame spread index Fs of greater than 200 and exhibited flaming drips. Further, each of samples E-J exhibit at least one of a flame spread index Fs and a four minute smoke density Ds that are significantly higher than the flame spread index Fs and the four minute smoke density Ds of Samples B and C.

Further comparative example tests comparing the flame, smoke and gaseous emissions of a control sample designated Sample K and exemplary samples of an embodiment of the invention designated Samples L and M. Sample L is similar to Sample A described above. Sample K is similar to Sample G described above and is a porous fiber-reinforced sheet formed from a blend of poly(ether-imide), commercially available from General Electric Company under the ULTEM trademark, and bisphenol A polycarbonate resin free of fire retardant additives, commercially available from General Electric Company under the LEXAN trademark.

Further comparative example tests comparing the flame, smoke and gaseous emissions of a control sample designated Sample K and exemplary samples of an embodiment of the invention designated Samples L and M were made using nominal 16 micron, 12.7 mm long wet chopped glass fibers and a blended mixture of powdered polyetherimide resin, a relatively high flow Bisphenol-A Polycarbonate (BPA-PC) resin with a nominal MFI≧25 g/10 min @300° C./12.kgf, and a random copolymer polycarbonate resin containing Bisphenol-A and Tetra-bromo Bisphenol A (TBBPA) units in the polymer backbone with a nominal 26% Bromine content and MFI≧7 g/10 min @300° C./12.kgf. The powder blending of the polycarbonate resins at different blend ratios allowed for tuning the total bromine content of the resins used in the core web. The core web had an area weight of around 2000±100 grams/m2 and a w/w glass content of around 45%±5%. Sample K was made without the bromine containing resin. The fiber-reinforced thermoplastic sheets for Samples K-M were made using the wet-laid paper making process described in United Kingdom Patent Nos. 1129757 and 1329409. The fiber-reinforced thermoplastic sheets were further subjected to heat and pressure in a double belt laminator at 325° C. and 2 bar to partially consolidate the sheet and have the resin wet the fibers.

TABLE IV Test Method Sample K Sample L Sample M Bromine Content in weight % 0 8.1 9.0 ASTM E-162: Average Flame Spread Index Fs 45 10 6 Flaming Drips None None None ASTM E-662: Smoke Density Ds at 1.5 minutes 18 9 4 Smoke Density Ds at 4.0 minutes 100 165 114 Maximum Smoke Density DsMax 388 315 272

The test results of Samples K-M show that the addition of bromine in Samples L and M reduces the flame spread index F, in comparison to control Sample M. Also shown, is that the addition of bromine in Samples Land M reduces the maximum smoke density D, in comparison to control Sample M.

When introducing elements of the methods and articles described and/or illustrated herein, including any and all embodiment(s) thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements.

While the invention has been described in terms of various specific embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the claims.

Claims

1. A composite sheet material comprising a porous core layer, said core layer comprising:

a web of open celled structures defined by random crossing over of reinforcing fibers held together by a thermoplastic polymer;
said web comprising about 20 weight percent to about 80 weight percent of reinforcing fibers based on a total weight of said porous core layer, and
an effective amount of a flame retardant agent, said flame retardant agent comprising at least one of N, P, As, Sb, Bi, S, Se, Te, Po, F, Cl, Br, I, and At.

2. A composite sheet material in accordance with claim 1 wherein said flame retardant agent comprises a halogenated thermoplastic polymer.

3. A composite sheet material in accordance with claim 2 wherein said halogenated thermoplastic polymer comprises tetrabromo bisphenol-A polycarbonate.

4. A composite sheet material in accordance with claim 2 wherein said core layer comprises about 2.0 weight percent to about 13.0 weight percent bromine.

5. A composite sheet material in accordance with claim 2 wherein said core layer comprises about 2.0 weight percent to about 5.0 weight percent bromine.

6. A composite sheet material in accordance with claim 1 further comprising a smoke suppressant composition, said smoke suppressant composition comprising at least one of stannates, zinc borates, zinc molybdate, magnesium silicates, calcium zinc molybdate, calcium silicates and calcium hydroxides.

7. A composite sheet material in accordance with claim 1 further comprising at least one of sodium trichlorobenzene sulfonate potassium and diphenyl sulfone-3-sulfonate.

