Abstract: A brazing method is disclosed. The brazing method includes providing a substrate, providing at least one groove in the substrate, providing a support member, positioning the support member over the at least one groove in the substrate, providing a braze material, applying the braze material over the support member to form an assembly, and heating the assembly to braze the braze material to the substrate. Another brazing method includes providing a preform, providing a wire mesh, pressing the wire mesh into the preform, heating the preform to form a braze material including the wire mesh, providing a substrate, providing at least one groove in the substrate, applying the braze material over the at least one groove in the substrate, then brazing the braze material to the substrate.

Abstract: A weld repair for repairing an imperfection in a nickel base superalloy article. The weld repair provides a weldment that includes a weld joint, a heat affected zone adjacent to the weld joint and a nickel base alloy base material adjacent to the heat affected zone and opposite the weld joint. The weld joint utilizes a nickel base weld filler material, having a composition, in weight percent of 0.03-0.13% C, 22.0-23.0% Cr, 18.5-19.5% Co, 1.8-2.2% W, 0.7-1.4% Nb, 2.2-2.4% Ti, 1.3-2.0% Al, 0.005-0.040% Zr, 0.002-0.008% B, up to 0.15% Mo, up to 0.35% Fe, up to 0.10% Mn, up to 0.10% Cu, up to 0.10% V, up to 0.15% Hf, up to 0.25% Si, and the balance Ni and incidental impurities. The weld filler material is characterized by an absence of Ta.

Abstract: A method of welding alloys having a ductility drop temperature range to limit strain-age cracking. The method involves the use of a welding device to weld a weld area of an article while maintaining temperatures throughout the weld area and a heat affected zone adjacent the weld area within a non-crack sensitive temperature range that is above a ductility drop temperature range of the alloy being welded. During welding, the temperatures of the weld area and the heat affected zone are predominantly controlled with heat input from the welding device. Once the welding has been terminated, the weld area and the heat affected zone are cooled from the non-crack sensitive temperature range through the ductility drop temperature range to a temperature below the ductility drop temperature range of the alloy.

Abstract: A process of welding an article and a welded turbine blade are disclosed. The process includes fusion welding over a primary symmetry line determined from a center of gravity on a first side of the article or blade and fusion welding over the primary symmetry line determined from the center of gravity on a second side of the article or blade. The fusion treating includes multiple fusion treatments.

Abstract: Hybrid welding methods include directing a laser beam from a laser onto a first component that is vertically offset from a second component, and, directing a weld arc from an arc welder onto a weld joint between the first component and the second component to weld the first and second components together.

Abstract: Turbine buckets include a pressure side, a suction side opposite the pressure side, and a bucket squealer tip attached to the pressure side and the suction side. The bucket squealer tip includes a plurality of high hot hardness shroud-cutting deposits deposited on its exterior surface that have a hardness of at least about 1100 kg mm?2 and a melting temperature of at least about 1500° C.

Abstract: A metal chemistry includes an amount of chromium weight of between about 9.0% and about 16% by weight, an amount of cobalt of between about 7.0% and about 14% by weight, an amount of molybdenum of between about 10% and about 20% by weight, an amount of iron of between about 1.0% and about 5.0% by weight, an amount of aluminum of between about 0.05% and about 0.75% by weight, an amount of titanium of between about 0.5% and about 2.0% by weight, an amount of manganese not to exceed about 0.8% by weight, an amount of carbon of between about 0.02% and about 0.10% by weight, an amount of a titanium+aluminum alloy of between about 0.55% and about 2.75% by weight, and an amount of nickel.

Abstract: A thermal management article, a method for forming a thermal management article and a thermal management method are disclosed. Forming a thermal management article includes forming a duct adapted to be inserted into a groove on the surface of a substrate, and attaching the duct to the groove so that the top outer surface of the duct is substantially flush with the surface of the substrate. Thermal management of a substrate includes transporting a fluid through the duct of a thermal management article to alter the temperature of the substrate.

Abstract: A brazing method is disclosed. The brazing method includes providing a substrate, providing at least one groove in the substrate, providing a support member, positioning the support member over the at least one groove in the substrate, providing a braze material, applying the braze material over the support member to form an assembly, and heating the assembly to braze the braze material to the substrate. Another brazing method includes providing a preform, providing a wire mesh, pressing the wire mesh into the preform, heating the preform to form a braze material including the wire mesh, providing a substrate, providing at least one groove in the substrate, applying the braze material over the at least one groove in the substrate, then brazing the braze material to the substrate.

