Abstract: A photovoltaic crucible mold release compound includes a powder mixture comprising silicon nitride powder having 1 ppm of impurities or less and silicon dioxide 1 ppm of impurities or less mixed in with the silicon nitride powder until the gray of the silicon nitride powder turns lighter in color which is from 1% silicon dioxide in weight up to 50% silicon dioxide in weight. Also included is a binder having a liquid. The powder mixture is mixed with the binder. The binder can be ethanol, water or alcohol. A photovoltaic crucible mold release compound can also include a photovoltaic crucible mold, so that the mold release compound is applied to an inside surface of the photovoltaic crucible mold to a thickness of 75 to 1500 microns.

Abstract: There is provided an adhesive comprising chitosan an optionally a crosslinking agent. A method for preparing such an adhesive is also disclosed. A wood-panel made with such an adhesive is also provided. Moreover, a method for manufacturing a wood-based panel is provided. The method comprises preparing a mixture comprising wood, chitosan, optionally a crosslinking agent, and optionally an acid, forming a mat with the mixture, and pressing the mat under heat and pressure so as to obtain the wood-based panel.

Abstract: There is provided a cellulose ester film comprising at least one plasticizer and satisfying the following expressions (1) to (5); |Re|?5 nm (1); 50 nm<Rth<300 nm (2); 25 ?m?d?65 ?m (3); 1×10?3?Rth/d?4×10?3 (4); 3.8 GPa<E?<5.0 GPa (5); wherein Re represents a retardation value in an in-plane direction; Rth represents a retardation value in a thickness direction; d represents a film thickness; and E? represents an elastic modulus of the film.

Abstract: Dispersion obtainable by reacting a) in 50 to 75 parts by weight of water b) 25 to 50 parts by weight of silica particles having a BET surface area of 30 to 500 m2/g and c) 100 to 300 ?g/m2 BET surface area of the silica particles from b) parts by weight of one or more aminofunctional, organosilicon compounds, the aminofunctional, organosilicon compound being a quaternary, aminofunctional, organosilicon compound which is obtainable by reacting at least one haloalkylfunctional silane as component A with a tertiary amine as component B in the presence of a defined amount of water and at least partly removing the resulting hydrolysis alcohol from the system.

Abstract: A method for producing a rutile titanium oxide sol having a particle diameter measured by dynamic light scattering of 5 nm to 100 nm, the method comprising: a process (a): mixing a tin oxalate aqueous solution, a titanium alkoxide, oxalic acid, a quaternary ammonium hydroxide, and water, while adjusting, per mole of titanium atoms, a proportion of tin atoms to be from 0.1 mol to 0.8 mol, a proportion of the oxalic acid to be from 0.01 mol to 5 mol, and a proportion of the quaternary ammonium hydroxide to be from 0.1 mol to 3.5 mol to prepare a titanium-containing aqueous solution having a concentration in terms of TiO2 of 0.1% by mass to 15% by mass; and a process (b): performing hydrothermal treatment on the titanium-containing aqueous solution produced in the process (a) at 100° C. to 200° C.

Abstract: A method of blending a fine precipitated calcium carbonate (PCC) filler with larger PCC, the resulting blend to be used alone or in conjunction with a ground carbonate, clay or other filler, resulting in improved porosity by the lowering of the porosity of supercalendered paper, thereby imparting improved and offset printability. The fine PCC can be ultrafine PCC filler which then is blended with other fillers including but not limited to pigments. These fillers which are blended with the fine PCC include commercial and experimental PCC and commercial clays. Ultrafine PCC has agglomerates of small, discrete particles. Ultrafine PCC for use in the invention has a specific surface area of about 20 m2/g as measured by BET gas adsorption. As measured by a sedigraph, the average size of these agglomerates is from 0.4 to 1.1 microns.

