Method of manufacturing an in-mold laminate component

Abstract

A method is provided for manufacturing a painted plastic component such as painted air bag covers, side cladding or exterior bumpers, which includes a painted film sheet and a one-piece thermoplastic elastomeric structural carrier. A bottom contact surface of the film sheet bonds with a front contact surface of the structural carrier by diffusion between the contact surfaces thereof within a mold cavity of an injection mold separate from the mold cavity of a vacuum mold which is utilized to vacuum-mold the film sheet to form the desired painted plastic component.

Description

CROSS-REFERENCE TO RELATED APPLICATION

[0001] This application is a continuation-in-part of U.S. patent application Ser. No. 551,517, filed Nov. 1, 1995, entitled “Method Of Manufacturing A Painted Vehicle Part.”

TECHNICAL FIELD

[0002] This invention relates to methods of manufacturing painted parts, and in particular to methods of manufacturing painted plastic parts adapted for use on motor vehicles such as air bag covers, side cladding, instrument panel cluster bezels, exterior bumpers, and the like.

BACKGROUND ART

[0003] Typically, plastic parts are painted after they are molded. The painting process requires elaborate facilities and consequently necessitates large expenses. For instance, significant square footage of a factory must be dedicated to a clean room environment for the spraying of paint and clear coat and for the baking and curing of paint on components, such as those components used in the automotive industry, such as body panels, air bag covers, instrument panels and the like. Moreover, solvent-based paints have in recent years raised significant environmental concerns because of the volatile organic components which are emitted into the air during the application of such solvent-based paints. As a result, the evaporation of such solvents must be strictly monitored to satisfy environmental and safety regulations.

[0004] In addition, automotive components, especially interior automotive components, are strictly scrutinized following the painting process in order to match or conform the automotive component to the styling and aesthetic requirements of the associated interior trim product. Painting such automotive components following the molding process, raises quality concerns with respect to the color, consistency, and thickness of each individual paint application.

[0005] U.S. Pat. No. 4,902,557, the Rohrbacher reference discloses a method and apparatus for manufacturing a thermoplastic polyolefin composite useful as an exterior auto or truck body part.

[0006] U.S. Pat. No. 4,769,100, the Short reference, teaches a method of applying a carrier film pre-printed with metallic paint to an automobile body panel in a vacuum forming process.

[0007] U.S. Pat. No. 4,952,351 and U.S. Pat. No. 5,466,412, the Parker patents, teach a method of manufacturing an air bag cover for an inflatable air bag system including a bondable film carrier, which is painted after the film carrier is molded.

[0008] However, the prior art fails to provide a method of manufacturing a painted component wherein the step of painting the component after molding is eliminated and further where the component has the structural integrity both in terms of durability and strength to support varying applications.

DISCLOSURE OF INVENTION

[0009] An object of the present invention is to provide a method for manufacturing a painted component while addressing paint quality issues such as: drips, runs, spits, dry spray, light coverage, gloss, color match, contamination and paint adhesion.

[0010] Another object of the present invention is to provide a method for manufacturing a painted component and reducing molding scrap due to splay, flow marks and minor surface imperfections which can be completely covered.

[0011] Yet still another object of the present invention is to provide a method of manufacturing a painted component, such as a composite air bag cover, side cladding, and the like, wherein the components have increased durability.

[0012] In carrying out the above objects and other objects of the present invention a method is provided for manufacturing a painted plastic component. The method includes the steps of providing a film sheet having top and bottom surfaces; vacuum molding the film sheet and the mold cavity to obtain a pre-form; placing the pre-form in a mold cavity of an injection mold having a shape defining the desired plastic component; and injecting a thermoplastic elastomer into the mold cavity of the injection mold to generate a structural carrier for the pre-form, the generation of the structural carrier creating sufficient pressure and heat to bond the structural carrier to the bottom surface of the pre-form to form the molded laminate component.

[0013] Further in carrying out the above objects and other objects of the present invention, a method is provided for manufacturing a molded laminate automotive component. The method includes the steps of inserting a film sheet into a vacuum forming station to form the film sheet into a predetermined automotive component shape to create a formed film sheet having top and bottom surfaces, placing the formed film sheet in a mold cavity of an injection mold having a shape defining the automotive component, and injecting a thermoplastic elastomer into the mold cavity of the injection mold, such that the thermoplastic elastomer is in mating contact with the bottom surface of the formed film sheet, to generate a structural carrier for the formed film sheet, the generation of the structural carrier creating sufficient pressure and heat to bond the structural carrier to the bottom surface of the formed film sheet to form the molded laminate automotive component.

