Abstract: A sulfonic acid modified polyvinyl alcohol resin comprising up to 15 mol % of a first comonomer comprising sulfonic acid groups. The modified polyvinyl alcohol resin has a hydroxyl unit content of at least 65 mol % and a gel fraction of 3.2 or less. Further, the modified polyvinyl alcohol resin has a disintegration time of 85 seconds or less, as measured in a mixture of 50 vol % water and 50 vol % isopropyl alcohol at 23° C. Additionally, the modified polyvinyl alcohol resin has a hard component present in a component ratio of 10% or greater and 55% or less and having a relaxation time of 0.0091 milliseconds or greater and 0.0104 milliseconds or less, as measured by the pulsed NMR Solid Echo method at 80° C. Also disclosed are methods for producing the sulfonic acid modified polyvinyl alcohol resins, which may advantageously be used in inks, paints, paper coatings, emulsions, or films.

Abstract: A vinyl alcohol-based polymer according to one embodiment of the present invention has an integral value (e) of 0.8 to 20 in the case when a sum of the following integral value (a) to (e) is 100 in a 1H-NMR spectrum. (a) integral value of peak confirmed at 5.70 to 5.96 ppm (b) integral value of peak confirmed at 5.97 to 6.63 ppm (c) integral value of peak confirmed at 6.64 to 7.55 ppm (d) integral value of peak confirmed at 7.56 to 7.81 ppm (e) integral value of peak confirmed at 7.82 to 8.

Abstract: Dispersing agents useful in a suspension polymerization process may be formed based on polyvinyl alcohols and processes discloses herein. The dispersing agent may include, for example: a polyvinyl alcohol having a degree of hydrolysis in the range from 60 to 80 mol %; an absorbance of not less than 0.3 measured at a wavelength of 320 nm with respect to a 0.1 wt % aqueous solution of the polyvinyl alcohol; a block character of remaining ester groups in the range from 0.4 to 0.5; and a cloud point in the range from 35° C. to 50° C. measured with respect to a 1 wt % aqueous solution of the polyvinyl alcohol. Carbonyl groups are theorized to be present along the polymer chain, which may be quantified by 1-H NMR spectra peaks.

Abstract: A method for dyeing hair includes applying a polyvinyl amine copolymer solution to the hair; and applying a hair dye composition to the hair. A hair dye composition includes an aqueous base fluid; a polyvinyl amine copolymer; and an anionic or cationic hair dye. A method of making a hair dye composition includes mixing a polyvinyl amine copolymer and an anionic or cationic hair dye into an aqueous base fluid.

Abstract: The polyvinyl alcohol according to the present invention to be used as a dispersant for suspension polymerization for polyvinyl chloride has a degree of saponification of 60 to 80 mol %, a block character of 0.4 to 0.6, an integration value defined by the following (a) of 0.04 to 0.1 and an integration value defined by the following (b) of 0.01 to 0.2 in a 1H-NMR spectrum, and a 0.1% by mass aqueous solution of the polyvinyl alcohol has a UV absorbance at a wavelength of 320 nm of 0.18 or more and less than 0.3. (a) An integration value from 5.42 to 5.62 ppm of a peak or peaks observed at 5.50 to 5.54 ppm when an integration value from 3.65 to 4.05 ppm of a peak or peaks observed at 3.83 to 3.87 ppm is assumed to be 100. (b) An integration value from 5.76 to 5.98 ppm of a peak or peaks observed at 5.86 to 5.90 ppm when an integration value from 3.65 to 4.05 ppm of a peak or peaks observed at 3.83 to 3.87 ppm is assumed to be 100.

Abstract: A water soluble film useful in unit-dose chemical packaging is disclosed. The film may include: a water soluble saccharide and a polyvinyl alcohol copolymer consisting essentially of: (a) from 80 to 99 mole percent of vinyl alcohol and vinyl ester monomer; and (b) from 1 to 20 mole percent of a pyrrolidone comonomer. Such compositions may be used to provide a water-soluble film simultaneously satisfying requirements in regard to water solubility, biodegradability, and physical properties, even when used for packaging a broad range of harsh, oxidizing chemicals.

