Abstract: An aqueous sealant system, a wood product sealed by the aqueous sealant system, and a method for sealing a wood-based substrate. The aqueous sealant system includes: a) a film-forming resin composition including an aqueous latex of an active hydrogen-containing polymer, a filler, and optional additional additives; and b) a multi-isocyanate hardener, wherein the ratio by weight of the component a) to the component b) is 100:3 to 100:10.

Abstract: Disclosed are polypropylene articles with improved optical properties and/or an increased temperature of crystallization comprising a polypropylene resin and uniformly dispersed therein from about 1 ppm to about 10 ppm of one or more polycyclic organic pigments selected from blue, green, magenta, red, yellow, orange and violet polycyclic organic pigments and from about 50 ppm to about 250 ppm of one or more aromatic trisamide nucleating agents, where the ppm levels are by weight based on the weight of the polypropylene resin. The polypropylene is for example polypropylene homopolymer. The articles exhibit reduced haze, increased temperature of crystallization and excellent clarity.

Abstract: A novel olefin or polyester (PET) fiber or yarn, or a textile fabric, tufted, knitted, woven and non-woven, is manufactured using olefin or polyester (PET) yarns that contain variable amounts of a unique dye acceptor additive. The fabrics and yarns using this invention can be processed using existing nylon dyeing and finishing systems at atmospheric pressure. The dye acceptor additive can be easily and inexpensively dosed into a conventional yarn or fiber extruder or can be incorporated in blended pellets which can be extruded into a nylon dyeable polyester (PET) or olefin fiber or yarn. A fabric with more than one tone of a color can be dyed in a single dye bath by using different amounts of additive in different yarns. This invention is of particular value in the apparel, carpet and home furnishings industries.

Abstract: Solvent-containing clearcoat coating composition comprising (A) an OH-functional (meth)acrylate (co)polymer comprising (A1) 30%-99% by weight, based on the mass of the nonvolatile fraction of (A), of at least one OH-functional (meth)acrylate (co)polymer having an OH number of 60-200 mg KOH/g and glass transition temperature Tg of 15° C. to 100° C., and (A2) 1%-70% by weight, based on the mass of the nonvolatile fraction of (A), of at least one OH-functional (meth)acrylate (co)polymer having an OH number of 60-200 mg KOH/g and a glass transition temperature Tg of ?100° C. to ?20° C., (B) a crosslinker component comprising functional groups reactive toward OH, (C) 0.02%-1.2% by weight, based on the mass of the nonvolatile fraction of (A), of at least one polyamide and (D) 0.04%-2.9% by weight, based on the mass of the nonvolatile fraction of (A), of at least one urea adduct of a polyisocyanate and benzylamine.

Abstract: Disclosed are an alkyl(meth)acrylate-based thermoplastic resin composition and a thermoplastic resin with modified scratch resistance and yellowness. The alkyl(meth)acrylate-based thermoplastic resin composition provides improved scratch resistance and low yellowness index while maintaining transparency, flowability, and impact strength, even when the total content of the vinyl cyan-based monomer contained in the resin composition is reduced to a level unattainable by conventional techniques, and the content of the alkyl(meth)acrylate-based monomer is increased.

Abstract: Disclosed are an acrylonitrile copolymer excellent in thermal stability as a solution (spinning dope) when dissolved in an amide solvent and capable of forming dense polyacrylonitrile fiber suitable for production of carbon fiber, an acrylonitrile copolymer solution in which the acrylonitrile copolymer is dissolved in an amide solvent, and a method for producing polyacrylonitrile precursor fiber for carbon fiber by use of the acrylonitrile copolymer solution. Specifically, an acrylonitrile copolymer contains a sulfonate group derived from a polymerization initiator in an amount of 1.0×10?5 equivalent/g or more, and the value (equivalent ratio) of (the content of a sulfate group derived from the polymerization initiator/the total content of the sulfonate group and the sulfate group) is 0.4 or less; an acrylonitrile copolymer solution contains the aforementioned acrylonitrile copolymer and an amide solvent.

