Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, PCD includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteads (“Oe”) or more and a specific magnetic saturation of about 15 Gauss·cm3/grams (“G·cm3/g”) or less. Other embodiments are directed to polycrystalline diamond compacts (“PDCs”) employing such PCD, methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.

Abstract: Embodiments of the invention relate to methods of fabricating polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding by carbon pumping, and PCD and polycrystalline diamond compacts formed by such methods. In an embodiment of a method of fabricating PCD, a plurality of diamond crystals and a metal-solvent catalyst may be provided. The diamond crystals and metal-solvent catalyst may be subjected to a first pressure-temperature condition during which carbon is dissolved in the metal-solvent catalyst. After subjecting the diamond crystals and metal-solvent catalyst to the first pressure-temperature condition, the diamond crystals and metal-solvent catalyst may be subjected to a second pressure-temperature condition at which diamond is stable.

Abstract: One aspect of the instant disclosure relates to a subterranean drilling assembly comprising a subterranean drill bit and a sub apparatus coupled to the drill bit. Further, the sub apparatus may include at least one cooling system configured to cool at least a portion of the drill bit. For example, the sub apparatus may include at least one cooling system comprising a plurality of refrigeration coils or at least one thermoelectric device. In another embodiment a subterranean drill bit may include at least one cooling system positioned at least partially within the subterranean drill bit. Also, a sub apparatus or subterranean drill bit may be configured to cool drilling fluid communicated through at least one bore of a subterranean drill bit and avoiding cooling drilling fluid communicated through at least another bore of the subterranean drill bit. Methods of operating a subterranean drill bit are disclosed.

Abstract: Embodiments relate to methods of manufacturing polycrystalline diamond compacts (“PDCs”). In an embodiment, a method of fabricating a PDC includes positioning a plurality of diamond particles adjacent to a cemented carbide material. The cemented carbide material includes one or more types of tungsten-containing eta phases. The method further includes subjecting the plurality of diamond particles and the cemented carbide material to a high-pressure/high-temperature process effective to sinter the plurality of diamond particles so that a polycrystalline diamond table is formed without tungsten carbide grains of the cemented carbide material exhibiting abnormal grain growth that project into the polycrystalline diamond table.

Abstract: Embodiments relate to methods of fabricating PCD materials by subjecting a mixture that exhibits a broad diamond particle size distribution to an HPHT process, PCD materials so-formed, and PDCs including a polycrystalline diamond table comprising such PCD materials. In an embodiment, a PCD material includes a plurality of bonded diamond grains that exhibit a substantially unimodal diamond grain size distribution characterized, at least in part, by a parameter ? that is less than about 1.0. ? = x 6 · ? , where x is the average grain size of the substantially unimodal diamond grain size distribution, and ? is the standard deviation of the substantially unimodal diamond grain size distribution.

Abstract: In an embodiment, a polycrystalline diamond compact (“PDC”) comprises a cemented carbide substrate including a first cemented carbide portion and a second cemented carbide portion bonded to the first cemented carbide portion and exhibiting an erosion resistance that is greater than the first cemented carbide portion. The PDC further comprises a polycrystalline diamond (“PCD”) table bonded to the first cemented carbide portion. The PCD table includes a plurality of bonded diamond grains exhibiting diamond-to-diamond bonding therebetween, with the plurality of bonded diamond grains defining a plurality of interstitial regions.

Abstract: Embodiments relate to polycrystalline diamond compacts (“PDCs”) including a polycrystalline diamond (“PCD”) table that is substantially free of defects formed due to abnormal grain growth of tungsten carbide grains, and methods of fabricating such PDCs. In an embodiment, a PDC comprises a cemented tungsten carbide substrate including an interfacial surface that is substantially free of tungsten carbide grains exhibiting abnormal grain growth, and a PCD table bonded to the interfacial surface of the cemented tungsten carbide substrate. The PCD table includes a plurality of bonded diamond grains defining a plurality of interstitial regions. At least a portion of the interstitial regions includes a metal-solvent catalyst disposed therein. The PCD table may be substantially free of chromium or the PCD table and the cemented tungsten carbide substrate may each include chromium.

Abstract: A polycrystalline diamond compact useful for wear, cutting, drilling, drawing and like applications is provided with a first diamond region remote from the working surface which has a metallic catalyzing material and a second diamond region adjacent to or including the working surface containing a non-metallic catalyst and the method of making such a compact is provided. This compact is particularly useful in high temperature operations, such as hard rock drilling because of the improved thermal stability at the working surface.

Abstract: Embodiments relate to methods of fabricating PCD materials by subjecting a mixture that exhibits a broad diamond particle size distribution to a HPHT process, PCD materials so-formed, and PDCs including a polycrystalline diamond table comprising such PCD materials. In an embodiment, a method includes subjecting a mixture to heat and pressure sufficient to form a PCD material. The mixture comprises a plurality of diamond particles exhibiting a diamond particle size distribution characterized, in part, by a parameter ? that is less than about 1.0, where ? = x 6 · ? , x is the average particle size of the diamond particle size distribution, and ? is the standard deviation of the diamond particle size distribution.

