Abstract: The present invention is a composition for forming a metal oxide film, including: (A) a metal oxide nanoparticle; (B) a flowability accelerator containing a resin having a structural unit represented by the following general formula (1); (C) a dispersion stabilizer having two or more benzene rings or having one benzene ring and a structure represented by the following general formula (C-1), and the dispersion stabilizer being composed of an aromatic group-containing compound having a molecular weight of 500 or less; and (D) an organic solvent, wherein the flowability accelerator (B) has a content of 9 mass % or more in an entirety of the composition, a ratio Mw/Mn of 2.50?Mw/Mn?9.00, and the flowability accelerator (B) having no cardo structure.

Abstract: An object of the present invention is to provide a wafer edge protection film having dry etching resistance superior to those of the previously-known wafer edge protection films, as well as excellent film forming property even at wafer edge portions, which are difficult to coat: a wafer edge protection film forming method for forming a protection film on a wafer edge of a substrate, including the steps of (i) coating a peripheral edge of the substrate with a composition for forming a protection film including an aromatic ring-containing resin (A) having an organic group represented by the following general formula (1), and a solvent; and (ii) curing the applied composition for forming a protection film by heat or optical irradiation to form the protection film on the peripheral edge of the substrate. wherein RA is a hydrogen atom or a monovalent organic group having 1 to 10 carbon atoms, and * represents a bonding site.

Abstract: A method for recycling a Ni-based single crystal superalloy part or unidirectionally solidified superalloy part provided with a thermal barrier coating containing at least a ceramic on a surface of a Ni-based single crystal superalloy substrate or Ni-based unidirectionally solidified superalloy substrate, in which the method including the steps of: melting and desulfurizing a Ni-based single crystal superalloy part or Ni-based unidirectionally solidified superalloy part at a temperature of the melting point or more of the Ni-based single crystal superalloy or Ni-based unidirectionally solidified superalloy and less than the melting point of the ceramic; heating a casting mold for a recycled Ni-based single crystal superalloy part or casting mold for a recycled Ni-based unidirectionally solidified superalloy part to a temperature of the melting point or more of the Ni-based single crystal superalloy or Ni-based unidirectionally solidified superalloy; pouring the desulfurized melted Ni-based single crystal supe

Abstract: The present invention provides first generation Ni-based directionally solidified alloy containing none of Co and Re, which has excellent TMF characteristics, creep property and environment-resistant characteristics, and is superior in cost performance in practical use. The Ni-based directionally solidified alloy according to one embodiment of the present invention consists of Cr: 6% by mass or more and 12% by mass or less; Mo: 0.4% by mass or more and 3.0% by mass or less; W: 6% by mass or more and 10% by mass or less; Al: 4.0% by mass or more and 6.5% by mass or less; Nb: 0% by mass or more and 1% by mass or less; Ta: 8% by mass or more and 12% by mass or less; Hf: 0% by mass or more and 0.15% by mass or less; Si: 0.01% by mass or more and 0.2% by mass or less; Zr: 0% by mass or more and 0.04% by mass or less; B: 0.01% by mass or more and 0.03% by mass or less; and C: 0.01% by mass or more and 0.3% by mass or less, and a balance of Ni and inevitable impurities.

Abstract: A method for recycling a Ni-based single crystal superalloy part or unidirectionally solidified superalloy part provided with a thermal barrier coating containing at least a ceramic on a surface of a Ni-based single crystal superalloy substrate or Ni-based unidirectionally solidified superalloy substrate, in which the method including the steps of: melting and desulfurizing a Ni-based single crystal superalloy part or Ni-based unidirectionally solidified superalloy part at a temperature of the melting point or more of the Ni-based single crystal superalloy or Ni-based unidirectionally solidified superalloy and less than the melting point of the ceramic; heating a casting mold for a recycled Ni-based single crystal superalloy part or casting mold for a recycled Ni-based unidirectionally solidified superalloy part to a temperature of the melting point or more of the Ni-based single crystal superalloy or Ni-based unidirectionally solidified superalloy; pouring the desulfurized melted Ni-based single crystal supe

Abstract: Provided is a Ni-based single crystal superalloy containing 6% by mass or more and 12% by mass or less of Cr, 0.4% by mass or more and 3.0% by mass or less of Mo, 6% by mass or more and 10% by mass or less of W, 4.0% by mass or more and 6.5% by mass or less of Al, 0% by mass or more and 1% by mass or less of Nb, 8% by mass or more and 12% by mass or less of Ta, 0% by mass or more and 0.15% by mass or less of Hf, 0.01% by mass or more and 0.2% by mass or less of Si, and 0% by mass or more and 0.04% by mass or less of Zr, and optionally containing at least one element selected from B, C, Y, La, Ce, and V, with a balance being Ni and inevitable impurities.