Abstract: Disclosed are colorants comprising a colored laked complex of (a) a chromogen molecule having at least one (i) carboxylic acid group, (ii) carboxylate group, (iii) sulfonic acid group, (iv) sulfonate group, or (v) combination thereof, and (b) a polymer, said chromogen molecule and said polymer each being complexed to (c) a metal. Also disclosed are phase change inks containing the colorants.

Abstract: A rubber composition is provided for coating a steel wire material having initial adhesion strength and water resistant adhesion strength with respect to a steel wire material at or above conventional levels, the rubber composition being compounded with a compound derived from a natural product. Specifically a rubber composition for coating a steel wire material is compounded with from 0.05 to 10 parts by weight of a salt compound per 100 parts by weight of a diene rubber, the salt compound including a dicarboxylic acid derived from a natural product and an amine of a decarboxylated amino acid derived from a natural product.

Abstract: The invention pertains to a process wherein initiators having a half-life from 0.0001 hour to 0.05 hour at the polymerization temperature are dosed to a polymerization mixture. The dosing of such initiator allows improved control of the polymerization rate and faster polymerization rates, and the process will render a polymer with very low residual initiator levels.

Abstract: A process for producing natural rubber-based acrylonitrile butadiene styrene (ABS) powder. The process comprises introducing a portion of natural rubber, mixing divinylbenzene (DVB) with the portion of natural rubber to produce vulcanized natural rubber, mixing the vulcanized natural rubber with a monomer solution to produce grafted natural rubber, mixing a plurality of grafted polybutadiene rubbers with the grafted natural rubber to produce a latex masterbatch and mixing a coagulant to a portion of the latex masterbatch to produce natural rubber-based ABS powder. By mixing the DVB with the portion of natural rubber, an intermediate step which is required in conventional methods before the polymerization process, can be eliminated. A natural rubber-based acrylonitrile butadiene styrene (ABS) powder produced by the process is also disclosed.

Abstract: The present invention provides a process for the production of functionalized carbon nanotubes. The inventive process for the production of functionalized carbon nanotubes involves reacting carboxylic acid moieties of oxidized carbon nanotubes with vapors of a compound containing carboxylic acid reactive groups to produce functionalized carbon nanotubes. The present invention also provides a composition made from a plastic resin and functionalized carbon nanotubes produced by reacting carboxylic acid moieties of oxidized carbon nanotubes with a vapor containing carboxylic acid reactive groups to produce functionalized carbon nanotubes. The inventive process is useful with single-walled carbon nanotubes, double-walled carbon nanotubes and multi-walled carbon nanotubes.

Abstract: An additive mixture containing the components (A), (B) and optionally (C), wherein component (A) is at least one compound of the formula (I) wherein p is zero or 1; m and n are independently of one another an integer from zero to 3; and the radicals R are independently of one another C1-C8alkyl, C1-C8alkoxy, hydroxy, halogen, C1-C8alkylthio, C1-C8alkylsulfoxy or 2 radicals R form together with 2 adjacent carbon atoms of the unsaturated parent ring a 5- to 7-membered carbocyclic or heterocyclic ring; component (B) is at least one compound of the formula (II) wherein x and y are independently of one another an integer from 2 to 10; the radicals A1, A2 and A3 are independently of one another C1-C10alkyl, C5-C12cycloalkyl unsubstituted or substituted by 1 to 3 C1-C10alkyl; phenyl unsubstituted or substituted by 1 to 3 C1-C10alkyl; or C7-C12phenylalkyl, and the radicals A2 and A3 are additionally hydrogen; with the proviso that at least one of the radicals A1 and A2 is branched C3-C10alkyl, C5-C12cycloal

Abstract: The present invention is directed to a golf ball having at least one layer which includes a polymer composition containing at least 50 wt % of an acid polymer and at least 0.5 wt % of a plasticizer selected from the group consisting of alkylamines, alkanol amines, and fatty acid amines, wherein the weight percentages are based on the total polymeric weight of the polymer composition. At least 70% of the acid groups of the acid polymer are neutralized by a cation source or a metal salt thereof.

