Catalyst system for alpha-olefin oligomerization

Abstract

It is disclosed a new catalyst system, having high catalytic activity in the oligomerization of &agr;-olefins, comprising a bridged bis-amido Group 4 metal compound of formula (I): 1

Description

FIELD OF THE INVENTION

[0001] The present invention relates to new catalyst systems and to their use in the oligomerization and co-oligomerization of &agr;-olefins; said catalyst systems are particularly useful in ethylene oligomerization in order to obtain (&agr;-olefinic oligomers having from 4 to 24 carbon atoms.

PRIOR ART DISCLOSURE

[0002] High linear &agr;-olefins, i.e. &agr;-olefins having from 4 to 24 carbon atoms, and more specifically 6 to 20 carbon atoms, are in great demand as intermediates in the preparation of detergents, lubricant additives and polyolefins; &agr;-olefins having 6-20 carbon atoms are suitable for a large number of applications in different technical fields.

[0003] However, oligomerization processes commonly known in the state of the art lead to the obtainment, together with the target products, of undesirable by-products, such as internal olefins, branched olefins and olefins having a number of carbon atoms outside the above mentioned range.

[0004] Olefin polymerization processes employing homogeneous Ziegler-Natta catalyst systems or metallocene/alumoxane catalyst systems are well known in the state of the art; these catalyst systems are also used in oligomerization processes of lower olefins to give higher olefins.

[0005] For instance, the British patent application GB 135,873 describes the preparation of C4-C20 linear &agr;-olefins by ethylene oligomerization in the presence of a catalyst composition comprising a divalent nickel salt, a boron hydride and a tertiary organophosphorus compound.

[0006] The international patent application WO 94/25416 discloses a catalyst system for the preparation of C4-C24 linear &agr;-olefins comprising the reaction product of a bis-tetramethyl-cyclopentadienyl metallocene and a bulky, labile and non-coordinating anion.

[0007] Bridged bis-amido Group 4 (IUPAC 1988 notation) metal compounds are also known, as components of catalyst systems for the preparation of polyolefins, such as polyethylene and polypropylene. The international patent application WO 92/12162 discloses catalyst systems for the polymerization of &agr;-olefins, comprising an amido transition metal compound having the following formula: 2

[0008] wherein M is Ti, Zr or Hf; X is an univalent anionic ligand; the groups R, linked to trivalent N atoms, are selected from halogens and linear or branched hydrocarbon radicals, optionally containing one or more heteroatoms; T is a covalent unsubstituted or substituted hydrocarbon bridging group, optionally containing one element of Group IV-A or VI-A (Deming notation; corresponding to Group 14 and 16 of the IUPAC 1988 notation); y is 1 or 0; z is 2−y;

[0009] in association with an alumoxane.

[0010] Suitable alumoxanes are obtained by hydrolysis of a trialkylaluminium or haloalkylaluminium, such as trimethylaluminium, triethylaluminium and the corresponding chlorides; the most preferred alumoxane is methylalumoxane (MAO).

[0011] The catalysts disclosed in the above-mentioned WO 92/12162, which do not envisage amido compounds having a bridging group containing two heteroatoms, are used in the production of high molecular weight polyolefins, having a molecular weight well in excess of 100,000, and more specifically of high molecular weight isotactic polypropylene.

[0012] The international patent application WO 96/27439 describes a new class of oligomerization catalysts comprising a bridged bis-amido Group 4 metal compound, such as {1,2-bis(t-butylamide)tetramethyl-disilane}-zirconium dibenzyl or dimethyl, in association with suitable activating agents, capable of providing a bulky, labile and non-coordinating anion, containing at least one boron atom, such as B(C6F5)3 or [Me2PhNH]+[B(C6F5)4]−.

[0013] These catalyst systems are active in the oligomerization or co-oligomerization of &agr;-olefins to produce linear &agr;-olefins. In the specification of WO 96/27439 it is mentioned the possibility of adding to the catalytic compositions further components, for example in order to increase the solubility and/or the stability of the same compositions, although not affecting the catalytic activity. For instance, it is mentioned the possibility of adding organoaluminium compounds, such as trimethylaluminium (TMA), triethylaluminium (TEA), triisopropylaluminium and triisobutylaluminium (TIBA), acting as scavenging agents, although without any influence of the catalytic activity of the system.

[0014] Nevertheless, there is room for improvement in the oligomerization yields when these catalyst systems are used. They tend to be sensitive to the presence of minor contaminants, resulting in low yields. In order to achieve a satisfactory activity the catalyst concentrations should not be too low, whereas relatively high concentrations may lead to exothermic reactions which are difficult to control. Further, the activity stability of the catalyst systems described in WO 96/27439 is not optimal, as shown by their activity decay.

[0015] Therefore, it is felt the need of lowering the decay rate and improving the catalytic activity of the above mentioned oligomerization catalysts, in order to allow their industrial exploitation.

SUMMARY OF THE INVENTION

[0016] The Applicant has now unexpectedly found that the catalytic activity in &agr;-olefin oligomerization of the above-mentioned bridged bis-amido Group 4 metal compounds, in association with boron activating compounds, can be surprisingly enhanced by adding to these components a specific class of branched alkylaluminiums and/or alumoxanes of branched alkylaluminiums, leading to &agr;-olefin oligomers having from 4 to 30 carbon atoms, in high yields and with a high selectivity towards &agr;-olefins.

[0017] More specifically, the present invention concerns a catalyst system for &agr;-olefin oligomerization comprising the product obtainable by contacting the following components:

[0018] (A) one or more bis-amido compounds having formula (I): 3

[0019] wherein M is Ti, Zr or Hf;

[0020] N is a trivalent nitrogen atom;

[0021] the Y atoms, the same or different from each other, are selected from the group consisting of Si, Ge and Sn;

[0022] the X groups, the same or different from each other, are selected from the group consisting of H, halogen, linear or branched, saturated or unsaturated C1-C20 alkyl, C1-C20 alkoxyl, C3-C20 cycloalkyl C6-C20 aryl, C6-C20 aryloxyl, C7-C20 alkylaryl and C7-C20 arylalkyl radicals, optionally containing one or more Si, Ge, O, S, P, B or N atoms; or two X groups form a ring having from 4 to 8 members;

[0023] R1, R2, R3, R4, R5 and R6, the same or different from each other, are linear or branched, saturated or unsaturated C1-C20 alkyl, C3-C20 cycloalkyl, C6-C20 aryl, C7-C20 alkylaryl or C7-C20 arylalkyl radicals, optionally containing one or more Si, Ge, O, S, P, B or N atoms; or are Si(R7)3 groups, wherein the groups R7, the same or different from each other, are linear or branched, saturated or unsaturated C1-C10 alkyl, C3-C10 cycloalkyl, C6-C15 aryl, C7-C15 alkylaryl or C7-C15 arylalkyl groups; or two or four substituents of R1, R2, R3, R4, R5 and R6, linked to two vicinal atoms, form one or two rings having from 4 to 8 members;

[0024] Q is a neutral Lewis base; and

[0025] m is an integer ranging from 0 to 2;

[0026] said bis-amido compound being optionally present in the form of a dimer;

[0027] (B) one or more activating cocatalysts selected from:

[0028] compounds having formula Y+Z−, wherein Y+ is a cation capable of reacting irreversibly with a substituent X of the compound of formula (I), and Z− is a compatible non-coordinating anion comprising at least one boron atom; and

[0029] neutral strongly Lewis acidic compounds comprising at least one boron atom;

