Abstract: Resorbable multifilament yarns and monofilament fibers including poly-4-hydroxybutyrate and copolymers thereof with high tenacity or high tensile strength have been developed. The yarns and fibers are produced by cold drawing the multifilament yarns and monofilament fibers before hot drawing the yarns and fibers under tension at temperatures above the melt temperature of the polymer or copolymer. These yarns and fibers have prolonged strength retention in vivo making them suitable for soft tissue repairs where high strength and strength retention is required. The multifilament yarns have tenacities higher than 8.1 grams per denier, and in vivo, retain at least 65% of their initial strength at 2 weeks. The monofilament fibers retain at least 50% of their initial strength at 4 weeks in vivo. The monofilament fibers have tensile strengths higher than 500 MPa. These yarns and fibers may be used to make various medical devices for various applications.

Abstract: Resorbable multifilament yarns and monofilament fibers including poly-4-hydroxybutyrate and copolymers thereof with high tenacity or high tensile strength have been developed. The yarns and fibers are produced by cold drawing the multifilament yarns and monofilament fibers before hot drawing the yarns and fibers under tension at temperatures above the melt temperature of the polymer or copolymer. These yarns and fibers have prolonged strength retention in vivo making them suitable for soft tissue repairs where high strength and strength retention is required. The multifilament yarns have tenacities higher than 8.1 grams per denier, and in vivo, retain at least 65% of their initial strength at 2 weeks. The monofilament fibers retain at least 50% of their initial strength at 4 weeks in vivo. The monofilament fibers have tensile strengths higher than 500 MPa. These yarns and fibers may be used to make various medical devices for various applications.

Abstract: Compositions of P4HB with high purity have been developed. The compositions are prepared by washing P4HB biomass prior to solvent extraction, and precipitating P4HB from solution. The same solvent is preferably used to wash the P4HB biomass, and as a non-solvent to precipitate the polymer from a P4HB solvent solution. The highly pure P4HB compositions are suitable for preparing implants. The implants may be used for the repair of soft and hard tissues.

Abstract: Absorbable implants for breast surgery that conform to the breast parenchyma and surrounding chest wall have been developed. These implants support newly lifted breast parenchyma, and/or a breast implant. The implants have mechanical properties sufficient to support a reconstructed breast, and allow the in-growth of tissue into the implant as it degrades. The implants have a strength retention profile allowing the support of the breast to be transitioned from the implant to regenerated host tissue, without significant loss of support. Three-dimensional implants for use in minimally invasive mastopexy/breast reconstruction procedures are also described, that confer shape to a patient's breast. These implants are self-reinforced, can be temporarily deformed, implanted in a suitably dissected tissue plane, and resume their preformed three-dimensional shape. The implants are preferably made from poly-4-hydroxybutyrate (P4HB) and copolymers thereof.

Abstract: Toughened compositions of PLA and PLA copolymers are disclosed, which also have low tensile modulus values and greater elongation to break. These toughened compositions are prepared by blending PLA and PLA copolymers with poly-4-hydroxybutyrate, and copolymers thereof. Blending of poly-4-hydroxybutyrate with PLA and its copolymers has been found to impart advantageous properties to the resulting blend. These compositions, and objects formed from these compositions, have improved toughness and lower stiffness than polylactic acid polymers or copolymers alone.

Abstract: Toughened compositions of PLA and PLA copolymers are disclosed, which also have low tensile modulus values and greater elongation to break. These toughened compositions are prepared by blending PLA and PLA copolymers with poly-4-hydroxybutyrate, and copolymers thereof. Blending of poly-4-hydroxybutyrate with PLA and its copolymers has been found to impart advantageous properties to the resulting blend. These compositions, and objects formed from these compositions, have improved toughness and lower stiffness than polylactic acid polymers or copolymers alone.

Abstract: Absorbable polyester fibers, braids, and surgical meshes with prolonged strength retention have been developed. These devices are preferably derived from biocompatible copolymers or homopolymers of 4-hydroxybutyrate. These devices provide a wider range of in vivo strength retention properties than are currently available, and could offer additional benefits such as anti-adhesion properties, reduced risks of infection or other post-operative problems resulting from absorption and eventual elimination of the device, and competitive cost. The devices may also be particularly suitable for use in pediatric populations where their absorption should not hinder growth, and provide in all patient populations wound healing with long-term mechanical stability. The devices may additionally be combined with autologous, allogenic and/or xenogenic tissues to provide implants with improved mechanical, biological and handling properties.

