Abstract: A method of producing a uniform silica glass block comprising using silica powder as a raw material, and treating it at high temperature and pressure by a hot press and/or a hot isostatic press in vacuum or in an inert gas atmosphere, preferably with a capsule of silica glass or a high-melting point metal. By conducting calcination in fluorine, chlorine or their compound gas and then in oxygen, the OH group content of the silica glass can be reduced dramatically.

Abstract: A ceramic orthodontic bracket having an unobtrusive color, is obtained by sintering a molded body of a powdery mixture composed of 2-15 mole % of yttrium oxide, 5-20 mole % of titanium dioxide and the balance of zirconia.

Abstract: A zirconia type sintered body consisting essentially of 50 to 98% by weight of zirconia (ZrO.sub.2) containing 1.5 to 5 mole % of yttria (Y.sub.2 O.sub.3) and 50 to 2% by weight of alumina (Al.sub.2 O.sub.3), spinal (MgAl.sub.2 O.sub.4) or mullite (3Al.sub.2 O.sub.3.2SiO.sub.2), and having a three-point bending strength of at least 1700 MPa is provided. This sintered body is prepared by a process wherein a powdery composition consisting essentially of 50 to 98% by weight of (a1) a powder of zirconia containing 1.5 to 5 mole % of yttria or (a2) a mixture comprising 1.5 to 5 mole % of yttria powder and 95 to 98.5 mole % of a zirconia powder and 2 to 50% by weight of (b) a powder of an alumina type oxide selected from alumina, and alumina-magnesia type oxide, an alumina-silica type oxide, a mixture of alumina and magnesia and a mixture of alumina and silica is subjected to a hot isotactic pressing treatment under a pressure of at least 50 MPa at temperature of 1300.degree. C. to 1700.degree. C.

Abstract: A zirconia sintered body comprising zirconia (ZrO.sub.2), yttria (Y.sub.2 O.sub.3) and titania (TiO.sub.2) [Y.sub.2 O.sub.3 /ZrO.sub.2 =at least 2/98 by mole and TiO.sub.2 /(ZrO.sub.2 +Y.sub.2 O.sub.3)=3/97 to 20/80 by mole] has a high translucence giving improved light transmittance. A zirconia sintered body comprising, in addition to ZrO.sub.2, Y.sub.2 O.sub.3 and TiO.sub.2, 0.1 to 3 mole % of an oxide of a rare earth element of the lanthanum group has a fluorescence-radiating property as well as a high translucence.

Abstract: A sintered product of zirconia comprising ZrO.sub.2 and CeO.sub.2 in a molar ratio of CeO.sub.2 /ZrO.sub.2 of 8/92-30/70, and consisting of a crystal phase which is a mixed phase consisting essentially of a tetragonal phase and a cubic phase, or which is a phase consisting essentially of a tetragonal phase, has a high mechanical strength and a high rupture toughness, and is applicable as the constituting materials of tools for machining and cutting, various kinds of dies and nozzles, parts for sliding and other industrial materials.

Abstract: A high strength metal working tool such as cutting tools and dies made of a zirconia-base sintered material comprising 50 to 98 weight percent of zirconia (ZrO.sub.2) containing 1.5 to 5 mol percent of yttira (Y.sub.2 O.sub.3) and 50 to 2 weight percent of alumina (Al.sub.2 O.sub.3) and/or spinel (MgAl.sub.2 O.sub.4) and having a three point bending strength of not less than 1700 MPa.

Abstract: A zirconia type sintered body consisting essentially of 50 to 98% by weight of zirconia (ZrO.sub.2) containing 1.5 to 5 mole % of yttria (Y.sub.2 O.sub.3) and 50 to 2% by weight of alumina (Al.sub.2 O.sub.3), spinal (MgAl.sub.2 O.sub.4) or mullite (3Al.sub.2 O.sub.3.2SiO.sub.2), and having a three-point bending strength of at least 1700 MPa is provided. This sintered body is prepared by a process wherein a powdery composition consisting essentially of 50 to 98% by weight of (a1) a powder of zirconia containing 1.5 to 5 mole % of yttria or (a2) a mixture comprising 1.5 to 5 mole % of a yttria powder and 95 to 98.5 mole % of a zirconia powder and 2 to 50% by weight of (b) a powder of an alumina type oxide selected from alumina, an alumina-magnesia type oxide, an alumina-silica type oxide, a mixture of alumina and magnesia and a mixture of alumina and silica is subjected to a hot isotactic pressing treatment under a pressure of at lesast 50 MPa at temperature of 1300.degree. C. to 1700.degree. C.