[0030] (C) one or more compounds selected from the following classes:

[0031] (a) organometallic aluminium compounds having formula (II):

Al(CH2—CR8R9R10)xR11yHz  (II)

[0032] wherein, in the (CH2—CR8R9R10) groups, the same or different from each other, R8 is a linear or branched, saturated or unsaturated C1-C10 alkyl, C3-C13 cycloalkyl or C7-C16 alkylaryl radical; R9 is a saturated or unsaturated C1-C50 alkyl, C3-C50 cycloalkyl, C6-C50 aryl, C7-C50 alkylaryl or C7-C50 arylalkyl radical, said radical being different from a straight alkyl or alkenyl group; or

[0033] R8 and R9 form together a ring having from 4 to 6 carbon atoms; R10 is hydrogen or a linear or branched, saturated or unsaturated C1-C10 alkyl, C6-C15 aryl, C7-C16 alkylaryl radical or arylalkyl radical, optionally containing one or more Si or Ge atoms;

[0034] R11 is a linear or branched, saturated or unsaturated C1-C10 alkyl, C3-C15 cycloalkyl, C6-C15 aryl, C7-C16 alkylaryl or C7-C16 arylalkyl radical;

[0035] x is an integer ranging from 1 to 3; z is 0 or 1; and y is 3−x−z; and

[0036] (b) the reaction products of water with organometallic aluminium compounds of formula (III):

AlR123−wHw  (III)

[0037] wherein the substituents R12, the same or different from each other, are selected from the group consisting of linear or branched, saturated or unsaturated C1-C50 alkyl, C3-C50 cycloalkyl, C6-C50 aryl, C7-C50 alkylaryl and C7-C50 arylalkyl radicals, optionally containing one or more Si or Ge atoms, wherein at least one of said substituents R12 is different from a straight alkyl group; and w is 0 or 1; the molar ratio between said organometallic aluminium compound and water being comprised between 1:1 and 100:1.

[0038] The present invention further provides a process for the oligomerization of olefins comprising the reaction of oligomerization of one or more olefinic monomers in the presence of a catalyst system as reported above.

DETAILED DESCRIPTION OF THE INVENTION

[0039] The catalyst systems for olefin oligomerization and the process using them, according to the present invention, will be better described in the following detailed description.

[0040] In the bis-amido compounds (A) having formula (I), M is Ti, Zr or Hf, and preferably is Zr.

[0041] The groups Y are preferably the same, and are more preferably two Si atoms.

[0042] The groups X are preferably selected from hydrogen, methyl, ethyl, propyl, n-butyl, phenyl, 4-alkyl-phenyl and benzyl groups; two X groups can form, together with the metal M, a ring having from 4 to 8 members, and preferably a metallacyclobutane.

[0043] R1, R2, R3, R4, R5 and R6, the same or different from each other, are preferably methyl, ethyl, propyl, n-butyl, t-butyl, t-amyl, cyclohexyl, phenyl, dimethyl-phenyl, diisopropyl-phenyl, trimethylsilyl, tri-t-butyl-silyl, phenylmethyl-ethyl, diphenyl-ethyl and triphenyl-methyl.

[0044] Preferred examples of the neutral Lewis base Q are diethylether, tetrahydrofuran, dimethylaniline, aniline, n-butylamine and trimethylphosphine.

[0045] Preferred bis-amido compounds of formula (I) according to the present invention are:

[0046] {1,2-bis(t-butylamide)-tetramethyldisilane}metal dibenzyl {(Me2SiNCMe3)2}M(CH2Ph2)

[0047] {1,2-bis(t-butylamide)-tetramethyldisilane}metal dimethyl, {(Me2SiNCMe3)2}MMe2

[0048] {1,2-bis(t-butylamide)-tetramethyldisilane}metal di(n-butyl), {(Me2SiNCMe3)2}M(n-BU)2

[0049] {1,2-bis(t-butylamide)-tetramethyldisilane}metal diphenyl, {(Me2SiNCMe3)2}MPh2

[0050] {1,2-bis(t-butylamide)-tetramethyldisilane}metal dip(4-methylpheny 1),

[0051] {(Me2SiNCMe3)2}M{CH2(4-Me-Ph)}2

[0052] {1,2-bis(t-butylamide)-tetramethyldisilane}metallacyclobutane,

[0053] {(Me2SiNCMe3)2}{MCH2CH2CH2}

[0054] {1,2-bis(t-butylamide)-tetramethyldisilane}metal dihydride, {(Me2SiNCMe3)2}MH2

[0055] {1,2-bis(t-amylamide)-tetramethyldisilane}metal dibenzyl,

[0056] {(Me2SiNCMe2Et)2}M(CH2Ph)2

[0057] {1,2-bis(cyclohexylamide)-tetramethyldisilane}metal dibenzyl, {(Me2SiNCy)2}M(CH2Ph)2

[0058] {1,2-bis(ethylamide)-tetramethyldisilane}metal dibenzyl, {(Me2SiNEt)2}M(CH2Ph)2

[0059] {1,2-bis(phenylamide)-tetramethyldisilane}metal dibenzyl, {(Me2SiNPh)2}M(CH2Ph)2

[0060] {1,2-bis(2,6-dimethylphenylamide)-tetramethyldisilane}metal dibenzyl,

[0061] {(Me2SiN[2,6-Me2-Ph])2}M(CH2Ph)2

[0062] {1,2-bis(trimethylsilylamide)-tetramethyldisilane}metal dibenzyl,

[0063] {(Me2SiNSiMe3)2}M(CH2Ph)2

[0064] {1,2-bis tri(t-butyl)silylamide)-tetramethyldisilane}metal dibenzyl,

[0065] [{(Me2SiNSi(CMe3)3}2]M(CH2Ph)2

[0066] {1,2-bis(t-butylamide)-tetraethyldisilane}metal dibenzyl, {(Et2SiNCMe3)2}M(CH2Ph)2

[0067] {1,2-bis(t-butylamide)-tetraethyldisilane}metal dimethyl, {(Et2SiNCMe3)2}MMe2

[0068] {1,2-bis(t-butylamide)-tetraphenyldisilane}metal dibenzyl, {(Ph2SiNCMe3)2}M(CH2Ph)2

[0069] {1,2-bis(t-butylamide)-tetramethyldigermane}metal dibenzyl,

[0070] {(Me2GeNCMe3)2}M(CH2Ph)2

[0071] {1,2-bis(t-butylamide)-tetramethyldistannane}metal dibenzyl,

[0072] {(Me2SnNCMe3)2}M(CH2Ph)2,

[0073] {1,2-bis(1,1,3,3-tetramethylbutylamide)-tetramethyldisilane}metal dibenzyl,

[0074] {(Me2SiNCMe2CH2CMe3)2}M(CH2Ph)2, and

[0075] {1,2-bis(2,6-diisopropylphenylamide)-tetramethyldisilane}metal dibenzyl,

[0076] {(Me2SiN[2,6-iPr2Ph])2}M(CH2Ph)2,

[0077] wherein M has the meaning reported above.

[0078] The bis-amido Group 4 metal compounds of formula (I), i.e. components (A) of the catalyst systems of the invention, can be prepared according to procedures known in the state of the art, and more specifically as described in the international patent application WO 96/27439.

[0079] Said bis-amido compounds can be in the form of a dimer, corresponding to the following formula (IV): 4

[0080] wherein M, Y, X, R1, R2, R3, R4, R5, R6 and Q have the meaning reported above and n is 0 or 1.