Abstract: The present invention relates to solid silica preparations composed of the components (A) 20% to 80% by weight, based on the total weight of the preparation, of a silica; (B) 20% to 50% by weight, based on the total weight of the preparation, of at least one additive selected from the group consisting of a water-soluble, nonionic, surface-active additive based on polyethers, a water-soluble, surface-active additive containing carboxylate groups, a polyurethane, an anionic, surface-active additive based on acidic phosphoric, phosphonic, sulfuric or sulfonic esters; (C) if appropriate, further components, the further components comprising no pigments, and the sum of all components (A), (B), and (C) making 100% by weight. The invention further relates to methods of producing them and also to methods of coloring high molecular mass organic or inorganic materials, more particularly of coloring plastics.

Abstract: The present invention provides a producing method of powder particles having an average particle diameter on the order of submicrons. Specifically, the producing method is a producing method of powder particles obtained by grinding a product to be ground by using plural grinding media, wherein the grinding media including at least one kind (grinding medium A) having an average particle diameter of 0.01 to 5 times and at least one kind (grinding medium B) having an average particle diameter of 10 to 450 times, with respect to the average particle diameter of the product to be ground before being ground, are used.

Abstract: The composition applied to the refractory structure has a magnesia-based refractory material, calcia source and a binder. After application of the refractory material to a refractory structure and upon application of heat to the applied refractory material a matrix is formed which protects against penetration of the slag into the refractory material. The resulting refractory material has improved hot strength, slag resistance and durability.

Abstract: A composition and method for reducing freeze-thaw heave risk over flash-filled voids are disclosed. A composition can include cementitious fly ash, water and cellular foam. The composition can optionally include a filler, e.g., Type F fly ash, or additional desired components. A method can include mixing the desired composition and applying the composition to a void. The method can optionally include determining the desired composition based on various factors.

Abstract: Cementitious compositions in which the cementitious properties of fly ash are carefully controlled are described. The cementitious compositions may be substantially free harsh acids and bases such as citric acids (?pH 2.2) and alkali metal activators including alkali hydroxides (?pH 12-14) and metal carbonates (?pH 11.6). The use of these harsh chemicals creates acid base reactions during use of the products. Instead of these harsh chemicals, a lactic acid salt based activator is be used as a reaction accelerator. Boric compounds may be used as a retarder in the compositions.

Abstract: A cementitious mixture for high-volume production of masonry products comprises a hydraulic binder accounting for 20 wt % or more of the cementitious mixture, the hydraulic binder comprising 75 to 100 wt % Class C fly ash with a CaO equivalent content of at least 15% by weight. The cementitious mixture also comprises one or more aggregates, and a set control system.

Abstract: The present disclosure provides improved water-repellent admixtures for cementitious materials. The water-repellent admixtures are incorporated during masonry processing to improve the water resistance of the final product. Solid water-repellent admixtures may be conveniently incorporated into pre-blended dry mortar mixes. In some variations, a pre-blended dry mortar mix comprises a cementitious material, an aggregate, and a dry water-repellent admixture, wherein the water-repellent admixture contains one or more materials selected from the group consisting of silanes, siloxanes, free fatty acids, fatty acid derivatives, particulated polymers, and particulated copolymers, and wherein the water-repellent admixture is present in the pre-blended dry mortar mix in a dosage from about 0.01% to about 1.00% by weight of the pre-blended dry mortar mix.

Abstract: After adding phosphorus (P) and germanium (Ge) into a silicon melt or adding phosphorus into a silicon/germanium melt, a silicon monocrystal is grown from the silicon melt by a Czochralski method, where a phosphorus concentration [P]L(atoms/cm3) in the silicon melt, a Ge concentration in the silicon monocrystal, an average temperature gradient Gave (K/mm) and a pull speed V (mm/min) are controlled to satisfy a formula (1) as follows, a phosphorus concentration [P](atoms/cm3) and the Ge concentration [Ge](atoms/cm3) in the silicon monocrystal satisfy a relationship according to a formula (2) as follows while growing the silicon monocrystal, where dSi(?) represents a lattice constant of silicon, rSi(?) represents a covalent radius of silicon, rP(?) represents a covalent radius of phosphorus, and rGe(?) represents a covalent radius of Ge: [ P ] L + ( 0.3151 × [ Ge ] + 3.806 × 10 18 ) / 1.5 < 0.

