Abstract: A process for producing an object from a precursor comprises the steps of: I) depositing a free-radically crosslinked resin atop a carrier to obtain a ply of a construction material joined to the carrier which corresponds to a first selected cross section of the precursor; II) depositing a free-radically crosslinked resin atop a previously applied ply of the construction material to obtain a further ply of the construction material which corresponds to a further selected cross section of the precursor and which is joined to the previously applied ply; III) repeating step II) until the precursor is formed; wherein the depositing of a free-radically crosslinked resin at least in step II) is effected by exposure and/or irradiation of a selected region of a free-radically crosslinkable resin corresponding to the respectively selected cross section of the object and wherein the free-radically crosslinkable resin has a viscosity (23° C., DIN EN ISO 2884-1) of ?5 mPas to ?100000 mPas.

Abstract: A process for producing an object from a precursor comprises the steps of: depositing a free-radically crosslinked resin atop a carrier to obtain a ply of a construction material joined to the carrier which corresponds to a first selected cross section of the precursor; depositing a free-radically crosslinked resin atop a previously applied ply of the construction material to obtain a further ply of the construction material which corresponds to a further selected cross section of the precursor and which is joined to the previously applied ply; repeating step II) until the precursor is formed; wherein the depositing of a free-radically crosslinked resin at least in step II) is effected by exposure and/or irradiation of a selected region of a free-radically crosslinkable resin corresponding to the respectively selected cross section of the object and wherein the free-radically crosslinkable resin has a viscosity (23° C., DIN EN ISO 2884-1) of ?5 mPas to ?100000 mPas.

Abstract: A method for producing an article in which a layer (200) of meltable polymer is selectively melted at least partially. This takes place according to a selected cross section of the article to be formed. The at least partially melted material is added on layer by layer to a carrier (500) or to previous layers bonded to the carrier (500). A system that is suitable for carrying out the method according to the invention has a substrate (100), a control unit (600), an application unit (700) for applying the particles to the substrate (100), an energy exposure unit (700) and a contacting unit (800).

Abstract: A method for producing a foam body (10) having an internal structure (100, 200, 300), comprising the steps: I) selecting an internal structure (100, 200, 300) to be formed in the foam body (10), the structure comprising a first polymer material; II) providing a foam body (10), the foam body (10) comprising a second polymer material which is different to the first polymer material; III) injecting, by means of an injection means (20), a predefined amount of a melt of the first polymer material or a predefined amount of a reaction mixture (30, 31, 32) which reacts to form the first polymer material at a predefined location inside the foam body (10), corresponding to a volume element of the internal structure (100, 200, 300); IV) repeating step III) for further predefined locations inside the foam body (10), corresponding to further volume elements of the internal structure (10), until the internal structure (10) is formed.

Abstract: A method for producing an article in which a layer with a radically cross-linkable resin is selectively crosslinked at least partially. This takes place according to a selected cross section of the article to be formed by means of selective application of a radical initiator. The at least partially crosslinked material is added on layer by layer to a carrier or to previous layers bonded to the carrier. A system that is suitable for carrying out the method according to the invention has a substrate, a control unit, an application unit for applying the resin to the substrate, an application unit for applying an initiator to the resin, an energy exposure unit and a contacting unit.

Abstract: It is a feature of a porous body comprising a three-dimensional network of node points joined to one another by struts, and a void volume present between the struts, that the struts have an average length of ?200 ?m to ?50 mm, the struts have an average thickness of ?100 ?m to ?5 mm, and that the porous body has a compression hardness (40% compression, DIN EN ISO 3386-1: 2010-09) in at least one spatial direction of ?10 to ?100 kPa. The porous body according to the invention combines the advantages of a conventional mattress or cushion with ventilatability which results from its porous structure and is not achievable in conventional foams. The invention further relates to a method of producing such a porous body and to an apparatus comprising said body for supporting and/or bearing a person.

Abstract: The invention relates to a method for producing a visco-elastic damping element comprising at least one visco-elastic spring element, characterized in that the visco-elastic spring element is structured from at least one visco-elastic material having a tan ? of at least 0.5, determined according to DIN 53535: 1982-03, and produced by means of a 3D printing method. The invention further relates to a visco-elastic damping element, which is produced or can be produced according to said method, and to a solid body comprising or consisting of a plurality of damping elements.

Abstract: The present invention relates to novel anisotropic composite materials and processes for production thereof. The composite materials are based on the crosslinking of polyisocyanates and feature good weathering stability.

