Abstract: The method of this invention provides a simple and inexpensive method for manufacturing self-sealing pneumatic rubber tires of the tubeless type having a higher degree of uniformity than can be made utilizing conventional manufacturing procedures that are currently being practiced. In the practice of this invention a low viscosity sealant formulation, which would ordinarily be difficult to handle and build into an uncured tire, is encapsulated in a stiff rubber formulation. This makes it relatively easy to build the sealant layer into the tire since the low viscosity sealant formulation is contained with the more rigid solid material. The low viscosity sealant material requires little and preferably no depolymerization to act effectively as a sealant. Accordingly, it does not need to be depolymerized with a peroxide which causes off-gassing and the resultant tire uniformity and balance issues normally associated with polymer break down.

Abstract: A resin composition comprises a prepolymer of crosslinking agent and benzoxazine resin and a maleimide resin. The resin composition may be used to make various articles, such as a prepreg, a resin film, a resin-coated copper, a laminate or a printed circuit board, and achieves improvements in at least one, more or all of the properties including laminate reflow shrinkage, T288 thermal resistance, ten-layer board T300 thermal resistance, dissipation factor, copper foil peeling strength, and resin filling property in open area.

Abstract: A conjugated diene polymer satisfying following conditions (1) to (4): (1) the conjugated diene polymer has two or more peaks in a molecular weight distribution curve obtained by measurement with gel permeation chromatography (GPC); (2) the molecular weight distribution curve contains a peak (A) having a peak molecular weight of 500,000 to 2,500,000 and a peak (B) having a peak molecular weight of 150,000 to 600,000; (3) a total value of an area of the peak (A) and an area of the peak (B) is 70% or more of a total area of the molecular weight distribution curve; and (4) an absolute value of difference between a glass transition temperature of a conjugated diene polymer in the peak (A) (Tg (A)) and a glass transition temperature of a conjugated diene polymer in the peak (B) (Tg (B)) is 2° C. to 30° C.

Abstract: A thermoplastic modacrylic resin composition includes a modacrylic resin and a plasticizer. The modacrylic resin includes 15 to 85 wt % of acrylonitrile, 15 to 85 wt % of vinyl chloride and/or vinylidene chloride, and 0 to 20 wt % of another vinyl monomer, and the plasticizer is an organic compound that is compatible with the modacrylic resin and has a boiling point of at least 200° C. A method for manufacturing a thermoplastic modacrylic resin composition includes melt-kneading a powder mixture obtained by mixing a modacrylic resin powder and an organic compound that is compatible with the modacrylic resin and has a boiling point of at least 200° C. Acrylic fibers are composed of a thermoplastic modacrylic resin composition.

Abstract: A thermoplastic modacrylic resin composition includes a modacrylic resin and a plasticizer. The modacrylic resin includes 15 to 85 wt % of acrylonitrile, 15 to 85 wt % of vinyl chloride and/or vinylidene chloride, and 0 to 20 wt % of another vinyl monomer, and the plasticizer is an organic compound that is compatible with the modacrylic resin and has a boiling point of at least 200° C. A method for manufacturing a thermoplastic modacrylic resin composition includes melt-kneading a powder mixture obtained by mixing a modacrylic resin powder and an organic compound that is compatible with the modacrylic resin and has a boiling point of at least 200° C. Acrylic fibers are composed of a thermoplastic modacrylic resin composition.

Abstract: A method of oxidatively dehydrogenating a n-butenes to butadiene includes oxidatively dehydrogenating dehydrogenation reactant in a first adiabatic, catalytic reaction zone to provide a first-stage effluent stream enriched in butadiene at a first-stage effluent temperature above the first-stage inlet temperature, cooling the first-stage effluent stream in a first heat transfer zone to a second-stage inlet temperature lower than said first-stage effluent temperature to provide a second gaseous feed stream comprising superheated steam, n-butene and butadiene, wherein the second stage inlet temperature is lower than said first stage effluent temperature and oxidatively dehydrogenating n-butene in the second stream to provide a product stream further enriched in butadiene at a second stage effluent temperature above said second-stage inlet temperature. The first reaction zone temperature rise and the second reaction zone temperature rise are at least 200° F. (111° C.

