Abstract: Glass fibers formed from the inventive composition may be used in applications that require high stiffness and have a specific modulus between 34 and 40 MJ/kg. Such applications include woven fabrics for use in forming wind turbine blades and aerospace structures.
Abstract: A vehicle interior material made of a rose-gold-colored copper alloy may include 0.07 to 0.21 wt % of aluminum (Al), 0.06 to 0.19 wt % of magnesium (Mg), 0.17 to 0.52 wt % of zinc (Zn), and a balance of copper (Cu) and unavoidable impurities, wherein the sum of the aluminum (Al), the magnesium (Mg), and the zinc (Zn) is 0.5 to 1.5 at %.
Type:
Grant
Filed:
November 12, 2019
Date of Patent:
December 13, 2022
Assignees:
Hyundai Motor Company, Kia Motors Corporation, Industry-Academia Cooperation Group of Sejong University
Inventors:
Hoo-Dam Lee, Chang-Yeol Yoo, Jong-Kook Lee, Sung-Ho Yoon, Ye-Lim Kim, Yeon-Beom Jeong, Ki-Buem Kim
Abstract: The present invention relates to the use of N,N?,N?-substituted hexahydro-1,3,5-triazine in the anionic polymerization of conjugated diene monomer and vinylaromatic monomer. Use of this polar additive produces copolymers having both high vinylaromatic and low vinyl contents, while the blockiness of the vinylaromatic unit can be tailored.
Abstract: A method for manufacturing of steel tube from a long steel strip, including providing a length of steel strip material to the process, forming a tube of the steel strip material, welding the formed tube in longitudinal direction, giving the tube a heat treatment wherein the mentioned steps are performed in one continuous in-line manufacturing line and the heat treatment includes a heating regime such that in successive cross-sections of the tube a microstructure is achieved which holds at least 50 vol % austenite and a cooling trajectory to re-introduce ferrite, and/or bainite in desired volume fractions.
Type:
Grant
Filed:
July 13, 2017
Date of Patent:
December 6, 2022
Assignee:
TATA STEEL NEDERLAND TUBES BV
Inventors:
Steven Celotto, Gerardus Jacobus Paulussen, Arjen Kamp, Robertus Flipsen
Abstract: Provided is a method of predicting fouling during a process of preparing polyolefin. According to the present invention, occurrence of fouling may be predicted by calculating R value according to the following Equation 1 in real-time with high reliability during a copolymerization process of preparing polyolefin: R (ratio of unreacted alpha-olefin comonomer to produced polyolefin polymer) =amount of unreacted alpha-olefin comonomer (unit: kg/hr) / amount of produced polyolefin polymer (unit: kg/hr) ??[Equation 1] Therefore, productivity of the polyolefin preparation process may be further increased.
Abstract: There is provided a polyamide-imide resin film including a polyamide-imide block copolymer having a specific structure and having a predetermined retardation.
Type:
Grant
Filed:
December 7, 2018
Date of Patent:
December 6, 2022
Assignee:
LG CHEM, LTD.
Inventors:
Yunah Yu, Hyungsam Choi, Byungguk Kim, Youngsik Eom, Sungyeol Choi, Sanggon Kim, Duk Hun Jang
Abstract: Disclosed are a wire rod and a manufacturing method therefor, the wire rod comprising, by weight %: 0.05-0.20% of C, 0.2% or less of Si, 5.0-6.0% of Mn, 0.020% or less of P, 0.020% or less of S, 0.010-0.050% of Al, 0.010-0.020% of N, and a balance of Fe and inevitable impurities and having a microcrystalline structure composed of two phases of austenite and ferrite, wherein the austenite has an area fraction of 15-25%.