Abstract: A process is described for producing a three dimensional structure, the process including the following steps a) applying of at least a first material M1 onto a substrate to build a first layer L1 on the substrate; b) layering of at least one further layer Ly of the first material M1 or of a further material Mx onto the first layer L1, wherein the at least one further layer Ly covers the first layer L1 and/or previous layer Ly?1 at least partially to build a precursor of the three dimensional structure; c) curing the precursor to achieve the three dimensional structure; wherein at least one of the materials M1 or Mx provides a Mooney viscosity of >10 ME at 60° C. and of <200 ME at 100° C. before curing and wherein at least one of the first material Mi or of the further material Mx is a powder. Also, a three dimensional structure is described which is available according to the process according to the invention.

Abstract: A process is described for producing a three dimensional structure, the process including the following steps a) applying of at least a first material M1 onto a substrate to build a first layer L1 on the substrate; b) layering of at least one further layer Ly of the first material M1 or of a further material Mx onto the first layer L1, wherein the at least one further layer Ly covers the first layer L1 and/or previous layer Ly-1 at least partially to build a precursor of the three dimensional structure; c) curing the precursor to achieve the three dimensional structure; wherein at least one of the materials M1 or Mx provides a Mooney viscosity of >10 ME at 60° C. and of <200 ME at 100° C. before curing. Also, a three dimensional structure is described which is available according to the process according to the invention.

Abstract: The present invention relates to a polyisocyanurate foam obtainable by reacting a mixture in the presence of a catalyst and optionally an initiator, comprising or consisting of: A) a polyisocyanate component comprising at least one aliphatic polyisocyanate; B) a component reactive to isocyanate comprising at least one polyol and/or an alcohol and also optionally an amine; C) at least one blowing agent; D) at least one foam stabilizer and E) optionally at least one additive, characterized in that the mixture, upon accompanying use of an isocyanate-reactive component (polyol, alcohol, amine), has an index of at least 200. The invention further relates to a process for producing such a foam and use thereof as an insulating material, as a construction element, as facade insulation, as reactor insulation, as battery insulation, as superheated steam insulation, as insulation for a still, or as weather-resistant insulating material.

Abstract: It is a feature of a porous body (10, 20) comprising a three-dimensional network of node points (200) joined to one another by struts (100), and a void volume (300) present between the struts (100), that the struts (100) have an average length of ?200 to ?50 mm, the struts (100) have an average thickness of ?100 ?m to ?5 mm, and that the porous body has a compression hardness (40% compression, DIN EN ISO 3386-1: 2010-09) in at least one spatial direction of ?10 to ?100 kPa. The porous body according to the invention combines the advantages of a conventional mattress or cushion with ventilatability which results from its porous structure and is not achievable in conventional foams. The invention further relates to a method of producing such a porous body (10, 20) and to an apparatus comprising said body (10, 20) for supporting and/or bearing a person.

Abstract: A process for manufacturing an article comprises the steps of: I) applying a filament of an at least partially fused construction material to a support so as to obtain a layer of the construction material which corresponds to a first selected cross-section of the article; II) applying a filament of the at least partially fused construction material to a previously applied layer of the construction material so as to obtain a further layer of the construction material which corresponds to a further selected cross-section of the article and which is bonded to the previously applied layer; and III) repeating step II) until the article is formed. At least steps II) and III) are carried out in a chamber and the construction material comprises a fusible polymer. The fusible polymer has a fusion range (DSC, differential scanning calorimetry; 2nd heating at a heating rate of 5 K/min.) of ?20° C. to ?100° C.

Abstract: The present invention relates to process for producing polyisocyanurate plastics, comprising the following steps: a) providing a polyisocyanate composition A) which comprises oligomeric polyisocyanates and is low in monomeric diisocyanates, “low in monomeric diisocyanates” meaning that the polyisocyanate composition A) has a content of monomeric diisocyanates of not more than 20% by weight, b) catalytically trimerizing the polyisocyanate composition A) using at least one tertiary organic phosphine catalyst B). The invention further relates to polyisocyanurate plastics obtainable by the process according to the invention, to coatings, films, semifinished products and mouldings comprising or consisting of the polyisocyanurate plastic according to the invention, and to the use of the polyisocyanurate plastics according to the invention for production of coatings, films, semifinished products and mouldings.

