Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a particulate polyimide matting agent and a low conductivity carbon black. The particulate polyimide matting agent is present in an amount from 1.6 to 9 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a non-carbon black pigment and a particulate polyimide matting agent. The particulate polyimide matting agent is present in an amount from 1.6 to 9 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a particulate polyimide matting agent and a low conductivity carbon black. The particulate polyimide matting agent is present in an amount from 1.6 to 9 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a particulate polyimide matting agent and a low conductivity carbon black. The particulate polyimide matting agent is present in an amount from 1.6 to 9 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a non-carbon black pigment and a particulate polyimide matting agent. The particulate polyimide matting agent is present in an amount from 1.6 to 9 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a particulate polyimide matting agent having a density from 1.3 to 1.5 g/cc and either a non-carbon black pigment or a dye. The particulate polyimide matting agent is present in an amount from 1.6 to 20 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a particulate polyimide matting agent and a low conductivity carbon black. The particulate polyimide matting agent is present in an amount from 1.6 to 9 weight percent of the base film.

Abstract: The present disclosure is directed to a base film having a chemically converted polyimide, a particulate polyimide matting agent and a low conductivity carbon black. The particulate polyimide matting agent is present in an amount from 1.6 to 20 weight percent of the base film.

Abstract: The present disclosure is directed to methods of reducing the amount of colorant in a multilayer film and achieving an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer containing a matting agent, submicron carbon black and submicron fumed metal oxide.

Abstract: The present disclosure is directed to methods of reducing the amount of colorant in a multilayer film and achieving an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer containing a matting agent, submicron carbon black and submicron fumed metal oxide.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 63 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 35 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to multilayer film having has an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer. The second polyimide layer has 25 to 50 wt % of a polyimide, 15 to 35 wt % of a polyimide particle matting agent, greater than 0 and less than 20 wt % of at least one submicron carbon black and 15 to 50 wt % of at least one submicron fumed metal oxide.

Abstract: The present disclosure is directed to multilayer film having has an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer. The second polyimide layer has 45 to 67 wt % of a polyimide, greater than 14 wt % of a silica matting agent or a mixture of silica matting agent and at least one additional matting agent, and at least one submicron carbon black, wherein the total amount of the submicron carbon black and the polyimide is less than 85 wt % and greater than 45 wt %.

Abstract: The present disclosure is directed to multilayer film having has an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer. The second polyimide layer has 25 to 50 wt % of a polyimide, greater than 0 and less than 20 wt % of a silica matting agent, greater than 0 and less than 20 wt % of at least one submicron carbon black and 15 to 50 wt % of at least one submicron fumed metal oxide.

Abstract: The present disclosure is directed to multilayer film having has an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer. The second polyimide layer has 25 to 50 wt % of a polyimide, 15 to 35 wt % of a polyimide particle matting agent, greater than 0 and less than 20 wt % of at least one submicron carbon black and 15 to 50 wt % of at least one submicron fumed metal oxide.

Abstract: The present disclosure is directed to multilayer film having has an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer. The second polyimide layer has 45 to 67 wt % of a polyimide, greater than 14 wt % of a silica matting agent or a mixture of silica matting agent and at least one additional matting agent, and at least one submicron carbon black, wherein the total amount of the submicron carbon black and the polyimide is less than 85 wt % and greater than 45 wt %.

Abstract: The present disclosure is directed to multilayer film having has an L* color less than 30 and a 60 degree gloss value less than 10. The multilayer film has a first polyimide layer and a second polyimide layer. The second polyimide layer has 25 to 50 wt % of a polyimide, greater than 0 and less than 20 wt % of a silica matting agent, greater than 0 and less than 20 wt % of at least one submicron carbon black and 15 to 50 wt % of at least one submicron fumed metal oxide.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 63 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 35 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, and has a median particle size from 1.3 to 10 microns. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also optionally directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.