Abstract: A water soluble film useful in unit-dose chemical packaging is disclosed. The film may include: a water soluble saccharide and a polyvinyl alcohol copolymer consisting essentially of: (a) from 80 to 99 mole percent of vinyl alcohol and vinyl ester monomer; and (b) from 1 to 20 mole percent of a pyrrolidone comonomer. Such compositions may be used to provide a water-soluble film simultaneously satisfying requirements in regard to water solubility, biodegradability, and physical properties, even when used for packaging of harsh, oxidizing chemicals.

Abstract: Dispersing agents useful in a suspension polymerization process may be formed based on polyvinyl alcohols and processes discloses herein. The dispersing agent may include, for example: a polyvinyl alcohol having a degree of hydrolysis in the range from 60 to 80 mol %; an absorbance of not less than 0.3 measured at a wavelength of 320 nm with respect to a 0.1 wt % aqueous solution of the polyvinyl alcohol; a block character of remaining ester groups in the range from 0.4 to 0.5; and a cloud point in the range from 35° C. to 50° C. measured with respect to a 1 wt % aqueous solution of the polyvinyl alcohol. Carbonyl groups are theorized to be present along the polymer chain, which may be quantified by 1-H NMR spectra peaks.

Abstract: Water soluble films and coatings herein address the problem of water insolubility, color formation, and brittleness upon exposure to oxidizing chemicals, including strong or aggressive oxidizing chemicals. The water soluble films or coatings may include a water soluble polymer and a reactive precursor, such as an alkanolamine or an alkyl alkanolamine. The reactive precursor is water soluble and reactive with oxidizing compounds. Water soluble films or coatings herein may also include a water soluble polymer and an additive mixture including an alkanolamine or an alkyl alkanolamine. The films or coatings, upon exposure to an oxidizing chemical for 8 weeks at 40° C. and ambient humidity, may dissolve fully or achieve 90% dissolution at times of less than 10 minutes. The water soluble films and coatings may advantageously be used with oxidizing chemicals while maintaining water solubility, acceptable color, and flexibility, such as in unit dose packaging, even over extended exposure periods.

Abstract: Water soluble films and coatings herein address the problem of water insolubility, color formation, and brittleness upon exposure to oxidizing chemicals, including strong or aggressive oxidizing chemicals. The water soluble films or coatings may include a water soluble polymer and a reactive precursor, such as an alkanolamine or an alkyl alkanolamine. The reactive precursor is water soluble and reactive with oxidizing compounds. Water soluble films or coatings herein may also include a water soluble polymer and an additive mixture including an alkanolamine or an alkyl alkanolamine. The films or coatings, upon exposure to an oxidizing chemical for 8 weeks at 40° C. and ambient humidity, may dissolve fully or achieve 90% dissolution at times of less than 10 minutes. The water soluble films and coatings may advantageously be used with oxidizing chemicals while maintaining water solubility, acceptable color, and flexibility, such as in unit dose packaging, even over extended exposure periods.

Abstract: A water soluble polyvinyl alcohol copolymer having a diad syndiotacticity of greater than about 60% and less than about 70%. In some embodiments, the water soluble polyvinyl alcohol copolymer is soluble in water at a concentration of at least 1 wt % at a temperature of less than 100° C. In other embodiments, the composition is soluble in water at a concentration of at least 5 wt % at a temperature in the range from about 90° C. to less than 100° C. The high solubility of the high syndiotactic poly vinyl alcohols disclosed herein may provide various advantages as described herein, including ease of processing and decreased use of harmful solvents.

Abstract: Epilatory compositions may be formed from: 40 to 80 wt % water; 5 to 30 wt % of a mixture of at least one polyvinyl alcohol and at least one polyvinyl alcohol copolymer; 1 to 15 wt % plasticizer, where the plasticizer is a linear or branched composition having from 3 to 15 wt % OH; and up to 40 wt % of one or more additives. Pore strip, keratonic plug removal, and other cosmetic applications may be formed from a similar composition, where the plasticizer is a linear, cyclic, or branched composition having greater than 25 wt % OH; and up to 40 wt % of one or more additives. The adhesive properties of the formulations may be tailored, where a low OH content may result in increased adhesion relative to plasticizers having a high OH content.