Abstract: Golf balls containing at least one layer made from a rubber composition comprising a benzenetrisamide nucleating agent are provided. The rubber composition preferably contains a free-radical initiator agent, cross-linking agent, and fillers along with the base rubber and nucleating agent. Golf balls of various constructions may be made including two-piece, three-piece, and four-piece balls. The composition is used preferably to form a golf ball core having improved resiliency, durability, toughness, and impact strength.

Abstract: A composition comprising a clear thermoplastic blend comprising: (a) a polycarbonate component; and (b) a polyester component comprising (i) a polyester based substantially on 1,4 cyclohexane dimethanol and terephthalic acid monomer units, (ii) copolymers polyester based substantially on 1,4 cyclohexane dimethanol and terephthalic acid monomer units and modified with up to 25 mol % of copolymerizable acid and/or diol monomers, and (iii) combinations thereof. The polycarbonate component and the polyester component are present in sufficient proportions to form a molding composition capable of being molded into an article that exhibits transparency and structural integrity after the article is exposed to a caustic aqueous environment for at least 70 hours. The invention also relates to articles made from the composition, methods for making the compositions, and methods for using articles.

Abstract: The invention is directed to a masterbatch comprising a nucleating organic compound which, on changing to the solid phase, forms crystals and which in its melt phase is soluble in the molten polyethylene and polyethylene. The ingredients of this masterbatch are applied as a nucleating agent masterbatch during the production of polyethylene foam.

Abstract: Disclosed are an acrylonitrile copolymer excellent in thermal stability as a solution (spinning dope) when dissolved in an amide solvent and capable of forming dense polyacrylonitrile fiber suitable for production of carbon fiber, an acrylonitrile copolymer solution in which the acrylonitrile copolymer is dissolved in an amide solvent, and a method for producing polyacrylonitrile precursor fiber for carbon fiber by use of the acrylonitrile copolymer solution. Specifically, an acrylonitrile copolymer contains a sulfonate group derived from a polymerization initiator in an amount of 1.0×10?5 equivalent/g or more, and the value (equivalent ratio) of (the content of a sulfate group derived from the polymerization initiator/the total content of the sulfonate group and the sulfate group) is 0.4 or less; an acrylonitrile copolymer solution contains the aforementioned acrylonitrile copolymer and an amide solvent.

Abstract: The use of a methacrylic resin composition for hot plate welding, wherein the methacrylic resin composition contains a polymer obtained by polymerization of monomers consisting mainly of methyl methacrylate, and at least one additive selected from the group consisting of fatty acid amides, fatty acid alkyl esters, fatty acid glycerides and aliphatic alcohols.

Abstract: A composition containing a) a natural or synthetic polymer and b) one or more compounds of the formula (I), (II) or (III) wherein R1, R2 and R3 or Y1, Y2 and Y3 or Z1, Z2 and Z3 are e.g. branched C3-C20alkyl.

Abstract: Disclosed are a composition for controlling the crystallization rate of a polyolefin-based resin, the composition comprising (A) an amide-based compound which is a substituted or unsubstituted cyclohexylamide of 1,2,3-propanetricarboxylic acid or 1,2,3,4-butanetetracarboxylic acid and (B) a fatty acid metal salt, wherein the component (A):component (B) weight ratio is from 100:0 to 30:70; a method for controlling the crystallization rate of a polyolefin-based resin, comprising incorporating the composition into the polyolefin-based resin to obtain a polyolefin-based resin composition and molding the resin composition; molded products obtained by the method; and the like.

Abstract: A process for improving the flow properties of a melt containing a thermoplastic polymer, which comprises incorporating 0.005% to 0.5% by weight, relative to the weight of the thermoplastic polymer, of one or more additives selected from the group consisting of organic and inorganic compounds with needle-like morphology in their solid state into said thermoplastic polymer prior to or during melt processing.

