Abstract: A high strength hot rolled steel sheet having a tensile strength of 780 MPa or more is produced by specifying the composition to contain C: more than 0.035% and 0.07% or less, Si: 0.3% or less, Mn: more than 0.35% and 0.7% or less, P: 0.03% or less, S: 0.03% or less, Al: 0.1% or less, N: 0.01% or less, Ti: 0.135% or more and 0.235% or less, and the remainder composed of Fe and incidental impurities, on a percent by mass basis, in such a way that C, S, N, and Ti satisfy ((Ti?(48/14)N?(48/32)S)/48)/(C/12)<1.0 (C, S, N, and Ti: content of the respective elements (percent by mass)) and specifying the microstructure in such a way that a matrix includes more than 95% of ferritic phase on an area fraction basis and fine Ti carbides having an average grain size of less than 10 nm are precipitated in the grains of the above-described ferritic phase.

Abstract: The present invention focuses on Sn and has as its problem to not only improve the corrosion resistance and rust resistance of Cr-containing ferritic stainless steel but also improve the ridging resistance. The present invention derives the relationship between Ap, which shows the ?-phase rate at 1100° C. due to a predetermined ingredient, and Sn in ferritic stainless steel which becomes a dual phase structure of ?+? in the hot rolling temperature region, applies and adds Sn, and hot rolls the steel to give a total rolling rate of 15% or more in 1100° C. or higher hot rolling to thereby obtain ferritic stainless steel sheet which has good ridging resistance, which also has excellent corrosion resistance and rust resistance, and which can be applied to general durable consumer goods: 0.060?Sn?0.634?0.

Abstract: Disclosed is a medium carbon steel sheet for cold working that has a hardness of 500 HV to 900 HV when subjected to high-frequency quenching in which a temperature is raised at an average heating rate of 100° C./second, the temperature is held at 1,000° C. for 10 seconds, and a quick cooling to a room temperature is carried out at an average cooling rate of 200° C./second. The medium carbon steel sheet includes, by mass %, C: 0.30 to 0.60%, Si: 0.06 to 0.30%, Mn: 0.3 to 2.0%, P: 0.03% or less, S: 0.0075% or less, Al: 0.005 to 0.10%, N: 0.001 to 0.01%, and Cr: 0.001 to 0.10%, the balance composed of Fe and inevitable impurities. An average diameter d of a carbide is 0.6 ?m or less, a spheroidizing ratio p of the carbide is equal to or more than 70% and less than 90%, and the average diameter d (?m) of the carbide and the spheroidizing ratio p % of the carbide satisfy d?0.04×p?2.6.

Abstract: A high-tensile-strength hot-rolled steel sheet is provided having a composition which contains 0.02 to 0.08% C, 0.01 to 0.10% Nb, 0.001 to 0.05% Ti and Fe and unavoidable impurities as a balance, wherein the steel sheet contains C, Ti and Nb in such a manner that (Ti+(Nb/2))/C<4 is satisfied, and the steel sheet has a structure where a primary phase of the structure at a position 1 mm away from a surface in a sheet thickness direction is one selected from a group consisting of a ferrite phase, tempered martensite and a mixture structure of a ferrite phase and tempered martensite, a primary phase of the structure at a sheet thickness center position is formed of a ferrite phase, and a difference ?V between a structural fraction (volume %) of a secondary phase at the position 1 mm away from the surface in the sheet thickness direction and a structural fraction (volume %) of a secondary phase at the sheet thickness center position is 2% or less.

Abstract: A low specific gravity and high strength steel sheet includes C of 0.2% to 0.8%, Mn of 2% to 10%, P of 0.02% or less, S of 0.015% or less, Al of 3% to 15%, and N of 0.01% or less. A ratio of Mn/Al is 0.4 to 1.0. Retained austenite in a structure is included in the range of 1% or more. The steel sheet further includes one or two or more elements selected from the group consisting of Si of 0.1% to 2.0%, Cr of 0.1% to 0.3%, Mo of 0.05% to 0.5%, Ni of 0.1% to 2.0%, Cu of 0.1% to 1.0%, B of 0.0005% to 0.003%, Ti of 0.01% to 0.2%, Zr of 0.005% to 0.2%, Nb of 0.005% to 0.2%, W of 0.1% to 1.0%, Sb of 0.005% to 0.2%, and Ca of 0.001% to 0.2%.

