Abstract: The invention relates to a composition comprising: (A) a propylene-based polymer which is a propylene homopolymer or a propylene copolymer consisting of at least 90 wt % of propylene monomer units and at most 10 wt % of ethylene monomer units and/or an ?-olefin monomer units having 4 to 10 carbon atoms and (B) a copolymer of ethylene and ?-olefin comonomer having 4 to 10 carbon atoms, wherein the elastomer has a density of 0.850 to 0.910 g/cm3 and a melt flow rate of 15 to 50 dg/min measured in accordance with IS01 133 using a 2.16 kg weight and at a temperature of 190° C., wherein the amount of (A) the propylene-based polymer is 60 to 99 wt % and the amount of (B) the copolymer is 1 to 40 wt %, with respect to the total composition.

Abstract: A process forms an implantable product including poly(glycerol sebacate) urethane (PGSU) loaded with an active pharmaceutical ingredient (API). The process includes homogeneously mixing a flowable poly(glycerol sebacate) (PGS) resin with the API and a catalyst to form a resin blend. The process also includes homogeneously combining the resin blend with an isocyanate to form a reaction mixture and injecting the reaction mixture to form the PGSU loaded with the API. An implantable product includes a PGSU loaded with an API. In some embodiments, the implantable product includes at least 40% w/w of the API, and the implantable product releases the API by surface degradation of the PGSU at a predetermined release rate for at least three months under physiological conditions. In some embodiments, the PGSU is formed from a PGS reacted with an isocyanate at an isocyanate-to-hydroxyl stoichiometric (crosslinking) ratio in the range of 1:0.25 to 1:1.25.

Abstract: A heterophasic propylene polymerization material containing a propylene homopolymer component or a specific propylene copolymer component, and a specific ethylene-?-olefin copolymer component, in which (i) the amount of the xylene-soluble component is 40% by weight or more, (ii) the limiting viscosity [?]C X I S of the xylene-insoluble component is 1.50 dL/g or more, (iii) the ratio of the limiting viscosity [?]C X S of the xylene-soluble component to the limiting viscosity [?]C X I S of the xylene-insoluble component is 1.5 or less, and (iv) the content of monomer units derived from ethylene and ?-olefins having 4 to 12 carbon atoms in the xylene-insoluble component is 6% by weight or more.

Abstract: An ethylene bis-12-hydroxystearamide grafted glycidyl citrate (EBH-g-ECA) and a preparation method thereof are provided; the EBH-g-ECA can be used as a multifunctional auxiliary agent in a polymer material, and particularly has a chain extension and a crystal nucleation effect in a polyester polymer material. A heat-resistant polylactic acid continuously-extruded foamed material containing EBH-g-ECA is further provided. The continuous foaming technology can be realized by using the heat-resistant polylactic acid foamed material, and the prepared foamed product has a high heat resistance, a uniform appearance, a low density, and complete biodegradation. A polylactic acid foamed material preparation method for a heat-resistant is provided, which is easy to be industrialized and has a great significance for realizing the large-scale replacement of petroleum-based plastic disposable foamed products such as PP and PS.

Abstract: A polyolefin composition comprising a heterophasic propylene copolymer and a polar modified ?-polyolefin.

Abstract: The present invention relates to compositions (compounds) which can be used as seal material in vessel caps, even under pasteurization conditions and possibly sterilization conditions. More specifically, the invention relates to such compositions that are suitable for vessel caps that can be unscrewed, such as lug screw caps and in particular Press-on/Twist-Off® caps, and that result in a reduced migration of undesirable substances.

Abstract: A highly saturated nitrile rubber composition containing a carboxyl group-containing highly saturated nitrile rubber (A1) which contains ?,?-ethylenically unsaturated nitrile monomer units 15 to 60 wt % and ?,?-ethylenically unsaturated dicarboxylic acid monoester monomer units 1 to 60 wt % and has an iodine value of 120 or less, a highly saturated nitrile rubber (A2) which contains ?,?-ethylenically unsaturated nitrile monomer units 15 to 60 wt %, has a content of the ?,?-ethylenically unsaturated dicarboxylic acid monoester monomer units of 0.9 wt % or less, and has an iodine value of 120 or less, and a polyamide resin (B), a content ratio of the carboxyl group-containing highly saturated nitrile rubber (A1) and the highly saturated nitrile rubber (A2) being a weight ratio of “carboxyl group-containing highly saturated nitrile rubber (A1):highly saturated nitrile rubber (A2)” of 2:98 to 98:2, is provided.

