Therapeutic compositions and methods

Abstract

Methods of promoting healing through enhanced regeneration of tissue (e.g. hard tissue or soft tissue) by contacting the tissue or the surrounding tissue with an anti-inflammatory agent. These methods are useful in a variety of dental and orthopedic applications.

Description

RELATED APPLICATIONS

[0001] This application claims priority to U.S. Provisional Application No. 60/XXXXX, which was filed on Dec. 7, 1999 as U.S. patent application Ser. No. 09/455,861, for which a petition under 37 C.F.R §1.53(c) to convert the non-provisional application to a provisional application was filed on Dec. 6, 2000.

FIELD OF THE INVENTION

[0002] The present invention relates to the use of anti-inflammatory agents to enhance the regeneration and healing of tissue (e.g. hard tissue and soft tissue).

BACKGROUND OF THE INVENTION

[0003] Polymers comprising aromatic or aliphatic anhydrides have been studied extensively over the years for a variety of uses. For example, in the 1930s fibers comprising aliphatic polyanhydrides were prepared for use in the textile industry. In the mid 1950s, aromatic polyanhydrides were prepared with improved film and fiber forming properties. More recently, attempts have been made to synthesize polyanhydrides with greater thermal and hydrolytic stability and sustained drug release properties.

[0004] U.S. Pat. Nos. 4,757,128 and 4,997,904 disclose the preparation of polyanhydrides with improved sustained drug release properties from pure, isolated prepolymers of diacids and acetic acid. However, these biocompatible and biodegradable aromatic polyanhydrides have aliphatic bonds resulting in compounds with slow degradation times as well as relatively insoluble degradation products unless incorporated into a copolymer containing a more hydrophilic monomer, such as sebacic acid. The aromatic polyanhydrides disclosed in the '128 Patent and the '904 Patent are also insoluble in most organic solvents. A bioerodible controlled release device produced as a homogenous polymeric matrix from polyanhydrides with aliphatic bonds having weight average molecular weights greater than 20,000 and an intrinsic velocity greater than 0.3 dL/g and a biologically active substance is also described in U.S. Pat. No. 4,888,176. Another bioerodible matrix material for controlled delivery of bioactive compounds comprising polyanhydride polymers with a uniform distribution of aliphatic and aromatic residues is disclosed in U.S. Pat. No. 4,857,311.

[0005] Biocompatible and biodegradable aromatic polyanhydrides prepared from para-substituted bis-aromatic dicarboxylic acids for use on wound closure devices are disclosed in U.S. Pat. No. 5,264,540. However, these compounds exhibit high melt and glass transition temperatures and decreased solubility, thus making them difficult to process. The disclosed polyanhydrides also comprise radical or aliphatic bonds which cannot be hydrolyzed by water.

[0006] Polyanhydride polymeric matrices have also been described for use in orthopedic and dental applications. For example, U.S. Pat. No. 4,886,870 discloses a bioerodible article useful for prosthesis and implantation which comprises a biocompatible, hydrophobic polyanhydride matrix. U.S. Pat. No. 5,902,599 also discloses biodegradable polymer networks for use in a variety of dental and orthopedic applications which are formed by polymerizing anhydride prepolymers.

[0007] Biocompatible and biodegradable aromatic polyanhydrides have now been developed with improved degradation, processing and solubility properties, as well as therapeutic utilities. As demonstrated herein, the new aromatic polyanhydrides are particularly useful in enhancing regeneration and healing of tissue. Thus, these new polyanhydrides can be used in a variety of dental and orthopedic applications.

SUMMARY OF THE INVENTION

[0008] It has unexpectedly been discovered that the local administration of an anti-inflammatory agent to tissue provides beneficial effects on the healing and growth of the tissue and on proximally located tissues.

[0009] Accordingly, the invention provides a method to promote healing of tissue comprising administering an effective amount of an anti-inflammatory agent to or near the tissue.

[0010] The invention provides a method to promote healing of hard tissue comprising administering an effective amount of an anti-inflammatory agent to the hard tissue or to soft tissue near the hard tissue.

[0011] The invention also provides a method of treating periodontal disease comprising administering an effective amount of an anti-inflammatory agent at the site of the periodontal disease.

[0012] The invention also provides a method of treating a bone fracture comprising fixing the fracture with an orthopedic device comprising an anti-inflammatory agent.

[0013] The invention also provides a method to enhance regeneration of tissue comprising administering an effective amount of an anti-inflammatory agent to or near the tissue.

[0014] The invention also provides a method to enhance regeneration of bard tissue comprising administering an effective amount of an anti-inflammatory agent to the hard tissue or to soft tissue near the hard tissue.

[0015] The invention also provides a method to decrease bone resorption at a site in the body of a patient comprising administering an effective amount of an anti-inflammatory agent at or near the site.

[0016] The invention also provides a method to promote healing of bone comprising contacting the bone and surrounding soft tissue with an aromatic polyanhydride comprising a repeating unit having the structure: 1

[0017] wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates so that regeneration of bone is enhanced.

[0018] The invention also provides a method of treating periodontal diseases in a patient comprising administering to the patient at the site of the periodontal disease an aromatic polyanhydride comprising a repeating unit having the structure: 2

[0019] wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

[0020] The invention also provides a method of treating bone fractures in a patient comprising fixing the bone fracture with an orthopedic device comprised of or coated with an aromatic polyanhydride comprising a repeating unit having the structure: 3

[0021] wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

[0022] The invention also provides pharmaceutical compositions comprising an anti-inflammatory agent and a pharmaceutically acceptable carrier, which are formulated to provide controlled release of the agent at or near tissue (e.g. hard or soft tissue). Preferably, the compositions are formulated to provide local release of an effective amount of the agent over a period of at least about 2, about 5, about 10, about 20, or about 40 days. The compositions can also preferably be formulated to provide local release of an effective amount of the agent over a period of up to about 3 months, about 6 months, about 1 year, or about 2 years.

[0023] The invention also provides the use of an anti-inflammatory agent to prepare a medicament useful for promoting the healing of tissue by administration to or near the tissue.

[0024] The invention also provides the use of an anti-inflammatory agent to prepare a medicament useful for decreasing bone resorption at a site in the body of a mammal by administration at or near the site.

[0025] The invention also, provides the use of an anti-inflammatory agent to prepare a medicament useful to enhance regeneration of tissue by administration to or near the tissue.

[0026] The preparation of aromatic polyanhydrides from ortho-substituted bis-aromatic carboxylic acid anhydrides disrupts the crystallinity of the resulting polymer, enhancing solubility and processability, as well as degradation properties: The use of hydrolyzable bonds such as esters, amides, urethanes, carbamates and carbonates as opposed to aliphatic bonds in these compounds further enhances these properties.

[0027] These aromatic polyanhydrides have a repeating unit within the structure of Formula I: 4

[0028] wherein Ar is a substituted or unsubstituted aromatic ring and R is a difunctional organic moiety substituted on each Ar ortho to the anhydride group. Ar and R are preferably selected so that the hydrolysis products of the polyanhydrides have a the chemical structure of an anti-inflammatory agent, particularly salicylates such as aspirin, non-steroidal anti-inflammatory compounds, or other aromatic anti-inflammatory compounds. Ar is preferably a phenyl group and R is preferably —Z1—R1—Z1— in which R1, is a difunctional moiety and both Z1s are independently either an ester —C(═O)O—, amide —C(═O)N—, anhydride —C(═O)—O—C(═O)—, carbonate —O—C(═O)—O—, urethane —N—C(═O)—N—, or sulfide —S— groups. R1 is preferably an alkylene group containing from 1 to 20 carbon atoms, or a group with 2-20 carbon atoms having a structure selected from (—CH2—CH2—O—)m, —(CH2—CH2—CH2—O—)m and (—CH2—CHCH3—O—)m.