Abstract: The present invention provides a hot coil for line pipe use which can reduce deviation in ordinary temperature strength and improve low temperature toughness despite the numerous restrictions in production conditions due to the coiling step and provides a method of production of the same, specifically makes the steel plate stop for a predetermined time between rolling passes in the recrystallization temperature range and performs cooling by two stages after hot rolling so as to thereby make the steel structure at the center part of plate thickness and effective crystal grain size of 3 to 10 ?m, make the total of the area ratios of bainite and acicular ferrite 60 to 99%, and make the absolute value of A-B 0 to 30% when the totals of the area ratios of bainite and acicular ferrite at any two portions are designated as respectively A and B.

Abstract: Hot rolled steel sheet which has a maximum tensile strength of 600 MPa or more and has an excellent low temperature impact energy absorption and HAZ softening resistance and a method of production of the same are provided, that is, sheet which contains, by mass %, C: 0.04 to 0.09%, Si: 0.4% or less, Mn: 1.2 to 2.0%, P: 0.1% or less, S: 0.02% or less, Al: 1.0% or less, Nb: 0.02 to 0.09%, Ti: 0.02 to 0.07%, and N: 0.005% or less, where 2.0?Mn+8[% Ti]+12[% Nb]?2.6, has a balance of Fe and unavoidable impurities, has an area percentage of pearlite of 5% or less, has a total area percentage of martensite and retained austenite of 0.5% or less, has a balance of a metal structure of ferrite and/or bainite, has an average grain size of ferrite and bainite of 10 ?m or less, has an average particle size of alloy carbonitrides with incoherent interfaces which contain Ti and Nb of 20 nm or less, and has a yield ratio of 0.85 or more.

Abstract: High strength steel sheet which secures tensile maximum strength 900 MPa or more high strength while having excellent shapeability, which high strength steel sheet which is excellent in shapeability characterized by having a predetermined composition of ingredients, by the steel sheet structure including a ferrite phase and martensite phase, by the ratio of Cu particles incoherent with the bcc iron being 15% or more with respect to the Cu particles as a whole, by a density of Cu particles in the ferrite phase being 1.0×1018/m3 or more, and by an average particle size of Cu particles in the ferrite phase being 2.0 nm or more.

Abstract: A method for hot rolling a metal strip or metal sheet, wherein 1.a) the slab or the strip or sheet is subjected in a first step to one or more reshaping actions in a hot rolling mill for producing a uniform, fine, recrystallised austenite structure and 2) the slab or the strip or sheet is then subjected in a second step to cooling for producing a fine-grain structure. The slab or the strip or sheet is subjected to heating between at least two roll stands of the hot rolling mill during performance of the step 1.a). The roll stands are arranged to follow one another in a rolling direction and in each of which the slab or the strip or sheet is subjected to reshaping. A heater for heating the rolling stock is arranged between at least two of the roll stands.

Abstract: A process for manufacturing a ferritic hot rolled steel strip is provided. The process includes providing a steel slab, hot rolling the slab to produce a transfer bar and ferritic hot rolling the transfer bar to produce hot rolled strip. The ferritic hot rolled strip is coiled at temperatures between 580-780° C. and has a yield strength between 130-210 MPa, a tensile strength greater than 260 MPa, a uniform elongation greater than 15%, a total elongation to failure greater than 30%, and an n-value greater than 0.2.

Abstract: The invention relates to a bainite steel consisting of the following elements in weight %: C: 0.25-0.55 Si: 0.5-1.8 Mn: 0.8-3.8 Cr: 0.2-2.0 Ti: 0.0-0.1 Cu: 0.0-1.2 V: 0.0-0.5 Nb: 0.0-0.06 Al: 0.0-2.75 N: <0.004 P: <0.025 S: <0.025 and a method for manufacturing a bainite steel strip that comprises the step of cooling the coiled strip of such composition to ambient temperature, during which the bainite transformation takes place.

Abstract: A high-strength hot-rolled steel sheet has a tensile strength (TS) of 540 to 780 MPa, only small variations in strength, and excellent uniformity in strength using a general-purpose Ti-containing steel sheet, which is inexpensive. The high-strength hot-rolled steel sheet includes, on a mass percent basis, 0.05%-0.12% C, 0.5% or less Si, 0.8%-1.8% Mn, 0.030% or less P, 0.01% or less S, 0.005%-0.1% Al, 0.01% or less N, 0.030%-0.080% Ti, and the balance being Fe and incidental impurities. The microstructure have a bainitic ferrite fraction of 70% or more, and the amount of Ti present in a precipitate having a size of less than 20 nm is 50% or more of the value of Ti* calculated using formula (1): Ti*=[Ti]?48/14×[N] (1) where [Ti] and [N] represent a Ti content (percent by mass) and a N content (percent by mass), respectively, of the steel sheet.