Abstract: Described herein are methods for continuous solution polymerization. The method may comprise polymerizing one or more monomers and comonomers in the presence of a solvent in a polymerization reactor to produce a polymer solution; determining the composition of the polymer solution exiting the polymerization reactor in an on-line fashion; determining at least one of the critical pressure or critical temperature; comparing the critical pressure and/or critical temperature to the actual temperature of the polymer solution and the actual pressure of the polymer solution; heating or cooling the polymer solution to a temperature within 50° C. of the critical temperature; and passing the polymer solution through a pressure letdown valve into a liquid-liquid separator, where the pressure of the polymer solution is reduced or raised to a pressure within 50 psig of the critical pressure to induce a separation of the polymer solution into two liquid phases.

Abstract: Provided is a resin acid ester-based tackifier having a good compatibility with a synthetic rubber elastomer, being capable of reducing the melt viscosity of the elastomer, and being capable of imparting excellent adhesive properties and/or pressure-sensitive adhesive properties to the elastomer.

Abstract: Elastomeric compounds having increased cold flow resistance may be obtained by utilizing from 10-100 phr of a functionalized rubbery polymer containing specified types of functionalizing units, at least 0.01 phr of a multivalent metal organic salt and 0-90 phr of at least one additional rubbery polymer.

Abstract: A polyimide precursor, a polyimide using the polyimide precursor, and a polyimide film using the polyimide. The polyimide precursor comprises a structural unit represented by general formula (AI): in which A is tetravalent aromatic group or aliphatic group, B is divalent aromatic group, and each R2 independently represents hydrogen, an alkyl group having 1 to 6 carbon atoms, or an alkylsilyl group having 3 to 9 carbon atoms, in which B in general formula (AI) includes a triazine moiety represented by following formula (AB1): in which R1 represents hydrogen, an alkyl group having 1 to 6 carbon atoms or an aromatic group, and R3 represents hydrogen, methyl or ethyl.

Abstract: An organic polymer solution may include about 0.1%-30% by weight of a specific polymer having rigid rod-like molecules. These molecules may include various cores, spacers, and sides groups to ensure their solubility, viscosity, and cross-linking ability. The rigid rod-like molecules are selected in such a way that they form self-assembling structures in the polymer solution, which makes it a lyotropic liquid crystal. The organic polymer solution, when properly deposited on a substrate and dried to remove solvents, forms a solid optical retardation layer of positive A-type substantially transparent to electromagnetic radiation in the visible spectral range.

Abstract: The present invention relates to a novel diamine compound, wherein two substituents R and R? are introduced asymmetrically, and a polymer thereof. The polymer may have excellent solubility in the organic solvent and allows for easy processibility after imidization, thus giving proper film maintaining superior properties, such as thermal, mechanical, and optical properties for applications in electrical, electronic, or optical materials.

Abstract: Provided is a resin acid ester-based tackifier having a good compatibility with a synthetic rubber elastomer, being capable of reducing the melt viscosity of the elastomer, and being capable of imparting excellent adhesive properties and/or pressure-sensitive adhesive properties to the elastomer. The tackifier is composed of an ester composition characterized by (i) the ester composition comprising 70% by weight or more of a resin acid ester represented by the general formula (1): and (ii) the S?NMR/SNMR ratio of the ester composition being at least 6% in the 1H-NMR spectrum of the ester composition, wherein S?NMR is the total integral value of the proton signal(s) appearing in the region of 6 to 8 ppm and SNMR is the total integral value of all the proton signals appearing over the entire range of the 1H-NMR spectrum.

