Water dispersed primers

Abstract

A water dispersed primer composition comprising a solution of a halogenated hydrocarbon polymer in organic solvent; and a dispersing agent added to the solution to form a fluid primer to be dispersed in water to provide the water dispersed primer composition. Optionally, fluid primers may include photoreactive components to provide photoreactive water dispersed primer compositions. The invention further includes water based priming adhesive compositions comprising an adhesive dispersion of an adhesive polymer dispersed in water, and a primer mixed with the adhesive dispersion to form the priming adhesive.

Description

[0001] This application is a continuation-in-part of U.S. application Ser. No. 09/558,464, filed April 25, 2000.

DESCRIPTION

[0002] 1. Field of the Invention

[0003] The present invention relates to primer compositions that may be mixed with water and water-based adhesives to provide a range of primers and priming adhesive compositions for bond improvement between polymers of similar or dissimilar types. Compositions according to the present invention optionally include olefinically unsaturated monomers or oligomers for added bond strength after exposure to ultraviolet radiation. More particularly the present invention relates primarily to water-based dispersions of surface modifying components for enhancing bond formation between substrates, such as polyolefins, which are known for low interfacial bond strength. Priming adhesives of the present invention improve adhesive bonding between materials without the application of surface pre-treatments.

[0004] 2. Background of the Invention

[0005] Adhesives provide a relatively rapid and convenient way for attaching one type of material to another. Over the years, development of adhesive systems has addressed ways to modify the strength of the adhesive bond between selected materials. Depending on the application, the adhesive of choice may include a pressure sensitive adhesive, a structural adhesive, a hot-melt adhesive or a repositionable adhesive. Regardless of the wide range of available adhesives, the surfaces of some commonly occurring polymer substrates still lack suitable adhesive affinity to form strong bonds with other materials, whether similar or dissimilar. Lack of bonding to surfaces with low adhesive affinity also affects the bonding and retention of surface coatings or printing inks that may be used for surface marking or decoration.

[0006] One solution to poor bond formation and poor retention of coatings and inks lies in the use of special treatments to change the condition of a surface by increasing its surface energy. Surface treatments for increased surface energy include oxidizing pretreatments or the use of adhesion promoters. Oxidizing pre-treatments include the use of flame, ultraviolet radiation, corona discharge, and chemical oxidizing agents and the like. Adhesion promoters include chemical compositions containing e.g. solutions of styrene-ethylene/butylene-styrene block copolymers or acrylate polymers in an organic solvent. These compositions improve the bonding of pressure sensitive adhesives and structural adhesives to polymer substrates.

[0007] Unfortunately, these methods for raising surface energy are not without problem. For example, chemical oxidizing agents are typically hazardous materials requiring special handling. Surface treatment using flame, corona discharge, etc. usually requires special equipment of a design more suited to sheet or film or web processing than to surface treatment of shaped articles.

[0008] Both oxidizing and adhesion promoter pre-treatments provide improvement in bond formation associated with low surface energy polymers such as polyethylene (PE), polypropylene (PP), ethylene-propylene-diene terpolymer (EPDM) and ethylene-alpha olefin copolymers. Substrates of this type may also include ethylene-vinyl acetate copolymers as representative of polymers that are substantially free from ethylenic unsaturation.

[0009] Polymeric substrates that have some degree of ethylenic unsaturation also benefit from the use of surface pre-treatments. It is known, for example, that rubbers comprising styrene/butadiene copolymers (SBR) require treatment with chlorinating agents including solutions of halogen donors such as trichloroisocyanuric acid, and N,N-dichlorobenzenesulfonamide, for improved bonding with adhesive bonding agents. Such halogen donors may be incorporated into primers or adhesives separately. The effectiveness of treatment by chlorination appears somewhat limited to substrates having a high level of ethylenic unsaturation such as polybutadiene, polyisoprene, natural rubber, styrene-butadiene copolymers, polychloroprene and the like. Also the addition of halogen donors reduces the stability of some adhesives, including polyurethane adhesives.

[0010] Further improvement in bonding to numerous types of substrates may be possible by abrading the surface of a substrate even before applying any pre-treatment. Mechanical means for surface roughening then represents a preliminary step to surface pre-treatments. Regardless of their effectiveness, pre-treatments represent an additional step in the process of manufacturing a product. Additional process steps incur additional time and expense and thereby add undesirable cost to a final product.

[0011] The development of primer pre-treatments, primarily in solvent, has yielded some improvement in adhesive bonding to low energy surfaces. U.S. Pat. No. 6,008,286, for example, provides compositions comprising mixtures of hydrocarbon polymers, halogen-substituted hydrocarbon polymers and substituted aliphatic isocyanates which, coated from solvent, improve the bond between low energy substrates and adhesives, coatings, printing inks and the like. Unfortunately the benefits of solvent-based primers are diminished by the need to limit volatile organic compounds (VOC) to a level that avoids health hazards and prevents environmental contamination.

[0012] Ultraviolet irradiation of solvent-based primers, including chlorinated polymers, may lead to modification of polyolefin surfaces. United States Patent No. U.S. Pat. No. 4,303,697 describes the use of a primer containing chlorinated polypropylene applied to the surface of a thermoplastic polyolefin. Subsequent exposure to ultraviolet radiation of the surface improves the adhesion of paint coatings. U.S. Pat. No. 4,859,540 compares the benefits of repeated exposure to low intensity ultraviolet radiation versus a single exposure to high intensity ultraviolet as a means for improving adhesion of solvent-based primers to both adhesives and substrates. Multiple exposures to low intensity ultraviolet radiation is time consuming and probably adds to processing costs.

[0013] The description of solvent-based primer solutions and water-based priming dispersions of chlorinated polymers provided by WO 98/05704 suggests that coating of such primers on a polyolefin surface, followed by exposure to ultraviolet radiation, improves adhesion to the polyolefin surface. Stabilizers for the water-based chlorinated polymer dispersions of WO 98/05704 include surfactants, emulsifiers, thickening agents and sodium hydroxide. These materials are moisture sensitive and require careful control in order to attain a strong and hydrolytically stable bond of the primer to either a low-energy substrate or an adhesive.

[0014] U.S. Pat. No. 5,446,083 describes a coating formulation comprising an aqueous dispersion including an olefinic unsaturated monomer and a solution of a chlorinated polyolefin in organic solvent. Stabilization of the dispersed phase, of the aqueous dispersion, requires the use of a surfactant. Unsaturated monomer in the dispersed phase becomes polymerized upon exposure to heat, ultraviolet radiation or electron beam radiation. This reference indicates lack of compatibility between chlorinated polyolefin compositions and film forming polymers including polyurethanes and acrylic polymers. To add further confusion, U.S. Pat. No. 5,446,083 teaches successful use of coatings containing chlorinated polyolefins in the presence of polymerizable acrylate monomers, suspension polymerized polyacrylates or mixtures thereof.

[0015] Solvent based or aqueous based thermosettable primers may be used, for bond improvement, without a flame or corona preliminary treatment. U.S. Pat. No. 6,001,469 describes primers and topcoats of this type used with e.g. thermoplastic polyolefins (TPO) and reaction injection molded polyurethane (RIM). These materials may be suitably cured on the substrate at temperatures in the region of 130° C. for 30 minutes. Similarly WIPO publication WO 94/28077 describes aqueous-based compositions requiring heat treatment at 130° C. for 40 minutes. It is known (see e.g. R. Ryntz in “Waterborne, High Solids Powder Coatings Symposium,” Univ. of Southern Mississippi 1995), that high temperature treatment may also affect the surface morphology of thermoplastic polyolefin polymers. Such changes may be beneficial in some cases, but in others the relatively high temperature for curing may be sufficiently close to the material melting point to produce substrate dimensional changes and associated problems.

