Abstract: A laminate includes a first glass article having a first thickness, a first annealing point, and a first softening point, a second glass article having a second thickness, a second annealing point, and a second softening point, and an interlayer disposed between the first glass article and the second glass article. The first thickness is greater than the second thickness, the second annealing point is less than or equal to the first annealing point, and the second softening point is greater than the first softening point.

Abstract: A glass-based article includes an amorphous phase and a crystalline phase, and a first surface and a second surface opposing the first surface thereby defining a thickness (t) of the glass-based article. The glass-based article has a stress profile with a surface compressive stress (CS) and a maximum central tension (CT). The maximum CT is greater than or equal to 80 MPa and less than or equal to 95 MPa, and the maximum CT is positioned within the glass-based article at a range from greater than or equal to 0.4·t and less than or equal to 0.6·t. The surface CS of the glass-based article is greater than or equal to 200 MPa; and a depth of compression (DOC) is from greater than or equal to 0.14·t and less than or equal to 0.25·t.

Abstract: Embodiments of glass articles exhibiting a grey or a green tint are described. In one or more embodiments, the glass article comprises a glass composition including SiO2, Al2O3 B2O3 or MgO, a non-zero amount of alkali metal oxides (R2O), R2O—Al2O3 in the range from about ?0.5 to about 1.5; and up to 1 mol % Fe2O3. In one or more embodiments, the glass composition includes a ratio of R2O to Al2O3 equal to or greater than about 1, Na2O, from 0-13 mol % MgO, at least one of K2O, SnO2 and TiO2. Laminates including such glass articles and methods of making the glass articles are also described.

Abstract: Ion exchangeable glasses containing SiO2, Al2O3, Na2O, MgO, B2O3, and P2O5 are provided. The compressive stresses of these ion exchanged glasses are greater than 900 megapascals (MPa) at a depth of 45 or 50 microns (?m) with some glasses exhibiting a compressive stress of at least 1 gigaPascals (GPa). The ion exchange rates of these glasses are much faster than those of other alkali aluminosilicate glasses and the ion exchanged glass is resistant damage to impact damage. A method of ion exchanging the glass is also provided.

Abstract: Described herein are alkali-free, boroalumino silicate glasses exhibiting desirable physical and chemical properties for use as substrates in flat panel display devices, such as, active matrix liquid crystal displays (AMLCDs) and active matrix organic light emitting diode displays (AMOLEDs). In accordance with certain of its aspects, the glasses possess good dimensional stability as a function of temperature.

Abstract: A glass article includes a glass core layer and a glass cladding layer adjacent to the core layer. An average coefficient of thermal expansion (CTE) of the core layer is greater than an average CTE of the cladding layer. An effective 109.9 P temperature of the glass article is at most about 750° C.

Abstract: Ion exchangeable glasses containing SiO2, Al2O3, Na2O, MgO, B2O3, and P2O5 are provided. The compressive stresses of these ion exchanged glasses are greater than 900 megapascals (MPa) at a depth of 45 or 50 microns (?m) with some glasses exhibiting a compressive stress of at least 1 gigaPascals (GPa). The ion exchange rates of these glasses are much faster than those of other alkali aluminosilicate glasses and the ion exchanged glass is resistant damage to impact damage. A method of ion exchanging the glass is also provided.

Abstract: Embodiments of a glass-based article including a first surface and a second surface opposing the first surface defining a thickness (t) of about 3 millimeters or less (e.g., about 1 millimeter or less), and a stress profile, wherein all points of the stress profile between a thickness range from about 0·t up to 0.3·t and from greater than about 0.7·t up to t, comprise a tangent with a slope having an absolute value greater than about 0.1 MPa/micrometer, are disclosed. In some embodiments, the glass-based article includes a non-zero metal oxide concentration that varies along at least a portion of the thickness (e.g., 0·t to about 0.3·t) and a maximum central tension in the range from about 80 MPa to about 100 MPa. In some embodiments, the concentration of metal oxide or alkali metal oxide decreases from the first surface to a value at a point between the first surface and the second surface and increases from the value to the second surface. The concentration of the metal oxide may be about 0.

Abstract: A fining agent for reducing the concentration of seeds or bubbles in a silicate glass. The fining agent includes at least one inorganic compound, such as a hydrate or a hydroxide that acts as a source of water. In one embodiment, the fining agent further includes at least one multivalent metal oxide and, optionally, an oxidizer. A fusion formable and ion exchangeable silicate glass having a seed concentration of less than about 1 seed/cm3 is also provided. Methods of reducing the seed concentration of a silicate glass, and a method of making a silicate glass having a seed concentration of less than about 1 seed/cm3 are also described.

Abstract: Disclosed herein are glass-ceramics having crystalline phases including ?-spodumene ss and either (i) pseudobrookite or (ii) vanadium or vanadium containing compounds so as to be colored and opaque glass-ceramics having coordinates, determined from total reflectance—specular included—measurements, in the CIELAB color space of the following ranges: L*=from about 20 to about 45; a*=from about ?2 to about +2; and b*=from about ?12 to about +1. Such CIELAB color space coordinates can be substantially uniform throughout the glass-ceramics. In each of the proceeding, ?-quartz ss can be substantially absent from the crystalline phases. If present, ?-quartz ss can be less than about 20 wt % or, alternatively, less than about 15 wt % of the crystalline phases. Also Further crystalline phases might include spinel ss (e.g., hercynite and/or gahnite-hercynite ss), rutile, magnesium zinc phosphate, or spinel ss (e.g., hercynite and/or gahnite-hercynite ss) and rutile.

