Abstract: A bioabsorbable implant for non-luminal region comprising: a core structure including a magnesium alloy having a predetermined shape; a first corrosion-resistant layer containing a magnesium fluoride layer as a main component formed on the core structure via fluorination of a surface of the magnesium alloy; and a second corrosion-resistant layer containing a parylene formed on the magnesium fluoride layer.

Abstract: A magnesium alloy which has excellent tensile strength and elongation at a room temperature, as well as an excellent heat resistance represented by creep resistance is obtained. The magnesium alloy is produced which comprises 3.0% by mass or more and less than 6.0% by mass of Al, 0.10% by mass or more and 0.60% by mass or less of Mn, more than 0.50% by mass and less than 2.0% by mass of Ca, and more than 0.10% by mass and less than 0.40% by mass of Si, and has a balance composed of Mg and unavoidable impurities.

Abstract: A magnesium alloy containing: Al: 0.2-1.6 wt. % Zn: 0.2-0.8 wt. % 5 Mn: 0.1-0.5 wt. % Zr 0-0.5 wt. % La: 1-3.5 wt. % Y: 0.05-3.5 wt. % Ce: 0-2 wt. % 10 Nd: 0-2 wt. % Gd: 0-3 wt. % Pr: 0-0.5 wt. % Be: 0-20 ppm the balance being Mg and incidental elements.

Abstract: An apparatus for testing the edge strength of a discrete sheet of material such as glass where the sheet has an irregular free-form shaped outline is disclosed. The apparatus can include a plurality of assemblies configured for selectively applying a 3-point bending load on an edge of the sheet of material in a test region of the apparatus, a detection mechanism that optically measures strain in the sheet of material in the region, and a processor that determines the stress in the sheet based on the measured strain by calculating the stress that would be required to produce the measured strain in the sheet of material.

Abstract: The present invention relates to a magnesium alloy sheet and a manufacturing method thereof. In detail, the magnesium alloy sheet includes 0.5 to 3.5 wt % of Al, 0.5 to 1.5 wt % of Zn, 0.1 to 1.0 wt % of Ca, 0.01 to 1.0 wt % of Mn, a remainder of Mg, and other inevitable impurities with respect to an entire 100 wt % of a magnesium alloy sheet, wherein an average crystal grain size of the magnesium alloy sheet is 3 to 15 ?m, the magnesium alloy sheet includes a stringer, and a length of the stringer in a rolling direction (RD) is equal to or less than the maximum value of 50 ?m.

Abstract: A magnesium alloy is provided that includes: 5.0 mass % or more and 15.0 mass % or less of Al; 2.5 mass % or more and 7.0 mass % or less of Sr; 0.05 mass % or more and less than 3.0 mass % of Ca; and 0.1 mass % or more and 0.6 mass % or less of Mn, with a remainder including Mg and inevitable impurities.

Abstract: To provide a magnesium alloy having high incombustibility, high strength and high ductility together. A magnesium alloy including Ca in an amount of “a” atomic %, Al in an amount of “b” atomic % and a residue of Mg, including (Mg, Al)2Ca in an amount of “c” volume %, wherein “a”, “b” and “c” satisfy the following equations (1) to (4), and having the (Mg, Al)2Ca dispersed therein. 3?a?7??(1) 4.5?b?12??(2) 1.2?b/a?3.

Abstract: The present disclosure is directed to a method of physically separating and electrically isolating the chamber where the ohmic heating of the feedstock occurs by delivering current through the electrodes (heating barrel), from the chamber where the feedstock deformation and flow through the runner takes place by the motion of the plungers (forming barrel). The method also includes transferring the feedstock from the heating barrel to the forming barrel between the heating and the forming processes at a high enough rate such that negligible cooling and no substantial crystallization of the feedstock occurs during the transfer.