[0014] The above objects and other objects, features and advantages of the present invention are readily apparent from the following detailed description of the best mode for carrying out the invention when taken in connection with the accompanying drawings.

BRIEF DESCRIPTION OF DRAWINGS

[0015] FIG. 1 is a front elevational view of one type of air bag cover adapted to be mounted on a side door;

[0016] FIG. 2 is a rear elevational view of the air bag cover depicted in FIG. 1;

[0017] FIG. 3 is a sectional view of the air bag cover of FIG. 1 taken along lines 3-3;

[0018] FIG. 4 is a schematic view of a conventional injection molding system which may be utilized to make the plastic components of the present invention, the system is depicted in an open position with the pre-form placed between two plates of the mold body;

[0019] FIG. 5 is a schematic view of a conventional injection molding system depicted in a closed position, with the pre-form placed between the two plates of mold body; and,

[0020] FIG. 6 is a schematic view of a conventional injection molding system depicting the mold cavity with the molten resin injected therein to form the structural carrier for the pre-form.

BEST MODE FOR CARRYING OUT THE INVENTION

[0021] While the examples and figures provided herein refer to automotive plastic components, this invention has substantial application in other areas and is thus intended to have broader scope than the cited representative examples. In essence, this invention can be used with any application calling for a painted plastic component.

[0022] Referring now to the drawing figures, there is illustrated in FIG. 1 a front elevational view of one type of air bag cover, generally indicated at 10, adapted to be mounted on an automotive side door. The air bag cover 10 includes a painted one-piece outer layer 12, composed of a film sheet, preferably a pre-painted film sheet, which is vacuum molded in a vacuum mold from a material compatible with the air bag body or structural carrier 14, which is preferably injection molded in an injection mold. The air bag body 14 is preferably composed of a thermoplastic elastomer. The elastomer of the air bag body or structural carrier 14 should be compatible with the outer layer 12 so that a bottom contact surface of the outer layer 12, mounts with the front contact surface of the air bag body 14 by diffusion between the surfaces thereof in the injection mold to prevent the air bag body 14 from separating from the outer layer 12 during use of the air bag cover 10.

[0023] The outer layer 12 is composed of a film sheet that is pre-painted. The film sheet is preferably a polyester sheet such as Mylar®, a polyurethane or polycarbonate sheet.

[0024] In the preferred embodiment, the outer layer comprises a film sheet with the following coatings placed thereon, a layer of acrylic color in mating contact with the film sheet and a layer of polyvinylidine fluoride (PVDF) with an acrylic clear coat to protect the film from damage and to provide film elasticity, chemical resistance, stain resistance, weathering and UV protection. In the most preferred embodiment, PVDF comprises 72% of the total film thickness which is 0.2 mils.

[0025] The thermoplastic elastomer of the air bag body or structural carrier 14 is preferably a thermoplastic elastomer such as a thermoplastic polyolefin, thermoplastic urethane, polyester, polycarbonate, a mixture of polycarbonate and ABS (acrylonitrile/butadiene/styrene) or similar material.

[0026] For other automotive applications, the carrier 14 is varied to accommodate the intended use. Accordingly, for bumper/fascia applications, the structural carrier 14 can be selected from at least the following materials: lomod®, bexloy® and thermoplastic polyolefin. For cluster bezel applications, the structural carrier 14 can be selected from at least the following materials: ABS (acrylonitrile/ butadiene/styrene), a mixture of polycarbonate and ABS, polycarbonate, and polypropylene.

[0027] The durometer and elastic or flex modulus of the materials also vary depending on the desired stiffness of the component. Typically, the durometer of the air bag body 14 will be in the range of about 20 Shore D to 100 Shore D, while the flexural modulus will be in the range of about 15,000 to about 400,000 psi. Also, typically, the durometer of the outer layer 12 will be in the range of about 15 Shore A to 100 Shore A. These ranges of course vary depending on the desired plastic component to be manufactured and are only illustrative of one example.

[0028] As depicted in FIG. 3, a sectional view of the air bag cover of FIG. 1 taken along lines 3-3, in a manufactured component, the air bag body or structural carrier 14 supports the outer layer 12 which has a pre-painted coating 16 placed thereon, followed by a base coat 18, preferably a layer of acrylic color, and a clear coat 20, preferably an acrylic clear coat and a layer of PVDF.

[0029] Referring now to FIG. 4, there is illustrated a conventional injection mold, generally indicated at 22, for making a plastic component pursuant to the present invention.

