Abstract: A method for manufacturing a high-strength galvanized steel sheet. The method includes a first heating step of holding the steel sheet in a temperature range of 750° C. to 880° C. for 20 s to 600 s in an atmosphere having an H2 concentration of 0.05% to 25.0% by volume and a dew point of ?45° C. to ?10° C., a cooling step, a rolling step of rolling the steel sheet with a rolling reduction of 0.3% to 2.0%, a pickling step of pickling the steel sheet with a pickling weight loss of 0.02 gram/m2 to 5 gram/m2 in terms of Fe, a second heating step of holding the steel sheet in a temperature range of 720° C. to 860° C. for 20 sec. to 300 sec. in an atmosphere having an H2 concentration of 0.05% to 25.0% by volume and a dew point of ?10° C. or lower, and a galvanizing step.

Abstract: Provided are a high-strength steel sheet, which is suitable as a material of automotive parts, and a method for producing the high-strength steel sheet. In the high-strength steel sheet, the C content is 0.15% or less, the area ratio of ferrite is 8% to 45%, the area ratio of martensite is 55% to 85%, the proportion of martensite grains adjacent to only ferrite grains in the entire microstructure is 15% or less, the average crystal grain sizes of ferrite and martensite are each 10 ?m or less, and the area ratio of ferrite grains having a size of 10 ?m or more to all the ferrite grains included in a portion of the steel sheet which extends from 20 to 100 ?m below the surface thereof is less than 5%.

Abstract: A high-strength galvanized steel sheet that includes a chemical composition containing, by mass %, C: 0.15% or more and 0.25% or less, Si: 0.50% or more and 2.5% or less, Mn: 2.3% or more and 4.0% or less, P: 0.100% or less, S: 0.02% or less, Al: 0.01% or more and 2.5% or less, and Fe and inevitable impurities. The steel sheet having a microstructure containing, by an area percentage basis, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 20% or less, and other phases: 10% or less (including 0%), the other phases containing a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%).

Abstract: A high-strength galvanized steel sheet and method for producing the same. The high-strength galvanized steel sheet including a specified chemical composition and a microstructure comprising, in terms of area fraction, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 15% or less, and other phases: 10% or less (including 0%), the other phases comprising a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%), the tempered martensite phase having an average grain size of 8 ?m or less, the ferrite phase having an average grain size of 5 ?m or less, and the retained austenite phase having a C content less than 0.7% by mass.

Abstract: A high-strength hot-dip galvanized steel sheet having a surface coated with a hot-dip galvanized coating, the steel sheet having a chemical composition comprising C: more than 0.10% and less than 0.18%, Si: 0.01 to 1.00%, Mn: 1.5 to 4.0%, P: 0.100% or less, S: 0.020% or less, Al: 0.010 to 0.500%, Cr: 0.010 to 2.000%, Nb: 0.005 to 0.100%, Ti: 0.005 to 0.100%, B: more than 0.0005% and 0.0030% or less, and Fe and incidental impurities, and a method for producing the same. The steel sheet has a microstructure including ferrite having an area fraction in the range of 0 to 10%, martensite having an area fraction in the range of 15 to 60%, tempered martensite having an area fraction in the range of 20 to 50%, and bainitic ferrite having an area fraction in the range of 20 to 50%.

Abstract: A high-strength galvanized steel sheet having improved post-work impact resistance, a method for producing the high-strength galvanized steel sheet, and a high-strength member produced using the steel sheet. The high-strength galvanized steel sheet includes a steel sheet having a microstructure including ferrite and carbide-free bainite, martensite and carbide-containing bainite, and retained austenite, the total area fraction of ferrite and carbide-free bainite being 0% to 55%, the total area fraction of martensite and carbide-containing bainite being 45% to 100%, and the area fraction of retained austenite being 0% to 5%. Additionally, a galvanizing layer is disposed on the steel sheet. The density of gaps that cut across the entire thickness of the galvanizing layer in a cross section of the galvanizing layer, which is taken in the thickness direction so as to be perpendicular to the rolling direction, is 10 gaps/mm or more.

Abstract: A method of manufacturing a galvanized steel sheet having a composition containing, by mass %, C: 0.05% or more and 0.5% or less, Si: 0.01% or more and 2.5% or less, Mn: 0.5% or more and 3.5% or less, P: 0.003% or more and 0.100% or less, S: 0.02% or less, Al: 0.010% or more and 0.5% or less, B: 0.0002% or more and 0.005% or less, Ti: 0.05% or less, a relationship of Ti>4N being satisfied, and the balance comprising Fe and inevitable impurities, and a microstructure containing 60% or more and 95% or less of tempered martensite in terms of area ratio and 5% or more and 20% or less of retained austenite in terms of area ratio.

