Abstract: A hard facing chromium-base alloy consisting essentially of 30.0 to 48.0% by weight of nickel, 1.5 to 15.0% by weight of tungsten and/or 1.0 to 6.5% by weight of molybdenum, the balance being more than 40.0% by weight of chromium, and the maximum sum of tungsten and molybdenum being 15.0% by weight. The alloy may also contain one or more of iron, cobalt, carbon, boron, aluminum, silicon, niobium and titanium. When the alloy is used in powder form as a material for hard facing by welding, the alloy may further contain 0.01 to 0.12% by weight of aluminum, yttrium, misch metal, titanium, zirconium and hafnium. 0.01 to 0.1% by weight of oxygen may also be added to the alloy. The alloy has a high degree of toughness, wear resistance and corrosion resistance. The alloy can be used as a hard facing material to be applied to various objects, such as automobile engine valves.

Abstract: A zinc-plated metallic material resistant to corrosion at elevated temperatures comprising a metallic material; a plating layer consisting of zinc or zinc alloy containing 70% by weight or more of zinc; and a coating layer on the plating layer comprising 10 to 5,000 mg. of magnesium oxide or hydrated magnesium oxide and 50 to 5,000 mg. of chromium oxide or hydrated chromium oxide per square meter of the coating layer.

Abstract: In forming a weld bead of pure copper on a ferroalloy base material by laying a powder of copper and melting the powder by a high density energy source such as laser beams, TIG arc or electron beams, the powder of copper is beforehand mixed with a powder of an auxiliary metal having a higher melting point than pure copper. In order to ensure the substantial purity in copper of the weld bead, the powder mixture should not include more than 16 wt % nickel.

Abstract: A wear-resistant copper-base alloy having superior self-lubricity includes, by weight %,Ni: 10.0 to 30.0%;Si: 0.5 to 3%;Co: 2.0 to 15.0%;at least one metal selected from the group consisting of Mo, W, Nb and V:2.0 to 15.0%; andthe balance being Cu and unavoidable impurities, and having a structure in which hard phase grains containing 5 vol% or more of silicide of at least one metal selected from the group consisting of Mo, W, Nb and V are uniformly dispersed in an amount of 10 to 60 vol% in a copper-rich matrix, to which 2.0 to 15.0% of Fe and/or 1.0 to 10.0% of Cr may be further added.

Abstract: An oscillatory mirror device having a mirror and a pair of exciting systems to exert a couple of forces to turn the mirror around an axis of oscillation in an oscillating manner.

Abstract: A flicker compensating apparatus for compensating for flickering due to a variation in the reactive power generated from a DC arc furnace connected by an AC/DC converter to an AC power system, comprises: a current detector for detecting a DC current flowing in the DC arc furnace; a controller for determining the phase control angle of a thyristor included in the AC/DC converter in accordance with the difference between the detected DC current and a predetermined reference current; a calculator for calculating reactive power to be generated by the DC arc furnace, from the detected DC current, the determined phase control angle, and a no-load DC voltage; a compensator including a reactive load connected via thyristor to the power system; and a controller for controlling the phase control angle of the thyristor of the compensator in accordance with the calculated reactive power, for controlling a current flowing across the reactive load, and for permitting the compensator to generate such reactive power as to co

Abstract: A device for processing optical data comprising:an optical waveguide formed on a substrate,a light source for the laser beam to be admitted into the waveguide,lens means provided on the waveguide for causing the beam propagating through the waveguide to emerge obliquely upward and focusing the emergent beam two-dimensionally,means for receiving the beam reflected obliquely from above,a base provided with the laser light source, the substrate and the light receiving means,a focusing drive mechanism for adjusting the position of the base upward or downward, anda tracking drive mechanism for adjusting the position of the base laterally.

Abstract: A copper base alloy exhibits improved wear resistance particularly at elevated temperatures, which consists essentially of, in percent by weight, 10-40% of Ni, 1-7% of Si, 0.5-5% of B, 1-20% of Cr, and the balance of Cu, wherein particles of at least one of chromium boride and chromium silicide having a size of about 0.1 to about 50 .mu.m are evenly dispersed in a copper-nickel base matrix. The alloy may further contain W, Mo or Fe and/or a high-melting carbide such as WC and TaC.