8. A composite sheet material in accordance with claim 1 further comprising at least one skin, each said skin covering at least a portion of a surface of said porous core layer, said skin comprising at least one of a thermoplastic film, an elastomeric film, a metal foil, a thermosetting coating, an inorganic coating, a fiber based scrim, a non-woven fabric, and a woven fabric, said skin having a limiting oxygen index greater than about 22, as measured at a predetermined thickness used to cover at least a portion of a surface of said porous core layer per ISO 4589-2, first edition, 1996.

9. A composite sheet material in accordance with claim 8 wherein said thermoplastic film comprises at least one of poly(ether imide), poly(ether ketone), poly(ether-ether ketone), poly(phenylene sulfide), poly(arylene sulfone), poly (ether sulfone), poly(antde-imide) poly(amide-imide), poly(1,4-phenylene), polycarbonate, nylon, and silicone.

10. A composite sheet material in accordance with claim 8 wherein said fiber based scrim comprises at least one of glass fibers, aramid fibers, graphite fibers, carbon fibers, inorganic mineral fibers, metal fibers, metalized synthetic fibers, and metalized inorganic fibers.

11. A composite sheet material in accordance with claim 10 wherein said fiber based scrim comprises at least one of polyacrylonitrile, p-aramid, m-aramid, poly(p-phenylene2,6,benzobisoxazole), poly(ether-imide) and poly(phenylene sulfide).

12. A composite material in accordance with claim 8 wherein said thermal setting coating comprises at least one of unsaturated polyurethartes polyurethanes, vinyl esters, phenolics and epoxies.

13. A composite material in accordance with claim 8 wherein said inorganic coating comprises minerals containing cations selected from Ca, Mg, Ba, Si, Zn, Ti and Al.

14. A composite material in accordance with claim 13 wherein said inorganic coating comprises at least one of gypsum, calcium carbonate and mortar.

15. A composite sheet material in accordance with claim 8 comprising:

a first porous core layer having a first surface and a second surface; and
at least one skin covering at least a portion of at least one of said first and second surface.

16. A composite sheet material in accordance with claim 8 comprising:

a first and a second porous core layer, each said core layer comprising a first and a second surface, said second surface of said first core layer positioned adjacent said first surface of said second core layer; and
at least one skin covering at least a portion of at least one of said first and second surfaces of said first core layer and said first and second surface of said second core layer.

17. A composite sheet material in accordance with claim 16 wherein said first porous core layer comprises at least one of a different thermoplastic material and a different fiber than said second porous core layer.

18. A composite sheet material in accordance with claim 8 comprising:

a first, a second, and a third porous core layer, each said core layer comprising a first and a second surface, said second surface of said first core layer positioned adjacent said first surface of said second core layer, said second surface of said second core layer positioned adjacent said first surface of said third core layer; and
at least one skin covering at least one of said first and second surfaces of said first core layer, said first and second surface of said second core layer, and said first and second surface of said third core layer.

19. A composite sheet material in accordance with claim 18 wherein one of said porous core layers comprises at least one of a different thermoplastic material and a different fiber than at least one of said other layers.

20. A composite sheet material according to claim 1 wherein said thermoplastic polymer comprises at least one of polyethylene, polypropylene, polystyrene, acrylonitryistyrene, butadiene, polyethyleneterephthalate, polybutyleneterephthalate, polybutyleneterachlorate, polyvinyl chloride, polyphenylene ether, polycarbonates, polyestercarbonates, thermoplastic polyesters, polyetherimides, acrylonitrile-butylacrylate-styrene polymers, amorphous nylon, polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone, polyether sulfone, poly(1,4phenylene) compounds, and silicones.