Abstract: A method of chemically strengthening a glass. The method includes heating an ion exchange solution to a temperature less than about 360° C., and contacting the glass and the strengthening solution at the temperature for a duration from about 0.5 hours to about 24 hours. The ion exchange solution includes a primary nitrate and at least one monovalent or divalent cation nitrate component in an amount from about 1 wt. % to about 10 wt. %.

Abstract: Embodiments of a glass-based article including a first surface and a second surface opposing the first surface defining a thickness (t) of about 3 millimeters or less (e.g., about 1 millimeter or less), and a stress profile, wherein all points of the stress profile between a thickness range from about 0·t up to 0.3·t and from greater than about 0.7·t up to t, comprise a tangent with a slope having an absolute value greater than about 0.1 MPa/micrometer, are disclosed. In some embodiments, the glass-based article includes a non-zero metal oxide concentration that varies along at least a portion of the thickness (e.g., 0·t to about 0.3·t) and a maximum central tension in the range from about 80 MPa to about 100 MPa. In some embodiments, the concentration of metal oxide or alkali metal oxide decreases from the first surface to a value at a point between the first surface and the second surface and increases from the value to the second surface. The concentration of the metal oxide may be about 0.

Abstract: A silicate glass that is tough and scratch resistant. The toughness is increased by minimizing the number of non-bridging oxygen atoms in the glass. In one embodiment, the silicate glass is an aluminoborosilicate glass in which ?15 mol %?(R2O+R?O—Al2O3—ZrO2)—B2O3?4 mol %, where R is one of Li, Na, K, Rb, and Cs, and R? is one of Mg, Ca, Sr, and Ba.

Abstract: A glass article includes a glass core layer and a glass cladding layer adjacent to the core layer. An average coefficient of thermal expansion (CTE) of the core layer is greater than an average CTE of the cladding layer. An effective 109.9 P temperature of the glass article is at most about 750° C.

Abstract: Disclosed herein are glass-ceramics having crystalline phases including ?-spodumene ss and either (i) pseudobrookite or (ii) vanadium or vanadium containing compounds so as to be colored and opaque glass-ceramics having coordinates, determined from total reflectance—specular included—measurements, in the CIELAB color space of the following ranges: L*=from about 20 to about 45; a*=from about ?2 to about +2; and b*=from about ?12 to about +1. Such CIELAB color space coordinates can be substantially uniform throughout the glass-ceramics. In each of the proceeding, ?-quartz ss can be substantially absent from the crystalline phases. If present, ?-quartz ss can be less than about 20 wt % or, alternatively, less than about 15 wt % of the crystalline phases. Also Further crystalline phases might include spinel ss (e.g., hercynite and/or gahnite-hercynite ss), rutile, magnesium zinc phosphate, or spinel ss (e.g., hercynite and/or gahnite-hercynite ss) and rutile.

Abstract: A silicate glass that is tough and scratch resistant. The toughness is increased by minimizing the number of non-bridging oxygen atoms in the glass. In one embodiment, the silicate glass is an aluminoborosilicate glass in which ?15 mol %?(R2O+R?O—Al2O3—ZrO2)—B2O3?4 mol %, where R is one of Li, Na, K, Rb, and Cs, and R? is one of Mg, Ca, Sr, and Ba.

Abstract: A glass article includes a glass core layer and a glass cladding layer adjacent to the core layer. An average coefficient of thermal expansion (CTE) of the core layer is greater than an average CTE of the cladding layer. An effective 109.9 P temperature of the glass article is at most about 750° C.

Abstract: A silicate glass that is tough and scratch resistant. The toughness is increased by minimizing the number of non-bridging oxygen atoms in the glass. In one embodiment, the silicate glass is an aluminoborosilicate glass in which ?15 mol %?(R2O+R?O?Al2O3?ZrO2)?B2O3?4 mol %, where R is one of Li, Na, K, Rb, and Cs, and R? is one of Mg, Ca, Sr, and Ba.

Abstract: A method of strengthening an alkali aluminoborosilicate glass. A compressive layer extending from a surface of the glass to a depth of layer is formed by exchanging larger metal cations for smaller metal cations present in the glass. In a second step, metal cations in the glass are exchanged for larger metal cations to a second depth in the glass that is less than the depth of layer and increase the compressive stress of the compressive layer. Formation of the compressive layer and replacement of cations with larger cations can be achieved by a two-step ion exchange process. An alkali aluminoborosilicate glass having a compressive layer and a crack indentation threshold of at least 3000 gf is also provided.

Abstract: A glass and an enclosure, including windows, cover plates, and substrates for mobile electronic devices comprising the glass. The glass has a crack initiation threshold that is sufficient to withstand direct impact, has a retained strength following abrasion that is greater than soda lime and alkali aluminosilicate glasses, and is resistant to damage when scratched. The enclosure includes cover plates, windows, screens, and casings for mobile electronic devices and information terminal devices.