Abstract: The present invention provides a resist composition giving a resist pattern excellent in CD uniformity and focus margin. A chemically amplified photoresist composition comprises a resin (A) and an acid generator (B), and the resin (A) contains, as a part or an entirety thereof, a copolymer (A1) which is obtained by polymerizing at least: a (meth)acrylic monomer (a1) having C5-20 alicyclic hydrocarbon group which becomes soluble in an aqueous alkali solution by the action of an acid; a (meth)acrylic monomer (a2) having a hydroxy group-containing adamantyl group; and a (meth)acrylic monomer (a3) having a lactone ring, and the copolymer (A1) has a weight-average molecular weight of 2500 or more and 5000 or less, and a content of the copolymer (A1) is not less than 50 parts by mass with respect to 100 parts by mass of the resin (A).

Abstract: A sulfonated polymer comprising a 3-substituted fused thienothiophene repeat unit, a composition comprising the polymer, a method of making the polymer, and a device comprising the polymer. The polymers can be used in hole injection or hole transport layers, or other applications in organic electronic devices.

Abstract: The present invention provides a resist composition giving a resist pattern excellent in CD uniformity and focus margin. A chemically amplified photoresist composition comprises a resin (A) and an acid generator (B), and the resin (A) contains, as a part or an entirety thereof, a copolymer (A1) which is obtained by polymerizing at least: a (meth)acrylic monomer (a1) having C5-20 alicyclic hydrocarbon group which becomes soluble in an aqueous alkali solution by the action of an acid; a (meth)acrylic monomer (a2) having a hydroxy group-containing adamantyl group; and a (meth)acrylic monomer (a3) having a lactone ring, and the copolymer (A1) has a weight-average molecular weight of 2500 or more and 5000 or less, and a content of the copolymer (A1) is not less than 50 parts by mass with respect to 100 parts by mass of the resin (A).

Abstract: A biocompatible polymeric composition for cross-linking in-situ in a wound is disclosed comprising 1) one or more polyanionic polymers such as alginates or hyaluronates, able to be cross-linked the surface of the wound and 2) one or more polycationic polymers such as chitosan or DEAE-Dextran, that assists in the solidification process as well as speeds up hemostasis without the need for applying pressure. The biocompatible polymeric composition may further comprise a cross-linking agent such as aqueous calcium chloride. The invention encompasses an initial polymeric composition, the solidified matrix cross-linked and integrated at the wound site, including the methods of using, applying, and cross-linking the composition.

Abstract: Processes involving wetting fibers with an aqueous dispersion of micronized thermoplastic powders; processes for producing an aqueous dispersion of micronized thermoplastic powders; processes of chemically surface cross-linking micronized particles; and articles of produced therefrom.

Abstract: Non-aqueous emulsions comprise a continuous organic phase comprising an organic vehicle. The non-aqueous emulsions further comprise a discontinuous phase comprising a polyfluoropolyether silane. Methods of preparing surface treated articles therewith are also disclosed.

Abstract: A water-based ink for use in a computer-to-plate inkjet printing and a preparation method therefor. A polymer of 5 to 40 wt %, an additive of 0.01 to 10 wt %, a dye or pigment of 0.01 to 10 wt %, an organic solvent of 1 to 30 wt %, an anti-foaming agent of 0 to 5 wt %, and deionized water are stirred and mixed at room temperature. When the polymer is dissolved, the mixed solution is filtered. The filtrate is the water-based ink. The water-based ink is sprayed via a computer-to-plate machine onto a surface of a metal substrate (which may be an aluminum plate, a zinc plate, or a copper plate) to form a graphic region. A printing plate allowing for computer-to-plate printing is acquired after solidification. The printing plate acquired is allowed to achieve a halftone dot reproduction rate between 2 and 99% and a recognition rate of 175 lpi.

