Abstract: A white glass contains, in terms of mole percentage on the basis of the following oxides, from 50 to 80% of SiO2, from 0 to 10% of Al2O3, from 11 to 30% of MgO, from 0 to 15% of Na2O and from 0.5 to 15% of P2O5.

Abstract: Embodiments of glass composition including at least about 65 mol % SiO2, Al2O3 in the range from about 7 mol % to about 11 mol %, Na2O in the range from about 13 mol % to about 16 mol %; and a non-zero amount of one or more alkali earth metal oxides selected from MgO, CaO and ZnO, wherein the sum of the alkali earth metal oxides is up to about 6 mol %, are disclosed. The glass compositions can be processed using fusion forming processes and float forming processes and are ion exchangeable. Glass articles including such glass compositions and methods of forming such glass articles are also disclosed. The glass articles of one or more embodiments exhibit a Vickers indentation crack initiation load of at least 8 kgf.

Abstract: A tempered glass substrate has a compression stress layer on a surface thereof, and has a glass composition comprising, in terms of mass %, 40 to 70% of SiO2, 12 to 21% of Al2O3, 0 to 3.5% of Li2O, 10 to 20% of Na2O, 0 to 15% of K2O, and 0 to 4.5% of TiO2, wherein the tempered glass substrate has a plate thickness of 1.5 mm or less, and an internal tensile stress in the tempered glass substrate is 15 to 150 MPa.

Abstract: According to one embodiment, a glass container may include a body formed from a Type I, Class B glass composition according to ASTM Standard E438-92. The body may have an inner surface, an outer surface and a wall thickness extending between the outer surface and the inner surface. The body may also include a compressively stressed layer extending into the wall thickness from at least one of the outer surface and the inner surface. A lubricous coating may be positioned on at least a portion of the outer surface of the body, wherein the outer surface of the body with the lubricous coating has a coefficient of friction less than or equal to 0.7.

Abstract: Ion exchangeable glasses that comprise at least one of a transition metal oxide or a rare earth oxide and have compositions that simultaneously promote a surface layer having a high compressive stress and deep depth of layer or, alternatively, reduced ion exchange time.

Abstract: The present invention relates to a chemically strengthened glass for a display device, having a visible light transmittance Tva of 50% or more and less than 91% at a thickness of 1 mm using A light source, and an excitation purity Pe of less than 0.5% at a thickness of 1 mm.

Abstract: A glass substrate for chemical strengthening is formed by a float process. The glass substrate includes at least one layer of a film formed of an inorganic material that contains H atoms in a concentration of 1.0×1015 to 1.0×1019 atom/mm3. The at least one layer is formed on at least one surface of the glass substrate.

Abstract: An ion exchangeable glass having a high degree of resistance to damage caused by abrasion, scratching, indentation, and the like. The glass comprises alumina, B2O3, and alkali metal oxides, and contains boron cations having three-fold coordination. The glass, when ion exchanged, has a Vickers crack initiation threshold of at least 10 kilogram force (kgf).

Abstract: A glass for a magnetic recording medium substrate permitting the realization of a magnetic recording medium substrate affording good chemical durability and having an extremely flat surface, a magnetic recording medium substrate comprised of this glass, a magnetic recording medium equipped with this substrate, and methods of manufacturing the same. The glass is an oxide glass not including As or F.

Abstract: A method capable of forming a sufficiently thick low alkali concentration region without heating glass to a high temperature and even in an atmosphere which is not an atmosphere of plasma formation gas such as helium and argon, is provided. A glass substrate having a pair of main surfaces and being made of glass containing an alkali oxide in its composition, is disposed between a first electrode and a second electrode so that one main surface is separated from the first electrode and the other main surface is brought into contact with the second electrode, and a corona discharge is generated by applying a direct-current voltage to the first electrode as a positive electrode and the second electrode as a negative electrode, in a positive-electrode-side surface layer portion of the glass substrate, at least one positive ion including an alkali ion migrate toward the negative-electrode-side.

Abstract: A process for producing a chemically strengthened glass is provided. The method for producing a chemically strengthened glass includes subjecting a phase-separated glass to an ion exchange treatment. A chemically strengthened glass which is obtained by the process and a phase-separated glass which has been subjected to the ion exchange treatment are also provided.

