Abstract: The present invention relates to a steel sheet for a hot press formed member having excellent coating adhesion, and a method for manufacturing the same. A steel sheet for hot press forming according to one aspect of the present invention is an aluminum alloy plated steel sheet, wherein an average Fe content in a plating layer may be 40 wt % or more, and a concentration gradient of a section having a Fe content of 45 wt % to 80 wt % in the plating layer may 7 wt %/?m or less of a concentration gradient at a section having an Fe content of 45% to 80% in the plating layer in a thickness direction from a surface of the plating layer according to a result of GDS analysis.

Abstract: The present invention provides a steel plate plated with an aluminum-iron alloy for hot press forming, the steel plate comprising a base steel sheet and an alloy plated layer formed on the base steel sheet, wherein the alloy plated layer comprises: an alloyed layer (I) formed on the base steel sheet and containing, by weight, Al: 5-30%; an alloyed layer (II) formed on the alloyed layer (I) and containing, by weight, Al: 30-60%; and an alloyed layer (III) formed on the alloyed layer (II) and containing, by weight, Al: 20-50%, wherein the alloy layer (II) has a FeAl (Si) alloy phase dispersed and distributed therein, the FeAl(Si) alloy phase comprising, by weight, Al: 20-50% and Si: 5-20%, and the number density of the FeAl(Si) alloy phase having a circle-equivalent diameter of 5 ?m or less is 103/mm2 or more.

Abstract: The present invention provides an aluminum-based plated steel plate used in hot-press forming, the steel plate comprising: a base steel plate; and a plating layer formed on the base steel plate, wherein the plating layer comprises: an alloying layer formed on the surface of the base steel plate and including one or more of Fe 3Al, FeAl(Si), Fe 2Al 5, and FeAl 3; and an aluminum layer formed on the alloying layer and having a thickness less than 10% of the thickness of the plating layer, and the plating layer has a thickness of 5-20 ?m and an oxygen content of 10 weight % or less, as measured by GDS, at a depth of 0.1 ?m from the surface of the plating layer.

Abstract: The present invention provides a steel sheet plated with aluminum-iron and a preparation method therefor, the steel sheet comprising: a base steel sheet; and a plated layer formed on the surface of the base steel sheet and comprising: an alloyed layer containing at least one of Fe3Al, FeAl(Si), Fe2Al5, and FeAl3; and an aluminum layer formed on the alloyed layer and having a thickness less than 10% of that of the plated layer, wherein the plated layer is 20-35 ?m in thickness and contains 1-20 wt % of Mg as measured by GDS at a position 0.1 ?m deep from the surface of the plated layer and 10 wt % of oxygen as measured by GDS at a position 0.1 ?m deep from the surface of the plated layer.

Abstract: The present invention provides an iron-aluminum-based plated steel sheet, and a manufacturing method therefor, the iron-aluminum-based plated steel sheet comprising a base steel sheet and a plated layer formed on the surface of the base steel sheet, wherein the alloy plated layer comprises: a diffusion layer comprising an Fe—Al-based intermetallic compound having a cubic structure; and an alloyed layer formed on the diffusion layer and composed of an alloy phase differing from that of the cubic structure, the thickness of the diffusion layer is 3-20 ?m, and the thickness of the diffusion layer is greater than 50% of the total thickness of the plated layer.

Abstract: The present invention pertains to a hot press forming member having excellent resistance to hydrogen embrittlement, and a method for manufacturing same. An aspect of the present invention provides a hot press forming member having excellent resistance to hydrogen embrittlement, the hot press forming member comprising a base steel plate and an alloy-plated layer formed on the surface of the base steel plate, wherein the alloy-plated layer contains pores such that pores having a size of 5 ?m or less constitute 3-30% of the surface area of the alloy-plated layer as viewed in a cross-section taken in the thickness direction of the member.

Abstract: The present invention provides: a plated steel sheet for hot press forming having excellent impact properties after hot press forming; a hot press formed member manufactured using the plated steel sheet for hot press forming; and manufacturing methods thereof. The plated steel sheet comprises: a base steel sheet containing, by weight, 0.15-0.4% of C, 0.1-1% of Si, 0.6-8% of Mn, 0.001-0.05% of P, 0.0001-0.02% of S, 0.01-0.1% of Al, 0.001-0.02% of N, and 0.01-0.5% of Cr, with the remainder comprising Fe and miscellaneous impurities; and a plating layer formed on the surface of the base steel sheet and composed of zinc, aluminum, or an alloy containing zinc and aluminum, wherein the ratio (C S/C B) of the content (C S) of C in a surface layer to the content (C B) of C in the base steel sheet is 0.6 or less, and the ratio ((Mn S+Cr S)/(Mn B+Cr B)) of the total content (Mn S+Cr S) of Mn and Cr in the surface layer to the total content (Mn B+Cr B) of Mn and Cr in the base steel sheet is 0.8 or more.

Abstract: The present disclosure relates to an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: The present disclosure provides a hot-press formed part comprising a plated steel sheet and an aluminum alloy plated layer formed on the plated steel sheet, wherein the aluminum alloy plated layer comprises: an alloying layer (I) formed on the plated steel sheet and containing, by weight %, 5-30% of Al; an alloying layer (II) formed on the alloying layer (I) and containing, by weight %, 30 to 60% of Al; an alloying layer (III) formed on the alloying layer (II) and containing, by weight %, 20-50% of Al and 5-20% of Si; and an alloying layer (IV) formed continuously or discontinuously on at least a part of the surface of the alloying layer (III), and containing 30-60% of Al, wherein the rate of the alloying layer (III) exposed on the outermost surface of the aluminum alloy plated layer is 10% or more.