[0030] Briefly, with an injection molding system there is included an injection molding machine, having a nozzle, generally indicated at 24, for injecting predetermined amounts or shots of molten resin. The injection molding machine includes a hydraulic screw ram which is disposed in a bore formed in a barrel of the injection molding machine. The ram plasticizes and advances resin towards the nozzle 24. Upon complete plasticization of the resin, the screw ram is hydraulically advanced towards threaded portions of the barrel to inject molten plastic through the nozzle 24, as is well known in the art.

[0031] As depicted in FIG. 4, opposing surfaces of male and female mold parts 26 and 28 respectively define a mold cavity 30.

[0032] As illustrated in FIG. 5, there is a depiction of a one-piece pre-form 32 created from the vacuum molded film sheet which is first placed in the mold cavity 30. Thereafter, as depicted in FIG. 6, the air bag body or structural carrier 14 is molded in the plastic injection molding system to form a completed unitary laminate plastic component.

[0033] The body of the air bag cover 14 may also be formed from thermoplastic polyolefin, polycarbonate, tee tpe, sebs tpe, and a mixture of polycarbonate and acrylonitrile/butadiene/styrene (ABS). The corresponding film sheet 12 must be compatible with the plastic of the body so that diffusion between contact surfaces occurs. Additionally, the laminate should be compatible with the substrate on which the laminate is to be adhered. In general, this requirement is achieved by selecting a structural carrier 14 with at least one or more materials common to the substrate on which the laminate is to be adhered. As an example, with a thermoplastic polyolefin substrate, the structural carrier should include polypropylene.

[0034] In an alternative embodiment, the mold can be modified to produce a plastic component with embossed lettering. This embossed effect is achieved by etching into the mold the desired pattern or letters so that the letters have at least a 0.5 mm radius on the edge of the letter, or else the film will tear and stretch.

[0035] The unique features of the laminate plastic components are 1) a stiff inner material to support the intended application; 2) reduction and/or elimination of paint problems such as drips, runs, spits, dry spray, light coverage and gloss and improved color match and paint adhesion; 3) reduced molding scrap due to splay, flow marks and minor surface imperfections, which can be completely covered; and 4) increased durability of the resulting plastic laminate components.

[0036] It should be understood that the film sheet can be positioned in the injection mold either by way of a pre-form, as described above, or by way of a film roll supply. In this way, one can mold in the color at the press or mold thereby avoiding a secondary painting operation.

[0037] While the best mode for carrying out the invention has been described in detail, those familiar with the art to which this invention relates will recognize various alternative designs and embodiments for practicing the invention as defined by the following claims. 1 APPENDIX A TO CONFIRMATORY ASSIGNMENT U.S. Pat. No. Issued Attorney Docker No. 5,276,957 01-11-94 VEI0101PUS 5,062,661 11-05-91 VEI0102PUS 5,487,557 01-30-96 VEI0112PUS 5,497,709 03-12-96 VEI0116PUS 5,486,658 01-23-96 VEI0118PUS 5,639,112 06-17-97 VEI0124PUS 5,552,992 09-03-96 VEI0126PUS 5,549,323 08-27-96 VEI0144PUS 5,558,364 09-24-96 VEI0145PUS 5,678,849 10-21-97 VEI0146PUS 5,590,902 01-07-97 VEI0147PUS 5,520,412 05-28-96 VEI0152PUS 5,542,694 08-06-96 VEI0153PUS 5,642,901 07-01-97 VEI0157PUS 5,685,561 11-11-97 VEI0168PUS 5,529,336 06-25-96 VEI0169PUS 5,765,864 06-16-98 VEI0173PUS 5,776,522 07-07-98 VEI0175PUS 5,744,210 04-28-98 VEI0176PUS 5,683,101 11-04-97 VEI0178PUS 6,073,056 06-06-00 VEI0192PUS 5,922,368 07-13-99 VEI0205PUS 6,053,720 04-25-00 VEI0222PUS 5,927,286 07-27-99 VEI0224PUS 5,868,988 02-09-99 VEI0225PUS 5,979,933 11-09-99 VEI0227PUS 6,042,355 03-28-00 VEI0231PUS 6,062,842 05-16-00 VEI0232PUS 6,042,140 03-28-00 VEI0233PUS 5,869,105 02-09-99 VEI0234PUS 6,042,356 03-28-00 VEI0235PUS 6,042,361 03-28-00 VEI0236PUS 6,017,481 01-25-00 VEI0237PUS 6,047,984 04-11-00 VEI0239PUS 6,082,762 07-04-00 VEI0249PUS 6,079,734 06-27-00 VEI0255PUS 6,053,526 04-25-00 VEI0259PUS 6,050,594 04-18-00 VEI0260PUS

