Abstract: A alkali storage cell includes a non-sintered type nickel electrode which includes a highly efficient nickel hydroxide active material and which causes no capacity decrease during an over-discharge operation. The nickel electrode contains an active material composed of nickel hydroxide, a solid solution of at least one of zinc, cadmium, magnesium, and calcium which are added to the nickel hydroxide, and cobalt compound layers which are formed over the surfaces of particles of the nickel hydroxide. The cobalt compound layers have an oxidation number of larger than 2 and a disordered crystal structure. Such an active material can be manufactured by mixing nickel hydroxide powder containing a solid solution of at least one of zinc, cadmium, magnesium, and calcium with either metallic cobalt or a cobalt compound, and subjecting the mixture to heat treatment in the presence of oxygen and alkali.

Abstract: A alkali storage cell includes a non-sintered type nickel electrode which includes a highly efficient nickel hydroxide active material and which causes no capacity decrease during an over-discharge operation. The nickel electrode contains an active material composed of nickel hydroxide, a solid solution of at least one of zinc, cadmium, magnesium, and calcium which are added to the nickel hydroxide, and cobalt compound layers which are formed over the surfaces of particles of the nickel hydroxide. The cobalt compound layers have an oxidation number of larger than 2 and a disordered crystal structure. Such an active material can be manufactured by mixing nickel hydroxide powder containing a solid solution of at least one of zinc, cadmium, magnesium, and calcium with either metallic cobalt or a cobalt compound, and subjecting the mixture to heat treatment in the presence of oxygen and alkali.

Abstract: Fine-grained nickel electrode active material, each of which contributing to electrode reaction; production method of the fine-grained nickel electrode active material; and a nickel alkali storage cell of high capacity which is excellent in over discharge characteristics. In order to produce the fine-grained nickel electrode active material, fine-grained nickel hydroxide is precipitated by adding a given amount of alkali to solution in which at least a nickel compound is dissolved while the solution is stirred. Each of the fine-grained nickel hydroxide has pores with 20 vol % or more of a combined volume of the pores being composed of pores of diameter 60 .ANG. or greater. Next, a given amount of alkali is gradually added to suspension including the fine-grained nickel hydroxide and dissolved cobalt compound so that cobalt hydroxide is precipitated on the external surface of the fine-grained nickel hydroxide. The fine-grained nickel electrode active material is produced in the above mentioned way.