[0016] Attempts to include primer compositions and/or adhesion promoter compositions with adhesive or coating compositions, have met with limited success. According to an article in the Journal of Coating Technology, 65, No. 827 p. 21 (1993), it is known that chlorinated polyolefin primer compositions do not provide the same level of priming when included as an adhesive additive. The chlorine content of a chlorinated polyolefin affects its use as a primer or coating additive. A chlorinated polyolefin having a chlorine content below about 30 wt % on a 15,000 number average molecular weight polymer will be incompatible with most coating resins. It is known that effective priming compositions typically have a chlorine content less than 30 wt. %. However, high chlorine content could also lead to poor priming performance because of solubility of such primers in solvent-based topcoat compositions.

[0017] Similar limitation of use applies to water based adhesive compositions and primers for polyolefins, described in U.S. Pat. No. 5,298,552. These compositions appear primarily useful for applications requiring bonding of polyolefin sheets to porous fibrous substrates such as water-absorbent paper board and similar paper pulp or wood fiber products. Also, in this case, the composition of the adhesive component of the formulations appears to have more impact on the bonding force developed between a polyolefin and absorbent substrate than the chlorinated polyolefin. It appears that common solvents, such as toluene, xylene etc. are unsuitable for use with compositions described in U.S. Pat. No. 5,298,552. Instead, the preferred solvent is relatively uncommon dodecyl benzene.

[0018] Known water based primer compositions derive their stability from the use of conventional surfactant materials to keep active components dispersed in the aqueous phase. The amount of surfactant requires careful control. Insufficient surfactant leads to instability and precipitation of the dispersed phase. Addition of too much surfactant produces a primer having poor adhesion to substrates that require priming. Good adhesion is essential to effective performance of priming compositions.

[0019] In view of the above described deficiencies associated with the use of known adhesive bonding agents, particularly the use of multiple treatments at substrate surfaces, the present invention has been developed to alleviate these drawbacks and provide further improvement and cost reduction. These enhancements and benefits are described in greater detail hereinbelow with respect to several alternative embodiments of the present invention.

SUMMARY OF THE INVENTION

[0020] The present invention in its several disclosed embodiments alleviates the drawbacks described above with respect to water-dispersed primers and priming adhesive compositions and incorporates several additionally beneficial features. Of particular interest is the provision of primer solutions suitable for mixing with water and aqueous based adhesive dispersions to provide water dispersed primers and priming adhesive compositions. Depending upon the application, the variation of dispersed primer relative to dispersed adhesive produces a range of compositions from those functioning essentially as primers to others that contribute properties of priming and placement of an adhesive on a treated surface. Water dispersed primers and priming adhesives, according to the present invention, allow substantial reduction in the use of solvents. Solvent removal provides the benefit of substantial elimination of volatile organic compound (VOC) emission during improved processing and bond formation between polymer substrates. Improved processing refers to the elimination of pre-treatments, such as flame and corona treatments, and the beneficial use of ultraviolet radiation for improved adhesive bonding using primers and priming adhesives according to the present invention.

[0021] More specifically the present invention provides a water dispersed primer composition comprising a solution of a halogenated hydrocarbon polymer in organic solvent and a dispersing agent added to the solution to form a fluid primer to be dispersed in water to provide the water dispersed primer composition. Organic solvents may be selected from cyclohexane, heptane, hexane, xylene, toluene, chlorotoluene, mixed hydrocarbon solvents and mixtures thereof.

[0022] The present invention further includes a water based priming adhesive composition comprising an adhesive dispersion of an adhesive polymer dispersed in water, and a primer mixed with the adhesive dispersion to form the priming adhesive. The primer comprises a solution of a halogenated hydrocarbon polymer in organic solvent selected from the group consisting of cyclohexane, heptane, hexane, xylene, toluene, chlorotoluene, mixed hydrocarbon solvents and mixtures thereof. A primer composition may optionally contain a particulate dispersing agent.

[0023] A photoreactive, fluid primer composition, according to the present invention comprises a solution having a halogenated hydrocarbon polymer dissolved in an organic solvent selected from the group consisting of cyclohexane, heptane, hexane, xylene, toluene, chlorotoluene, mixed hydrocarbon solvents, and mixtures thereof, and further including a dispersing agent.

[0024] Optionally, fluid primer compositions may include organic solvent soluble halogenated hydrocarbon polymers, photoreactive components and combinations thereof.

[0025] A photoreactive water dispersed primer composition comprises water and a fluid primer composition as described previously.

Definitions

[0026] The following definitions clarify the meaning of terms used herein:

[0027] The term, “water-based” may be used interchangeably with the term “water dispersed” to indicate a composition having a fluid primer as a dispersed phase in water.

[0028] The term, “fluid primer” refers to a solution of polymers and optionally monomers and, oligomers in organic solvents that also contain a dispersing agent.

[0029] The term “photoreactive component” refers to monomeric or oligomeric species that react to form polymers or crosslinked polymers under the influence of actinic radiation.

[0030] The beneficial effects described above apply generally to water dispersed primers, priming adhesives and related compositions. Specific compositions providing these benefits will be described in detail hereinbelow.

DETAILED DESCRIPTION OF THE INVENTION

[0031] As required, detailed embodiments of the present invention are disclosed herein, however, it is to be understood that the disclosed embodiments are merely exemplary of the various and alternative forms of the invention. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the present invention.

[0032] Water dispersed primers and priming adhesives, according to the present invention, may be produced by adding a solution of a primer, in organic solvent, to water, or to a water dispersed adhesive composition or to a solvent based adhesive. The resulting compositions improve adhesive bonding to surfaces known to have low affinity for adhesive bond formation. Adhesive bonding improves even in the absence of oxidizing pre-treatments and conventional adhesion promoters.

[0033] Commonly owned U.S. Pat. No. 6,008,286 provides solutions of surface priming compositions dissolved in organic solvents. These priming compositions improve bonding of e.g. adhesives, inks and other coatings to substrates including organic high polymers that can be synthetic or natural and typically include elastomeric materials.

[0034] The benefits of the previously discussed solutions of primers in organic solvent may be realized, according to the present invention, using primer compositions dispersed in water or aqueous adhesive dispersions. Combinations of differing quantities of primer solutions with water and water dispersed adhesives provide a range of compositions that either behave simply as surface primers or priming adhesives. Surfaces primed with these water-based dispersions participate in strong adhesive bond formation with similar and dissimilar substrates. Surface primers and priming adhesives may be applied by spraying, or brushing, or wiping, or any other conventional coating method, followed by drying, by evaporation, to produce a primed surface. The use of water dispersed primers and priming adhesives has been shown to eliminate the need for pre-treatment of substrate surfaces.

[0035] Substrates suitable for use with primers and priming adhesives according to the present invention include uniform polymeric sections, filled materials and foamed materials. They fall mainly into the two classes of ethylenically unsaturated materials and those containing little or no ethylenic unsaturation, as follows:

[0036] Substrates with ethylenic unsaturation include: polybutadiene, polyisoprene, styrene-butadiene copolymer, styrene-butadiene-styrene block copolymer.