[0029] Ortho-substituted bis-aromatic carboxylic acid anhydrides of the present invention are used in the preparation of the aromatic polyanhydrides of the present invention. The ortho-substituted bis-aromatic carboxylic acid anhydrides have the structure of Formula II: 5

[0030] wherein Ar and R, and the preferred species thereof, are the same as described above with respect to Formula I and R is substituted on each Ar ortho to the anhydride group.

[0031] The aromatic polyanhydrides of the present invention meet the need for moldable biocompatible biodegradable polymers and are particularly useful in enhancing the healing process of bone and surrounding soft tissue.

[0032] Accordingly, the present invention relates to compositions and methods of using compositions comprising a aromatic polyanhydride with a repeating unit of Formula I to enhance healing of tissue (e.g. hard tissue); It has been found that these compositions promote healing in hard tissue by inhibiting inflammation and/or pain in the surrounding soft tissues and by enhancing hard tissue regeneration by promoting growth and/or by reducing bone resorption. To use these compositions to enhance tissue regeneration, it is preferred that the compositions be incorporated into fibers, films, membranes, pastes or microspheres. For this use, it is also preferred that the compositions comprise poly(anhydride-esters), referred to herein as bioactive polyanhydrides that degrade into salicylic acid, an anti-inflammatory, antipyretic and analgesic agent. The hard tissue and surrounding soft tissue are directly contacted with the composition so that regeneration and healing is enhanced.

[0033] A more complete appreciation of the invention and other intended advantages can be readily obtained by reference to the following detailed description of the preferred embodiments and claims, which disclose the principles of the invention and the best modes which are presently contemplated for carrying them out.

BRIEF DESCRIPTION OF THE FIGURES

[0034] FIG. 1 illustrates a perspective view of a bioactive implant as constructed in accordance with one embodiment

DETAILED DESCRIPTION OF THE INVENTION

[0035] Applicant has discovered that the local administration of an anti-inflammatory agent on or near hard tissue, such as bone or tooth, enhances the growth and regeneration of the hard tissue and the surrounding soft tissue. Preferably, the anti-inflammatory agent is administered in a form that provides a controlled release of the agent at or near the hard tissue over a period of days or months.

[0036] Numerous controlled release mechanisms are known in the art (for example see R. Langer, 1990, ScienceI, 249, 1527-1533. Any controlled release mechanism can be used in conjunction with the methods of the invention, provided it allows for the controlled release of the anti-inflammatory agent at or near the site of the tissue. One preferred method for providing the controlled release of an anti-inflammatory agent is to incorporate the agent into a polymer (e.g. a bio-degradable polymer). The agent can be dispersed through the polymer matrix, can be appended to the backbone of the polymer, or can be incorporated directly into a biodegradable polymer backbone. Typically, any anti-inflammatory agent can be dispersed through a polymer matrix to provide a suitable controlled release formulation. However, the ability of an agent to be appended to or incorporated into a polymer may depend on the functional groups present in the agent. Preferred anti-inflammatory agents that can be appended to or incorporated into a polymer to provide a suitable controlled release formulation are described in greater detail below.

[0037] Anti-inflammatory Agent

[0038] Anti-Inflammatory agents are a well known class of pharmaceutical agents which reduce inflammation by acting on body mechanisms (Stedman's Medical Dictionary 26 ed., Williams and Wilkins, (1995); Physicians Desk Reference 51 ed., Medical Economics, (1997)).

[0039] Anti-inflammatory agents useful in the methods of the invention include Non-steroidal Anti-Inflammatory Agents (NSAIDS). NSAIDS typically inhibit the body's ability to synthesize prostaglandins. Prostaglandins are a family of hormone-like chemicals, some of which are made in response to cell injury. Specific NSAIDS approved for administration to humans include naproxen sodium, diclofenac, sulindac, oxaprozin, diflunisal, aspirin, piroxicam, indomethocin, etodolac, ibuprofen, fenoprofen, ketoprofen, mefenamic acid, nabumetone, tolmetin sodium, and ketorolac trometharmine.

[0040] Other anti-inflammatory agents useful in the methods of the invention include salicylates, such as, for example, salicilic acid, acetyl salicylic acid, choline salicylate, magnesium salicylate, sodium salicylate, olsalazine, and salsa late.

[0041] Other anti-inflammatory agents useful in the methods of the invention include cyclooxygenase (COX) inhibitors. COX catalyzes the conversion of arachidonate to prostaglandin H2 (PGH2); a COX inhibitor inhibits this reaction. COX is also known as prostaglandin H synthase, or PGH synthase. Two Cox genes, Cox-1 and Cox-2 have been isolated in several species. COX-2 is tightly regulated in most tissues and usually only induced in abnormal conditions, such as inflammation, rheumatic and osteo-atrhitis, kidney disease and osteoporosis COX-1 is believed to be constitutively expressed so as to maintain platelet and kidney function and integral homeostasis. Typical COX inhibitors useful in the methods of the invention include etodolac, celebrex, meloxicam, piroxicam, nimesulide, nabumetone, and rofecoxib.

[0042] Preferred anti-inflammatory agents that can be incorporated into a polymer matrix for administration in the methods of the invention include: Isonixin, Amtolmetin Guacil, Proglumetacin, Piketoprofen, Difenamizole, Epirizole, Apazone, Feprazone, Morazone, Phenylbutazone, Pipebuzone, Propyphenazone, Ramifenazone, Thiazolinobutazone, Aspirin, Benorylate, Calcium Acetylsalicylate, Etersalate, Imidazole Salicylate, Lysine Acetylsalicylate, Morpholine Salicylate, 1-Naphthyl Salicylate, Phenyl Acetylsalicylate, Ampiroxicam, Droxicam, S-Adenosylmethionine, Amixetrine, Benzydamine, Bucolome, Difenpiramide, Emorfazone, Guaiazulene, Nabumetone, Nimesulide, Proquazone, Superoxide Dismutase, and Tenidap.

[0043] Preferred anti-inflammatory agents that can be appended to a polymer for administration in the methods of the invention include: Etofenamate, Talniflumate Terofenamate, Acemetacin, Alclofenac, Bufexamac, Cinmetacin, Clopirac, Felbinac, Fenclozic Acid, Fentiazac, Ibufenac, Indomethacin, Isofezolac, Isoxepac, Lonazolac, Metiazinic Acid, Mofezolac, Oxametacine, Pirazolac, Sulindac, Tiaramide, Tolmetin, Tropesin, Zomepirac, Bumadizon, Butibufen, Fenbufen, Xenbucin, Clidanac, Ketorolac, Tinoridine, Benoxaprofen, Bermoprofen, Bucloxic Acid, Fenoprofen, Flunoxaprofen, Flurbiprofen, Ibuprofen, Ibuproxam, Indoprofen, Ketoprofen, Loxoprofen, Naproxen, Oxaprozin, Pirprofen, Pranoprofen, Protizinic Acid, Suprofen, Tiaprofenic Acid, Zaltoprofen, Benzpiperylon, Mofebutazone, Oxyphenbutazone, Suxibuzone, Acetaminosalol, Parsalmide, Phenyl Salicylate, Salacetamide, Salicylsulfuric Acid, Isoxicam, Lomoxicam, Piroxicam, Tenoxicam, &egr;-Acetamidocaproic Acid, Bendazac, &agr;-Bisabolol, Paranyline, Perisoxal, and Zileuton.

