Abstract: The invention provides a prepreg that can give a fiber-reinforced composite material exhibiting stable and excellent interlaminar fracture toughness and impact resistance under wide molding conditions. The prepreg includes at least a reinforcement fiber [A], a thermosetting resin [B], and the following component [C] wherein 90% or more of the material [C] is present inside a region of the prepreg that extends from any surface of the prepreg to a prepreg site having, from the surface, a depth of 20% of the thickness of the prepreg. The component [C] satisfies requirements that (i) the storage elastic modulus G? of the material constituting the particles is more than 1 MPa, and 70 MPa or less at 180° C., and that (ii) the ratio of the storage elastic modulus G? of the material constituting the particles at 160° C. to the storage elastic modulus G? of the material at 200° C. ranges from 1 to 5; and is insoluble in the thermosetting resin [B].

Abstract: The invention provides a prepreg that can give a fiber-reinforced composite material exhibiting stable and excellent interlaminar fracture toughness and impact resistance under wide molding conditions. The prepreg includes at least a reinforcement fiber [A], a thermosetting resin [B], and the following component [C] wherein 90% or more of the material [C] is present inside a region of the prepreg that extends from any surface of the prepreg to a prepreg site having, from the surface, a depth of 20% of the thickness of the prepreg. The component [C] satisfies requirements that (i) the storage elastic modulus G? of the material constituting the particles is more than 1 MPa, and 70 MPa or less at 180° C., and that (ii) the ratio of the storage elastic modulus G? of the material constituting the particles at 160° C. to the storage elastic modulus G? of the material at 200° C. ranges from 1 to 5; and is insoluble in the thermosetting resin [B].

Abstract: Provided are: a fiber-reinforced composite material which is suppressed in morphology variation due to the molding conditions, while having excellent mode I interlaminar fracture toughness and excellent wet heat resistance; an epoxy resin composition for obtaining the fiber-reinforced composite material; and a prepreg which is obtained using the epoxy resin composition. An epoxy resin composition for fiber-reinforced composite materials, which contains at least the following constituent elements [A]-[F], and which is characterized by containing 5-25 parts by mass of constituent element [C] and 2-15 parts by mass of constituent element [E] per 100 parts by mass of the total epoxy resin blended therein. [A] A bifunctional amine type epoxy resin. [B] A tetrafunctional amine type epoxy resin. [C] A bisphenol F type epoxy resin having an epoxy equivalent weight of 450-4,500. [D] An aromatic amine curing agent. [E] A block copolymer having a reactive group that can be reacted with as epoxy resin.

Abstract: The invention provides a fiber reinforced composite material having high interlaminar toughness and compressive strength under wet heat conditions, as well as an epoxy resin composition for production thereof and a prepreg producible from the epoxy resin composition. The prepreg comprises at least constituents [A], [B], and [C] as specified below and reinforcement fiber, wherein 90% or more of constituent [C] exists in the depth range accounting for 20% of the prepreg thickness from the prepreg surface: [A] epoxy resin [B] epoxy resin curing agent [C] polymer particles insoluble in epoxy resin and falling under any of the following [Cx] to [Cz]: [Cx] polymer particles insoluble in epoxy resin and giving a particle diameter distribution chart meeting the following requirements from (x-i) to (x-iii): (x-i) the chart has at least two peaks, (x-ii) the particles giving the two highest peaks have a diameter ratio in the range of 1.

Abstract: Transferring and/or fusing part(s) for electrophotographic use consisting of a base and a releasing layer which is made of an organic-inorganic hybrid material containing fluoroalkyl group and formed on said base, is provided in the present invention. Said transferring and/or fusing part(s) have an excellent heat resistance, durability and toner releasing property.