Abstract: A flexible fuel cell power system comprising one or more fuel cell cartridges (which contain fuel cell modules) connected to a fuel cell system is provided. The components of the flexible fuel cell power system may be placed on a shared backbone with flexible joints, and may be made of flexible materials so that the entire system can be worn by a human being.

Abstract: In order to provide a rubber composition which is improved in dispersibility of silica in rubber compositions and can be improved as well in heat build-up and processability without causing increasing a viscosity of unvulcanized rubber and retarding a vulcanization rate, and a tire prepared by using the same, the rubber composition is endowed with a constitution in which at least one rubber component selected from natural rubber and/or diene base synthetic rubbers is compounded with a white filler and at least one of monoalkanolamides represented by the following Formula (I): [in Formula (I) described above, R1 represents an alkyl group or an alkenyl group having 1 to 13 carbon atoms, and the alkyl group and alkenyl group may be any of a linear type, a branched type and a cyclic type; and R2 represents a hydroxyalkyl group or a hydroxyalkyl group having an oxyalkylene unit].

Abstract: A polymer comprises reaction product of (a) one or more diacid, diester thereof, glycolide, and (b) one or more polyol, wherein component (a) comprises glycolide or combinations thereof, and component (b) comprises one or more polyol comprising a mixture of 1,3-cyclohexanedimethanol and 1,4-cyclohexanedimethanol, or 2,2,4,4-tetramethyl-1,3-cyclobutanediol, or combinations thereof.

Abstract: A polymer comprising reaction product of (a) one or more diacid, diester thereof, glycolide, and (b) one or more polyol, wherein component (a) comprises (i) 2,6-naphthalene dicarboxylic acid, C1 to C10 alkyl diester thereof, glycolic acid, glycolide or combinations thereof, and (ii) 2,5-furan dicarboxylic acid, one or more C1 to C10 alkyl diester thereof, or combinations thereof, and component (b) comprises isosorbide.

Abstract: The present invention provides a rubber composition that can enhance the fuel economy, wet-grip performance, abrasion resistance, and processability in a balanced manner, and also provides a pneumatic tire using this rubber composition. The present invention relates to a rubber composition that contains a rubber component, silica, and a compound represented by formula (1) below, wherein the rubber component contains, based on 100% by mass of the rubber component, not less than 5% by mass of a conjugated diene polymer containing a constituent unit based on a conjugated diene and a constituent unit represented by formula (I) below, at least one terminal of the polymer being modified with a specific compound; and an amount of the silica is 5 to 150 parts by mass per 100 parts by mass of the rubber component.

Abstract: Disclosed are polypropylene articles with improved optical properties and/or an increased temperature of crystallization comprising a polypropylene resin and uniformly dispersed therein from about 1 ppm to about 10 ppm of one or more polycyclic organic pigments selected from blue, green, magenta, red, yellow, orange and violet polycyclic organic pigments and from about 50 ppm to about 250 ppm of one or more aromatic trisamide nucleating agents, where the ppm levels are by weight based on the weight of the polypropylene resin. The polypropylene is for example polypropylene homopolymer. The articles exhibit reduced haze, increased temperature of crystallization and excellent clarity.

Abstract: The purpose of the present invention is to propose a composition of slip additive agents for use in thermoplastic resins, preferably polyolefins, and consequently the presence of this composition on at least one of the layers of mono-extruded or coextruded, laminated or non-laminated films. More particularly, the invention comprehends a composition of additives which comprises at least one primary amide of the generic formula R—CO—NH2 and a secondary amide of the bis amide type of the generic formula R?—CO—NH—CH2—CH2—NH—CO—R?. Films comprising this composition stand out by achieving Coefficient of Friction (CoF) values lower than 0.35 and particularly by their ability to maintain good control over these values for use in the automated packaging industry.

Abstract: The present invention is in the field of polymer interlayers used in multiple layer glass panels, and specifically the present invention is in the field of antiblocking agents for polymer interlayers and methods of effectively incorporating such agents into interlayers.