[0044] Preferred anti-inflammatory agents that can be incorporated into a polymer backbone for administration in the methods of the invention include: Enfenamic Acid, Aceclofenac, Glucametacin, Alminoprofen, Carprofen, Ximoprofen, Salsalate, 3-Amino-4-hydroxybutyric Acid, Ditazol, Fepradinol, and Oxaceprol.

[0045] Preferred anti-inflammatory agents that posses suitable ortho functionality to be incorporated into the backbone of a polymer of formula (I) as described herein include: Flufenamic Acid, Meclofenamic Acid, Mefenamic Acid, Niflumic Acid, Tolfenamic Acid, Amfenac, Bromfenac, Diclofenac Sodium, Etodolac, Bromosaligenin, Diflunisal, Fendosal, Gentisic Acid, Glycol Salicylate, Salicilic Acid, Mesalamine, Olsalazine, Salicylamide O-Acetic Acid, Sulfasalazine,

[0046] For any anti-inflammatory agent referred to herein by a trade name it is to be understood that either the trade name product or the active ingredient possessing anti-inflammatory activity from the product can be used. Additionally, preferred agents identified herein for incorporation into a polymer backbone can also preferably be appended to a polymer or can be incorporated into a polymer matrix. Preferred agents that can be appended to a polymer can also preferably be incorporated into a polymer matrix.

[0047] Definitions

[0048] As used herein the term “hard tissue” includes tissue that has become mineralized, such as, for example, bone, cartilage, and tooth.

[0049] As used herein, administering an agent “to or near the tissue” means administering the agent so that it is in direct contact with the tissue or administering the agent to a location proximal to tissue, so that the agent can produce the desired or stated therapeutic effect.

[0050] As used herein, “administering an anti-inflammatory agent to hard tissue” means applying the agent so that it is in direct contact with the hard tissue.

[0051] As used herein, “administering an anti-inflammatory agent to the soft tissue near hard tissue” means applying the agent to the soft tissue proximal to the hard tissue, so that the agent can produce the desired or stated therapeutic effect.

[0052] As used herein the term, “formulated for controlled release” means that the agent is formulated such that it will be released over an extended period of time when administered according to the methods of the invention. For example, the agent can conveniently be formulated so that it will be released over a period of at least about 2, about 5, about 10, about 20, or about 40 days. Preferably, the agent is formulated so that it is released over at least about 5 or about 10 days. The agent can also preferably be formulated so that it is released over a period of about 30 to about 90 days. For the treatment of hard tissue, the agent is preferably formulated so that it is released over a period of about 30 to about 90 days. For the treatment of soft tissue, the agent is preferably formulated so that it is released over a period of about 1 to about 30 days, more preferably about 2 to about 25 days.

[0053] As used herein, an agent is “appended” to a polymer when the agent is bonded to the polymer as a side chain or side group, but is not part of the polymer backbone. Preferably, the agent is bonded to the polymer through a linkage that is suitable to release the agent when the polymer is administered according to the methods of the invention. For example, the agent can conveniently be linked to a polymer through a hydrolyzable linkage such as an anhydride or ester linkage.

[0054] As used herein, the tern “dispersed through the polymer matrix” means that an anti-inflammatory agent is located within the matrix of a polymer such that it can be released in a controlled fashion within the body. Preferably, the polymer matrix comprises a biodegradable polymer.

[0055] As used herein, the term “at the site of the periodontal disease” means at a site that is at or proximal to the site of the periodontal disease, such that when an agent is administered to the site, the agent can produce a beneficial effect and ameliorate one or more symptoms of the periodontal disease.

[0056] As used herein, the term “gingival cleft” means the space between the soft tissue of the gum and the tooth.

[0057] As used herein, the term “fixing the fracture” means to hold the fractured pieces together or to stabilize the fracture.

[0058] As used herein, the term “enhance regeneration of hard tissue” means to allow or to facilitate the growth of the hard tissue in a normal manner.

[0059] As used herein, “administering an anti-inflamnatory agent at the site” means applying the agent so that it is in direct contact with the site.

[0060] As used herein, “administering an anti-inflammatory agent near the site” means applying the agent proximal to the site, so that the agent can produce the desired or stated therapeutic effect (e.g. reduce bone resorption at the site).

[0061] As used herein, the term “periodontal disease” includes any abnormality, either inflammatory or degenerative, of the tissue around the tooth.

[0062] As used herein, the term “healing” means the restoration to normal health.

[0063] Aromatic polyanhydrides with improved degradation properties and processability have now been developed These compounds have repeating units with the structure of Formula I: 6

[0064] wherein Ar is a substituted or unsubstituted aromatic ring and R is a difunctional organic moiety substituted on each Ar ortho to the anhydride group. Ar and R are preferably selected so that the hydrolysis products of the polyanhydrides have a chemical structure resembling pharmaceutically-active materials, particularly salicylates such as aspirin, non-steroidal anti-inflammatory naphthyl or phenyl propionates such as ibuprofen, ketoprofen, naproxen, and the like, or other aromatic anti-inflammatory compounds such as indomethacin, indoprofen, and the like. In particular, Ar is preferably a phenyl group and R is preferably —Z1—R1—Z1— in which R1, is a difunctional moiety and both Z1s are independently either an ester, amide, anhydride, carbonate, urethane or sulfide groups. R1 is preferably an alkylene group containing from 1 to 20 carbon atoms, or a group with 2-20 carbon atoms having a structure selected from (—CH2—CH2—O—)m, (CH2—CH2—CH2—O—)m and (—CH2—CHCH3—O—)m or R1 may have the structure —R2—Z2—R3—1 wherein R2 and R3 are independently alkylene groups containing from 1 to 19 carbon atoms or groups having from 2 to 18 carbon atoms having a structure selected from (—CH2—CH2—O—)m, (—CH2—CH2—CH2—O—)m, and (—CH2—CHCH3—O—)m, and Z2 is selected from the difunctional moieties described above with respect to Z1.

[0065] Ar may be an alkylaryl group, in which a difunctional organic moiety is positioned between each anhydride carbonyl group and the corresponding aromatic ring. Preferably, however, each carbonyl group is directly substituted on the corresponding aromatic ring.

[0066] Preferred polymers of the present invention have repeating units with the structure of Formula I in which Ar is a phenyl ring and R is selected from —Z1—(—CH2—)mZ1—, —Z1(—CH2—CH2—O—)m, —Z1—, —Z1(—CH2—CH2—CH2—O—)m—Z1—, and —Z1(—CH2—CHCH3—O—)m—Z1—, wherein Z1 is an ester or amide group and n is from 1 to 20 inclusive, and preferably is 6, and m is selected so that R has from 2 to 20, and preferably 6, carbon atoms.

[0067] A preferred polymer useful in the methods of the invention is a polymer of Formula I: 7

[0068] wherein Ar is a substituted or unsubstituted aromatic ring and R is a difunctional organic moiety. R is preferably —Z1—R1—Z1— in which R1, is a difunctional moiety and each Z1 is independently an ester —C(═O)O—, amide —C(═O)N—, anhydride—C(═O)—O—C(═O)—, carbonate —O—(═O)—O—, urethane —N—C(═O)—N—, or thioester —C(═O)S—. R1 is preferably an alkylene group containing from 1 to 20 carbon atoms.

