Abstract: An endless metal belt including a ring formed by laminating endless metal plates; and multiple elements continuously attached to the ring. Each of the elements has a body, a head connected to the body by a pillar, and slots formed between the body and the head on left and right sides of the pillar, respectively, for receiving the ring. The elements satisfy the equations (h/t)<1 and (S/h)>40, where h is a width of the slots, t is a plate thickness of the elements, and S is an area of the head.

Abstract: There is provided a galvanized steel sheet that has various properties such as corrosion resistance and adhesion and allows for high conductivity at a low contact pressure. A first layer film is formed by applying a surface treatment solution having a pH of 8 to 10 onto the surface of the galvanized steel sheet and drying the surface treatment solution by heating, the surface treatment solution containing a water-soluble zirconium compound, a tetraalkoxysilane, an epoxy group-containing compound, a chelating agent, a silane coupling agent, vanadic acid, and a metal compound in a specific ratio. Subsequently, a second layer film is formed by applying a surface treatment solution containing an organic resin onto the surface of the first layer film and drying the surface treatment solution by heating.

Abstract: A surface-treatment agent contains a resin compound having a specific bisphenol skeleton, a cationic urethane resin emulsion, a silane coupling agent, an organic titanium chelate compound, a tetravalent vanadyl compound, and water, with predetermined proportions and having a pH of 4 to 5; a method for producing a coated steel sheet using the surface-treatment agent; and a coated steel sheet.

Abstract: A method for making a phosphate-treated galvanized steel sheet, including forming a phosphate film on the surface of a galvanized layer of a galvanized steel sheet using a phosphate treatment solution containing Zn2+ and Mg2+ so as to satisfy 2.0<Zn2+?5.0 g/L, 2.0?Mg2+?5.0 g/L, and 0.4?Mg2+/Zn2+?2.5, and satisfying 0.020?free acidity/total acidity<0.10. The method allows for the quick formation of a uniform phosphate film, whereby a phosphate-treated galvanized steel sheet having excellent corrosion resistance and blackening resistance is obtained.

Abstract: An endless metal belt including a ring formed by laminating endless metal plates; and multiple elements continuously attached to the ring. Each of the elements has a body, a head connected to the body by a pillar, and slots formed between the body and the head on left and right sides of the pillar, respectively, for receiving the ring. The elements satisfy the equations (h/t)<1 and (S/h)>40, where h is a width of the slots, t is a plate thickness of the elements, and S is an area of the head.

Abstract: A hot-dip Zn—Al alloy coated steel sheet exhibiting a beautiful coating appearance with metallic luster, in which no spangle or very fine spangles are formed, and having excellent blackening resistance and a method for manufacturing the hot-dip Zn—Al alloy coated steel sheet are provided. The hot-dip Zn—Al alloy coated steel sheet includes a hot-dip Zn—Al alloy coating layer containing 1.0 to 10 percent by mass of Al, 0.2 to 1.0 percent by mass of Mg, 0.005 to 0.1 percent by mass of Ni, and the balance being Zn and incidental impurities on at least one surface of a steel sheet. The manufacturing method includes the steps of dipping the steel sheet into a hot-dip Zn—Al alloy coating bath and pulling up and cooling the steel sheet, wherein the steel sheet pulled up from the coating bath is cooled to 250° C. at a cooling rate of 1° C. to 15° C./sec.

Abstract: An aqueous surface-treatment liquid is a treatment liquid containing a water-soluble zirconium compound, water-dispersive particulate silica, a silane coupling agent, a vanadic acid compound, a phosphoric acid compound, a nickel compound, and an acrylic resin emulsion in particular proportions. A surface-treated galvanized steel sheet produced using the treatment liquid is a galvanized steel sheet having a surface-treatment coating on a surface thereof, and the coating contains a zirconium compound, particulate silica, a silane-coupling-agent-derived component, a vanadic acid compound, a phosphoric acid compound, a nickel compound, and an acrylic resin in particular proportions. The amount of coating on a zirconium basis is 10 to 200 mg/m2. This surface-treated galvanized steel sheet is chromate-free and has superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming.

Abstract: A method for making a phosphate-treated galvanized steel sheet, including forming a phosphate film on the surface of a galvanized layer of a galvanized steel sheet using a phosphate treatment solution containing Zn2+ and Mg2+ so as to satisfy 2.0<Zn2+?5.0 g/L, 2.0?Mg2+?5.0 g/L, and 0.4?Mg2+/Zn2+?2.5, and satisfying 0.020?free acidity/total acidity<0.10. The making method allows the quick formation of a uniform phosphate film, whereby a phosphate-treated galvanized steel sheet having excellent corrosion resistance and blackening resistance is obtained.

Abstract: A surface-treated steel sheet is disclosed, including a zinc based plated steel sheet having thereon a surface-treated film containing titanium, nickel, aluminum and fluorine and having a film thickness of from 0.05 to 1.0 ?m, the surface-treated film having a titanium deposition amount of from 0.01 to 0.5 g/m2 and containing from 0.01 to 5 parts by mass of nickel, from 0.1 to 25 parts by mass of aluminum and from 1 to 500 parts by mass of fluorine relative to 100 parts by mass of titanium. This surface-treated steel sheet does not contain hexavalent chromium in the film thereof at all and has excellent heat discoloration resistance, corrosion resistance and resistance to blackening.