Abstract: Fabrication of doped AlN crystals and/or AlGaN epitaxial layers with high conductivity and mobility is accomplished by, for example, forming mixed crystals including a plurality of impurity species and electrically activating at least a portion of the crystal.

Abstract: A method of growing a p-type thin film of ?-Ga2O3 includes preparing a substrate including a ?-Ga2O3 single crystal, and growing a p-type thin film of ?-Ga2O3 on the substrate. The p-type thin film is grown in a manner that Ga in the thin film is replaced by a p-type dopant selected from H, Li, Na, K, Rb, Cs, Fr, Be, Mg, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Tl, and Pb.

Abstract: A unibody, multi-piece crucible for use in for use in elemental purification, compounding, and growth of semi-conductor crystals, e.g., in the process of molecular beam epitaxy (MBE) for melting silicon and the like at high temperature. The crucible has an outer coating layer that fixedly joins the multi pieces making up the crucible. The invention also provides a method for making a unibody containing structure comprising pyrolytic boron nitride having a negative draft, which method obviates the need of complicated overhang structure of graphite mandrels or the removal of the graphite mandrels by burning at high temperatures.

Abstract: Provided is a thin film production apparatus that enables cost reduction and improvement of deposition efficiency by employing a common component. In a thin film production apparatus according to the present invention, a volume of a reaction space is optimized by determining the volume of the reaction space with an inner block disposed inside a vacuum tank, that is, by merely altering a size of an inner diameter of the inner block without altering a size of the vacuum tank. Accordingly, film formation on plural kinds of substrates having different sizes becomes possible using the common vacuum tank. Further, increase of the number of apparatus structural components to be prepared for each size of the substrate to be processed can be minimized, whereby the cost of the components can be reduced, and, while simplifying assembling operation, product inspection operation, and adjusting operation, excellent deposition efficiency and stable film formation can be realized.

Abstract: Embodiments of the invention provide apparatuses and methods for atomic layer deposition (ALD), such as plasma-enhanced ALD (PE-ALD). In some embodiments, a PE-ALD chamber is provided which includes a chamber lid assembly coupled with a chamber body having a substrate support therein. In one embodiment, the chamber lid assembly has an inlet manifold assembly containing an annular channel encompassing a centralized channel, wherein the centralized channel extends through the inlet manifold assembly, and the inlet manifold assembly further contains injection holes extending from the annular channel, through a sidewall of the centralized channel, and to the centralized channel.

Abstract: The present invention is generally directed to a system for controlling placement of nanoparticles, and methods of using same. In one illustrative embodiment, the device includes a substrate and a plurality of funnels in the substrate, wherein each of the funnels comprises an inlet opening and an elongated, rectangular shaped outlet opening. In one illustrative embodiment, the method includes creating a dusty plasma comprising a plurality of carbon nanotubes, positioning a mask between the dusty plasma and a desired target for the carbon nanotubes, the mask having a plurality of openings extending therethrough, and extinguishing the dusty plasma to thereby allow at least some of the carbon nanotubes in the dusty plasma to pass through at least some of the plurality of openings in the mask and land on the target.

Abstract: The purpose of the invention is increasing the efficiency of utilizing an EL material and providing a deposition method and a vapor deposition apparatus which is one of the film formation systems which are excellent in throughput and uniformity in film thickness in forming an EL layer. According to the invention, evaporation is performed by moving or reciprocating an evaporation source holder in which a plurality of containers (crucible) each encapsulating an evaporation material are set only in an X direction while moving a substrate at regular intervals. Further, in the plurality of evaporation source holders, film thickness meters of adjacent evaporation sources are disposed alternately so as to sandwich the movement pathway of the substrate.

Abstract: A substrate support useful for a plasma processing apparatus includes a metallic heat transfer member and an overlying electrostatic chuck having a substrate support surface. The heat transfer member includes one or more passage through which a liquid is circulated to heat and/or cool the heat transfer member. The heat transfer member has a low thermal mass and can be rapidly heated and/or cooled to a desired temperature by the liquid, so as to rapidly change the substrate temperature during plasma processing.

