Abstract: A glass substrate of the present invention for magnetic recording media having high heat resistance and easy chemical strengthening ability at once has not been obtained, which is a glass composition essentially comprising 60 to 70 wt % SiO2, 5 to 20 wt % Al2O3, 0 to 1 wt % Li2O, 3 to 18 wt % Na2O, 0 to 9 wt % K2O, 0 to 10 wt % MgO, 1 to 15 wt % CaO, 0 to 4.5 wt % SrO, 0 to 1 wt % BaO, 0 to 1 wt % TiO2 and 0 to 1 wt % ZrO2, wherein the sum of Li2O, Na2O and K2O is from 5 to 25 wt %, and the sum of MgO, CaO, SrO and BaO is from 5 to 20 wt %.

Abstract: A random copolymer obtained by polymerizing a monomer composition comprising allylamine or a salt thereof and a monomer bearing a phosphorylcholine-like group, comprising 0.01 to 9 mole % of constituent units (A1) derived from allylamine or a salt thereof and 91 to 99.99 mole % of constituent units (A2) derived from a monomer bearing a phosphorylcholine-like group, and having a number-average molecular weight of 50000 to 5000000. This copolymer is excellent in biocompatibility, can be easily fixed on the surfaces of substrates, and exhibit good surface lubricity when formed into films, thus being useful as medical material.

Abstract: An application control method to control operations of applications by solving logical names described by development descriptors is provided. The method includes at least the step to create an allocation list that indicates allocation rules to allocate physical values to logical names described in applications, and the step to allocate physical values to the logical names described in the executed application according to an application status and the allocation rules in the allocation list.

Abstract: A high transmittance glass sheet is provided that is formed of a soda-lime-silica glass composition containing, expressed in wt. %, less than 0.020% of total iron oxide in terms of Fe2O3 and 0.006 to 2.0% of zinc oxide. The glass sheet allows the formation of nickel sulfide particles to be suppressed by the addition of a zinc compound to a glass raw material.

Abstract: The present invention is to provide a high transmittance glass sheet that has a composition containing as coloring components, expressed in wt. %, 0.005 to less than 0.02% of total iron oxide in terms of Fe2O3, less than 0.008% of FeO, and 0 to 0.25% of cerium oxide and having a ratio of FeO in terms of Fe2O3 to the total iron oxide of lower than 40%, and exhibits high visible light transmittance and solar radiation transmittance. Alternatively, a high transmittance glass sheet is provided that contains not more than 0.06% of total iron oxide and 0.025 to 0.20% of cerium oxide and has a ratio of a fluorescence intensity at 395 nm to a fluorescence intensity at 600 nm of 10% or higher when subjected to ultraviolet irradiation at a wavelength of 335 nm.

Abstract: A glass substrate for use as an information recording medium has an average surface roughness (Ra) in the range of 0.3 nm≦Ra<3.0 nm and includes surface irregularities shaped and distributed isotropically and arranged substantially in succession. The surface irregularities include 5 to 50,000 convexities having a height of at least 3 nm and no convexities having a height of at least 15 nm within an area of 50 &mgr;m×50 &mgr;m. A porous region produced by an acid treatment process in the glass substrate would be completely removed if excessively etched by an alkaline solution. However, the etching process using the alkaline solution can be stopped at a stage where the pores in the porous region are enlarged by controlling conditions for the acid and alkali treatment processes.