Abstract: Glass-ceramics exhibiting a Vickers indentation crack initiation threshold of at least 15 kgf are disclosed. These glass-ceramics may be ion exchangeable or ion exchanged. The glass-ceramics include a crystalline and amorphous phases generated by subjecting a thin precursor glass article to ceramming cycle having an average cooling rate in the range from about 10° C./minute to about 25° C./minute. In one or more embodiments, the crystalline phase may comprise at least 20 wt % of the glass-ceramics. The glass-ceramics may include ?-spodumene ss as the predominant crystalline phase and may exhibit an opacity ?about 85% over the wavelength range of 400-700 nm for an about 0.8 mm thickness and colors an observer angle of 10° and a CIE illuminant F02 determined with specular reflectance included of a* between ?3 and +3, b* between ?6 and +6, and L* between 88 and 97.

Abstract: An object is to devise a tempered glass substrate that has high mechanical strength and hardly undergoes breakage even though having a large size. A tempered glass substrate has a compressive stress layer in a surface thereof, and includes 1 piece/cm3 or less of devitrified stones containing Zr.

Abstract: A process for reinforcing a glass-ceramic article, into which a maximum tension is introduced beneath the surface of the glass-ceramic, advantageously in proximity to said surface. The invention also relates to an enamel that can be used for this reinforcement, this enamel being formed from a glass frit having the following composition, the proportions being expressed as weight percentages: SiO2 50-66% MgO 3-8% Na2O ?7-15% K2O 0-3% Li2O ?0-12% CaO ?0-10% BaO ?0-15% Al2O3 0-3% ZrO2 0-3% ZnO 0-5% B2O3 0-8% the sum of the alkaline-earth metal oxides CaO+BaO moreover being between 8 and 15%, and the sum of the alkali metal oxides Na2O+K2O+Li2O moreover being between 7 and 20%. The reinforced glass-ceramics obtained by the process.

Abstract: A glass sheet has one surface and the other surface facing the one surface in a thickness direction, wherein a fluorine concentration (average fluorine concentration by SIMS at a depth of 1 to 24 ?m) in the one surface is higher than that in the other surface. The following expression is satisfied: 0.07??F/?H2O. ?F (mol %) is a value obtained by subtracting an average fluorine concentration in the surface having the lower fluorine concentration from that in the surface having the higher fluorine concentration, and ?H2O (mol %) is an absolute value of a value obtained by subtracting an average H2O concentration in the surface having the higher fluorine concentration from that in the surface having the lower fluorine concentration.

Abstract: Alkali boroaluminosilicate glasses with high resistance to crack initiation and damage due to sharp impact are provided. The glass compositions have melting and forming temperatures that allow forming the glass into sheets via float-based processes while still allowing for the glass to be efficiently ion exchanged. The glass compositions contain MgO, and when ion exchanged, have a Vickers indentation crack initiation load of at least about 10-15 kgf.

Abstract: The embodiments described herein relate to chemically and mechanically durable glass compositions and glass articles formed from the same. In another embodiment, a glass composition may include from about 70 mol. % to about 80 mol. % SiO2; from about 3 mol. % to about 13 mol. % alkaline earth oxide; X mol. % Al2O3; and Y mol. % alkali oxide. The alkali oxide may include Na2O in an amount greater than about 8 mol. %. A ratio of Y:X may be greater than 1 and the glass composition may be free of boron and compounds of boron. In some embodiments, the glass composition may also be free of phosphorous and compounds of phosphorous. Glass articles formed from the glass composition may have at least a class S3 acid resistance according to DIN 12116, at least a class A2 base resistance according to ISO 695, and a type HGA1 hydrolytic resistance according to ISO 720.

Abstract: The embodiments described herein relate to chemically and mechanically durable glass compositions and glass articles formed from the same. In another embodiment, a glass composition may include from about 70 mol. % to about 80 mol. % SiO2; from about 3 mol. % to about 13 mol. % alkaline earth oxide; X mol. % Al2O3; and Y mol. % alkali oxide. The alkali oxide may include Na2O in an amount greater than about 8 mol. %. A ratio of Y:X may be greater than 1 and the glass composition may be free of boron and compounds of boron. In some embodiments, the glass composition may also be free of phosphorous and compounds of phosphorous. Glass articles formed from the glass composition may have at least a class S3 acid resistance according to DIN 12116, at least a class A2 base resistance according to ISO 695, and a type HGA1 hydrolytic resistance according to ISO 720.