[0081] The catalyst systems of the invention further comprise one or more activating cocatalysts (component B) of formula Y+Z−, wherein Y+ is a cation capable of reacting irreversibly with a substituent X of the compound of formula (I) or (IV), and Z is a bulky and labile anion, substantially non-coordinating under the reaction conditions, and containing at least one boron atom. Further suitable activating cocatalysts are neutral Lewis acidic compounds, containing at least one boron atom, which are capable of abstracting one of the radicals X of the first component, thereby also contributing an anion Z−. Said anion must be capable of stabilizing the active catalytic species originating by the reaction of the compound (I) or (IV) with said activating cocatalyst and must be sufficiently labile to be able to be displaced by an olefinic substrate.

[0082] Components (A) and (B) form together an ionic compound of formula (V): 5

[0083] wherein M, Y, X, R1, R2, R3, R4, R5, R6, Q, Z and m have the meaning reported above; or, when the component (A) is in the form of the above reported dimer (IV), an ionic compound of formula (VI): 6

[0084] wherein M, Y. X, R1, R2, R3, R4, R5, R6, Q, Z and n have the meaning reported above.

[0085] In component (B), Y+ is preferably a Broensted acid, capable of donating a proton and of reacting irreversibly with a substituent X of the compound of formula (I) or (IV); the cation Y+ is preferably a quaternary ammonium cation, and more preferably a trihydrocarbyl-ammonium cation, such as tri-n-butylammonium and dimethylanilinium.

[0086] Alternatively Y+ is a not proton-donating cation, in particular a metal cation, such as a silver ion or a triphenyl carbenium ion.

[0087] In component (B), the anion Z−, containing one boron atom, is preferably a borate of formula [B(R1)4]−, wherein R1 is selected from the group consisting of hydrogen, C1-C10 alkyl, C3-C10 cycloalkyl, C6-C15 aryl, C7-C15 alkylaryl and C7-C15 arylalkyl groups, optionally substituted with one or more halogens; suitable examples are [B(C6F5)4]−, [R1B(C6F5)3]−, [B(FC6H4)4]−, [R1B(FC6H4)3]−, [B{(CF3)2(C6H3)}4]− and [R−B{(CF3)2(C6H3)}3]−, wherein R1 has the meaning reported above. Examples of anion Z− containing a plurality of boron atoms are the carborates, such as [B11CH12]−.

[0088] The activating cocatalyst Y+Z− is preferably selected from the group consisting of:

[0089] dimethylanilinium tetrakis(pentafluorophenyl)borate [PhMe2NH][B(C6F5)4],

[0090] tri(n-butyl)ammonium tetrakis(pentafluorophenyl)borate [Bu3NH][B(C6F5)4],

[0091] dimethylanilinium tetrakis(2,3,5,6-tetrafluorophenyl)borate

[0092] [PhMe2NH][B(2,3,5,6-C6F4H)4],

[0093] dimethylanilinium tetrakis(3,5-bis-trifluoromethyl-phenyl)borate

[0094] [PhMe2NH][B(3,5-(CF3)2-C6H3)4],

[0095] dimethylanilinium tetrakis(4-fluorophenyl)borate [PhMe2NH][B(4-C6H4F)4],

[0096] dimethylanilinium tetraphenylborate [PhMe2NH][B(C6H5)4],

[0097] triphenylcarbonium tetrakis(pentafluorophenyl)borate [Ph3C][B(C6F5)4],

[0098] ferrocenium tetrakis(pentafluorophenyl)borate [(C5H5)2Fe][B(C6F5)4],

[0099] silver tetrakis(pentafluorophenyl)borate [Ag][B(C6F5)4],

[0100] tri(n-butyl)ammonium 1-carbodecaborate [Bu3NH][CB11H12]and

[0101] diethyloxonium tetrakis(3,5-bis-trifluoromethyl-phenyl)borate

[0102] [H(OEt2)2][B(3,5-(CF3)2-C6H3)4]

[0103] When component (B) is a neutral strongly Lewis acidic compound, it is preferably selected from the group consisting of:

[0104] tris(pentafluorophenyl)borane B(C6F5)3,

[0105] tris(2,3,5,6-tetrafluorophenyl)borane B(2,3,5,6-C6F4H)3, and trimethylboron B(CH3)3.

[0106] The boron containing components (B) of the catalyst systems of the invention can be prepared according to procedures known in the state of the art, and in particular as described in the international patent application WO 96/27439.

[0107] Component (C) of the catalyst systems according to the present invention can be one or more organometallic aluminium compounds belonging to the following classes:

[0108] (a) organometallic aluminium compounds of formula (II):

Al(CH2—CR8R9R10)xR11yHz  (II)

[0109] wherein R8, R9, R10, R11, x, y and z have the meaning reported above; and

[0110] (b) reaction products of water with organometallic aluminium compounds of formula (III):

AIR123−wHw  (III)

[0111] wherein R12 and w have the meaning reported above.

[0112] In the organometallic aluminium compound belongs to the class (a), formula (II), R8 is preferably methyl or ethyl; R9 is preferably a saturated or unsaturated branched-chain C3-C30 alkyl or alkylaryl group, and more preferably a C4-C10 alkyl or alkylaryl group, or it is an optionally substituted phenyl group; R10 is preferably hydrogen; R11 is preferably a C1-C5 alkyl group, and more preferably an isobutyl group.

[0113] The above organometallic aluminium compounds can be suitably prepared according to the methods known in the state of the art, and preferably as described in the international patent application WO 96/02580.

[0114] A subclass of organometallic aluminium compounds particularly advantageous in the catalyst systems according to the present invention are the compounds of formula (II) wherein the (CH2—CR8R9R10) groups, the same or different from each other, are &bgr;,&dgr;-branched groups, corresponding to formula (CH2-CR8R10-CH2-CR13R14R15), wherein R8 and R10 have the meaning reported above; R13 and R14, the same or different from each other, are linear or branched, saturated or unsaturated C1-C20 alkyl, C3-C20 cycloalkyl, C6-C20 aryl, C7-C20 alkylaryl and C7-C20 arylalkyl radicals; and R15 is hydrogen or has the same meaning of R13 and R14. Non limiting examples of these compounds are tris(2,4,4-trimethylpentyl)aluminium (TIOA), bis(2,4,4-trimethylpentyl)aluminium hydride, isobutyl-bis(2,4,4-trimethylpentyl)aluminium, diisobutyl-(2,4,4-trimethylpentyl)aluminium, tris(2,4-dimethylheptyl)aluminium and bis(2,4-dimethylheptyl)aluminium hydride.

[0115] Another particular class of organometallic aluminium compounds of formula (II), suitable as a component (C) of the catalyst systems of the invention, are those wherein the (CH2—CR8R9R10) groups derive from the product of the oligomerization of lower &agr;-olefins, such as propylene or 1-butene. In this case, x is preferably 1 or 2.

[0116] These compounds can be prepared as described in the above-mentioned international patent application WO 96/02580.

[0117] A particularly preferred subclass of organometallic aluminium compounds is constituted by the compounds of formula (II) wherein the (CH2—CR8R9R10) groups, the same or different from each other, are &bgr;,&dgr;-branched groups, corresponding to formula (CH2—CR8R10—CR13R14R15), wherein R8, R10, R13, R14 and R15 have the meaning reported above.