[0037] Substrates with essentially no ethylenic unsaturation include ethylene-propylene-diene terpolymer (EPDM), styrene-ethylene-butylene-styrene block copolymer, ethylene-propylene rubber, butyl rubber, bromo-butyl rubber, ethylene-alpha olefin copolymer, polypropylene, polyethylene, polyethylene vinyl acetate, and synthetic leather and blends and mixtures thereof.

[0038] Water dispersed primer compositions contain active materials based upon halogenated hydrocarbon polymers dissolved in an organic solvent. A priming composition may also include non-halogenated hydrocarbon polymers as a blend with halogenated hydrocarbon polymers. Halogenated hydrocarbon polymers may also include functional groups such as sulfonate groups, carboxylic acid anhydride groups, hydroxyl groups, epoxide groups, carboxylic acid ester groups, carboxylic acid amide groups, carboxylic acid groups and the like. Suitable halogenated hydrocarbon polymers include chlorinated polyethylene, chlorinated polypropylene, chlorosulfonated polyethylene, maleic anhydride modified chlorinated polyethylene and blends and reaction products thereof. Preferred halogenated hydrocarbon polymers are chlorinated polypropylenes modified with maleic anhydride and available commercially as CP 343-1, available from Eastman Chemical Company, Kingsport Tenn., HARDLEN CY-9122P, available from Toyo Kasei Kogyo, Ltd., Osaka, Japan, and HYPALON CP-826, available from DuPont Dow Elastomers L.L.C., Wilmington Del.

[0039] Non-halogenated hydrocarbon polymers, suitable for blend formation with halogenated polymers, may also include functional groups such as: carboxylic acid anhydride groups; hydroxyl groups; epoxide groups; carboxylic acid ester groups; carboxylic acid amide groups; carboxylic acid groups and the like. Suitable polymers include styrene-ethylene/butylene-styrene triblock copolymers (e.g. KRATON G-1657 available from Shell Chemical Co., Houston Tex.), maleic anhydride modified styrene-ethylene/butylene-styrene triblock copolymers, maleic anhydride modified ethylene-propylene copolymers, maleic anhydride modified polypropylene, maleic anhydride modified ethylene vinyl acetate copolymers and ethylene/butylene copolymers having terminal hydroxy functionality. Preferred non-halogenated hydrocarbon, commercially available polymers include: KRATON FG-1901X; and HPVM 2203, both available from Shell Chemical Co., Houston Tex.; FUSABOND MC-190D, available from DuPont Canada Inc., Mississauga, Ontario, Canada; and an ethylene vinyl acetate copolymer containing 72% ethylene, available from Polysciences Inc., Warrington Pa.

[0040] Preferred primers and priming adhesives require addition of solutions of halogenated hydrocarbon polymers, and optionally their blends with non-halogenated hydrocarbon polymers, in organic solvent, to water, water-dispersed adhesives and solution adhesives. Other optional components of primer compositions according to the present invention include unsaturated photoreactive components preferably ultraviolet radiation sensitive monomers and oligomers.

[0041] Solvents used in the preparation of surface primer solutions include aliphatic hydrocarbons, aromatic hydrocarbons and halogenated derivatives thereof. Suitable solvents include cyclohexane, heptane, hexane, xylene, toluene, chlorotoluene and mixed hydrocarbon solvents, available from Shell Chemical Co., Houston Tex., as SHELL CYCLO SOL (R) 100 and SHELL CYCLO SOL (R) 150. Preferably, the organic solvent, for priming compositions, is a mixture including a weight ratio of from about 95:5 to about 5:95, more preferably from about 80:20 to about 20:80, and most preferably from about 60:40 to 40:60 of either cyclohexane or heptane combined with xylene or SHELL CYCLO SOL (R) 100 or SHELL CYCLO SOL (R) 150. Alcohols, aliphatic ketones, and esters of carboxylic acids may also be used as solvents or for dispersion stabilization.

[0042] Solutions of halogenated hydrocarbon polymers, or their blends with non-halogenated hydrocarbon polymers in the solvent mixtures, have solids contents from about 0.5 wt. % to about 30 wt. %, preferably about 2.0 wt. % to about 15 wt. %. Solutions of this type may be added to water, water dispersed adhesives, aqueous solutions of olefinically unsaturated species and solution adhesives to provide primers and priming adhesives according to the present invention. Preferably the solutions are dispersed in the dispersion medium using from about 0.1 wt. % to about 5.0 wt. % of a dispersing aid such as fumed silica. The ratio of a solution of primer to dispersion phase formulation may be from about 90:10 to about 10:90, preferably about 50:50 to about 15:85 and more preferably about 25:75 based on the weights of each material.

[0043] Optional inclusion of olefinically unsaturated species, such as olefinic monomers and oligomers, according to the present invention, provides photosensitive priming compositions that preferably react upon exposure to ultraviolet radiation. Preferred olefinic monomers and oligomers include acrylate and substituted acrylate functionality having one or more reactive substituents. The term (meth)acrylate, used herein, refers to a molecule having either acrylate or methacrylate functionality in its structure. Suitable examples of olefinic unsaturated monofunctional monomers include alkyl (meth)acrylates, acrylamides, N-alkylacrylamides, vinyl halides and heterocyclic vinyl compounds. Multifunctional monomers and oligomers include those having a plurality of reactive substituents including di(meth)acrylate, tri(meth)acrylate and tetra-(meth)acrylate. In addition, the olefinically unsaturated monomer, oligomer or blend may contain one or more functional groups such as carboxylic acid, glycidyl, amino, halogen and hydroxyl. Suitable examples include (meth)acrylic, glycidyl (meth)acrylate, 2-hydroxyl ethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, the reaction products of hydroxy functional (meth)acrylates with alkyl or aromatic, saturated or ethylenically unsaturated monobasic or dibasic acid anhydrides, 2-dimethylaminoethyl (meth)acrylate, 2-chloroethyl (meth)acrylate and the like. Others may include maleic anhydride, maleic acid, maleimide, bismaleimides, mono and dialkyl maleic acid esters, fumaric acid and mono and dialkyl fumaric acid esters.

[0044] Acrylate or methacrylate terminated oligomers or polymers may also be used alone or in blends suitable examples include water-dispersed polyurethane acrylates such as NR-440 and NR-3709 available from Neo Resins, Wilmington, Mass., polybutadienediacrylate, polyurethane acrylates and epoxy acrylates, available from Sartomer Company, Exton, Pa. They may be present in the water dispersed primer or primer adhesive compositions from 0.1 wt. % to about 10 wt. %, more preferably from 0.1 wt. % to about 5 wt. %. The olefinic unsaturated monomers or oligomers or blends thereof may be present only in the solvent phase, only in the aqueous phase or both depending upon solubility of the monomer or oligomer or blend.

[0045] Most commercial sources of ultraviolet radiation can be used to irradiate the dried, primed substrate. As used herein, the term “ultraviolet radiation” is intended to mean all radiation emitted by an ultraviolet source within the wavelength range of 200-400 nm. It is important to control the amount of radiation used. Too little radiation will not adequately bond the primer to the substrate, while excessive ultraviolet radiation will cause degradation of the exposed surface. In the process of this invention, it is preferred to adjust the radiation exposure time so that the radiation energy received by the primed surface is about 0.10-6.0 J/cm2. The optimum radiation energy range is about 0.20-3.5 J/cm2.