Abstract: High-strength galvannealed steel sheet including any of a) an oxide containing Fe and Mn, b) an oxide containing Fe and Mn and an Fe oxide, c) an oxide containing Fe and Mn and a Mn oxide, d) an oxide containing Fe and Mn, an Fe oxide, and a Mn oxide, and e) an Fe oxide and a Mn oxide is present in a zinc coated layer. The total amount of oxide is 0.01 to 0.100 g/m2; the ratio by mass % of Mn to Fe, e.g., Mn/Fe, contained in the oxide is 0.10 to 10.00; an oxide of at least one selected from Fe and Mn is present in an amount of 60% or more; and an oxide of at least one selected from Fe and Mn is present in a surface layer portion of a steel sheet in an amount of 0.040 g/m2 or less (not including zero).

Abstract: A method for producing high-strength galvannealed steel sheets having excellent workability and fatigue resistance. The method comprises subjecting a steel sheet to an oxidation treatment, the oxidation treatment including heating the steel sheet in an upstream stage at a temperature in the range of 400° C. to 750° C. in an atmosphere having an O2 concentration of not less than 1000 ppm by volume and a H2O concentration of not less than 1000 ppm by volume and a downstream stage at a temperature in the range of 600° C. to 850° C. in an atmosphere having an O2 concentration of less than 1000 ppm by volume and a H2O concentration of not less than 1000 ppm by volume. The method further comprises subjecting the steel sheet to reducing annealing, hot-dip galvanizing treatment and alloying treatment.

Abstract: A high-strength galvanized steel sheet and a method for producing the steel sheet. The steel sheet has a composition that includes C: 0.030% to 0.250%, Si: 0.01% to 3.00%, Mn: 2.00% to 10.00%, P: 0.001% to 0.100%, S: 0.0001% to 0.0200%, N: 0.0005% to 0.0100%, Ti: 0.005% to 0.200%, on a mass basis, and Fe and inevitable impurities. Additionally, the steel sheet has concentration of solute Mn at a depth of 5 ?m or less from a surface of the steel sheet that is 1.50% by mass or less, and a value obtained by dividing the average mass percentage of Mn in retained austenite by the average mass percentage of Mn in ferrite is 2.0 or more.

Abstract: A high-strength hot-dip coated hot-rolled steel sheet excellent in terms of surface appearance quality and coating adhesiveness and a method for manufacturing. The method includes performing hot rolling followed by pickling on steel to form a pickled steel sheet, the steel having a chemical composition containing, by mass %, C: 0.02% or more and 0.30% or less, Si: 0.01% or more and 1.0% or less, Mn: 0.3% or more and 2.5% or less, P: 0.08% or less, S: 0.02% or less, Al: 0.001% or more and 0.20% or less, and Fe and inevitable impurities. The method further includes performing rolling with a rolling reduction ratio of 1% or more and 10% or less, and a hot-dip coating treatment. The obtained steel sheet has an arithmetic average roughness Ra of 2.0 ?m or less on the surface of the steel sheet, and a tensile strength of 590 MPa or more.

Abstract: There is provided a method for manufacturing a high-strength galvannealed steel sheet having excellent coating adhesiveness and corrosion resistance whose base material is a high-strength steel sheet containing Si and Mn. The method includes performing an oxidation treatment on a steel sheet including Si and Mn in a first zone having an atmosphere of an oxygen concentration in the range of more than 0 vol % and less than 1 vol %, thereafter performing an oxidation treatment in a second zone having an atmosphere of an oxygen concentration in the range of 1 vol % or more, thereafter performing reduction annealing and galvanizing, and further performing an alloying treatment by heating the galvanized steel sheet.

Abstract: Provided are a cold-rolled steel sheet which can preferably be used for manufacturing a high-strength galvanized steel sheet and methods for manufacturing the steel sheets. The cold-rolled steel sheet has a specified chemical composition, in which the Mn concentration in a surface layer of the steel sheet satisfies relational expression (1) and relational expression (2) below. 8?(Cp/Cc)×Mn??(1) (Cmin/Cc)×Mn?2.5??(2) where Cp: maximum Mn concentration in a region within 0.5 ?m of the surface of a steel sheet in the thickness direction; Cc: average Mn concentration in a region from a position located 5 ?m from a surface of a steel sheet in the thickness direction to a position located 5 ?m from an opposite surface in the thickness direction; Cmin: minimum Mn concentration in a region from 0.

