Abstract: A transparent coloured lithium aluminium silicate glass ceramic and method of producing are provided. The glass ceramic has a brightness Y of 0.1% to 80% at thickness 4 mm. The glass ceramic has a D65 standard illuminant light, after passing through the glass ceramic with thickness 4 mm, with a colour locus in a white region W1 determined by coordinates in a chromaticity diagram CIExyY-2°: White region W1 x y 0.27 0.21 0.22 0.25 0.32 0.37 0.45 0.45 0.47 0.34 0.36 0.29.

Abstract: A fitout article or article of equipment for a kitchen or laboratory is provided. The article has a display device, a separating element, and a covering. The covering is on an interior side of the separating element and has a cutout at the separating element. The separating element has a light transmittance of at least 5% and at most 70%. The covering has light transmittance of at most 7% and a colour locus in the CIELAB colour space with coordinates L* of 20 to 40, a* of ?6 to 6 and b* of ?6 to 6, and the colour locus of D65 standard illuminant light, after passing through the substrate, is within a white region W1 determined in the chromaticity diagram CIExyY-2° by the coordinates: White region W1 x Y 0.27 0.21 0.22 0.25 0.32 0.37 0.45 0.45 0.47 0.34 0.36 0.29.

Abstract: A transparent colored glass ceramic, in particular an LAS glass ceramic, suitable for use as a cooking surface is provided. The transparent colored glass ceramic includes high-quartz solid solution (HQ s.s.) as a main crystal phase and exhibits thermal expansion of ?1 to +1 ppm/K in the range from 20° C. to 700° C. The glass ceramic has from 3.0 to 3.6 percent by weight of lithium oxide (Li2O) as constituents and either is colored with 0.003 to 0.05 percent by weight of vanadium oxide (V2O5) or is colored with 0.003 to 0.25 percent by weight of molybdenum oxide (MoO3).

Abstract: A fitout article or article of equipment for a kitchen or laboratory is provided. The article has a lighting and separating element. The separating element in a region of the lighting element has light transmittance of at least 0.1% and less than 12%. The lighting element in the interior emits light that passes through the separating element and to the exterior. The separating element has a glass or glass-ceramic substrate having a CTE of 0 to 6 ppm/K and has a colour locus in the CIELAB colour space with the coordinates L* of 20 to 40, a* of ?6 to 6 and b* of ?6 to 6. D65 standard illuminant light, after passing through the separating element, is within a white region W1 determined in the chromaticity diagram CIExyY?2° by the following coordinates: White region W1 x y 0.27 0.21 0.22 0.25 0.32 0.37 0.45 0.45 0.47 0.34 0.36 0.29.

Abstract: A sightglass for a stove is provided that has a substrate made of transparent coloured lithium aluminium silicate glass ceramic. The sightglass has a light transmittance of 0.1% to 50%. Standard illuminant D65 light, after passing through the glass ceramic, at a thickness of 4 mm, has a colour locus in the white region W1 determined by the following coordinates in the chromaticity diagram CIExyY-2°: White region W1 x y 0.27 0.21 0.22 0.25 0.32 0.37 0.45 0.45 0.47 0.34 0.36 ?0.29.

Abstract: A composite material is provided that includes at least one first material and particles. The particles have a negative coefficient of thermal expansion and the particles have a sphericity ? of at least 0.7. The composite material includes at least 30 vol % of the particles at a particle size of d50?1.0 ?m or at least 40 vol % of the composite material at a particle size d50>1.0 ?m.

Abstract: A glass ceramic article is provided so that a reliable coloring with a defined transmittance is ensured. The reliable coloring of the glass ceramic article is based on a high content of iron oxide of more than 0.1 percent by weight which itself has a strongly coloring effect does not further reduce transmittance but rather interacts with vanadium oxide to attenuate the absorption caused by vanadium oxide.

Abstract: A glass-ceramic cooktop is provided that is made of glass-ceramic material with a flat upper side and an underside. The glass-ceramic material has transmittance values of greater than 0.1% in the visible light range in the total wavelength region greater than 420 nm, a light transmittance in the visible range of 0.8-2.5%, and a transmittance of 0-85% in the infrared at 1600 nm, and wherein the glass-ceramic material has high quartz mixed crystals as the prevalent crystal phase. The underside is flat, unstructured, and coplanar with the upper side.

Abstract: An LAS-glass for producing a transparent glass-ceramic and an LAS-glass-ceramic having a predetermined chroma C* and a predetermined visually determinable scatter value (S) are provided. The LAS-glass and LAS-glass-ceramic has a process window as large as possible during the nucleus formation process with respect to the residence time in the relevant temperature range for the formation of nuclei.