Abstract: A method for making a cellular seal member for a turbine is disclosed. The method includes, in sequence, forming a diffusion aluminide coating on a surface of a cellular seal to form a coated cellular seal. The method also includes brazing the coated cellular seal to a seal substrate.

Abstract: A method of fabricating a component and a fabricated component are disclosed. The method includes depositing a material to a component and manipulating the material to form a boundary region and a filler region for desired properties. The component includes the boundary region and the filler region, thereby having the desired properties.

Abstract: Various embodiments include apparatuses adapted to be used as a replacement oil cartridge tip. In some embodiments apparatuses include a replacement swirler ring for an oil cartridge tip, the replacement swirler ring having an annular main body including an inner diameter surface sized to be joined to an outer diameter surface of the oil cartridge tip by a metal joining process including one of brazing, welding temperature or mechanical interference and an outer diameter surface including channels evenly spaced about a primary axis of the annular main body, wherein the annular ring includes a material that is at least as wear-resistant as a material of the oil cartridge tip.

Abstract: A brazing process and plate assembly are disclosed. The brazing process includes positioning a braze foil on a first workpiece, then securing the braze foil to the first workpiece to form a brazable component, then positioning a second workpiece proximal to the brazable component, and then brazing the second workpiece to the brazable component. Additionally or alternatively, the brazing process includes positioning the braze foil on a tube, then securing the braze foil to the tube to form a brazable tube, then positioning a plate of a plate assembly proximal to the brazable tube, and then brazing the plate to the brazable tube. The plate assembly includes a plate and a tube brazed to the plate by a braze foil secured to the tube.

Abstract: A method for repairing a component with a leak are disclosed. In an embodiment, a component having at least one fluid flow path with a leak therein is provided. The component may be made of a first material. A second material may be introduced into the fluid flow path, and propelled into the location of the leak in the flow path. Once there, the second material is melted and solidified, forming a plug that occludes the leak.

Abstract: Methods for modifying a plurality of cooling holes of a component include disposing a recess-shaped modification in a recess of the component comprising a plurality of cooling hole outlets, wherein the recess-shaped modification is formed to substantially fill the recess and comprising a plurality of modified cooling holes passing there through. The method further includes aligning the plurality of modified cooling holes of the recess-shaped modification with the plurality of cooling hole outlets of the component, and, bonding the recess-shaped modification disposed in the recess to the component, wherein the plurality of modified cooling holes of the recess-shaped modification is fluidly connected with the plurality of cooling holes of the component.

Abstract: A method of fabricating a component and a fabricated component are disclosed. The method includes depositing a material to a component and manipulating the material to form a boundary region and a filler region for desired properties. The component includes the boundary region and the filler region, thereby having the desired properties.

Abstract: A joining process and a joined article are disclosed. The joining process includes positioning an article having a base material, and friction joining a pre-sintered preform to the base material. The pre-sintered preform forms a feature on the article. The joined article includes a feature joined to a base material by friction joining of a pre-sintered preform.

Abstract: Disclosed is a method for affixing a metal cladding to a metal base. The method includes: heating the metal cladding and a surface of the metal base with a heating device to create a molten metal pool having molten metal cladding layered upon molten metal base material in the metal base; stabilizing a temperature gradient of the molten metal pool with a laser beam directed into the molten metal pool; and cooling the molten metal pool to affix solidified cladding to the metal base.

Abstract: According to one aspect of the invention, a method for manufacturing a hot gas path component of a turbine is provided, the method including forming cooling channels in a surface of a member. The method also includes disposing a layer on the surface of the member to enclose the cooling channels, the layer being disposed on a portion of the member to be cooled and bonding the layer to the surface, wherein bonding comprises heating the member and the layer.

Abstract: A welding process, welding system and welded article are disclosed. The welding process includes directing energy from one or more fusion beams to join a first element to a second element and to join the first element to a third element. The directing of the energy is at a first lateral angle and a second lateral angle with respect to the first element. The welding system includes an energy emitting device, a first fusion beam and a second fusion beam. The first fusion beam and the second fusion beam are oriented to extend diagonally through an article. The laser welded article includes the first element joined to the second element, and the first element joined to the third element. A fillet weld is formed in a first inaccessible portion between the first element and the second element and a second inaccessible portion between the first element and the third element.