Abstract: A heat-resistant superalloy having chromium, aluminum, cobalt, titanium, and ruthenium added thereto as main components, and having a subcomponent(s) optionally added thereto, the remainder, excluding the main components and the subcomponent(s), comprising nickel and an impurity inevitably contained, wherein the amount of the chromium added is 2 to 25% by mass, the amount of the aluminum added is 0.2 to 7% by mass, the amount of the cobalt added is 19.5 to 55% by mass, the amount of the titanium added is [0.17×(% by mass for cobalt-23)+3] to [0.17×(% by mass for cobalt-20)+7]% by mass (with the proviso that the amount of the titanium added is 5.1% by mass or more), and the amount of the ruthenium added is 0.1 to 10% by mass.

Abstract: An oxide particle dispersion-strengthened Ni-base superalloy includes Ni, 0.1% by weight to 14.0% by weight of Ru, 0.1% by weight to 14.0% by weight of Al, and inevitable impurities and has a crystal structure containing 0.01% by weight to 3.0% by weight of dispersed oxide particles based on the total amount of the superalloy.

Abstract: Provided is a Ni-based single crystal superalloy containing 6% by mass or more and 12% by mass or less of Cr, 0.4% by mass or more and 3.0% by mass or less of Mo, 6% by mass or more and 10% by mass or less of W, 4.0% by mass or more and 6.5% by mass or less of Al, 0% by mass or more and 1% by mass or less of Nb, 8% by mass or more and 12% by mass or less of Ta, 0% by mass or more and 0.15% by mass or less of Hf, 0.01% by mass or more and 0.2% by mass or less of Si, and 0% by mass or more and 0.04% by mass or less of Zr, and optionally containing at least one element selected from B, C, Y, La, Ce, and V, with a balance being Ni and inevitable impurities.

Abstract: The object of the present invention is to provide an Ni-based single crystal super alloy capable of improving strength by preventing precipitation of a TCP phase at high temperatures. This object is achieved by an Ni-based single crystal super alloy having a composition comprising 5.0-7.0 wt % of Al, 4.0-10.0 wt % of Ta, 1.1-4.5 wt % of Mo, 4.0-10.0 wt % of W, 3.1-8.0 wt % of Re, 0-0.50 wt % of Hf, 2.0-5.0 wt % of Cr, 0-9.9 wt % of Co and 4.1-14.0 wt % of Ru in terms of its weight ratio, with the remainder consisting of Ni and unavoidable impurities. Furthermore, in this Ni-based single crystal super alloy, when lattice constant of matrix is taken to be a1 and lattice constant of precipitation phase is taken to be a2, a2?0.999a1.

Abstract: There is provided a nickel alloy having an excellent creep strength as well as high-temperature oxidation resistance. The nickel alloy of the present invention comprises, by mass percent, Cr in a range of 11.5 to 11.9%, Co in a range of 25 to 29%, Mo in a range of 3.4 to 3.7%, W in a range of 1.9 to 2.1%, Ti in a range of 3.9 to 4.4%, Al in a range of 2.9 to 3.2%, C in a range of 0.02 to 0.03%, B in a range of 0.01 to 0.03%, Zr in a range of 0.04 to 0.06%, Ta in a range of 2.1 to 2.2%, Hf in a range of 0.3 to 0.4%, and Nb in a range of 0.5 to 0.8%, the balance being Ni and unavoidable impurities, and contains carbides and borides precipitating in crystal grains and at grain boundaries.

Abstract: A nickel-base superalloy having excellent oxidation resistance is provided. It is useful as high-temperature members such as turbine blades and turbine vanes for jet engines or gas turbines. The nickel-base superalloy has a composition containing Co: 0.1 to 15% by weight, Cr: 0.1 to 10% by weight, Mo: 0.1 to 4.5% by weight, W: 0.1 to 15% by weight, Al: 2 to 8% by weight, Ta+Nb+Ti: 0 to 16% by weight, Hf: 0 to 5% by weight, Re: 0.1 to 16% by weight, Ru: 0.1 to 16% by weight, Si: 0.2 to 5% by weight and a balance made of Ni and unavoidable impurities.