Abstract: A magnesium alloy structural member having excellent corrosion resistance is provided. The magnesium alloy structural member includes a magnesium alloy substrate that contains more than 7.5% by mass of Al and an anticorrosive layer formed on a surface of the substrate by chemical conversion treatment. The substrate contains a precipitate, typically, particles dispersed therein. The particles are made of an intermetallic compound containing at least one of Al and Mg and have an average particle size of 0.05 ?m or more and 1 ?m or less. The total area of the particles accounts for 1% by area or more and 20% by area or less. The anticorrosive layer includes a lower sublayer and a surface sublayer on the substrate in this order. The surface sublayer is denser than the lower sublayer. The substrate of the magnesium alloy structural member has high corrosion resistance because of a high Al content.

Abstract: Magnesium-based hydrogen storage alloys with addition of transition and rare earth elements were produced by conventional induction melting and by rapid solidification. The magnesium based-alloys of this invention posses reversible hydrogen storage capacities ranging from 3 to over 6 wt. %, and excellent performance on the hydrogen absorption and desorption kinetics.

Abstract: To provide a magnesium alloy having high incombustibility, high strength and high ductility together. A magnesium alloy including Ca in an amount of “a” atomic %, Al in an amount of “b” atomic % and a residue of Mg, including (Mg, Al)2Ca in an amount of “c” volume %, wherein “a”, “b” and “c” satisfy the following equations (1) to (4), and having the (Mg, Al)2Ca dispersed therein. 3?a?7??(1) 4.5?b?12??(2) 1.2?b/a?3.

Abstract: Magnesium alloys comprising a long period stacking order (LPSO) phase having an 14H-i or an 18R-i structure are provided. The alloys comprise magnesium as a majority element, a first alloying element that is larger than magnesium and a second alloying element that is smaller than magnesium. The first alloying elements include non-rare earth elements.

Abstract: The invention offers a magnesium alloy sheet having excellent warm plastic formability, a production method thereof, and a formed body produced by performing warm plastic forming on this sheet. The magnesium alloy sheet is produced by giving a predetermined strain to a rolled sheet RS that is not subjected to a heat treatment aiming at recrystallization. The sheet is not subjected to the foregoing heat treatment even after the giving of a strain. The strain is given through the process described below. A rolled sheet RS is heated in a heating furnace 10. The heated rolled sheet RS is passed between rollers 21 to give bending to the rolled sheet RS. The giving of a strain is performed such that the strain-given sheet has a half peak width of 0.20 deg or more and 0.59 deg or less in a (0004) diffraction peak in monochromatic X-ray diffraction. The alloy sheet exhibits high plastic deformability by forming continuous recrystallization during warm plastic forming through the use of the remaining strain.

Abstract: A magnesium alloy material having excellent impact resistance is provided. The magnesium alloy material is composed of a magnesium alloy that contains more than 7.5% by mass of Al and has a Charpy impact value of 30 J/cm2 or more. Typically, the magnesium alloy material has an elongation of 10% or more at a tension speed of 10 m/s in a high-speed tensile test. The magnesium alloy is composed of a precipitate, typically made of an intermetallic compound containing at least one of Al and Mg, and contains particles having an average particle size of 0.05 ?M or more and 1 ?m or less dispersed therein. The total area of the particles accounts for 1% by area or more and 20% by area or less. The magnesium alloy material containing fine precipitate particles dispersed therein has high impact absorption capacity through dispersion strengthening and has excellent impact resistance.

Abstract: A magnesium alloy material having high corrosion resistance is provided. The magnesium alloy material contains a magnesium alloy containing 7.3% to 16% by mass Al, wherein a region having an Al content of 0.8x % by mass or more and 1.2x % by mass or less occupies 50% by area or more, a region having an Al content of 1.4x % by mass or more occupies 17.5% by area or less, wherein x % by mass denotes the Al content of the entire magnesium alloy material, and there is substantially no region having an Al content of 4.2% by mass or less. The magnesium alloy material has small variations in Al concentration and includes a few regions having a very low Al content, thereby effectively preventing and retarding local corrosion. Thus, the magnesium alloy material has higher corrosion resistance than die-cast components having the same Al content.

