Abstract: A magnetic ink composition for three-dimensional (3D) printing a bonded magnet is provided. The magnetic ink composition includes magnetic particles, a polymer binder and a solvent. A 3D printing method for fabrication of a bonded magnet using the magnetic ink composition is also provided.

Abstract: A method for producing a bonded permanent magnet, comprising: (i) incorporating a solid precursor material comprising a thermoplastic crosslinkable polymer and magnetic particles into an additive manufacturing device, wherein the crosslinkable polymer has a delayed crosslinking ability; (ii) melting the precursor material by heating it to a temperature of at least and no more than 10° C. above its glass transition temperature; (iii) extruding the melt through the additive manufacturing device and, as the extrudate exits from the nozzle and is deposited on a substrate as a solidified preform of a desired shape, exposing the resultant extrudate to a directional magnetic field of sufficient strength to align the magnetic particles; and (iv) curing the solidified preform by subjecting it to conditions that result in crosslinking of the thermoplastic crosslinkable polymer to convert it to a crosslinked thermoset. The resulting bonded permanent magnet and articles made thereof are also described.

Abstract: Compositions and methods of making compositions are provided for nitride- and/or oxide-modified electrode compositions. In certain embodiments, the nitride- and/or oxide-modified compositions have the general formula M1?zM?zOaF3?xNy. Such compositions may be used as bulk or surface compositions, and used in a battery as the anode or cathode. In other embodiments, the electrode includes a surface coating composition selected from metal nitrides and metal oxides, and a core composition having the formula M1?zM?zOaF3?x, or an oxide fluoride.

Abstract: A method of making a supercapacitor from waste tires, includes the steps of providing rubber pieces and contacting the rubber pieces with a sulfonation bath to produce sulfonated rubber; pyrolyzing the sulfonated rubber to produce a tire-derived carbon composite comprising carbon black embedded in rubber-derived carbon matrix comprising graphitized interface portions; activating the tire-derived carbon composite by contacting the tire-derived carbon composite with a specific surface area-increasing composition to increase the specific surface area of the carbon composite to provide an activated tire-derived carbon composite; and, mixing the activated tire-derived carbon composite with a monomer and polymerizing the monomer to produce a redox-active polymer coated, activated tire-derived carbon composite. The redox-active polymer coated, activated tire-derived carbon composite can be formed into a film. An electrode and a supercapacitor are also disclosed.

Abstract: Compositions and methods of making are provided for coated electrodes and batteries comprising the same. The compositions may comprise a base composition having an active material selected from the group consisting of LiCoO2, LiMn2O4, Li2MnO3, LiNiO2, LiMn1.5Ni0.5O4, LiFePO4, Li2FePO4F, Li3CoNiMnO6, Li(LiaNixMnyCoz)O2, and mixtures thereof. The compositions may also comprise a coating composition that covers at least a portion of the base composition, wherein the coating composition comprises a non-metal or metalloid element. The methods of making comprise providing the base composition and a doped carbon coating composition, and mixing the coating composition with the base electrode composition at an elevated temperature in a flowing inert gas atmosphere.

Abstract: Compositions and methods of making are provided for a high energy density lithium-aluminum battery. The battery comprises an anode comprising aluminum metal. The battery further comprises a cathode comprising a lithium metal oxide. The battery further comprises an electrolyte capable of supporting reversible deposition and stripping of aluminum at the anode, and reversible intercalation and deintercalation of lithium at the cathode.

Abstract: A method for producing magnet-polymer pellets useful as a feedstock in an additive manufacturing process, comprising: (i) blending thermoplastic polymer and hard magnetic particles; (ii) feeding the blended magnet-polymer mixture into a pre-feed hopper that feeds directly into an inlet of a temperature-controlled barrel extruder; (iii) feeding the blended magnet-polymer mixture into the barrel extruder at a fixed feed rate of 5-20 kg/hour, wherein the temperature at the outlet is at least to no more than 10° C. above a glass transition temperature of the blended magnet-polymer mixture; (iv) feeding the blended magnet-polymer mixture directly into an extruding die; (v) passing the blended magnet-polymer mixture through the extruding die at a fixed speed; and (vi) cutting the magnet-polymer mixture at regular intervals as the mixture exits the extruding die at the fixed speed. The use of the pellets as feed material in an additive manufacturing process is also described.

