Abstract: The present invention provides a heat-shrinkable polyester film with very good perforation-tear property and also very high productivity. A heat-shrinkable polyester film made of a polyester resin including ethylene terephthalate as a main constituent and containing 15% by mole or more of at least one monomer capable of forming an amorphous component in the whole components of the polyester resin, which exhibits specific heat shrinkage properties and specific mechanical properties after the heat shrinkage.

Abstract: Disclosed is a heat shrinkable polyester film which does not suffer (namely natural shrinkage), is suppressed in decrease of the shrinkage in the main shrinkage direction, and is able to be beautifully and efficiently fitted to a container or the like without changing the temperature conditions for heat shrinkage when the heat shrinkable polyester film is fitted, as a label, to the container or the like by means of heat shrinkage even after high-temperature summer storage in an out door warehouse which has no temperature control system. Specifically disclosed is a heat shrinkable polyester film which is formed from a polyester resin that is mainly composed of ethylene terephthalate and contains 3-12% by mole (inclusive) of one or more monomer components, which can be amorphous components, relative to all the polyester resin components. The heat shrinkable polyester film is characterized in that the shrinkage in 80° C. glycerin, the shrinkage in 130° C.

Abstract: Disclosed is a heat-shrinkable polyester film which, even when stored in an outside warehouse which is not temperature-controlled during a hot summer, does not result in the film shrinking (so-called natural shrinkage); which further has a low decrease in shrinkage rate in the main shrinkage direction, and which can be attached aesthetically and efficiently without changing the temperature conditions for causing heat shrinkage when attaching as a label by heat-shrinking the same to a container (e.g., a plastic bottle). The disclosed heat-shrinkable polyester film comprises a polyester resin having ethylene terephthalate as a main component and containing at least 7 mol % of at least one monomer capable of forming an amorphous component in the whole component of polyester resin. In the heat-shrinkable polyester film, the 80° C.-120° C.

Abstract: The inventive heat-shrinkable polystyrene film is high in shrinkability in the longitudinal direction that is its main shrinkage direction, is excellent in perforated line openability, and has high toughness. The heat-shrinkable polystyrene film is characterized by particular values with respect to hot-water heat shrinkage ratio in the longitudinal and width directions, right angle tear strength in the width direction, and breaking energies in the longitudinal and width directions.

Abstract: A heat-shrinkable polyester film is obtained which is extremely satisfactory in openability along a perforation, has exceedingly high productivity, and is less apt to split in the lengthwise direction in processing, e.g., printing. Provided is a label which is formed from the heat-shrinkable film and is satisfactorily tearable. The label is one formed from a tubular material which comprises as a base a heat-shrinkable film thermally shrinking mainly in the film width direction and which has been cut according to an object to be packaged, both edges in the film width direction having been bonded to each other. The tubular material has been thermally shrunk to constitute the label, with which at least part of the periphery of the object to be packaged is covered. The label has an angle tear strength in the direction perpendicular to the main shrinkage direction (i.e., in the film length direction) of 100-310 N/mm and a tensile break strength in the direction perpendicular to the main shrinkage direction (i.e.

Abstract: Disclosed is a void-containing heat-shrinkable polyester film which is composed of at least two layers, wherein at least one of the layers is a polyester resin layer comprising a cyclic polyolefin resin and containing voids. The film has an apparent specific gravity of less than 1.00 and has specified heat shrinking properties and mechanical properties. Also disclosed is a void-containing heat-shrinkable polyester film as mentioned above, which exhibits specified cuttability along a perforation. Further disclosed is a process for producing a void-containing heat-shrinkable polyester film as mentioned above.

Abstract: There is provided a thermally shrinkable polyester film where the opening ability along the perforation is very good. A thermally shrinkable polyester film comprising polyester resin in which ethylene terephthalate is a main constituting component and not less than 13 molar % of one or more monomer component (s) which can become non-crystalline component is/are contained in the total polyester resin components, wherein the film has specific thermally shrinking characteristics and specific mechanical characteristics after thermal shrinking treatment.