Abstract: Zinciferous surfaces, particularly those of galvanized steel, may be effectively coated with an adherent corrosion resistant black layer of fine metal particles by contacting the surfaces with an aqueous solution containing (A) at least 0.5 g/L of the treatment solution of Ni.sup.2+ and/or Co.sup.2+ ions; and (B) an amount, sufficient to complex all the ions of component (A), of a weak complexing component selected from the group consisting of ammonia, saturated aliphatic compounds having at least two amino groups of which at least one is a primary amino group, and/or amino acids; and, optionally but preferably, (C) at least 50 parts per million ("ppm") by weight of a component selected from the group consisting of nitrite ions, nitrate ions, carbonate ions, thiocyanate ions, thiosulfate ions, thiourea, hypophosphite ions, phosphite ions, and/or perchlorate ions.

Abstract: Herein disclosed, as a Ni-based corrosion-resistant alloy to be used for build-up welding, is an alloy which contains 0.5 to 2.3 wt % of copper, 0.1 to 5.3 wt % of molybdenum, 1.0 to 29.0 wt % of at least one carbide forming element except molybdenum, 1.0 to 30.0 wt % of iron, 0.6 to 2.5 wt % of silicon, 0.008 up to 1.0 wt % of boron, and 0.04 to 1.6 wt % of carbon, the remainder being composed of nickel and incidental impurities.

Abstract: A dispersion strengthened Cu (copper)-base alloy for a wear-resistant overlay formed on a metal substrate consists essentially of, by weight %,Ni: 5 to 30%;B: 0.5 to 3%;Si: 1 to 5%;Fe: 4 to 30%;Sn: 3 to 15% and/or An: 3 to 30%; andthe remainder being Cu and unavoidable impurities, and has a structure in which particles of boride and silicide of the Fe-Ni system are dispersed in a Cu-base matrix, and Cu-base primary crystals contain Sn and/or Zn in a solid solution state. If necessary, 0.1 to 5% of Al, 0.1 to 5% of Ti, and/or 1 to 10% of Mn may be added. 0.02 to 2% of C, and 0.1 to 10% of Cr and/or 0.3 to 5% of Ti may be further added. Instead of or along with Sn and/or Zn, 2 to 20% of Pb can be used, and nonsoluble Pb particles are uniformly dispersed between Cu-base .alpha. phase dendrites and serve as a solid lubricant.

Abstract: Zinc and zinc alloy surfaces can be given an effective corrosion inhibiting treatment by contact for less than a minute with an alkaline aqueous solution having a pH not more than 11 and containing at least 0.020 g/L of dissolved nickel ions and sufficient ammonia to give a molar ratio of ammonia to nickel ion of at least 6. If the concentration of nickel ions in the treating solution is at least 1.0 g/L, a durable blackening of the surface is also produced. Both the corrosion resistance and the quality of the blackening can usually be further improved by subsequent conventional phosphate conversion coating.

Abstract: Disclosed is a Zn-based composite-plated metallic material, comprising a plating layer on a metal substrate. The plating layer consists essentially of (1) Zn or as Zn alloy electroplated onto a metallic substrate and (2) the cathodic precipitation reaction product of aluminum, calcium, magnesium, strontium, titanium, zirconium, molybdenum, and/or tungsten. The latter metal constitutes 0.002 to 10% by weight of the plating layer. The cathodic precipitation-reaction product may be hydroxide, hydroxide hydrate or a phosphate.

Abstract: A corrosion-resistant phosphate chemical conversion coating layer is formed on a steel material surface by a process comprising bringing the steel material into contact with a treatment liquid containing mixed anions consisting of phosphate ions and at least one other type of active anions, at least one type of metal ions, and an oxidizing agent, to provide a phosphate chemical conversion coating layer on the surface of the steel material, wherein the ratio (P/An) in weight of the phosphate ions (P) to the total of mixed anions (An) is 1/2 or less and the temperature of the treatment liquid is maintained at a level of 40.degree. C. or less without external heating.

