Abstract: Heat-resistant resin composition including (A) 100 parts by weight of a poly(arylene sulfide) of a substantially linear structure containing 50% by weight or higher or recurring units of the formula ##STR1## and a logarithmic viscosity number of 0.1 to 1.0 dl/g; (B) from 0.01 to less than 25 parts by weight of a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR2## wherein the --CO-- and --S-- are in the para position to each other, and having a melting point of 310.degree.-380.degree. C., a residual melt crystallization enthalpy of at least 10 J/g, a melt crystallization temperature of at least 210.degree. C. and a reduced viscosity of 0.2 to 2 dl/g; and (C) at least one of fibrous fibers and/or at least one of inorganic fillers in a proportion of 0 to 400 parts by weight per 100 parts by weight of the resin component including said poly(arylene sulfide) and said poly(arylene thioether-ketone).

Abstract: Disclosed herein is a process for the preparation of a poly(arylene thioether-ketone) improved in melt stability, which comprises subjecting a poly(arylene thioether-ketone) (PTK) to a heat treatment for 5-5.times.10.sup.3 minutes in a powdery state and a temperature range of 200.degree.-350.degree. C. The PTK has predominant recurring units of the formula ##STR1## and has a melting point, Tm of 310.degree.-380.degree. C., a melt crystallization temperature, Tmc (420.degree. C./10 min) of at least 210.degree. C., a residual melt crystallization enthalpy, .DELTA.Hmc (420.degree.C./10 min) of at least 10 J/g and a reduced viscosity of 0.2-2.0 dl/g. PTKs improved in melt stability and prepared in accordance with the above-described preparation process are also disclosed.

Abstract: Disclosed herein is a process for the preparation of a poly(arylene thioether-ketone) improved in melt stability, which comprises subjecting a poly(arylene thioether-ketone) (PTK) to a heat treatment for 5-5.times.10.sup.3 minutes in a powdery state and a temperature range of 200.degree.-350.degree. C. The PTK has predominant recurring units of the formula ##STR1## and has a melting point, Tm of 310.degree.-380.degree. C., a melt crystallization temperature, Tmc (420.degree. C./10 min) of at least 210.degree. C., a residual melt crystallization enthalpy, .DELTA.Hmc (420.degree. C./10 min) of at least 10 J/g and a reduced viscosity of 0.2-2.0 dl/g. PTKs improved in melt stability and prepared in accordance with the above-described preparation process are also disclosed.

Abstract: A method of analyzing an autoradiograph of plural resolved rows which are formed by resolving base-specific DNA fragments or base-specific RNA fragments labeled with a radioactive element in one-dimensional direction on a support medium, to determine the base sequence of nucleic acids by:(1) electrically displaying the autoradiograph as an image on a screen on the basis of digital signals corresponding to said autoradiograph;(2) displaying a read cursor on the screen; and(3) displaying a name of a base to which a band is assigned on the screen, which is determined by using the read cursor, together with the read cursor. A method of analyzing an autoradiograph which comprises recording and storing pattern information, cursor information and base sequence information, and a method which comprises verifying and/or correcting the determined sequence of bands are also disclosed.

Abstract: Disclosed herein are stretched poly(arylene thioether) block copolymer films and a production processes thereof, said block copolymer film comprising a thermoplastic material composed of (A) 100 parts by weight of a particular poly(arylene thioether) block copolymer, (B) up to 100 parts by weight of at least one other thermoplastic resin, and (C) up to 15 parts by weight of at least one filler.

Abstract: Disclosed herein are melt-stable thermoplastic resin compositions comprising (A) 100 parts by weight of a particular poly(arylene thioether) block copolymer, (B) --400 parts by weight of at least one of thermoplastic resins, and (C) 0-400 parts by weight of at least one filler per 100 parts by weight of the resin components. At least either one of Component (B) and Component (C) is contained in a proportion of at least 0.1 part by weight per 100 parts by weight of Component (A). The poly(arylene thioether) block copolymer alternately comprise at least one poly(arylene thioether-ketone) block having predominant recurring units of the formula ##STR1## wherein the --CO-- and --S-- are in the para position to each other and at least one poly(arylene thioether) block having predominant recurring units of the formula ##STR2## Also disclosed are compositions obtained by stabilizing by the melt-stable thermoplastic resin compositions with a basic compound and products molded or formed product from these compositions.

Abstract: Disclosed herein are poly(arylene thioether) block copolymer fibers formed by melt-spinning a thermoplastic material composed of (A) 100 parts by weight of a particular poly(arylene thioether) block copolymer, (B) up to 50 parts by weight of at least one other thermoplastic resin and (C) up to 10 parts by weight of at least one filler.