Abstract: Shelf-stable, rapid crosslinking, “all-in-one” pastes useful as “inks” in additive manufacturing are provided. These pastes exhibit desirable rheological flow properties and crosslinking upon exposure to UV light. The pastes are based on vinylsilyl-functionalized, completely amorphous, linear terpolysiloxanes containing predominantly dimethylsiloxy-repeat units with small amounts of diphenylsiloxy-, methylphenylsiloxy-, diethylsiloxy-, and/or methyltrifluoroalkylsiloxy-crystallization disruptors. The base polymers are preferably compounded with a trimethylsilylated-hydrophobic silica filler, thixotropic flow agent, hydrosilyl-functionalized oligomeric crosslinker, and a catalytic system comprising platinum(II) acetylacetonate or trimethyl(methylcyclopentadienyl)-platinum(IV), and diethyl azodicarboxylate.
Type:
Grant
Filed:
May 11, 2021
Date of Patent:
November 29, 2022
Assignee:
Honeywell Federal Manufacturing & Technologies, LLC
Inventors:
Jamie Michael Messman, Steven Michael Patterson, Petar Dvornic, Alisa Zlatanic, James Beach
Abstract: Provided are a hydrophilic polyamide and polyimide retaining characteristics particular to polyamides and polyimides, such as heat resistance. A polymeric compound is provided having a repeating unit represented by the following formula (1): wherein M1 and M2 each independently represent any one selected from the group consisting of a hydrogen atom, a monovalent metal atom, an alkaline earth metal atom and an ammonium ion, provided that M1 and M2 are not a hydrogen atom at the same time; X1 and X2 represent an organic group; m and n each independently represent the number of substituents; Z1 represents a hydrogen atom or an optionally substituted carbonyl group; Z2 represents an optionally substituted hydrocarbon group; Z3 represents a hydrogen atom or an optionally substituted carbonyl group; and when Z1 or Z3 is an optionally substituted carbonyl group, they optionally form a ring structure together with Z2, each independently.
Abstract: The invention provides a resin molded article containing a wholly aromatic liquid crystalline polyester resin and formed by being subjected to heat treatment, in which the enthalpy change ? H1 at the melting point of the first cycle and the enthalpy change ? H2 at the melting point of the second cycle of the temperature elevation process measured by a differential scanning calorimeter satisfy ? H1/? H2?2.0, and the dielectric loss tangent measured by the split-post dielectric resonator (SPDR) method at a measurement frequency of 10 GHz is 0.85×10?3 or less.
Abstract: To provide modified colloidal silica capable of improving the stability of the polishing speed with time when used as abrasive grains in a polishing composition for polishing a polishing object that contains a material to which charged modified colloidal silica easily adheres, such as a SiN wafer, and to provide a method for producing the modified colloidal silica. Modified colloidal silica, being obtained by modifying raw colloidal silica, wherein the raw colloidal silica has a number distribution ratio of 10% or less of microparticles having a particle size of 40% or less relative to a volume average particle size based on Heywood diameter (equivalent circle diameter) as determined by image analysis using a scanning electron microscope.
Abstract: A polymer having a first monomer operatively connected to Rose Bengal, a second monomer, and a surfactant, wherein the surfactant is selected from the group consisting of ionic surfactants, anionic surfactants, cationic surfactants, nonionic surfactants, zwitterionic surfactants, and mixtures thereof. The Rose Bengal in polymer in an amount effective for rendering the polymer antimicrobial or antiviral upon exposure of said polymer to light; and the polymer produces singlet oxygen from air in the presence of light. A substrate have these features is also included.
Type:
Grant
Filed:
March 24, 2017
Date of Patent:
November 15, 2022
Inventors:
William Clary Floyd, Josef S Schneider, Bernard W Wolff
Abstract: This invention relates to a polymer composition comprising: (A) at least one polymer comprising at least one diol residue, and (B) a stabilizer composition comprising: (1) at least one primary antioxidant comprising at least one phenolic antioxidant; and (2) at least one secondary antioxidant comprising at least one phosphite, and (3) at least one chain extending agent; wherein the b* value for said polymer composition is less than 10 according to the L*, a* and b* color system of the CIE (International Commission on Illumination) after being heated for at least three hours at 200° C. or 24 hours at 175° C.