21. A method of manufacturing a porous fiber-reinforced thermoplastic sheet, said method comprising:

providing a porous fiber-reinforced thermoplastic sheet comprising at least one porous core layer comprising a web of open celled structures defined by random crossing over of reinforcing fibers held together by a thermoplastic material, said web comprising from about 20 weight percent to about 80 weight percent fibers, and an effective amount of a flame retardant agent, said flame retardant agent comprising at least one of N, P, As, Sb, Bi, S, Se, Te, Po, F, Cl, Br, I, and At; and
laminating at least one skin to a surface of the porous fiber-reinforced thermoplastic sheet, each skin comprising at least one of a thermoplastic film, an elastomeric film, a metal foil, a thermosetting coating, an inorganic coating, a fiber based scrim, a non-woven fabric, and a woven fabric, the skin having a limiting oxygen index greater than about 22, as measured per ISO 4589-2, first edition, 1996, to enhance at least one of the flame, smoke, heat release and gaseous emissions characteristics of the porous fiber-reinforced thermoplastic sheet.

22. A method in accordance with claim 21 wherein the flame retardant agent comprises a halogenated thermoplastic polymer.

23. A method in accordance with claim 22 wherein the halogenated thermoplastic polymer comprises tetrabromo bisphenol-A polycarbonate.

24. A method in accordance with claim 21 wherein the core layer comprises about 2.0 weight percent to about 13.0 weight percent bromine.

25. A method in accordance with claim 21 wherein the core layer further comprises a smoke suppressant composition, said smoke suppressant composition comprising at least one of stannates, zinc borates, zinc molybdate, magnesium silicates, calcium zinc molybdate, calcium silicates and calcium hydroxides.

26. A method in accordance with claim 21 wherein the core layer further comprises at least one of sodium trichlorobenzene sulfonate potassium and diphenyl sulfone-3-sulfonate.

27. The composite sheet material of claim 1, in which the at least one thermoplastic polymer has a limiting oxygen index greater than about 22, as measured per ISO 4589-2, first edition, 1996.

28. The composite sheet material of claim 1, in which the at least one thermoplastic polymer is a polyetherimide polymer.

29. The composite sheet material of claim 1, in which the at least one thermoplastic polymer is a polycarbonate polymer.

30. The composite sheet material of claim 1, further comprising at least one skin disposed on at least a portion of said porous core layer.

31. The composite sheet material of claim 30, in which said skin comprises glass fibers.

32. A composite sheet material comprising a porous core layer, said porous core layer comprising a web of open celled structures defined by random crossing over of reinforcing fibers held together by a thermoplastic polymer blend, said thermoplastic polymer blend comprising at least two resins at least one of which comprises an effective amount of a flame retardant agent.

33. The composite sheet material of claim 32, in which the thermoplastic polymer blend has a limiting oxygen index greater than about 22, as measured per ISO 4589-2, first edition, 1996.

34. The composite sheet material of claim 32, in which the thermoplastic polymer blend comprises a polyetherimide polymer.

35. The composite sheet material of claim 32, in which the thermoplastic polymer blend comprises a polycarbonate polymer.

36. The composite sheet material of claim 32, further comprising at least one skin disposed on at least a portion of the porous core layer.

37. The composite sheet material of claim 36, in which said skin comprises glass fibers.

38. The composite sheet material of claim 32, further comprising a first skin disposed on at least a portion of a first surface of the porous core layer, and a second skin disposed on at least a portion of a second surface of the porous core layer opposite the first surface of the porous core layer.

39. The composite sheet material of claim 32, in which said web comprises about 20 weight percent to about 80 weight percent of reinforcing fibers based on a total weight of said porous core layer.

40. The composite sheet material of claim 32, in which the thermoplastic polymer blend comprises a halogenated thermoplastic polymer.

41. The composite sheet material of claim 40, in which the halogenated thermoplastic polymer is a polycarbonate polymer comprising bromine.

42. The composite sheet material of claim 32, in which the thermoplastic polymer blend comprises two polymers comprising the same polymer backbone.

43. The composite sheet material of claim 42, in which the two polymers comprising the same polymer backbone are polycarbonate polymers.