Abstract: A carbon steel sheet having high formability due to a microscopic and uniform carbide distribution and having a good characteristic of final heat treatment, and a manufacturing method thereof. The carbon steel sheet having excellent formability includes, in wt %, C at 0.2-0.5%, Mn at 0.1-1.2%, Si at less than or equal to 0.4%, Cr at less than or equal to 0.5%, Al at 0.01-0.1%, S at less than or equal to 0.012%, Ti at less than or equal to 0.5×48/14×[N]% to 0.03% when the condition of B and N is not satisfied, B at 0.0005-0.0080%, N at less than or equal to 0.006%, Fe, and extra inevitable elements; an average size of carbide is less than or equal to 1 ?m; and an average grain size of ferrite is less than or equal to 5 ?m.

Abstract: The present invention is the thin steel sheet containing C, Si, Mn, P, S, Al, Mo, Ti, B, and N wherein a value Z calculated by the equation described below is 2.0-6.0, an area ratio against all the structure is 1% or above for retained austenite and 80% or above for total of bainitic ferrite and martensite, a mean axis ratio of the retained austenite crystal grain is 5 or above, and tensile strength is 980 MPa or above where Value Z=9×[C]+[Mn]+3×[Mo]+490×[B]+7×[Mo]/{100×([B]+0.001),and the thin steel sheet has 980 MPa or above tensile strength and enhanced hydrogen embrittlement resistance properties.

Abstract: A high carbon steel sheet having a chemical composition containing C: 0.20% to 0.50%, Si: 1.0% or less, Mn: 2.0% or less, P: 0.03% or less, S: 0.02% or less, sol. Al: 0.08% or less, N: 0.02% or less, and the remainder composed of Fe and incidental impurities, on a percent by mass basis, and a microstructure composed of ferrite and cementite, wherein the fraction of pro-eutectoid ferrite, among the ferrite, in the whole steel microstructure is 20% or more and less than 50%, the average grain size dc of the cementite in the region from the position at one-quarter of the sheet thickness of the steel sheet to the sheet thickness center is 0.50 to 1.5 ?m, and the average grain size ds of the cementite in the region from the surface of the steel sheet to the position at one-quarter of the sheet thickness satisfies ds/dc?0.8.

Abstract: This hot-rolled steel sheet contains, in terms of mass %, C: 0.015% or more to less than 0.040%; Si: less than 0.05%; Mn: 0.9% or more to 1.8% or less; P: less than 0.02%; S: less than 0.01%; Al: less than 0.1%; N: less than 0.006%; and Ti: 0.05% or more to less than 0.11%, with the remainder being Fe and inevitable impurities, wherein Ti/C is in a range of 2.5 or more to less than 3.5, Nb, Zr, V, Cr, Mo, B and W are not included, a microstructure includes a mixed microstructure of polygonal ferrite and quasi-polygonal ferrite in a proportion of greater than 96%, a maximum tensile strength is 520 MPa or more and less than 720 MPa, an aging index AI is more than 15 MPa, a product of a hole expansion ratio (?) % and a total elongation (El) % is 2350 or more, and a fatigue limit is 200 MPa or more.

Abstract: A high strength hot rolled steel sheet having excellent blanking workability is provided. The composition contains C: 0.050 to 0.15%, Si: 0.1 to 1.5%, Mn: 1.0 to 2.0%, P: 0.03% or less, S: 0.0030% or less, Al: 0.01 to 0.08%, Ti: 0.05 to 0.15%, N: 0.005% or less, and the balance being Fe and unavoidable impurities. More than 95% of the microstructure is formed of a bainite phase in terms of area fraction. Average grain diameters of the bainite phase in a region having a thickness equal to ¼ of the sheet thickness from the surface in the sheet thickness direction is 5 ?m or less in an L-direction cross section and 4 ?m or less in a C-direction cross section. The number of crystal grains extended in the rolling direction and having an aspect ratio of 5 or more is 7 or less in a sheet thickness center portion.

Abstract: A hot rolled steel sheet includes, as a chemical composition, at least one selected from Ti, REM, and Ca, and includes, as a metallographic structure, a ferrite as a primary phase, at least one of a martensite and a residual austenite as a secondary phase, and plural inclusions, wherein a total length in the rolling direction of both inclusion-cluster whose length in the rolling direction is 30 ?m or more and independent-inclusion whose length in the rolling direction is 30 ?m or more is 0 mm to 0.25 mm per 1 mm2.