Abstract: A pedestal positioning assembly system for use in a substrate processing system includes a pedestal rigidly attached to a pedestal shaft, a reference rigidly attached to the substrate processing system, a lateral adjustment assembly to adjust a lateral location of the pedestal relative to the reference, and a vertical adjustment assembly to adjust a tilt of the pedestal relative to the reference. The lateral adjustment assembly and the vertical adjustment assembly are external to a processing chamber and are coupled to the pedestal disposed within the processing chamber through the pedestal shaft. The reference can be a ring and the lateral adjustment assembly substantially centers the pedestal within the ring. A method of adjusting a pedestal includes leveling the pedestal, translating the pedestal, calibrating the pedestal height to a preheat ring level, and checking the level and location of the pedestal while rotating the pedestal.

Abstract: Methods are disclosed for controlling the rate of cellulose hydrolysis and reducing the rate of glucose degradation by adjusting the pH during cellulose hydrolysis.

Abstract: A tobacco-free oral pouch product providing immediate and long lasting flavor release comprises a pouch wrapper and tobacco-free flavor beads contained within the pouch wrapper. The flavor beads comprise at least one of microcrystalline cellulose, pectin and sodium alginate, at least one polymer having a higher solubility in saliva than microcrystalline cellulose, pectin and/or sodium alginate, and at least one flavorant. The pectin and sodium alginate are cross-linked. The tobacco-free flavor beads provide immediate release of the flavorant upon placement of a pouch product in a user's mouth and long lasting release of the flavorant for about 15 minutes to about 80 minutes. The oral pouch product contains only tobacco-free flavor beads.

Abstract: An apparatus and method for adaptive materials arranged in a variety of orientations and with a wide range of attachment configurations to induce structural vibrations at extremely high frequencies. These mechanical vibrations cause fouling agents to become detached and accordingly “clean” an otherwise dirty element or wire of a hot-wire anemometer, planar or curvilinear sensor surface, or display surfaces. They also can be made to vibrate at such frequencies with such intensities that local droplets of water are either shaken off or instantaneously cavitate, thereby allowing the elements to be used in all weather conditions.

Abstract: A residue-removing solution for removing residues after a dry process, which includes an amine salt of a monocarboxylic acid and/or a salt of a polycarboxylic acid that forms a 7- or more-membered ring chelate with copper, and water, the residue-removing solution containing aqueous solution (A) or (B) as described herein. Also disclosed is a method for removing residues present on a semiconductor substrate after dry etching and/or ashing. Further, a method for manufacturing semiconductor devices is further disclosed, which includes subjecting a semiconductor substrate having Cu as an interconnect material, and a low dielectric constant film as an interlayer dielectric material, to dry etching and/or ashing; and bringing the processed semiconductor substrate into contact with the above residue-removing solution.

Abstract: A device for cleaning submergible surfaces includes a mandrel having a handle at a proximal end and a connector at a distal end. The handle can be removably mounted to an air tool. A cleaning tip holder has an opening at a distal end leading into an interior space. The cleaning tip holder can be connected with the mandrel connector and can be removably retained therewith. A cleaning tip includes a generally rectangular element having beveled front and side edges and can be removably retained partially within the cleaning tip holder interior space. In use, a cleaning tip is mounted in the cleaning tip holder interior space, and that combination is mounted to the mandrel connector. The mandrel handle is affixed to an air tool having an outlet hose, which, when activated, produces a reciprocating action in the device, creating a scrubbing action with the cleaning tip.

Abstract: A method for collecting effluent from an engine comprising: providing a portable trailer having a plurality of sides in a retracted and non-operational configuration forming an internal compartment and at least one droplet separator panel; and moving at least two of said sides from said retracted and non-operational configuration to an open position and an operational configuration wherein said two sides create a path for channeling an effluent/air mixture containing engine wash water from said engine to said at least one droplet separator panel; and separating said engine wash water from said air with said at least one droplet separator panel.