Abstract: Disclosed herein are poly(arylene thioether) block copolymer fibers formed by melt-spinning a thermoplastic material composed of (A) 100 parts by weight of a particular poly(arylene thioether) block copolymer, (B) up to 50 parts by weight of at least one other thermoplastic resin and (C) up to 10 parts by weight of at least one filler.

Abstract: Disclosed herein are stretched poly(arylene thioether) block copolymer films and production processes thereof, said block copolymer film comprising a thermoplastic material composed of (A) 100 parts by weight of a particular poly(arylene thioether) block copolymer, (B) up to 100 parts by weight of at least one other thermoplastic resin, and (C) up to 15 parts by weight of at least one filler.

Abstract: Heat-resistant resin composition comprising (A) 100 parts by weight of a poly(arylene sulfide) of a substantially linear structure containing 50% by weight or higher of recurring units of the formula ##STR1## and a logarithmic viscosity number of 0.1 to 1.0 dl/g; (B) from 0.01 to less than 25 parts by weight of a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR2## wherein the --CO-- and --S-- are in the para position to each other, and having a melting point of 310.degree.-380.degree. C., a residual melt crystallization enthalpy of at least 10 J/g, a melt crystallization temperature of at least 210.degree. C. and a reduced viscosity of 0.2 to 2 dl/g; and (C) at least one of fibrous fibers and/or at least one of inorganic fillers in a proportion of 0 to 400 parts by weight per 100 parts by weight of the resin component comprising said poly(arylene sulfide) and said poly(arylene thioether-ketone).

Abstract: Disclosed herein are a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR1## and having a melting point, Tm of 310.degree.-380.degree. C., a residual melt crystallization enthalpy, .DELTA.Hmc (420.degree. C./10 min) of at least 10 J/g, a melt crystallization temperature, Tmc (420.degree. C./10 min) of at least 210.degree. C., and a reduced viscosity of 0.2-2 dl/g as measured at 25.degree. C. and a polymer concentration of 0.5 g/dl in 98 wt. % sulfuric acid as well as a production process of the poly(arylene thioether-ketone). The poly(arylene thioether-ketone) has melt stability so that conventional melt processing techniques can be applied easily. The poly(arylene thioether-ketone) is a highly-crystalline polymer whose density is at least 1.34 g/cm.sup.3 when annealed at 280.degree. C. for 30 minutes.

Abstract: Disclosed herein is a melt-stable poly(arylene thioether-ketone) composition, which comprises:(A) 100 parts by weight of a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR1## and having a melting point, Tm of 310.degree.-380.degree. C., a residual melt crystallization enthalpy, .DELTA.Hmc (420.degree. C./10 min) of at least 10 J/g, a melt crystallization temperature, Tmc (420.degree. C./10 min) of at least 210.degree. C. and a reduced viscosity of 0.2-2 dl/g;(B) 0-400 parts by weight of at least one of thermoplastic resins; and(C) at least one of fibrous fillers and/or at least one of inorganic fillers in a proportion of 0-400 parts by weight per 100 parts by weight of the sum of said components (A) and (B).At least either one of the components (B) or (C) is contained in a proportion of at least 0.1 part by weight per 100 parts by weight of the component (A).

Abstract: Disclosed herein are a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR1## and having a melting point, Tm of 310.degree.-380.degree. C., a residual melt crystallization enthalpy, .DELTA.Hmc (420.degree. C./10 min) of at least 10 J/g, a melt crystallization temperature, Tmc (420.degree. C./10 min) of at least 210.degree. C., and a reduced viscosity of 0.2-2 dl/g as measured at 25.degree. C. and a polymer concentration of 0.5 g/dl in 98 wt. % sulfuric acid as well as a production process of the poly(arylene thioether-ketone). The poly(arylene thioether-ketone) has melt stability so that conventional melt processing techniques can be applied easily. The poly(arylene thioether-ketone) is a highly-crystalline polymer whose density is at least 1.34 g/cm.sup.3 when annealed at 280.degree. C. for 30 minutes.

Abstract: Disclosed herein is a polyarylene thioether composition comprising: 100 parts by weight of a polyarylene thioether (A) which contains not less than 70 wt % of a repeating unit of ##STR1## and 0.01 to 15 parts by weight of a polyarylene thioether (B), which is a nucleating agent and contains not less than 50 wt % of a repeating unit of ##STR2## as the main constituent and has a melting point of not lower than 290.degree. C. or a melt crystallization temperature of not lower than 220.degree. C. This composition may further comprise 0.1 to 300 parts by weight of an inorganic filler and/or a fibrous filler. A 50% crystallization time, t.sub.1/2, at 250.degree. C. of the polyarylene thioether composition is not more than 1/1.5 of the 50% crystallization time of a polyarylene thioether which does not contain the polyarylene thioether (B) Accordingly, its melt molding cycle is short and its molded product has a high strength.