Abstract: The present invention provides a bainite-containing-type high-strength hot-rolled steel sheet. The steel sheet, containing C: greater than 0.07 to 0.2%, Si: 0.001 to 2.5%, Mn: 0.01 to 4%, P: 0.15% or less, S: 0.03% or less, N: 0.01% or less, Al: 0.001 to 2% and a balance being composed of Fe and impurities, has an average value of pole densities of the {100}<011> to {223}<110> orientation group at a sheet thickness center portion being a range of ? to ? in sheet thickness from the surface of the steel sheet is 4.0 or less, and a pole density of the {332}<113> crystal orientation is 4.8 or less, an average crystal grain diameter is 10 ?m or less and vTrs is ?20° C. or lower, and a microstructure is composed of 35% or less in a structural fraction of pro-eutectoid ferrite and a balance of a low-temperature transformation generating phase.

Abstract: The present invention provides a low-alloy high-purity ferritic stainless steel sheet provided with improved oxidation resistance and high-temperature strength by utilizing Sn addition in trace amounts without relying on excessive alloying of Al and Si which reduces fabricability and weldability or addition of rare elements such as Nb, Mo, W, and rare earths, and a process for producing the same. The high-purity ferritic stainless steel sheet includes C: 0.001 to 0.03%, Si: 0.01 to 2%, Mn: 0.01 to 1.5%, P: 0.005 to 0.05%, S: 0.0001 to 0.01%, Cr: 16 to 30%, N: 0.001 to 0.03%, Al: 0.05 to 3%, and Sn: 0.01 to 1% (% by mass), with the remainder being Fe and unavoidable impurities. A stainless steel slab having such steel components is heated, wherein an extraction temperature is 1100 to 1250° C., and a winding temperature after hot rolling is 650° C. or lower. A hot-rolled sheet is annealed at 900 to 1050° C., and cooled at 10° C./sec or less over a temperature range of 550 to 850° C.

Abstract: This hot-rolled ferritic stainless steel sheet has a steel composition containing, in terms of % by mass: 0.02% or less of C; 0.02% or less of N; 0.1% to 1.5% of Si; 1.5% or less of Mn; 0.035% or less of P; 0.010% or less of S; 1.5% or less of Ni; 10% to 20% of Cr; 1.0% to 3.0% of Cu; 0.08% to 0.30% of Ti; and 0.3% or less of Al, with the balance being Fe and unavoidable impurities, and the hot-rolled ferritic stainless steel sheet has a Vickers hardness of less than 235 Hv.

Abstract: A steel having a composition that includes C: 0.05 to 0.15%, Si: 0.2 to 1.2%, Mn: 1.0 to 2.0%, Al: 0.005 to 0.10%, N: 0.006% or less, and at least one selected from Ti: 0.03 to 0.13%, Nb: 0.02 to 0.10%, and V: 0.02 to 0.15% is subjected to rough rolling at a reduction of 80% or more and finish rolling at a finish rolling delivery temperature in the range of 800 to 950° C. The finish rolled sheet is subjected to cooling including cooling the finish rolled sheet from the finish rolling delivery temperature to a cooling end temperature in the range of 550 to 610° C. at an average cooling rate of 25° C./sec. or more and cooling the finish rolled sheet from the cooling end temperature of the previous process to a coiling temperature at an average cooling rate of 100° C./sec. or more.

Abstract: A high-strength, high-workability steel sheet for cans contains 0.070% to less than 0.080% C, 0.003% to 0.10% Si, 0.51% to 0.60% Mn, and the like on a mass basis and has a tensile strength of 500 MPa or more and a yield elongation of 10% or more. The average size and elongation rate of crystal grains are 5 ?m or more and 2.0 or less, respectively, in cross section in the rolling direction thereof. The hardness difference obtained by subtracting the average Vickers hardness of a cross section ranging from a surface to a depth equal to one-eighth of the thickness of the sheet from the average Vickers hardness of a cross section ranging from a depth equal to three-eighths of the sheet thickness to a depth equal to four-eighths of the sheet thickness is 10 points or more and/or the maximum Vickers hardness difference is 20 points or more.

Abstract: A steel sheet contains, on a mass percent basis, 0.03%-0.12% C, 0.5% or less Si, 0.8%-1.8% Mn, 0.030% or less P, 0.01% or less S, 0.005%-0.1% Al, 0.01% or less N, 0.035%-0.100% Ti, and the balance being Fe and incidental impurities and has microstructures with a fraction of polygonal ferrite of 80% or more, the polygonal ferrite having an average grain size of 5 to 10 ?m. The amount of Ti present in a precipitate having a size of less than 20 nm is 70% or more of the value of Ti* calculated using expression (1): Ti*=[Ti]?48×[N]/14??(1) where [Ti] and [N] represent a Ti content (percent by mass) and a N content percent by mass), respectively, of the steel sheet.