Referenced Cited
U.S. Patent Documents
1707008 May 1929 Havemeyer
2815979 December 1957 Seymour
2976577 March 1961 Gould
3022210 February 1962 Phillips
3179782 April 1965 Matvay
3437550 April 1969 Paul
3484223 December 1969 Vanderbilt
3627603 December 1971 Greig
3639157 February 1972 Winckler
3639424 February 1972 Gray
3684645 August 1972 Temple
3713962 January 1973 Ackley
3716449 February 1973 Gatward
3779592 December 1973 Goize
3809420 May 1974 Weller
3849241 November 1974 Butin
3850723 November 1974 Ackley
3853808 December 1974 Sishikawa
3857813 December 1974 Stain
3865661 February 1975 Hata
3871952 March 1975 Robertson
3883333 May 1975 Ackley
4044188 August 23, 1977 Segal
4052241 October 4, 1977 Walter
4098943 July 4, 1978 Degginger
4172293 October 30, 1979 Vistins
4178411 December 11, 1979 Cogswell
4201823 May 6, 1980 Russell
4208069 June 17, 1980 Huber
4211590 July 8, 1980 Steward
4235952 November 25, 1980 Holmes
4248935 February 3, 1981 Temple
4263082 April 21, 1981 Temple
4277531 July 7, 1981 Picone
4278720 July 14, 1981 Shannon
4285767 August 25, 1981 Page
4335176 June 15, 1982 Baumann
4341877 July 27, 1982 Das
4358501 November 9, 1982 Temple
4366204 December 28, 1982 Briggs
4369234 January 18, 1983 Baumann
4379801 April 12, 1983 Weaver
4379802 April 12, 1983 Weaver
4390384 June 28, 1983 Turner
4412854 November 1, 1983 Layden
4413085 November 1, 1983 Temple
4423000 December 27, 1983 Teraoka
4457547 July 3, 1984 Sekiyama
4464432 August 7, 1984 Dost
4469543 September 4, 1984 Segal
4476183 October 9, 1984 Holtrop
4482180 November 13, 1984 Huber
4495238 January 22, 1985 Adiletta
4508499 April 2, 1985 Spengler
4519766 May 28, 1985 Spengler
4529641 July 16, 1985 Holtrop
4543288 September 24, 1985 Radvan
4579774 April 1, 1986 Kuwazuru
4586739 May 6, 1986 Loren
4587278 May 6, 1986 Dotzauer
4612238 September 16, 1986 Della Vecchia
4615717 October 7, 1986 Neubauer
4616866 October 14, 1986 Loren
4634483 January 6, 1987 Spengler
4635984 January 13, 1987 Loren
4637951 January 20, 1987 Gill
4663369 May 5, 1987 Kawai
4670331 June 2, 1987 Radvan
4670343 June 2, 1987 Makino
4671550 June 9, 1987 Molnar
4681798 July 21, 1987 Gill
4692375 September 8, 1987 Neubauer
4694031 September 15, 1987 Morita
4704423 November 3, 1987 Iwanami
4713283 December 15, 1987 Cogswell
4714650 December 22, 1987 Obayashi
4717143 January 5, 1988 Spengler
4734321 March 29, 1988 Radvan
4741945 May 3, 1988 Brant
4749613 June 7, 1988 Yamada
4755575 July 5, 1988 Domeier
4762352 August 9, 1988 Enomoto
4762643 August 9, 1988 Bohrn
4762750 August 9, 1988 Girgis
4767321 August 30, 1988 Chilva
4775725 October 4, 1988 Depasquale
4778722 October 18, 1988 Yamamura
4793802 December 27, 1988 Chilva
4802843 February 7, 1989 Chilva
4804577 February 14, 1989 Hazelton
4828910 May 9, 1989 Haussling
4840832 June 20, 1989 Weinle
4851167 July 25, 1989 Marc
4882229 November 21, 1989 Hwo
4892780 January 9, 1990 Cochran
4913774 April 3, 1990 Goguelin
4923547 May 8, 1990 Yamaji
4924224 May 8, 1990 Suniszek
4925615 May 15, 1990 Willis
4940629 July 10, 1990 Weber
4943607 July 24, 1990 Tanisake
4944843 July 31, 1990 Wallace
4950532 August 21, 1990 Das
4951986 August 28, 1990 Hanafusa
4952448 August 28, 1990 Bullock
4963603 October 16, 1990 Felegi