Abstract: A hard floor surface care process comprising a process of identifying, cleaning, polishing, and protecting manmade and natural stone hard floor surfaces having a single surface or multi-surface quality. The hard floor surface care process comprising an acid reactive or nonreactive hard floor surface identifying process; an emulsifying solution, agitating, and toweling cleaning process; a polishing process utilizing a lubricating solution with a polishing chemistry or pad, and a protecting process utilizing a protecting chemistry selected as a function of the identifying process.

Abstract: A method of cleaning comprising propelling a sublimable media in a first direction through a discharge wand, inserting the discharge end of the wand into coils of a boiler, impinging on inner and outer surfaces the coils with the sublimable media, which subsequently dissipates or is consumed.

Abstract: Apparatus and methods are disclosed for cleaning interiors of passageways in endoscopes or other luminal medical devices by flow of liquid and gas therethrough. The liquid flow may include rivulets, droplets or other liquid entities which move on the internal surfaces of the passageways, and may include a three-phase contact interface between liquid and dry solid and gas.

Abstract: A concentrate cleaning composition includes water, glycerine, and at least one alkyl polyglycoside. The water may be present in an amount of greater than about 65% by weight. Glycerine may be present in an amount between about 0.05% and about 8% by weight of the cleaning composition. The at least one alkyl polyglycoside may be present in an amount of between about 1% and about 25% by weight of the cleaning composition.

Abstract: A dishwashing machine includes a tub having a sidewall. The sidewall has a first wall and a second wall connected by a bottom wall. The sidewall is connected to a first end wall and a second end wall. The first end wall is connected to the first wall, the second wall, and the bottom wall on a first end of the sidewall and the second end wall is connected to the first wall, the second wall, and the bottom wall on a second end of the sidewall forming an interior volume. The tub has the same amount of welding regardless of a length of the sidewall.

Abstract: A carbonitriding method that allows the permeating rate of nitrogen to be increased to improve the efficiency of the carbonitriding process is directed to carbonitriding a workpiece formed of steel containing at least 0.8 mass % of carbon, including an atmosphere control step of controlling the atmosphere in a heat treatment furnace, and a heating pattern control step of controlling the temperature history applied to a workpiece. The atmosphere control step includes an undecomposed ammonia concentration control step of controlling the undecomposed ammonia concentration in the heat treatment furnace, and a partial pressure control step of controlling the partial pressure of at least one of carbon monoxide and carbon dioxide in the heat treatment furnace.

Abstract: The invention relates to a method for producing corrosion-resistant surfaces of nitrated or nitrocarburated steel components, the surfaces having roughness heights (Rz) of Rz?1.5 ?m. The method comprises the following steps: oxidation of the surfaces of the nitrated or nitrocarburated components in a first oxidation step; carrying out at least a second oxidation of the component surfaces in an immediately subsequent oxidation step; polishing the component surface in a final method step, directly after the final oxidation.

Abstract: Provided is a maraging steel strip which has such a composition that can reduce the content of TiN acting as the starting point of fatigue fracture in a high-cycle region, and the bending fatigue strength of which has been improved by the precipitation hardening effect yielded by precipitating coherent nitrides in the nitrided structure. A maraging steel strip produced by nitriding a managing steel which contains by mass, C: 0.01% or less, Si: 0.1% or less, Mn: 0.1% or less, P: 0.01% or less, S: 0.005% or less, Ni: 8.0 to 22.0%, Cr: 0.1 to 8.0%, Mo: 2.0 to 10.0%, Co: 2.0 to 20.0%, Ti: 0.1% or less, Al: 2.5% or less, N: 0.03% or less, and O: 0.005% or less, with the balance being Fe and unavoidable impurities, wherein Baker-Nutting orientation relationship with an orientation difference within 10° exists between the Cr nitride precipitated in the nitrided layer and the matrix martensite.

