Abstract: An indium oxide sintered compact containing zirconium as an additive, wherein the ratio of atomic concentration of zirconium to the sum of the atomic concentration of indium and the atomic concentration of zirconium is in the range of 0.5 to 4%, the relative density is 99.3% or higher, and the bulk resistance is 0.5 m?·cm or less. This invention aims to provide an indium oxide transparent conductive film of high transmittance in the visible light region and the infrared region, with low film resistivity, and in which the crystallization temperature can be controlled, as well as the manufacturing method thereof, and an oxide sintered compact for use in producing such transparent conductive film.

Abstract: Provided is a sputtering target of sintered Ti—Nb based oxide, wherein the sputtering target consists of titanium (Ti), niobium (Nb), and remainder being oxygen and unavoidable impurities, and the atomic ratio of Ti and Nb is 0.39?(Nb/(Ti+Nb))?0.79. The sputtering target of sintered Ti—Nb based oxide has a high refractive index and a low extinction coefficient. Also provided is a thin film of Ti—Nb based oxide obtained by using the foregoing target, which enables high-rate deposition. The thin film has superior transmittance, is subject to minimal reduction and variation of reflectivity, and is useful as an interference film or a protective film of an optical information recording medium, or as a part of a constituent layer of an optical recording medium. The thin film can also be applied to a glass substrate; that is, it can be used as a heat reflecting film, an antireflection film, or an interference filter.

Abstract: A thin film comprising titanium oxide as its main component, wherein the thin film includes titanium, oxygen and copper, content of Ti is 29.0 at % or higher and 34.0 at % or less and content of Cu is 0.003 at % or higher and 7.7 at % or less with remainder being oxygen and unavoidable impurities, and ratio of oxygen component to metal components, O/(2Ti+0.5Cu), is 0.96 or higher.

Abstract: A sputtering target is provided that has a relative density of 80% or more and contains a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. A ZnO based sputtering target is obtained which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.

Abstract: A sputtering target is provided that has a relative density of 80% or more and contains a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. A ZnO based sputtering target is obtained which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.

Abstract: A Ge—Cr alloy sputtering target containing 5 to 50 at % of Cr and having a relative density of 95% or more, and a manufacturing method of such a Ge—Cr alloy sputtering target wherein Cr powder having a minus sieve of 75 ?m or less, and Ge powder having a minus sieve of 250 ?m or less and having a BET specific surface area of 0.4 m2/g or less are dispersively mixed in an even manner, and sintered thereafter. Thereby provided is a Ge—Cr alloy sputtering target capable of suppressing variation of the deposition speed and film composition, as well as improving the production yield, of the GeCrN layer deposited with reactive sputtering as the intermediate layer between the recording layer and protective layer of a phase change optical disk, and the manufacturing method of such a target.

Abstract: Provided is a thin film mainly comprising titanium oxide, wherein the thin film comprises components of Ti, Ag and O and contains 29.6 at % or more and 34.0 at % or less of Ti, 0.003 at % or more and 7.4 at % or less of Ag, and oxygen as the remainder thereof, and O/(2Ti+0.5Ag) as a ratio of oxygen to metals is 0.97 or more. This invention aims to provide a thin film mainly comprising titanium oxide having a high refractive index and a low extinction coefficient, a sintered sputtering target mainly comprising titanium oxide suitable for producing the thin film, and a method of producing a thin film mainly comprising titanium oxide. This invention also aims to provide a thin film that has superior transmittance, minimally deteriorates in reflectance, and is useful as an interference film or a protective film for an optical information recording medium.

Abstract: A sputtering target is provided that has a relative density of 80% or more and contains a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X<m, 0?Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. A ZnO based sputtering target is obtained which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.

Abstract: A sputtering target is provided that has a relative density of 80% or more and contains a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. A ZnO based sputtering target is obtained which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particUlarly 90% or more.

Abstract: A sputtering target is provided that has a relative density of 80% or more and contains a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. A ZnO based sputtering target is obtained which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.

Abstract: Provided is a sputtering target having a relative density of 80% or more and containing a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. Obtained is a ZnO based sputtering target which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.