Abstract: A thin high strength steel sheet having excellent formability has a composition which includes, by mass %, 0.08 to 0.15% of C, 0.5 to 1.5% of Si, 0.5 to 1.5% of Mn, 0.01 to 0.1% of Al, and 0.005% or less of N to form a hot rolled sheet is conducted.

Abstract: The present invention provides a steel sheet with chemical components including, by mass%, 0.18-0.35% of C, 1.0%-3.0% of Mn, 0.01%-1.0% of Si, 0.001%-0.02% of P, 0.0005%-0.01% of S, 0.001%-0.01% of N, 0.01%-1.0% of Al, 0.005%-0.2% of Ti, 0.0002%-0.005% of B, and 0.002%-2.0% of Cr, and the balance of Fe and inevitable impurities, wherein: by volume%, a fraction of the ferrite is 50% or more, and a fraction of a non-recrystallized ferrite is 30% or less; and Cr?/CrM is 2 or less, where Cr? is a concentration of Cr subjected to solid solution in iron carbide and CrM is a concentration of Cr subjected to solid solution in a base material, or Mn0/MnM is 10 or less, where Mn0 is a concentration of Mn subjected to solid solution in an iron carbide, and MnM is a concentration of Mn subjected to solid solution in a base material.

Abstract: A high-strength hot-rolled steel sheet having excellent formability has a composition containing, by mass, 0.04% to 0.1% of C, 0.3% to 1.3% of Si, 0.8% to 1.8% of Mn, 0.03% or less of P, 0.005% or less of S, 0.005% or less of N, 0.005% to 0.1% of Al, and at least one element selected from 0.002% to less than 0.03% of Ti, 0.002% to less than 0.03% of V, and 0.002% to less than 0.02% of Nb, the balance being Fe and incidental impurities. The steel sheet has a microstructure in which the area fraction of ferrite phase in the entire structure is 85% or more, the area fraction of bainite phase in the entire structure is 10% or less, the area fraction of phases other than the ferrite and bainite phases in the entire structure is 5% or less, and the area fraction of acicular ferrite phase in the entire ferrite phase is 30% to less than 80%.

Abstract: A high strength hot-rolled steel sheet with a tensile strength of not less than 590 MPa which exhibits excellent bake hardenability and stretch-flangeability has a chemical composition including, in terms of mass %, C at 0.040 to 0.10%, Si at not more than 0.3%, Mn at 1.7 to 2.5%, P at not more than 0.030%, S at not more than 0.005%, Al at not more than 0.1% and N at 0.006 to 0.025%, and microstructure wherein a bainite phase represents not less than 60%, the total of a ferrite phase and a pearlite phase represents not more than 10%, and the bainite phase includes grains among which cementite grains have been precipitated at not less than 1.4×104 grains/mm2 and the cementite grains have an average grain diameter of not more than 1.5 ?m.

Abstract: A high strength steel sheet excellent in warm stamp formability and a method for manufacturing the same. The steel has a composition containing, in terms of % by mass, C: 0.01 to 0.2%, Si: 0.5% or lower, Mn: 2% or lower, P: 0.03% or lower, S: 0.01% or lower, Al: 0.07% or lower, and N: 0.01% or lower and further containing one or two or more elements selected from Ti, Nb, V, Mo, W, and B.

Abstract: A high-strength steel sheet has a chemical composition comprising C: 0.05-0.20%, Si: 0.02-3.0%, Mn: 0.5-3.0%, P: at most 0.5%, S: at most 0.05%, Cr: 0.05-1.0%, sol. Al: 0.01-1.0%, one or more elements selected from the group consisting of Ti, Nb, Mo, V, and W: a total of 0.002-0.03%, and a remainder of Fe and impurities. The sheet has an average grain diameter of ferrite of at most 3.0 ?m at least in a region of 100-200 ?m in the sheet thickness direction from the surface of the steel sheet. The average spacing in the sheet thickness direction of the remaining structure in this region is at most 3.0 ?m. Mechanical properties include at least 750 MPa tensile strength and at least 13,000 MPa·% (tensile strength×elongation).

Abstract: Hot-rolled steel has a chemical composition containing, by mass%, C: 0.18% or more and 0.29% or less, N: 0.0050% or less, Ti: 0.002% or more and 0.05% or less, B: 0.0005% or more and 0.0050% or less, and appropriately controlled amounts of Si, Mn, P, S, Al, and a tensile strength of 500 MPa or less with a variation in tensile strength of 60 MPa or less throughout a region including the edges in the width direction of the steel sheet, and having excellent cold formability and hardenability.