[0118] In said subclass, R8 is preferably a C1-C5, more preferably a C1-C3 alkyl group; according to a preferred embodiment, said R8 is methyl. R10 is preferably hydrogen. R13 and R14 are preferably C1=l -C5, and more preferably C1-C3 alkyl groups. R15 is preferably hydrogen or a C1-C5 alkyl group, and more preferably a C1-C3 alkyl group.

[0119] Within this subclass, particularly preferred organometallic aluminium compounds are:

[0120] tris(2,3-dimethyl-butyl)aluminium, tris(2,3,3-trimethyl-butyl)aluminium,

[0121] tris(2,3-dimethyl-pentyl)aluminium, tris(2,3-dimethyl-hexyl)aluminium,

[0122] tris(2,3-dimethyl-heptyl)aluminium, tris(2-methyl-3-ethyl-pentyl)aluminium,

[0123] tris(2-methyl-3-ethyl-hexyl)aluminium, tris(2-methyl-3-ethyl-heptyl)aluminium,

[0124] tris(2-methyl-3-propyl-hexyl)aluminium, tris(2-ethyl-3-methyl-butyl)aluminium,

[0125] tris(2-ethyl-3-methyl-pentyl)aluminium, tris(2,3 -diethyl-pentyl)aluminium,

[0126] tris(2-propyl-3-methyl-butyl)aluminium, tris(2-isopropyl-3-methyl-butyl)aluminium,

[0127] tris(2-isobutyl-3-methyl-pentyl)aluminium, tris(2,3,3-trimethyl-pentyl)aluminium,

[0128] tris(2,3,3-trimethyl-hexyl)aluminium, tris(2-ethyl-3,3-dimethyl-butyl)aluminium,

[0129] tris(2-ethyl-3,3-dimethyl-pentyl)aluminium, tris(2-isopropyl-3,3-dimethyl-butyl)aluminium,

[0130] tris(2-trimethylsilyl-propyl)aluminium, tris(2-methyl-3-phenyl-butyl)aluminium,

[0131] tris(2-ethyl-3-phenyl-butyl)aluminium, tris(2,3-dimethyl-3-phenyl-butyl)aluminium,

[0132] and the corresponding compounds wherein one of the hydrocarbyl groups is replaced by hydrogen, and those wherein one or two of the hydrocarbyl groups are replaced by an isobutyl group.

[0133] These organoaluminium compounds can be prepared according to procedures known in the state of the art, and in particular as described in the International Application no. PCT/EP 98/06732.

[0134] When component (C) of the catalyst systems according to the present invention belongs to class (b), it is the reaction product of water with an organometallic aluminium compounds of formula (III), as reported above. The molar ratio between said organometallic aluminium compound and water ranges from 1:1 to 100:1, and preferably from 1:1 to 50:1. A particularly advantageous value of said molar ratio is 2:1.

[0135] In formula (III), R12 is preferably a substituted or unsubstituted non-straight C1-C10 alkyl or C7-C16 alkylaryl, optionally containing Si or Ge atoms; more preferably, all the substituents R12 are isoalkyl radicals.

[0136] The compounds of formula (III) are preferably selected from the group consisting of Al(iBu)3 (TIBA), AlH(iBu)2, Al(iHex)3, Al(C6H5)3, Al(CH2C6H5)3, Al(CH2CMe3)3, Al(CH2SiMe3)3, AlMe2iBu and AlMe(iBu)2.

[0137] According to a further preferred embodiment of the catalyst system of the invention, said organometallic aluminium compounds of formula (III) corresponds to the compounds of formula (II), as reported above, and the preferred compounds are the above-mentioned ones.

[0138] According to a further preferred embodiment of the invention, in said compound of formula (III), at least one R12 group has formula (CH2—CR8R9R10), wherein R8, R9 and R10 have the meaning reported above; more preferably said R12 group is a &bgr;,&dgr;-branched or a &bgr;,&dgr;-branched group.

[0139] When component (C) belong to class (b), water can be gradually added to the alkyl aluminium compound of formula (III) in solution, in an aliphatic or aromatic inert hydrocarbon solvent such as heptane or toluene; preferably, compound (C) of formula (III) can be brought into contact with the wet monomer or solvent in the reactor and the mixture of components (A) and (B) and an additional amount of compound (C) is then introduced into the reactor.

[0140] According to another embodiment, water can be reacted in combined form as hydrated salt, or it can be absorbed or adsorbed on an inert support, such as silica. According to a further embodiment, the alkyl aluminium compound (III) can be allowed to react with boric anhydride or with boric acid.

[0141] The components of the catalyst system according to the present invention can be brought into contact in different manners. The catalyst system may be formed by mixing together components (A), (B) and (C), following different orders of addition, preferably in solution, in a suitable non-polar solvent such as toluene, benzene, chlorobenzene, an alkane or an alkene, to form a liquid catalyst system. A preferred way of forming the catalyst system of the invention comprises first mixing components (A) and (B), and subsequently adding to the obtained mixture a solution of component (C), preferably in toluene.

[0142] The three-components catalyst system may be formed prior to its introduction into the reaction vessel, or it may be formed in situ.

[0143] Components (A) and (B) are preferably employed with a molar ratio ranging from 0.1:1 to 5:1, and more preferably ranging from 0.9:1 to 1.1:1.

[0144] The molar ratio between the aluminium of component (C) and the metal M of the bis-amido compound (A) preferably ranges from 1:1 to 1000:1, more preferably from 10:1 to 500:1, and even more preferably from 20:1 to 150:1.

[0145] The catalysts of the present invention can also be used on inert supports. This is achieved by depositing the components (A), (B) and/or (C), either singly or in mixture, on inert supports such as silica, alumina, silica/alumina, titania, zirconia, magnesia; suitable inert supports are olefin polymers or prepolymers, such as polyethylenes, polypropylenes or styrene/divinylbenzene copolymers. The thus obtained supported catalyst systems can be advantageously used in gas-phase oligomerization.

[0146] The catalyst systems according to the present invention can be conveniently used in oligomerization processes. In fact, the Applicant has surprisingly found that the presence of the component (C) in the catalyst system according to the present invention leads to higher oligomerization yields, lower decay rates and better reproducibility, as well as to a better specificity in the obtainment of &agr;-olefins, thus avoiding the undesired formation of internal or branched olefins. Therefore, it is another object of the present invention a process for the oligomerization or co-oligomerization of &agr;-olefins of formula CH2═CHR, wherein R is hydrogen or a C1-C20 alkyl, C5-C20 cycloalkyl or C6-C20 aryl radical, and preferably ethylene, in order to obtain linear &agr;-olefinic oligomers having a chain length from 4 to 30 carbon atoms and preferably 6-20 carbon atoms; said process is characterized in that the oligomerization reaction is performed in the presence of a catalyst system according to the present invention.

[0147] Non limiting examples of olefinic monomers which are suitable to be used in the oligomerization process according to the present invention are ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 4,6-dimethyl-1-heptene, 1-octene, 1-decene, 1-dodecee. 1-tetradecene, 1-hexadecene, 1-octadecene and allylcyclohexane, as well as cycloolefins (such as cyclopentene and cyclohexene) and conjugated or non-conjugated dienes (such as 1,4-hexadiene, isoprene, 1,3-butadiene, 1,5-hexadiene and 1,6-heptadienes).

[0148] The (co)oligomerization process according to the present invention can be carried out in the liquid phase or in gas phase; in the former case, it is advantageously carried out in the presence of an inert hydrocarbon solvent either aromatic, preferably toluene, or aliphatic, such as propane, hexane, heptane, isobutane, isopentane, cyclohexane and isooctane, and preferably isopentane or isooctane. Said solvent can serve even as a suitable solvent for the catalyst system.