Abstract: Disclosed are a magnesium mother alloy, a manufacturing method thereof, a metal alloy using the same, and a method of manufacturing the metal alloy. In particular, there are provided a magnesium mother alloy with improved oxidation and ignition properties, and a manufacturing method thereof, and also provided a metal alloy with low cost that is suitable for design purposes using the magnesium mother alloy, and a method of manufacturing the metal alloy. The magnesium mother alloy includes a plurality of magnesium grains, and scandium dissolved in the magnesium grains, or a scandium compound crystallized at grain boundaries which are not inside but outside the magnesium grains. Also, the metal alloy suitable for design purposes is manufactured at low cost by adding the magnesium mother alloy containing scandium into a magnesium alloy or an aluminum alloy.

Abstract: A magnesium-based alloy powder is made of a magnesium-based alloy that contains 0.2 mass % to 5 mass % of calcium, wherein the magnesium-based alloy powder has an average particle diameter of 100 ?m to 1,500 ?m, wherein the magnesium-based alloy powder has a particle average aspect ratio of 0.5 to 1, wherein the magnesium-based alloy powder has an apparent density of 0.2 g/cm3 to 1.2 g/cm3, and wherein the mean value of hardness variation index values obtained by dividing the difference of the maximum value and the minimum value of micro Vickers hardnesses taken at 10 measurement points in a particle cross section by the maximum value is 0.3 or less.

Abstract: Provided by the present invention are a fine crystallite high-function metal alloy member, a method for manufacturing the same, and a business development method thereof, in which a crystallite of a metal alloy including a high-purity metal alloy whose crystal lattice is a face-centered cubic lattice, a body-centered cubic lattice, or a close-packed hexagonal lattice is made fine with the size in the level of nanometers (10?9 m to 10?6 m) and micrometers (10?6 m to 10?3 m), and the form thereof is adjusted, thereby remedying drawbacks thereof and enhancing various characteristics without losing superior characteristics owned by the alloy.

Abstract: Disclosed herein is a non-heat treatable magnesium alloy sheet, including: 1˜3 wt % of aluminum (Al); 0.5˜3 wt % of tin (Sn); and a balance of magnesium, wherein the maximum deviation of average Vickers hardness (Hv) thereof, caused by center segregation and inverse segregation, is 10 Hv or less.

Abstract: The production of microstructured surfaces in magnesium alloys, containing zinc as the major alloying element, in particular in absorbable implants such as stents, wherein microstructures in sizes of up to 5 ?m (micrometers) are generated on a magnesium alloy base body of the absorbable implant, for example of the absorbable stent, by way of optionally combined, pickling and electrochemical micropolishing processes, and allow better adhesion of a polymer coating (including higher break resistance) and higher corrosion resistance. The microstructured surface is produced out of the bulk material and exhibits no delamination from the base material during the mechanical deformation of the implant.

Abstract: A method for reducing impurities in magnesium comprises: combining a zirconium-containing material with a molten low-impurity magnesium including no more than 1.0 weight percent of total impurities in a vessel to provide a mixture; holding the mixture in a molten state for a period of time sufficient to allow at least a portion of the zirconium-containing material to react with at least a portion of the impurities and form intermetallic compounds; and separating at least a portion of the molten magnesium in the mixture from at least a portion of the intermetallic compounds to provide a purified magnesium including greater than 1000 ppm zirconium. A purified magnesium including at least 1000 ppm zirconium and methods for producing zirconium metal using magnesium reductant also are disclosed.

Abstract: The present invention relates to an Mg—Al—Ca based master alloy for Mg alloys and to a production method therefor, and concerns an alloying master alloy used for magnesium or magnesium alloys. To this end, a feature of the invention is that, while the Ca:Al ration in the composition is maintained at between 7:3 and 1:9, based on percentages by weight in the alloy, a balance of Mg is added in an amount of up to 85% of the entire weight of the master alloy, based on percentage by weight. The production method comprises the steps of: preparing components of a master alloy by selecting a composition in which, while the Ca:Al ration in the composition is maintained at between 7:3 and 1:9, based on percentages by weight in the alloy, there is a balance of Mg in an amount of up to 85% of the entire weight of the master alloy, based on percentage by weight; sequentially melting Mg, Al and Ca; completely melting the components by applying an adequate amount of heat; and rapidly cooling the molten pool.