Abstract: A process for manufacturing an article comprises the steps of: applying a layer that consists of particles to a target area; allowing, in a chamber, energy to act on a selected portion of the layer, according to a cross-section of the article, so that the particles in the selected portion are bonded, and repeating the steps of applying and allowing energy to act for a plurality of layers so that the bonded portions of the adjacent layers are bonded to form the article, at least part of the particles comprising a fusible polymer. The fusible polymer has a fusion range (DSC, differential scanning calorimetry; 2nd heating at a heating rate of 5 K/min.) of ?20 ° C. to ?100 ° C. The fusible polymer further has a complex viscosity \?*\ (determined by viscosity measurement in the melt using a plate-plate oscillating viscometer according to ISO 6721-10 at 100° C. and a shear rate of 1/s) of ?10 Pas to ?1000000 Pas. Finally, the temperature inside the chamber is ?50° C.

Abstract: A method of treating at least part of a surface (110) of an article (100) in which an article (100) is treated, at least part of a surface (110, 111) of the article having been produced by an additive manufacturing method from a construction material, and the construction material provides a temperature TG? at which the storage modulus G? of the construction material (determined by dynamic-mechanical analysis according to ISO 6721 at a shear rate of 1/s) is 10 MPa. The article is preferably placed into an evacuable volume and the volume is evacuated. By heating and exerting pressure, the surface is plastically deformed and can be smoothed thereby.

Abstract: The invention relates to a method for producing a polyisocyanurate composite material, comprising the following steps: a) providing a polyisocyanate composition A) which contains monomer polyisocyanates at an amount of at least 2 wt. %, and b) catalytically trimerising the polyisocyanate composition A) in the presence of at least one fibrous filler material B) and a trimerisation catalyst C), to form the polyisocyanurate composite material, said trimerisation catalyst C) comprising at least one quaternary ammonium salt and/or a metal salt. The invention also relates to polyisocyanurate composite materials that can be obtained according to the claimed method, and to the use of same to produce a component and components consisting of or containing a claimed polyisocyanurate composite material.

Abstract: The present invention relates to novel modified polyisocyanurate plastics obtainable by catalytic trimerization of a composition A), wherein the composition A) comprises oligomeric modified polyisocyanates B) that are a reaction product of an oligomeric polyisocyanate B1) and at least one functionalizing reagent B2) reactive toward isocyanate groups, where the composition A) has a content of monomeric diisocyanates of not more than 20% by weight and where the at least one functionalizing reagent B2) reactive toward isocyanate groups has at least one functional group reactive toward isocyanate groups which is not an isocyanate group. The invention further relates to the process from which the polyisocyanurate plastics of the invention are obtainable, to the use of the polyisocyanurate plastics of the invention for production of coatings, films, semifinished products, composites and moldings, and to substrates coated with such a coating.

Abstract: The invention relates to a process for producing a composite polyisocyanurate material, comprising the following steps: a) providing a polyisocyanate composition A) which comprises oligomeric polyisocyanates and is low in monomeric diisocyanates, “low in monomeric diisocyanates” meaning that the polyisocyanate composition A) has a content of monomeric diisocyanates of not more than 20% by weight, and b) catalytically trimerizing the polyisocyanate composition A) in the presence of at least one fibrous filler B) and of a trimerization catalyst C) to give the composite polyisocyanurate material, where the trimerization catalyst C) comprises at least one metal salt and/or quaternary ammonium salt. The invention further relates to composite polyisocyanurate materials obtainable by the process according to the invention and to the use thereof for production of a component, and to components consisting of or comprising a composite polyisocyanurate material according to the invention.

Abstract: The invention relates to novel modified polyisocyanurate plastics, obtainable by means of catalytic trimerization of a composition (A), wherein the composition (A) contains oligomeric, modified polyisocyanates (B), which represent a reaction product from an oligomeric polyisocyanate (B1) and at least one functionalization reagent (B2) which is reactive to isocyanate groups, wherein the composition (A) comprises a content of monomeric diisocyanates of 20 wt % at maximum and wherein the at least one functionalization reagent (B2) which is reactive to isocyanate groups has at least one relative functional group which is reactive to isocyanate groups and which is not an isocyanate group. The invention further relates to the method by which the polyisocyanurate plastics according to the invention are obtainable, to the use of the polyisocyanurate plastics according to the invention for producing coatings, films, semi-finished products, composite materials and molded parts, and substrates coated by such a coating.