[0149] Alternatively, the (co)oligomerization process may be carried out in an olefin solvent, and particularly in a mixture of linear &agr;-olefins and/or higher branched or internal olefins.

[0150] The starting &agr;-olefins can be supplied to the reactor together with an inert diluent, such as nitrogen or helium, when the reactant is gaseous, or in a liquid solvent when the reactant is in the liquid form.

[0151] The (co)oligomerization temperature is preferably comprised between −20° C. and 150° C., more preferably between 10° C. and 100° C., and even more preferably between 40 and 90° C.

[0152] The (co)oligomerization pressure is preferably comprised between 100 and 10,000 kPa, more preferably between 200 and 8,000 kPa, and even more preferably between 500 and 2,000 kPa.

[0153] Reaction times of from 1 minute to 5 hours have been found to be suitable, depending on the activity of the catalyst system and on the reaction conditions. At the end of the oligomerization reaction, a conventional catalyst deactivating agent, such as water, methanol, or another alcohol, may be added to the reaction mixture, in order to terminate the reaction. The reaction can be terminated also by introducing air.

[0154] Suitable operating conditions, in particular pressure and temperature, can be selected in order to yield oligomers having a “K factor” ranging from 0.3 to 0.8, wherein said “K factor” is the molar ratio [Cn−2]/[Cn], calculated from the slope of the graph of log [Cnmol %] versus n, wherein n is the number of carbon atoms in the olefinic product. The “K factor” gives an indication of the relative proportions of the olefins obtained from the oligomerization process.

[0155] The oligomerization product is a mixture of &agr;-olefins, preferably linear, having a chain length ranging from 4 to 30 carbon atoms, and preferably from 6 to 20 carbon atoms. Said olefins can be suitably recovered by conventional distillation and separation techniques, known in the state of the art. It is also possible to recover unconverted starting material and/or oligomeric products having a molecular weight outside the desired molecular weight, in order to process or recycle them.

[0156] The following experimental examples are reported for illustrative and non limiting purposes.

[0157] GENERAL PROCEDURES AND CHARACTERIZATIONS

[0158] All the operations with the catalyst systems and the catalyst components (A)-(C) were carried out under nitrogen atmosphere.

[0159] Oligomerization solvents

[0160] Isooctane (2,4,4-trimethylpentane, 99.8% purity) was dried by prolonged nitrogen purge, followed by passage over molecular sieves (water content of about 1 ppm).

[0161] Anhydrous toluene (99.8% purity) from Aldrich was dried over 4 Å molecular sieves (water content of about 3 ppm).

[0162] Ethylene (99.5% purity) was purified over a column containing 4 Å molecular sieves and BTS catalyst (purchased from BASF) in order to reduce water and oxygen content to <1 ppm.

[0163] Oligomers characterization

[0164] In order to evaluate oligomer product distribution, oligomers were characterized by GC characterization by using a HP 5890 apparatus, with the following chromatographic conditions:

[0165] Column: Cp-Sil 5 CB, film thickness=0.4 &mgr;m, internal diameter=0.22 mm, length 50 m (by Chrompack, catalogue no. 7719, 1986); injection temperature: 340° C.; detection temperature: 340° C.; initial temperature: 35° C. for 10 minutes; temperature program rate: 10.0° C./minute; final temperature: 325° C. for 20 minutes; internal standard: n-hexylbenzene. Response factors for the even linear &agr;-olefins and for cis- and trans-2-hexene, 2-ethyl-1-butene and n-hexylbenzene (internal standard) were determined using a standard calibration mixture. The yields of the C4-C30 olefins obtained from the GC analysis were used to calculate the “K factor” in oligomerization (via regression analysis).

[0166] The relative amounts of the different hexene isomers found from the GC analysis are a measure of the catalysts selectivity towards linear &agr;-olefin formation.

[0167] CATALYST COMPONENTS

[0168] Component (A):

[0169] {1,2-bis(t-butylamide)tetramethyldisilane}-zirconium dibenzyl

[0170] {1,2-bis(t-butylamide)tetramethyldisilane}-zirconium dibenzyl was prepared as described in the international patent application WO 96/27439 (Example 1.2.1).

[0171] Component (B):

[0172] [Me2PhNH]+[B(C6F5)4]−

[0173] Dimethylanilinium tetrakis(pentafluorophenyl)borate, [Me2PhNH]−[B(C6F5)4]−, was obtained from Akzo-Nohel (catalogue 1997).

[0174] Component (C):

[0175] Tris(2-methyl-propyl)aluminium (TIBA)

[0176] Tris(2-methyl-propyl)aluminium was obtained from Aldrich (catalogue n. 25, 720-6, 1996-7).

[0177] Tris(2,4,4-trimethyl-pentyl)aluminium (TIOA)

[0178] Tris(2,4,4-trimethyl-pentyl)aluminium was prepared as described in WO 96/02580.

[0179] Tris(2,3-dimethyl-hexyl)aluminium (TDMHA)

[0180] Tris(2,3-dimethyl-hexyl)aluminium was prepared as described in the International Application no. PCT/EP 98/06732.

[0181] Tris(2,3-dimethyl-butyl)aluminium (TDMBA)

[0182] Tries(2,3-dimethyl-butyl)aluminium was prepared as described in the International Application no. PCT/EP 98/06732.

[0183] (2-Methyl-propyl)aluminoxane (TIBAO)

[0184] TIBAO was either obtained from Witco as a 30% w/w solution in cyclohexane (Examples 14-17) or prepared immediately prior to use by reacting a 0.45 M toluene solution of TIBA (obtained as reported above) with a half-equivalent of water, whilst maintaining the reaction temperature in the range 5-15° C. (Example 9). In Example 3, TIBAO was prepared in situ by addition of TIBA to the autoclave containing wet isooctane (0.19 mmol water in 190 g isooctane) at 50° C. and stirring for 30 minutes.

[0185] (2,4,4-Trimethyl-pentyl)aluminoxane (TIOAO)

[0186] (2,4,4-Trimethyl-pentyl)aluminoxane was prepared immediately prior to use by reacting a 0.45 M toluene solution of tris(2,4,4-trimethyl-pentyl)aluminium (TIOA, prepared as described above) with a half-equivalent of water, whilst maintaining the reaction temperature in the range 5-15° C.

[0187] (2,3Dimethyl-hexyl)aluminoxanie (TDMHAO)

[0188] (2,3)-Dimethyl-hexyl)aluminoxane was prepared immediately prior to use, according to the procedure used to prepare TJOAO.

[0189] (2,3-Dimethyl-butyl)aluminoxane (TDMBAO)

[0190] (2,3-Dimethyl-butyl)aluminoxane was prepared immediately prior to use, according to the procedure used to prepare TIOAO.

[0191] Methylalumoxane (MAO)

[0192] Methylalumoxane was obtained from Akzo-Nobel as a solution in toluene (11.3% w/w Al, 1997).

[0193] CATALYST SYSTEM PREPARATION

[0194] Catalyst preparation was carried out under nitrogen in a Braun MB 200-G dry box.

[0195] Component (A) and Component (B) were placed in a reaction bottle. A mixture of toluene and component (C) was added to the stirred mixture, which was then maintained under stirring for 20 minutes, giving a very pale yellow homogeneous solution. This solution was then used immediately in the oligomerization reaction.