Abstract: The invention relates to a bituminous binder composition comprising: (a) 60-99.75 wt. % bitumen; (b) 0.05-5.0 wt. % of an elastomer; (c) 0.1-30.0 wt. % of a mono-alkyl ester of a vegetate e oil or an animal oil; and (d) 0.1-5.0 of an amide additive; based on the total weight of the bituminous binder composition, and a process for preparing the bituminous binder composition. The inventions further relates to the use of the bituminous binder composition in surface dressing, in particular road construction, road renovation, joint filling and sealing purposes.

Abstract: Disclosed herein are aromatic amide derivatives of the formulae: wherein X1 and X2 are independently selected from the group consisting of —OH, —OR, —OM, —NH2, and —NHR; M is a metal; and R, R1, and R2 are independently selected hydrocarbyl groups.

Abstract: A coating composition suitable for protecting a substrate from abrasion. The coating composition comprises chlorosulfonated polyolefin, a monomer mixture and catalyst. The monomer mixture is made from (meth)acrylate monomers. The coating composition also acts as a sound deadener, an anti-slip coating, and an anti-wear coating. It can be applied to a variety of substrates especially on a truck bed as a bedliner.

Abstract: There is provided a packaging material for a photographic light-sensitive material, the packaging material being formed from a resin composition that contains a compound having an unsaturated double bond or that contains a poly(conjugated diene) component, a metal ion that can promote a catalytic oxidation reaction of the unsaturated double bond and the poly(conjugated diene), and a chelating agent that can coordinate the metal ion in an amount sufficient to suppress the catalytic oxidation reaction. There is also provided a photographic light-sensitive material package formed by housing the photographic light-sensitive material in the packaging material for the photographic light-sensitive material.

Abstract: A polyoxymethylene resin composition, which comprises (A) 100 parts by weight of polyoxymethylene resin, (B) 0.01 to 5 parts by weight of at least one polymer selected from homopolymers of N-vinylcarboxylic acid amides and copolymers of N-vinylcarboxylic acid amides and other vinyl monomers, and (C) 0.01 to 5 parts by weight of at least one compound selected from the group consisting of polyalkylene glycol and its derivatives, fatty acid amides, esters of alcohols and fatty acids, and esters of alcohols and dicarboxylic acids. Such a polyoxymethylene resin composition has a small amount of released formaldehyde gas during production and molding and suppressed scorching generation and is also distinguished in the water resistance and repeated impact resistance of the resulting moldings.

Abstract: The instant invention relates to a thermoplastic polymer composition useful in greenhouse films to enhance plant growth or in general bio-mass production. Further aspects of the invention are a process for enhancing plant growth in greenhouses by incorporating a photoactive additive together with light stabilizers into the greenhouse film and the use of the condensation product of dialkylamino benzaldehyde and barbituric acid together with light stabilizers as a plant growth enhancing additive in polymeric greenhouse films.

Abstract: To provide a method for producing a blend composition of an acrylic type polymer having an excellent mechanical characteristic as well as a low temperature characteristic, and to provide a blend composition of an acrylic type polymer, and also to provide a blend composition of an acrylic type polymer for sealing materials having an excellent abrasion resistance which is important for sealing materials.

Abstract: One aspect of the invention is directed to a rubber composition which includes at least one sulfur-vulcanizable elastomer containing olefinic unsaturation, a first processing aid, and a second processing aid of the formula: wherein each of R1 and R2 independently is selected from the group consisting of alkyls having from 12 to 24 carbon atoms, and alkenyls having from 12 to 24 carbon atoms. The elastomer is present in an amount of 100 parts by weight. Also, the first processing aid may be present in an amount of 0 to 20 phr, and the second processing aid may be present in an amount of 0.2 to 20 phr. Another aspect of the invention is directed to a method of making the rubber composition described immediately above, with the method including the step of mixing the elastomer, first processing aid, and second processing aid.