Abstract: A separator film for an electric battery is provided to substantially eliminate electric contact between an anode component and a cathode component. The film includes a vinyl alcohol copolymer with functional comonomer units such as sulfonic acid functionalized units or salts thereof. The films are desirable for use in battery separators because they exhibit superior resistance to degeneration by oxidation, enabling the manufacture of batteries with improved conductivity, longer discharge times, and longer cycle lives.

Abstract: Various processes and methods are disclosed for incorporating polyvinyl alcohol additives into products. In one embodiment, polyvinyl alcohol particles are dissolved in a solvent without the use of external heat to form a polyvinyl alcohol solution for incorporation into a product. In an alternative embodiment, polyvinyl alcohol particles are directly incorporated into a starch-based adhesive composition. Through the processes of the present disclosure, solid polyvinyl alcohol particles can be delivered directly to a manufacturing facility where the product that incorporates the polyvinyl alcohol additive is being made or formulated. In this manner, since the polyvinyl alcohol particles are not predissolved, the costs associated with shipping and transporting the polyvinyl alcohol product are greatly reduced.

Abstract: A water soluble polyvinyl alcohol copolymer having a diad syndiotacticity of greater than about 60% and less than about 70%. In some embodiments, the water soluble polyvinyl alcohol copolymer is soluble in water at a concentration of at least 1 wt % at a temperature of less than 100° C. In other embodiments, the composition is soluble in water at a concentration of at least 5 wt % at a temperature in the range from about 90° C. to less than 100° C. The high solubility of the high syndiotactic poly vinyl alcohols disclosed herein may provide various advantages as described herein, including ease of processing and decreased use of harmful solvents.

Abstract: A chemical delivery product for delivering an oxidizing chemical into an aqueous system is disclosed. For instance, in one embodiment, a substrate containing an oxidizing chemical, such as trichloroisocyanuric acid, is coated with a water soluble polymer in order to prevent the oxidizing chemical from degrading prior to use and in order to facilitate handling. In accordance with the present disclosure, a neutralizing agent is contacted with the substrate in order to prevent the substrate from degrading the water soluble coating. In an alternative embodiment, a package is formed from a water soluble film forming composition combined with a base.

Abstract: Epilatory compositions may be formed from: 40 to 80 wt % water; 5 to 30 wt % of a mixture of at least one polyvinyl alcohol and at least one polyvinyl alcohol copolymer; 1 to 15 wt % plasticizer, where the plasticizer is a linear or branched composition having from 3 to 15 wt % OH; and up to 40 wt % of one or more additives. Pore strip, keratonic plug removal, and other cosmetic applications may be formed from a similar composition, where the plasticizer is a linear, cyclic, or branched composition having greater than 25 wt % OH; and up to 40 wt % of one or more additives. The adhesive properties of the formulations may be tailored, where a low OH content may result in increased adhesion relative to plasticizers having a high OH content.

Abstract: Various cosmetic compositions are disclosed that may be useful in face masks, epilatories, and pore strips. Also disclosed is a method of designing a cosmetic composition that may include: receiving a request to tailor a cosmetic composition to have a selected property or a selected property set. The method may be used to design and manufacture cosmetic compositions, such as epilatory compositions, face or skin care mask compositions used for cleansing and/or exfoliating the skin, and eyeliners, among others, having advantageous properties.

Abstract: A water-soluble film which comprises a saccharide component and a vinyl alcohol resin component, where the vinyl alcohol resin may include functional comonomer units such as sulfonic acid functional groups or salts thereof. Preferred are polyvinyl alcohol/2-methylacrylamido-2 methyl propane sulfonic acid resins (PVOH/AMPS) which may be purchased commercially with relatively higher or relatively lower characteristic viscosity. The films exhibit superior resistance to aggressive oxidizing chemicals and remain soluble in water after prolonged exposure thereto. The films are particularly useful for unit-dose packaging of chlorine-containing pool chemicals, such as trichloroisocyanuric acid.

Abstract: A water soluble film useful in unit-dose chemical packaging is disclosed. The film may include: a water soluble saccharide and a polyvinyl alcohol copolymer consisting essentially of: (a) from 80 to 99 mole percent of vinyl alcohol and vinyl ester monomer; and (b) from 1 to 20 mole percent of a pyrrolidone comonomer. Such compositions may be used to provide a water-soluble film simultaneously satisfying requirements in regard to water solubility, biodegradability, and physical properties, even when used for packaging of harsh, oxidizing chemicals.