Abstract: The Ni-based single crystal alloy disclosed here is a single crystal and has a chemical composition containing, as % by mass, Co: 8 to 12%, Cr: 5 to 7.5%, Mo: 0.2 to 1.2%, W: 5 to 7%, Al: 5 to 6.5%, Ta: 8 to 12%. Hf: 0.01 to 0.2%, Re: 2 to 4%, Si: 0.005 to 0.1%, with the balance of Ni and inevitable impurities.

Abstract: A Ni-base superalloy having a chemical composition comprising Cr: 3.0-5.0 wt %, Co: 5.0-10.0 wt %, Mo: 0.5-3.0 wt %, W: 8.0-10.0 wt %, Ta: 5.0-8.0 wt %, Nb: 3.0 wt % or less, Al: 4.5-6.0 wt %, Ti: 0.1-2.0 wt %, Re: more than 3.0-4.0 wt %, Ru: 0.2-4.0 wt %, Hf: 0.01-0.2 wt %, and the balance being Ni and unavoidable impurities, a method for producing the same, and turbine blade or turbine vane components are disclosed. The Ni-base superalloy has high creep strength and textural stability under high temperature environment, and is excellent in applicability to turbine blade or turbine vane components of large-sized gas turbines.

Abstract: A heating section 20 having heating elements using carbon which generates heat when a high-frequency electric current is fed to a coil whose pitch can be adjusted as desired is arranged in a heating chamber 10. A cooling chamber 80 configured to cool metal is disposed below the heating chamber 10 in communication with the heating chamber 10 via a connection section 60. A water-cooled vertically movable shaft 90 which is capable of supporting the metal to be heat-treated and entering the heating chamber 10 is disposed so as to penetrate through the bottom portion of the cooling chamber 80. A gas introducing pipe 81 configured to introduce gas for cooling heated metal to be heat-treated supported by the water-cooled vertically movable shaft 90 and moved from the heating chamber 10 to the cooling chamber 80 is disposed in the cooling chamber 80.

Abstract: A Ni-based single crystal superalloy according to the invention has, for example, a composition including: 5.0 to 7.0 wt % of Al, 4.0 to 10.0 wt % of Ta, 1.1 to 4.5 wt % of Mo, 4.0 to 10.0 wt % of W, 3.1 to 8.0 wt % of Re, 0.0 to 2.0 wt % of Hf, 2.5 to 8.5 wt % of Cr, 0.0 to 9.9 wt % of Co, 0.0 to 4.0 wt % of Nb, and 1.0 to 14.0 wt % of Ru in terms of weight ratio; and the remainder including Ni and incidental impurities. In addition, the contents of Cr, Hf and Al are preferably set so as to satisfy the equation OP?108. According to the Ni-based single crystal superalloy of the invention, high creep strength can be maintained and the oxidation resistance can be improved.

Abstract: Disclosed is a novel heat-resistant superalloy for turbine disks having a chemical composition consisting of, in mass %, 19.5-55% of cobalt, 2-25% of chromium, 0.2-7% of aluminum, 3-15% of titanium and the balance of nickel and inevitable impurities.

Abstract: A Ni-base superalloy having a chemical composition comprising Al: 4.5-7.0 wt %, Ta+Nb+Ti: 0.1-4.0 wt %, with Ta being less than 4.0 wt %, Mo: 1.0-8.0 wt %, W: 0.0-10.0 wt %, Re: 2.0-8.0 wt %, Hf: 0.0-1.0 wt %, Cr: 2.0-10.0 wt %, Co: 0.0-15.0 wt %, Ru: 0.0-5.0 wt %, and the balance being Ni and unavoidable impurities, and a method for producing the same are disclosed. The Ni-base superalloy has excellent creep property at high temperature and is suitable for use as a member at high temperature under high stress.

Abstract: The oxide matrix composite material is obtained by subjecting a fiber composed of at least one oxide or complex oxide and a matrix composed of at least one oxide or complex oxide to composite formation. For the fiber and the matrix, a component composition is selected such that the fiber and the matrix keep thermodynamic equilibrium to each other in a temperature range not exceeding the melting temperature, and a fiber diameter of the fiber at the time of equilibrium keeps ½ or more of a fiber diameter of the fiber at the start of the composite formation.