Abstract: A method for producing a bonded permanent magnet by additive manufacturing, comprising: (i) incorporating components of a solid precursor material into at least one deposition head of at least one multi-axis robotic arm of a big area additive manufacturing (BAAM) system, the components of the solid precursor material comprising a thermoplastic polymer and hard magnetic powder; said deposition head performs melting, compounding, and extruding functions; and said BAAM system has an unbounded open-air build space; and (ii) depositing an extrudate of said solid precursor material layer-by-layer from said deposition head until an object constructed of said extrudate is formed, and allowing the extrudate to cool and harden after each deposition, to produce the bonded permanent magnet. The resulting bonded permanent magnet and articles made thereof are also described.

Abstract: A method of making a supercapacitor from waste tires, includes the steps of providing rubber pieces and contacting the rubber pieces with a sulfonation bath to produce sulfonated rubber; pyrolyzing the sulfonated rubber to produce a tire-derived carbon composite comprising carbon black embedded in rubber-derived carbon matrix comprising graphitized interface portions; activating the tire-derived carbon composite by contacting the tire-derived carbon composite with a specific surface area-increasing composition to increase the specific surface area of the carbon composite to provide an activated tire-derived carbon composite; and, mixing the activated tire-derived carbon composite with a monomer and polymerizing the monomer to produce a redox-active polymer coated, activated tire-derived carbon composite. The redox-active polymer coated, activated tire-derived carbon composite can be formed into a film. An electrode and a supercapacitor are also disclosed.

Abstract: A method of making solid acid catalysts includes the step of sulfonating waste tire pieces in a first sulfonation step. The sulfonated waste tire pieces are pyrolyzed to produce carbon composite pieces having a pore size less than 10 nm. The carbon composite pieces are then ground to produce carbon composite powders having a size less than 50 ?m. The carbon composite particles are sulfonated in a second sulfonation step to produce sulfonated solid acid catalysts. A method of making biofuels and solid acid catalysts are also disclosed.

Abstract: A method of making solid acid catalysts includes the step of sulfonating waste tire pieces in a first sulfonation step. The sulfonated waste tire pieces are pyrolyzed to produce carbon composite pieces having a pore size less than 10 nm. The carbon composite pieces are then ground to produce carbon composite powders having a size less than 50 ?m. The carbon composite particles are sulfonated in a second sulfonation step to produce sulfonated solid acid catalysts. A method of making biofuels and solid acid catalysts are also disclosed.

Abstract: A solid particulate composition useful in extracting a lithium salt from aqueous solutions, the composition comprising lithium, metal atoms, oxygen atoms, and at least one anionic species (X) selected from halide, nitrate, sulfate, carbonate and bicarbonate, all in a framework structure, wherein said metal atoms are selected from at least one of oxophilic main group metal and oxophilic transition metal atoms, provided that, if the metal atoms comprise aluminum atoms, then at least 10 mol % of said aluminum atoms are substituted with at least one metal atom selected from said at least one oxophilic main group and oxophilic transition metal atoms, other than aluminum, and wherein said lithium is present in said composition in an amount less than a saturated amount in order to permit extraction of lithium salt. Methods for extracting and recovering a lithium salt from an aqueous solution by use of the above-described composition are also described.

Abstract: This disclosure relates to methods that include depositing a first component and a second component to form a film including a plurality of nanostructures, and coating the nanostructures with a hydrophobic layer to render the film superhydrophobic. The first component and the second component can be immiscible and phase-separated during the depositing step. The first component and the second component can be independently selected from the group consisting of a metal oxide, a metal nitride, a metal oxynitride, a metal, and combinations thereof. The films can have a thickness greater than or equal to 5 nm; an average surface roughness (Ra) of from 90 to 120 nm, as measured on a 5 ?m×5 ?m area; a surface area of at least 20 m2/g; a contact angle with a drop of water of at least 120 degrees; and can maintain the contact angle when exposed to harsh conditions.

