Abstract: A solid state device includes a first material and a second material. A barrier layer is formed between the first material and the second material to prevent diffusion between the first material and the second material. The barrier layer includes a metal form of at least one of Ru and Re. The barrier layer is preferably formed using a low temperature deposition process, where the substrate is less than 400 degrees C.

Abstract: A method for depositing metal layers on semiconductor substrates by a thermal chemical vapor deposition (TCVD) process. The TCVD process utilizes high flow rate of a dilute process gas containing a metal-carbonyl precursor to deposit a metal layer. In one embodiment of the invention, the metal-carbonyl precursor can be selected from at least one of W(CO)6, Ni(CO)4, Mo(CO)6, Co2(CO)8, Rh4(CO)12, Re2(CO)10, Cr(CO)6, and Ru3(CO)12. In another embodiment of the invention, a method is provided for depositing a W layer from a process gas comprising a W(CO)6 precursor at a substrate temperature of about 410° C. and a chamber pressure of about 200 mTorr.

Abstract: A method for depositing metal layers with good surface morphology using sequential flow deposition includes alternately exposing a substrate in a process chamber to a metal-carbonyl precursor gas and a reducing gas. During exposure with the metal-carbonyl precursor gas, a thin metal layer is deposited on the substrate, and subsequent exposure of the metal layer to the reducing gas aids in the removal of reaction by-products from the metal layer. The metal-carbonyl precursor gas and a reducing gas exposure steps can be repeated until a metal layer with a desired thickness is achieved. The metal-carbonyl precursor can, for example, be selected from W(CO)6, Ni(CO)4, Mo(CO)6, Co2(CO)8, Rh4(CO)12, Re2(CO)10, Cr(CO)6, and Ru3(CO)12.

Abstract: A method for depositing metal layers on semiconductor substrates by a thermal chemical vapor deposition (TCVD) process includes introducing a process gas containing a metal carbonyl precursor in a process chamber and depositing a metal layer on a substrate. The TCVD process utilizes a short residence time for the gaseous species in the processing zone above the substrate to form a low-resistivity metal layer. In one embodiment of the invention, the metal carbonyl precursor can be selected from at least one of W(CO)6, Ni(CO)4, Mo(CO)6, Co2(CO)8, Rh4(CO)12, Re2(CO)10, Cr(CO)6, and Ru3(CO)12 precursors. In another embodiment of the invention, a method is provided for depositing low-resistivity W layers at substrate temperatures below about 500° C., by utilizing a residence time less than about 120 msec.

Abstract: A method is provided for forming a metal layer on a substrate using an intermittent precursor gas flow process. The method includes exposing the substrate to a reducing gas while exposing the substrate to pulses of a metal-carbonyl precursor gas. The process is carried out until a metal layer with desired thickness is formed on the substrate. The metal layer can be formed on a substrate, or alternately, the metal layer can be formed on a metal nucleation layer.