Abstract: Provided are a rolled Mg alloy material whose mechanical properties are locally different in a width direction, a Mg alloy structural member produced by plastically working the rolled Mg alloy material, and a method for producing the rolled Mg alloy material. The method for producing a rolled Mg alloy material includes rolling a Mg alloy material with a reduction roll. The reduction roll has three or more regions in the width direction. The temperature is controlled in each of the regions so that a difference between a maximum temperature and a minimum temperature exceeds 10° C. in the width direction of a surface of the reduction roll. The rolled state in the width direction is varied by varying a difference in temperature over the width direction of the reduction roll. As a result, it is possible to produce a rolled Mg alloy material whose mechanical properties are locally different in the width direction.

Abstract: A method of enhancing the ductility of magnesium alloy sheets containing 85% or more by weight of magnesium is described. An annealed, substantially strain free, sheet of generally uniform grain size is locally deformed in local regions to develop strained ‘islands’ of a predetermined strain embedded in a substantially strain-free matrix and then annealed. The deformed regions undergo recrystallization and grain growth while the remainder of the sheet suffers only minor change in grain size, leading to sheet with grains having a bimodal size distribution. The ductility of alloys processed in this way is significantly greater than the ductility of the unprocessed, uniform grain size alloy without compromise to the tensile strength of the alloy.

Abstract: Provided are an extruded aluminum (Al)-magnesium (Mg) material and a method of producing the same. An Al—Mg master alloy having a first Mg content is provided. An Al—Mg alloy having a second Mg content less than the first Mg content is prepared by adding the Al—Mg master alloy into molten Al and then casting the molten Al. An extruded Al—Mg material is prepared by extruding the Al—Mg alloy.

Abstract: Magnesium-based hydrogen storage alloys having metallic magnesium (Mg) and a magnesium-containing intermetallic compound (MgxMy wherein y is 1?x) and containing not less than 60 mass-% of magnesium in total, and having a phase of a primarily crystallized magnesium-containing intermetallic compound in its solidification structure.

Abstract: Provided is a composite material suitable for forming a part for continuous casting capable of producing cast materials of excellent surface quality for a long period of time and with which a molten metal is inhibited from flowing into a gap between a nozzle and a moving mold. A composite material (nozzle 1) includes a porous body 2 having a large number of pores and a filler incorporated in at least part of a portion that comes into contact with the molten metal, the portion being part of a surface portion of the porous body. The filler incorporated in the porous body 2 is at least one selected from a nitride, a carbide, and carbon.

Abstract: An implant made in total or in parts of a biodegradable magnesium alloy consisting of Y: 2.0-6.0% by weight, Nd: 1.5-4.5% by weight, Gd: 0-4.0% by weight, Dy: 0-4.0% by weight, Er: 0-4.0% by weight, Zr: 0.1-1.0% by weight, Li:0-0.2% by weight, Al: 0-0.3% by weight, under the condition that a) a total content of Er, Gd and Dy is in the range of 0.5-4.0% by weight and b) a total content of Nd, Er, Gd and Dy is in the range of 2.0-5.5% by weight, the balance being magnesium and incidental impurities up to a total of 0.3% by weight.

Abstract: The present invention relates to a desulfurizing agent of improved oxidation resistance, ignition resistance and productivity, and a method for manufacturing the desulfurizing agent. The desulfurizing agent may include a plurality of magnesium-aluminum alloy grains with grain boundaries, and a compound of one selected from consisting of magnesium and aluminum and one selected from consisting of alkaline metal and alkaline earth metal, the compound exists in the grain boundaries and is not inside but outside of the magnesium-aluminum alloy grains.