Abstract: Low transmittance glass is composed of soda-lime-silica glass including 0.001 to 2 wt. % Li2O and, as colorant, 0.7 to 2.2 wt. % total iron oxide expressed as Fe2O3 (T-Fe2O3). The glass has visible light transmittance (YA) of not greater than 65%, measured by using the CIE illuminant A, total solar radiation transmittance (TG) of not greater than 60%, and ultraviolet transmittance defined by ISO 9050 of not greater than 25%, when the glass has a thickness between 2.1 mm and 6 mm. Ultraviolet/infrared absorbent green glass is composed of soda-lime-silica glass including 0.001 to 2 wt. % Li2O and, as colorant, 0.4 to 2 wt. % total iron oxide expressed as Fe2O3 (T-Fe2O3) wherein FeO expressed as Fe2O3 is 15 to 60% of T-Fe2O3. The glass has visible light transmittance (YA) of not less than 70%, measured by using the CIE illuminant A, and total solar radiation transmittance (TG) of not greater than 60%, when the glass has a thickness between 2.1 mm and 6 mm.

Abstract: An adapter component capable of connecting to a connector component, and an adapter execution unit for accepting an execution request from an EAI system to initiate the adapter component are provided as an adapter program. With these components, data outputted from the EAI system is received as input, and converted into a format available for the connector component. The converted data is outputted to the connector component.

Abstract: A method and a system for multiplexing voice packets without delay variation even if the number of multiplexed channels is increased, wherein a packet buffering unit receives compressed voice data, and stores voice data groups during voice activity intervals in each channel as talk; a scheduling FIFO block sequentially stores the channel numbers of a predetermined number of multiplexed channels which are read according to priority over the other channels, thereby controlling reading contention. A write decision block controls writing of talk spurts in the buffer areas of the respective channels in a packet buffering unit and also controls writing of the channel numbers in the scheduling FIFO block. A scheduling FIFO controller selects channel numbers from the scheduling FIFO block and a read decision block outputs voice packets by controlling the multiplexing sequence of talk spurts of the selected channel numbers.

Abstract: A glass substrate for use as an information recording medium has an average surface roughness (Ra) in the range of 0.3 nm≦Ra<3.0 nm and includes surface irregularities shaped and distributed isotropically and arranged substantially in succession. The surface irregularities include 5 to 50,000 convexities having a height of at least 3 nm and no convexities having a height of at least 15 nm within an area of 50 &mgr;m×50 &mgr;m. A porous region produced by an acid treatment process in the glass substrate would be completely removed if excessively etched by an alkaline solution. However, the etching process using the alkaline solution can be stopped at a stage where the pores in the porous region are enlarged by controlling conditions for the acid and alkali treatment processes.

Abstract: A glass substrate for an information recording medium has an acid resistance represented by an etching rate of at most 45 nm/min. upon contact with a hydrofluoric acid having a temperature of 50° C. and a concentration of 0.1 weight %. The glass substrate has a recording surface having an average surface roughness Ra smaller than 0.3 nm.

Abstract: A glass substrate for an information recording medium has an acid resistance represented by an etching rate of at most 45 nm/min. upon contact with a hydrofluoric acid having a temperature of 50° C. and a concentration of 0.1 weight %. The glass substrate has a recording surface having an average surface roughness Ra smaller than 0.3 nm.

Abstract: A glass substrate for use as an information recording medium has an average surface roughness (Ra) in the range of 0.3 nm≦Ra<3.0 nm and includes surface irregularities shaped and distributed isotropically and arranged substantially in succession. The surface irregularities include 5 to 50,000 convexities having a height of at least 3 nm and no convexities having a height of at least 15 nm within an area of 50 &mgr;m×50 &mgr;m. A porous region produced by an acid treatment process in the glass substrate would be completely removed if excesively etched by an alkaline solution. However, the etching process using the alkaline solution can be stopped at a stage where the pores in the porous region are enlarged by controlling conditions for the acid and alkali treatment processes.

Abstract: A glass article of the present invention has a rate of dissolution in an acidic liquid of from 10 to 100 nm/min in terms of etching rate in immersing in a 0.1% by weight 50° C. aqueous solution of hydrofluoric acid and an average linear thermal expansion coefficient of 70×10−7/° C. or higher as measured in the range of from −50° C. to 70° C., and the working temperature T4 (° C.) and the liquidus temperature TL (° C.) thereof satisfy the relationship: T4−TL≧−100° C.

