Abstract: A positive electrode active material for lithium secondary batteries which is able to doped/undoped with lithium ions and contains at least Ni, in which a ratio P/Q (atom %/mass %) of a concentration P (atom %) of sulfur atoms being present in a surface of the positive electrode active material to a concentration Q (mass %) of sulfuric acid radicals being present in the whole positive electrode active material is more than 0.8 and less than 5.0, and the Q (mass %) is 0.01 or more and 2.0 or less.

Abstract: Provided are a transition metal mixed hydroxide comprising an alkali metal other than Li, SO4 and a transition metal element, wherein the molar ratio of the molar content of the alkali metal to the molar content of the SO4 is not less than 0.05 and less than 2, and a lithium mixed metal oxide obtained by calcining a mixture of the transition metal mixed hydroxide and a lithium compound by maintaining the mixture at a temperature of 650 to 1000° C.

Abstract: The present invention provides a method of producing a lithium mixed metal oxide, a lithium mixed metal oxide and a nonaqueous electrolyte secondary battery. The method includes a step of calcining a mixture of one or more compounds of M wherein M is one or more elements selected from the group consisting of nickel, cobalt and manganese, and a lithium compound, in the presence of one or more inactive fluxes selected from the group consisting of a fluoride of A, a chloride of A, a carbonate of A, a sulfate of A, a nitrate of A, a phosphate of A, a hydroxide of A, a molybdate of A and a tungstate of A, wherein A is one or more elements selected from the group consisting of Na, K, Rb, Cs, Ca, Mg, Sr and Ba. The lithium mixed metal oxide contains nickel, cobalt and manganese, has a BET specific surface area of from 3 m2/g to 15 m2/g, and has an average particle diameter within a range of 0.1 ?m or more to less than 1 ?m, the diameter determined by a laser diffraction scattering method.

Abstract: An antimicrobial peptide LL-37 has an action to promote expression of a nerve repulsion factor Sema3A. LL-37 is a peptide composed of the C-terminal 37 residues of human cathelicidin hCAP18. Use of this antimicrobial peptide enables normalization of expression of axon guidance molecules such as nerve repulsion factor in lesions of pruritic dermatoses including atopic dermatitis and xeroderma, and thus enables alleviation of pruritus and amelioration of skin lesions.

Abstract: A positive electrode active material, which has a crystallite size ?/crystallite size ? ratio (?/?) of 1 to 1.75 or less, wherein the crystallite size ? is within a peak region of 2?=18.7±1° and the crystallite size ? is within a peak region of 2?=44.6±1°, each determined by a powder X-ray diffraction measurement using Cu-K? ray, and has a composition represented by formula (I) below: Li[Lix(NiaCobMncMd)1-x]O2??(I) wherein 0?x?0.2, 0.3<a<0.7, 0<b<0.4, 0<c<0.4, 0?d<0.1, a+b+c+d=1, and M is at least one metal selected from the group consisting of Fe, Cr, Ti, Mg, Al and Zr.

Abstract: The object of the present invention is to provide a positive electrode active material usable for a lithium ion battery capable of high charge/discharge cycle performance and high discharge capacity. The positive electrode active material for a lithium secondary battery has a layered structure and comprises at least nickel, cobalt and manganese. Further, the positive electrode active material satisfies requirements (1) to (3) below: (1) a primary particle size of 0.1 ?m to 1 ?m, and a 50% cumulative particle size D50 of 1 ?m to 10 ?m, (2) a ratio (D90/D10) of volume-based 90% cumulative particle size D50 to volume-based 10% cumulative particle size D10 of 2 to 6, and (3) a lithium carbonate content in a residual alkali on particle surfaces of 0.1% by mass to 0.8% by mass as measured by neutralization titration.

Abstract: A lithium composite metal oxide that contains Li, Ni, and Mn, has a layered structure, has a diffraction peak in a range of 2?=20.8±1° in a powder X-ray diffraction pattern obtained with powder X-ray diffraction measurement using a Cu-K? radiation, has a BET specific surface area in a range of 6 m2/g to 30 m2/g, and has an average particle diameter measured with a laser diffraction scattering method in a range of 0.1 ?m to 10 ?m.

Abstract: A lithium composite metal oxide that contains Li, Ni, and Mn, has a layered structure, has a diffraction peak in a range of 2?=20.8±1° in a powder X-ray diffraction pattern obtained with powder X-ray diffraction measurement using a Cu—K? radiation, has a BET specific surface area in a range of 6 m2/g to 30 m2/g, and has an average particle diameter measured with a laser diffraction scattering method in a range of 0.1 ?m to 10 ?m.

Abstract: A positive electrode active material for a lithium secondary battery, comprising a lithium-containing composite metal oxide in the form of secondary particles formed by aggregation of primary particles capable of being doped and undoped with lithium ions, each of the secondary particles having on its surface a coating layer, the positive electrode active material satisfying the following requirements (1) to (3): (1) the metal oxide has an ?-NaFeO2 type crystal structure of following formula (A): Lia(NibCocM11-b-c)O2??(A) wherein 0.9?a?1.2, 0.9?b<1, 0<c?0.1, 0.9<b+c?1, and M1 represents at least one optional metal selected from Mg, Al, Ca, Sc, Ti, V, Cr, Mn, Fe, Cu, Zn, Ga, Ge, Sr, Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, In and Sn; (2) the coating layer comprises Li and M2, wherein M2 represents at least one optional metal selected from Al, Ti, Zr and W; and (3) the active material has an average secondary particle diameter of 2 to 20 ?m, a BET specific surface area of 0.1 to 2.