Abstract: The present invention provides compositions that enable excellent early hardness development in coating applications, the compositions comprising a blend of one or more acrylic emulsion copolymer, pA, having a Tg of 20° C. or higher, and one or more acrylic emulsion copolymer, pB, having a Tg at least 15° C. lower than that of pA, together with one or more additive chosen from a coalescent having a normal boiling point no greater than 300° C., a naturally derived plasticizer, and mixtures thereof. The compositions may be ambient curable.

Abstract: Processes for making water-absorbent cross-linked polymers, such as polyacrylic acids/polyacrylates, using supercritical medium; and water-absorbent polymers, e.g. particles thereof, obtained by such processes, where such particles may be porous.

Abstract: A hot-melt adhesive composition intended to form a film: a) from 20 to 60% by weight of a styrene block copolymer; b) from 5 to 50% by weight of a particular tackifying resin; c) from 10 to 40% of a Fischer-Tropsch type wax; and d) from 1 to 30% of a polyethylene wax and/or at least one polyolefin polymerized by metallocene catalysis; said composition having a Brookfield viscosity at 180° C. from 3,000 to 70,000 mPa·s, a softening point of 80 at 130° C., and a modulus of elasticity at 60° C. of 2×105 to 108 Pa. A film for hot-melt adhesive product constituted by a hot-melt adhesive material of such a composition. A ready-to-use hot-melt adhesive product and its production, said hot-melt adhesive product having a coating constituted by such a film.

Abstract: Disclosed is an organic piezoelectric material which has excellent piezoelectric characteristics and excellent handling properties. Also disclosed are an ultrasound transducer using the organic piezoelectric material, an ultrasound probe, and an ultrasound medical diagnostic imaging system. Specifically disclosed is an organic piezoelectric material which contains a base material that is formed from a resin, and a specific compound (1) that has at least one linking group selected from among specific linking groups. The organic piezoelectric material is characterized in that the relation shown below is satisfied when the CLogP values of the specific compound (1) and the base material are respectively represented by CLogP(1) and CLogP(base material). Relation: |CLogP(1)?CLogP(base material)|?3.0.

Abstract: A sealant capable of tightly sealing an electric device at a low temperature and a sealing method of using the sealant are provided. The sealant for sealing a device comprises a copolyamide-series resin powder having a particle diameter of not more than 1 mm. The copolyamide-series resin powder contains at least a fine particle (e.g., a copolyamide-series resin particle having an average particle diameter of 20 to 400 ?m), or may contain the fine particle in combination with a coarse particle (e.g., a copolyamide-series resin particle having an average particle diameter of 450 to 800 ?m). The copolyamide-series resin may be a crystalline resin. The copolyamide-series resin may have a melting point or softening point of 75 to 160° C. The copolyamide-series resin may be, e.g., a binary or ternary copolymer.

Abstract: An elastomer composition includes a base polymer including not less than 50 mass % of ethylene-?-olefin copolymer, and a talc that has a mass ratio of silicon to magnesium (Si/Mg) of 0.9 to 1.8 and is mixed in an amount of 100 to 250 parts by mass per 100 parts by mass of the ethylene-?-olefin copolymer.

Abstract: Disclosed is a phase change ink comprising an ink carrier which comprises: (a) a crystalline trans-cinnamic diester; and (b) an amorphous polyterpene resin.

Abstract: Polyolefin composition comprising a heterophasic propylene copolymer and glass material, wherein said heterophasic propylene copolymer has • a xylene cold soluble fraction in the range of 25 to 50 wt.-%, and • a comonomer content in the range of 10.0 to 15.0 wt.-%, wherein further the xylene cold soluble fraction of the heterophasic propylene copolymer has a comonomer content in the range of 20 to 30 wt.-% and the polyolefin composition has a melt flow rate MFR2 (230° C.) of 2.0 to 15.0 g/10 min.

Abstract: A novel, branched, saturated, primary fatty acid amide is disclosed. Application areas are as a slip and/or antiblocking agent or mold release agent. The branched, saturated, primary fatty acid has a formula R—CO—NH2 where R is a saturated, branched hydrocarbon chain having 11 to 23 carbon atoms, wherein at least 60% by weight of the R—CO—NH2 molecules have monoalkyl branches and less than 25% by weight of the R—CO—NH2 molecules have polyalkyl branches.