[0069] The aromatic polyanhydrides of the present invention may be prepared by the method described in Conix, Macromol. Synth., 2, 95-99 (1996), in which dicarboxylic acids are acetylated in an excess of acetic anhydride followed by melt condensation of the resulting carboxylic acid anhydride at 180° C. for 2-3 hours. The resulting polymers are isolated by precipitation into diethyl ether from methylene chloride. The described process is essentially the conventional method for polymerizing bis-aromatic dicarboxylic acid anhydrides into aromatic polyanhydrides.

[0070] Aromatic polyanhydrides in accordance with the present invention have average molecular weights of about 1500 daltons, up to about 50,000 daltons, calculated by Gel Permeation Chromatography (GPC) relative to narrow molecular weight polystyrene standards. Preferred aromatic polyanhydrides have average molecular weights of about 1500 daltons, up to about 35,000 daltons.

[0071] The aromatic polyanhydrides of the present invention are produced from ortho-substituted bis-aromatic carboxylic acid anhydrides having the structure of Formula II: 8

[0072] in which Ar, R and the preferred species thereof are the same as described above with respect to Formula I. As noted above, ortho-substituted bis-aromatic carboxylic acid anhydrides are prepared by acetylation of the corresponding ortho-substituted bis-aromatic carboxylic acids in an excess of acetic anhydride. The dicarboxylic acids have the structure of Formula III 9

[0073] wherein Ar, R and the preferred species thereof are the same as described above with respect to Formula I.

[0074] The dicarboxylic acids are prepared by reacting a stoichiometric ratio of aromatic carboxylic acid having the structure Z3—Ar—COOH and a compound having a structure Z4—R—Z4 wherein Ar is a substituted or unsubstituted aromatic ring on which Z3 is substituted ortho to the carboxylic acid group, R is a difunctional organic moiety and Z3 and Z4 are functional groups selected to provide the linkage desired between the difunctional organic moiety and the two aromatic rings.

[0075] Suitable Z3 and Z4 functional groups, and the manner in which they may be reacted to produce the bis-aromatic dicarboxylic acids of the present invention, may be readily determined by those of ordinary skill in the art without undue experimentation. For example, for aromatic polyanhydrides having the structure of Formula I in which Ar is a phenyl group and R is —O—(CH2—)6—O—, the ortho-substituted bis-aromatic dicarboxylic acid starting material may be prepared by reacting o-salicylic acid with 1,6dibromohexane. For aromatic polyanhydrides having the structure of Formula I in which Ar is a phenyl group and R is —O—C(═O)—(CH2—)6—C(═O)—O—, the ortho-substituted bis-aromatic dicarboxylic acid starting material may be prepared by reacting o-salicylic acid with 1,6dioctanoic acid.

[0076] The aromatic polyanhydrides used in the present invention can be isolated by known methods commonly employed in the field of synthetic polymers to produce a variety of useful articles with valuable physical and chemical properties. The new polymers can be readily processed into pastes, and gels or solvent cast to yield films, membranes, coatings, microspheres, chips and fibers with different geometric shapes for design of various medical implants, and may also be processed by compression molding and extrusion. Medical implant applications include the use of aromatic polyanhydrides to form shaped articles such as vascular grafts and stents, bone plates, sutures, implantable sensors, implantable drug delivery devices, stents for tissue regeneration, scaffolding for supporting new cell growth and other articles that decompose harmlessly within a known time period. For the present invention, it is preferred that the polyanhydride be incorporated into films, membranes, pastes, gels, microspheres, chips or fibers useful in dental and orthopedic applications.

[0077] It has now been demonstrated that the polymers comprising these aromatic polyanhydrides having a repeating unit with the structure of Formula I in which Ar and R are selected to provide aromatic polyanhydrides that hydrolyze to form therapeutically useful salicylates are particularly useful in enhancing regeneration of tissue. Examples of the therapeutically useful salicylates include, but are not limited to, thymotic acid, 4,4sulfinyldinailine, 4-sulfanilamidosalicylic acid, sulfanilic acid, sulfanilylbenzylamine, sulfaloxic acid, succisulfone, salicylsulfuric acid, salsallate, salicylic alcohol, salicilic acid, orthocaine, mesalamine, gentisic acid, enfenamic acid, cresotic acid, aminosalicylic acid, aminophenylacetic acid, acetylsalicylic acid, and the like. The identification of Ar and R moieties that provide aromatic polyanhydrides that hydrolyze to form such therapeutically useful salicylates can be readily determined by those of ordinary skill in the art without undue experimentation.

[0078] A preferred salicylate for incorporation into the polymers of formula (I) is salicylic acid, thymotic acid, 4-sulfanilamidosalicylic acid, mesalamine, gentisic acid, enfenamic acid, cresotic acid, or aminosalicylic acid.

[0079] The quantity of aromatic polyanhydride that hydrolyzes to form an amount of therapeutic salicylate effective to relieve inflammation and promote healing of bone can be readily determined by those of ordinary skill in the art without undue experimentation. The quantity essentially corresponds stoichiometrically to the amount of salicylate known to produce an effective treatment. Oral dosage forms of aromatic polyanhydrides that hydrolyze to form other therapeutic non-steroidal anti-inflammatory compounds and other therapeutic compounds are prepared and administered in a similar manner.

[0080] Most degradable or absorbable devices for dental or orthopedic applications cause local inflammation. In the present invention, however, use of compositions such as films, membranes, fibers, pastes, gels and microspheres comprising an aromatic polyanhydride that hydrolyzes to form a therapeutically useful salicylate in dental and orthopedic applications actually decreases local inflammation and/or pain. These compositions can also be incorporated into matrices to provide preformed or adaptable scaffolding for cell ingrowth. Further, it has been found that use of these compositions promotes the healing process of the tissue (e.g. bone) through enhanced regeneration of these tissues. Selection of the form of the composition to be used is performed routinely by those of skill in the art based upon the type of injury and the tissue healing to be promoted.

[0081] Compositions comprising an aromatic polyanhydride can be used to coat orthopedic devices for fixation of bone fractures such as pins or screws, thereby decreasing the local inflammation and bone resorption associated with these devices. Films comprising an aromatic polyanhydride are also believed to be useful as orthopedic devices to enhance the healing process of bone fractures.

[0082] Fibers useful as suture materials can also be comprised of the aromatic polyanhydride. For example, polymer fibers are used frequently in oral surgery to suture cleft palates. Use of an aromatic polyanhydride which degrades to a therapeutic salicylate would enhance the regeneration of the tissue via the sutures while decreasing the pain and inflammation associated with the surgery via the degradation products.

[0083] Films, membranes, pastes, gels, chips and microspheres comprising the aromatic polyanhydrides can also be used to decrease dental pain and promote healing within a tooth, in the pulp chamber and root canal.

[0084] Films or membranes comprising the aromatic polyanhydrides can also be used in guided bone or tissue regeneration. Following surgery, especially oral or dental surgery, proper healing of the wound requires both bone and soft tissue regeneration. It is well known, however, that bone heals more slowly than the surrounding tissues such as the gums. In fact, oftentimes ingrowth of other tissues into an area prevents the required regeneration of the bone. For example, removal of a substantial portion of the tooth root due to resorption or disease leaves a cavity which is oftentimes quickly filled by connective tissue. This ingrowth of connective tissue effectively prevents bone regeneration.

[0085] Accordingly, a procedure referred to as guided bone or tissue regeneration has been developed to overcome this difficulty. In this method, a membrane is surgically inserted around the periphery of the wound cavity. The membrane prevents or inhibits the invasion of the wound cavity by unwanted cells types and allows the preferred cells to grow into the cavity, thereby healing the wound. This procedure is also used to regenerate bone around teeth and on edentulous jaw ridges in association with implant reconstruction.