Abstract: Compositions of P4HB with high purity have been developed. The compositions are prepared by washing P4HB biomass prior to solvent extraction, and precipitating P4HB from solution. The same solvent is preferably used to wash the P4HB biomass, and as a non-solvent to precipitate the polymer from a P4HB solvent solution. The highly pure P4HB compositions are suitable for preparing implants. The implants may be used for the repair of soft and hard tissues.

Abstract: Resorbable multifilament yarns and monofilament fibers including poly-4-hydroxybutyrate and copolymers thereof with high tenacity or high tensile strength have been developed. The yarns and fibers are produced by cold drawing the multifilament yarns and monofilament fibers before hot drawing the yarns and fibers under tension at temperatures above the melt temperature of the polymer or copolymer. These yarns and fibers have prolonged strength retention in vivo making them suitable for soft tissue repairs where high strength and strength retention is required. The multifilament yarns have tenacities higher than 8.1 grams per denier, and in vivo, retain at least 65% of their initial strength at 2 weeks. The monofilament fibers retain at least 50% of their initial strength at 4 weeks in vivo. The monofilament fibers have tensile strengths higher than 500 MPa. These yarns and fibers may be used to make various medical devices for various applications.

Abstract: Compositions of P4HB with high purity have been developed. The compositions are prepared by washing P4HB biomass prior to solvent extraction, and precipitating P4HB from solution. The same solvent is preferably used to wash the P4HB biomass, and as a non-solvent to precipitate the polymer from a P4HB solvent solution. The highly pure P4HB compositions are suitable for preparing implants. The implants may be used for the repair of soft and hard tissues.

Abstract: Absorbable polyester fibers, braids, and surgical meshes with prolonged strength retention have been developed. These devices are preferably derived from biocompatible copolymers or homopolymers of 4-hydroxybutyrate. These devices provide a wider range of in vivo strength retention properties than are currently available, and could offer additional benefits such as anti-adhesion properties, reduced risks of infection or other post-operative problems resulting from absorption and eventual elimination of the device, and competitive cost. The devices may also be particularly suitable for use in pediatric populations where their absorption should not hinder growth, and provide in all patient populations wound healing with long-term mechanical stability. The devices may additionally be combined with autologous, allogenic and/or xenogenic tissues to provide implants with improved mechanical, biological and handling properties.

Abstract: Compositions of P4HB (poly-4-hydroxybutyrate) and copolymers thereof, have been developed for pultrusion, as well as processes to produce profiles from these compositions by pultrusion. These pultrusion processes provide profiles without causing structural damage to the surface of the profile. The profiles may be used in medical applications. These compositions include P4HB, and copolymers thereof, having intrinsic viscosities less than 3.2 dl/g but greater than 0.8 dl/g. The profile may be formed using conditions such as: pull rate of 0.1 to 100 mm/min, die temperature of up to 95° C., rod stock temperature up to 95° C., draw ratio of up to 100×, pulling force of greater than 10 MPa, and clamping pressure at least 10% higher than the pulling force. Preferably, the profile is formed by pulling the rod stock through a series of dies placed at intervals with the hole sizes decreasing in diameter by 0.1 to 10 mm.

Abstract: Oriented resorbable implants made from poly-4-hydroxybutyrate (P4HB) and copolymers thereof, have been developed that contain one or more antimicrobial agents to prevent colonization of the implants, and reduce or prevent the occurrence of infection following implantation in a patient. These oriented implants are particularly suitable for use in procedures where prolonged strength retention is necessary and there is a risk of infection. Coverings and receptacles made from poly-4-hydroxybutyrate and copolymers thereof, containing antimicrobial agents, have also been developed for use with implantable devices to prevent colonization of these devices, and to reduce or prevent the occurrence of infection following implantation of these devices in a patient. These coverings and receptacles may be used to hold, or partially or fully cover, devices such as pacemakers and neurostimulators.

