Abstract: The present invention relates to a method for producing biodegradable fibers on the basis of a silane compound, said silane compound being crosslinked during production and, at least to some extent, an organic acid being incorporated into the forming crosslinked structure via covalent bonds and/or contributing to the crosslinking. The present invention also relates to the fibers that can be produced by the method according to the invention and to the use thereof.

Abstract: The invention provides a dust repellant and anti-reflective inorganic coating and the method for preparing the coating. The dust repellant and anti-reflective inorganic coating includes nano-porous silica (SiO2) network of about 5 nm to about 35 nm and is characterized by cracks. The method of preparing the dust repellant and anti-reflective inorganic coating on a substrate includes mixing of aqueous SiO2 solution with a solvent. The aqueous SiO2 solution with the solvent is stirred to form a solution. The solution is coated on the substrate to form a film on the surface of the substrate. Thereafter, the film is annealed by heating the film to a temperature of about 500° C. to about 700° C. within a period of about 2 minutes to about 2 hours. Finally, the film is allowed to cool down.

Abstract: The present invention relates to a method for producing biodegradable fibers on the basis of a silane compound, said silane compound being crosslinked during production and, at least to some extent, an organic acid being incorporated into the forming crosslinked structure via covalent bonds and/or contributing to the crosslinking. The present invention also relates to the fibers that can be produced by the method according to the invention and to the use thereof.

Abstract: The invention provides an illumination measuring module which includes a housing and a photo detector. The housing is molded with a plurality of surfaces. Each surface of the housing is affixed with respective side edges of the plurality of the surfaces to form a predetermined shape. Each surface includes an external surface and an inner surface. One surface of the plurality of surfaces is a glass surface. The glass surface transmits illumination collected from an external ambience of the housing to one or more inner surfaces corresponding to the plurality of surfaces. On an inner surface of the glass surface, a plane white sheet is positioned which homogenously scatters illumination collected from the external ambience into the one or more inner surfaces in the housing. The photo detector measures scattered illumination diffused from the one or more inner surfaces corresponding to the plurality of surfaces.

Abstract: The invention concerns a novel silica sol material and its use for producing bioabsorbable and biodegradable silica gel materials having improved properties. The materials such as for example fibers, fibrous nonwoven webs, powders, monoliths and/or coatings are used, for example, in medical technology and/or human medicine, in particular for wound treatment.

Abstract: The invention provides an illumination measuring module which includes a housing and a photo detector. The housing is molded with a plurality of surfaces. Each surface of the housing is affixed with respective side edges of the plurality of the surfaces to form a predetermined shape. Each surface includes an external surface and an inner surface. One surface of the plurality of surfaces is a glass surface. The glass surface transmits illumination collected from an external ambience of the housing to one or more inner surfaces corresponding to the plurality of surfaces. On an inner surface of the glass surface, a plane white sheet is positioned which homogenously scatters illumination collected from the external ambience into the one or more inner surfaces in the housing. The photo detector measures scattered illumination diffused from the one or more inner surfaces corresponding to the plurality of surfaces.

Abstract: The invention provides a dust repellant and anti-reflective inorganic coating and the method for preparing the coating. The dust repellant and anti-reflective inorganic coating includes nano-porous silica (SiO2) network of about 5 nm to about 35 nm and is characterized by cracks. The method of preparing the dust repellant and anti-reflective inorganic coating on a substrate includes mixing of aqueous SiO2 solution with a solvent. The aqueous SiO2 solution with the solvent is stirred to form a solution. The solution is coated on the substrate to form a film on the surface of the substrate. Thereafter, the film is annealed by heating the film to a temperature of about 500° C. to about 700° C. within a period of about 2 minutes to about 2 hours. Finally, the film is allowed to cool down.

Abstract: The present invention relates to a product containing bioabsorbable carrier materials especially for tissue regeneration and to a packaging, and also to processes for the production of the product.

Abstract: The invention relates to a nontoxic polysiloxane material and ripened polysiloxane material which has been formed using one or more different polysiloxane materials. According to the invention, such a ripened polysiloxane material can be spun, for example, into bioabsorbable and/or bioactive fibers and then be further processed into fibrous nonwoven webs.

