Abstract: Examples described herein relate to a molded article provided with a resin part formed with a polyolefin resin composite material, the polyolefin resin composite material containing a polyolefin resin and 10 to 150 parts by mass of cellulose based on 100 parts by mass of the polyolefin resin, wherein an area of an aggregate of the cellulose is less than 20,000 ?m2.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition containing 5 to 70 parts by mass of cellulose based on 100 parts by mass of the thermoplastic resin and containing an organic peroxide, wherein a tensile strength of a resin molded body formed with the thermoplastic resin composition measured in accordance with JIS K 7161 is 40 MPa or more.

Abstract: A thermoplastic resin composition, containing a thermoplastic synthetic resin, a cellulose in the content of 10 to 70 parts by mass with respect to 100 parts by mass of the thermoplastic synthetic resin, and an organic peroxide, in which the tensile strength of a resin composed of the thermoplastic resin composition measured in conformity with JIS K7161 is 40 MPa or more; a cellulose-reinforced thermoplastic resin composition; a molded article of a cellulose-reinforced resin; and a method of producing a cellulose-reinforced thermoplastic resin composition or a molded article.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition. The thermoplastic resin composition containing thermoplastic resins and cellulose, wherein at least one of the thermoplastic resins is a resin having in a polymer molecule at least one group selected from a group containing a partial structure of an acid anhydride and a group containing an acylated cellulose structure.

Abstract: A thermoplastic resin composition, containing a thermoplastic synthetic resin, a cellulose and an ionic compound; in which a content of the cellulose is from 1 to 100 parts by mass, with respect to 100 parts by mass of the thermoplastic synthetic resin, and a content of the ionic compound is 0.001 times or more and less than 1.000 time of the content of the cellulose; a method of producing a thermoplastic resin composition; a molded article of a cellulose-reinforced resin; and a method of producing a molded article of a cellulose-reinforced resin.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition. The molded article is provided with a resin part formed with a thermoplastic resin composition. The thermoplastic resin composition containing a thermoplastic resin, cellulose, and an ionic compound, wherein a content of the cellulose is 1 to 100 parts by mass based on 100 parts by mass of the thermoplastic resin, and a content of the ionic compound is 0.001 times or more and less than 1.000 times the content of the cellulose.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition. The thermoplastic resin composition containing thermoplastic resins and cellulose, wherein at least one of the thermoplastic resins is a resin having in a polymer molecule at least one group selected from a group containing a partial structure of an acid anhydride and a group containing an acylated cellulose structure.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition. The thermoplastic resin composition containing thermoplastic resins and cellulose, wherein at least one of the thermoplastic resins is a resin having in a polymer molecule at least one group selected from a group containing a partial structure of an acid anhydride and a group containing an acylated cellulose structure.

Abstract: A polyolefin resin composition, containing: a polyolefin resin; and cellulose microfibrils, in which a content of the cellulose microfibrils is 0.5 to 20 parts by mass, with respect to 100 parts by mass of an entire resin component in the polyolefin resin composition, a molded article and a back door for a vehicle.

Abstract: A polyolefin resin composite material, containing: a polyolefin resin; and 10 to 150 parts by mass of cellulose fibers with respect to 100 parts by mass of the polyolefin resin, wherein an area of aggregates of the cellulose fibers is less than 20,000 ?m2; and a method of producing the same.

Abstract: A method of producing a thermoplastic resin composition containing a thermoplastic synthetic resin and a cellulose, in which at least one type of the thermoplastic synthetic resin is a resin having a group containing a partial structure of an acid anhydride in the polymer molecule; a molded article of a cellulose-reinforced resin; and a method of producing a molded article of a cellulose-reinforced resin.

Abstract: A glass fiber-reinforced polyolefin resin material, containing: a glass fiber; and a thermoplastic resin, wherein said thermoplastic resin contains: at least, a specific graft-modified polypropylene, wherein, with respect to the graft-modified polypropylene, each specific amounts of the glass fiber and a compound or polymer having an acid anhydride structure are contained, and wherein, in the content of a graft-modification component in the graft-modified polypropylene, the content of a component obtained from the (meth)acrylate containing an epoxy group is 0.5 or more and 10 or less parts by mass with respect to 100 parts by mass of said polypropylene, and a component obtained from the aromatic vinyl compound has a mass equal to or less than said component obtained from the (meth)acrylate; a composition for said resin material; a method of producing the same; and a composite.