Abstract: Provided is chromic oxide powder for a sputtering target comprised of chromic oxide wherein sulfur is 100 wtppm or less. This sputtering target contains chromic oxide of 5 molar % or higher or chromic oxide, wherein the sulfur content in the sputtering target is 100 wtppm or less, and the purity excluding gas components of moisture, carbon, nitrogen and sulfur is 99.95 wt % or higher. The chromic oxide powder for a sputtering target is able to increase the purity of the chromic oxide itself as well as increase the sintered density upon manufacturing a sputtering target. As a result of manufacturing a sputtering target using this chromic oxide powder, the crystal grains are refined, and provided is a uniform and dense sputtering target that does not generate cracks.

Abstract: The present invention provides a sputtering target for a phase change memory and a phase change memory film formed with such a target, and the manufacturing method thereof, characterized in that the sputtering target is composed from elements of not less than a three component system and has as its principal component one or more components selected from stibium, tellurium and selenium, and the compositional deviation in relation to the intended composition is ±1.0 at % or less.

Abstract: A sputtering target is provided that has a relative density of 80% or more and contains a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. A ZnO based sputtering target is obtained which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.

Abstract: A manufacturing method of a sputtering target having mainly oxychalcogenide containing La and Cu by sintering at least one or more powders selected from an elementary substance of a constituent element, oxide or chalcogenide as the raw material, characterized in including a reaction step of retaining the [material] at a temperature of 850° C. or less for 1 hour or more during the sintering step, wherein this [material], after the reaction step, is subject to pressure sintering at a temperature that is higher than the reaction step temperature. In addition to increasing the density of a P-type transparent conductive material target having mainly oxychalcogenide containing La and Cu and enabling the enlargement of the target at a low manufacturing cost, the existence of unreacted matter in the target can be eliminated, the production yield can be improved by suppressing the generation of cracks in the target, and the quality of deposition formed by sputtering this kind of target can also be improved.

Abstract: A Ge—Cr alloy sputtering target containing 5 to 50 at % of Cr and having a relative density of 95% or more, and a manufacturing method of such a Ge—Cr alloy sputtering target wherein Cr powder having a minus sieve of 75 ?m or less, and Ge powder having a minus sieve of 250 ?m or less and having a BET specific surface area of 0.4 m2/g or less are dispersively mixed in an even manner, and sintered thereafter. Thereby provided is a Ge—Cr alloy sputtering target capable of suppressing variation of the deposition speed and film composition, as well as improving the production yield, of the GeCrN layer deposited with reactive sputtering as the intermediate layer between the recording layer and protective layer of a phase change optical disk, and the manufacturing method of such a target.

Abstract: Provided is a sputtering target and an optical recording medium having formed thereon a phase change optical disc protective film having zinc sulfide as its principal component employing such a target, as well as the manufacturing method thereof, characterized in that the sputtering target has zinc sulfide as its principal component, and is capable of adjusting the refractive index of a film containing conductive oxide in the range of 2.0 to 2.6. This sputtering target, and an optical recording medium having formed thereon a phase change optical disc protective film having zinc sulfide as its principal component employing such a target, is capable of reducing particles (dust emission) and nodules that arise during sputtering, has minimal variation in quality and is capable of improving mass productiveness, and in which the crystal grain is fine and has a high density of 90% or more.

Abstract: The present invention provides a sputtering target for a phase change memory and a phase change memory film formed with such a target, and the manufacturing method thereof, characterized in that the sputtering target is composed from elements of not less than a three component system and has as its principal component one or more components selected from stibium, tellurium and selenium, and the compositional deviation in relation to the intended composition is ±1.0 at % or less.

Abstract: The present invention provides a sputtering target for a phase change memory and a phase change memory film formed with such a target, and the manufacturing method thereof, characterized in that the sputtering target is composed from elements of not less than a three component system and has as its principal component one or more components selected from stibium, tellurium and selenium, and the compositional deviation in relation to the intended composition is ±1.0 at % or less.

Abstract: Provided is a sputtering target having a relative density of 80% or more and containing a compound having as its principal component zinc oxide satisfying AXBYO(KaX+KbY)/2(ZnO)m, 1<m, X?m, 0<Y?0.9, X+Y=2, where A and B are respectively different positive elements of trivalence or more, and the valencies thereof are respectively Ka and Kb. Obtained is a ZnO based sputtering target which does not contain ZnS and SiO2, and, upon forming a film via sputtering, is capable of reducing the affect of heating the substrate, of performing high speed deposition, of adjusting the film thickness to be thin, of reducing the generation of particles (dust) and nodules during sputtering, of improving the productivity with small variation in quality, and which has fine crystal grains and a high density of 80% or more, particularly 90% or more.