Abstract: A method for producing a polylactic acid resin composition, including the following steps (1) and (2): step (1): subjecting an organic crystal nucleating agent to a wet pulverization in the presence of a carboxylic acid ester having a weight-average molecular weight of from 150 to 600 and a viscosity at 23° C. of from 1 to 500 mP·s and/or a phosphoric ester having a weight-average molecular weight of from 150 to 600 and a viscosity at 23° C. of from 1 to 500 mPa·s to give a finely pulverized organic crystal nucleating agent composition; and step (2): melt-kneading a raw material for a polylactic acid resin composition comprising the finely pulverized organic crystal nucleating agent composition obtained in the step (1) and a polylactic acid resin.

Abstract: A rubber compound based on propylene-oxide rubber SKPO, including sulfur, stearic acid, zinc oxide, thiuram disulphide, carbon black P-803. The compound is characterized by replacement of 2-mercaptobenzothiazole (kaptax), as well as fluoroplastic F-4, with dibenzothiazyl disulfide (altax), phenyl-?-naphthylamine (neozone D), dibutoxyethyl adipate, and ultrafine polytetrafluoroethylene (UPTFE). Such replacement of ingredients allows for significant improvement of wear resistance, frost resistance, and relative elongation. Additionally, relatively less UPTFE (compared to fluoroplastic F-4) can be used to achieve similar beneficial results, significantly reducing the cost of manufacturing the material.

Abstract: A rubber compound based on propylene-oxide rubber SKPO, including sulfur, stearic acid, zinc oxide, thiuram disulphide, carbon black P-803. The compound is characterized by replacement of 2-mercaptobenzothiazole (kaptax), as well as fluoroplastic F-4, with dibenzothiazyl disulfide (altax), phenyl-?-naphthylamine (neozone D), dibutoxyethyl adipate, and natural bentonites. Use of a rubber compound with the proposed composition increases the service life of rubber seals during their operation in sealing devices, due to higher frost resistance and a lower residual compressive strain value. Also, the compound can be manufactured by a simpler method compared to modern production technology, eliminating the stage of joint mechanical activation of zeolite and dibutyl phthalate.

Abstract: The present disclosure provides pre-treatment compositions and related methods. As such, a pre-treatment coating for a print medium can include an evaporable solvent, a matrix, and a wax. The matrix can include from 50 wt % to 80 wt % of a fixer and from 5 wt % to 20 wt % of a low Tg latex. The wax can be present at from 5 wt % to 30 wt %. The weight percentages of the matrix and the wax are based on a total amount present in the pre-treatment coating after removal of the solvent.

Abstract: Disclosed is a polypropylene resin composition and interior and exterior materials for vehicles using the same, particularly an olefin-based polypropylene resin composition including: about 50 to 70% by weight of a high crystalline polypropylene; about 10 to 20% by weight of a reactor made thermoplastic polyolefin (RTPO) polypropylene; about 5 to 20% by weight of an inorganic filler; about 10 to 20% by weight of a rubber elastomer; and about 3% by weight or less of a slip agent, based on the total weight of the composition. The composition provides excellent physical properties such as high strength and impact resistance, and thus superior resistance to damage, and shows low gloss characteristics and excellent fluidity.

Abstract: A phase change ink composition including an ink vehicle; an optional colorant; and ethylene vinyl acetate in an amount of from about 0.1 to about 10 percent by weight based on the total weight of the phase change ink composition.

Abstract: The instant invention concerns a composition comprising a base polymer, at least one compound of the formula E-(L-E)x wherein: E is and L is a linking group; and at least one transition metal in a positive oxidation state. The invention also concerns packages containing walls comprising such compositions, methods of forming such packages, and methods of packaging an oxygen-sensitive item within such a package.

Abstract: An aliphatic polyester-based sheet including at least Layer A including an aliphatic polyester, wherein XA of the Layer A is 3-60% and the Layer A contains a crystal nucleating agent and a compound having hydrogen bonding properties with the crystal nucleating agent, and haze of the entire sheet is less than 10%.

Abstract: Highly water repellent coated articles may be made by applying to a substrate a coating having dispersed therein or sprinkled thereon partially or fully fluorinated polymer microparticles. The coating includes a partially fluorinated hexafluoropropylene copolymer binder in a nonfluorinated solvent that dissolves the binder and does not dissolve the microparticles. The coating is heated sufficiently to bond the microparticles to the binder but not so much as to cause the receding water contact angle for the coating to fall below 80°.