[0046] An ultraviolet arc lamp system commercially available from RPC Industries, Hayward, Calif., uses commercially available 47 cm, high intensity, medium pressure mercury vapor lamps (Tradename—FUSION H) operating at about 80 W/cm2 to provide ultraviolet radiation suitable for primer compositions according to the present invention.

[0047] Primer compositioins according to the present invention may include from about 0.5 wt. % to about 15 wt. % and preferably about 1.0 wt. % to about 5.0 wt. % of a photosensitizer or a photoinitiator. Photosensitizers or photoinitiators may further promote the reactivity of the olefinically unsaturated species. Suitable photosensitizers include benzophenone, fluorine, anthrone, p-chlorobenzophenone, and mixtures thereof. Representative photoinitiators include 2-hydroxy-2-methyl-1-phenylpropan-1-one, available as DAROCUR-1173, 1-hydroxy-cyclohexyl-phenyl ketone, available as IRGACURE-184, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1, available as IRGACURE-369, 2,2 dimethoxy-1,2 diphenyl ethan-1-one, available as IRGACURE-651, 1-[4-(2-hydroxyethoxy)-phenyl]-2-hydroxy-2-methyll-1-propane-1-one, available as IRGACURE-2959, and mixtures thereof, all available from CIBA Specialty Chemicals, Tarrytown, N.Y.

[0048] Dispersing agents provide stability to water based dispersions according to the present invention. Suitable dispersing agents include particulate materials and polymeric materials. Fumed silica is a preferred particulate dispersing agent. Examples of suitable fumed silica include AEROSIL 200, AEROSIL 300, AEROSIL 380, AEROSIL R-812 and AEROSIL R-972, all available from Degussa Corp., Ridgefield N.J. Polymeric dispersing agents include polyurethane polymers and acrylate polymers. A preferred polyurethane polymer dispersant is DISPERCOLL U-54, available from Bayer Corp., Pittsburgh Pa. An example of preferred polyacrylate dispersions is HYCAR 2671, available from B.F. Goodrich Performance Materials, Cleveland Ohio.

[0049] Optional additives for solutions containing primer, as described above, include: silane coupling agents; biocides; fungicides; optical brighteners; antioxidants; silica; pigments; dyes and acid scavengers, such as epoxy resins. Such additives, used alone or in combination, preferably represent less than 10 wt. % of the water dispersed formulations.

[0050] Fluid priming compositions, comprising chlorinated hydrocarbon polymers in organic solvent or solvent mixture and a dispersing agent, when added with stirring to water, produce water dispersed primers according to the present invention. Optional ingredients for the fluid priming compositions include non-halogenated hydrocarbon polymers and reactive components preferably ultraviolet radiation sensitive monomers and oligomers having olefinic unsaturation. Similar priming compositions when added with stirring to water dispersed adhesives provide adhesive primers according to the present invention. A comparable non-aqueous priming adhesive also forms upon addition of these priming compositions to solvent-based adhesives.

[0051] Adhesives used for the preparation of priming adhesives include water dispersed adhesives and solvent-based or solution adhesives. Useful water dispersed adhesives include polyurethane latices and acrylate polymer latices and blends thereof Suitable polyurethane latex adhesives comprise from about 35% to about 60% of polymer solids dispersed in water, including DISPERCOLL U-53, DISPERCOLL U-54 and BAYHYDROL DLN, all of which are available from Bayer Corp., Pittsburgh Pa. Acrylate latex adhesives, having from about 50% to about 65% of polymer solids in water, include HYCAR 2671, available from B.F. Goodrich Performance Materials, Cleveland Ohio, and RHOPLEX A-920, available from Rohm and Haas Chemical Company, Philadelphia Pa.

[0052] Solution adhesives, useful for the present invention, may be selected from a range of polyurethane adhesives containing from about 15 wt. % to about 30 wt. % solids dissolved in a solvent such as methyl ethyl ketone (MEK). Suitable commercially available polyurethane adhesives include DESMOCOLL 306, DESMOCOLL 530, DESMOCOLL KA8741, DESMOCOLL 620, DESMODUR CB-55N, and DESMODUR CB-72N, all available from Bayer Corp., Pittsburgh Pa.; PEARLSTICK 45-60/18, and PEARLSTICK 45-60/25, available from Aries Technologies Inc., Dervy N.H., and MORTHANE CA-100 series adhesives available from Rohm and Haas Inc., Philadelphia Pa.

[0053] For added hydrolytic stability and adhesive strength, polyurethane adhesives used herein may employ from about 3.0 wt. % to about 5.0 wt %, of the total composition, of a polyfunctional isocyanate crosslinker. Suitable materials for use in solution adhesives include: DESMODUR RFE, available from Bayer Corp., Pittsburgh Pa.; and/or IRODUR E-321 available from Rohm and Haas Inc., Philadelphia Pa. Crosslinkers used with aqueous-based latex adhesives include: DESMODUR DA; and DESMODUR DN, available from Bayer Corp., Pittsburgh Pa. Catalysts such as dialkyl tin carboxylates, metal acetyl acetonates, metal carboxylates, mixtures of metal acetyl acetonates with tertiary amines and the like may be used to accelerate reaction between crosslinkers and adhesive polymers.

[0054] The water dispersed primers and primer adhesives of the present invention are very versatile. They may be applied to the cleaned substrate by any suitable means, dried and adhesively bonded to give useful bond strengths. The primed substrate may instead be irradiated with ultraviolet light and adhesively bonded to give significantly improved bond strengths. The primer may be modified by the addition of olefinically unsaturated monomers and optionally photosensitizers or photoinitiators, applied to the substrate, dried and irradiated with ultraviolet light and adhesively bonded to give further improved bonding.

EXPERIMENTAL

Primer Solution Preparation

EXAMPLE 1

[0055] A solvent mixture of 3.0 parts of cyclohexane to 2.0 parts of xylene was thoroughly dried over type 4A Grade molecular sieve (available from W.R. Grace and Company, Davison Chemical Div., Baltimore, Md.).

[0056] An amount of 2.0 g of maleic anhydride modified chlorinated polypropylene (HARDLEN CY-9122P, available from Toyo Kasei Kogyo Co. Ltd.) was dissolved in 31.5 g of the dried solvent mixture to provide a 6% solution of the polymer. Fumed silica (0.3 g of AEROSIL R-972, available from Degussa Corp., Ridgefield Park, N.J.) was added to the solution.

EXAMPLE 2

[0057] As for Example 1 except HARDLEN CY-9122P was replaced by a maleic anhydride modified chlorinated polypropylene designated CP-343-1 available from Eastman Chemical Company, Kingsport, Tenn.

EXAMPLE 3

[0058] As for Example 1 except in this case the maleic anhydride modified chlorinated polypropylene was HYPALON CP-826 available from DuPont Elastomers, Wilmington, Del.

EXAMPLE 4

[0059] A primer composition containing a blend of halogenated hydrocarbon polymers was prepared by mixing together equal amounts of Example 1 and Example 3.