Abstract: A glass substrate for an information recording medium has an acid resistance represented by an etching rate of at most 45 nm/min. upon contact with a hydrofluoric acid having a temperature of 50° C. and a concentration of 0.1 weight %. The glass substrate has a recording surface having an average surface roughness Ra smaller than 0.3 nm.

Abstract: A glass substrate for magnetic recording medium, having a composition of, in % by weight: 61-70% SiO2, 9-18% Al2O3, 2-4.5% Li2O, 6-13% Na2O, 0-5% K2O, 10-16% R2O (with the proviso of R2O=Li2O+Na2O+K2O), 0-3.5% MgO, 1-7% CaO, 0-2% SrO, 0-2% BaO, 2-10% RO (with the proviso of RO=MgO+CaO+SrO +BaO), 0-2% TiO2, 0-2% CeO2, 0-2% Fe2O3, and 0-1% MnO (with the proviso of TiO2+CeO2+Fe2O3+MnO=0.01-3%). The glass substrate has melting temperature and working temperature suitable for the float process, and has good water resistance and weathering resistance after tempering treatment.

Abstract: A glass composition having a high Young's modulus and a low density is disclosed which can be mass-produced by a continuous process and easily made to have high surface smoothness. Also disclosed are a substrate including the glass composition and reduced in bending and resonance even upon high-speed rotation, a recording medium usable at a lower flying height, and an information recording device having a higher recording capacity and a shorter access time. The glass composition includes, in terms of mol %, 40 to 55% silicon dioxide (SiO2), 0.5 to 6% aluminum oxide (Al2O3), 2 to 20% lithium oxide (Li2O), 0 to 10% sodium monoxide ((Na2O), 2 to 30% R2O (R2O=Li2O+Na2O), 5 to 25% magnesium oxide (MgO), 0 to 25% calcium oxide (CaO), 0 to 10% strontium oxide (SrO), 10 to 40% RO (RO=MgO+CaO+SrO), 0 to 10% titanium dioxide (TiO2), and 0 to 5% zirconium oxide (ZrO2).

Abstract: A glass composition is disclosed which has a high modulus of elasticity (Young's modulus) and a high rigidity (modulus of elasticity/specific gravity) and is capable of being effectively inhibited from bending or vibrating. Also disclosed is a process for producing the glass composition. The glass composition comprises, in terms of mol %, 40 to 65% SiO2, 5 to 25% Al2O3, 2 to 20% Li2O, 0 to 9% Na2O, 0 to 10% TiO2, 0 to 10% ZrO2, 0 to 25% MgO, 0 to 25% CaO, and 0 to 10% SrO, provided that the content of RO (RO=MgO+CaO+SrO) is from 2 to 40% and the sum of (Li2O)/2 and Na2O is from 1 to 10 mol %, said glass composition further containing, as clarifiers, from 0.01 to 5 mol % SnO2 and up to 0.1 mol % sulfur (S) in terms of the amount of SO3.

Abstract: A glass composition is disclosed which has a high modulus of elasticity (Young's modulus) and a high rigidity (modulus of elasticity/specific gravity) and is capable of being effectively inhibited from bending or vibrating. Also disclosed is process for producing the glass composition. The glass composition comprises, in terms of mol %, 40 to 65% SiO2, 5 to 25% Al2O3, 2 to 20% Li2O, 0 to 9% Na2O, 0 to 10% TiO2, 0 to 10% ZrO2, 0 to 25% MgO, 0 to 25% CaO, and 0 to 10% SrO, provided that the content of RO (RO=MgO+CaO+SrO) is from 2 to 40% and the sum of (Li2O)/2 and Na2O is from 1 to 10 mol %, said glass composition further containing, as clarifiers, from 0.01 to 5 mol % SnO2 and up to 0.1 mol % sulfur (S) in terms of the amount of SO3.