4978489 December 18, 1990 Radvan
4983247 January 8, 1991 Kim
5002830 March 26, 1991 Gillis
5009747 April 23, 1991 Viazmensky
5030682 July 9, 1991 Nomura
5043368 August 27, 1991 Minnick
5092952 March 3, 1992 Minnick
5093171 March 3, 1992 Sheahan
5098781 March 24, 1992 Minnick
5115077 May 19, 1992 Matsuo
5122398 June 16, 1992 Seiler
5137975 August 11, 1992 Kelusky
5147345 September 15, 1992 Young
5151320 September 29, 1992 Homonoff
5165990 November 24, 1992 Nakano
5175198 December 29, 1992 Minnick
5180628 January 19, 1993 Haardt
5186777 February 16, 1993 Perenon
5188778 February 23, 1993 Jeffs
5219913 June 15, 1993 Tomatsu
5231126 July 27, 1993 Shi et al.
5246538 September 21, 1993 Johnson
5262491 November 16, 1993 Jain
5267827 December 7, 1993 Provan
5269574 December 14, 1993 Bhutani
5288555 February 22, 1994 Exxon
5300360 April 5, 1994 Kocsis
5306739 April 26, 1994 Lucey
5316834 May 31, 1994 Matsuda
5322724 June 21, 1994 Levens
5338059 August 16, 1994 Inoue
5342463 August 30, 1994 Addeo
5344866 September 6, 1994 Hall
5348798 September 20, 1994 Berghuis
5354829 October 11, 1994 Swisher
5376701 December 27, 1994 Chow
5387382 February 7, 1995 Fottinger
5403654 April 4, 1995 Muto
5413661 May 9, 1995 Spengler
5437919 August 1, 1995 Welich
5464585 November 7, 1995 Fitzgibbon
5470658 November 28, 1995 Gasca
5484653 January 16, 1996 Kennedy
5486256 January 23, 1996 Romesberg
5502088 March 26, 1996 Hododi
5503903 April 2, 1996 Bainbridge
5529742 June 25, 1996 Strapazzini
5536556 July 16, 1996 Juriga
5540986 July 30, 1996 Kimura
5549776 August 27, 1996 Juriga
5565259 October 15, 1996 Juriga
5576080 November 19, 1996 Sugimoto
5582906 December 10, 1996 Romesberg
5591289 January 7, 1997 Souders
5614285 March 25, 1997 Gardill
5627226 May 6, 1997 Lustiger
5635129 June 3, 1997 Breezer
5639324 June 17, 1997 Biggs
5641554 June 24, 1997 Koizumi
5643989 July 1, 1997 Van de Grampel
5685560 November 11, 1997 Sugiyama
5709925 January 20, 1998 Spengler
5718791 February 17, 1998 Spengler
5775726 July 7, 1998 Timothy
5780519 July 14, 1998 Imoto
5795015 August 18, 1998 Corpe
5800749 September 1, 1998 Lewit
5800846 September 1, 1998 Hart
5804511 September 8, 1998 Kelman
5817408 October 6, 1998 Orimo
5839752 November 24, 1998 Yamasaki
5840812 November 24, 1998 Schultze
5845929 December 8, 1998 Schlett
5853628 December 29, 1998 Varona
5854149 December 29, 1998 Nagayama
5866051 February 2, 1999 Lin
5879608 March 9, 1999 Lammeck
5883021 March 16, 1999 Beer
5885691 March 23, 1999 Breezer
5888435 March 30, 1999 Mueller
5908524 June 1, 1999 Masui
5910458 June 8, 1999 Beer
5914163 June 22, 1999 Browne
5922626 July 13, 1999 Pelzer
5942321 August 24, 1999 Romesberg
5952089 September 14, 1999 Namura
5972444 October 26, 1999 Patel
5976451 November 2, 1999 Skaja
5979931 November 9, 1999 Totani
5981046 November 9, 1999 Masui
5985429 November 16, 1999 Plummer
6007898 December 28, 1999 Kim
6018927 February 1, 2000 Major
6042140 March 28, 2000 Blazaitis
6042141 March 28, 2000 Welch
6042765 March 28, 2000 Sugahara
6062635 May 16, 2000 Learman
6099055 August 8, 2000 Hirota
6120090 September 19, 2000 Van Ert
6146578 November 14, 2000 Van Ert
6150287 November 21, 2000 Boyd
6203304 March 20, 2001 Lopez Tonazzi