[0086] Two membranes commonly used in guided tissue regeneration include a synthetic, non-resorbable polytetrafluoroethylene membrane such as GORETEX and synthetic membranes formed from glycolide and lactide copolymers. U.S. Pat. No. 5,837,278 also describes a resorbable collagen membrane for use in guided tissue regeneration. It is believed that films comprising aromatic polyanhydrides would also be useful in this procedure.

[0087] Compositions comprising an aromatic polyanhydride that hydrolyzes to form a therapeutically useful salicylate are believed to be particularly useful in treatment of periodontal diseases. Periodontal diseases, including a group of related microbial-induced chronic inflammatory disorders and a disorder referred to periodontal dehiscence, destroy the tissue supporting the teeth. These diseases can result in loss of normal soft and hard tissue architectures at sites adjacent to the affected teeth. Incorporation of these compositions into films, membranes, pastes, fibers or microspheres for use in treatment of periodontal disease is expected to accelerate the recovery/restoration of new healthy periodontal architecture while reducing post-operative pain after periodontal surgery. Further, the lower pH environment which results from degradation into salicylates is unfavorable to growth of someperiodontic bacteria. Thus, use of these compositions is also expected to decrease infections in periodontal procedures.

[0088] In vivo studies were conducted to compare the affects of a polymer system of the present invention (referred to herein as the bioactive polymer or implant) and a chemically similar polyanhydride system (referred to herein as the control polyanhydride) on the healing process. The sole chemical difference between these two systems is the replacement of the ether bond in the polyanhydride of the bioactive polymer with an ester bond thereby resulting in degradation to salicylic acid as compared to a non-active component in the control polyanhydride. In these experiments, the polymers were compression-molded into films with thicknesses of 0.1, 0.2 and 0.3 mm and cut into 0.5 mm wide strips.

[0089] In these experiments, mice (n=10) were anesthetized and the palatal gingival mucosa adjacent to the maxillary first molar was reflected to expose the palatal and alveolar bone. A polymer film was then placed on the bone adjacent to the tooth. The tissue was repositioned and the procedure was repeated on the contra lateral side. Polymer films were randomly placed (left vs. right) with each mouse carrying both polymers. Mice were fed a ground diet and water ad libitum and weighed weekly. Mice were sacrificed at 1, 4 and 20 days post surgical insertion.

[0090] Visual intraoral examination of the mucosa covering the implantation sites was performed with a dissecting microscope under optimum lighting. Magnification was varied from 5 to 40 times normal size. Photographs were taken to record the morphological changes observed.

[0091] Polymer membranes of thicknesses 0.1 and 0.2 mm were not visible under the microscope at 4 and 20 days post insertion. However, thicker membranes (0.3 mm) were still observable after 20 days. For the control polyanhydride films, the mucosa was red and thin near the implant with the surrounding tissue inflamed at days 1 and 4. By day 14, the tissue was slightly puffy in three animals while the tissue was within normal limits for the remaining 5 animals. In contrast, the tissue surrounding the bioactive polymer implants was slight puffy after day 1 but within normal limits in all animals by day 4. Further, considerable swelling was observed on the side bearing the control polyanhydride, whereas the side with the bioactive polymer showed a progressively normal mucosa. The tissue surrounding the control polyanhydride was very swollen and white, whereas the tissue adjacent to the bioactive implant was less swollen and normal in color. The three maxillary molar palatal ridges (anterior, middle and posterior) were clearly visible. However, the anterior and middle ridges coalesced because of the swelling and blanching on the control polyanhydride side. This effect was most pronounced at day 13. By days 15 and 20, blanching and swelling on the control polyanhydride side were considerably diminished.

[0092] Histological examination of tissues from the mice was also performed. After sacrifice, tissues were fixed in 10% formalin, decalcified, embedded in paraffin, sectioned serially at 4 &mgr;m thickness, and stained with hematoxylin and eosin. The sections were subjected to microscopic evaluation and histometric assessment using 4, 10 and 20× magnifications. The histopathological examination correlated well with visual observations.

[0093] One mouse was sacrificed 24 hours post implantation. The histology showed heavy infiltration of polymorphonuclear (PMN) leucocytes and erythrocytes. The 0.1 mm films were mostly dissolved during the tissue processing procedure. The bone was denuded from the peritoneum and the polymer was in direct contact. The gingival epithelium and connective tissue below the subcular epithelium was broken. The coronal part of the periodontal ligament linking the alveolar bone to the coronal cementum was mostly intact. The method for reflecting the palatal mucosa was effective in not damaging the periodontal ligament below the level of the bone and coronal cementum. There was no significant difference between the bioactive and control side except for the decrease in swelling on the bioactive side.

[0094] Two mice were sacrificed four days post implantation. At this time point, some polymeric material remained in all sites. The 0.1 mm film was in direct contact with the palatal bone. An extensive, thin layer of palatal epithelium was observed that surrounded portions of the polymer specimens. The extent of the epithelium along the membranes was greater for the bioactive than for the control polyanhydride site. Similarly, the PMN cells inflammatory infiltrate was greater on the control polyanhydride side than on the bioactive polymer side. The infiltrate was denser below the epithelium adjacent to the membrane. The infiltrate along the palatal bone was much less.

[0095] Six mice were sacrificed at twenty days post implantation. At this time point, small remnants of a 0.3 mm film in only one specimen were present; all other specimens were devoid of polymer. Gingival epithelium including subcular and junctional were essentially restored on all sites. Two specimens showed external resorption that involved cementum and dentin on the controll polyanhydride side. Tissue specimens with bioactive polymer showed no alveolar bone, cementum and dentin resorption. However, a significant amount of new bone could be observed coronal to the reversal lines in the sites bearing bioactive films. New bone was also found in the control polyanhydride sites, but at insignificant amounts as compared to the bioactive polymer side. Inflammatory cell infiltrate was present and consisted primarily of PMN cells and macrophages. No erythrocytes were observed except within the vasculature. The intensity of the infiltrate was lower on the bioactive polymer sites.

[0096] Quantitative analyses were also performed via electronic images taken of the tissue sections using a Kodak MDS-120 camera attached to an Olympus CH-triocular microscope at magnifications of 4×, 10× and 40×. Using NIH Images 1.61 software, the area of bone, connective tissue, epithelium and artifacts at the lowest magnification were determined. Perpendicular to the widest part of the tooth, a square box was drawn with sides 575 pixels in length. The areas of bone, connective tissue, epithelium and artifacts were determined by the number of pixels within the defined box. All images were blindly analyzed. Sections were taken from mice sacrificed after 20 days from membranes that were either 0.3 or 2 mm thick. Results are shown in the following Table. 1 Bone Area Bone Area Polymer (0.3 mm) (0.2 mm) Control Polyanhydride 94,750 85,563 Bioactive Polymer 129,637 99,702

[0097] These experiments demonstrate that implantation of a film comprising an aromatic polyanhydride that hydrolyzes to form a therapeutically useful salicylate resulted in less swelling in tissues adjacent to the film and a decrease in the density of inflammatory cells as compared to other polyanhydride films. Further, little or no bone resorption was observed in the regions near the film as indicated by increased thickness of the palatal. In fact, data from quantitative analyses are indicative of compositions used in the present invention either promoting bone growth or decreasing bone resorption relative to the polyanhydride composition. Accordingly, use of compositions comprising an aromatic polyanhydride that hydrolyzes to form a therapeutically useful salicylate in dental and osteopathic applications enhances the healing process of bone as compared to other polymer systems routinely used in these applications.

