Abstract: There is provided a method of filling one or more recesses by providing the substrate in a reaction chamber; introducing a first reactant, to form first active species, for a first pulse time to the substrate; introducing a second reactant for a second pulse time to the substrate; and introducing a third reactant, to form second active species, for a third pulse time to the substrate. An apparatus for filling a recess is also disclosed and a structure formed using the method and/or apparatus is disclosed.

Abstract: Methods and precursors for forming silicon nitride films are provided. In some embodiments, silicon nitride can be deposited by atomic layer deposition (ALD), such as plasma enhanced ALD. In some embodiments, deposited silicon nitride can be treated with a plasma treatment. The plasma treatment can be a nitrogen plasma treatment. In some embodiments the silicon precursors for depositing the silicon nitride comprise an iodine ligand. The silicon nitride films may have a relatively uniform etch rate for both vertical and the horizontal portions when deposited onto three-dimensional structures such as FinFETS or other types of multiple gate FETs. In some embodiments, various silicon nitride films of the present disclosure have an etch rate of less than half the thermal oxide removal rate with diluted HF (0.5%). In some embodiments, a method for depositing silicon nitride films comprises a multi-step plasma treatment.

Abstract: There is provided a method of filling one or more gaps by providing the substrate in a reaction chamber and introducing a first reactant to the substrate with a first dose, thereby forming no more than about one monolayer by the first reactant on a first area; introducing a second reactant to the substrate with a second dose, thereby forming no more than about one monolayer by the second reactant on a second area of the surface, wherein the first and the second areas overlap in an overlap area where the first and second reactants react and leave an initially unreacted area where the first and the second areas do not overlap; and, introducing a third reactant to the substrate with a third dose, the third reactant reacting with the first or second reactant remaining on the initially unreacted area.

Abstract: There is provided a method of filling one or more gaps by providing the substrate in a reaction chamber and introducing a first reactant to the substrate with a first dose, thereby forming no more than about one monolayer by the first reactant on a first area; introducing a second reactant to the substrate with a second dose, thereby forming no more than about one monolayer by the second reactant on a second area of the surface, wherein the first and the second areas overlap in an overlap area where the first and second reactants react and leave an initially unreacted area where the first and the second areas do not overlap; and, introducing a third reactant to the substrate with a third dose, the third reactant reacting with the first or second reactant remaining on the initially unreacted area.

Abstract: A process for depositing a silicon carbon nitride film on a substrate can include a plurality of complete deposition cycles, each complete deposition cycle having a SiN sub-cycle and a SiCN sub-cycle. The SiN sub-cycle can include alternately and sequentially contacting the substrate with a silicon precursor and a SiN sub-cycle nitrogen precursor. The SiCN sub-cycle can include alternately and sequentially contacting the substrate with carbon-containing precursor and a SiCN sub-cycle nitrogen precursor. The SiN sub-cycle and the SiCN sub-cycle can include atomic layer deposition (ALD). The process for depositing the silicon carbon nitride film can include a plasma treatment. The plasma treatment can follow a completed plurality of complete deposition cycles.

Abstract: Atomic layer deposition (ALD) processes for forming Group VA element containing thin films, such as Sb, Sb—Te, Ge—Sb and Ge—Sb—Te thin films are provided, along with related compositions and structures. Sb precursors of the formula Sb(SiR1R2R3)3 are preferably used, wherein R1, R2, and R3 are alkyl groups. As, Bi and P precursors are also described. Methods are also provided for synthesizing these Sb precursors. Methods are also provided for using the Sb thin films in phase change memory devices.

Abstract: Methods for selectively depositing oxide thin films on a dielectric surface of a substrate relative to a metal surface are provided. The methods can include at least one plasma enhanced atomic layer deposition (PEALD) cycle including alternately and sequentially contacting the substrate with a first precursor comprising oxygen and a species to be included in the oxide, such as a metal or silicon, and a second plasma reactant. In some embodiments the second plasma reactant comprises a plasma formed in a reactant gas that does not comprise oxygen. In some embodiments the second plasma reactant comprises plasma generated in a gas comprising hydrogen.

Abstract: Methods and precursors for depositing silicon nitride films by atomic layer deposition (ALD) are provided. In some embodiments the silicon precursors comprise an iodine ligand. The silicon nitride films may have a relatively uniform etch rate for both vertical and the horizontal portions when deposited onto three-dimensional structures such as FinFETS or other types of multiple gate FETs. In some embodiments, various silicon nitride films of the present disclosure have an etch rate of less than half the thermal oxide removal rate with diluted HF (0.5%).

Abstract: A process for depositing a silicon carbon nitride film on a substrate can include a plurality of complete deposition cycles, each complete deposition cycle having a SiN sub-cycle and a SiCN sub-cycle. The SiN sub-cycle can include alternately and sequentially contacting the substrate with a silicon precursor and a SiN sub-cycle nitrogen precursor. The SiCN sub-cycle can include alternately and sequentially contacting the substrate with carbon-containing precursor and a SiCN sub-cycle nitrogen precursor. The SiN sub-cycle and the SiCN sub-cycle can include atomic layer deposition (ALD). The process for depositing the silicon carbon nitride film can include a plasma treatment. The plasma treatment can follow a completed plurality of complete deposition cycles.

Abstract: Methods of depositing boron and carbon containing films are provided. In some embodiments, methods of depositing B,C films with desirable properties, such as conformality and etch rate, are provided. One or more boron and/or carbon containing precursors can be decomposed on a substrate at a temperature of less than about 400° C. In some embodiments methods of depositing silicon nitride films comprising B and C are provided. A silicon nitride film can be deposited by a deposition process including an ALD cycle that forms SiN and a CVD cycle that contributes B and C to the growing film.