Abstract: Provided is a method of manufacturing a high-carbon hot-rolled steel sheet, including the steps of i) preparing high-carbon steel materials comprising C: 0.7 to 0.9%, Si: 0.5% or less, Mn: 0.1 to 1.5%, Cr: 0.5% or less, P: 0.05% or less, and S: 0.03% or less in wt % and remaining Fe and other inevitable impurities; ii) heating the high-carbon steel materials again and manufacturing a steel sheet by performing hot rolling in an austenite region in which a finishing temperature for the hot rolling is an Ar3 transformation temperature or higher; iii) rapidly cooling the steel sheet at 520 to 620° C. before phase transformation is started in a Run-Out Table (ROT); iv) uniformly maintaining a cooling retention temperature so that the cooled steel sheet is subject to phase transformation in any one temperature between 520 to 620° C.; and v) winding the steel sheet in the cooling retention temperature. Also provided is the high-carbon steel sheet made by the above-described method.

Abstract: A high-strength hot-rolled steel sheet containing C: 0.05 to 0.15%, Si: no more than 1.50% (excluding 0%), Mn: 0.5 to 2.5%, P: no more than 0.035% (excluding 0%), S: no more than 0.01% (including 0%), Al: 0.02 to 0.15%, and Ti: 0.05 to 0.2%, which is characterized in that its metallographic structure is composed of 60 to 95 vol % of bainite and solid solution-hardened or precipitation-hardened ferrite (or ferrite and martensite) and its fracture appearance transition temperature (vTrs) is no higher than 0° C. as obtained by impact tests (% in terms of % by weight).

Abstract: A steel sheet including C at 0.05 to 0.15%, Si at 0.2 to 1.2%, Mn at 1.0 to 2.0%, P at not more than 0.04%, S at not more than 0.0030%, Al at 0.005 to 0.10%, N at not more than 0.005% and Ti at 0.03 to 0.13%, the balance being Fe and inevitable impurities, includes surface regions having an area fraction of bainite of less than 80% and an area fraction of a ferrite phase with a grain diameter of 2 to 15 ?m of not less than 10%, the surface regions extending from both surfaces of the steel sheet each to a depth of 1.5 to 3.0% relative to a total sheet thickness, as well as an inner region other than the surface regions having an area fraction of a bainite phase of more than 95%, and has a tensile strength of not less than 780 MPa.

Abstract: The steel sheet includes C: 0.04 to 0.12%, Si: 0.5 to 1.2%, Mn: 1.0 to 1.8%, P: not more than 0.03%, S: not more than 0.0030%, Al: 0.005 to 0.20%, N: not more than 0.005% and Ti: 0.03 to 0.13%, the balance being Fe and inevitable impurities, includes a microstructure containing a bainite phase at an area fraction exceeding 95% and having an average grain diameter of not more than 3 ?m, has a difference ?Hv1 of not more than 50 between a Vickers hardness value at 50 ?m from the surface and a Vickers hardness value at ¼ of a sheet thickness, has a difference ?Hv2 of not more than 40 between the Vickers hardness value at ¼ of the sheet thickness and a Vickers hardness value at ½ of the sheet thickness.

Abstract: A high carbon steel wire material which is made of high carbon steel as a raw material for wire products such as steel cords, bead wires, PC steel wires and spring steel, allows for these wire products to be manufactured efficiently at a high wire drawing rate and has excellent wire drawability and a manufacturing process thereof. This high carbon steel wire material is made of a steel material having specific contents of C, Si, Mn, P, S, N, Al and O, and the Bcc-Fe crystal grains of its metal structure have an average crystal grain diameter (Dave) of 20 ?m or less and a maximum crystal grain diameter (Dmax) of 120 ?m or less, preferably an area ratio of crystal grains having a diameter of 80 ?m or more of 40% or less, an average sub grain diameter (dave) of 10 ?m or less, a maximum sub grain diameter (dmax) of 50 ?m or less and a (Dave/dave) ratio of the average crystal grain diameter (Dave) to the average sub grain diameter (dave) of 4.5 or less.

Abstract: The present invention provides a wire rod with a composition at least including: C: 0.95-1.30 mass %; Si: 0.1-1.5 mass %; Mn: 0.1-1.0 mass %; Al: 0-0.1 mass %; Ti: 0-0.1 mass %; P: 0-0.02 mass %; S: 0-0.02 mass %; N: 10-50 ppm; O: 10-40 ppm; and a balance including Fe and inevitable impurities, wherein 97% or more of an area in a cross-section perpendicular to the longitudinal direction of the wire rod is occupied by a pearlite, and 0.5% or less of an area in a central area in the cross-section and 0.5% or less of an area in a first surface layer area in the cross-section are occupied by a pro-eutectoid cementite.