Abstract: The present invention relates generally to gels that flow through an orifice. Specifically the invention relates to gels that are dispensed through a trigger spray nozzle or aerosol spray valve. Still more specifically, the invention relates to nonaquious gels containing polymers whose instantaneous viscosity reversibly decreases when the gel experiences shear loads. The invention includes spray gel compositions, methods of making spray gels and methods of dispensing gels whose viscosity exhibits an instantaneous temporary decrease in viscosity when the gel is subjected to shear force as happens when it flows through an orifice, such as a spray nozzle or aerosol valve.

Abstract: Provided is a polylactic acid resin composition obtained by adding a carboxylic acid amide and a carboxylic acid ester each of which has at least one polar group in a molecule to a polylactic acid resin reacted with a (meth)acrylate compound. Also provided is a polylactic acid resin molded article which is a molded article obtained by molding the polylactic acid resin composition, manufactured by setting a mold temperature to a glass transition temperature of a polylactic acid resin plus 20° C. or higher and a melting point thereof minus 20° C. or lower, at the time of injection molding the polylactic acid resin composition. Thus, a resin composition in which a moldability is improved at a temperature at which a polylactic acid resin is crystallized, and a molded article therefrom are provided.

Abstract: Disclosed are colorants comprising a colored laked complex of (a) a chromogen molecule having at least one (i) carboxylic acid group, (ii) carboxylate group, (iii) sulfonic acid group, (iv) sulfonate group, or (v) combination thereof, and (b) a polymer, said chromogen molecule and said polymer each being complexed to (c) a metal. Also disclosed are phase change inks containing the colorants.

Abstract: The invention provides a nonwoven electret web comprising fibers made from a thermoplastic polymer material which comprises a polymer, a first additive (a) and a second additive (b), wherein the first additive (a) comprises a hindered amine and the second additive (b) comprises a metal salt of a carboxylic acid and/or an organic amide derived from a carboxylic acid and an amine. The invention further provides a process for making the nonwoven electret web, a fiber, a process for making the fiber, a mullti-layer sheet, and the use of the nonwoven electret web, the fiber or the multilayered sheet as a filter material or as a dust-removing fabric for cleaning purposes.

Abstract: The invention provides a film comprising at least one layer formed from a composition comprising a propylene-based polymer and a saturated compound, selected from the group consisting of aliphatic amides, hydrocarbon waxes, hydrocarbon oils, fluorinated hydrocarbons, siloxanes, and combinations thereof; and wherein the propylene-based polymer has less than 0.01 mole percent total unsaturations, as determined by 1H NMR.

Abstract: The invention relates to a biaxially oriented, single-layer microporous film which has a shut-off function and is made of propylene homopolymer, propylene block copolymer I and ?-nucleation agent. The melting range of the propylene block copolymer I starts at a temperature ranging from 50 to 120° C. The invention also relates to using the film as a separator in primary or secondary battery.

Abstract: A composition includes specific amounts of a poly(arylene ether), an unfunctionalized hydrogenated triblock copolymer, an unfunctionalized polyolefin, and magnesium dihydroxide. The composition is useful for forming insulation and sheath layers of wire and cable.

Abstract: A polypropylene resin having: (1) a melt flow rate (MFR) of 6 to 100 g/10 minutes, (2) a molecular weight distribution (Mw/Mn), measured by gel permeation chromatography, of 3 to 6, and (3) a 116° C. non-eluted component content (100-W116(%)) of 50% or more and a content of components eluted at 90° C. or less (W90) of 10 to 30%, measured by temperature-rising fractional chromatography (TREF).

Abstract: Disclosed is a vulcanizable rubber composition for use in an air spring, which has excellent low-temperature behavior, and a vulcanized rubber formed product for air springs, which is obtained by vulcanization of the rubber composition. Also disclosed is a vulcanizable rubber composition for use in an air spring, comprising: an epihalohydrin-based copolymer comprising 50 to 70 mol % of a constituent unit derived from ethylene oxide and/or propylene oxide, 20 to 50 mol % of a constituent unit derived from epihalohydrin, and 0 to 15 mol % of a constituent unit derived from allyl glycidyl ether; a vulcanizing agent; a plasticizer; and an acid acceptor, and a rubber formed product for air springs, which is obtained by vulcanization of the composition.