6214456 April 10, 2001 Boyd
6238518 May 29, 2001 Rokman
6286879 September 11, 2001 Haque
6287678 September 11, 2001 Spengler
6293045 September 25, 2001 Morgan
6322658 November 27, 2001 Byma
6365533 April 2, 2002 Horner
6368702 April 9, 2002 Erickson
6369157 April 9, 2002 Winckler
6420047 July 16, 2002 Winckler
6423933 July 23, 2002 Nicholas
6436854 August 20, 2002 North
6503372 January 7, 2003 Rokman
6565712 May 20, 2003 Lindenfelser
6572723 June 3, 2003 Tilton
6596389 July 22, 2003 Hallett
6610904 August 26, 2003 Thomas
6631785 October 14, 2003 Khambete
6639009 October 28, 2003 Winckler
6649248 November 18, 2003 Schneider
6652021 November 25, 2003 Dykman
6696164 February 24, 2004 Clifford
6702914 March 9, 2004 North
6762138 July 13, 2004 Ferreira
6774068 August 10, 2004 Sung-Ho
6808576 October 26, 2004 Shimizu
6815053 November 9, 2004 Inoue
6841028 January 11, 2005 Tsukada
6994914 February 7, 2006 Winckler
7047668 May 23, 2006 Burris
7060217 June 13, 2006 Dunton
7157034 January 2, 2007 Bristow
7236348 June 26, 2007 Asano
7244501 July 17, 2007 Raghavendran
7255391 August 14, 2007 Bristow
7318498 January 15, 2008 Woodman
7329457 February 12, 2008 Renard
7378143 May 27, 2008 Schneider
7431980 October 7, 2008 Woodman
7435469 October 14, 2008 Maupetit
7482048 January 27, 2009 Boutghrit
7629278 December 8, 2009 Sabbagh
7682697 March 23, 2010 Raghavendran
7695815 April 13, 2010 Agarwal
7759267 July 20, 2010 Conover
7845265 December 7, 2010 Park
7922854 April 12, 2011 Sabbagh
7972685 July 5, 2011 Raghavendran
8021746 September 20, 2011 Chen
20010036788 November 1, 2001 Sandoe
20010037854 November 8, 2001 Byma
20020009936 January 24, 2002 North
20020017805 February 14, 2002 Carroll
20030008592 January 9, 2003 Block
20030134101 July 17, 2003 Kikuchi
20030138594 July 24, 2003 Lobovsky
20030164218 September 4, 2003 Brahm
20040002274 January 1, 2004 Tilton
20040081797 April 29, 2004 Simmons
20040112501 June 17, 2004 Dittmar
20040216949 November 4, 2004 Tompson
20040231915 November 25, 2004 Thompson
20040235377 November 25, 2004 Byma
20040254299 December 16, 2004 Lee
20050032452 February 10, 2005 Helwig
20050095415 May 5, 2005 Raghavendran
20050153120 July 14, 2005 Birrell
20050215698 September 29, 2005 Raghavendran
20050217932 October 6, 2005 Woodman
20060099393 May 11, 2006 Woodman
20060182947 August 17, 2006 Jerri
20060240242 October 26, 2006 Raghavendran
20060244170 November 2, 2006 Brentup
20070008869 January 11, 2007 Tsukamoto
20070196637 August 23, 2007 Good
20070238378 October 11, 2007 Conover
20070269644 November 22, 2007 Harper
20070269645 November 22, 2007 Raghavendran et al.
20070269654 November 22, 2007 Raghavendran
20080001429 January 3, 2008 Willis
20080008869 January 10, 2008 Good
20080032094 February 7, 2008 Raghavendran
20080070019 March 20, 2008 Good
20080233342 September 25, 2008 Birrell
20090011210 January 8, 2009 Gao
20090053458 February 26, 2009 Birrell
20090155522 June 18, 2009 Raghavendran
20100021718 January 28, 2010 Vos
Foreign Patent Documents
661949 August 1993 AU
842919 May 1970 CA
938391 December 1973 CA
1266540 March 1990 CA
2054975 November 1991 CA
2129453 August 1993 CA
1335740 May 1995 CA
1188279 March 1965 DE
2231637 February 1973 DE