Abstract: Described is a high tensile strength hot rolled steel sheet having high strength and formability, and a manufacturing method. It has tensile strength?980 MPa and excellent formability, and specifically identified ranges by mass % of C, Si, Mn, P, S, N, Al, Ti, V, Solute V, and Solute Ti; (ii) microstructure with fine carbides dispersion precipitated therein, the fine carbides containing Ti and V and having the average particle diameter<10 nm, as well as volume ratio with respect to the entire microstructure?0.007; and matrix as ferrite phase having area ratio with respect to the entire microstructure?97%. C, Ti, V, S and N satisfy (1) Ti?0.08+(N/14×48+S/32×48) and (2) 0.8?(Ti/48+V/51)/(C/12)?1.2, where “C”, “Ti”, “V”, “S” and “N” represent contents (mass %) of corresponding elements, respectively.

Abstract: A high strength hot-rolled steel sheet has a composition containing more than 0.035% to 0.055% C, 0.2% or less Si, 0.35% or less Mn, 0.03% or less P, 0.03% or less S, 0.1% or less Al, 0.01% or less N, 0.08% to 0.25% Ti, and 0.0005% to 0.0035% B on a mass basis, solute B being 0.0005% or more, the remainder being Fe and unavoidable impurities; a matrix containing a ferrite phase having an area fraction of more than 95%; a microstructure in which Ti carbides having an average grain size of less than 10 nm are finely precipitated in grains of the ferrite phase and the volume fraction of the Ti carbides is 0.0015 to 0.007; and a tensile strength of 780 MPa or more.

Abstract: The present invention provides a method of cooling a hot-rolled steel strip which has passed through a finishing rolling, including: cooling the hot-rolled steel strip from a first temperature of not lower than 600° C. and not higher than 650° C. to a second temperature of not higher than 450° C. with cooling water having the water amount density of not lower than 4 m3/m2/min and not higher than 10 m3/m2/min, wherein with respect to the area of the target surface, the area of a portion where a plurality of spray jets of the cooling water directly strikes on the target surface is at least 80%.

Abstract: A high strength hot-rolled steel sheet has a tensile strength of not less than 780 MPa and exhibits excellent stretch flangeability and excellent fatigue resistance. A steel has a composition containing C at 0.05 to 0.15%, Si at 0.2 to 1.2%, Mn at 1.0 to 2.0%, P at not more than 0.04%, S at not more than 0.005%, Ti at 0.05 to 0.15%, Al at 0.005 to 0.10% and N at not more than 0.007%.

Abstract: A method of making hot rolled steel sheet having a dual phase microstructure with a martensite phase of less than 35% by volume and a ferrite phase of more than 50% by volume and a composition containing by percent weight: 0.01?C?0.2; 0.3?Mn?3; 0.2?Si?2; 0.2?Cr+Ni?2; 0.01?Al?0.10; Mo less than about 0.2%, 0.0005?Ca?0.01, with the balance iron and incidental ingredients. Hot rolled sheet for cold rolling, the silicon range may be from about 0.05% to about 2%, and the amount of molybdenum may be up to 0.5%. Also, the hot rolled steel sheet has a tensile strength of at least 500 megapascals, a hole expansion ratio more than about 50%, and a yield strength/tensile strength ratio less than 70%.

Abstract: Steel sheet having a composition of ingredients containing substantially, by mass %, C: 0.005 to 0.200%, Si: 2.50% or less, Mn: 0.10 to 3.00%, N: 0.0100% or less, Nb: 0.005 to 0.100%, and Ti: 0.002 to 0.150% and satisfying the relationship of Ti?48/14×N?0.0005, having a sum of the X-ray random intensity ratios of the {100}<001> orientation and the {110}<001> orientation of a ? sheet thickness part of 5 or less, having a sum of the maximum value of the X-ray random intensity ratios of the {110}<111> to {110}<112> orientation group and the X-ray random intensity ratios of the {211}<111> orientation of 5 or more, and having a high rolling direction Young's modulus measured by the static tension method and a method of production of the same are provided.

Abstract: This high strength hot-rolled steel sheet includes: in terms of percent by mass, C: 0.05 to 0.12%; Si: 0.8 to 1.2%; Mn: 1.6 to 2.2%; Al: 0.30 to 0.6%; P: 0.05% or less; S: 0.005% or less; and N: 0.01% or less, with the remainder being Fe and unavoidable impurities, wherein a microstructure includes specific ranges (in area %) of ferrite phases as well as martensite phases, and a maximum concentration of Al detected by a glow discharge emission spectroscopic analysis is in a range of 0.75 mass % or less in a region from a surface of the steel sheet to a thickness of 500 nm after being acid-pickled.