Abstract: Mechanisms for coating surfaces of materials, the resulting coated materials, and solutions for use in material-coating processes are described. Triblock molecule components may be selected for desired properties. When applied in solution to a material, the molecules self-assemble into similarly oriented micro- or nanostructures coating the surface of the material. Various molecule properties can be tailored to produce a range of desirable surface coating properties. The surface coating may optionally be self cleaning if selected to be appropriately hydrophobic, allowing water and particulates to roll off of the surface with minimal friction.

Abstract: A conductive paste including a combination of: a conductive powder, a metallic glass, and a dispersing agent represented by the following Chemical Formula 1 R1-L1-(OR2)n—(OR3)m—O-L2-COOH.??Chemical Formula 1 In Chemical Formula 1, R1 is a substituted or unsubstituted C5 to C30 branched alkyl group, R2 and R3 are each independently a substituted or unsubstituted C2 to C5 alkylene group, L1 is a substituted or unsubstituted C6 to C30 arylene group, L2 is a single bond or a C1 to C4 alkylene group, n and m are each independently integers ranging from 0 to about 30, and 3?n+m?30.

Abstract: Novel stable aqueous suspensions of a functionalized, completely or partially hydrogenated nitrite rubber are provided with very low emulsifier content and small particle diameter, furtheron a process for production thereof and the use thereof for producing composite materials via coating of substrate materials with the suspension.

Abstract: A composition and method of using the composition are described. The composition is useful for quickly bonding chlorinated polyvinylchloride during installation and repair operations. Embodiments of the composition include at least one volatile organic solvent, chlorinated polyvinylchloride dissolved in the solvent and the composition is substantially free of cyclohexanone.

Abstract: Highly fluorinated ion-exchange polymers achieve dissolution in aqueous tetrahydrofuran at lower pressures and temperatures than in other solvents, with few or no side products being formed.

Abstract: A method for providing urea particles in a solvent medium, said method comprising at least the steps of: providing at least one polyisocyanate component dissolved in a first solvent; providing at least one isocyanate-reactive polyamine component dissolved in a second solvent; providing at least one isocyanate-reactive monoamine, optionally dissolved in a third solvent; combining and reacting said isocyanate-reactive monoamine optionally dissolved in said third solvent with said polyisocyanate dissolved in said first solvent, thereby providing an urea-modified polyisocyanate dissolved in said first solvent and said optionally third solvent, and then combining and reacting said urea-modified polyisocyanate dissolved in said first solvent and said optionally third solvent with said polyamine component dissolved in said second solvent.

Abstract: A resin composition containing: a polymer having at least one structural unit (i) selected from a group consisting of a structural unit represented by formula (1) and a structural unit represented by formula (2); and at least one organic solvent selected from a group consisting of ether solvents, ketone solvents, ester solvents and amide solvents.

Abstract: A coating composition comprises a high molecular weight polycarbodiimide. The high molecular weight polycarbodiimide is produced via a method. A method of preparing the coating composition and a method of forming a coating on a substrate with the coating composition are also disclosed.

Abstract: A stable caulk or sealant composition containing as principal ingredients styrene-ethylene/butylene-styrene copolymer, heptane solvent, and a resin is disclosed. The composition is generally employed in a canister pressurized with a propellant to expel a stream of water-impervious sealant to fill cracks, crevices and gaps to water damage. When desired, the sealant is removable from the application area, typically by manually pulling (e.g., with one's bare hands). In some embodiments, a propellant is added with the sealant in a container to propel the sealant out of the container when the sealant is applied.

Abstract: The present teachings provide a composition that includes a functionalized polyfluoropolyether and functionalized polybutadiene in a weight ratio of functionalized polyfluoropolyether/functionalized polybutadiene of from about 20/80 to about 80/20 in a solvent. The composition can be used to form a surface layer having a water contact angle of greater than about 90° and a hexanedecane contact angle greater than about 45°.

Abstract: A mixture of a functionalized polyfluoropolyether and a benzoxazine resin in a weight ratio of from about 1/99 to about 99/1.