Abstract: Methods of preparing polyolefin-based molded materials with improved adhesive/coating compatibility by incorporating aromatic carboxylic acid amides and transition metal compounds in the polyolefin-based material prior to molding are described. Methods of producing coated or bonded polyolefin-based, molded materials are also described.

Abstract: The present invention provides a resin of the formula: 1

Abstract: The present invention relates to aqueous formulations comprising: i. at least one hydrophilic particulate polymer P1, as an aqueous dispersion, composed essentially of monoethylenically unsaturated monomers having a water-solubility in the range from 10 to 100 g/l (at 25° C. and 1 bar), and ii. at least one hydrophobic particulate polymer P2, as an aqueous dispersion, composed essentially of ethylenically unsaturated monomers having a water-solubility below 10 g/l (at 25° C. and 1 bar), the glass transition temperature Tg1 of the polymer P1 being less than 10 K different from the glass transition temperature Tg2 of the polymer P2.

Abstract: A polyacrylamide gel utilising a buffer system comprising Tris(hydroxymethyl)aminomethane at the concentration range 0.15 to 0.25 M titrated with hydrochloric acid to a pH between 6.5 and 7.5. The gel is substantially stable to polyacrylamide hydrolysis during storage for at extended periods and has an acceptable shelf-life of at least 6 months after storage at about 4° C.

Abstract: A film for adhering to a molding compound paste composite during its manufacture, said film being formed from a blend of a film forming polyamide resin and at least one release agent material selected from the group consisting of N, N′ ethylene bis amides of the formula: R1—CO—NH—CH2—CH2—NH—CO—R2, wherein R1 is an aliphatic hydrocarbon chain of about 14 to about 42 carbon atoms, and R2 is a hydrogen atom or an aliphatic hydrocarbon chain of about 14 to about 42 carbon atoms; calcium stearate; a mixture of calcium stearate and silicone; a mixture of calcium stearate and polytetraflurorethylene; polypropylene; modified polypropylene; waxes; fluoroelastomers; silicones; molybdenum disulphide; boron nitride; N, N′ ethylene bis stearamide and polytetrafluoroethylene; N, N′ ethylene bis stearamide and silicone; N, N′ ethylene bis stearamide and graphite; N, N′ ethylene bis stearamide and polypropylene; N, N′ ethylene bis stearamide and

Abstract: This invention provides a composition for double glazing use which satiskfies the requirement of both low moisture permeability and weather-resistant adhesiveness and also has rapid hardenability by addition type curing, can be produced by a line process and is able to be used as a one-pack sealant having excellent shelf stability and mechanical properties, and the composition for double glazing use of this invention comprises (A) a hydrocarbon polymer having at least one alkenyl group in its molecule and a molecular weight of 500 to 300,000, (B) a curing agent having at least two hydrosilyl groups in its molecule, (C) a hydrosilylation catalyst and (D) a tackifier as essential components. When the composition for double glazing use requires one-pack adhesive property, shelf stability improving agent (E) is further used in addition to the components (A) to (D). An isobutylene polymer is desirable as the component (A), and a polyorgano hydrogen siloxane as the component (B).

Abstract: Benzotriazole UV absorbers which are substituted at the 5-position of the benzo ring by an electron withdrawing group exhibit enhanced durability and very low loss rates when incorporated into automotive coatings.

Abstract: There is provided a highly water-absorptive polymer composition comprising:(A) 100 parts by weight of a highly water-absorptive polymer having a crosslinked structure, comprising as its constituent a carboxyl group and/or a carboxylate group; and(B) 0.05 to 10 parts by weight of an additive selected from the group consisting of an oxalic acid (salt) compound, a sulfate of a metal selected from titanium, zirconium and vanadium, and a crystalline or noncrystalline, high-purity particulate titania having a mean particle diameter of 1 .mu.m or less, a specific surface area of 10 m.sup.2 /g or more as determined by the Brunauer-Emmett-Teller method, and, when crystalline, a crystal structure of a mixed type of rutile and anatase.