[0098] The invention also provides for bioactive implants which are useful for treating periodontal disease. As shown in FIG. 1, a bioactive implant 100 comprises a film of material which is sized and shaped to be received in or near the gingival cleft. For instance, the film has a height 102 of about 1-2 mm, a width 104 of about 1-5 mm, and a thickness 106 of about 0.1-2.0 mm. It should be noted, however, that other suitably sized films may be configurable to be received in or near the gingival cleft. Other examples for the bioactive implant 100 include, but are note limited to membranes, pastes, gels, chips, or microspheres. The bioactive agent further includes an anti-inflammatory agent, for instance, any of the agents discussed above. Options for the anti-inflammatory agent include, but are not limited to, coatings, agents molded in or with a polymer matrix, or agents embedded in a polymer.

[0099] The following non-limiting examples set forth hereinbelow illustrate certain aspects of the invention. All parts and percentages are by weight unless otherwise noted and all temperatures are in degrees Celsius. Except for acetic anhydride and ethyl ether (Fisher Scientific), all solvents and reagents were obtained from Aldrich Chemical. All solvents were HPLC grade. All other reagents were of analytical grade and were purified by distillation or recrystallization.

[0100] All compounds were characterized by a proton nuclear magnetic resonance (NMR) spectroscopy, infrared (IR) spectroscopy, gel permeation chromatography (GPC), high performance liquid chromatography (HPLC), differential scanning calorimetry (DSC), and thermal gravimetric analysis (TGA). Infrared spectroscopy was preformed on an ATI Mattson Genesis (M100) FTIR Spectrophotometer. Samples were prepared by solvent casting on NaCl plates. 1H and 13CNMR spectroscopy was obtained on a Varian 200 MHZ or Varian 400 MHZ spectrometer in solutions of CDCl3 or DMSO-d6 with solvent as the internal reference.

[0101] GPC was performed on a Perkin-Elmer Advanced LC Sample Processor (ISS 200) with PE Series 200 LC pump and a PE Series LC Refractive Index Detector to determine molecular weight and polydispersity. The data analysis was carried out using Turbochrom 4 software on a DEC Celebris 466 computer. Samples were dissolved in tetrahydrofuran and eluted through a mixed bed column (PE PL gel, 5 &mgr;m mixed bed) at a flow rate of 0.5 mL/minute. Samples (about 5 mg/mL) were dissolved into the tetrahydrofuran and filtered using 0.5 &mgr;m PTFE syringe filters prior to column injection. Molecular weights were determined relative to narrow molecular weight polystyrene standards (Polysciences, Inc.).

[0102] Thermal analysis was performed on a Perkin-Elmer system consisting of a TGA 7 thermal gravimetric analyzer equipped with PE AD-4 autobalance and Pyris 1 DSC analyzer. Pyris software was used to carry out data analysis on a DEC Venturis 5100 computer. For DSC, an average sample weight of 5-10 mg was heated at 10° C./minute at a 30 psi flow of N2. For TGA, an average sample weight of 10 mg was heated at 20° C./minute under a 8 psi flow of N2. Sessile drop contact angle measurements were obtained with an NRL Goniometer (Rame-hart) using distilled water. Solutions of polymer in methylene chloride (10% wt/volume) were spun-coated onto glass slips, at 5,000 rpm for 30 seconds.

EXAMPLES

Example 1

Preparation of 1,6-Bis(o-Carboxyphenoxy) Hexane Dicarboxylic Acid

[0103] To a mixture of salicylic acid (77.12 g, 0.5580 mole) and distilled water (84 mL) sodium hydroxide (44.71 g, 1.120 mole) was added. The reaction was brought to reflux temperature before 1,6dibromohexane (45.21 g, 0.2790 mole) was added drop-wise. Reflux was continued for 23 hours after which additional sodium hydroxide (11.17 g, 0.2790 mole) was added. The mixture was refluxed for 16 more hours, cooled, filtered, and washed with methanol. The yield was 48.8%.

Example 2

Preparation of 1,6-Bis(o-Carboxyphenoxy) Hexane Monomer (o-CPH)

[0104] The dicarboxylic acid of Example 1 was acetylated in an excess of acidic anhydride at reflux temperature. The resulting monomer was precipitated with methylene chloride into an excess of diethyl ether. The yield was 66.8%.

Example 3

Preparation of Poly(1,6-Bis(o-Carboxyphenoxy) Hexane) (Poly(o-CPH))

[0105] The monomer of Example 2 was polymerized in a melt condensation performed at 180° C. for 3 hours under vacuum in a reaction vessel with a side arm.

[0106] The polymerization vessel was flushed with nitrogen at frequent intervals. The polymer was isolated by precipitation into diethyl ether from methylene chloride. The yield was quantitative.

[0107] All compounds were characterized by nuclear magnetic resonance spectroscopy, GPC, differential scanning calorimetry (DSC), thermal gravimetric analysis, contact angle measurements, UV spectroscopy, mass spectroscopy, elemental analysis and high pressure liquid chromatography (HPLC).

[0108] The o-CPH monomer was polymerized by melt polycondensation for 60 minutes at temperatures ranging from 100° C. to 300° C. Analysis of the resulting polymers by GPC indicated that the highest molecular weight, coupled with the lowest polydispersity index occurred at 260° C.

[0109] The poly(o-CPH) was generally soluble in methylene chloride and chloroform, while the poly(p-CPH) was not. The poly(o-CPH) was slightly soluble in tetrahydrofuran, acetone and ethyl acetate.

[0110] Disks of poly(o-CPH), poly(p-CPH) and, as a reference, poly(lactic acid glycolic acid) were prepared and placed in 0.1 phosphate buffer solution at 37° C. for 4 weeks. The degradation media was replaced periodically. The degradation profile was linear up to three weeks time. In prior art polyanhydride systems, the aromatic groups are para-substituted. This substitution pattern results in higher melt and glass transition temperatures and decreased solubility, thus ultimately making these parasubstituted polymers difficult to process.

[0111] Poly(o-CPH), unlike poly(p-CPH), has both a lower melting point (65° C. vs. 143° C.) and glass transition temperature (35° C. vs. 47° C.). It is also possible to solution cast poly(o-CPH) using low-boiling solvents whereas poly(p-CPH) is relatively insoluble in most organic and aqueous solvents. This structural modification gives a polymer whose hydrolysis products are chemically similar to aspirin. Aspirin is an anti-inflammatory agent derived from salicylic acid, which is one of the reagents used to synthesize the inventive polyanhydrides. Therefore, the degradation products of this polymer actually aid in patient recovery. Because of pliability and ease of processing, the aromatic polyanhydrides of the present invention have great potential as polymer scaffolds for wound healing.

Example 4

Preparation of 1,3-bis(o-carboxyphenoxy)propane dicarboxylic acid

[0112] 1,3-dibromopropane (14.7 mL, 0.145 mole) was added to a mixture of salicylic acid (40.0 g, 0.290 mole), distilled water (44 mL) and sodium hydroxide (23.2 g, 0.580 mole) using the method described in Example 1. After 4 hours, additional sodium hydroxide (5.79 g, 0.145 mole) was added to the reaction mixture. Reflux was continued for another 4 hours, after which the mixture was cooled, filtered and washed using the methods described in Example 1. The yield was 37.7%

Example 5

Preparation of poly(1,3-bis(o-carboxyphenoxy)propane)

[0113] The dicarboxylic acid of Example 4 was acetylated using the methods of Example 2. The acetylated dicarboxylic acid was then polymerized using the methods described in Example 3. The resulting polymer had a Mw of 8,500 daltons and a polydispersity of 2.3.