EXAMPLE 5

[0060] As for Example 1 except HARDLEN CY-9122P was replaced by a mixture of HARDLEN CY-9122P (1.6 g) with KRATON 1901X (0.4 g maleated styrene-ethylene/butylene-styrene block copolymer available from Shell Chemical Co. Houston Tex.).

EXAMPLE 6

[0061] As for Example 5 except for the replacement of KRATON 1901X with an ethylene/butylene copolymer diol HPVM 2203 also available from Shell Chemical Co.

EXAMPLE 7

[0062] As for Example 5 except for the replacement of KRATON 1901X with an ethylene vinyl acetate containing 72% ethylene, available from Polysciences Inc., Warrington, Pa.

EXAMPLE 8

[0063] As for Example 5 except for the replacement of KRATON 1901X with a maleated polyethylene vinyl acetate, available as FUSABOND MC-190 from DuPont Canada Inc., Mississauga, Ontario, Canada.

EXAMPLE 9

[0064] As for Example 5 except for the replacement of KRATON 1901X with a styrene-ethylene/butylene-styrene block copolymer, available as KRATON G-1657 from Shell Chemical Co.

EXAMPLE 10

[0065] This example was prepared by mixing 50 parts of the primer composition of Example 5 with 50 parts of the primer composition of Example 9.

EXAMPLE 11

[0066] Equal amounts of the primer compositions of Example 4 and Example 10 were mixed to provide a blend containing halogenated hydrocarbon polymers with non-halogenated hydrocarbon polymers.

EXAMPLE 12

[0067] As for example 5 except dried CYCLO SOL(R) 100 replaced xylene in the solvent mixture.

EXAMPLE 13

[0068] As for Example 12 without AEROSIL R-972 fumed silica.

[0069] Preparation of Primer Compositions Dispersed in Water Each of the primer compositions of Examples 1-12 was converted into a water based primer dispersion by the addition, with stirring, of 3.0 g of a selected composition to 7.0 g distilled water. In all cases, the resulting dispersion remained stable for at least eight hours. Observation of some separation after about twelve hours was easily corrected by stirring or shaking to re-establish a stable dispersion.

[0070] Preparation of Primer Compositions Containing Adhesive Polymer Dispersed in Water

EXAMPLE 14

[0071] A 2% solids aqueous dispersion of a polyurethane adhesive was prepared by diluting 0.5 g of a 50% polyurethane latex adhesive (DISPERCOLL U-54, available from Bayer Corp., Pittsburgh Pa.) with 12 g distilled water. Addition of 3.0 g of Example 12 to 7.0 g of the diluted adhesive provided a stable primer composition that combined primer and adhesive dispersions. The dispersion was uniform and stable for at least twelve hours.

EXAMPLE 15

[0072] As for the water dispersed primer of Example 14 except for replacement of the diluted latex adhesive with a 2% solids aqueous dispersion made from 0.25 g of DISPERCOLL U-54 mixed with 0.25 g of a polyacrylate dispersion in water (HYCAR 2671 available from B.F. Goodrich Performance Materials, Cleveland Ohio). As before the mixed adhesive dispersion was diluted with 12 g of distilled water and 7.0 g of the product was used to disperse 3.0 g of the primer composition described in Example 12. A stable dispersion was obtained by stirring the primer composition into the diluted adhesive.

EXAMPLE 16

[0073] Prepared as for Example 14 using in place of Example 12 the composition of Example 13 which contained no fumed silica. The resulting dispersion was uniform and stable for about twelve hours.

EXAMPLE 17

[0074] A 2% solids aqueous dispersion of a polyacrylate was prepared by diluting 0.5 g of a 50% polyacrylate dispersion (HYCAR 2671) with 12 g of distilled water. Addition of 3.0 g of Example 13 to 7.0 g of the diluted polyacrylate dispersion provided a stable primer composition. Shaking or stirring corrected any phase separation that may have occurred in about twelve hours.

EXAMPLE 18

[0075] Prepared as for Example 15 using the primer composition of Example 13 in place of that of Example 12.

[0076] Preparation of Priming Adhesives Containing Polyurethane Adhesives Dispersed in Water

[0077] Examples 19-27 were prepared by adding 3.0 g of the primer compositions of Examples 1-3 and 5-10, with stirring, to 7.0 g of DISPERCOLL U-54 (50% solids dispersion in water) to produce a stable dispersion of a priming adhesive in water.

[0078] Preparation of Priming Adhesives Containing Acrylate Adhesives Dispersed in Water

EXAMPLE 28

[0079] A stable uniform dispersion was made by dissolving HARDLEN 9122P (1.8 g) and KRATON 1901X (0.2 g) in a 31.5 g of a dried solvent mixture of 3 parts of cyclobexane to 2 parts of CYCLO SOL(R) 100. AEROSIL R-972 fumed silica (0.3 g) was added to the solution and the resulting dispersion (3.0 g) was added to 7.0 g of an acrylate latex designated as RHOPLEX A-920, available from Rohm & Haas Inc., Philadelphia Pa.

EXAMPLE 29

[0080] As for Example 29 except for the replacement of RHOPLEX A-920 with an acrylate latex designated HYCAR 2671 available from B.F. Goodrich Performance Materials, Cleveland, Ohio.

EXAMPLE 30

[0081] As for Example 29 except for the replacement of RHOPLEX A-920 with a 50:50 blend of RHOPLEX A-920 with DISPERCOLL U-54.

EXAMPLE 31

[0082] As for Example 30 except for the replacement of HYCAR 2671 with a 50:50 blend of HYCAR 2671 with DISPERCOLL U-54.

EXAMPLE 32

[0083] A mixture of CY-9122P (1.6 g) with KRATON 1901X (0.4 g maleated styrene-ethylene/butylene-styrene block copolymer—Shell Chemical Co. Houston Tex.) in dried mixed solvent as described in Example 1, was added to a polyurethane latex (7.0 g) designated BAYHYDROL DLN available from Bayer Corp., Pittsburgh, Pa., mixed with 0.35 g of a polyisocyanate designated DESMODUR KA8703, also known as DESMODUR DN, both being available from Bayer Corp. to provide a stable dispersion. This example provides a non-adhesive priming coating composition which bonds well to low surface energy substrates after drying at 60° C. for ten (10) minutes. Such coatings provide substrate coverage and protection for a variety of applications such as automotive applications.

EXAMPLE 33

[0084] A solution (3 g) containing HARDLEN CY-9122P in mixed, dried solvent as in Example 1 was added to DESMOCOLL 306 (7.0 g), a 20% solution of a polyurethane adhesive in methyl ethyl ketone containing 1.0 wt. % AEROSIL R-972 dispersed in the solution.

[0085] Preparation of Primer Compositions Containing Unsaturated Photoreactive Components

EXAMPLE 34

[0086] A solvent mixture of 3.0 parts of cyclohexane, 1.5 parts of CYPAR-9 (Shell Chemical Co., Houston, Tex.) and 0.5 parts of AROMATIC D-150 (Exxon Chemical Co., Houston, Tex.) was thoroughly dried over type 4A Grade molecular sieve (available from W.R. Grace and Company, Davison Chemical Div., Baltimore, Md.).

[0087] Material comprising 1.6 g of CY-9122P and 0.2 g of KRATON 1901X was dissolved in 27.7 g of the dried solvent mixture to provide a 6.5% solution of the polymer. Fumed silica (0.6 g of AEROSIL R-972, available from Degussa Corp., Ridgefield Park, N.J.) was added to the solution.