Abstract: A glass sheet includes 4 mol % or more of Al2O3. In the glass sheet, a surface Na2O amount in one surface of the glass sheet is lower than the surface Na2O amount in the other surface of the glass sheet by 0.2 mass % to 1.2 mass %.

Abstract: A front glass plate for a stacked structure includes greater than or equal to 5 mol % of Al2O3, in terms of an oxide, as a component, 50% crack initiation load of the front glass plate being greater than or equal to 0.5 kg.

Abstract: Ion exchangeable glasses having coefficients of thermal expansion (CTE) at least about 90×10?7 ° C.?1. The glasses undergo rapid ion exchange, for example, in a molten KNO3 salt bath to a depth of layer of greater than 30 microns in less than 2 hours at temperatures of 370° C. to 390° C. When ion-exchanged to a depth of layer between 30 to 50 microns, the glasses exhibit a Vickers median/radial crack initiation threshold exceeding 30 kilograms force (kgf). The glasses are fusion formable and, in some embodiments, compatible with zircon.

Abstract: Ion exchangeable glasses containing SiO2, Al2O3, Na2O, MgO, B2O3, and P2O5 are provided. The compressive stresses of these ion exchanged glasses are greater than 900 megapascals (MPa) at a depth of 45 or 50 microns (?m) with some glasses exhibiting a compressive stress of at least 1 gigaPascals (GPa). The ion exchange rates of these glasses are much faster than those of other alkali aluminosilicate glasses and the ion exchanged glass is resistant damage to impact damage. A method of ion exchanging the glass is also provided.

Abstract: Glass-ceramics and precursor glasses that are crystallizable to glass-ceramics are disclosed. The glass-ceramics of one or more embodiments include rutile, anatase, armalcolite or a combination thereof as the predominant crystalline phase. Such glasses and glass-ceramics may include compositions of, in mole %: SiO2 in the range from about 45 to about 75; Al2O3 in the range from about 4 to about 25; P2O5 in the range from about 0 to about 10; MgO in the range from about 0 to about 8; R2O in the range from about 0 to about 33; ZnO in the range from about 0 to about 8; ZrO2 in the range from about 0 to about 4; B2O3 in the range from about 0 to about 12, and one or more nucleating agents in the range from about 0.5 to about 12. In some glass-ceramic articles, the total crystalline phase includes up to 20% by weight of the glass-ceramic article.

Abstract: Disclosed is a method of producing a glass substrate for an information recording medium including a rough polishing step of performing a rough polishing on a glass material containing 0.01 to 2 mass % of cerium oxide; a washing step of washing the glass material after the rough polishing step, so that the cerium content of the glass material surface becomes 0.125 ng/cm2 or less; and a precision polishing step of performing precision polishing on the glass material after the washing step by cyclically using a polishing material containing colloidal silica.

Abstract: The present disclosure relates to fusion formable highly crystalline glass-ceramic articles whose composition lies within the SiO2—R2O3—Li2O/Na2O—TiO2 system and which contain a silicate crystalline phase comprised of lithium aluminosilicate (?-spodumene and/or ?-quartz solid solution) lithium metasilicate and/or lithium disilicate. Additionally, these silicate-crystal containing glass-ceramics can exhibit varying Na2O to Li2O molar ratio extending from the surface to the bulk of the glass article, particularly a decreasing Li2O concentration and an increasing Na2O concentration from surface to bulk. According to a second embodiment, disclosed herein is a method for forming a silicate crystalline phase-containing glass ceramic.

Abstract: A method of manufacturing a tempered glass substrate includes: melting glass raw materials blended so as to have a glass composition including, in terms of mass %, 40 to 71% of SiO2, 3 to 23% of Al2O3, 0 to 3.5% of Li2O, 7 to 20% of Na2O, and 0 to 15% of K2O; forming the resultant molten glass into a sheet shape; and performing ion exchange treatment in a KNO3 molten salt, the KNO3 molten salt having a controlled concentration of Na ions, to form a compressive stress layer in a surface of the glass.