Abstract: A composition for shrinkable film which excells in heat-sealability, transparency, strength, and particularly low-temperature quick shrinking property and, therefore, suits production chiefly of packaging materials, a film made of the composition and a process for the manufacture of the film are disclosed. Specifically, the composition comprises one of the specific combinations of components (A), (B) and (C), i.e. the combinations of (A)+(B), (B)+(C) and (A)+(B)+(C), wherein (A) is non-rigid polyolefine resins such as ethylene vinyl acetate, (B) is an elastomer comprising a specific ethylene- .alpha.-olefin copolymer and an elastomer consisting of block copolymer having at least one monovinyl substituted aromatic hydrocarbon polymer block and at least one polyolefin polymer block selected from at least one saturated polymer or unsaturated polymer made from mainly aliphatic conjugate diene derivative, and (C) is rigid polyolefin resins such as polypropylene.

Abstract: An optical fiber cable comprising a water blocking layer, an optical fiber disposed inside the water blocking layer and a water blocking material filling the space between the water blocking layer and the optical fiber, the water blocking material comprising a grease having a worked penetration of 85 to 475 as measured according to ASTM-D-712 at room temperature.

Abstract: A composition for shrinkable film which excels in heat-sealability, transparency, strength, and particularly low-temperature quick shrinking property and, therefore, suits production chiefly of packaging materials, a film made of the composition and a process for the manufacture of the film are disclosed. Specifically, the composition comprises one of the specific combinations of components (A), (B) and (C), i.e. the combinations of (A)+(B), (B)+(C) and (A)+(B)+(C), wherein (A) is non-rigid polyolefine resins such as ethylene vinyl acetate, (B) is an elastomer comprising a specific ethylene-.alpha.-olefin copolymer, and (C) is rigid polyolefin resins such as polypropylene.

Abstract: A pulse number detection circuit used, for example, in a digital audio disk player comprises a counter counting a reference clock signal in synchronism with one inverting edge of the clock signal when an input data signal takes one logic level, first to third detectors producing first to third signals when the count value of the counter is zero, N, and (M+1), respectively, a first flip-flop producing a fourth signal in response to the other inverting edge of the clock signal when the first or second signal is produced, a second flip-flop producing a fifth signal in response to the other inverting edge of the clock signal when the first or third signal is produced, a first output circuit responding to the second and fourth signals and producing a first output signal, and a second output circuit responding to the third and fifth signals and producing a second output signal. This circuit detects that the count value is larger than (M+1/2) or smaller than (N-1/2).

Abstract: An interpolation circuit and method corrects a data word having an error by either substituting the most recent prior correct data word or substituting the mean value of the most recent prior correct data word and the data word subsequent to the one having the error. The method is carried out using a novel architecture having memory access control. A RAM stores the most recent prior correct word, A.sub.j, which will be the current word A.sub.n if A.sub.n has no error. If the subsequent workd A.sub.n+1 is without error it is stored. The two memory locations are, in effect, reversible, to enable the subsequent work A.sub.n+1 to become the most recent correct prior word, A.sub.j, for subsequent processing, where appropriate, using a minimum of hardware.The most recent prior word A.sub.j (which may be A.sub.n) is read to an adder which performs addition and division by two. Depending upon the error content of A.sub.n and A.sub.n+1, A.sub.j is either added to itself or to A.sub.

Abstract: A composition for shrinkable film which excells in heat-sealability, transparency, strength, and particularly low-temperature quick shrinking property and, therefore, suits production chiefly of packaging materials, a film made of the composition and a process for the manufacture of the film are disclosed. Specifically, the composition comprises one of the specific combinations of components (A), (B) and (C), i.e. the combinations of (A)+(B), (B)+(C) and (A)+(B)+(C), wherein (A) is non-rigid polyolefine resins such as ethylene vinyl acetate, (B) is an elastomer comprising a specific ethylene-.alpha.-olefin copolymer and an elastomer consisting of block copolymer having at least one monovinyl substituted aromatic, hydrocarbon polymer block and at least one polyolefin polymer block selected from at least one saturated polymer or unsaturated polymer made from mainly aliphatic conjugate diene derivative, and (C) is rigid polyolefin resins such as polypropylene.