EXAMPLE 35

[0088] A solvent mixture of 3.0 parts of cyclohexane, 2.0 parts of AROMATIC D-150 (Exxon Chemical Co., Houston, Tex.) was thoroughly dried over type 4A Grade molecular sieve (available from W.R. Grace and Company, Davison Chemical Div., Baltimore, Md.). Material comprising 2.42 g of CY-9122P, 0.95 g of a 1:1 mixture of IRGACURE 184 and DAROCURE 11730 and 1.45 g of AEROSIL R-972 was added to 76.7 g of the dried solvent mixture and agitated until soluble material dissolved.

EXAMPLE 36

[0089] As for Example 35 with the addition of 1.2 g of isobornyl methacrylate SR-423A, available from Sartomer Company, West Chester, Pa.

EXAMPLE 37

[0090] As for Example 36, except that 1.2 g of ethyl methacrylate was used in place of isobornyl methacrylate.

EXAMPLE 38

[0091] As for Example 36, except that 1.2 g of maleic acid was used in place of isobomyl methacrylate.

[0092] Preparation of Photoreactive Primer Compositions Dispersed in Water

[0093] Each of the primer compositions of Examples 34, and 36-38 was converted into a water based primer dispersion by the addition of 3.0 g of a selected composition to 7.0 g of a mixture of 4.5% DISPERCOLL U-54 in distilled water and stirring with a dispersator for about one hour to provide a smooth dispersion which was stable for at least eight hours. Stirring or shaking to re-establish a stable dispersion easily corrected any separation occurring after about twelve hours. The water based dispersion of Example 35, containing 2.6 g of primer composition in 7.0 g of diluted DISPERCOLL U-54, was prepared in similar fashion. In all cases, the resulting dispersion remained stable for at least eight hours.

EXAMPLE 39

[0094] As for Example 38, except that the amount of DISPECOLL U-54 was increased to 9.0% in deionized water.

Test Results

[0095] Sample Preparation:

[0096] Canvas specimen preparation:—

[0097] Canvas specimens were prepared from greige cotton (49×30 threads per inch) No. 10 duck ribbon, available from West Point Pepperell Inc., Palatine, Ill. by cutting the fabric into specimens 38 mm×100 mm×1 mm. Approximately 75 mm of the length of each specimen was coated by brush coating each specimen twice with an adhesive (DISPERCOLL U-54) thickened with 0.2% of BORCHIGEL L75N, a thickener available from Bayer Corp., Pittsburgh, Pa. with drying at 60° C. for fifteen (15) minutes. The samples after cooling were conditioned at room temperature for at least twenty four (24) hours.

[0098] Foam specimen preparation:—

[0099] Test specimens were made from injection molded polyethylene vinyl acetate (IMEVA) foam (ECLIPSE 2050), available from Eclipse Polymers Co. Ltd., Kyeong Nam, Korea. The test specimens measured 25.4 mm×127 mm×15 mm. A solvent mixture of 3 parts of cyclohexane to 2 parts of xylene was applied to clean the surface of each test specimen using a solvent-saturated, lintless tissue (KIMWIPE available from Kimberly Clark Corp., Roswell, Ga.).

[0100] The cleaned foam specimens were dried at 60° C. for 10 minutes and coated, while still warm and between 35° C. and 45° C. with the water dispersed primers and priming adhesives previously described in Examples 1-12 and 14-27.

[0101] A stronger, more dense injection molded polyethylene vinyl acetate (IMEVA) foam (ECLIPSE 2000), available from Eclipse Polymers Co. Ltd., Kyeong Nam, Korea, replaced ECLIPSE 2050 as the foam substrate for coating with the primer dispersions prepared using Examples 34-39. Substrate samples of ECLIPSE 2000 were dried for 5 minutes at 60° C. after solvent cleaning and coated while still warm and between 35° C. and 45° C. with primer dispersion. The coated samples were dried for 5 minutes at 60° C. followed by exposure to about 0.5 J/cm2 of ultraviolet radiation.

[0102] Test Sample Preparation:

[0103] Canvas specimens, prepared as above, and foam specimens coated with water dispersed primers of Examples 1-12 and 14-18 were overcoated, at approximately the same time, with a brush coating of the adhesive of DISPERCOLL U-54 to which 4% by weight of a water dispersible polyisocyanate (designated as DESMODUR KA8703 or DESMODUR DN) had been added with stirring. The coated materials were then dried at 60° C. for five (5) minutes. The adhesive coated sides of the canvas and foam specimens were bonded together under a pressure of approximately 10 KPascals before conditioning the bonded, laminated samples for approximately three (3) days under ambient conditions.

[0104] Examples 19-27, previously coated with priming adhesives as described above, were similarly bonded to adhesive coated canvas.

[0105] Examples 34-38, previously coated with adhesive, were dried and immediately bonded together under a pressure of about 10 Kpa. The resulting samples were conditioned for twenty four hours prior to testing.

[0106] Alternative Test Sample Preparation:

[0107] Test samples of Examples 16-18 and 39 were also prepared by bonding a foam specimen coated with priming composition, i.e. no additional adhesive, to a canvas specimen, overcoated with adhesive, (DISPERCOLL U-54 to which 4% by weight of a water dispersable polyisocyanate (DESMODUR KA8703 or DESMODUR DN) had been added with stirring).

[0108] Peel Adhesions:

[0109] Each of the laminated samples was subjected to 180° peel testing using a peel tester available from Instron Corp., Canton Mass. The peel tester operated at a jaw separation speed of 12.7 cm per minute and at least three samples of each of Examples 1-12 and 14-27 were submitted to testing.

[0110] Results:

[0111] Examples 1-12 and 14-27 exhibited adhesions of at least 354 N/100 mm with internal failure of the substrate and not the adhesive bond. This indicates strong bond formation between dissimilar materials without pre-treating the surfaces as by plasma.

[0112] Acrylate Series adhesives:

[0113] Specimens of Examples 28-31 were prepared in similar to fashion to Examples 1-12 and 14-27.

[0114] Results:

[0115] Examples 28 and 29 gave peel values of 63 N/100 mm, and 58 N/100 mm thereby demonstrating effective priming of the IMEVA foam substrate and adhesion of the canvas thereto. Examples 30 and 31 recorded values of at least 354 N/100 mm with internal failure of the substrate polymer.

[0116] Photoreactive Primer Compositions:

[0117] Specimens of Examples 34-39, were prepared as indicated previously. In some cases, test samples of this series of priming dispersions were prepared without exposure to ultraviolet radiation.

[0118] Results:

[0119] Example 34 recorded a value of 560 N/100 mm with exposure to ultraviolet radiation. Without exposure to radiation, adhesion values decreased to about 325 N/100 mm. This shows the improvement in bond strength due to the presence of photoreactive components in priming compositions according to the present invention.

[0120] Examples 35-38 gave test values, with exposure to ultraviolet radiation, of 598 N/100 mm, 645 N/100 mm, 600 N/100 mm and 670 N/100 mm respectively.

[0121] Using alternative test sample preparation, with immediate bonding of canvas and foam test specimens after drying, Example 39 exhibited average peel values of about 500 N/100 mm. This indicates the benefits provided by ultraviolet exposure in the absence of adhesive overcoating of the primed foam surface.

