Abstract: Compositions and processing conditions are disclosed for the production by rotomolding of polypropylene foams, hither to satisfactorily produced only by injection molding and extrusion molding. Rheological properties of the polypropylene resin, processing conditions and choice of composition of the chemical blowing agent were found to play important roles in obtaining high quality polypropylene foam structures. High strength fine-cell polypropylene foams could in particular be formed by first melt compounding a suitable chemical blowing agent with the resin under conditions which allow for homogeneous mixing without appreciable decomposition of the blowing agent.

Abstract: An extrusion system for providing a foamed material in which a material such as a polymer material is supplied to an extruder for movement through a rotating screw member. The material is placed in a molten state and a foaming agent, such as a supercritical fluid, is introduced into the extruder at a selected pressure so that a two-phase mixture of the molten material and the foaming agent is formed. The foaming agent is then diffused into and dissolved in the molten material to form a single-phase solution which is forwarded from a solution formation to a nucleation device. A thermodynamic instability is induced through a rapid pressure drop, e.g., higher than 0.9 GPa/s in the nucleation device to nucleate microcells in the solution. A further shaping device, e.g., a die, can be used to produce a foamed material of a desired shape.

Abstract: An extrusion system for providing a foamed material in which a material such as a polymer material is supplied to an extruder for movement through a rotating screw member. The material is placed in a molten state and a foaming agent, such as a supercritical fluid, is introduced into the extruder at a selected pressure so that a two-phase mixture of the molten material and the foaming agent is formed. The foaming agent is then diffused into and dissolved in the molten material to form a single-phase solution which is forwarded from a solution formation to a nucleation device. A thermodynamic instability is induced through a rapid pressure drop, e.g., higher than 0.9 GPa/s in the nucleation device to nucleate microcells in the solution. A further shaping device, e.g., a die, can be used to produce a foamed material of a desired shape.

Abstract: A supermicrocellular foamed material and a method for producing such material, the material to be foamed such as a polymerplastic material, having a supercritical fluid, such as carbon dioxide in its supercritical state, introduced into the material to form a foamed fluid/material system having a plurality of cells distributed substantially throughout the material. Cell densities lying in a range from about 10.sup.9 to about 10.sup.15 per cubic centimeter of the material can be achieved with the average cell sizes being at least less than 2.0 microns and preferably in a range from about 0.1 micron to about 1.0 micron.

Abstract: A supermicrocellular foamed material and a method for producing such material, the material to be foamed such as a polymerplastic material, having a supercritical fluid, such as carbon dioxide in its supercritical state, introduced into the material to form a foamed fluid/material system having a plurality of cells distributed substantially throughout the material. Cell densities lying in a range from about 10.sup.9 to about 10.sup.15 per cubic centimeter of the material can be achieved with the average cell sizes being at least less than 2.0 microns and preferably in a range from about 0.1 micron to about 1.0 micron.