Abstract: A method for producing a hot-dip galvanized steel sheet which includes a hot-dip galvanization step, a temper rolling step and an oxidation step.

Abstract: A surface-treated steel sheet is disclosed, including a zinc based plated steel sheet having thereon a surface-treated film containing titanium, nickel, aluminum and fluorine and having a film thickness of from 0.05 to 1.0 ?m, the surface-treated film having a titanium deposition amount of from 0.01 to 0.5 g/m2 and containing from 0.01 to 5 parts by mass of nickel, from 0.1 to 25 parts by mass of aluminum and from 1 to 500 parts by mass of fluorine relative to 100 parts by mass of titanium. This surface-treated steel sheet does not contain hexavalent chromium in the film thereof at all and has excellent heat discoloration resistance, corrosion resistance and resistance to blackening.

Abstract: A hot-dip galvanized steel sheet includes a plating layer substantially composed of the ? phase and an oxide layer disposed on a surface of the plating layer. The oxide layer has an average thickness of 10 nm or more and includes a Zn-based oxide layer and an Al-based oxide layer. A method for producing the hot-dip galvanized steel sheet includes a hot-dip galvanization step, a temper rolling step, and an oxidation step.

Abstract: A hot-dip galvanized steel sheet includes a plating layer substantially composed of the ? phase and an oxide layer disposed on a surface of the plating layer. The oxide layer has an average thickness of 10 nm or more and includes a Zn-based oxide layer and an Al-based oxide layer. A method for producing the hot-dip galvanized steel sheet includes a hot-dip galvanization step, a temper rolling step, and an oxidation step.

Abstract: The zinc-base plated steel sheet has a steel sheet, a zinc-base plating layer on the steel sheet, and a composite coating film formed on the plating layer, which composite coating layer contains a P ingredient, an N ingredient, and at least one element selected from the group consisting of Mg, Al, Ca, Ti, Fe, Co, Ni, Cu, and Mo, and is prepared by applying an aqueous solution containing a cationic ingredient (?) and a phosphoric acid ingredient (?) onto the surface of plating layer on the zinc-base plated steel sheet, and then drying the applied aqueous solution, without giving washing with water, and which cationic ingredient (?) consists essentially of at least one metallic ion selected from the group consisting of Mg, Al, Ca, Ti, Fe, Co, Ni, Cu, Mo, and NH4+ ions.

Abstract: The method for manufacturing galvanized steel sheet has a step of adjusting the surface texture thereof by blasting solid particles against the surface thereof. The surface texture is defined by at least one parameter selected from the group of parameters consisting of mean roughness Ra on the surface of steel sheet, peak count PPI on the surface of steel sheet, and filtered centerline waviness Wca on the surface of steel sheet. The galvanized steel sheet has a surface in dimple-pattern texture.

Abstract: The zinc-base plated steel sheet has a steel sheet, a zinc-base plating layer on the steel sheet, and a composite coating film formed on the plating layer, which composite coating layer contains a P ingredient, an N ingredient, and at least one element selected from the group consisting of Mg, Al, Ca, Ti, Fe, Co, Ni, Cu, and Mo, and is prepared, by applying an aqueous solution containing a cationic ingredient (&agr;) and a phosphoric acid ingredient (&bgr;) onto the surface of plating layer on the zinc-base plated steel sheet, and then drying the applied aqueous solution, without giving washing with water, and which cationic ingredient (&agr;) consists essentially of at least one metallic ion selected from the group consisting of Mg, Al, Ca, Ti, Fe, Co, Ni, Cu, Mo, and NH4+ ions.

Abstract: The method for manufacturing galvanized steel sheet has a step of adjusting the surface texture thereof by blasting solid particles against the surface thereof. The surface texture is defined by at least one parameter selected from the group of parameters consisting of mean roughness Ra on the surface of steel sheet, peak count PPI on the surface of steel sheet, and filtered centerline waviness Wca on the surface of steel sheet. The galvanized steel sheet has a surface in dimple-pattern texture.

Abstract: A coated steel sheet having excellent corrosion resistance comprises: a zinc or a zinc alloy plated steel sheet or an aluminum or an aluminum alloy plated steel sheet; a composite oxide coating formed on the surface of the plated steel sheet; and an organic coating formed on the composite oxide coating. The composite oxide coating contains a fine particle oxide and a phosphoric acid and/or a phosphoric acid compound. The organic coating has thickness of from 0.1 to 5 &mgr;m.

Abstract: Steel sheet having organic coating comprises: a zinc or a zinc alloy plated steel sheet or an aluminum or an aluminum alloy plated steel sheet; a composite oxide coating formed on the surface of the plated steel sheet and containing at least one metal selected from the group consisting of Mn and Al; and an organic coating formed on the composite oxide coating and containing a rust-preventive additive component.

Abstract: A phosphate-treated steel plate comprises a zinc-base plated steel plate; a zinc phosphate coating layer formed on the surface of the zinc-base plated steel plate; and an organic or inorganic coating formed on the zinc phosphate coating layer. The organic coating comprises at least one organic resin selected from the group consisting of an ethylene-base resin, an epoxy-base resin, a urethane-base resin, and an acrylic-base resin. The inorganic coating comprises a phosphate coating consisting mainly of a phosphate.