Abstract: A galvannealed steel sheet having a galvanized layer on a surface thereof is provided, having a composition which contains C: 0.10% to 0.35%, Si: 0.3% to 3.0%, Mn: 0.5% to 3.0%, P: 0.001% to 0.10%, Al: 0.01% to 3.00%, and S: 0.200% or less on a mass basis, the remainder being Fe and incidental impurities. The steel sheet has a SiC/SiO2 ratio of more than 0.20, the SiC/SiO2 ratio being a ratio of SiC amount to SiO2 amount at a depth of 1 ?m or less in the steel sheet from an interface between the steel sheet and the galvanized layer, and Fe in the galvanized layer constitutes 8% to 13% by mass.

Abstract: A high-strength galvanized steel sheet comprising a cold-rolled steel sheet, an intermetallic compound formed on the cold-rolled steel sheet, and a galvanizing layer formed on the intermetallic compound, the cold-rolled steel sheet having a specific composition and a microstructure having a martensite area ratio of 7% or more and less than 25% and a ferrite area ratio of 50% or more and which includes a base metal surface portion in which the amount of internal oxides per single side is 0.05 g/m2 or less.

Abstract: A high-strength galvanized steel sheet comprising a cold-rolled steel sheet, an intermetallic compound formed on the cold-rolled steel sheet, and a galvanizing layer formed on the intermetallic compound, the cold-rolled steel sheet having a specific composition and a microstructure having a martensite area ratio of 7% or more and less than 25% and a ferrite area ratio of 50% or more and which includes a base metal surface portion in which the amount of internal oxides per single side is 0.05 g/m2 or less.

Abstract: A hot-dip galvanized steel sheet having a good appearance and good adhesion to a coating, the hot-dip galvanized steel sheet having a composition containing, on a mass basis: C: 0.08% or more and less than 0.20%, Si: 0.1% to 3.0%, Mn: 0.5% to 3.0%, P: 0.001% to 0.10%, Al: 0.01% to 3.00%, and S: 0.200% or less, a remainder being Fe and incidental impurities, wherein the hot-dip galvanized steel sheet includes an internal oxidation layer and a decarburized layer, the internal oxidation layer having a thickness of 5 ?m or less, the decarburized layer having a thickness of 20 ?m or less, and 50% or more by area of the internal oxidation layer is composed of a Si oxide containing Fe and/or Mn represented by Fe2XMn2-2XSiOY, wherein X ranges from 0 to 1, and Y is 3 or 4.

Abstract: A method of producing a galvannealed steel sheet whereby favorable coating appearance can be obtained with high coating adhesion even in the case of galvannealing a steel strip whose Si content is 0.2 mass % or more, and a decrease in tensile strength can be prevented by lowering the alloying temperature. Mixed gas of humidified gas and dry gas, and dry gas are supplied to a soaking zone in an annealing furnace. The mixed gas is timely supplied from a position of lower half of the soaking zone. The dry gas is timely supplied from near an upper hearth roll in the soaking zone, and furnace gas is timely discharged from a gas discharge port located higher than the upper hearth roll, to control a dew point in at least an uppermost part of the soaking zone to ?20° C. or more and 0° C. or less.

Abstract: Provided is a hot-dip Al—Zn—Mg—Si coated steel sheet having good corrosion resistance in flat parts and edge parts, and also having excellent worked part corrosion resistance. The hot-dip Al—Zn—Mg—Si coated steel sheet includes a base steel sheet and a hot-dip coating on a surface of the base steel sheet. The hot-dip coating includes an interfacial alloy layer present at an interface with the base steel sheet and a main layer present on the interfacial alloy layer, and contains from 25 mass % to 80 mass % of Al, from greater than 0.6 mass % to 15 mass % of Si, and from greater than 0.1 mass % to 25 mass % of Mg. The Mg content and Si content in the hot-dip coating satisfy formula (1): MMg/(MSi?0.6)>1.7 ??(1) where MMg represents the Mg content (mass %) and MSi represents the Si content (mass %).

Abstract: A high-strength galvanized steel sheet and method for producing the same. The high-strength galvanized steel sheet including a specified chemical composition and a microstructure comprising, in terms of area fraction, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 15% or less, and other phases: 10% or less (including 0%), the other phases comprising a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%), the tempered martensite phase having an average grain size of 8 ?m or less, the ferrite phase having an average grain size of 5 ?m or less, and the retained austenite phase having a C content less than 0.7% by mass.