Abstract: A substrate (1) has a surface covered with an insulation layer (2), on which an active layer (3') made of non-single crystal silicon through thin film technique is provided. A gate electrode layer (5') is partially provided on said active layer through a gate insulation layer (4'). Said active layer (3') is subject to injection of P-type or N-type impurities to provide an image sensor of MOS structure. Bias potential is applied to a gate electrode so that a circuit between a source and a drain is in an On state, so that input light through said substrate or said gate electrode is applied to said active layer, and electrical output depending upon said input light is obtained from said source electrode or said drain electrode. Other MOS transistors for switching element and/or shift registers for operating said image sensor are provided on said substrate (1).

Abstract: A MOS-FET transistor is produced on a substrate made of glass which has a non single crystal semiconductor film (2'). The average diameter of a crystal grain in said film is in the range between 0.5 times and 4 times of thickness of said film, and said average diameter is 250 .ANG.-8000 .ANG., and said film thickness is 500 .ANG.-2000 .ANG.. The density of oxygen in the semiconductor film (2') is less than 2.times.10.sup.19 /cm.sup.3. A photo sensor having PIN structure is also produced on the substrate, to provide an image sensor for a facsimile transmitter together with the transistors. Said film (2') is produced by placing amorphous silicon film on the glass substrate through CVD process using disilane gas, and effecting solid phase growth to said amorphous silicon film by heating the substrate together with said film in nitrogen gas atmosphere. The film (2') thus produced is subject to implantation of dopant for providing a transistor.

Abstract: A MOS-FET transistor is produced on a substrate made of glass which has a non single crystal semiconductor film (2'). The average diameter of a crystal grain in said film is in the range between 0.5 times and 4 times of thickness of said film, and said average diameter is 250 .ANG.-8000 .ANG. , and said film thickness is 500 .ANG.-2000 .ANG.. The density of oxygen in the semiconductor film (2') is less than 2.times.10.sup.19 /cm.sup.3. A photo sensor having PIN structure is also produced on the substrate, to provide an image sensor for a facsimile transmitter together with the transistors. Said film (2') is produced by placing amorphous silicon film on the glass substrate through CVD process using disilane gas, and effecting solid phase growth to said amorphous silicon film by heating the substrate together with said film in nitrogen gas atmosphere. The film (2') thus produced is subject to implantation of dopant for providing a transistor.