2650096 October 1976 DE
2527781 December 1976 DE
3125987 January 1983 DE
9214896 December 1992 DE
69207432 May 1996 DE
19520477 December 1996 DE
20102194 May 2001 DE
20106096 June 2001 DE
10160442 August 2002 DE
20106096 June 2006 DE
0001176 March 1979 EP
0056703 July 1982 EP
011104555 April 1984 EP
0148760 July 1985 EP
0148763 July 1985 EP
0150931 August 1985 EP
0177961 April 1986 EP
0255316 February 1988 EP
0278409 August 1988 EP
0312414 April 1989 EP
0381857 August 1990 EP
0404303 December 1990 EP
0410678 January 1991 EP
9100021 July 1991 EP
0450638 October 1991 EP
502141 September 1992 EP
0502414 September 1992 EP
0625104 November 1994 EP
0625544 November 1994 EP
0631862 January 1995 EP
0635462 January 1995 EP
0319589 February 1995 EP
0651003 May 1995 EP
0753402 July 1995 EP
0671259 September 1995 EP
0671259 September 1995 EP
0729829 August 1996 EP
0758577 February 1997 EP
0794215 September 1997 EP
0808944 November 1997 EP
0808944 November 1997 EP
0858481 August 1998 EP
0945253 September 1999 EP
1031467 August 2000 EP
1211138 June 2002 EP
1211138 June 2002 EP
1373375 January 2004 EP
1812637 May 2006 EP
1737650 January 2007 EP
1844927 October 2007 EP
1857261 November 2007 EP
0625104 November 1994 FR
1550358 August 1979 GB
2077311 December 1981 GB
62017048 January 1987 JP
62157782 June 1987 JP
62195030 August 1987 JP
63230542 September 1988 JP
1083087 March 1989 JP
1083088 March 1989 JP
2138349 May 1990 JP
1016660 January 1998 JP
11342552 December 1999 JP
9207983 May 1992 WO
9315933 August 1993 WO
9400418 January 1994 WO
9415884 July 1994 WO
9427840 December 1994 WO
03035435 January 1995 WO
9612849 May 1996 WO
9716846 September 1997 WO
9831626 July 1998 WO
9834778 August 1998 WO
9948683 September 1999 WO
0208316 January 2002 WO
0208316 January 2002 WO
02077076 October 2002 WO
02081802 October 2002 WO
02081802 October 2002 WO
03002330 January 2003 WO
03086725 October 2003 WO
2004004303 August 2004 WO
2005070664 August 2005 WO
2005097879 October 2005 WO
2005100708 October 2005 WO
2006008529 January 2006 WO
2006052967 May 2006 WO
2006089025 August 2006 WO
Other references
  • U.S. Appl. No. 11/437,997, filed May 19, 2006.
  • U.S. Appl. No. 13/416,617, filed Mar. 9, 2013.
  • U.S. Appl. No. 11/893,613, filed Oct. 22, 2007.
  • High Performance SuperLite Sheet, Disclosed Anonymously, IP.com, Aug. 2, 2002, 8 pgs.
  • Azdel Superlite Sheet—Technical Guide Part 1, Disclosed Anonymously, IP.com, Aug. 5, 2002, 21 pgs.
  • Azdel Superlite Sheet—Commercial Guide Part 1, Disclosed Anonymously, IP.com, Aug. 5, 2002, 8 pgs.
  • Azdel Superlite Sheet—Processing Guides, Disclosed Anonymously, IP.com, Aug. 6, 2002, 3 pgs.
  • Azdel Superlite Sheet—Technical Guide Part 2, Disclosed Anomymously, IP.com, Aug. 5, 2002, 32 pgs.
  • European Search Report; Aug. 13, 2008; 13 pages.
Patent History
Patent number: RE44893
Type: Grant
Filed: Mar 22, 2012
Date of Patent: May 13, 2014
Assignee: Hanwha Azdel, Inc. (Forest, VA)
Inventors: Venkat Krishna Raghavendran (Greer, SC), Thomas Arnold Ebeling (Forest, VA)
Primary Examiner: Terressa Boykin
Application Number: 13/427,131
Classifications
Current U.S. Class: Of Polycarbonate (428/412)
International Classification: B32B 27/36 (20060101); B32B 27/38 (20060101);