[0114] Contact angle measurements on solvent-cast films demonstrated that the hexyl chain of the polymer of Example 3 increased the surface hydrophobicity relative to the shorter propyl chain of the polymer of Example 5. A comparison of thermal characteristics emphasized the effects of lengthening the alkyl chain. In particular, the polymer of Example 3 has a Tg of 34° C. and a Td of 410° C., while the polymer of Example 5 had a Tg of 50° C. and a Td of 344° C. Thus, the hexyl chain decreased the glass transition temperature (Tg) relative to the propyl chain, reflecting the increased flexibility of the polymer chain. The opposite trend was observed for decomposition temperatures (Td), with the longer alkyl chain increasing the Td.

[0115] Optimum polycondensation conditions were determined for the polymer of Example 3. Optimum conditions were defined as those that yielded a crude polymer with the highest molecular weight and highest Tg. Higher reaction temperatures decreased the Mw values (measured by GPC) with a concurrent increase in polydispersity. As expected for a condensation polymerization, longer reaction times yielded polymers with higher molecular weights. However, over longer reaction times, there appeared a subsequent decrease in Tg. Based on these results, the optimum conditions were defined as temperatures of 220° C. for 150 minutes under a vacuum.

Example 6

Preparation of 1,8-bis[o-(benzylcarboxy) carboxyphenyl] octane dicarboxlic acid ester

[0116] The initial synthesis of poly(anhydride-ester) dicarboxylic acid monomers was attempted using the same methodology used for the poly(anhydride-ether) dicarboxylic monomers of Example 3. It was found, however, that the reactivity of the phenol was enhanced by benzylation of the carboxylic acid group. In addition, the solubility of benzyl salicylate in organic media increased the ability of the reaction to move forward.

[0117] Thus, benzyl salicylate (1.530 g, 6.720 mmole) and distilled tetrahydrofuran were combined under an inert atmosphere in a reaction flask. An ice-salt bath was placed under the reaction flask and the addition of 60% sodium hydride (0.4840 g, 12.10 mmole) followed. After one hour, sebacoyl chloride (0.7850 g, 3.280 mmole) was added drop-wise to the 0° C. reaction mixture. After 30 minutes, the reaction mixture was vacuum filtered, the filtrate collected and the solvent removed to yield the free carboxylate as a white solid residue. Purification was performed using a chromatron with ethyl acetate/methylene chloride (20/80) as the solvent system. The yield was 43%.

Example 7

Polymerization of Poly(1,8-bis(o-dicarboxyphenyl) octane)

[0118] To remove the benzyl protecting groups, the 1,8-bis[(benzylcarboxy)carboxyphenyl]octane dicarboxylic acid ester of Example 6 (0.06000 g, 0.9620 mmole) was dissolved in methylene chloride in a reaction flask (60.00 mL). The catalyst Pd-C (10%, 1.200 g) was added to the reaction flask and hydrogen was bubbled through the solution. After 30 minutes, the reaction was complete. The reaction mixture was filtered and the solvent removed to yield the free dicarboxylic acid as a white solid residue which was recrystallized using petroleum ether and methylene chloride. The yield was 45%.

[0119] The dicarboxylic acid was acetylated using the methods described in Example 2 and the acetylated dicarboxylic acid was then polymerized using the methods described in Example 3. The resulting polymer had a Mw of 3,000 daltons and a polydispersity of 1.40.

[0120] Subsequent polymerizations yielded polymers with Mw's ranging from 2,000 to 5,000 daltons with corresponding polydispersities of approximately 1.40.

[0121] The poly(anhydride esters) of Example 7 were compression molded into circular discs and placed in phosphate buffered saline solution under acidic, neutral and basic conditions. Over the course of a three-week degradation study, the polymers in the acidic and neutral solutions showed no observable changes, whereas the polymer in the basic media showed significant morphological changes over time.

Example 8

Preparation of Poly[(1,8-bis (o-dicarboxyphenyl) octane)-(1,6-bis (p-carboxyphenoxy) hexane] copolymers

[0122] The 1,8-bis(o-dicarboxyphenyl) octane of Example 2 was copolymerized with 1,6-bis(p-carboxyphenoxy) hexane using the methods described in Example 3. In an in vivo mouse study, each mouse was implanted with 2 polymers, the copolymer of Example 8 and poly(1,6-bis(p-carboxyphenoxy) hexane). Each polymer was compression molded for 1 to 5 minutes at 1 to 20 K psi depending on the thickness of polymer needed. The polymer was placed under the palatal gingival mucosa adjacent to the first maxillary molars.

[0123] All publications, patents, and patent documents (including U.S. patent application Ser. Nos. 09/455,861 and 09/5b8,217; as well as International Patent Application PCT/US98/18816) are incorporated by reference herein, as though individually incorporated by reference. The invention has been described with reference to various specific and preferred embodiments and techniques.

[0124] However, it should be understood that many variations and modifications may be made while remaining within the spirit and scope of the invention.

Claims

1. The use of an anti-inflammatory agent to prepare a medicament useful for treating periodontal disease by administration at the site of the periodontal disease.

2. The use of claim 1 wherein the agent is a salicylate.

3. The use of claim 1 wherein the agent is a non-steroidal anti-inflammatory compound.

4. The use of claim 1 wherein the agent is an aromatic anti-inflammatory compound.

5. The use of claim 1 wherein the agent is a cyclooxygenase inhibitor.

6. The use of claim 1 wherein the agent is a cyclooxygenase-1 inhibitor.

7. The use of claim 1 wherein the agent is a cyclooxygenase-2 inhibitor.

8. The use of claim 1 wherein the agent is etodolac, celebrex, meloxicam, piroxicam, nimesulide, nabumetone, or rofecoxib.

9. The use of claim 1 wherein the agent is formulated for controlled release at the site of the periodontal disease.

10. The use of claim 9 wherein the agent is incorporated in the matrix of a biodegradable polymer.

11. The use of claim 10 wherein the agent is Isonixin, Amtolmetin Guacil, Proglumetacin, Piketoprofen, Difenamizole, Epirizole, Apazone, Feprazone, Morazone, Phenylbutazone, Pipebuzone, Propyphenazone, Ramifenazone, Thiazolinobutazone, Aspirin, Benorylate, Calcium Acetylsalicylate, Etersalate, Imidazole Salicylate, Lysine Acetylsalicylate, Morpholine Salicylate, 1-Naphthyl Salicylate, Phenyl Acetylsalicylate, Ampiroxicam, Droxicam, S-Adenosylmethionine, Amixetrine, Benzydamine, Bucolome, Difenpiramide, Emorfazone, Guaiazulene, Nabumetone, Nimesulide, Proquazone, Superoxide Dismutase, or Tenidap.