Abstract: Provided is a positive electrode active material which is useful for a lithium secondary battery having a battery resistance lower than that of the conventional positive electrode active material below freezing point. The positive electrode active material for a lithium secondary battery contains at least one element selected from a group consisting of nickel, cobalt and manganese, the positive electrode active material having a layered structure and satisfying all of the following requirements (1) to (3): (1) a primary particle size is 0.1 ?m to 1 ?m and a secondary particle size is 1 ?m to 10 ?m; (2) in an X-ray powder diffraction measurement using CuK? radiation, a crystallite size in the peak within 2?=18.7±1° is 100 ? to 1200 ? and a crystallite size in the peak within 2?=44.6±1° is 100 ? to 700 ?; and (3) in a pore distribution obtained by a mercury intrusion method, a pore peak exists in a range where the pore size is 10 nm to 200 nm and a pore volume in the said range is 0.01 cm3/g to 0.05 cm3/g.

Abstract: Provided are a transition metal mixed hydroxide comprising an alkali metal other than Li, SO4 and a transition metal element, wherein the molar ratio of the molar content of the alkali metal to the molar content of the SO4 is not less than 0.05 and less than 2, and a lithium mixed metal oxide obtained by calcining a mixture of the transition metal mixed hydroxide and a lithium compound by maintaining the mixture at a temperature of 650 to 1000° C.

Abstract: Provided are a transition metal mixed hydroxide comprising an alkali metal other than Li, SO4 and a transition metal element, wherein the molar ratio of the molar content of the alkali metal to the molar content of the SO4 is not less than 0.05 and less than 2, and a lithium mixed metal oxide obtained by calcining a mixture of the transition metal mixed hydroxide and a lithium compound by maintaining the mixture at a temperature of 650 to 1000° C.

Abstract: The present invention provides a positive electrode active material. The positive electrode active material is represented by the following formula (I) and has a BET specific surface area of larger than 5 m2/g and not larger than 15 m2/g: LixM1yM31-yO2??(I) wherein M1 is at least one transition metal element selected from Group 5 elements and Group 6 elements of the Periodic Table, M3 is at least one transition metal element other than M1 and selected from among transition metal elements excluding Fe, x is not less than 0.9 and not more than 1.3, and y is more than 0 and less than 1.

Abstract: The present invention provides a positive electrode active material. The positive electrode active material is represented by the following formula (I) and has a BET specific surface area of larger than 5 m2/g and not larger than 15 m2/g: LixM1yM31-yO2??(I) wherein M1 is at least one transition metal element selected from Group 5 elements and Group 6 elements of the Periodic Table, M3 is at least one transition metal element other than M1 and selected from among transition metal elements excluding Fe, x is not less than 0.9 and not more than 1.3, and y is more than 0 and less than 1.

Abstract: A lithium mixed metal oxide, shown by the following formula (A): Lix(Mn1?y?z?dNiyFezMd)O2??(A) wherein M is one or more elements selected from the group consisting of Al, Mg, Ti, Ca, Cu, Zn, Co, Cr, Mo, Si, Sn, Nb and V; x is 0.9 or more and 1.3 or less; y is 0.3 or more and 0.7 or less; z is more than 0 and 0.1 or less, and d is more than 0 and 0.1 or less. A positive electrode active material, including the lithium mixed metal oxide. A positive electrode, including the positive electrode active material. A nonaqueous electrolyte secondary battery, including the positive electrode.

Abstract: The present invention provides a lithium mixed metal oxide, an electrode and a nonaqueous electrolyte secondary battery. The lithium mixed metal oxide is represented by the following formula (A): Lix(Mn1?(y+z)NiyFez)O2??(A) wherein x is not less than 0.9 and not more than 1.3, y is more than 0.5 and not more than 0.7, and z is more than 0 and not more than 0.1.

Abstract: A lithium composite metal oxide that contains Li, Ni, and Mn, has a layered structure, has a diffraction peak in a range of 2?=20.8±1° in a powder X-ray diffraction pattern obtained with powder X-ray diffraction measurement using a Cu—K? radiation, has a BET specific surface area in a range of 6 m2/g to 30 m2/g, and has an average particle diameter measured with a laser diffraction scattering method in a range of 0.1 ?m to 10 ?m.

Abstract: The present invention provides a positive electrode active material. The positive electrode active material is represented by the following formula (I) and has a BET specific surface area of larger than 5 m2/g and not larger than 15 m2/g: LixM1yM31-yO2??(I) wherein M1 is at least one transition metal element selected from Group 5 elements and Group 6 elements of the Periodic Table, M3 is at least one transition metal element other than M1 and selected from among transition metal elements excluding Fe, x is not less than 0.9 and not more than 1.3, and y is more than 0 and less than 1.

Abstract: The present invention provides a non-aqueous electrolyte secondary battery capable of exhibiting high discharge capacity maintenance rate at a high current rate, a lithium composite metal oxide useful therefor, and a method for producing the lithium composite metal oxide. This lithium composite metal oxide comprises Ni, Mn, Co, and Fe, and the BET specific surface area thereof is 3 m2/g to 15 m2/g. According to the present invention, a non-aqueous electrolyte secondary battery which exhibits high discharge capacity maintenance rate at a high current rate compared to a conventional lithium secondary battery can be obtained, and thus the secondary battery is very useful especially for applications where high discharge capacity maintenance rate at a high current rate is required, that is, non-aqueous electrolyte secondary batteries for automobiles or for power tools such as electric tools.

Abstract: Provided are a transition metal mixed hydroxide comprising an alkali metal other than Li, SO4 and a transition metal element, wherein the molar ratio of the molar content of the alkali metal to the molar content of the SO4 is not less than 0.05 and less than 2, and a lithium mixed metal oxide obtained by calcining a mixture of the transition metal mixed hydroxide and a lithium compound by maintaining the mixture at a temperature of 650 to 100000.