Abstract: A magnesium alloy material having excellent impact resistance is provided. The magnesium alloy material is composed of a magnesium alloy that contains more than 7.5% by mass of Al and has a Charpy impact value of 30 J/cm2 or more. Typically, the magnesium alloy material has an elongation of 10% or more at a tension speed of 10 m/s in a high-speed tensile test. The magnesium alloy is composed of a precipitate, typically made of an intermetallic compound containing at least one of Al and Mg, and contains particles having an average particle size of 0.05 ?M or more and 1 ?m or less dispersed therein. The total area of the particles accounts for 1% by area or more and 20% by area or less. The magnesium alloy material containing fine precipitate particles dispersed therein has high impact absorption capacity through dispersion strengthening and has excellent impact resistance.

Abstract: A method and apparatus is provided for processing a medical device formed from a bioabsorbable metallic material. The method begins by generating a beam of radiation onto the bioabsorbable metallic material. The radiation beam is transmitted through a fluid medium and onto a heat affected zone (HAZ) of the bioabsorbable metallic material to thereby cool the HAZ and reduce a concentration of oxygen surrounding the HAZ.

Abstract: One exemplary embodiment includes a cast alloy including Al present in an amount of about 6.5 wt % to about 9.0 wt %; Sn present in an amount of about 1.0 wt % to about 3.0 wt %; Ce present in an amount of about 0 wt % to about 1.0 wt %; and, Mg comprising a balance of the alloy minus an amount of minor and trace elements wherein Mg is present at an amount of greater than about 85 wt %.

Abstract: Provided is a magnesium alloy for room temperature, which is manufactured by adding CaO onto a surface of a molten magnesium alloy and exhausting the CaO through a reduction reaction of the CaO with the molten magnesium alloy. Resultantly, the magnesium alloy with CaO added has more improved room-temperature mechanical properties (tensile strength, yield strength, elongation) than magnesium alloys without using CaO. Furthermore, as the added amount of CaO increases, room-temperature mechanical properties (tensile strength, yield strength, elongation) increase as well.

Abstract: Magnesium alloys containing: Y: 2.0-6.0% by weight Nd: 0-4.0% by weight Gd: 0-5.5% by weight Dy: 0-5.5% by weight Er: 0-5.5% by weight Zr: 0.05-1.0% by weight Zn+Mn: <0.11% by weight, optionally other rare earths and heavy rare earths, the balance being magnesium and incidental impurities and the total content of Gd, Dy and Er is in the range of 0.3-12% by weight, wherein either the alloy contains low amounts of Yb and Sm and exhibits a corrosion rate as measured according to ASTM B117 of less than 30 Mpy, and/or the area percentage of any precipitated particles arising when the alloy is processed having an average particle size greater than 1 m and less than 15 m is less than 3%.

Abstract: The grain size of magnesium alloys is effectively refined and made smaller by the addition of a small amount of titanium. The effect of the reduction of grain size is often an improvement in the strength and processability of a cast magnesium alloy. Often less than about 0.1% by weight of titanium need be used. It may be preferred to incorporate the titanium with another alloying constituent (such as aluminum) for addition to a melt of a magnesium base alloy.

Abstract: A Ti particle-dispersed magnesium-based composite material is a material having titanium particles uniformly dispersed in a magnesium matrix, and is characterized by having a titanium-aluminum compound layer at an interface between the magnesium alloy matrix and the titanium particles dispersed in the magnesium alloy matrix.

Abstract: The present invention provides a method for producing a magnesium alloy sheet capable of producing a magnesium alloy sheet having excellent plastic workability such as press workability. The method of the present invention includes rolling a magnesium alloy blank with a reduction roll. The rolling includes controlled rolling performed under the following conditions (1) and (2) wherein M (% by mass) is the Al content in a magnesium alloy constituting the blank: (1) the surface temperature Tb (° C.) of the magnesium alloy blank immediately before insertion into the reduction roll satisfies the following expression: 8.33×M+135?Tb?8.33×M+165 wherein 1.0?M?10.0; and (2) the surface temperature Tr of the reduction roll is 150° C. to 180° C.