[0196] OLIGOMERIZATION TRIALS

COMPARATIVE EXAMPLES 1, 2, 4, 8 and 13, and EXAMPLES 3, 5-7, 9-12 and 14-17.

[0197] Oligomerization trials were performed in a 1-litre steel autoclave, with jacket cooling with two Julabo baths, with anchor stirrer (autoclave 1) or turbine/gas stirrer (autoclave 2). In order to remove traces of water from the reactor, the reactor was evacuated overnight at 2 kPa, at 70° C. The reactor temperature was then decreased to 50° C. and the reactor pressurized with N2 (100 kPa). Subsequently, the reactor was scavenged with a solution of TIBA (100 mg in Autoclave 1, Examples 1-12; 300 mg in Autoclave 2, Example 13) or TIBAO (300 mg in Autoclave 2, Examples 14-17) in isooctane (30 g in Autoclave 1; 70 g in Autoclave 2) and continuous stirring was applied for 30 minutes. The reactor contents were discharged via a tap in the base of the autoclave.

[0198] The reactor was evacuated to 0.02 bar and loaded with the amounts of isooctane reported in Table 1; the reactor was heated to 50° C. and pressurized to 600 kPa with ethylene. The amounts of component (C) indicated in Table 1 (reactor) and n-hexylbenzene (0.5-3.5 g) as internal standard were added to the reactor and the stirring was continued for 30 minutes.

[0199] A catalyst system prepared as described above, containing {1,2-Bis(t-butylamide)tetramethyldisilane}-zirconium dibenzyl (Component A) and [Me2PhNH][B(C6F5)4]− (Component B) in the amounts reported in Table 1, was introduced into the reactor using an injection system. In autoclave 2, an additional amount of isooctane (about 4 g) was utilized in the injection of the catalyst solution. Addition of the catalyst solution resulted in a moderate exotherm (in the range of 51-57° C.), which reached a maximum within 1-2 minutes and was followed by rapid re-establishment of the original temperature. Temperature and pressure were monitored throughout the reaction, as well as ethylene consumption, whilst maintaining a constant ethylene pressure. After 60 minutes, the oligomerization was stopped by rapid venting of the ethylene, decanting the product mixture into a collection bottle using a tap in the base of the autoclave and opening of the autoclave. Exposure of the mixture to air resulted in rapid deactivation of the catalyst.

[0200] All the reaction conditions are reported in Table 1.

[0201] The small amount of polyethylene (PE) by-product contained in the crude reaction product mixture was collected by filtration, followed by washing with hexane (500 ml) for 1 hour.

[0202] The polymer was dried overnight (13 kPa, 70° C.) applying a stream of N2 and finally weighed. The yields of oligomers and PE are reported in Table 2 and give a measure of the selectivity of the catalyst towards oligomerization compared to polymerization.

[0203] The amount of the C6 fraction in the final product is reported in Table 2 (Yld. Hexene); the composition of said C6 fraction, made up of 1-hexene (1-H), cis-2-hexene (c-2-H), trans-2-hexene (t-2-H) and 2-ethyl-1-butene (2-EB), is reported in Table 3.

[0204] Furthermore, the amount of the C12 fraction in the final product is reported in Table 2 (Yld. Dodecene); the composition of said C12 fraction is reported in Table 3.

[0205] The obtained data demonstrate the unexpectedly higher oligomerization activities obtained with the catalyst systems according to the present invention, in comparison with the activities obtainable with the catalysts known in the state of the art, wherein no organometallic aluminium compounds are used (Comp. Example 1).

[0206] Furthermore, catalyst compositions containing organometallic aluminium compounds not envisaged by the specific class according to the present invention show poor oligomerization yields (see Comp. Examples 2, 4 and 13, in comparison with Examples 3, 9 and 14 respectively).

[0207] Finally, the obtained results sustain the inventiveness of the catalyst systems according to the present invention, wherein component (C) is selected among a specified group of compounds; in fact, Comp. Example 8 shows that a catalyst comprising MAO is able to exert only a poor activity in ethylene oligomerization, much lower than the activities shown by the organometallic aluminium compounds of the invention (see Examples 9-12). 1 TABLE 1 Component (A) Component (B) (C) premix (C) reactor Toluene Isooctane Example Reactor (&mgr;mol) (&mgr;mol) Component (C) (mmol) (mmol) (g) (g) COMP. 1 1 14.1 14.9 none 0 0 11.2 190 COMP. 2 1 16.4 16.9 TIBA 0.37 0.87 11.2 190  3 1 14.4 15.3 TIBAO 0.37 0.88 11.2 190 COMP. 4 1 7.3 7.8 TIBA 0.18 0.42 5.6 196  5 1 7.5 7.8 TIOA 0.19 0.41 5.6 196  6 1 7.4 7.7 TDMBA 0.19 0.42 5.6 196  7 1 7.4 7.8 TDMHA 0.17 0.45 5.6 196 COMP. 8 1 7.5 7.8 MAO 0.18 0.45 5.5 196  9 1 7.3 7.5 TIBAO 0.21 0.45 5.6 196 10 1 7.4 8.2 TIOAO 0.23 0.49 5.6 196 11 1 7.3 7.3 TDMBAO 0.18 0.45 5.6 196 12 1 7.7 7.9 TDMHAO 0.19 0.42 5.6 196 COMP. 13 2 14.8 15.3 TIBA 0.37 0.90 11.3 207 14 2 15.3 15.5 TIBAO 0.38 1.02 11.3 229 15 2 15.4 17.9 TIBAO 0.01 0.72 11.3 228 16 2 14.9 14.7 TIBAO 0.19 0.50 11.3 228 17 2 15.3 16.4 TIBAO 0.10 0.26 11.3 228

[0208] 2 TABLE 2 Yld. C4-C30 Activity C4-C30 &agr;-olefins &agr;-olefins Yld. PE Yld. PE Yld. Hexene Yld. Dodecene Example Comp. (C) (g) (Kg/gZr · h) (g) (% wt.) (g) (g) K factor COMP. 1 none 38.9 30.3 0.3 0.7 5.7 5.3 0.72 COMP. 2 TIBA 80.2 53.4 1.4 1.7 10.7 10.2 0.73  3 TIBAO 99.0 75.1 0.4 0.4 14.8 12.5 0.72 COMP. 4 TIBA 28.5 43.0 0.4 1.4 4.0 3.8 0.73  5 TIOA 58.3 85.0 0.9 1.5 8.6 7.5 0.71  6 TDMBA 56.0 83.2 1.6 2.8 7.7 7.1 0.73  7 TDMHA 61.0 90.0 1.0 1.7 8.4 7.9 0.73 COMP. 8 MAO 26.6 38.7 0.35 1.3 4.0 3.5 0.72  9 TIBAO 64.7 97.7 1.3 1.9 9.8 8.8 0.70 10 TIOAO 71.7 105.8 4.8 6.3 9.6 9.3 0.73 11 TDMBAO 73.6 109.9 2.0 2.6 11.7 10.1 0.69 12 TDMHAO 77.7 110.8 1.2 1.6 11.7 10.5 0.70 COMP. 13 TIBA 67.6 50.1 0.3 0.4 10.6 8.0 0.67 14 TIBAO 106.7 76.3 0.3 0.3 18.9 12.6 0.68 15 TIBAO 151.3 107.7 0.1 0.1 26.5 17.9 0.68 16 TIBAO 116.8 85.9 0.4 0.3 22.4 13.2 0.69 17 TIBAO 128.5 92.4 0.4 0.3 24.9 14.6 0.68