Abstract: Embodiments in accordance with the present invention encompass polymer compositions that are useful in the assembly of microelectronic components onto a variety of substrate materials. Such polymer compositions providing for both holding the microelectronic components at desired positions on a substrate, providing fluxing for the solder bonding of such components to the substrate and remaining in place as an underfill for such components.

Abstract: Coating systems and processes are disclosed for uniformly coating objects. The system comprises a pre-treatment unit, a first processing unit, a first post-treatment unit and one or more coating apparatus each configured to engage an object and rotate the object around or about two or more axes. The coating apparatus used in the system can comprise a first, second and/or third gimbals connected to rotational mechanisms to allow rotation of the gimbals around or about first, second and/or third axis. An object holder is connected to the third gimbal. When an object is present in the object holder, it can be immersed in a coating solution to form a coated object. The coated object is then rotated around or about two or three axes which produces a multidirectional centrifugal force which causes the coating solution to spread evenly over the surface of the object to produce a uniform thin film.

Abstract: The present teachings provide a fuser member. The fuser member includes a substrate layer comprising a polyimide polymer and an amine neutralized phosphate ester.

Abstract: The present teachings provide a composition that includes a functionalized polyfluoropolyether and functionalized polybutadiene in a weight ratio of functionalized polyfluoropolyether/functionalized polybutadiene of from about 20/80 to about 80/20 in a solvent. The composition can be used to form a surface layer having a water contact angle of greater than about 90° and a hexanedecane contact angle greater than about 45°.

Abstract: The present teachings provide a fuser member. The fuser member includes a substrate layer comprising a polyimide polymer and polyethylene glycol ester.

Abstract: The present invention describes the process of producing biopolymeric membranes and the membranes obtained by this process. Particularly, the biopolymeric membranes of the present invention comprise poly(urethane-caprolactone) and can be used for nerve and bone regeneration.

Abstract: Premixes suitable for the production of membrane materials are described. Products of this invention are suitable for the formation of membranes and membrane modules that may be in the form of flat sheets, tubes, or hollow fibers.

Abstract: The invention is directed to polyimide based adhesives having a coefficient of thermal expansion (“CTE”) equal to or below 50 ppm/° C. The adhesives of the present invention contain a polyimide base polymer present in the overall adhesive in an amount from 25 to 95 weight percent. The polyimide base polymer has a glass transition temperature (“Tg”) in a range of from about 150 to about 300° C. and typically has a coefficient of thermal expansion above 50 ppm/° C. The polyimide based adhesives of the invention also contain an aramid micro fiber filler in an amount from 5 to 75 weight percent, based upon the total weight of the polyimide based adhesive. The fiber filler can be used to lower CTE of the overall adhesive to match (or nearly match) the CTE of other materials like metal, silicon wafers, other polymers (including polyimide) and the like.

Abstract: A method for varying the transport properties of a film cast from a polymer having at least two polymer end blocks A and at least one polymer interior block B wherein each A block is a polymer block resistant to sulfonation and each B block is a polymer block susceptible to sulfonation, and wherein said A and B blocks do not contain any significant levels of olefinic unsaturation. The method includes casting the polymer using a solvent mixture having two or more solvents selected from the group consisting of polar solvents and non-polar solvents.

Abstract: A method for varying the transport properties of a film cast from a polymer having at least two polymer end blocks A and at least one polymer interior block B wherein each A block is a polymer block resistant to sulfonation and each B block is a polymer block susceptible to sulfonation, and wherein said A and B blocks do not contain any significant levels of olefinic unsaturation. The method includes casting the polymer using a solvent mixture having two or more solvents selected from the group consisting of polar solvents and non-polar solvents.