[0038] 2 APPENDIX B TO CONFIRMATORY ASSIGNMENT U.S. Ser. No. Filed Attorney Docket No. 09/305,531 05-05-99 VEI0206PUS 09/460,826 12-14-99 VEI0213PUS 08/908,773 08-08-97 VEI0219PUS 09/075,497 05-08-98 VEI0221PUS 09/040,841 03-18-98 VEI0229PUS 09/114,393 07-13-98 VEI023OPUS 09/112,965 07-09-98 VEI0238PUS 09/083,943 05-22-98 VEI0240PUS 09/098,212 06-16-98 VEI0242PUS 09/527,755 03-17-00 VEI0245PUS 09/141,884 08-28-98 VEI0248PUS 09/144,315 08-31-98 VEI0253PUS 09/148,262 09-04-98 VEI0254PUS 09/248,128 02-10-99 VEI0256PUS 09/213,072 12-16-98 VEI0258PUS 09/228,585 01-11-99 VEI0262PUS 09/482,747 01-13-00 VEI0265PUS 09/483,140 01-13-00 VEI0266PUS 09/493,778 01-28-00 VEI027OPUS 09/305,515 05-05-99 VEI0272PUS 09/525,352 03-15-00 VEI0275PUS 09/392,878 09-09-99 VEI0277PUS 09/469,198 12-21-99 VEI0279PUS 09/489,535 01-21-00 VEI0288PUS 09/489,434 01-21-00 VEI0299PUS 09/451,970 11-30-99 VEI0303PUS 09/528,761 03-17-00 VEI0313PUS 09/578,024 05-24-00 VEI0315PUS 09/461,154 12-14-99 VEI0317PUS 09/445,356 12-10-99 VEI0318PUSA 09/464,153 12-16-99 VEI0322PUS 09/468,969 12-22-99 VEI0323PUS 09/482,384 01-12-00 VEI0327PUS 09/485,142 02-04-00 VEI0329PUSA 09/566,938 05-08-00 VEI0335PUS

Claims

1. A method of manufacturing a molded plastic component, comprising:

providing a film sheet having top and bottom surfaces, the film sheet being selected from the group consisting of polyester, polyurethane and polycarbonate;

vacuum molding-the film sheet in a mold cavity to obtain a pre-form;

placing the pre-form in a mold cavity of an injection mold having a shape defining the desired plastic component; and

injecting a thermoplastic elastomer into the mold cavity of the injection mold to generate a structural carrier for the pre-form, the generation of the structural carrier creating sufficient pressure and heat to bond the structural carrier to the bottom surface of the pre-form to form the molded laminate plastic component.

2. The method of claim 1, wherein the thermoplastic elastomer is selected from the group consisting of a thermoplastic polyolefin, thermoplastic urethane, polyester, polycarbonate, acrylonitrile/butadiene/styrene, polypropylene, lomod, bexloy, a mixture of acrylonitrile/butadiene/styrene and polycarbonate, and mixtures thereof.

3. The method of claim 1, wherein the step of injecting a thermoplastic elastomer into the mold cavity occurs in a temperature of 420° F. and at a pressure of 50 psi to 15,000 psi.

4. The method of claim 1, further comprising the step of cutting the pre-form prior to the step of placing.

5. The method of claim 1, wherein the structural carrier has a flexural modulus in the range of 15,000 to 400,000.

6. The method of claim 1, wherein the structural carrier has a durometer in the range of 15 Shore D to 100 Shore D.

7. The method of claim 1, wherein the film sheet is coated with a layer of acrylic color and polyvinylidine fluoride and an acrylic clear coat layer.

8. The method of claim 7, wherein the polyvinylidine fluoride comprises more than 50% of the total thickness of the film sheet.

9. The method of claim 1, wherein the film sheet has a total thickness of 0.2 mils.

10. A method of manufacturing a molded laminate automotive component, comprising:

inserting a film sheet into a vacuum forming station to form the film sheet into a predetermined automotive component shape to create a formed film sheet having top and bottom surfaces, the film sheet being selected from the group consisting of polyester, polyurethane and polycarbonate;

placing the formed film sheet in a mold cavity of an injection mold having a shape defining the automotive component;

injecting a thermoplastic elastomer into the mold cavity of the injection mold, such that the thermoplastic elastomer is in mating contact with the bottom surface of the formed film sheet, to generate a structural carrier for the formed film sheet, the generation of the structural carrier creating sufficient pressure and heat to bond the structural carrier to the bottom surface of the formed film sheet to form the molded laminate automotive component.