Abstract: A plasma enhanced chemical vapor deposition (PECVD) method is disclosed for forming a SiON encapsulation layer on a magnetic tunnel junction (MTJ) sidewall that minimizes attack on the MTJ sidewall during the PECVD or subsequent processes. The PECVD method provides a higher magnetoresistive ratio for the MTJ than conventional methods after a 400° C. anneal. In one embodiment, the SiON encapsulation layer is deposited using a N2O:silane flow rate ratio of at least 1:1 but less than 15:1. A N2O plasma treatment may be performed immediately following the PECVD to ensure there is no residual silane in the SiON encapsulation layer. In another embodiment, a first (lower) SiON sub-layer has a greater Si content than a second (upper) SiON sub-layer. A second encapsulation layer is formed on the SiON encapsulation layer so that the encapsulation layers completely fill the gaps between adjacent MTJs.

Abstract: A method for fabricating an improved magnetic tunneling junction (MTJ) structure is described. A bottom electrode is provided on a substrate. A MTJ stack is deposited on the bottom electrode. A top electrode is deposited on the MTJ stack. A first stress modulating layer is deposited between the bottom electrode and the MTJ stack, or a second stress modulating layer is deposited between the MTJ stack and the top electrode, or both a first stress modulating layer is deposited between the bottom electrode and the MTJ stack and a second stress modulating layer is deposited between the MTJ stack and the top electrode. The top electrode and MTJ stack are patterned and etched to form a MTJ device. The stress modulating layers reduce crystal growth defects and interfacial defects during annealing and improve the interface lattice epitaxy. This will improve device performance.

Abstract: A method for fabricating an improved magnetic tunneling junction (MTJ) structure is described. A bottom electrode is provided on a substrate. A MTJ stack is deposited on the bottom electrode. A top electrode is deposited on the MTJ stack. A first stress modulating layer is deposited between the bottom electrode and the MTJ stack, or a second stress modulating layer is deposited between the MTJ stack and the top electrode, or both a first stress modulating layer is deposited between the bottom electrode and the MTJ stack and a second stress modulating layer is deposited between the MTJ stack and the top electrode. The top electrode and MTJ stack are patterned and etched to form a MTJ device. The stress modulating layers reduce crystal growth defects and interfacial defects during annealing and improve the interface lattice epitaxy. This will improve device performance.

Abstract: A perpendicularly magnetized magnetic tunnel junction (p-MTJ) is disclosed wherein a free layer (FL) has a first interface with a MgO tunnel barrier, a second interface with a Mo or W Hk enhancing layer, and is comprised of FexCoyBz wherein x is 66-80, y is 5-9, z is 15-28, and (x+y+z)=100 to simultaneously provide a magnetoresistive ratio >100%, resistance x area product <5 ohm/?m2, switching voltage <0.15V (direct current), and sufficient Hk to ensure thermal stability to 400° C. annealing. The FL may further comprise one or more M elements such as 0 or N to give (FexCoyBz)wM100-w where w is >90 atomic %. Alternatively, the FL is a trilayer with a FeB layer contacting MgO to induce Hk at the first interface, a middle FeCoB layer for enhanced magnetoresistive ratio, and a Fe or FeB layer adjoining the Hk enhancing layer to increase thermal stability.

Abstract: A method for etching a magnetic tunneling junction (MTJ) structure is described. A stack of MTJ layers is provided on a bottom electrode. A top electrode is provided on the MTJ stack. The top electrode is patterned. Thereafter, the MTJ stack not covered by the patterned top electrode is oxidized or nitridized. Then, the MTJ stack is patterned to form a MTJ device wherein any sidewall re-deposition formed on sidewalls of the MTJ device is non-conductive and wherein some of the dielectric layer remains on horizontal surfaces of the bottom electrode.

Abstract: A magnetic tunnel junction (MTJ) is disclosed wherein first and second interfaces of a free layer (FL) with a first metal oxide (Hk enhancing layer) and second metal oxide (tunnel barrier), respectively, produce perpendicular magnetic anisotropy (PMA) to increase thermal stability. In some embodiments, a capping layer that is a conductive metal nitride such as MoN contacts an opposite surface of the Hk enhancing layer with respect to the first interface to reduce interdiffusion of oxygen and nitrogen compared with a TiN capping layer and maintain an acceptable resistance×area (RA) product. In other embodiments, the capping layer may comprise an insulating nitride such as AlN that is alloyed with a conductive metal to minimize RA. Furthermore, a metallic buffer layer may be inserted between the capping layer and Hk enhancing layer. As a result, electrical shorts are reduced and the magnetoresistive ratio is increased.

