Abstract: This disclosure involves an adsorption-desorption material, e.g., crosslinked epoxy-amine material having an Mw from about 500 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and a CO2 adsorption capacity of at least about 0.2 millimoles CO2 per gram of crosslinked material, and/or linear epoxy-amine material having an Mw from about 160 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and a CO2 adsorption capacity of at least about 0.2 millimoles CO2 per gram of linear material. This disclosure also involves processes for preparing the crosslinked epoxy-amine materials and linear epoxy-amine materials, as well as selective removal of CO2 and/or other acid gases from a gaseous stream using the epoxy-amine materials.

Abstract: Improved CO2 sorbents comprised of a mesoporous silica functionalized with a polyamine are obtained by the in-situ polymerization of azetidine. Also included herein are processes utilizing the improved CO2 sorbents wherein CO2 is chemisorbed onto the polyamine portion of the sorbent and the process is thermally reversible.

Abstract: An adsorption-desorption material, in particular, crosslinked vinylepoxide-amine polymeric materials having an Mw from about 500 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and an adsorption capacity of at least about 0.2 millimoles adsorbed CO2 per gram of adsorption-desorption material, and linear vinylepoxide-amine polymeric materials having an Mw from about 140 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and an adsorption capacity of at least about 0.2 millimoles adsorbed CO2 per gram of adsorption-desorption material. This disclosure also relates to processes for preparing the crosslinked and linear vinylepoxide-amine materials, as well as to selective removal of CO2 and/or other acid gases from a gaseous stream using the vinylepoxide materials.

Abstract: This disclosure involves an adsorption-desorption material, e.g., crosslinked epoxy-amine material having an Mw from about 500 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and a CO2 adsorption capacity of at least about 0.2 millimoles CO2 per gram of crosslinked material, and/or linear epoxy-amine material having an Mw from about 160 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and a CO2 adsorption capacity of at least about 0.2 millimoles CO2 per gram of linear material. This disclosure also involves processes for preparing the crosslinked epoxy-amine materials and linear epoxy-amine materials, as well as selective removal of CO2 and/or other acid gases from a gaseous stream using the epoxy-amine materials.

Abstract: An adsorption-desorption material, in particular, crosslinked organo-amine polymeric materials having an Mw from about 500 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and an adsorption capacity of at least about 0.2 millimoles adsorbed CO2 per gram of adsorption-desorption material, and linear organo-amine polymeric materials having an Mw from about 160 to about 1×106, a total pore volume from about 0.2 cc/g to about 2.0 cc/g, and an adsorption capacity of at least about 0.2 millimoles adsorbed CO2 per gram of adsorption-desorption material. This disclosure also relates to processes for preparing the crosslinked and linear organo-amine materials, as well as to selective removal of CO2 and/or other acid gases from a gaseous stream using the adsorption-desorption materials.

Abstract: This disclosure involves an adsorption-desorption material, e.g., crosslinked polyvinyl-amine material having an Mw from about 500 to about 1×106, total pore volume from about 0.2 cc/g to about 2.0 cc/g, and a CO2 adsorption capacity of at least about 0.2 millimoles per gram of crosslinked material, and/or linear polyvinyl-amine material having an Mw from about 160 to about 1×106, total pore volume from about 0.2 cc/g to about 2.0 cc/g, and a CO2 adsorption capacity of at least about 0.2 millimoles per gram of linear material. This disclosure also involves processes for preparing the crosslinked polyvinyl-amine materials and linear polyvinyl-amine materials, as well as selective removal of CO2 and/or other acid gases from a gaseous stream using the polyvinyl-amine materials.

Abstract: A method is described for separating CO2 and/or H2S from a mixed gas stream by contacting the gas stream with a non-aqueous, liquid absorbent medium of a primary and/or secondary aliphatic amine, preferably in a non-aqueous, polar, aprotic solvent under conditions sufficient for sorption of at least some of the CO2. The solution containing the absorbed CO2 can then be treated to desorb the acid gas. The method is usually operated as a continuous cyclic sorption-desorption process, with the sorption being carried out in a sorption zone where a circulating stream of the liquid absorbent contacts the gas stream to form a CO2-rich sorbed solution, which is then cycled to a regeneration zone for desorption of the CO2 (advantageously at <100° C.). Upon CO2 release, the regenerated lean solution can be recycled to the sorption tower. CO2:(primary+secondary amine) adsorption molar ratios >0.5:1 (approaching 1:1) may be achieved.

Abstract: A CO2 amine scrubbing process uses an absorbent mixture combination of an amine CO2 sorbent in combination with a non-nucleophilic, relatively stronger, typically nitrogenous, base. The weaker base(s) are nucleophilic and have the ability to react directly with the CO2 in the gas stream while the relatively stronger bases act as non-nucleophilic promoters for the reaction between the CO2 and the weaker base. The sorption and desorption temperatures can be varied by selection of the amine/base combination, permitting effective sorption temperatures of 70 to 90° C., favorable to scrubbing flue gas.

Abstract: Improved CO2 sorbents comprised of a mesoporous silica functionalized with a polyamine are obtained by the in-situ polymerization of azetidine. Also included herein are processes utilizing the improved CO2 sorbents wherein CO2 is chemisorbed onto the polyamine portion of the sorbent and the process is thermally reversible.