Abstract: A martensitic stainless steel for inexpensive seamless pipe having 655 MPa yield strength, high toughness and excellent corrosion resistance in high CO2 environments, and a method for manufacturing thereof is provided. The steel comprises C: 0.005-0.05%, Si: 0.1-0.5%, Mn: 0.1-2.0%, P: ?0.05%, S: ?0.005%, Cr: 10.0-12.5%, Mo: 0.1-0.5%, Ni: 1.5-3.0%, N: ?0.02%, Al: 0.01-0.1%, by weight, while FI value defined by the formula [FI=Cr+Mo?Ni?30(C+N)] being 5.00 to 8.49, and balance of substantially Fe. The method comprises the steps of reheating the cooled steel at temperatures from 780° C. to 960° C., quenching the reheated steel, and then tempering the quenched steel at temperatures from 550° C. to 650° C.

Abstract: This high-carbon pearlitic steel rail having excellent ductility, includes: in terms of percent by mass, C: more than 0.85% to 1.40%; Si: 0.10% to 2.00%; Mn: 0.10% to 2.00%; Ti: 0.001% to 0.01%; V: 0.005% to 0.20%; and N: less than 0.0040%, with the balance being Fe and inevitable impurities, wherein contents of Ti and V fulfill the following formula (1), and a rail head portion has a pearlite structure.

Abstract: High yield ratio high-strength hot rolled thin steel sheet superior in weldability and ductility comprising, by mass %, C: over 0.030 to less than 0.10%, Si: 0.30 to 0.80%, Mn: 1.7 to 3.2%, P: 0.001 to 0.02%, S: 0.0001 to 0.006%, Al: 0.060% or less, N: 0.0001 to 0.0070%, containing further Ti: 0.01 to 0.055%, Nb: 0.012 to 0.055%, Mo: 0.07 to 0.55%, B: 0.0005 to 0.0040%, and simultaneously satisfying 1.1?14×Ti(%)+20×Nb(%)+3×Mo(%)+300×B(%)?3.7, the balance comprised of iron and unavoidable impurities, and having a yield ratio of 0.64 to less than 0.92, a TS×El1/2 of 3320 or more, an YR×TS×El1/2 of 2320 or more, and a maximum tensile strength (TS) of 780 MPa or more.

Abstract: A steel having excellent formability, fatigue endurance after quenching, low temperature toughness, resistance for hydrogen embrittlement, and corrosion fatigue endurance. A method includes heating a steel slab at 1160° C. to 1320° C., hot-finish-rolling the steel slab at a finisher delivery temperature of 750° C. to 980° C., and then coiling the hot-rolled steel at a coiling temperature of 560° C. to 740° C. after slow cooling for a time of 2 seconds or more to produce a hot-rolled steel strip having a structure in which the ferrite grain diameter df corresponding to a circle is 1.1 ?m to less than 1.2 ?m and the ferrite volume fraction Vf is 30% to 98%, the steel slab containing 0.18 to 0.29% of C, 0.06 to 0.45% of Si, 0.91 to 1.85% of Mn, 0.019% or less of P, 0.0029% or less of S, 0.015 to 0.075% of sol. Al, 0.0049% or less of N, 0.0049% or less of O, 0.0001 to 0.0029% of B, 0.001 to 0.019% of Nb, 0.001 to 0.029% of Ti, 0.001 to 0.195% of Cr, and 0.001 to 0.

Abstract: A solder layer and an electronic device bonding substrate having high bonding strength of a device and low bonding failure even by a simplified bonding method of a device to a substrate and a method for manufacturing the same are provided. A device bonding substrate 1 including a substrate 2 and a lead free solder layer 5 formed on said substrate has a solder layer 5 consisting of a plurality of layers having mutually different phases, and oxygen concentration on the upper surface of the solder layer is lower than 30 atomic % of the concentration of the metal component which is the most oxidizable among the metal components making up the upper layer of the solder layer 5. Carbon concentration on the upper surface of the solder layer 5 may be lower than 10 atomic % of the concentration of the metal component which is the most oxidizable among the metal components making up the upper layer of the solder layer.

Abstract: New 7XXX alloys having improved ballistics performance are disclosed. The new alloys generally are resistant to armor piercing rounds at 2850 fps, resistant to fragment simulated particles at 2950 fps, and are resistant to spalling. To achieve the improved ballistics properties, the alloys are generally overaged so as to obtain a tensile yield strength that is (i) at least about 10 ksi lower than peak strength and/or (ii) no greater than 70 ksi.