Abstract: An etch-resistant composition is provided. The etch-resistant composition comprises a polymer and a first organic solvent. The polymer is prepared by copolymerizing a polymerization unit comprising styrene-based monomer(s) and acrylate-based monomer(s), and has a weight average molecular weight of at least about 35,000. Based on the total weight of the etch-resistant composition, the amount of the polymer is about 20.0 to about 60.0 wt % and the amount of the solvent is about 40.0 to about 80.0 wt %. The etch-resistant composition can be used for preparing a selective emitter of a solar cell.

Abstract: Disclosed herein is a new use for water-stable, oil-modified, nonreactive alkyd resins. It has now been found that such resins can be used as the predominant component of a construction adhesive employed in the manufacture of disposable absorbent articles, for example. As such, the construction adhesive need not employ plasticizers, tackifiers, and conventional polymers required by hot-melt adhesives typically used as construction adhesives. Furthermore, in the manufacture of disposable absorbent articles, the construction adhesive containing a water-stable, oil-modified, nonreactive, alkyd resin does not need to be processed or applied at the high temperatures required of construction adhesives containing reactive alkyds.

Abstract: A polylactic acid resin composition containing 100 parts by weight of a polylactic acid compound (A) having a specific moiety represented by the formula (1): —X1—R1—X2— and having a weight average molecular weight (Mw) of 5,000 to 500,000, 5 to 2,000 parts by weight of a lactic acid resin (B) and 0.1 to 10 parts by weight of at least one kind of a transparent nucleating agent (C) selected from carboxylic acid amides, aliphatic alcohols and aliphatic carboxylic acid esters. In the formula (1), X1, X2 and R1 are defined. The resin composition can exhibit improved heat resistance (high crystallinity) and transparency without impairing the rigidity of the polylactic acid resin. A molded article composed of the resin composition is also provided.

Abstract: Disclosed is a phase change ink comprising a colorant, an initiator, and a phase change ink carrier, said carrier comprising at least one radically curable monomer compound and a compound of the formula wherein R1 and R1? are the same, and wherein R1 and R1? are each an aromatic group; and wherein R2 and R2? and R3 each, independently of the others, are alkylene groups, arylene groups, arylalkylene groups, or alkylarylene groups; or wherein, in embodiments, R1 and R1? can be the same or different, and wherein R1 and R1? each, independently of the other is an alkyl group having a least one ethylenic unsaturation, an arylalkyl group having at least one ethylenic unsaturation, an alkylaryl group having at least one ethylenic unsaturation, or an aromatic group, provided that at least one of R1 and R1? is an aromatic group; and provided that neither of R1 or R1? is a photoinitiator group. Also disclosed herein is a method of printing with the phase change ink.

Abstract: The invention concerns processes for forming a polymer comprising residues of terephthaloyl chloride, paraphenylene diamine, and a salt of formula I wherein A? is a halogen anion, HSO4?, OH?, NO3?, C2H3O2?, or H2PO4?; the process comprising the steps of: a) forming a mixture comprising salt of formula I and paraphenylene diamine in a solvent system comprising an organic solvent and an inorganic salt; and b) adding terephthaloyl chloride to the mixture and allowing the formation of the polymer.

Abstract: The present invention aims to provide a molded product excellent in jet-blackness, weather resistance, mold-processability, boss strength, abrasion resistance and opaqueness, and a resin composition to provide the molded product. The present invention relates to a resin composition comprising: an acrylic resin (A); and a carbon black (B) having a number average particle diameter of 10 to 40 nm.

Abstract: Disclosed are colorants comprising a colored laked complex of (a) a chromogen molecule having at least one (i) carboxylic acid group, (ii) carboxylate group, (iii) sulfonic acid group, (iv) sulfonate group, or (v) combination thereof, and (b) a polymer, said chromogen molecule and said polymer each being complexed to (c) a metal. Also disclosed are phase change inks containing the colorants.

Abstract: The present invention relates to mould-release agent combinations for plastics comprising A. at least one amide wax and B. at least one ester wax and/or C. at least one saponified wax, and also to the use of the mould-release agent combinations for plastics, where the plastic is polyamide, and also to thermoplastic moulding compositions based on polyamide comprising these mould-release agent combinations, and to processes for their production.