Abstract: A magnetic tunnel junction (MTJ) is disclosed wherein a free layer (FL) interfaces with a first metal oxide (Mox) layer and second metal oxide (tunnel barrier) to produce perpendicular magnetic anisotropy (PMA) in the FL. In some embodiments, conductive metal channels made of a noble metal are formed in the Mox that is MgO to reduce parasitic resistance. In a second embodiment, a discontinuous MgO layer with a plurality of islands is formed as the Mox layer and a non-magnetic hard mask layer is deposited to fill spaces between adjacent islands and form shorting pathways through the Mox. In another embodiment, end portions between the sides of a center Mox portion and the MTJ sidewall are reduced to form shorting pathways by depositing a reducing metal layer on Mox sidewalls, or performing a reduction process with forming gas, H2, or a reducing species.

Abstract: A method for etching a magnetic tunneling junction (MTJ) structure is described. A stack of MTJ layers is provided on a bottom electrode. A top electrode is provided on the MTJ stack. The top electrode is patterned. Thereafter, the MTJ stack not covered by the patterned top electrode is oxidized or nitridized. Then, the MTJ stack is patterned to form a MTJ device wherein any sidewall re-deposition formed on sidewalls of the MTJ device is non-conductive and wherein some of the dielectric layer remains on horizontal surfaces of the bottom electrode.

Abstract: A seed layer stack with a uniform top surface having a peak to peak roughness of 0.5 nm is formed by sputter depositing an amorphous layer on a smoothing layer such as Mg where the latter has a resputtering rate 2 to 30× that of the amorphous layer. The uppermost seed (template) layer is NiW, NiMo, or one or more of NiCr, NiFeCr, and Hf while the bottommost seed layer is one or more of Ta, TaN, Zr, ZrN, Nb, NbN, Mo, MoN, TiN, W, WN, and Ru. Accordingly, perpendicular magnetic anisotropy in an overlying magnetic layer is substantially maintained during high temperature processing up to 400° C. and is advantageous for magnetic tunnel junctions in embedded MRAMs, spintronic devices, or in read head sensors. The amorphous seed layer is SiN, TaN, or CoFeM where M is B or another element with a content that makes CoFeM amorphous as deposited.

Abstract: A seed layer stack with a uniform top surface having a peak to peak roughness of 0.5 nm is formed by sputter depositing an amorphous layer on a smoothing layer such as Mg where the latter has a resputtering rate 2 to 30× that of the amorphous layer. The seed layer stack may be repeated to give a laminate of two amorphous layers and two smoothing layers, and is advantageous for enhancing performance in magnetic tunnel junctions in embedded MRAMs, spintronic devices, or in read head sensors. A template layer such as NiCr may be formed on the uppermost smoothing layer to promote and maintain perpendicular magnetic anisotropy in an overlying magnetic layer during high temperature processing up to 400° C. The amorphous seed layer is SiN, TaN, or CoFeM where M is B or another element with a content that makes CoFeM amorphous as deposited.

Abstract: A plasma enhanced chemical vapor deposition (PECVD) method is disclosed for forming a SiON encapsulation layer on a magnetic tunnel junction (MTJ) sidewall that minimizes attack on the MTJ sidewall during the PECVD or subsequent processes. The PECVD method provides a higher magnetoresistive ratio for the MTJ than conventional methods after a 400° C. anneal. In one embodiment, the SiON encapsulation layer is deposited using a N2O:silane flow rate ratio of at least 1:1 but less than 15:1. A N2O plasma treatment may be performed immediately following the PECVD to ensure there is no residual silane in the SiON encapsulation layer. In another embodiment, a first (lower) SiON sub-layer has a greater Si content than a second (upper) SiON sub-layer. A second encapsulation layer is formed on the SiON encapsulation layer so that the encapsulation layers completely fill the gaps between adjacent MTJs.