[0122] Alternative Test Surfaces

[0123] An ethylene/1-octene polymer elastomer (POE) available as ENGAGE 8003 from DuPont Dow Elastomers L.L.C., Wilmington, Del. was converted into test specimens 100 mm×25 mm×6 mm (110 mm×20 mm×6 mm for Examples 34-39). A thermoplastic polyolefin polymer (TPO) available as ETA 3163 from Himont USA Inc., Lansing, Mich. was converted into test specimens 110 mm×25.4 mm×3.5 mm (110 mm×20 mm×3.5 mm for Examples 34-39). A vulcanized ethylene propylene diene terpolymer (EPDM) available as SHORE A-6 from Shin Ho Inc., Pusan, Korea, was converted into test specimens 127 mm×25.4 mm×2.5 mm (110 mm×20 mm×2.5 mm for Examples 34-39).

[0124] All test specimens were cleaned, dried at 60° C. for 10 minutes as previously described and coated, while still warm, with the latex bonding agent of Example 22. Canvas specimens, as previously described, were laminated, with adhesive to adhesive bonding, to the specimens coated with Example 22. After conditioning the laminated samples were subjected to 180° peel testing.

[0125] Results:

[0126] POE—447 N/100 mm

[0127] TPO—252 N/100 mm

[0128] EPDM—271 N/100 mm

[0129] Test specimens for exposure to ultraviolet radiation were prepared as described above before coating, while still warm, with the bonding agent of Example 38. Dried coatings were exposed to 0.5 J/cm2 ultraviolet radiation. Canvas specimens, as previously described, were laminated, with adhesive to adhesive bonding, to the specimens coated with Example 38. After conditioning the laminated samples were subjected to 180° peel testing.

[0130] Results:

[0131] POE—350 N/100 mm

[0132] TPO—290 N/100 mm

[0133] EPDM—290 N/100 mm

[0134] Composition of Styrene-Butadiene Rubber (SBR) 1 SBR 1502 65 parts SBR 1904 35 parts 100 parts Silica 20 phr Carbon black 25 phr Sulfur 1.8 phr Coumarone-Indene Resin 3.0 phr Zinc Oxide 3.8 phr Stearic Acid 1.8 phr N-cyclohexyl-2-benzothiazolsulfonamide 1.1 phr Phenolic antioxidant 0.8 phr

[0135] A rubber having the composition indicated above was compounded and converted into plaques by Rubber Industries Inc., Shakopee, Minn. Specimens 127 mm×25.4 mm×3.1 mm were prepared for testing. Each specimen of SBR rubber was primed with a solution of 2% trichloroisocyanuric acid in dry ethyl acetate. The primed samples were conditioned at ambient conditions for about 30 minutes before applying adhesives as described for the preparation of canvas specimens. Specimens of POE and IMEVA foam were coated with the latex bonding agent of Example 22 before drying, along with the adhesive coated SBR specimens, at 60° C. for five (5) minutes. After adhesive to adhesive lamination, bond strength was tested using 180° peel.

[0136] Results:

[0137] POE/SBR—307 N/100 mm

[0138] IMEVA/SBR—360 N/100 mm

[0139] IMEVA/POE—406 N/100 mm

COMPARATIVE EXAMPLES C1-C4

EXAMPLE C1

[0140] This example reflects the teachings of U.S. Pat. No. 4,303,697.

[0141] A 1.0% solution of maleic anhydride modified chlorinated polyolefin (CP 343-1 available from Eastman Chemicals Co., Kingsport, Tenn.) was prepared by dissolving 1.52 g of CP 343-1 in 148.5 g of xylene.

EXAMPLE C2

[0142] This example reflects the teachings of WO 98/105704.

[0143] An amount of 3.69 g of CP 343-1 was added to a mixture of 109.8 g toluene and 34.36 g acetone. A photoreactive composition comprising 1.74 g methyl methacrylate and 0.74 g benzophenone was added to the resulting solution to prepare a solvent-based primer solution.

EXAMPLE C3

[0144] This example is based on the teachings of WO 98/105704.

[0145] An amount of 3.86 g of a polychloroprene dispersion, (DISPERCOLL C-74 available from Bayer Corp.) and 0.59 g CARBOPOL EZ-1, (available from B.F. Goodrich Specialty & Chemicals Division, Cleveland Ohio) was added with stirring to 151.6 g of deionized water containing 0.97 g NaOH, Example C4 This example was formulated using a commercially available, water reducible chlorinated polyolefin (CP-310 W, available from Eastman Chemicals Co., Kingsport, Tenn.).

[0146] A 2.66 wt. % solution of a water reducible chlorinated polyolefin was prepared by adding 10.05 g of CP-310W to 80.25 g of deionized water.

[0147] Specimens on solvent cleaned ECLIPSE 2000 (IMEVA) foam were primed using Examples C1-C4, followed by exposure to about 0.5 J/cm2 of ultraviolet radiation. All specimens were bonded to canvas coated with DISPERCOLL U-54 adhesive, as described previously. Values of 180° peel were obtained for samples that were allowed to condition at room temperature for twenty four hours prior to testing. The following table shows an average of three peel values for each specimen. 2 180° Peel Adhesions for Comparative Examples C1-C4 Comparative Example Peel Value N/100 mm C1 410 C2 430 C3  90 C4 255

[0148] These results show that prior art solvent solutions (i.e. C1) of chlorinated polyolefins and solvent solutions of chlorinated polyolefins containing an olefinically unsaturated monomer, methyl methacrylate (i.e. C2) give acceptable peel values. However, water-based dispersions of chlorinated polyolefins (i.e C3 and C4) give significantly lower peel values than primer compositions containing photoreactive components according to the present invention.

Priming Coating Compositions

[0149] The priming effect of priming compositions, according to the present invention, may also be imparted to coating compositions. A water dispersed priming coating composition, as in Example 32 was coated on thermoplastic polyolefin polymer (TPO) available as ETA 3163 from Himont USA Inc., Lansing, Mich. in the form of test specimens 110 mm×25.4 mm×3.5 mm that had been previously cleaned and heated to evaporate the cleaner. The coating was applied while the specimens were still warm, followed by drying at 60° C. for ten (10) minutes. Control samples, omitting the primer solution, were prepared using the same procedure. All specimens were conditioned at room temperature for about twenty four (24) hours.

[0150] A new razor blade was used for producing intersecting horizontal and vertical score marks having a separation of approximately 1.0 mm. A length of adhesive tape (Scotch™ Brand 810 Magic™ Tape available from 3M Company, St. Paul Minn.) was placed in firm adhesive contact with the coating before removal by rapid peeling with a single continuous pulling action. Four fresh samples of tape were removed in this way from the bonded coatings.

[0151] Results:

[0152] Two of three samples coated with the priming coating of Example 32 showed no coating removal. The third sample lost only three of the tiny squares, produced by the scoring procedure. In contrast, the control samples could not be tested because they released from the TPO surface without showing any evidence of bonding.