Abstract: A carbon steel sheet having high formability due to a microscopic and uniform carbide distribution and having a good characteristic of final heat treatment, and a manufacturing method thereof. The carbon steel sheet having excellent formability includes, in wt %, C at 0.2-0.5%, Mn at 0.1-1.2%, Si at less than or equal to 0.4%, Cr at less than or equal to 0.5%, Al at 0.01-0.1%, S at less than or equal to 0.012%, Ti at less than or equal to 0.5×48/14×[N] % to 0.03% when the condition of B and N is not satisfied, B at 0.0005-0.0080%, N at less than or equal to 0.006%, Fe, and extra inevitable elements; an average size of carbide is less than or equal to 1 ?m; and an average grain size of ferrite is less than or equal to 5 ?m.

Abstract: A carbon steel sheet having high formability due to a microscopic and uniform carbide distribution and having a good characteristic of final heat treatment, and a manufacturing method thereof. The carbon steel sheet having excellent formability, includes, in wt %, C at 0.2-0.5%, Mn at 0.1-1.2%, Si at less than or equal to 0.4%, Cr at less than or equal to 0.5%, Al at 0.01-0.1%, S at less than or equal to 0.012%, Ti at less than or equal to 0.5×48/14×[N]% when the condition of B(atomic %)/N(atomic %)>1 is satisfied or by 0.5×48/14×[N]% to 0.03% when the condition of B and N is not satisfied, B at 0.0005-0.0080%, N at less than or equal to 0.006%, Fe, and extra inevitable elements; an average size of carbide is less than or equal to 1 ?m; and an average grain size of ferrite is less than or equal to 5 ?m.

Abstract: A steel sheet contains, on a mass percent basis, 0.03%-0.12% C, 0.5% or less Si, 0.8%-1.8% Mn, 0.030% or less P, 0.01% or less S, 0.005%-0.1% Al, 0.01% or less N, 0.035%-0.100% Ti, and the balance being Fe and incidental impurities and has microstructures with a fraction of polygonal ferrite of 80% or more, the polygonal ferrite having an average grain size of 5 to 10 ?m. The amount of Ti present in a precipitate having a size of less than 20 nm is 70% or more of the value of Ti* calculated using expression (1): Ti*=[Ti]?48×[N]/14??(1) where [Ti] and [N] represent a Ti content (percent by mass) and a N content percent by mass), respectively, of the steel sheet.

Abstract: High-strength steel sheet excellent in hole-expandability and ductility, characterized by; comprising, in mass %, C: not less than 0.01% and not more than 0.20%, Si: not more than 1.5%, Al: not more than 1.5%, Mn: not less than 0.5% and not more than 3.5%, P: not more than 0.2%, S: not less than 0.0005% and not more than 0.009%, N: not more than 0.009%, Mg: not less than 0.0006% and not more than 0.01%, O: not more than 0.005% and Ti: not less than 0.01% and not more than 0.20% and/or Nb: not less than 0.01% and not more than 0.10%, with the balance consisting iron and unavoidable impurities, having Mn %, Mg %, S % and O % satisfying equations (1) to (3), and having the structure primarily comprising one or more of ferrite, bainite and martensite. [Mg %]?([O %]/16×0.8)×24??(1) [S %]?([Mg %]/24?[O %]/16×0.8+0.00012)×32??(2) [S %]?0.

Abstract: A high-strength steel sheet includes a composition containing, in mass percent, 0.08% to 0.20% of carbon, 0.2% to 1.0% of silicon, 0.5% to 2.5% of manganese, 0.04% or less of phosphorus, 0.005% or less of sulfur, 0.05% or less of aluminum, 0.07% to 0.20% of titanium, and 0.20% to 0.80% of vanadium, the balance being iron and incidental impurities.

Abstract: Disclosed is a ferritic stainless steel sheet which has excellent corrosion resistance against sulfuric acid in the high-temperature environment and shows less surface roughness at a bent part which is bent at 90° or more. Specifically disclosed is a ferritic stainless steel sheet which has the following chemical composition: C: 0.02 mass % or less, Si: 0.05 to 0.8 mass %, Mn: 0.5 mass % or less, P: 0.04 mass % or less, S: 0.010 mass % or less, Al: 0.10 mass % or less, Cr: 20 to 24 mass % Cu: 0.3 to 0.8 mass %, Ni: 0.5 mass % or less, Nb: 0.20 to 0.55 mass %, and N: 0.02 mass % or less, with the remainder being Fe and unavoidable impurities; and which has such a structure that the maximum particle diameter of an S-containing precipitate is 5 ?m or smaller.