Abstract: Disclosed are a magnesium mother alloy, a manufacturing method thereof, a metal alloy using the same, and a method of manufacturing the metal alloy. In particular, there are provided a magnesium mother alloy with improved oxidation and ignition properties, and a manufacturing method thereof, and also provided a metal alloy with low cost that is suitable for design purposes using the magnesium mother alloy, and a method of manufacturing the metal alloy. The magnesium mother alloy includes a plurality of magnesium grains, and scandium dissolved in the magnesium grains, or a scandium compound crystallized at grain boundaries which are not inside but outside the magnesium grains. Also, the metal alloy suitable for design purposes is manufactured at low cost by adding the magnesium mother alloy containing scandium into a magnesium alloy or an aluminum alloy.

Abstract: A magnesium alloy member includes a member main body formed of a magnesium alloy containing aluminum, and an anodic oxidation coating covering at least a portion of the member main body. The anodic oxidation coating includes a porous first layer and a second layer located between the first layer and the member main body and having a higher aluminum content than that of the first layer. The ratio of the thickness of the second layer with respect to the thickness of the anodic oxidation preferably is about 5% to about 20%.

Abstract: The present invention provides a magnesium-based composite material that can achieve excellent performance such as high tensile strength not only at ordinary temperature but also at high temperature. The magnesium-based composite material of the present invention is Al2Ca-containing magnesium-based composite material, wherein said composite material is obtained by a solid-phase reaction of an aluminum-containing magnesium alloy and an additive, said additive being calcium oxide, and said composite material contains Al2Ca formed in the solid-phase reaction. In the magnesium-based composite material, CaO, in combination with Al2Ca, can be dispersed.

Abstract: The present invention provides a method for producing a magnesium alloy sheet capable of producing a magnesium alloy sheet having excellent plastic workability such as press workability. The method of the present invention includes rolling a magnesium alloy blank with a reduction roll. The rolling includes controlled rolling performed under the following conditions (1) and (2) wherein M (% by mass) is the Al content in a magnesium alloy constituting the blank: (1) the surface temperature Tb (° C.) of the magnesium alloy blank immediately before insertion into the reduction roll satisfies the following expression: 8.33×M+135?Tb?8.33×M+165 wherein 1.0?M?10.0; and (2) the surface temperature Tr of the reduction roll is 150° C. to 180° C.

Abstract: A method of forming a coated article is disclosed. The method involves heating a magnesium alloy component, positioning the component in a mold such that a gap exists between component outer surfaces and mold inner surfaces, and heating a magnesium-containing alloy material above its melting temperature, which is lower than that of the component. The material is formed from magnesium alloyed with i) the component element, but at a higher concentration, ii) at least one element that is different than the component element, or iii) the component element and at least one other element. The method further includes introducing the material into the gap, thereby covering at least the outer surfaces of the component, and cooling the material to form a substantially evenly distributed solidified coating on the outer surfaces of the component. The coating has a higher wear and/or corrosion resistance than that of the magnesium alloy component.

Abstract: The present invention relates to a magnesium aluminum alloy with enhanced creep resistance. The alloy contains barium and calcium in low proportions, and possesses a higher creep resistance in comparison to alloys containing rare earth elements. The alloy may additionally include zinc, tin, lithium, manganese, yttrium, neodymium, cerium and/or praseodymium in proportions of up to 7% by weight, respectively.

Abstract: The invention offers (a) a method of producing a magnesium-alloy material, the method being capable of obtaining a magnesium-alloy material having high strength, (b) a magnesium-alloy material having excellent strength, and (c) a magnesium-alloy wire having high strength. A molten magnesium alloy is supplied to a continuous casting apparatus provided with a movable casting mold to produce a cast material. The cast material is supplied to between at least one pair of rolls to perform an area-reducing operation (a rolling operation). The rolling operation is performed such that pressure is applied to the cast material using the rolls from at least three directions in the cross section of the cast material. A magnesium-alloy material obtained through the above-described production method has a fine crystal structure and is excellent in plastic processibility.