[0209] 3 TABLE 3 Yld. Hexene 1-H* c-2-H* t-2-H* 2-EB* Yld. Dodecene 1-Dodecene Example Comp. (C) (g) (% wt.) (% wt.) (% wt.) (% wt.) (g) (% wt.) COMP. 1 none 5.7 99.84 0.05 0.03 0.07 5.3 99.0 COMP. 2 TIBA 10.7 99.53 0.07 0.00 0.40 10.2 96.9  3 TIBAO 14.8 99.46 0.10 0.07 0.37 12.5 97.4 COMP. 4 TIBA 4.0 99.67 0.00 0.00 0.33 3.8 98.1  5 TIOA 8.6 99.73 0.05 0.00 0.22 7.5 98.2  6 TDMBA 7.7 99.66 0.05 0.00 0.27 7.1 97.8  7 TDMHA 8.4 99.72 0.06 0.00 0.21 7.9 97.5 COMP. 8 MAO 4.0 99.73 0.05 0.00 0.22 3.5 98.4  9 TIBAO 9.8 99.68 0.10 0.00 0.22 8.8 97.9 10 TIOAO 9.6 99.70 0.07 0.00 0.23 9.3 97.8 11 TDMBAO 11.7 99.67 0.07 0.06 0.20 10.1 97.6 12 TDMHAO 11.7 99.67 0.10 0.00 0.17 10.5 97.6 COMP. 13 TIBA 10.6 99.53 0.08 0.00 0.39 8.0 97.3 14 TIBAO 18.9 99.56 0.09 0.08 0.27 12.6 97.9 15 TIBAO 26.5 99.49 0.13 0.10 0.28 17.9 97.3 16 TIBAO 22.4 99.56 0.08 0.12 0.24 13.2 96.9 17 TIBAO 24.9 99.67 0.05 0.08 0.19 14.6 97.1 *1-H = 1-hexene; c-2-H = cis-2-hexene; t-2-H = trans-2-hexene; 2-EB = 2-ethyl-1-butene

Claims

1. A catalyst system for &agr;-olefin oligomerization comprising the product obtainable by contacting the following components:

(A) one or more bis-amido compounds having formula (I):

7

wherein M is Ti, Zr or Hf;

N is a trivalent nitrogen atom;

the Y atoms, the same or different from each other, are selected from the group consisting of Si, Ge and Sn;

the X groups, the same or different from each other, are selected from the group consisting of hydrogen, halogen, linear or branched, saturated or unsaturated C1-C20 alkyl, C1-C20 alkoxyl, C3-C20 cycloalkyl, C6-C20 aryl, C6-C20 aryloxyl, C7-C20 alkylaryl and C7-C20 arylalkyl radicals, optionally containing one or more Si, Ge, O, S, P, B or N atoms; or two X groups form a ring having from 4 to 8 members;

R1, R2, R3, R4, R5 and R6, the same or different from each other, are linear or branched, saturated or unsaturated C1-C20 alkyl, C3-C20 cycloalkyl, C6-C20 aryl, C7-C20 alkylaryl or C7-C20 arylalkyl radicals, optionally containing one or more Si, Ge, O, S, P, B or N atoms; or are Si(R7)3 groups, wherein the groups R7, the same or different from each other, are linear or branched, saturated or unsaturated C1-C10 alkyl, C3-C10 cycloalkyl, C6-C15 aryl, C7-C15 alkylaryl or C7-C15 arylalkyl groups; or two or four substituents of R1, R2, R3, R4, R5 and R6, linked to two vicinal atoms, form one or two rings having from 4 to 8 members;

Q is a neutral Lewis base; and

m is an integer ranging from 0 to 9;

said bis-amido compound being optionally present in the form of a dimer;

(B) one or more activating cocatalysts selected from:

compounds having formula Y+Z−, wherein Y+ is a cation capable of reacting irreversibly with a substituent X of the compound of formula (I), and Z− is a compatible non-coordinating anion comprising at least one boron atom; and

neutral strongly Lewis acidic compounds comprising at least one boron atom;

(C) one or more compounds selected from the following classes:

(a) organometallic aluminium compounds having formula (II):

Al(CH2—CR8R9R10)xR11yHz  (II)

wherein, in the (CH2—CR8R9R10) groups, the same or different from each other, R8 is a linear or branched, saturated or unsaturated C1-C10 alkyl, C3-C13 cycloalkyl or C7-C16 alkylaryl radical;

R9 is a saturated or unsaturated C1-C50 alkyl, C3-C50 cycloalkyl, C6-C50 aryl, C7-C50 alkylaryl or C7-C50 arylalkyl radical, said radical being different from a straight alkyl or alkenyl group;

or R8 and R9 form together a ring having from 4 to 6 carbon atoms;

R10 is hydrogen or a linear or branched, saturated or unsaturated C1-C10 alkyl, C6-C15 aryl, C7-C16 alkylaryl radical or arylalkyl radical, optionally containing one or more Si or Ge atoms;

R11 is a linear or branched, saturated or unsaturated C1-C10 alkyl, C3-C15 cycloalkyl, C6-C15 aryl, C7-C16 alkylaryl or C7-C16 arylalkyl radical;

x is an integer ranging from 1 to 3; z is 0 or 1; and y is 3−x−z; and

(b) the reaction products of water with organometallic aluminium compounds of formula (III):

AlR123−wHw  (III)

wherein the substituents R12, the same or different from each other, are selected from the group consisting of linear or branched, saturated or unsaturated C1-C50 alkyl, C3-C50 cycloalkyl, C6-C50 aryl, C7-C50 alkylaryl and C7-C50 arylalkyl radicals, optionally containing one or more Si or Ge atoms, wherein at least one of said substituents R12 is different from a straight alkyl group; and w is 0 or 1;

the molar ratio between said organometallic aluminium compound and water being comprised between 1:1 and 100:1.

2. The catalyst system according to claim 1, characterized in that said bis-amido compound is present in the form of a dimer having formula (IV):

8

wherein M, Y, X, R1, R2, R3, R4, R5, R6 and Q have the meaning reported in claim 1, and n is 0 or 1.

3. The catalyst system according to claim 1 or 9, characterized in that, in said bis-amido compound of formula (I) or (IV), M is Zr and the Y atoms are Si atoms.

4. The catalyst system according to anyone of claims 1 to 3, characterized in that, in said bis-amido compound of formula (I) or (IV), X is selected from the group consisting of hydrogen, methyl, ethyl, propyl, n-butyl, phenyl, 4-alkyl-phenyl and benzyl radicals.

5. The catalyst system according to anyone of claim 1 to 4, characterized in that, in said bis-amido compound of formula (I) or (IV), R1, R2, R3, R4, R5 and R6 are selected from the group consisting of methyl, ethyl, propyl, n-butyl, t-butyl, t-amyl, 1,1,3,3-tetramethyl-butyl, cyclohexyl, phenyl, dimethyl-phenyl, diisopropyl-methyl, trimethyl-silyl, tri-t-butyl-silyl phenylmethyl-ethyl, diphenyl-ethyl and triphenyl-methyl.

6. The catalyst system according to any one of claims 1 to 5, characterized in that, in said bis-amido compound of formula (I) or (IV), Q is selected from the group consisting of diethylether, tetrahydrofuran, dimethylaniline, aniline, n-butylamine and trimethylphosphine.