Abstract: Examples described herein relate to a molded article provided with a resin part formed with a polyolefin resin composite material, the polyolefin resin composite material containing a polyolefin resin and 10 to 150 parts by mass of cellulose based on 100 parts by mass of the polyolefin resin, wherein an area of an aggregate of the cellulose is less than 20,000 ?m2.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition containing 5 to 70 parts by mass of cellulose based on 100 parts by mass of the thermoplastic resin and containing an organic peroxide, wherein a tensile strength of a resin molded body formed with the thermoplastic resin composition measured in accordance with JIS K 7161 is 40 MPa or more.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition. The thermoplastic resin composition containing thermoplastic resins and cellulose, wherein at least one of the thermoplastic resins is a resin having in a polymer molecule at least one group selected from a group containing a partial structure of an acid anhydride and a group containing an acylated cellulose structure.

Abstract: The present disclosure relates to a molded article provided with a resin part formed with a thermoplastic resin composition. The molded article is provided with a resin part formed with a thermoplastic resin composition. The thermoplastic resin composition containing a thermoplastic resin, cellulose, and an ionic compound, wherein a content of the cellulose is 1 to 100 parts by mass based on 100 parts by mass of the thermoplastic resin, and a content of the ionic compound is 0.001 times or more and less than 1.000 times the content of the cellulose.

Abstract: A polyolefin-based thermoplastic elastomer and a crosslinked body of the same which can undergo a silane-crosslinking process excellent in productivity and have a rubber property required as a substitute material for EPDM is disclosed herein and can use a silane-crosslinkable ethylene-propylene copolymer characterized in that an organic peroxide (B) and a silane coupling agent (C) are compounded with an ethylene-propylene copolymer resin (A) which comprises 5 to 25% by mass of an ethylene component and 75 to 95% by mass of a propylene component, and whose MFR measured at 230° C. and with a load of 2.16 kg applied is 20.0 g/10 min or less. and further a compounded amount of the organic peroxide is 0.1 to 0.6 pts. mass based on 100 pts. mass of the ethylene-propylene copolymer resin (A) and a one-minute half-life temperature of the organic peroxide is 175.2° C. or less.

Abstract: A polyolefin resin composite material, containing: a polyolefin resin; and 10 to 150 parts by mass of cellulose fibers with respect to 100 parts by mass of the polyolefin resin, wherein an area of aggregates of the cellulose fibers is less than 20,000 ?m2; and a method of producing the same.

Abstract: A glass fiber-reinforced polyolefin resin material, containing: a glass fiber; and a thermoplastic resin, wherein said thermoplastic resin contains: at least, a specific graft-modified polypropylene, wherein, with respect to the graft-modified polypropylene, each specific amounts of the glass fiber and a compound or polymer having an acid anhydride structure are contained, and wherein, in the content of a graft-modification component in the graft-modified polypropylene, the content of a component obtained from the (meth)acrylate containing an epoxy group is 0.5 or more and 10 or less parts by mass with respect to 100 parts by mass of said polypropylene, and a component obtained from the aromatic vinyl compound has a mass equal to or less than said component obtained from the (meth)acrylate; a composition for said resin material; a method of producing the same; and a composite.

Abstract: A fired precast block prevents itself from dropping off early due to corrosion and increases service life of a blast furnace runner, etc. when used in a very vulnerable portion of the blast furnace runner, etc., and can be produced at low costs. The fired precast block has an upper surface to contact molten metal or slag, a lower surface opposing the upper surface, and a plurality of side surface. The fired precast block is used by being embedded in a castable in such a manner that the upper surface is exposed from the castable and the lower surface and the plurality of side surfaces contact the castable. Each side surface of at least one opposing pair of side surfaces includes a planar portion and an uneven portion. The uneven portion has at least one groove-shaped concave portion.