Abstract: A flame retardant comprising a) at least one sulfur compound of the formula (I) A1-(Z1)m—(S)n—(Z2)p-A2??(I) where the definitions of the symbols and indices are as follows: A1 and A2 are identical or different, being C6-C12-aryl, cyclohexyl, Si(ORa)3, a saturated, partially unsaturated, or aromatic, mono- or bicyclic ring having from 3 to 12 ring members and comprising one or more heteroatoms from the group of N, O, and S, where the system is unsubstituted or has substitution by one or more substituents of the group of O, OH, S, SH, COORb, CONRcRd, C1-C18-alkyl, C1-C18-alkoxy, C1-C18-thioalkyl, C6-C12-aryl, C6-C12-aryloxy, C2-C18-alkenyl, C2-C18-alkenoxy, C2-C18-alkynyl, and C2-C18-alkinoxy; Z1 and Z2 are identical or different, being —CO— or —CS—; Ra is C1-C18-alkyl; Rb, Rc, and Rd are identical or different, being H, C1-C18-alkyl, C6-C12-aryl, or an aromatic, mono- or bicyclic ring having from 3 to 12 ring members and comprising one or more heteroatoms from the group of N, O, and S; m and p are

Abstract: Novel stable aqueous suspensions of a functionalized, completely or partially hydrogenated nitrite rubber are provided with very low emulsifier content and small particle diameter, furtheron a process for production thereof and the use thereof for producing composite materials via coating of substrate materials with the suspension.

Abstract: A granulated powder comprises a plurality of metal particles and an organic binder. It is obtainable by binding a plurality of metal particles to one another by the organic binder. The organic binder contains polyvinyl alcohol or a derivative thereof, a wax, and a nonionic surfactant. The total amount of the wax and the nonionic surfactant is preferably from 0.01 to 1 part by weight based on 100 parts by weight of the metal particles. Further, the organic binder preferably further contains a polyol and an organic amine.

Abstract: Highly fluorinated ion-exchange polymers achieve dissolution in aqueous tetrahydrofuran at lower pressures and temperatures than in other solvents, with few or no side products being formed.

Abstract: A composition which cures in ambient conditions to form a film substantially impenetrable to heavy metals, contains water, a water-miscible organic solvent, a water-borne primary resin having a glass transition temperature of 25 degrees C. or less, and a hydrophobic surfactant.

Abstract: A sulfonated polymer comprising a 3-substituted fused thienothiophene repeat unit, a composition comprising the polymer, a method of making the polymer, and a device comprising the polymer. The polymers can be used in hole injection or hole transport layers, or other applications in organic electronic devices.

Abstract: A stable caulk or sealant composition containing as principal ingredients styrene-ethylene/butylene-styrene copolymer and Diethyl ether is disclosed. The composition is generally employed in a canister pressurized with a propellant to expel a stream of water-impervious sealant to fill cracks, crevices and gaps to water damage. When desired, the sealant is removable from the application area.

Abstract: The present invention discloses a fabrication method of a basic polymer electrolyte film of blended polyvinyl alcohol and quaternary amine, wherein hydrophilic polyvinyl alcohol and quaternary amine are separately dissolved in a polar organic solvent, and then, the solutions are blended to obtain a glutinous polymeric solution; the glutinous polymeric solution is baked to form a film, and then, the film is soaked in an alkali hydroxide solution to obtain a basic electrolyte-containing solid-state polymer electrolyte film. The basic polymer electrolyte film of the present invention has the characteristics of superior chemical stability, high mechanical strength and high ionic conductivity. When the present invention applies to a zinc-air battery, the utilization rate of zinc is promoted. The basic polymer electrolyte film of the present invention can be widely used in various energy storage systems, such as alkaline battery systems, alkaline fuel cells and capacitors.

Abstract: The present disclosure provides lubricious antimicrobial coating vehicles for medical devices capable of reducing the coefficient of friction of such devices upon exposure thereof to moisture and imparting antimicrobial properties to said devices. The coating vehicle allows the introduction of a pharmacological additive having a release rate that is within acceptable pharmacokinetic criteria.