Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: A method for cleaning a deposition chamber includes forming a deposited layer over an interior surface of the deposition chamber, wherein the deposited layer has a deposited layer stress and a deposited layer modulus; forming a cleaning layer over the deposited layer, wherein a material comprising the cleaning layer is selected such that the cleaning layer adheres to the deposited layer, and has a cleaning layer stress and a cleaning layer modulus, wherein the cleaning layer stress is higher than the deposited layer stress, and wherein the cleaning layer modulus is higher than the deposited layer modulus; and removing the deposited layer and the cleaning layer from the interior of the deposition chamber.

Abstract: A method of forming an integrated circuit structure includes forming a cap layer above a first ILD layer of a first metal level, the first ILD layer includes a recess filled with a first conductive material to form a first interconnect structure. Next, a second ILD layer is formed above the cap layer and a via is formed within the second ILD layer as a second interconnect structure of a second metal level. The via is aligned with the first interconnect structure. Subsequently, a portion of the cap layer is removed to extend the via to expose a top portion of the first conductive material then a passivation cap is selectively formed at a bottom portion of the via in the second ILD layer and the passivation cap contacting the top portion of the first conductive material. The passivation cap includes a metal alloy to form an interface between the bottom portion of the via and the first conductive material.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: The present invention provides a stabilized fine textured metal microstructure that constitutes a durable activated surface usable for bonding a 3D stacked chip. A fine-grain layer that resists self anneal enables metal to metal bonding at moderate time and temperature and wider process flexibility.

Abstract: Pitch-dependent dishing and erosion following CMP treatment of copper features is quantitatively assessed by atomic force microscopy (AFM) and transmission electron microscopy (TEM). A new sequence of processing steps presented herein is used to prevent dishing and to reduce significantly the local pitch- and pattern density-induced CMP non-uniformity for copper metal lines having widths and spacing in the range of about 32-128 nm. The new process includes a partial copper deposition step followed by deposition of a silicon carbide/nitride (SiCxNy) blocking layer. A multi-step CMP process planarizes areas of the resulting irregular surface that have narrow features, while the blocking layer protects areas that have wide features.

Abstract: The invention is directed to a method for removing copper oxide from a copper surface to provide a clean copper surface, wherein the method involves exposing the copper surface containing copper oxide thereon to an anhydrous vapor containing a carboxylic acid compound therein, wherein the anhydrous vapor is generated from an anhydrous organic solution containing the carboxylic acid and one or more solvents selected from hydrocarbon and ether solvents.

Abstract: Ions depleted from a chemical bath by a reaction such as plating are continually replenished by production and moving of ions through selectively permeable membranes while isolating potential contaminant ions from the chemical bath.

Abstract: A metal interconnect structure provides high adhesive strength between copper atoms in a copper-containing structure and a self-aligned copper encapsulation layer, which is selectively deposited only on exposed copper surfaces. A lower level metal interconnect structure comprises a first dielectric material layer and a copper-containing structure embedded in a lower metallic liner. After a planarization process that forms the copper-containing structure, a material that forms Cu—S bonds with exposed surfaces of the copper-containing structure is applied to the surface of the copper-containing structure. The material is selectively deposited only on exposed Cu surfaces, thereby forming a self-aligned copper encapsulation layer, and provides a high adhesion strength to the copper surface underneath. A dielectric cap layer and an upper level metal interconnect structure can be subsequently formed on the copper encapsulation layer.

Abstract: Methods of forming integrated circuit devices include forming an interlayer insulating layer having a trench therein, on a substrate and forming an electrical interconnect (e.g., Cu damascene interconnect) in the trench. An upper surface of the interlayer insulating layer is recessed to expose sidewalls of the electrical interconnect. An electrically insulating first capping pattern is formed on the recessed upper surface of the interlayer insulating layer and on the exposed sidewalls of the electrical interconnect, but is removed from an upper surface of the electrical interconnect. A metal diffusion barrier layer is formed on an upper surface of the electrical interconnect, however, the first capping pattern is used to block formation of the metal diffusion barrier layer on the sidewalls of the electrical interconnect. This metal diffusion barrier layer may be formed using an electroless plating technique.

Abstract: Methods of forming integrated circuit devices include forming an interlayer insulating layer having a trench therein, on a substrate and forming an electrical interconnect (e.g., Cu damascene interconnect) in the trench. An upper surface of the interlayer insulating layer is recessed to expose sidewalls of the electrical interconnect. An electrically insulating first capping pattern is formed on the recessed upper surface of the interlayer insulating layer and on the exposed sidewalls of the electrical interconnect, but is removed from an upper surface of the electrical interconnect. A metal diffusion barrier layer is formed on an upper surface of the electrical interconnect, however, the first capping pattern is used to block formation of the metal diffusion barrier layer on the sidewalls of the electrical interconnect. This metal diffusion barrier layer may be formed using an electroless plating technique.