Abstract: The invention relates to a hydrogen storage material comprising an alloy of magnesium. The invention further relates to an electrochemically active material and an electrochemical cell provided with at least one electrode comprising such a hydrogen storage material. Also, the invention relates to electronic equipment comprising such an electrochemical cell.

Abstract: An alloy with a high glass forming ability characterized by containing a group of elements A with atomic radii of less than 0.145 nm of a total of 20 to 85 atm %, a group of elements B with atomic radii of 0.145 nm to less than 0.17 nm of a total of 10 to 79.7 atm %, and a group of elements C with atomic radii of 0.17 nm or more of a total of 0.3 to 15 atm %; when the elements with the greatest contents in the group of elements A, group of elements B, and group of elements C are respectively designated as the “element a”, “element b”, and “element c”, by the ratio of the content of the element a in the group of elements A (for example, Zn and/or Al), the ratio of the content of the element b in the group of elements B (for example, Mg), and the ratio of the content of the element c in the group of elements C (for example, Ca) all being 70 atm % or more; and by the liquid forming enthalpy between any two elements selected from the element a, element b, and element c being negative.

Abstract: As a novel biodegradable metallic material the degradation speed of which in vivo can be controlled over a broad scope while achieving desired mechanical properties such as strength, work hardening and ductility without restricting the shape of an implant device, it is intended to provide a magnesium-based biodegradable metallic material which comprises Mg containing Mg as the major composition and having a concentration of inevitable impurities equal to or less than 0.05 atomic %, is free from precipitates or intermetallic compounds, and has an average grain size being regulated to equal to or less than ¼ of the minimum part of the material.

Abstract: A method for making Mg(magnesium)-based intermetallic compound uses a thermal process during a melting process to produce largely the Mg-based intermetallic compound. The vapor pressure of Mg is high, thereby Mg is prone to be vaporized from a melt and a wrought solid alloy in the melting process of high temperature, for purifying the wrought Mg-based intermetallic compound. The method may simplify the process and devices for making the Mg-based intermetallic compound, and produce efficiently a larger of high purity Mg-based intermetallic compound.

Abstract: The invention is to provide a magnesium alloy material such as a magnesium alloy cast material or a magnesium alloy rolled material, excellent in mechanical characteristics and surface precision, a producing method capable of stably producing such material, a magnesium alloy formed article utilizing the rolled material, and a producing method therefor. The invention provides a producing method for a magnesium alloy material, including a melting step of melting a magnesium alloy in a melting furnace to obtain a molten metal, a transfer step of transferring the molten metal from the melting furnace to a molten metal reservoir, and a casting step of supplying a movable mold with the molten metal from the molten metal reservoir, through a pouring gate, and solidifying the molten metal to continuously produce a cast material. In a process from the melting step to the casting step, parts contacted by the molten metal are formed by a low-oxygen material having an oxygen content of 20 mass % or less.

Abstract: Disclosed is a wrought magnesium alloy having excellent strength and extrusion or rolling formability, and a method of producing the same. The wrought magnesium alloy comprises 0.1-1.5 at % group IIIa, 1.0-4.0 at % group IIIb, 0.35 at % or less of one selected from the group consisting of groups IIa, IVa, VIIa, IVb, and a mixture thereof, 1.0 at % or less of group IIb, and a balance of Mg and unavoidable impurities and thus has a second phase composite microstructure. The wrought magnesium alloy of the present invention has high strength, toughness, and formability in addition to the electromagnetic wave shield ability of magnesium. Accordingly, the wrought magnesium alloy is a material useful to portable electronic goods, such as notebook personal computers, mobile phones, digital cameras, camcorders, CD players, PDA, or MP3 players, automotive parts, such as engine room hoods, oil pans, or inner panel of door, or structural parts for airplane.