Abstract: Methods and precursors for depositing silicon nitride films by atomic layer deposition (ALD) are provided. In some embodiments the silicon precursors comprise an iodine ligand. The silicon nitride films may have a relatively uniform etch rate for both vertical and the horizontal portions when deposited onto three-dimensional structures such as FinFETS or other types of multiple gate FETs. In some embodiments, various silicon nitride films of the present disclosure have an etch rate of less than half the thermal oxide removal rate with diluted HF (0.5%).

Abstract: Methods and systems for selectively depositing dielectric films on a first surface of a substrate relative to a passivation layer previously deposited on a second surface are provided. The methods can include at least one cyclical deposition process used to deposit material on the first surface while the passivation layer is removed, thereby preventing deposition over the passivation layer.

Abstract: There is provided a method of filling one or more gaps by providing the substrate in a reaction chamber and introducing a first reactant to the substrate with a first dose, thereby forming no more than about one monolayer by the first reactant on a first area; introducing a second reactant to the substrate with a second dose, thereby forming no more than about one monolayer by the second reactant on a second area of the surface, wherein the first and the second areas overlap in an overlap area where the first and second reactants react and leave an initially unreacted area where the first and the second areas do not overlap; and, introducing a third reactant to the substrate with a third dose, the third reactant reacting with the first or second reactant remaining on the initially unreacted area.

Abstract: Methods and precursors for forming silicon nitride films are provided. In some embodiments, silicon nitride can be deposited by atomic layer deposition (ALD), such as plasma enhanced ALD. In some embodiments, deposited silicon nitride can be treated with a plasma treatment. The plasma treatment can be a nitrogen plasma treatment. In some embodiments the silicon precursors for depositing the silicon nitride comprise an iodine ligand. The silicon nitride films may have a relatively uniform etch rate for both vertical and the horizontal portions when deposited onto three-dimensional structures such as FinFETS or other types of multiple gate FETs. In some embodiments, various silicon nitride films of the present disclosure have an etch rate of less than half the thermal oxide removal rate with diluted HF (0.5%). In some embodiments, a method for depositing silicon nitride films comprises a multi-step plasma treatment.

Abstract: Methods and precursors for depositing silicon nitride films by atomic layer deposition (ALD) are provided. In some embodiments the silicon precursors comprise an iodine ligand. The silicon nitride films may have a relatively uniform etch rate for both vertical and the horizontal portions when deposited onto three-dimensional structures such as FinFETS or other types of multiple gate FETs. In some embodiments, various silicon nitride films of the present disclosure have an etch rate of less than half the thermal oxide removal rate with diluted HF (0.5%).

Abstract: A process for depositing a silicon carbon nitride film on a substrate can include a plurality of complete deposition cycles, each complete deposition cycle having a SiN sub-cycle and a SiCN sub-cycle. The SiN sub-cycle can include alternately and sequentially contacting the substrate with a silicon precursor and a SiN sub-cycle nitrogen precursor. The SiCN sub-cycle can include alternately and sequentially contacting the substrate with carbon-containing precursor and a SiCN sub-cycle nitrogen precursor. The SiN sub-cycle and the SiCN sub-cycle can include atomic layer deposition (ALD). The process for depositing the silicon carbon nitride film can include a plasma treatment. The plasma treatment can follow a completed plurality of complete deposition cycles.

Abstract: Methods of depositing boron and carbon containing films are provided. In some embodiments, methods of depositing B,C films with desirable properties, such as conformality and etch rate, are provided. One or more boron and/or carbon containing precursors can be decomposed on a substrate at a temperature of less than about 400° C. In some embodiments methods of depositing silicon nitride films comprising B and C are provided. A silicon nitride film can be deposited by a deposition process including an ALD cycle that forms SiN and a CVD cycle that contributes B and C to the growing film.

Abstract: Atomic layer deposition (ALD) processes for forming Te-containing thin films, such as Sb—Te, Ge—Te, Ge—Sb—Te, Bi—Te, and Zn—Te thin films are provided. ALD processes are also provided for forming Se-containing thin films, such as Sb—Se, Ge—Se, Ge—Sb—Se, Bi—Se, and Zn—Se thin films are also provided. Te and Se precursors of the formula (Te,Se)(SiR1R2R3)2 are preferably used, wherein R1, R2, and R3 are alkyl groups. Methods are also provided for synthesizing these Te and Se precursors. Methods are also provided for using the Te and Se thin films in phase change memory devices.

Abstract: Methods and precursors for depositing silicon nitride films by atomic layer deposition (ALD) are provided. In some embodiments the silicon precursors comprise an iodine ligand. The silicon nitride films may have a relatively uniform etch rate for both vertical and the horizontal portions when deposited onto three-dimensional structures such as FinFETS or other types of multiple gate FETs. In some embodiments, various silicon nitride films of the present disclosure have an etch rate of less than half the thermal oxide removal rate with diluted HF (0.5%).

Abstract: Atomic layer deposition (ALD) processes for forming Group VA element containing thin films, such as Sb, Sb—Te, Ge—Sb and Ge—Sb—Te thin films are provided, along with related compositions and structures. Sb precursors of the formula Sb(SiR1R2R3)3 are preferably used, wherein R1, R2, and R3 are alkyl groups. As, Bi and P precursors are also described. Methods are also provided for synthesizing these Sb precursors. Methods are also provided for using the Sb thin films in phase change memory devices.