Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 63 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 35 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 63 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 35 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a corona resistant structure having a polyimide layer and an adhesive layer. The polyimide layer is composed of a chemically converted polyimide and a corona resistant composite filler. The chemically converted polyimide is derived from at least 50 mole percent of an aromatic dianhydride and at least 50 mole percent of an aromatic diamine. The corona resistant composite filler has an organic component and an inorganic ceramic oxide component. The weight ratio of the organic component to the inorganic ceramic oxide component is from 0.01 to 1.0. At least a portion of the organic component comprises an organo-siloxane moiety or an organo-metaloxane moiety.

Abstract: The present disclosure is directed to a corona resistant structure having a polyimide layer. The polyimide layer is composed of a chemically converted polyimide and a corona resistant composite filler. The chemically converted polyimide is derived from at least 50 mole percent of an aromatic dianhydride and at least 50 mole percent of an aromatic diamine. The corona resistant composite filler has an organic component and an inorganic ceramic oxide component. The weight ratio of the organic component to the inorganic ceramic oxide component is from 0.01 to 1.0. At least a portion of the organic component comprises an organo-siloxane moiety or an organo-metaloxane moiety.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.

Abstract: The present disclosure is directed to a corona resistant composition having a polyimide layer and a fluoropolymer layer. The polyimide layer is composed of a chemically converted polyimide and a corona resistant composite filler. The chemically converted polyimide is derived from at least 50 mole percent of an aromatic dianhydride and at least 50 mole percent of an aromatic diamine. The corona resistant composite filler has an organic component, A and an inorganic ceramic oxide component, B. The weight ratio of A:B is from 0.01 to 1.0. At least a portion of an interface between the two components comprises an organo-siloxane or organo-metaloxane moiety.

Abstract: The present disclosure is directed to a base film having a thickness from 8 to 152 microns, a 60 degree gloss value from 2 to 35, an optical density greater than or equal to 2 and a dielectric strength greater than 1400 V/mil. The base film comprises a chemically converted (partially or wholly aromatic) polyimide in an amount from 71 to 96 weight percent of the base film. The base film further comprises a pigment and a matting agent. The matting agent is present in an amount from 1.6 to 10 weight percent of the base film, has a median particle size from 1.3 to 10 microns, and has a density from 2 to 4.5 g/cc. The pigment is present in an amount from 2 to 9 weight percent of the base film. The present disclosure is also directed to coverlay films comprising the base film in combination with an adhesive layer.