Abstract: A releasable aqueous coating composition used for temporarily protecting a finished coating film coated on an automobile body. It contains (A) an aqueous acrylic resin obtained by copolymerizing a monomer mixture of a (meth)acrylic ester monomer as an essential component and other polymerizable unsaturated monomer, except for (meth)acrylonitrile, as an optional component, and having a glass transition temperature of 5.degree. to 30.degree. C. and a weight average molecular weight of 20,000 or more, (B) an ultraviolet light absorber, and (C) a water repellent material. A method of temporarily protecting the finished coating film on the automobile body by coating the releasable aqueous coating composition onto a surface of a finished cured coating film coated onto the automobile body.

Abstract: Thermoplastic molding compositions containingA) ABS-type resin,B) aromatic polycarbonate resins,C) a compound bearing several carboxyl groups or mixtures thereof and optionallyD) further polymer resins,characterized in that an ABS resin with at least one basically acting additive is used as component A, component C is selected from compounds having a molecular weight of from 150 to 260 having at least two carboxyl groups (--COOH) in the molecule, and the weight ratio of basically acting additive in A: carboxyl groups in C is from 5:1 to 1:1.

Abstract: Incorporation of at least one lubricant and an ethylene-based polymer of the formula E/X/Y wherein E is ethylene, X is methyl acrylate, butyl acrylate, or ethyl acrylate, and Y is glycidyl methacrylate, glycidyl acrylate, or glycidyl vinyl ether into polyacetal compositions results in compositions having good wear resistance and good melt processing thermal stability. The compositions are useful, for example, when molded into parts to be used in sliding applications, such as gears, cams, and conveyor chains.

Abstract: A polypropylene resin containing an .alpha.-olefinic copolymer rubber and an inorganic filler is stabilized by incorporating therein the following 6 components:(A) a hindered phenolic compound having a molecular weight of not less than 500,(B) a high-molecular hindered piperidine compound such as poly[{6-(1,1,3,3-tetramethylbutyl)amino-1,3,5-triazine-2,4-diyl}{(2,2,6,6- tetramethyl-4-piperidyl)-imino}hexamethylene{(2,2,6,6-tetramethyl-4-piperid yl)imino}],(C) a low-molecular hindered piperidine compound such as 2-methyl-2-(2,2,6,6-tetramethyl-4-piperidyl)amino-N-(2,2,6,6-tetramethyl-4 -piperidyl)propionamide,(D) a benzoate compound such as 2,4-di-t-butylphenyl 3,5-di-t-butyl-4-hydroxybenzoate,(E) a phosphorous compound such as bis(2,4-di-t-butylphenyl) pentaerythritol diphosphite, and(F) an amide compound such as ethylene-bisstearylamide. This composition may also contain a sulfur compound such as dialkyl thiodipropionate and pentaerythritol tetrakis(3-alkylthiopropionate).

Abstract: Thermoplastic composition based on a crystalline polyester and a modified vinyl aromatic polymer. It comprises:from 50 to 97% by weight of at least one polymer phase (A) consisting of at least one terpolymer produced by grafting (a) at least one vinyl aromatic monomer and (b) at least one unsaturated nitrile onto (c) at least one rubber, the terpolymer being dispersed in a matrix of a copolymer comprising units derived from (d) at least one unsaturated nitrile and (e) at least one vinyl aromatic monomer, the overall composition of the polymer phase (A) being such that it contains from 17 to 35 parts of unsaturated nitrile, from 10 to 60 parts of rubber, and from 10 to 60 parts of vinyl aromatic monomer per 100 parts by weight of the polymer phase, andfrom 3 to 50% by weight of at least one high molecular weight polybutylene terephthalate (B).

Abstract: A thermoplastic resin composition having improved heat stability which comprises a thermoplastic resin which contains at least 5% by weight of an .alpha.-alkyl-substituted aromatic copolymer comprising .alpha.-alkyl-substituted aromatic vinyl compound and at least one other comonomer copolymerizable therewith, wherein the composition contains a metal-deactivating agent which has a molecular weight of not more than 2,000 and at least one group of the formula: ##STR1## or an organometallic colorant containing free metal in an amount of not more than 2,000 ppm, from which a molded article having no or less silver streaks can be produced.