Abstract: An ion exchangeable glass having a high degree of resistance to damage caused by abrasion, scratching, indentation, and the like. The glass comprises alumina, B2O3, and alkali metal oxides, and contains boron cations having three-fold coordination. The glass, when ion exchanged, has a Vickers crack initiation threshold of at least 10 kilogram force (kgf).

Abstract: A glass article is provided having from greater than or equal to about 40 mol % to less than or equal to about 68 mol % SiO2, less than or equal to about 11 mol % Al2O3, an R2O:R?O molar ratio of from greater than or equal to about 1:1 to less than or equal to about 2:1, and an MgO:CaO molar ratio of from greater than or equal to about 0.6:1 to less than or equal to about 1.8:1. The class article may also include a compressive stress layer on at least one surface thereof, the compressive stress layer having a compressive stress that is greater than or equal to about 800 MPa, and a depth that is greater than or equal to about 20 ?m.

Abstract: An ion exchangeable glass having a high degree of resistance to damage caused by abrasion, scratching, indentation, and the like. The glass comprises alumina, B2O3, and alkali metal oxides, and contains boron cations having three-fold coordination. The glass, when ion exchanged, has a Vickers crack initiation threshold of at least 10 kilogram force (kgf).

Abstract: Embodiments are directed to strengthened glass articles comprising a thickness t?1 mm (1000 ?m), an inner region under a central tension CT (in MPa), and at least one compressive stress layer adjacent the inner region and extending within the strengthened glass article from a surface of the strengthened glass article to a depth of layer DOL (in ?m), wherein the strengthened glass article is under a compressive stress at the surface CSs (in MPa), wherein the strengthened glass article is an alkali aluminosilicate glass article comprising 0-5 mol % Li2O, and at least 3 mol % Al2O3, and wherein the DOL?70 ?m, and a CSs/DOL ratio?2.5 MPa/?m.

Abstract: A method of strengthening an alkali aluminoborosilicate glass. A compressive layer extending from a surface of the glass to a depth of layer is formed by exchanging larger metal cations for smaller metal cations present in the glass. In a second step, metal cations in the glass are exchanged for larger metal cations to a second depth in the glass that is less than the depth of layer and increase the compressive stress of the compressive layer. Formation of the compressive layer and replacement of cations with larger cations can be achieved by a two-step ion exchange process. An alkali aluminoborosilicate glass having a compressive layer and a crack indentation threshold of at least 3000 gf is also provided.

Abstract: For an information storage medium a glass substrate is produced in a method including the steps of: polishing a glass substrate with a polishing agent applied thereon; and subsequently, chemically strengthening a major surface of the glass substrate. The polishing agent contains cerium oxide at a purity equal to or larger than 99% by mass for CeO2/TREO, and has an alkaline earth metal content having a total mass equal to or smaller than 10 ppm by mass. The step of polishing is performed with a soft polishing pad to polish the glass substrate.

Abstract: A glass that is down-drawable and ion exchangeable. The glass has a temperature T35kp which the viscosity is 35 kilopoise. T35kp is less than the breakdown temperature Tbreakdown of zircon.

Abstract: A tempered glass according to one embodiment of the present invention is a tempered glass having a compression stress layer in a surface thereof, the tempered glass including as a glass composition, in terms of mass %, 45 to 75% of SiO2, 10 to 25% of Al2O3, 0 to 10% of B2O2, 0 to 8% of MgO, 0 to 20% of SrO+BaO, and 0 to 14% of Na2O. Herein, the term “SrO+BaO” refers to the total amount of SrO and BaO.

Abstract: A colored glass, a surface of which is roughened in whole or in part. In the colored glass, an average value of gloss values measured at 9 points in the surface thereof at an incident angle of 60° in accordance with JIS 28741 (1991) is 30 or less, a ratio of a difference between a maximum gloss value and a minimum gloss value to the maximum gloss value is 20% or less, and a minimum value of visible-light transmittance at a thickness of 0.8 mm is 70% or less.