Abstract: Provided is a steel sheet for a hot press formed member having excellent coating adhesion, and a method for manufacturing the same. A steel sheet for hot press forming is an aluminum alloy plated steel sheet, wherein an average Fe content in a plating layer may be 40 wt % or more, and a concentration gradient of a section having a Fe content of 45 wt % to 80 wt % in the plating layer may 7 wt %/?m or less of a concentration gradient at a section having an Fe content of 45% to 80% in the plating layer in a thickness direction from a surface of the plating layer according to a result of GDS analysis.

Abstract: Provided is a steel sheet for a hot press formed member having excellent painting adhesion and post-painting corrosion resistance, and a method for manufacturing the same. A steel sheet for hot press forming according to one aspect of the present invention comprises a base steel sheet and a plated layer formed on a surface of the base steel sheet, wherein the ratio of an area occupied by pores to the entire area of a surface layer portion may be 10% or more in a cross section of the surface layer portion observed when the plated layer is cut in a thickness direction thereof.

Abstract: Provided is an aluminum-based plated steel that is provided for vehicles by hot forming, an aluminum-based alloy plated steel manufactured using the same, and method of manufacturing thereof.

Abstract: Provided is a steel sheet for a hot press formed member having excellent painting adhesion and post-painting corrosion resistance, and a method for manufacturing the same. A steel sheet for hot press forming according to one aspect of the present invention comprises a base steel sheet and a plated layer formed on a surface of the base steel sheet, wherein the ratio of an area occupied by pores to the entire area of a surface layer portion may be 10% or more in a cross section of the surface layer portion observed when the plated layer is cut in a thickness direction thereof.

Abstract: Provided is an Al—Fe-alloy plated steel sheet for hot forming, having excellent TWB welding characteristics since excellent hardness uniformity of a TWB weld zone after hot forming is obtained by suitably controlling a batch annealing condition, after plating Al, such that an Al—Fe-alloy layer is formed; a hot forming member; and manufacturing methods therefor.

Abstract: Provided is a plated steel sheet for hot press forming, having an excellent impact property, including: a base steel sheet comprising, by wt %, 0.15-0.4% of C, 0.05-1.0% of Si, 0.6-3.0% of Mn, 0.001-0.05% of P, 0.0001-0.02% of S, 0.01-0.1% of Al, 0.001-0.02% of N, 0.001-0.01% of B, 0.01-0.5% of Cr, 0.01-0.05% of Ti, and the balance of Fe and inevitable impurities; and an Al—Si plated layer formed on the surface of the base steel sheet. A thickness of a carbon-depleted layer in a surface layer part of the base steel sheet is 5 ?m or less. The surface layer part means a region from the surface of the base steel sheet to a depth of 200 ?m, and the carbon-depleted layer means a region which the carbon content is 50% or less of an average carbon amount (C0) of the base steel sheet.

Abstract: Provided is a plated steel sheet for hot press forming, having an excellent impact property, including: a base steel sheet comprising, by wt %, 0.15-0.4% of C, 0.05-1.0% of Si, 0.6-3.0% of Mn, 0.001-0.05% of P, 0.0001-0.02% of S, 0.01-0.1% of Al, 0.001-0.02% of N, 0.001-0.01% of B, 0.01-0.5% of Cr, 0.01-0.05% of Ti, and the balance of Fe and inevitable impurities; and an Al—Si plated layer formed on the surface of the base steel sheet. A thickness of a carbon-depleted layer in a surface layer part of the base steel sheet is 5 ?m or less. The surface layer part means a region from the surface of the base steel sheet to a depth of 200 ?m, and the carbon-depleted layer means a region which the carbon content is 50% or less of an average carbon amount (C0) of the base steel sheet.

Abstract: Provided is a cold-rolled steel plate for hot forming, which is excellent in corrosion-resistance and spot-weldability, contains, by weight %, C: 0.1-0.4%, Si: 0.5-2.0%, Mn: 0.01-4.0%, Al: 0.001-0.4%, P: 0.001-0.05%, S: 0.0001-0.02%, Cr: 0.5% to less than 3.0%, N: 0.001-0.02%, and a balance of Fe and inevitable impurities, satisfying formula (1) below, and includes an Si amorphous oxidation layer continuously or discontinuously formed at a thickness of 1 nm-100 nm on the surface thereof. Formula (1): 1.4?0.4*Cr+Si?3.2 (wherein element symbols denote measurements of respective element contents by weight %).

Abstract: Provided is a steel sheet for a hot press formed member having excellent coating adhesion, and a method for manufacturing the same. A steel sheet for hot press forming is an aluminum alloy plated steel sheet, wherein an average Fe content in a plating layer may be 40 wt % or more, and a concentration gradient of a section having a Fe content of 45 wt % to 80 wt % in the plating layer may 7 wt %/?m or less of a concentration gradient at a section having an Fe content of 45% to 80% in the plating layer in a thickness direction from a surface of the plating layer according to a result of GDS analysis.

Abstract: Provided is a steel sheet for a hot press formed member having excellent resistance to hydrogen delayed fracture, and a method for manufacturing the same. A steel sheet for a hot press formed member comprises: a base steel sheet; an aluminum alloy plating layer on a surface of the base steel sheet; and an oxide layer which is formed on a surface of the plating layer and has a thickness of 0.05 ?m or more.

Abstract: Provided is a steel sheet for a hot press formed member having excellent painting adhesion and post-painting corrosion resistance, and a method for manufacturing the same. A steel sheet for hot press forming according to one aspect of the present invention comprises a base steel sheet and a plated layer formed on a surface of the base steel sheet, wherein the ratio of an area occupied by pores to the entire area of a surface layer portion may be 10% or more in a cross section of the surface layer portion observed when the plated layer is cut in a thickness direction thereof.