Abstract: A method for improving the low temperature impact strength of a thermoplastic polyblend of PETG and SAN which method comprises incorporating therein an effective amount of a dispersant selected from the group consisting of mono- and di-carboxylic acids containing 6 to 36 carbon atoms; alkali and alkaline-earth metal salts and amides of such acids; and aliphatic alcohols containing 6 to 36 carbon atoms.

Abstract: A filler-containing polyolefin resin composition comprising a resin composition composed of a polyolefin resin and an inorganic filler exhibits an excellent thermal stability despite the presence of the inorganic filler by adding thereto a particular phenolic antioxidant, an amide or monoglyceride compound of a higher fatty acid and a particular metal inactivating agent.

Abstract: Disclosed is a styrene-based resin composition which comprises (a) 100 parts by weight of styrene-based polymer having a high degree of syndiotactic configuration, (b) 0.01 to 15 parts by weight of at least one nucleating agent selected from an organophosphorus compound and a metal salt of an organic acid, and (c) 0.01 to 15 parts by weight of at least one component selected from a polyoxyalkylene compound, a fatty acid and a derivative thereof.The composition can produce various molding products with excellent mold-releasing property, surface gloss, bending strength, bending modulus and heat resistance.

Abstract: An inorganic filler-containing polyolefin composition which comprises100 parts by weight of a polyolefin,1-100 parts by weight of an inorganic filler.0.01-1.0 part by weight of a phenolic antioxidant represented by the general formula (I) shown below, andat least one compound selected from the group consisting of the compounds represented by the general formulas (II) to (IV) shown below, and optionally 0.01-1.0 part by weight of a sulfur antioxidant and/or 0.01-2.0 parts by weight of a light stabilizer. ##STR1## wherein R.sub.1 represents an alkyl group of 1-3 carbon atoms,R.sub.2 --CO--NH--(CH.sub.2).sub.n --HN--CO--R.sub.2 (II)wherein R.sub.2 represents an alkyl group or an alkenyl group of 5-21 carbon atoms, and n is an integer of 1 to 6.R.sub.3 --COHN.sub.2 (III)wherein R.sub.3 represents an alkyl group or an alkenyl group of 5-21 carbon atoms. ##STR2## wherein R.sub.

Abstract: Rubber compositions which, in addition to conventional ingredients of an ethylene-propylene copolymeric rubber, an organopolysiloxane having ethylenically unsaturated linkages, a vulcanizing agent and finely divided reinforcing silica filler, contain an N,N'-alkylenediamine bis-stearoamide eliminate the problem of surface staining of the metal molds repeatedly used to mold the rubber composition caused by the aging retarder therein and thus enough aging retarder can be included therein so that rubber vulcinizates having excellent heat resistance can be prepared from the rubber compositions without creating a surface stain problem.

Abstract: A thixotropic hot-melt adhesive contains reactive silane groups and is still viscous and plastically moldable after cooling. It contains a mixture ofat least one thermoplastic material, andat least one thixotropic agent,wherein silane groups are contained either in the thermoplastic material itself or in at least one added silane-based binder.

Abstract: Novel aqueous adhesive and coating compositions composed of (1) an aqueous emulsion (latex) or dispersion of a polymer or interpolymer of one or more vinyl monomers such as an emulsion of a copolymer of vinyl acetate and butyl acrylate and (2) an aqueous emulsion or dispersion of a polyisocyanate which has at least partially reacted with an alcohol having the formula ROH wherein R is a hydrocarbon radical having .[.at least one carbon atom.]. .Iadd.from six to 30 carbon atoms .Iaddend.and wherein the dispersion or emulsion (2) is stabilized with a combined surfactant and alcohol having the formula R' wherein R' is a hydrocarbon radical having at least one carbon atom are described.