7. The catalyst system according to claim 1, characterized in that, in said activating cocatalyst of formula Y+Z−, Y+ is a quaternary ammonium cation or a metal cation, and Z− is a borate of formula [B(R1)4]−, wherein R1 is selected from the group consisting of hydrogen, C1-C10 alkyl, C3-C10 cycloalkyl, C6-C15 aryl, C7-C15 alkylaryl and C7-C15 arylalkyl groups, optionally substituted with one or more halogens.

8. The catalyst system according to claim 7, characterized in that Y− is tri-n-butylammonium or dimethylanilinium, and Z− is selected from the group consisting of [B(C6F5)4]−, [R1B(C6F5)3]−, [B(FC6H4)4]−, [KrB(FC6H4)3]−, [B{(CF3)2(C6H3)}] and [R1B{(CF3)2(C6H3)}3]−, wherein R1 has the meaning reported in claim 7.

9. The catalyst system according to claim 1, characterized in that said activating cocatalyst is a neutral strongly Lewis acidic compound selected from tris(pentafluorophenyl)borane, tris(2,3,5,6-tetrafluorophenyl)borane and trimethylboron.

10. The catalyst system according to claim 1, characterized in that, in said organometallic aluminium compound of formula (II), R8 is methyl or ethyl; R9 is a branched C4-C10 alkyl or alkylaryl group, or a phenyl group; R10 is hydrogen; and R11 is a C1-C5 alkyl group.

11. The catalyst system according to claim 1, characterized in that, in said organometallic aluminium compound of formula (II), the (CH2—CR8R9R10) groups, the same or different from each other, are &bgr;,&dgr;-branched groups.

12. The catalyst system according to claim 11, characterized in that said organometallic aluminium compound of formula (II) is selected from the group consisting of tris(2,4,4-trimethylpentyl)aluminium, bis(2,4,4-trimethylpentyl)aluminium hydride, isobutyl-bis(2,4,4-trimethylpentyl)aluminium, diisobutyl-(2,4,4-trimethylpentyl)aluminium, tris(2,4-dimethylheptyl) aluminium and bis(2,4-dimethylheptyl)aluminium hydride.

13. The catalyst system according to claim 11, characterized in that said &bgr;,&dgr;-branched groups correspond to formula (CH2—CR8R10—CH2—CR13R14R15), wherein R8 and R10 have the meaning reported in claim 1; R13 and R14, the same or different from each other, are linear or branched, saturated or unsaturated C1-C20 alkyl, C3-C20 cycloalkyl, C6-C20 aryl, C7-C20 alkylaryl and C7-C20 arylalkyl radicals; and R15 is hydrogen or has the same meaning of R13 and R14.

14. The catalyst system according to claim 1, characterized in that, in said organometallic aluminium compound of formula (II), the (CH2—CR8R9R10) groups, the same or different from each other, are &bgr;,&dgr;-branched groups.

15. The catalyst system according to claim 14, characterized in that said &bgr;,&dgr;-branched groups correspond to formula (CH2—CR8R10—CR13R14R15), wherein R8 and R10 have the meaning reported in claim 1; R13 and R14, the same or different from each other, are linear or branched, saturated or unsaturated C1=l -C20 alkyl, C3-C20 cycloalkyl, C6-C20 aryl. C7-C20 alkylaryl or C7-C20 arylalkyl radicals; and R15 is hydrogen or has the same meaning of R13 and R14.

16. The catalyst system according to claim 15, characterized in that said organometallic aluminium compound of formula (II) is selected from the group consisting of:

tris(2,3 -dimethyl-butyl)aluminium, tris(2,3,3-trimethyl-butyl)aluminium, tris(2,3-dimethyl-pentyl)aluminium, tris(2,3-dimethyl-hexyl)aluminium, tris(2,3 -dimethyl-heptyl)aluminium, tris(2-methyl-3-ethyl-pentyl)aluminium, tris(2-methyl-3-ethyl-hexyl)aluminium, tris(2-methyl-3-ethyl-heptyl)aluminium, tris(2-methyl-3-propyl-hexyl)aluminium, tris(2-ethyl-3-methyl-butyl)aluminium, tris(2-ethyl-3-methyl-pentyl)aluminium, tris(2,3-diethyl-pentyl)aluminium, tris(2-propyl-3-methyl-butyl)aluminium, tris(2-isopropyl-3-methyl-butyl)aluminium, tris(2-isobutyl-3-methyl-pentyl)aluminium, tris(2,3,3-trimethyl-pentyl)aluminium, tris(2,3,3-trimethyl-hexyl)aluminium, tris(2-ethyl-3,3-dimethyl-butyl)aluminium. tris(2-ethyl-3 3-dimethyl-pentyl)aluminium, tris(2-isopropyl-3,3-dimethyl-butyl)aluminium, tris(2-trimethylsilyl-propyl)aluminium, tris(2-methyl-3-phenyl-butyl)aluminium, tris(2-ethyl-3-phenyl-butyl)aluminium and tris(2,3-dimethyl-3-phenyl-butyl)aluminium.

17. The catalyst system according to claim 1, characterized in that, in said organometallic aluminium compound of formula (III), R12 is a substituted or unsubstituted non-straight C1-C10 alkyl or C7-C16 alkylaryl, optionally containing Si or Ge atoms.

18. The catalyst system according to claim 17, characterized in that said organometallic aluminium compound of formula (III) is selected from the group consisting of Al(iBu)3, AlH(iBu)2, Al(iHex)3, Al(C6H5)3, Al(CH2C6H5)3, Al(CH2CMe3)3, Al(CH2SiMe3)3, AlMe2iBu and AlMe(iBu)2.

19. The catalyst system according to claim 17, characterized in that, in said organometallic aluminium compound of formula (III), at least one group R12 is a &bgr;,&dgr;-branched group.

20. The catalyst system according to claim 19, characterized in that said organometallic aluminium compound is tris(2,3-dimethyl-butyl)aluminium or tris(2,3-dimethyl-hexyl)aluminium.

21. The catalyst system according to claim 17, characterized in that, in said organometallic aluminium compound of formula (III), at least one group R12 is a &bgr;,&dgr;-branched group.

22. The catalyst system according to claim 21, characterized in that said organometallic aluminium compound is tris(2,4,4-trimethylpentyl)aluminium.

23. The catalyst system according to claim 1, characterized in that, in component C, the molar ratio between said organometallic aluminium compound of formula (III) and water ranges from 1:1 to 50:1.

24. The catalyst system according to claim 1, characterized in that the molar ratio between component (A) and component (B) ranges from 0.1:1 to 5:1.

25. The catalyst system according to claim 1, characterized in that the molar ratio between the aluminium of component (C) and the metal M of the component (A) ranges from 10:1 to 500:1.

26. A process for the oligomerization or co-oligomerization of &agr;-olefins of formula CH2═CHR, wherein R is hydrogen or a C1-C20 alkyl, C5-C20 cycloalkyl or C6-C20 aryl radical, comprising the reaction of oligomerization of one or more &agr;-olefins in the presence of a catalyst system as described in any one of claims 1 to 25.

27. The process according to claim 26, characterized in that said &agr;-olefin is selected from the group consisting of ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 4,6-dimethyl-1-heptene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene and allylcyclohexane.

28. The process according to claim 26, characterized by being carried out in the presence of a solvent selected from isopentane, isooctane and toluene.

29. The process according to claim 26, characterized by being carried out at a temperature ranging from 10° C. to 100° C., at a pressure ranging from 200 to 8,000 kPa.