Abstract: Herein disclosed is a process for forming a dispersion alloy layer on a metallic base. The powder of an alloy system, which will separate into two or more multi-liquid phases at a temperature equal to or higher than its melting point and will solidify, when quenched, with its individual liquid phases being separate and in which the ratio of the minimum to the maximum specific weight its individual liquid phases is 0.3 or higher, such as the powder of any alloy system of Cu-Ni(15%)-Fe(8%)-Si(3%)-B(1.5%) is applied to a metallic base. The powder thus applied is then melting and agitated while being irradiated with a laser beam oscillated. The agitated melt of the powder is then quenched to solidify with the movement of the laser beam thereby to form on the metallic base the dispersion alloy layer in which the solid particles of at least one of those phase such as silicide particles are dispersed in the matrix of the remaining one of the phases.

Abstract: Herein disclosed is a dispersion strengthened copper-base alloy having an excellent wear resistance, which alloy contains 5 to 30% (in weight) of nickel, 1 to 5% of silicon, 0.5 to 3% of boron and 4 to 30% of iron, the remainder being copper and unavoidable impurities, and having a structure in which hard particles composed chiefly of a silicide of iron-nickel system are dispersed in a copper-base matrix. The copper-base alloy is suitably cladded (or deposited) locally on a metallic base. The alloy may contain at least one of 0.1 to 5% of aluminum, 0.1 to 5% of Ti and 1 to 10% of Mn, if necessary, in addition to the above specified components. If necessary, 0.02 to 2% of carbon and 0.5 to 10% of chromium and/or 0.3 to 5% of titanium may be further added. Then, the structure is modified such that both the particles composed chiefly of the iron-nickel silicide and carbide particles are coexistently dispersed in the copper-base matrix.

Abstract: In an engine valve comprising a valve body of an iron base material, a Stellite or similar alloy is clad on the body using a laser beam with a sufficient energy to form a cladding layer as a valve face such that the iron from the body-forming iron base material is diffused into the cladding layer throughout its thickness through an interface layer between the cladding layer and the valve body, whereby the cladding layer has 5 to 15 wt % of iron diffused and the interface layer has an iron content continuously decreasing from the iron content of the body-forming iron base material to that of the cladding layer.

Abstract: A two-dimensional light beam deflector for deflecting a light beam by a first deflector in a direction parallel to the plane of a thin film optical waveguide formed on a substrate, and also for deflecting the light beam, already deflected once by said first deflector, in a direction perpendicular to the plane of said thin film optical waveguide by a second deflector.

Abstract: A photo-pickup wherein a light emitting portion, a surface acoustic wave generating portion, a lens portion, a light receiving portion and a control portion are integrally integrated on a base plate formed on its surface with a light transmission path. The light emitting portion propagates a light beam to the light transmission path. The light beam propagating in the light transmission path is first deflected within a plane of the light transmission path by surface acoustic wave propagating on the light transmission path and propagated towards the lens portion. The lens portion is provided to project the light beram outside from the light transmission path and effect two-dimentional focusing of the projected beam and adjustment of focal position. The light receiving portion comprises a combination of a plurality of light receiving elements disposed at suitable intervals from the projected position of the light beam to receive a reflected light of the light beam.

Abstract: In this method for forming an alloy layer on the surface of an aluminum alloy substrate, a powder for alloying, containing a substance to be alloyed with the substrate and an element selected from the group consisting of silicon and bismuth, is disposed upon the surface of the aluminum alloy substrate. This powder is then irradiated with a CO.sub.2 laser, so as to be melted and fused together with a surface portion of the aluminum alloy substrate, so that these two are alloyed together. The powder for alloying may be a powder of an alloy of the substance to be alloyed with the aluminum alloy substrate and the element selected from the group consisting of silicon and bismuth, or alternatively may be a mixture of a powder of the substance to be alloyed with the aluminum alloy substrate and a powder of the element selected from the group consisting of silicon and bismuth.