Abstract: A constitution of cover glass, the compositions consist in terms of weight % on the oxide basis, of from 64 to 69 wt. % of SiO2; from 7 to 11.5 wt. % of Al2O3; from 1.5 to 2.5 wt. % of B2O3; from 4.5 to 7.5 wt. % of MgO; 0%<CaO?2.5%; 0%<ZnO?2%; 0%<ZrO2?0.2%; 0%<TiO2?1%; from 14.5 to 16.5 wt. % of Na2O; from 1 to 4 wt. % of K2O; and 0%<SnO2?0.4%. The constitution then can be melted to form cover glass. Thereafter, the cover glass is dipped in KNO3 solution so that sodium ions, which is smaller in volume, contained in certain depth from the surface layer of the cover glass can be substituted by potassium ions, which is larger in volume. In this manner, squeezing effect is generated on the surface layer so as to form cover glass having high strength and resistance in both abrasion and scratch.

Abstract: A tempered glass has a compressive stress layer in a surface thereof, includes as a glass composition, in terms of mass %, 50 to 80% of SiO2, 10 to 30% of Al2O3, 0 to 6% of B2O3, 0 to 2% of Li2O, and 5 to 25% of Na2O, and is substantially free of As2O3, Sb2O3, PbO, and F.

Abstract: Embodiments of this disclosure pertain to articles that exhibit scratch-resistance and improved optical properties. In some examples, the article exhibits a color shift of about 2 or less, when viewed at an incident illumination angle in the range from about 0 degrees to about 60 degrees from normal under an illuminant. In one or more embodiments, the articles include a substrate, and an optical film disposed on the substrate. The optical film includes a scratch-resistant layer and an optical interference layer. The optical interference layer may include one or more sub-layers that exhibit different refractive indices. In one example, the optical interference layer includes a first low refractive index sub-layer and a second a second high refractive index sub-layer. In some instances, the optical interference layer may include a third sub-layer.

Abstract: Described herein are various antimicrobial glass articles that have improved resistance to discoloration when exposed to harsh conditions. The improved antimicrobial glass articles described herein generally include a glass substrate that has a low concentration of nonbridging oxygen atoms, a compressive stress layer and an antimicrobial silver-containing region that each extend inward from a surface of the glass substrate to a specific depth, such that the glass article experiences little-to-no discoloration when exposed to harsh conditions. Methods of making and using the glass articles are also described.

Abstract: The present invention provides a cover glass for a display, having high durability to slow cracking and strong abraded strength even though a compressive stress is large and a depth of a compressive stress layer is deep. The present invention relates to a cover glass for a display, in which a depth of a compressive stress layer (DOL) is 30 ?m or more, a surface compressive stress is 300 MPa or more, a position (HW) at which a compressive stress is half of a value of the surface compressive stress is a position of 8 ?m or more from a glass surface, and the depth of the compressive stress layer (DOL) and the position (HW) at which the compressive stress is half of the value of the surface compressive stress satisfy the following formula: 0.05?HW/DOL?0.23??(1).

Abstract: Described herein are various antimicrobial glass articles that have improved strength and resistance to discoloration. The improved antimicrobial glass articles described herein generally include a glass substrate with a compressive stress layer and an antimicrobial silver-containing region that each extend inward from a surface of the glass substrate to a specific depth. In some embodiments, the compressive stress layer has a compressive stress at the surface of about 500 MPa or greater and the compressive stress decreases monotonically from the surface into the depth of the glass substrate. Methods of making and using the glass articles are also described and include forming a compressive stress layer and forming an antimicrobial silver-containing region by preferentially exchanging a plurality of silver cations in a silver-containing medium for a specific plurality of first cations ions in the glass substrate.

Abstract: A noble glass composition which is based on a known potassium-zinc crystal glass composition suitable for chemical strengthening, in which most of contained ZnO component is replaced with a combination of less expensive oxides. The noble glass composition is easily melted in a tank and formed by machine into table wares, and provides a chemical strengthened crystal glass article which has high practical strength as tableware and can be subjected to washing with an alkali.