[0153] Organic Solvent-Based Priming Adhesives

[0154] Canvas Specimen Preparation:

[0155] Canvas specimens were prepared from greige cotton (49×30 threads per inch) No. 10 duck ribbon, available from West Point Pepperell Inc., Palatine, Ill. by cutting the fabric into specimens 38 mm×100 mm×1 mm. Approximately 75 mm of the length of each specimen was coated by brush coating each specimen twice with an adhesive (DESMOCOLL 306) thickened with 1.0% of AEROSIL 972 fumed silica, and 3% by weight of a polyisocyanate available as IRODUR E-321, from Rohm and Haas Inc., Philadelphia Pa. with drying at 60° C. for fifteen (15) minutes. The samples after cooling were conditioned at room temperature for at least twenty four (24) hours. Foam specimen preparation: Test specimens were made from injection molded polyethylene vinyl acetate (IMEVA) foam (ECLIPSE 2050), available from Eclipse Polymers Co. Ltd., Kyeong Nam, Korea. The test specimens measured 25.4 mm×127 mm×15 mm. A solvent mixture of 3 parts of cyclohexane to 2 parts of xylene was applied to clean the surface of each test specimen using a solvent-saturated, lintless tissue (KIMWIPE available from Kimberly Clark Corp., Roswell, Ga.).

[0156] The cleaned foam specimens were dried at 60° C. for 10 minutes and coated, while still warm and between 35° C. and 45° C. with the solvent based adhesive of Example 33.

[0157] Test Sample Preparation:

[0158] Canvas specimens and foam specimens coated with solvent-based adhesives, were prepared at approximately the same time and then dried at 60° C. for seven (7) minutes. The adhesive coated sides of the canvas and foam specimens were bonded together under a pressure of approximately 10 KPascals before conditioning the bonded, laminated samples for approximately three (3) days under ambient conditions.

[0159] Results:

[0160] All test specimens exhibited 180° peel adhesions of at least 360 N/100 mm indicating substrate failure with the adhesive bond still intact. This provides examples of adhesive formulations suitable for applying directly to organic polymer substrates without oxidizing or similar pretreatment.

[0161] Primer compositions according to the present invention may be used for bonding polymeric substrates together or bonding polymeric substrates to other types of substrate such as those comprising metal, glass, ceramic, wood, and woven and non-woven fabrics, and the like. The bonding of polymer substrates to fabrics finds use in the manufacture of a wide variety of articles of clothing including footwear, particularly athletic footwear where secure bonding of fabric to elastomeric shoe components is important to the production of a lightweight high performance shoe. Common materials used for athletic shoe manufacture include fabrics, polymer mid-soles and durable outer soles. Suitable fabrics include natural or synthetic leather, nylon, cotton and the like. Foamed mid-soles include polymers, copolymers, and blends and mixtures thereof, based on monomers including ethylene vinyl acetate, ethylene/i -octene, propylene and suitable diene monomers. Preferred polymers and copolymers include polyethylene vinyl acetate (EVA) and ethylene-propylene-diene (EPDM) elastomers. Materials suitable as durable outer soles include the thermosetting polymers of vulcanized rubbers such as styrene-butadiene rubbers (SBR), styrene-butadiene-styrene (SBS) block copolymer rubbers and ethylene-propylene-diene (EPDM) rubbers.

[0162] As indicated above, primers and priming adhesives according to the present invention contribute to strong adhesive bonding of durable rubber outer sole materials to foamed mid-sole materials to produce a composite sole or stock that bonds strongly to material used for shoe upper after primer or priming adhesive treatment. In addition, the water dispersed primers and priming adhesives provide low hazard, low VOC containing products for safe use by workers who apply such products, usually by brushing or open spray techniques, during labor intensive manufacturing operations.

[0163] Water dispersed primers and priming adhesives and related solvent based systems have been described herein. These and other variations, which will be appreciated by those skilled in the art, are within the intended scope of this invention as claimed below. As previously stated, detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely exemplary of the invention that may be embodied in various forms.

Claims

1. A photoreactive, fluid primer composition comprising:

a solution having a halogenated hydrocarbon polymer dissolved in an organic solvent selected from the group consisting of cyclohexane, heptane, hexane, xylene, toluene, chlorotoluene, mixed hydrocarbon solvents, and mixtures thereof; and

a dispersing agent.

2. A photoreactive, fluid primer composition according to

claim 1 wherein said solution further comprises a photoreactive component.

3. A photoreactive, fluid primer composition according to

claim 2 wherein said fluid primer further includes a non-halogenated hydrocarbon polymer blended with said halogenated hydrocarbon polymer.

4. A photoreactive fluid primer composition according to

claim 2 wherein said photoreactive component is selected from the group consisting of olefinically unsaturated monomers and oligomers.

5. A photoreactive fluid primer composition according to

claim 4 wherein said olefinically unsaturated monomers and oligomers are selected from the group consisting of alkyl (meth)acrylates, acrylamides, N-alkylacrylamides, vinyl halides and heterocyclic vinyl compounds, di(meth)acrylates, tri(meth)acrylates and tetra-(meth)acrylates, (meth)acrylic acid, glycidyl (meth)acrylate, 2-hydroxyl ethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, alkyl (meth)acrylate esters, aryl (meth)acrylate esters, 2-dimethylaminoethyl (meth)acrylate, 2-chloroethyl (meth)acrylate, maleic anhydride, maleic acid, maleimide, bismaleimides, alkyl esters of maleic acid, fumaric acid and alkyl esters of fumaric acid polyurethane acrylates, polybutadienediacrylate, and epoxy acrylates and the like.

6. A photoreactive, fluid primer composition according to

claim 1 wherein said dispersing agent is a particulate dispersing agent.

7. A photoreactive, fluid primer composition according to

claim 6 wherein said particulate dispersing agent is a fumed silica.

8. A photoreactive water dispersed primer composition comprising:

water; and

a fluid primer composition including:

a solution having a halogenated hydrocarbon polymer dissolved in an organic solvent selected from the group consisting of cyclohexane, heptane, hexane, xylene, toluene, chlorotoluene, mixed hydrocarbon solvents, and mixtures thereof, and a dispersing agent.

9. A photoreactive water dispersed primer composition according to

claim 8 wherein said solution further comprises a photoreactive component.

10. A photoreactive water dispersed primer composition according to

claim 9 wherein said fluid primer further includes a non-halogenated hydrocarbon polymer blended with said halogenated hydrocarbon polymer.

11. A photoreactive water dispersed primer composition according to

claim 8 wherein said photoreactive component is selected from the group consisting of olefinically unsaturated monomers and oligomers.

12. A photoreactive water dispersed primer composition according to

claim 11 wherein said olefinically unsaturated monomers and oligomers are selected from the group consisting of alkyl (meth)acrylates, acrylamides, N-alkylacrylamides, vinyl halides and heterocyclic vinyl compounds, di(meth)acrylates, tri(meth)acrylates and tetra-(meth)acrylates, (meth)acrylic acid, glycidyl (meth)acrylate, 2-hydroxyl ethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, alkyl (meth)acrylate esters, aryl (meth)acrylate esters, 2-dimethylaminoethyl (meth)acrylate, 2-chloroethyl (meth)acrylate, maleic anhydride, maleic acid, maleimide, bismaleimides, alkyl esters of maleic acid, fumaric acid and alkyl esters of fumaric acid polyurethane acrylates, polybutadienediacrylate, and epoxy acrylates and the like.

13. A photoreactive water dispersed primer composition according to

claim 8 wherein said dispersing agent is a particulate dispersing agent.

14. A photoreactive water dispersed primer composition according to

claim 13 wherein said particulate dispersing agent is a fumed silica.