Abstract: The present disclosure relates to dual-headed organoaluminum compositions having the formula (I) and processes to prepare the same. In at least one aspect, the compositions having the formula (I) may be used during olefin polymerization.
Type:
Grant
Filed:
December 27, 2018
Date of Patent:
November 8, 2022
Assignee:
Dow Global Technologies LLC
Inventors:
Lixin Sun, Endre Szuromi, Jerzy Klosin, Edmund M. Carnahan, Jasson T. Patton, Longyan Liao
Abstract: An Al-based bearing alloy and a slide bearing incorporating the alloy exhibit high corrosion resistance and maintain high strength for a long period of time even in a high temperature environment. The Al-based bearing alloy and slide bearing includes an Al matrix, and acicular compounds which are needle-shaped that precipitate at a plurality of sites in a structure of the Al matrix, and that have a minor diameter and a major diameter.
Abstract: A method for producing gradient copolymers can include polymerizing a reaction mixture comprising a monomer and a comonomer in the presence of a metallocene catalyst in a loop reactor, wherein in the loop reactor a gradient monomer weight percent in the reaction mixture is about 3 wt % to about 50 wt %, thereby forming a gradient copolymer.
Type:
Grant
Filed:
October 6, 2020
Date of Patent:
November 8, 2022
Assignee:
EXXONMOBILE CHEMICALS PATENTS INC.
Inventors:
Yifeng Hong, Shanshan Zhang, Jay L. Reimers
Abstract: A SnBiSb series low-temperature lead-free solder and a preparation method thereof, which belongs to the technical field of low-temperature soldering. The lead-free solder includes by weight the following composition: 32.8-56.5% of Bi, 0.7-2.2% of Sb, with the remainder being Sn, wherein the weight percentages of Bi and Sb satisfy a relationship of b=0.006a2?0.672a+19.61+c, wherein the symbol a represents the weight percentage of Bi, the symbol b represents the weight percentage of Sb, and the range of c is ?1.85?c?1.85. The solder alloy has a peritectic or near peritectic structure with a low melting point, and has an excellent mechanical performance and reliability, and applicable to the field of low-temperature soldering.
Abstract: The present invention relates to a polymer comprising repeating units consisting of a substituted pyrrole ring. In particular, the repeating units consist of substituted pyrrole containing polar groups capable of interacting with carbon allotropes such as carbon nanotubes, graphene or nanographites, in order to improve the chemical-physical characteristics of the allotropes mainly by increasing their dispersibility and stability in liquid media and in polymer matrices. The invention also relates to products of addition of these polymers with carbon allotropes in order to obtain easily dispersible macromolecules.
Type:
Grant
Filed:
August 11, 2015
Date of Patent:
October 25, 2022
Assignee:
POLITECNICO DI MILANO
Inventors:
Maurizio Stefano Galimberti, Vincenzina Barbera, Ada Truscello, Roberto Sebastiano, Antonio Marco Valerio
Abstract: The invention relates to a footwear with a rubber sole where such sole is comprised of a rubber composition which contains zinc rosinate. The zinc rosin is provided to include zinc rosinate as a product formed in situ within the rubber composition of zinc oxide and freely added rosin acid. The footwear rubber sole is intended for ground engagement. In one embodiment, the rubber composition for the rubber sole further contains triglyceride vegetable oil. In one embodiment, the rubber composition for the rubber sole additionally contains a traction promoting resin.
Abstract: Provided are a high-yield-ratio high-strength galvanized steel sheet and a method for manufacturing thereof. The high-yield-ratio high-strength galvanized steel sheet has a steel sheet having a specified chemical composition and a metallographic structure including, in terms of area ratio, in terms of area ratio, 15% or less of ferrite, 20% or more and 50% or less of martensite, and bainite and tempered martensite in a total amount of 30% or more, and a galvanized layer formed on the steel sheet having a coating weight of 20 g/m2 to 120 g/m2 per side, in which a yield strength ratio is 65% or more, a tensile strength is 950 MPa or more, and Mn oxides are contained in the galvanized layer in an amount of 0.015 g/m2 to 0.050 g/m2.