Abstract: Described herein are glass, ceramic, or glass-ceramic articles having improved antimicrobial efficacy. Further described are methods of making and using the improved articles. The improved articles generally include a glass, ceramic, or glass-ceramic substrate, a compressive stress layer that extends inward from a surface of the glass, ceramic, or glass-ceramic substrate to a first depth therein, and an antimicrobial agent-containing region that extends inward from the surface of the glass, ceramic, or glass-ceramic substrate to a second depth therein.

Abstract: A glass ceramic precursor glass and a glass ceramic having low levels of rhodium and a method of controlling the amount of rhodium in such glasses and glass ceramics. The precursor glass and glass ceramic contain from about 1 ppm to about 10 ppm and, in certain embodiments, from about 1 ppm to about 6 ppm rhodium. The method of controlling of reducing rhodium dissolution from a rhodium-containing material such as, for example, an alloy into a glass melt comprises controlling and/or lowering the partial pressure of oxygen at the rhodium-containing vessel/glass interface by imposing a high humidity condition around the external (non-glass-contact) surface of the rhodium-containing material. The lower concentration of rhodium minimizes its coloring effect on the white color of the glass ceramic.

Abstract: Ion exchangeable glass articles are disclosed. In one embodiment, a glass article formed from alkali aluminosilicate glass which may include Ga2O3, Al2O3, Na2O, SiO2, B2O3, P2O5 and various combinations thereof. The glass article may generally include about X mol % of Ga2O3 and about Z mol % of Al2O3, wherein 0?X?20, 0?Z?25 and 10?(X+Z)?25. The glass article may also include from about 5 mol % to about 35 mol % Na2O, SiO2 may be present in an amount from about 40 mol % to about 70 mol % SiO2. The glass article may further include Y mol % B2O3 where Y is from 0 to about 10. The glass article may further include (10-Y) mol % of P2O5. Glass articles formed according to the present invention may be ion-exchange strengthened. In addition, the glass articles may have a low liquid CTE which enables the glass articles to be readily formed into complex shapes.

Abstract: The present disclosure relates to fusion formable highly crystalline glass-ceramic articles whose composition lies within the SiO2—R2O3—Li2O/Na2O—TiO2 system and which contain a silicate crystalline phase comprised of lithium aluminosilicate (?-spodumene and/or ?-quartz solid solution) lithium metasilicate and/or lithium disilicate. Additionally, these silicate-crystal containing glass-ceramics can exhibit varying Na2O to Li2O molar ratio extending from the surface to the bulk of the glass article, particularly a decreasing Li2O concentration and an increasing Na2O concentration from surface to bulk. According to a second embodiment, disclosed herein is a method for forming a silicate crystalline phase-containing glass ceramic.

Abstract: A sealed insulating glass unit comprises two glass sheets held apart by a spacer, optionally with a sealant between the edges of the glass sheets outside the spacer. The insulating glass unit contains an electronic device, having information relating to the origin, manufacture and/or properties of the insulating glass unit capable of being read from the device by means actuated from outside the insulating glass unit. The device is embedded within the spacer or sealant so that it is concealed within the insulating glass unit.

Abstract: To provide a glass substrate for a display cover glass not only having excellent strength and antibacterial properties but also having a high transparency and a high visible transmittance suitable as a cover glass for a display device. A glass substrate for a display cover glass, which comprises a surface compressive stress layer and an antibacterial substance-containing layer formed on the glass substrate surface, characterized by having a ratio (T1/T2) of the transmittance T1 at a wavelength of 428 nm to the transmittance T2 at a wavelength of 650 nm of the glass substrate of at least 0.95, and a transmittance at a wavelength of 428 nm of at least 86% when the thickness of the glass substrate is from 0.1 to 3.0 mm.

Abstract: An ion exchangeable glass that is free of lithium and comprising 0.1-10 mol % P2O5 and at least 5 mol % Al2O3. The presence of P2O5 enables the glass to be ion exchanged more quickly and to a greater depth than comparable glasses that do not contain P2O5.

Abstract: A glass and a glass composition are provided that, following chemical tempering, not only exhibit high values of compressive stress and depth of ion exchange, but also excellent scratch tolerance. The glass composition includes SiO2, Al2O3, B2O3, ZrO2, and Na2O.