Abstract: Compositions of P4HB with high purity have been developed. The compositions are prepared by washing P4HB biomass prior to solvent extraction, and precipitating P4HB from solution. The same solvent is preferably used to wash the P4HB biomass, and as a non-solvent to precipitate the polymer from a P4HB solvent solution. The highly pure P4HB compositions are suitable for preparing implants. The implants may be used for the repair of soft and hard tissues.

Abstract: Absorbable monofilament fibers and self-retaining sutures with high tensile strengths have been developed. The straight pull tensile strengths of the absorbable self-retaining sutures closely approximate, equal or exceed the average minimum knot-pull tensile standards set by the United States Pharmacopeia (USP). These higher strength absorbable self-retaining sutures can therefore be used either without needing to oversize the suture for a given procedure, or by oversizing the self-retaining suture by no more than 0.1 mm in diameter. In one embodiment, the absorbable self-retaining sutures are made from poly-4-hydroxybutyrate or copolymers thereof. Methods for producing absorbable self-retaining sutures that have high tensile strengths and pronounced sheath-core structures wherein the sheath is harder than the core are also provided.

Abstract: Absorbable implants for breast surgery that conform to the breast parenchyma and surrounding chest wall have been developed. These implants support newly lifted breast parenchyma, and/or a breast implant. The implants have mechanical properties sufficient to support a reconstructed breast, and allow the ingrowth of tissue into the implant as it degrades. The implants have a strength retention profile allowing the support of the breast to be transitioned from the implant to regenerated host tissue, without significant loss of support. Three-dimensional implants for use in minimally invasive mastopexy/breast reconstruction procedures are also described, that confer shape to a patient's breast. These implants are self-reinforced, can be temporarily deformed, implanted in a suitably dissected tissue plane, and resume their preformed three-dimensional shape. The implants are preferably made from poly-4-hydroxybutyrate (P4HB) and copolymers thereof.

Abstract: Devices, such as dressing and implants, for treatment of chronic wounds comprising controlled delivery systems for butyric acid or salts, polymers, or derivatives thereof are provided. These devices are particularly useful when it is desirable to promote angiogenesis in a chronic wound. In the preferred embodiment, the implants are resorbable, provide a temporary scaffold for the in-growth of cells, tissues, and blood vessels to help regenerate the extracellular matrix, and deliver butyric acid to the chronic wound. The dressings and implants may also contain one or more antibiotics to treat or prevent infection in the wound, and/or inhibitors of proteases to modulate protease activity in the wound.

Abstract: Resorbable three-dimensional implants that can be temporarily deformed, implanted by minimally invasive means, and resume their original shape in vivo, have been developed. These implants are particularly suitable for use in minimally invasive procedures for tissue reinforcement, repair of hernias, and applications where it is desirable for the implant to contour in vivo to an anatomical shape, such as the inguinofemoral region. In the preferred embodiment, the implants are made from meshes of poly-4-hydroxybutyrate monofilament that have reinforced outlying borders that allow the meshes to form three-dimensional shapes that can be temporarily deformed. These implants can resume three-dimensional shapes after being temporarily deformed that contour to the host's tissue or an anatomical shape, for example, in the repair of a hernia, and particularly a hernia in the inguinofemoral region.

Abstract: Compositions of P4HB and processes to injection mold these compositions have been developed. These compositions are prepared from P4HB polymers and blends having intrinsic viscosities less than 3.2 dl/g but greater than 0.8 dl/g, moisture contents of less than 0.5% by weight, and more preferably less than 0.05% by weight, and using a polymer melt temperature during molding of at least 150° C. A preferred embodiment comprises a P4HB molding with an intrinsic viscosity of less than 3.2 dl/g that degrades rapidly in vivo.

Abstract: Absorbable polyester fibers, braids, and surgical meshes with prolonged strength retention have been developed. These devices are preferably derived from biocompatible copolymers or homopolymers of 4-hydroxybutyrate. These devices provide a wider range of in vivo strength retention properties than are currently available, and could offer additional benefits such as anti-adhesion properties, reduced risks of infection or other post-operative problems resulting from absorption and eventual elimination of the device, and competitive cost. The devices may also be particularly suitable for use in pediatric populations where their absorption should not hinder growth, and provide in all patient populations wound healing with long-term mechanical stability. The devices may additionally be combined with autologous, allogenic and/or xenogenic tissues to provide implants with improved mechanical, biological and handling properties.