Abstract: An optically transparent, hydrophobic coating, exhibiting an average contact angle of at least 100 degrees with a drop of water. The coating can be produced using low-cost, environmentally friendly components. Methods of preparing and using the optically transparent, hydrophobic coating.

Abstract: A bulk high performance permanent magnet comprising a neodymium-iron-boron core having an outer surface, and a coercivity-enhancing element residing on at least a portion of said outer surface, with an interior portion of said neodymium-iron-boron core not having said coercivity-enhancing element therein. Also described herein is a method for producing the high-coercivity bulk permanent magnet, the method comprising: (i) depositing a coercivity-enhancing element on at least a portion of an outer surface of a neodymium-iron-boron core substrate to form a coated permanent magnet; and (ii) subjecting the coated permanent magnet to a pulse thermal process that heats said outer surface to a substantially higher temperature than an interior portion of said neodymium-iron-boron core substrate, wherein said substantially higher temperature is at least 200° C.

Abstract: Compositions and methods of making are provided for treated mesoporous metal oxide microspheres electrodes. The compositions include microspheres with an average diameter between about 200 nanometers and about 10 micrometers and mesopores on the surface and interior of the microspheres. The methods of making include forming a mesoporous metal oxide microsphere composition and treating the mesoporous metal oxide microspheres by at least annealing in a reducing atmosphere, doping with an aliovalent element, and coating with a coating composition.

Abstract: A carbon-metal oxide composite material comprising: (i) carbon-carbon composite particles in which an amorphous carbon black core is bonded to crystalline graphitic carbon shells; and (ii) a metal oxide material bonded with said carbon-carbon composite particles, wherein said metal oxide material is included in an amount of at least about 10 wt. % by weight of said carbon-carbon composite particles and metal oxide material. Alkali-ion batteries containing the above-described composite as anode are also described. Methods for producing the above-described composite are also described. The method can include, for example, subjecting pulverized rubber tire waste to a sulfonation process and pyrolyzing the sulfonated rubber to produce the carbon-carbon composite particles, as described above, followed by admixing and compounding a metal oxide material with the carbon-carbon composite particles.

Abstract: Compositions and methods of making are provided for a high energy density lithium-alum inum battery. The battery comprises an anode comprising aluminum metal. The battery further comprises a cathode comprising a lithium metal oxide. The battery further comprises an electrolyte capable of supporting reversible deposition and stripping of aluminum at the anode, and reversible intercalation and deintercalation of lithium at the cathode.

Abstract: Compositions and methods of making are provided for mesoporous metal oxide microspheres electrodes. The mesoporous metal oxide microsphere compositions comprise (a) microspheres with an average diameter between 200 nanometers (nm) and 10 micrometers (?m); (b) mesopores on the surface and interior of the microspheres, wherein the mesopores have an average diameter between 1 nm and 50 nm and the microspheres have a surface area between 50 m2/g and 500 m2/g. The methods of making comprise forming composite powders. The methods may also comprise refluxing the composite powders in a basic solution to form an etched powder, washing the etched powder with an acid to form a hydrated metal oxide, and heat-treating the hydrated metal oxide to form mesoporous metal oxide microspheres.

Abstract: A method of making a supercapacitor from waste tires, includes the steps of providing rubber pieces and contacting the rubber pieces with a sulfonation bath to produce sulfonated rubber; pyrolyzing the sulfonated rubber to produce a tire-derived carbon composite comprising carbon black embedded in rubber-derived carbon matrix comprising graphitized interface portions; activating the tire-derived carbon composite by contacting the tire-derived carbon composite with a specific surface area-increasing composition to increase the specific surface area of the carbon composite to provide an activated tire-derived carbon composite; and, mixing the activated tire-derived carbon composite with a monomer and polymerizing the monomer to produce a redox-active polymer coated, activated tire-derived carbon composite. The redox-active polymer coated, activated tire-derived carbon composite can be formed into a film. An electrode and a supercapacitor are also disclosed.