Abstract: A glass-ceramic cooktop is provided that is made of glass-ceramic material with a flat upper side and an underside. The glass-ceramic material has transmittance values of greater than 0.1% in the visible light range in the total wavelength region greater than 420 nm, a light transmittance in the visible range of 0.8-2.5%, and a transmittance of 0-85% in the infrared at 1600 nm, and wherein the glass-ceramic material has high quartz mixed crystals as the prevalent crystal phase. The underside is flat, unstructured, and coplanar with the upper side.

Abstract: A method of manufacturing glass ceramic articles such as glass ceramic plates for cooktops or fireplace windows is provided. The method facilitates the adjustment of a specific hue or a specific absorptivity of the glass ceramic in the visible spectral range. The method is based on the finding that the absorption of light by coloring agents which are appropriate for or present in glass ceramics can be attenuated during the ceramization process by adding substances that have a decoloring effect.

Abstract: A method for producing bubble-free glasses is provided, in which a glass mixture that is arsenic-free, antimony-free and tin-free with the exception of any unavoidable raw material impurities and at least one sulfate compound as a refining agent are used. The glass mixture and refining agent are melted and primarily refined in a first region of a melting tank, an average melting temperature (T1) is set at T1>1580° C. and an average melt residence time (t1) is set at t1>2 hours. A secondary refinement is carried out in a second region, an average melting temperature (T2) is set at T2>1660° C. and an average melt residence time (t2) is set at t2>1 hour, and the proportion of the SO3 resulting from decomposition of the sulfate is reduced to less than 0.002 wt. %.

Abstract: A panel like, double-sided coated substrate and a method for production are provided. The panel like substrate includes at least two layers applied by heating, the first layer being applied on a first side of the substrate and having at least a glass component and structure-forming particles, the particles producing elevations on the first layer, and the softening temperature or the melting temperature of the particles being greater than the softening temperature of the glass component, and the second layer being applied on a second side of the substrate.

Abstract: A glass flux material for applying an opaque coating is provided. The glass flux material includes at least one pigment and a glass component with the following composition: SiO2 55-70 mol %, Al2O3 2.5-8 mol %, Bi2O3 0.5-<4 mol %, B2O3 14-27 mol %, with at least 2.5 mol % of at least one oxide of the group Li2O, Na2O, and K2O, wherein the ratio of alkali oxides to aluminum oxide ?R2O/Al2O3 is less than 6.

Abstract: Transparent or transparent dyed lithium aluminum silicate (LAS) glass ceramic material is provided that has an adapted thermal expansion. The material includes high-quartz mixed crystals as the predominant crystalline phase, and a thermal expansion between room temperature and 700° C. from 1.0 to 2.5·10?6/K.

Abstract: An LAS-glass for producing a transparent glass-ceramic and an LAS-glass-ceramic having a predetermined chroma C* and a predetermined visually determinable scatter value (S) are provided. The LAS-glass and LAS-glass-ceramic has a process window as large as possible during the nucleus formation process with respect to the residence time in the relevant temperature range for the formation of nuclei.

Abstract: A highly crystalline transparent, translucent or opaque lithium aluminium silicate (LAS) glass-ceramic which has a proportion of residual glass phase of less than 20% by weight and also the use thereof is described.

Abstract: A syringe made of borosilicate glass and having a cone for fastening or mounting of transfer adapters and needles is provided. The cone includes a coating that increases roughness. The coating has structure-forming particles are embedded in a glass matrix and is free of Pb, Cd, Hg and CrVI.

Abstract: A transparent low-colour lithium aluminium silicate (LAS) glass ceramic and the use thereof are provided. The ceramic has an environmentally friendly composition with high-quartz mixed crystals as the main crystal phase. The glass ceramic contains the following components (in wt % on the basis of oxide): TiO2 1.6-<2.5; Nd2O3 0.005-0.15; MgO 0.2-1.0; ZnO 1-2.5; CaO+SrO 0-1.5; BaO 0-1.5 with the condition B1: MgO+ZnO>CaO+SrO +BaO. In some embodiments, the glass ceramic has a hue c* of less than 5.5, a light transmission Y greater than 81% and has no visually disruptive diffusion.

Abstract: A flexible article made of glass and metal foil, as well as the production thereof, are provided. The flexible article is a multilayered structure having at least one glass layer and one metal foil layer, and the shear strength between glass and metal foil is above 1 MPa/mm2. The glass layer of said flexible article has high electrical resistivity at ambient temperature, low roughness, low thickness, good adherence to metal foil, and the glass in the glass layer has high temperature stability and low flowing temperature, and the thermal expansion coefficient (20 to 300° C.) is 1×10?6/K to 25×10?6/K. The whole article is flexible and can be bent, and the curvature radius of the bent flexible article is above 1 mm.