Abstract: A process flow for forming magnetic tunnel junction (MTJ) nanopillars with minimal sidewall residue and minimal sidewall damage is disclosed wherein a pattern is first formed in a hard mask that is an uppermost MTJ layer. Thereafter, the hard mask sidewall is etch transferred through the remaining MTJ layers including a reference layer, free layer, and tunnel barrier between the free layer and reference layer. The etch transfer may be completed in a single RIE step that features a physical component involving inert gas ions or plasma, and a chemical component comprised of ions or plasma generated from one or more of methanol, ethanol, ammonia, and CO. In other embodiments, a chemical treatment with one of the aforementioned chemicals, and a volatilization at 50° C. to 450° C. may follow an etch transfer through the MTJ stack with an ion beam etch or plasma etch involving inert gas ions.

Abstract: A seed layer stack with a uniform top surface having a peak to peak roughness of 0.5 nm is formed by sputter depositing an amorphous layer on a smoothing layer such as Mg where the latter has a resputtering rate 2 × to 30 × that of the amorphous layer. The uppermost seed (template) layer is NiW, NiMo, or one or more of NiCr, NiFeCr, and Hf while the bottommost seed layer is Ta or TaN, for example. Accordingly, perpendicular magnetic anisotropy in an overlying magnetic layer is maintained during high temperature processing up to 400° C. and is advantageous for magnetic tunnel junctions in embedded memory devices, or read head sensors. The amorphous seed layer is SiN, TaN, or CoFeM where M may be B.

Abstract: A method for etching a magnetic tunneling junction (MTJ) structure is described. A stack of MTJ layers is provided on a bottom electrode. A top electrode is provided on the MTJ stack. The top electrode is patterned. Thereafter, the MTJ stack not covered by the patterned top electrode is oxidized or nitridized. Then, the MTJ stack is patterned to form a MTJ device wherein any sidewall re-deposition formed on sidewalls of the MTJ device is non-conductive and wherein some of the dielectric layer remains on horizontal surfaces of the bottom electrode.

Abstract: A magnetic device for magnetic random access memory (MRAM), spin torque MRAM, or spin torque oscillator technology is disclosed wherein a perpendicularly magnetized magnetic tunnel junction (p-MTJ) with a sidewall is formed between a bottom electrode and a top electrode. A first dielectric layer is 3 to 400 Angstroms thick, and formed on the p-MTJ sidewall with a physical vapor deposition RF sputtering process to establish a thermally stable interface with the p-MTJ up to temperatures around 400° C. during CMOS fabrication. The first dielectric layer may comprise one or more of B, Ge, and alloys thereof, and an oxide, nitride, carbide, oxynitride, or carbonitride. The second dielectric layer is up to 2000 Angstroms thick and may be one or more of SiOYNZ, AlOYNZ, TiOYNZ, SiCYNZ, or MgO where y+z>0.

Abstract: A seed layer stack with a uniform top surface having a peak to peak roughness of 0.5 nm is formed by sputter depositing an amorphous layer on a smoothing layer such as Mg where the latter has a resputtering rate 2 to 30× that of the amorphous layer. The uppermost seed (template) layer is NiW, NiMo, or one or more of NiCr, NiFeCr, and Hf while the bottommost seed layer is one or more of Ta, TaN, Zr, ZrN, Nb, NbN, Mo, MoN, TiN, W, WN, and Ru. Accordingly, perpendicular magnetic anisotropy in an overlying magnetic layer is substantially maintained during high temperature processing up to 400° C. and is advantageous for magnetic tunnel junctions in embedded MRAMs, spintronic devices, or in read head sensors. The amorphous seed layer is SiN, TaN, or CoFeM where M is B or another element with a content that makes CoFeM amorphous as deposited.

Abstract: In one aspect, a magnetic data storage device comprises a template layer, an underlayer, and a magnetic recording layer. The template layer includes a patterned array of protruding features. The underlayer is formed on the patterned array of protruding features of the template layer. The underlayer includes an array pattern of protruding features that aligns with the patterned array of protruding features of the template layer. The magnetic recording layer is formed on the underlayer. The magnetic recording layer includes columnar grains of magnetic material separated by grain boundaries of non-magnetic material, with each columnar grain being on a protruding feature of the array pattern of the underlayer, and the grain boundaries being in trenches between the protruding features of the array pattern of the underlayer.