Abstract: The invention relates to polytitanic acid esters having linear cross-linking structures, obtainable by reacting a titanium compound that is soluble in an alcohol, in water or in a mixture of water and alcohol and that has the composition (I) Ti(R)mXn??(I), wherein the groups R independently mean alkoxy, carboxy, or OH, X means halogen, m=0 to 4, n=0 to 4, and m+n=4, with a compound (II) that contains the following structural unit: [O?CR4—(CR5R3)p—CR1R2—O]?, wherein p is 0 or 1 and wherein (a) R1 and R2 are independently selected from among hydrogen, alkyl and alkenyl, R3 and R5 are independently selected from among hydrogen or an unsubstituted or substituted alkyl or alkenyl, R4 is OH or O(Mx+)1/x, wherein M is a metal or ammonium and x is 1 or 2, or (b) R1 and R2 together mean ?O and R3, R5 and R4 are independently selected from among hydrogen, alkyl and alkenyl, wherein the titanium compound (I) is reacted with compound (II) at a molar ratio of 1 to 0.5-1.

Abstract: The present invention relates to a coating material containing (a) first oxidic particles formed by hydrolytic condensation, in a size range of 5-20 nm, (b) second particles with a diameter in the size range of 80-300 nm, (c) a first aqueous solvent in which the source material for the oxidic particles formed by hydrolytic condensation can be dissolved and which allows or promotes the hydrolysis and condensation thereof, and (d) at least one second solvent, selected among specifically defined alcohols, ethers, organic acids, esters, ketones, amines and amic acids and mixtures thereof.

Abstract: The present invention relates to a product containing bioabsorbable carrier materials especially for tissue regeneration and to a packaging, and also to processes for the production of the product.

Abstract: The invention concerns a novel silica sol material and its use for producing bioabsorbable and biodegradable silica gel materials having improved properties. The materials such as for example fibres, fibrous nonwoven webs, powders, monoliths and/or coatings are used, for example, in medical technology and/or human medicine, in particular for wound treatment.

Abstract: The present invention relates to a coating material containing (a) first oxidic particles formed by hydrolytic condensation, in a size range of 5-20 nm, (b) second particles with a diameter in the size range of 80-300 nm, (c) a first aqueous solvent in which the source material for the oxidic particles formed by hydrolytic condensation can be dissolved and which allows or promotes the hydrolysis and condensation thereof, and (d) at least one second solvent, selected among specifically defined alcohols, ethers, organic acids, esters, ketones, amines and amic acids and mixtures thereof.

Abstract: The invention relates to a nontoxic polysiloxane material and ripened polysiloxane material which has been formed using one or more different polysiloxane materials. According to the invention, such a ripened polysiloxane material can be spun, for example, into bioabsorbable and/or bioactive fibres and then be further processed into fibrous nonwoven webs.

Abstract: In order to influence the human melatonin reservoir, the invention proposes the use of bodies, particularly glasses, having a transmittivity for light waves of a wavelength of about 460 nm of at least 92%, preferably of at least 95% or even 99%, as window glazings, for example, in the construction of houses, for sunrooms, or for indoor riding arenas. If said bodies are coated bodies, the invention proposes the use of a coating sol or gel, containing a hydrolyzable or partially or completely hydrolyzed silane and/or SiO2? and/or ZrO2? particle for producing the coating.

Abstract: The invention relates to ceramic slurry from which ductile ceramic fibrous composites can be produced. They can be stretched under tension without any of the brittleness typical for ceramic materials occurring.

Abstract: A coated glass product includes a glass substrate and a porous antireflection surface coating including SiO2-based particles having a first particle fraction including a first characteristic particle size range and a second particle fraction having a second characteristic particle size range that is different from the first characteristic particle size range. In addition, a method for producing the coated glass product is provided.

Abstract: Hybrid sol comprising [SiOx(OH)y]n particles, where 0<y<4 and 0<x<2, which consist of a mixture of a first fraction of particles having a particle size of 4–15 nm and a second fraction of particles having a mean particle size of 15–60 nm, water and a solvent; obtainable by hydrolytic polycondensation of tetraalkoxysilanes in an aqueous, solvent-containing medium with addition of a monodisperse silicon oxide hydroxide sol having a mean particle size of 15–60 nm and a maximum standard deviation of 20%, and the preparation and use thereof.

Abstract: The invention relates to thermally tempered safety glass comprising an non-abrasive and porous SiO2 layer which is stable during sintering and has a refractive index of between 1.25 and 1.40. The inventive safety glass can be obtained by coating standard soda-lime glass with an aqueous coating solution having a pH value of between 3 and 8 and containing between 0.5 and 5.0 wt. % of [SiOx(OH)y]n particles (0<y<4 and 0<x<2) having a particle size of between 10 and 60 nm, and a surfactant mixture. The coated glass is then dried, thermally hardened at temperatures of at least 600° C. for several minutes, and thermally tempered by a flow of air.