Abstract: A heat-shrinkable white polyester film is provided which has extremely satisfactory cuttability along a perforation and has light-shielding properties. Also provided are: a label; and a process for producing the film with high productivity. The heat-shrinkable white polyester film comprises a polyester resin constituted of ethylene terephthalate as a main constituent component and containing at least 13 mol % one or more monomer ingredients capable of serving as an amorphous component among all components of the polyester resin. This film has specific heat shrinkability, specific light-shielding properties, and specific mechanical properties. The process is excellent in the productivity of the film. The label is obtained from the heat-shrinkable white polyester film.

Abstract: In the heat-shrinkable polyester film of the present invention, the main shrinkage direction is the longitudinal direction. In addition, the hot-water heat shrinkage ratios in the longitudinal direction and the width direction when the film is treated in hot water at 90° C. for 10 seconds, the refractive indexes in the longitudinal direction and the width direction and the natural shrinkage ratio after aging at 40° C. and 65% RH for 700 hours or more are each controlled in predetermined ranges. The heat-shrinkable polyester film of the present invention is manufactured by stretching an unstretched film at a ratio of 2.5 times or more and 6.0 times or less in the width direction at a temperature of Tg+5° C. or more and Tg+40° C. or less, passing the film in an intermediate zone that does not execute an active heating operation, heat-treating the film at a temperature of 100° C. or more and 170° C. or less over a period of 1.0 second or more and 10.

Abstract: A heat-shrinkable polyester film is obtained which is extremely satisfactory in openability along a perforation, has exceedingly high productivity, and is less apt to split in the lengthwise direction in processing, e.g., printing. Provided is a label which is formed from the heat-shrinkable film and is satisfactorily tearable. The label is one formed from a tubular material which comprises as a base a heat-shrinkable film thermally shrinking mainly in the film width direction and which has been cut according to an object to be packaged, both edges in the film width direction having been bonded to each other. The tubular material has been thermally shrunk to constitute the label, with which at least part of the periphery of the object to be packaged is covered. The label has an angle tear strength in the direction perpendicular to the main shrinkage direction (i.e., in the film length direction) of 100-310 N/mm and a tensile break strength in the direction perpendicular to the main shrinkage direction (i.e.

Abstract: The invention aims at providing a heat-shrinkable polyester film which is excellent in tearability along perforations and in break resistance after storage when used as labels of beverage bottles. The invention relates to a heat-shrinkable polyester film which is made of a polyester resin comprising ethylene terephthalate as the main constituent and containing at least 13 mol % of at least one monomer capable of forming an amorphous component in the whole polyester resin component and which has specific heat shrinkage characteristics and exhibits specific mechanical characteristics after heat shrinking treatment. The film can be produced by a sequential biaxial orientation process comprising longitudinal orientation step, intermediate heat treatment step, positive cooling step, transverse orientation step, and final heat treatment step.

Abstract: The inventive heat-shrinkable polystyrene film is high in shrinkability in the longitudinal direction that is its main shrinkage direction, is excellent in perforated line openability, and has high toughness. The heat-shrinkable polystyrene film is characterized by particular values with respect to hot-water heat shrinkage ratio in the longitudinal and width directions, right angle tear strength in the width direction, and breaking energies in the longitudinal and width directions.

Abstract: The present invention provides a heat-shrinkable polyester film with very good perforation-tear property and also very high productivity. A heat-shrinkable polyester film made of a polyester resin including ethylene terephthalate as a main constituent and containing 15% by mole or more of at least one monomer capable of forming an amorphous component in the whole components of the polyester resin, which exhibits specific heat shrinkage properties and specific mechanical properties after the heat shrinkage.

Abstract: In the heat-shrinkable polyester film of the present invention, the main shrinkage direction is the longitudinal direction. In addition, the hot-water heat shrinkage ratios in the longitudinal direction and the width direction when the film is treated in hot water at 90° C. for 10 seconds, the refractive indexes in the longitudinal direction and the width direction and the natural shrinkage ratio after aging at 40° C. and 65% RH for 700 hours or more are each controlled in predetermined ranges. The heat-shrinkable polyester film of the present invention is manufactured by stretching an unstretched film at a ratio of 2.5 times or more and 6.0 times or less in the width direction at a temperature of Tg+5° C. or more and Tg+40° C. or less, passing the film in an intermediate zone that does not execute an active heating operation, heat-treating the film at a temperature of 100° C. or more and 170° C. or less over a period of 1.0 second or more and 10.