Abstract: The invention relates to the field of explosives, and more particularly relates to particles of an explosive, wherein they are in crystalline form, have a rounded shape and a majority of them contain no internal defect. Particles of an explosive in crystalline form include a volume fraction of closed pores of less than or equal to 0.05%. A method for preparing explosive particles includes preparing crystalline particles, a majority of which are without an internal defect; and rounding the crystalline particles.

Abstract: A self-wrapping, textile sleeve for routing and protecting elongate members from exposure to abrasion, thermal and other environmental conditions and method on construction thereof. The sleeve has an elongate wall constructed from interlaced yarns having interstices between adjacent yarns. At least one of the yarns is heat formed at one temperature to form the wall as a self-wrapping wall curling about a longitudinal axis of the sleeve. The wall has an inner surface providing a generally tubular cavity in which the elongate members are received. The wall also has an outer surface with a cured layer thereon. The cured layer is cured at the one temperature at which the yarns are heat formed into their self-wrapping configuration, wherein the cured layer fills the interstices between adjunct yarns to form an impervious layer on the wall.

Abstract: This invention is a manufacturing device for a permanent magnet disposed in a rotating electrical machine, in which a plurality of magnet pieces, each formed by being fractured and split along a notch groove, are aligned and joined to each other with an adhesive interposed between fractured surfaces. First pressing means for aligning the plurality of fractured and split magnet pieces with the fractured surfaces opposed to each other in a width direction by pressing from the width direction of the permanent magnet and second pressing means for aligning the plurality of magnet pieces in a thickness direction by pressing from a thickness direction of the permanent magnet are provided. Moreover, third pressing means for joining the opposing fractured surfaces of the magnet piece with the interposed adhesive by pressing the plurality of magnet pieces from a longitudinal direction of the permanent magnet is provided.

Abstract: A method and apparatus for welding ends of two separate articles or a single article to form a single welded article. The apparatus comprises first and second molds for supporting and clamping first and second ends of at least one article and an infrared heating element for thermally energizing over a prescribed period of time the first and second ends of the at least one article to a welding condition. The apparatus further comprises a regulator for altering the power supplied for energizing the infrared heater over at least a portion of the prescribed period of time to achieve increased electromagnetic radiation penetration into the body of the at least one article beyond the first and second ends. The apparatus also comprises an actuator for advancing the first and second ends into a contacting position to form a single welded article.

Abstract: A method of fabricating a fiber reinforced thermoplastic composite structure comprising: placing a first layer of fiber reinforced thermoplastic material on top of a second layer of fiber reinforced thermoplastic material; providing a local heating source and locally heating a portion of at least the upper layer of thermoplastic composite material; and providing an ultrasonic transducer and locally introducing ultrasonic energy waves to the heated portion of the thermoplastic material such that ultrasonic consolidation of the fiber reinforced thermoplastic occurs.

Abstract: A liner panel, such as a cassette 120 of a fan track liner of a gas turbine engine, is secured to a casing of the engine at flanges 124 and 126. Foam pads 42 are disposed between the casing 40 and the cassette 120 to support the cassette 120 from the casing 40. The pads 42 may be made from a reticulated polyurethane foam which is sufficiently resilient to be compressed and to expand to remain in contact with the cassette 120 and the casing 40 as the cassette 120 moves towards and away from the casing 40 during the assembly process. The foam is impregnated with a hardener composition which is uncured during installation of the cassette 120, but subsequently cures to increase the rigidity of the pads 42.

Abstract: A multi-layered material and a method for making the same are provided. The multi-layered material includes a first foamed layer, a substrate, a second foamed layer, and a surface layer. The first foamed layer has a plurality of first cells. The substrate is a fabric. The second foamed layer has a plurality of second cells. The foaming method of the second foamed layer is different from that of the first foamed layer. The size of the second cells is different from that of the first cells. The variation in size of the second cells is different from that of the first cells. The surface layer is disposed on the second foamed layer. Thus, when the multi-layered material is used as a surface cover of a ball, it can provide excellent resilience and control, and improve manufacturing efficiency.