12. The use of claim 10 wherein the polymer comprises anhydride bonds in the polymer backbone.

13. The use of claim 10 wherein the polymer is a polyanhydride comprising a repeating unit having the structure:

10

wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

14. The use of claim 9 wherein the agent is appended to a biodegradable polymer.

15. The use of claim 14 wherein the agent is Etofenamate, Talniflumate Terofenamate, Acemetacin, Alclofenac, Bufexamac, Cinmetacin, Clopirac, Felbinac, Fenclozic Acid, Fentiazac, Ibufenac, Indomethacin, Isofezolac, Isoxepac, Lonazolac, Metiazinic Acid, Mofezolac, Oxametacine, Pirazolac, Sulindac, Tiaramide, Tolmetin, Tropesin, Zomepirac, Bumadizon, Butibufen, Fenbufen, Xenbucin, Clidanac, Ketorolac, Tinoridine, Benoxaprofen, Bermoprofen, Bucloxic Acid, Fenoprofen, Flunoxaprofen, Flurbiprofen, Ibuprofen, Ibuproxam, Indoprofen, Ketoprofen, Loxoprofen, Naproxen, Oxaprozin, Pirprofen, Pranoprofen, Protizinic Acid, Suprofen, Tiaprofenic Acid, Zaltoprofen, Benzpiperylon, Mofebutazone, Oxyphenbutazone, Suxibuzone, Acetaminosalol, Parsalmide, Phenyl Salicylate, Salacetamide, Salicylsulfuric Acid, Isoxicam, Lomoxicam, Piroxicam, Tenoxicam, &egr;-Acetamidocaproic Acid, Bendazac, &agr;-Bisabolol, Paranyline, Perisoxal, or Zileuton.

16. The use of claim 1 wherein the agent is administered after periodontal surgery.

17. The use of claim 14 wherein the polymer comprises anhydride bonds in the polymer backbone.

18. The use of claim 14 wherein the polymer is a polyanhydride comprising a repeating unit having the structure:

11

wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

19. The use of claim 9 wherein the agent is incorporated into the backbone of a biodegradable polymer.

20. The use of claim 19 wherein the agent is Enfenamic Acid, Aceclofenac, Glucametacin, Alminoprofen, Carprofen, Ximoprofen, Salsalate, 3-Amino-4-hydroxybutyric Acid, Ditazol, Fepradinol, or Oxaceprol.

21. The use of claim 19 wherein the polymer comprises anhydride bonds in the polymer backbone.

22. The use of claim 19 wherein the polymer is an aromatic polyanhydride.

23. The use of claim 19 wherein the polymer is a polyanhydride comprising a repeating unit having the structure:

12

where Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

24. The use of claim 19 wherein Ar is Flufenamic Acid, Meclofenamic Acid, Mefenamic Acid, Niflumic Acid, Tolfenamic Acid, Amfenac, Bromfenac, Diclofenac Sodium, Etodolac, Bromosaligenin, Diflunisal, Fendosal, Gentisic Acid, Glycol Salicylate, Mesalamine, Olsalazine, Salicylamide O-Acetic Acid, Salicilic Acid, Sulfasalazine,

25. The use of claim 19 wherein the polymer is incorporated into a film, paste, gel, fiber, chip, microsphere or scaffolding for cell ingrowth.

26. The use of claim 23 wherein each Z1 is an ester.

27. An orthopedic device comprising an anti-inflammatory agent that is formulated for controlled release.

28. The device of claim 27 wherein the agent is incorporated in the matrix of a biodegradable polymer.

29. The device of claim 28 wherein the agent is Isonixin, Amtolmetin Guacil, Proglumetacin, Piketoprofen, Difenamizole, Epirizole, Apazone, Feprazone, Morazone, Phenylbutazone, Pipebuzone, Propyphenazone, Ramifenazone, Thiazolinobutazone, Aspirin, Benorylate, Calcium Acetylsalicylate, Etersalate, Imidazole Salicylate, Lysine Acetylsalicylate, Morpholine Salicylate, 1-Naphthyl Salicylate, Phenyl Acetylsalicylate, Ampiroxicam, Droxicam, S-Adenosylmethionine, Amixetrine, Benzydamine, Bucolome, Difenpiramide, Emorfazone, Guaiazulene, Nabumetone, Nimesulide, Proquazone, Superoxide Dismutase, or Tenidap.

30. The use of claim 28 wherein the polymer comprises anhydride bonds in the polymer backbone.

31. The device of claim 28 wherein the polymer is a polyanhydride comprising a repeating unit having the structure:

13

where Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

32. The device use of claim 28 wherein the agent is appended to a biodegradable polymer.

33. The use of claim 32 wherein the agent is Etofenamate, Talniflumate Terofenamate, Acemetacin, Alclofenac, Bufexamac, Cinmetacin, Clopirac, Felbinac, Fenclozic Acid, Fentiazac, Ibufenac, Indomethacin, Isofezolac, Isoxepac, Lonazolac, Metiazinic Acid, Mofezolac, Oxametacine, Pirazolac, Sulindac, Tiaramide, Tolmetin, Tropesin, Zomepirac, Bumadizon, Butibufen, Fenbufen, Xenbucin, Clidanac, Ketorolac, Tinoridine, Benoxaprofen, Bermoprofen, Bucloxic Acid, Fenoprofen, Flunoxaprofen, Flurbiprofen, Ibuprofen, Ibuproxam, Indoprofen, Ketoprofen, Loxoprofen, Naproxen, Oxaprozin, Pirprofen, Pranoprofen, Protizinic Acid, Suprofen, Tiaprofenic Acid, Zaltoprofen, Benzpiperylon, Mofebutazone, Oxyphenbutazone, Suxibuzone, Acetaminosalol, Parsalmide, Phenyl Salicylate, Salacetamide, Salicylsulfuric Acid, Isoxicam, Lomoxicam, Piroxicam, Tenoxicam, &egr;-Acetamidocaproic Acid, Bendazac, &agr;-Bisabolol, Paranyline, Perisoxal, or Zileuton.

34. The device of claim 32 wherein the polymer comprises anhydride bonds in the polymer backbone.

35. The device of claim 32 wherein the polymer is a polyanhydride comprising a repeating unit having the structure:

14

wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar ortho to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

36. The device of claim 28 wherein the agent is incorporated into the backbone of a biodegradable polymer.

37. The device of claim 36 wherein the agent is Enfenamic Acid, Aceclofenac, Glucametacin, Alminoprofen, Carprofen, Ximoprofen, Salsalate, 3-Amino4-hydroxybutyric Acid, Ditazol, Fepradinol, or Oxaceprol.

38. The device of claim 36 wherein the polymer comprises anhydride bonds in the polymer backbone.

39. The device of claim 36 wherein the polymer is an aromatic polyanhydride.

40. The device of claim 36 wherein the polymer is a polyanhydride comprising a repeating unit having the structure:

15

wherein Ar is a substituted or unsubstituted aromatic ring and R is —Z1—R1—Z1— substituted on each Ar orthio to the anhydride group, wherein R1 is a difunctional organic moiety and Z1 is a difunctional moiety selected from the group consisting of esters, amides, urethanes, carbamates and carbonates.

41. The device of claim 40 wherein Ar is Flufenamic Acid, Meclofenamic Acid, Mefenamic Acid, Niflumic Acid, Tolfenamic Acid, Amfenac, Bromfenac, Diclofenac Sodium, Etodolac, Bromosaligenin, Diflunisal, Fendosal, Gentisic Acid, Glycol Salicylate, Mesalamine, Olsalazine, Salicylamide O-Acetic Acid, Salicilic Acid, Sulfasalazine,

42. The device of claim 36 wherein the polymer is incorporated into a film, paste, gel, fiber, chip, microsphere or scaffolding for cell ingrowth.

43. The device of claim 40 wherein each Z1 is an ester.

44. The device of claim 27 wherein the agent enhances bone growth.

45. A bioactive implant comprising:

a polymer film configured to be received in or near the gingival cleft, the film including an anti-inflammatory agent.

46. The bioactive implant of claim 45, wherein the film has a thickness of about 0.1-2.0 mm, a width of about 1-5 mm, and a height of about 1-2 mm.

47. The bioactive implant of claim 45, wherein the film is configured to be disposed adjacent to a bone.