Abstract: A microstructure with regularly arranged micropores is obtained by anodizing an aluminum layer having a Vickers hardness Hv of up to 20. The microstructure has a well-ordered region of large surface area and can be manufactured at low cost.

Abstract: In order to provide a structure which has a sufficiently large signal strength and generates local plasmon resonance of excellent reproducibility, the invention provides a process for manufacturing a structure at least a portion of which is an aluminum member having on a surface thereof an anodized layer having a plurality of micropores, the process comprising the steps of, in order, anodizing a surface of an aluminum member so as to form an anodized layer having micropores present therein, sealing the micropores in the anodized layer by filling the micropores with metal, surface-treating the sealed anodized layer so as to remove at least a portion of upper layer surface thereof and set the average surface roughness (Ra) to at most 30 nm, and subjecting the surface-treated anodized layer to electrodeposition so as to form metal particles on the metal filled into the micropores during sealing.

Abstract: Described is a structural body including at least partially an aluminum member having on a surface an anodized film with micropores present, in which: the micropores have a coefficient of variation in pore size of 5 to 50%; and the micropores are each sealed with a metal. The structural body can generate localized plasmon resonance having a sufficiently large intensity and be produced at low cost through a simple production process, and having a large surface area.

Abstract: A lithographic printing plate precursor is disclosed, comprising a metal support having formed thereon an anodic oxide film, and an image-forming layer containing a light-to-heat converting agent, or a light-sensitive layer capable of image-forming with infrared laser exposure provided in this order from the support.

Abstract: A lithographic printing plate support comprising a substrate having thereon a porous layer comprising metal oxide particles bound by a compound containing a metal atom and a phosphorus atom.

Abstract: A lithographic printing plate precursor is disclosed, comprising a metal support having formed thereon an anodic oxide film, and an image-forming layer containing a light-to-heat converting agent, or a light-sensitive layer capable of image-forming with infrared laser exposure provided in this order from the support.

Abstract: A lithographic printing plate precursor which comprises a metal support having provided thereon a heat-insulating layer, a metal layer having a hydrophilic surface, and a lipophilic layer which is abraded by heating or whose solubility to alkali is transformed by heating, in this order from the support.

Abstract: A plate precursor for a lithographic printing plate requiring no development, which comprises a surface formed of a solid material of an inorganic compound comprising at least two kinds of elements selected from groups 13, 14 and 15 of the periodic table; a method for making a lithographic printing plate using the same; and a novel plate precursor for a lithographic printing plate in which an image can be formed and deleted.

Abstract: The present invention allows the reproduction of a crystalline aluminum hydroxide having a high particle strength and a high purity which can find wide application such as abrasive from a supersaturated sodium aluminate solution which is being recycled in the production of aluminum hydroxide or lithographic printing plate. In a process for the purification of aluminum hydroxide which comprises the hydrolysis reaction of a supersaturated solution of sodium aluminate to crystallize aluminum hydroxide, the improvement which comprises the steps of keeping the temperature of a suspension formed by mixing a mother liquor having a total caustic soda concentration of from 50 to 700 g/l and an aluminum concentration or from 0 to 300 g/l with crystalline aluminum hydroxide at a range of from 10.degree. C. to 200.degree. C. for at least 1 to 48 hours, mixing the suspension with the supersaturated solution of sodium aluminate, and then causing the crystallization reaction at the crystallization reaction temperature.