Abstract: Embodiments relate to superabrasive compacts including a diamond-silicon carbide composite table, and methods of fabricating such superabrasive compacts. In an embodiment, a method of fabricating a superabrasive compact is disclosed. An assembly comprising a mixture including diamond particles and silicon is formed. The silicon comprises amorphous silicon, crystalline silicon crystallized from amorphous silicon formed by a milling process, or combinations thereof. A substrate is positioned in proximity to the mixture. The assembly is subjected to a high-pressure/high-temperature process to form a superabrasive compact comprising a superabrasive table bonded to the substrate. The superabrasive table comprises diamond-silicon carbide composite including diamond grains dispersed through a matrix of silicon carbide grains.

Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, PCD includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteads (“Oe”) or more and a specific magnetic saturation of about 15 Gauss·cm3/grams (“G·cm3/g”) or less. Other embodiments are directed to polycrystalline diamond compacts (“PDCs”) employing such PCD, methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.

Abstract: Embodiments of the present invention relate to diamond-silicon carbide composites, superabrasive compacts including such diamond-silicon carbide composites, and methods of fabricating such diamond-silicon carbide composites and superabrasive compacts. In one embodiment, a superabrasive compact includes a substrate and a superabrasive table bonded to the substrate. The superabrasive table comprises diamond-silicon carbide composite including a matrix comprising nanometer-sized silicon carbide grains and micrometer-sized diamond grains dispersed through the matrix. In another embodiment, a method of fabricating a superabrasive compact is disclosed. An assembly comprising a mixture including diamond particles and silicon is formed. The silicon comprises amorphous silicon, crystalline silicon crystallized from amorphous silicon formed by a milling process, or combinations thereof. A substrate is positioned in proximity to the mixture.

Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, PCD includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteads or more and a specific magnetic saturation of about 15 Gauss·cm3/grams or less. Other embodiments are directed to polycrystalline diamond compacts (“PDCs”) employing such PCD, methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.

Abstract: Superabrasive compacts, methods of fabricating such compacts, and drilling tools that may utilize such compacts are disclosed. In one aspect of the present invention, a superabrasive compact includes a substrate and a superabrasive table attached to the substrate. At least one constituent of the superabrasive table exhibits a substantially monotonic distribution of size, concentration, or both in a selected direction of the superabrasive table. In another aspect of the present invention, a method of fabricating a superabrasive article is disclosed. A plurality of particles may be provided that exhibit a substantially monotonic distribution of particle size, concentration, or both in a selected direction. The particles may be subjected to a high-temperature, high-pressure process to consolidate and form a self-supporting body.

Abstract: A polycrystalline diamond compact useful for wear, cutting, drilling, drawing and like applications is provided with a first diamond region remote from the working surface which has a metallic catalyzing material and a second diamond region adjacent to or including the working surface containing a non-metallic catalyst and the method of making such a compact is provided. This compact is particularly useful in high temperature operations, such as hard rock drilling because of the improved thermal stability at the working surface.

Abstract: In an embodiment, a polycrystalline diamond compact (“PDC”) comprises a cemented carbide substrate including a first cemented carbide portion exhibiting a first concentration of chromium carbide and a second cemented carbide portion bonded to the first cemented carbide portion and exhibiting a second concentration of chromium carbide that is greater than the first concentration. The PDC further comprises a polycrystalline diamond (“PCD”) table bonded to the first cemented carbide portion. The PCD table includes a plurality of bonded diamond grains exhibiting diamond-to-diamond bonding therebetween, with the plurality of bonded diamond grains defining a plurality of interstitial regions. The PCD table includes chromium present in a concentration less than about 0.25 weight %.

Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, polycrystalline diamond compact (“PDC”) includes a PCD table having a maximum thickness. At least a portion of the PCD table includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteds (“Oe”) or more and a specific magnetic saturation of about 15 Gauss·cm3/grams (“G·cm3/g”) or less. The PDC includes a substrate having an interfacial surface that is bonded to the PCD table. The interfacial surface exhibits a substantially planar topography. Other embodiments are directed to methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.

Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, PCD includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteads (“Oe”) or more and a specific magnetic saturation of about 15 Gauss·cm3/grams (“G·cm3/g”) or less. Other embodiments are directed to polycrystalline diamond compacts (“PDCs”) employing such PCD, methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.

Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, PCD includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteads (“Oe”) or more and a specific magnetic saturation of about 15 Gauss·cm3/grams (“G·cm3/g”) or less. Other embodiments are directed to polycrystalline diamond compacts (“PDCs”) employing such PCD, methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.

Abstract: Embodiments of the invention relate to polycrystalline diamond (“PCD”) exhibiting enhanced diamond-to-diamond bonding. In an embodiment, PCD includes a plurality of diamond grains defining a plurality of interstitial regions. A metal-solvent catalyst occupies at least a portion of the plurality of interstitial regions. The plurality of diamond grains and the metal-solvent catalyst collectively exhibit a coercivity of about 115 Oersteads (“Oe”) or more and a specific magnetic saturation of about 15 Gauss·cm3/grams (“G·cm3/g”) or less. Other embodiments are directed to polycrystalline diamond compacts (“PDCs”) employing such PCD, methods of forming PCD and PDCs, and various applications for such PCD and PDCs in rotary drill bits, bearing apparatuses, and wire-drawing dies.