Abstract: A material for magnetic head sliders comprises a mixed powder consisting of 40 to 80% by weight of Al.sub.2 O.sub.3 and 20 to 60% by weight of TiO.sub.2, and further contains, per 100 parts by weight of the Al.sub.2 O.sub.3 and TiO.sub.2 mixture, 0.5 to 5 parts by weight of at least one of CaO, MgO and Y.sub.2 O.sub.3, and 0.5 to 10 parts by weight of ZrO.sub.2.

Abstract: This invention discloses zirconia-containing grinding media in the preparation of magnetic disc coating and method for producing such grinding media. The grinding media essentially consists of zirconia-sintered body containing 3.6% to 8.0% by weight of yttrium oxide, the zirconia sintered body having a means grain size of less than 2 .mu.m and the relative theoretical density of more than 98.0%.

Abstract: Sintered bodies having improved sinterability and toughness consist essentially of: (1) 100 parts by weight of titanium carbide, titanium oxide and aluminum oxide, the titanium carbide and titanium oxide accounting for 15 to 60 percent by weight and the aluminum oxide accounting for 85 to 40 percent by weight, the amount of titanium oxide relative to the titanium carbide and titanium oxide being 5 to 15 percent by weight, and (2) 0.039 to 1.575 parts by weight of yttrium. Sintering aids may include at least one of the oxides of magnesium, nickel, molybdenum, chromium, cobalt, iron and manganese.

Abstract: Sintering of a mixture of alumina and titanium carbide has been difficult heretofore, but by the intermediary action of titanium oxides, sintering of a powder mixture consisting of alumina and titanium carbide by hot-pressing at a comparatively lower temperature than that used in conventional processes becomes possible. Various procedures in which the above principle is applied, the powder mixture to be used therein and the materials produced thereby which are to be used for manuacturing cutting tools are disclosed.